Low temperature sintering and microwave dielectric properties of Li2ZnTi3O8 ceramics doped with ZnO–La2O3–B2O3 glass

Li₂ZnTi₃O₈ ceramics doped with ZnO–La₂O₃–B₂O₃ glass were prepared by the conventional solid-state ceramic route. The effects of the ZnO–La₂O₃–B₂O₃ glass on the sintering temperature, phase composition, microstructure and microwave dielectric properties of Li₂ZnTi₃O₈ ceramics were investigated. The addition of ZLB glass can reduce the sintering temperature of Li₂ZnTi₃O₈ ceramic from 1075 °C to 925 °C without obvious degradation of the microwave dielectric properties. Only a single phase Li₂ZnTi₃O₈ with cubic spinel structure is formed in Li₂ZnTi₃O₈ ceramic with ZLB addition sintered at 925 °C. Typically, 1.0 wt% ZLB-doped Li₂ZnTi₃O₈ ceramic sintered at 925 °C can reach a maximum relative density of 95.8% and exhibits good microwave dielectric properties of ε_r=24.34, Q×f=41,360 GHz and τ_f=−13.4 ppm/°C. Moreover, this material is compatible with Ag electrode, which makes it a promising candidate for LTCC application.     

Effects of Al2O3 addition on the sintering behavior and microwave dielectric properties of CaSiO3 ceramics

The effects of Al₂O₃ addition on the densification, structure and microwave dielectric properties of CaSiO₃ ceramics have been investigated. The Al₂O₃ addition results in the presence of two distinct phases, e.g. Ca₂Al₂SiO₇ and CaAl₂Si₂O₈, which can restrict the growth of CaSiO₃ grains by surrounding their boundaries and also improve the bulk density of CaSiO₃-Al₂O₃ ceramics. However, excessive addition (≥2 wt%) of Al₂O₃ undermines the microwave dielectric properties of the title ceramics since the derived phases of Ca₂Al₂SiO₇ and CaAl₂Si₂O₈ have poor quality factor. The optimum amount of Al₂O₃ addition is found to be 1 wt%, and the derived CaSiO₃-Al₂O₃ ceramic sintered at 1250 °C presents improved microwave dielectric properties of ?_r = 6.66 and Q × f = 24,626 GHz, which is much better than those of pure CaSiO₃ ceramic sintered at 1340 °C (Q × f = 13,109 GHz).     

Sintering of glass-added BaZn1/3Nb2/3O3 ceramics

The complex perovskite oxide Ba(Zn_1/3Nb_2/3)O₃ (BZN) has been studied for its attractive dielectric properties which place this material interesting for applications as multilayer ceramics capacitors or hyperfrequency resonators. This material is sinterable at low temperature with combined glass phase–lithium salt additions, and exhibits, at 1 MHz very low dielectric losses combined with relatively high dielectric constant and a good stability of this later versus temperature. The 2 wt.% of ZnO–SiO₂–B₂O₃ glass phase and 1 wt.% of LiF-added BZN sample sintered at 900 °C exhibits a relative density higher than 95% and attractive dielectric properties: a dielectric constant ?_r of 39, low dielectrics losses (tan(δ) < 10⁻³) and a temperature coefficient of permittivity τ_? of 45 ppm/°C⁻¹. The 2 wt.% ZnO–SiO₂–B₂O₃ glass phase and 1 wt.% of B₂O₃-added BZN sintered at 930 °C exhibits also attractive dielectric properties (?_r = 38, tan(δ) < 10⁻³) and it is more interesting in terms of temperature coefficient of the permittivity (τ_? = −5 ppm/°C). Their good dielectric properties and their compatibility with Ag electrodes, make these ceramics suitable for L.T.C.C applications.     

Influence of A-site Ba substitution on microwave dielectric properties of (BaxMg1−x)(A0.05Ti0.95)O3 (A=Zr,Sn) ceramics

The microwave dielectric properties of (Ba_xMg_1−x)(A_0.05Ti_0.95)TiO₃ (A=Zr, Sn) ceramics were investigated with regard to substitution of Ba for Mg of A-site. The microwave dielectric properties were correlated with the Ba content. With an increase in Ba content from 0.01 to 0.1, the dielectric constant and the τ_f value increased, but the Q×f value decreased. The sintered (Ba_xMg_1−x)(Zr_0.05Ti_0.95)TiO₃ (called B_xMZT) ceramics had a permittivity in the range of 19.1−20.6, quality factor from 180,000 to 25,000 GHz, and variation in temperature coefficient of resonant frequency from −35 to −39 ppm/°C with increasing composition x. For sintered (Ba_xMg_1−x)(Sn_0.05Ti_0.95)TiO₃ (called B_xMST) ceramics, the dielectric constant increased from 19 to 20.5, Q×f value increased from 120,000 to 37,000 (GHz), and the τ_f value increased from −50 to −3.3 ppm/°C as the x increased from 0.01 to 0.1. When A=Sn and x=0.1, (Ba_0.1Mg_0.9)(Sn_0.05Ti_0.95)TiO₃ ceramics exhibited dielectric constant of 20.5, Q×f value of 37,000 (GHz), and a near-zero τ_f value of −3.3 ppm/°C sintered at 1210 °C for 4 h.     

Low-temperature sintering and microwave dielectric properties of 3Z2B glass–Al2O3 composites

A potential low temperature co-fired ceramics system based on zinc borate 3ZnO–2B₂O₃ (3Z2B) glass matrix and Al₂O₃ filler was investigated with regard to phase development and microwave dielectric properties as functions of the glass content and sintering temperature. The densification mechanism for 3Z2B–Al₂O₃ composites was reported. The linear shrinkage of 3Z2B glass–Al₂O₃ composites exhibited a typical one-stage densification behavior. XRD patterns showed that a new crystalline phase, ZnAl₂O₄ spinel, formed during densification, indicating that certain chemical reaction took place between the 3Z2B glass matrix and the alumina filler. Meanwhile, several zinc borate phases, including 4ZnO·3B₂O₃, crystallized from the glass matrix. Both of the reaction product phase and crystallization phases played an important role in improving the microwave dielectric properties of composites. The optimal composition sintered at 850–950 °C showed excellent microwave dielectric properties: ?_r = ∼5.0, Q·f₀ = ∼8000 GHz, and τ_f = ∼−32 ppm/°C at ∼7.0 GHz.     

Microwave dielectric properties of SnO2-doped CaSiO3 ceramics

SnO₂-doped CaSiO₃ ceramics were successfully synthesized by a solid-state method. Effects of different SnO₂ additions on the sintering behavior, microstructure and dielectric properties of Ca(Sn_1−xSi_x)O₃ (x=0.5–1.0) ceramics have been investigated. SnO₂ improved the densification process and expanded the sintering temperature range effectively. Moreover, Sn⁴⁺ substituting for Si⁴⁺ sites leads to the emergence of Ca₃SnSi₂O₉ phase, which has a positive effect on the dielectric properties of CaO–SiO₂–SnO₂ materials, especially the Qf value. The Ca(Sn_0.1Si_0.9)O₃ ceramics sintered at 1375 °C possessed good microwave dielectric properties: ε_r =7.92, Qf =58,000 GHz and τ_f=−42 ppm/°C. The Ca(Sn_0.4Si_0.6)O₃ ceramics sintered at 1450 °C also exhibited good microwave dielectric properties of ε_r=9.27, Qf=63,000 GHz, and τ_f=−52 ppm/°C. Thus, they are promising candidate materials for millimeter-wave devices.     

Low temperature sintering and microwave dielectric properties of Ce2(WO4)3 ceramics

Ce₂(WO₄)₃ ceramics have been synthesized by the conventional solid-state ceramic route. Ce₂(WO₄)₃ ceramics sintered at 1000 °C exhibited ?_r = 12.4, Qxf = 10,500 GHz (at 4.8 GHz) and τ_f = −39 ppm/°C. The effects of B₂O₃, ZnO–B₂O₃, BaO–B₂O₃–SiO₂, ZnO–B₂O₃–SiO₂ and PbO–B₂O₃–SiO₂ glasses on the sintering temperature and microwave dielectric properties of Ce₂(WO₄)₃ were investigated. The Ce₂(WO₄)₃ + 0.2 wt% ZBS sintered at 900 °C/4 h has ?_r = 13.7, Qxf = 20,200 GHz and τ_f = −25 ppm/°C.     

Dielectric properties of B2O3-doped 0.98CeO2–0.02CaTiO3 ceramics at microwave frequency

Microwave dielectric properties and microstructure of 0.98CeO₂–0.02CaTiO₃ ceramics with B₂O₃ additions prepared with the conventional solid-state route have been investigated. 0.98CeO₂–0.02CaTiO₃ ceramics can be sintered at 1290 °C for 4 h due to the sintering aid effect resulting from the B₂O₃ additions. At sintering temperature of 1380 °C for 4 h, 0.98CeO₂–0.02CaTiO₃ ceramics with 0.25 wt% B₂O₃ addition possess a dielectric constant (?_r) of 21.3, a Q × f value of 60,000 (at 8 GHz) and a temperature coefficient of resonant frequency (τ_f) of −41 ppm/°C.     

Effects of CaSiO3 addition on sintering behavior and microwave dielectric properties of Al2O3 ceramics

The effects of CaSiO₃ addition on the sintering behavior and microwave dielectric properties of Al₂O₃ ceramics have been investigated. The addition of CaSiO₃ into Al₂O₃ ceramics resulted in the emergence of Ca₂Al₂SiO₇ and CaAl₂Si₂O₈, which acting as liquid sintering aids can effectively lower the sintering temperature of Al₂O₃ ceramic. The Q × f value of Al₂O₃-CaSiO₃ ceramics decreased with the CaSiO₃ addition increasing because of the lower Q × f value of Ca₂Al₂SiO₇ and CaAl₂Si₂O₈. Compared with the pure CaSiO₃ ceramic, the Al₂O₃-CaSiO₃ ceramic with 20 wt% CaSiO₃ addition possessed good dielectric properties of ?_r = 9.36 and Q × f = 13,678 GHz at the similar sintering temperature.     

Microwave dielectric properties and structure of ZnO-Nb2O5-TiO2 ceramics

Ceramic samples based on ZnO-Nb₂O₅-TiO₂ compositions have been prepared using solid state ceramic route. The work was carried out over a wide range of initial ZnNb₂O₆ and Zn_0.17Nb_0.33Ti_0.5O₂ compounds concentration. The crystal structure and microstructure developments were studied using X-ray diffraction (XRD) and scanning electron microscopy (SEM). It was shown that the phase compositions of the samples present itself a columbite type and mixture of two phases—solid solutions of columbite and rutile types.The sintering behavior, permittivity, its temperature coefficients and quality factor had been characterized for ceramic samples in depending on compositions. The permittivity of the samples in this system is within the limits from 24 to 80, τ_? from 150 to −560 ppm/°C. For the samples with τ_? ∼ 0, ?_r ∼ 43.8 and Q·f = 35000 GHz at f = 9 GHz. The comparatively low sintering temperature (≤1080 °C) and high dielectric properties in microwave range make these ceramics promising for application in electronics.     

Densification, microstructural evolution and microwave dielectric properties of fluxed sintered 12R-Ba(Ti0.5Mn0.5)O3 ceramics

Doped hexagonal BaTiO₃ (h-BaTiO₃) ceramics have recently been identified as potential candidates for use in microwave dielectric resonators. However, similar to other common microwave ceramics, doped h-BaTiO₃ ceramics require a sintering temperature higher than 1400 °C. In this study, the effects of Bi₂O₃ and Li₂CO₃ on the densification, microstructural evolution and microwave properties of hexagonal 12R-Ba(Ti_0.5Mn_0.5)O₃ ceramics were examined. Results indicate that Bi₂O₃ and Li₂CO₃ are able to effectively reduce the sintering temperature of 12R-Ba(Ti₀₅Mn_0.5)O₃ ceramics through liquid phase sintering while retaining the hexagonal structure and the microwave dielectric properties. The best results were obtained for the 12R-Ba(Ti_0.5Mn_0.5)O₃ with the additions of 5 wt% Bi₂O₃ sintered at 1200 °C (?_r: 36.0, Qf_r: 6779 GHz, and τ_f: 25.3 ppm/°C), and 5 wt% Li₂CO₃ sintered at 1200 °C (?_r: 28.1, Qf_r: 5304 GHz, and τ_f: 35.3 ppm/°C).     

Transparent polycrystalline MgAl2O4 ceramic fabricated by spark plasma sintering: Microwave dielectric and optical properties

The optical properties and microwave dielectric properties of transparent polycrystalline MgAl₂O₄ ceramics sintered by spark plasma sintering (SPS) through homemade nanosized MgAl₂O₄ powders at temperatures between 1250 °C and 1375 °C are discussed. The results indicate that, with increasing sintering temperatures, grain growth and densification occurred up to 1275 °C, and above 1350 °C, rapid grain and pore growth occurred. The in-line light transmission increases with the densification and decreases with the grain/pore growth, which can be as high as 70% at the wavelength of 550 nm and 82% at the wavelength of 2000 nm, respectively. As the sintering temperature increases, Q×f and dielectric constant ε_r values increase to maximum and then decrease respectively, while τ_f value is almost independent of the sintering temperatures and remains between −77 and −71 ppm/°C. The optimal microwave dielectric properties (ε_r=8.38, Q×f=54,000 GHz and τ_f=−74 ppm/°C) are achieved for transparent MgAl₂O₄ ceramics produced by spark plasma sintering at 1325 °C for 20 min.     

Effects of heating rate on microstructures and microwave dielectric properties of (1 − x)ZnAl2O4–xTiO2 (x = 0.21) ceramics

(1 − x)ZnAl₂O₄–xTiO₂ (x = 0.21) ceramics were synthesized at 1500 °C for 3 h using the solid-state reaction at a heating rate from 1 to 7 °C/min. The effects of heating rate on the microstructure, phase composition and oxidation state of titanium in the ceramics were investigated. The XRD results show that this system is composed of two phases, i.e. ZnAl₂O₄ spinel and rutile. The “black core” phenomenon resulting from reduction of Ti⁴⁺ ion valence appears after the ceramics are sintered at the speed of 1 and 3 °C/min. As the heating rate increases, the density and quality factor (Q·f) increase initially and reach the maximum value when the heating rate is 5 °C/min, and then reduce quickly to the minimum, while the dielectric constant (?_r) and temperature coefficient of resonator frequency (τ_f) nearly do not change. The optimal microwave dielectric properties can be achieved in (1 − x)ZnAl₂O₄–xTiO₂ (x = 0.21) ceramics sintered at a heating rate of 5 °C/min with an ?_r value of 11.6, a Q·f value of 74,000 GHz (at about 6.5 GHz), and a τ_f value of −0.4 ppm/°C.     

Effects of CaTiO3 addition on the densification and microwave dielectric properties of BiSbO4 ceramics

In this study, the effects of CaTiO₃ addition on the sintering characteristics and microwave dielectric properties of BiSbO₄ were investigated. Pure BiSbO₄ achieved a sintered density of 8.46 g/cm³ at 1100 °C. The value of sintered density decreased with increasing CaTiO₃, and sintering at a temperature higher than 1100 °C led to a large weight loss (>2 wt%) caused by the volatile nature of the compound. Samples either sintered above 1100 °C or with a CaTiO₃ content exceeding 3 wt% showed poor densification. SEM micrographs revealed microstructures with bimodal grain size distribution. The size of the smaller grains ranged from 0.5 to 1.2 μm and that of the larger grains between 3 and 7 μm. The microwave dielectric properties of the (1−x) BiSbO_4−x CaTiO₃ ceramics are dependent both on the x value and on the sintering temperature. The 99.0 wt% BiSbO₄–1.0 wt% CaTiO₃ ceramic sintered at 1100 °C reported overall microwave dielectric properties that can be summarized as ε_r≈21.8, Q×f≈61,150 GHz, and τ_f≈−40.1 ppm/°C, all superior to those of the BiSbO₄ ceramics sintered with other additives.     

Synthesis of Zn3Nb2O8 ceramics using a simple and effective process

Synthesis of Zn₃Nb₂O₈ ceramics using a simple and effective reaction-sintering process was investigated. The mixture of ZnO and Nb₂O₅ was pressed and sintered directly without any prior calcination. Single-phase Zn₃Nb₂O₈ ceramics could be obtained. Density of these ceramics increased with soaking time and sintering temperature. A maximum density 5.72 g/cm³ (99.7% of the theoretical density) was found for pellets sintered at 1170 °C for 2 h. Pores were not found and grain sizes >20 μm were observed in pellets sintered at 1170 °C. Abnormal grain growth occurred and grains >50 μm could be seen in Zn₃Nb₂O₈ ceramics sintered at 1200 °C for 2 h and 1200 °C for 4 h. Reaction-sintering process is then a simple and effective method to produce Zn₃Nb₂O₈ ceramics for applications in microwave dielectric resonators.     

TEM observation of liquid phase sintering in V2O5 modified Zr0.8Sn0.2TiO4 microwave ceramics

The phenomena of liquid phase sintering in the V₂O₅ modified (Zr_0.8, Sn_0.2)TiO₄ (ZST) microwave ceramics has been investigated by using transmission electron microscopy (TEM) and energy dispersive X-ray analysis (EDS). The amounts of second phase were too low to be detected by X-ray diffraction (XRD), but could be observed by TEM bright field image. However, the presence of grain boundary phases did not degrade the microwave properties of V₂O₅ modified ZST ceramics. The ?_r value of 37.2, Q × f value of 51,000 (at 7 GHz) and τ_f value of −2.1 ppm/°C were obtained for ZST ceramics with 1 wt% V₂O₅ addition sintered at 1300 °C.     

Effects of sintering temperature and poling conditions on the electrical properties of Ba0.70Ca0.30TiO3 diphasic piezoelectric ceramics

The effects of sintering temperature and poling conditions on the electrical properties of tetragonal and orthorhombic diphasic Ba_0.70Ca_0.30TiO₃ (BCT) lead-free ceramics have been systematically investigated. On the one hand, with increasing sintering temperature from 1270 °C to 1400 °C, the bulk density increases monotonically and the Curie temperature keeps almost constant with the value of ∼120 °C, whereas the grain size, the maximum relative dielectric constant, room temperature polarization reach the maximum values for samples sintered at 1340 °C. On the other hand, it is found that the piezoelectric property depends on poling electric field and poling temperature significantly. An enhanced piezoelectric behavior of d₃₃=126 pC/N, k_p=0.29, and Q_m=588 is obtained for the BCT ceramics poled at 100 °C with 30 kV/cm field for 20 min. The aging behavior of the piezoelectric property is also investigated.     

High piezoelectric coefficient of Pr2O3-doped Ba0.85Ca0.15Ti0.90Zr0.10O3 ceramics

Pr₂O₃-doped Ba_0.85Ca_0.15Ti_0.90Zr_0.10O₃ (BCTZ-xPr) ceramics were prepared by the conventional solid-state method. A tetragonal phase is only observed in these ceramics, and the introduction of Pr₂O₃ decreases their sintering temperature without affecting negatively the piezoelectric constant. Enhanced ferroelectric properties were obtained in these BCTZ-xPr ceramics. The ceramic with x=0.06 wt% exhibits a good electrical behavior of d₃₃∼460 pC/N, k_p∼47.6%, ε_r∼4638, and tan δ∼0.015 when sintered at a low temperature of ∼1400 °C. As a result, the BCTZ-xPr ceramic is a promising candidate for lead-free piezoelectric ceramics.     

Dielectric properties of CuO-doped La2.98/3Ba0.01(Mg0.5Sn0.5)O3 ceramics at microwave frequency

The microwave dielectric properties of La_2.98/3Ba_0.01(Mg_0.5Sn_0.5)O₃ ceramics prepared by the conventional solid-state method were investigated for application in mobile communication. A 100 °C reduction of the sintering temperature was obtained by using CuO as a sintering aid. A dielectric constant of 20.0, a quality factor (Q × f) of 50,100 GHz and a temperature coefficient of resonant frequency τ_f of −78.3 ppm/°C were obtained when La_2.98/3Ba_0.01(Mg_0.5Sn_0.5)O₃ ceramics with 0.25 wt.% CuO were sintered at 1500 °C for 4 h.     

Effects of Al2O3 addition on the microstructure and microwave dielectric properties of Ba4Nd9.33Ti18O54 ceramics

Ba₄Nd_9.33Ti₁₈O₅₄·x wt%Al₂O₃ (BNT-A) ceramics (x=0, 0.5, 1.0, 1.5, 2.0, 2.5) were prepared by the conventional solid state reaction. The effects of Al₂O₃ on the microstructure and microwave dielectric properties of Ba₄Nd_9.33Ti₁₈O₅₄ (BNT) ceramics were investigated. X-ray diffraction and backscatter electronic images showed that the Al₂O₃ additive gave rise to a second phase BaAl₂Ti₅O₁₄ (BAT). The formation mechanism and grain growth of the BAT phase were first discussed. Dielectric property test revealed that the Al₂O₃ additive had improved the dielectric properties of the BNT ceramics: increased the Q×f value from 8270 to 12,180 GHz and decreased the τ_f value from 53.4 to 11.2 ppm/°C. A BNT-A ceramic with excellent dielectric properties: ε_r=70.2, Q×f=12,180 GHz, τ_f=20 ppm/°C was obtained with 2.0 wt% Al₂O₃ added after sintering at 1320 °C for 4 h.