制备条件对Ge2Sb2Te5薄膜电学性能的影响

研究了磁控溅射制备Ge2Sb2Te5薄膜时,制备条件诸如功率、气压等对薄膜性能的影响.主要通过测量薄膜方块电阻随退火温度的变化情况,探索Ge2Sb2Te5薄膜的成长机理.实验结果表明,不同溅射功率下制备的薄膜经不同温度退火后方块电阻没有明显的区别,而随着溅射气压的上升,薄膜方块电阻随退火温度的增加,下降的速率增加,意味着由面心立方结构转变为六方结构所需的结晶温度降低.     

制备条件对Ge2Sb2Te5薄膜电学性能的影响

研究了磁控溅射制备Ge2Sb2Te5薄膜时,制备条件诸如功率、气压等对薄膜性能的影响.主要通过测量薄膜方块电阻随退火温度的变化情况,探索Ge2Sb2Te5薄膜的成长机理.实验结果表明,不同溅射功率下制备的薄膜经不同温度退火后方块电阻没有明显的区别,而随着溅射气压的上升,薄膜方块电阻随退火温度的增加,下降的速率增加,意味着由面心立方结构转变为六方结构所需的结晶温度降低.     

溅射参数对Ge2Sb2Te5薄膜光学常数的影响

研究了溅射参数对Ge2Sb2Te5薄膜的光学常数随波长变化关系的影响,结果表明：(1)当溅射功率一定时,随溅射氩气气压的增加Ge2Sb2Te5薄膜的折射率先增大后减小,而消光系数先减小后增大.(2)当溅射氩气气压一定时,对于非晶态薄膜样品,在500nm波长以下,折射率随溅射功率的增加先增加后减小,消光系数则逐渐减小;在500nm以上,折射率随溅射功率的增加逐渐减少,消光系数先减小后增加.对于晶态薄膜样品,在整个波长范围折射率随溅射功率的增加先减小后增加,消光系数则逐渐减少.(3)薄膜样品的光学常数都随波长的变化而变化,在长波长范围变化较大,短波长范围变化较小.探讨了影响Ge2Sb2Te5薄膜光学常数的机理.     

溅射参数对Ge_2Sb_2Te_5薄膜光学常数的影响

研究了溅射参数对 Ge2 Sb2 Te5 薄膜的光学常数随波长变化关系的影响 ,结果表明 :(1)当溅射功率一定时 ,随溅射氩气气压的增加 Ge2 Sb2 Te5 薄膜的折射率先增大后减小 ,而消光系数先减小后增大 .(2 )当溅射氩气气压一定时 ,对于非晶态薄膜样品 ,在 5 0 0 nm波长以下 ,折射率随溅射功率的增加先增加后减小 ,消光系数则逐渐减小 ;在 5 0 0 nm以上 ,折射率随溅射功率的增加逐渐减少 ,消光系数先减小后增加 .对于晶态薄膜样品 ,在整个波长范围折射率随溅射功率的增加先减小后增加 ,消光系数则逐渐减少 .(3)薄膜样品的光学常数都随波长的变化而变化 ,在长波     

溅射参数为Ge2Sb2Te5薄膜光学常数的影响

研究了溅射参数对Ge2Sb2Te5薄膜的光学常数随波长变化关系的影响。结果表明：（1）当浅射功率一定时,随溅射氩气气压的增加Ge2Sb2Te5薄膜的折射率先增大后减小,而消光系数先减小后增大。（2）当溅射氩气压一定时,对于非晶态薄膜样品,在500nm波长以下,折射率随溅射功率的增加先增加后减小,消光系数则逐渐减小;在500nm以上,折射率随溅射功率的增加逐渐减少,消光系数先减小后增加。 对于晶态薄膜样品,在整个波长范围折射率随溅射功率的增加先减小后增加,消光系数则逐渐减少。（3）薄膜样品的光学常数都随波长的变化而变化,在长波长范围变化较大,短波长范围变化较小,探讨了影响Ge2Sb2Te5薄膜光学常数的机理。     

硅离子注入对Ge2Sb2Te5结构和电阻的影响

采用磁控射频溅射法制备了Ge2Sb2Te5薄膜，利用离子注入法研究了硅掺杂对薄膜结构和电阻性能的影响. 研究发现，由于硅的掺杂，Ge2Sb2Te5薄膜的结构不仅保留了原有的面心立方低温晶相和六方高温晶相，而且出现了菱形六面体的Sb2Te3晶相；掺杂硅后，Ge2Sb2Te5薄膜的电阻有较大变化，晶态电阻的提高有利于降低非晶化相变过程的操作电流，薄膜电阻-温度稳定性的改善可保证有较宽的操作电流波动范围.     

硫系相变材料Ge1Sb2Te4和Ge2Sb2Te5薄膜相变速度及电学输运性质研究

利用磁控溅射方法制备了Ge1Sb2Te4和Ge2Sb2Te5两种相变存贮材料的薄膜.原位X射线衍射(XRD)的结果表明,随着退火温度的升高,Ge1Sb2Te4和Ge2Sb2Te5薄膜都逐步晶化,材料结构发生了从非晶态到面心立方结构、再到六角密堆结构的转变.由衍射峰的半宽高可以看出,在达到第一次相变温度后,Ge2Sb2T...     

硅离子注入对Ge2Sb2Te5结构和电阻的影响

采用磁控射频溅射法制备了Ge2Sb2Te5薄膜,利用离子注入法研究了硅掺杂对薄膜结构和电阻性能的影响.研究发现,由于硅的掺杂,Ge2Sb2Te5薄膜的结构不仅保留了原有的面心立方低温晶相和六方高温晶相,而且出现了菱形六面体的Sb2Te3晶相;掺杂硅后,Ge2Sb2Te5薄膜的电阻有较大变化,晶态电阻的提高有利于降低非晶化相变过程的操作电流,薄膜电阻-温度稳定性的改善可保证有较宽的操作电流波动范围.     

硅离子注入对Ge2Sb2Te5结构和电阻的影响

采用磁控射频溅射法制备了Ge2Sb2Te5薄膜,利用离子注入法研究了硅掺杂对薄膜结构和电阻性能的影响.研究发现,由于硅的掺杂,Ge2Sb2Te5薄膜的结构不仅保留了原有的面心立方低温晶相和六方高温晶相,而且出现了菱形六面体的Sb2Te3晶相;掺杂硅后,Ge2Sb2Te5薄膜的电阻有较大变化,晶态电阻的提高有利于降低非晶化相变过程的操作电流,薄膜电阻-温度稳定性的改善可保证有较宽的操作电流波动范围.     

Sb2Te3热电薄膜磁控溅射制备工艺

Sb2Te3基半导体合金是目前性能较好的热电半导体材料.将材料低维化处理可以获得较块状材料更大的热电优值.通过磁控溅射工艺制备低维Sb2Te3薄膜,并通过AFM、XRD和XPS测试方法对薄膜的成分、薄膜表面以及原子偏析进行表征.通过退火工艺去除薄膜应力,观察退火工艺前后薄膜表面形貌的变化以及退火温度对薄膜表面质量的影响.试验结果表明通过磁控溅射工艺所制备出的Sb2Te3薄膜为非晶态,随着溅射功率增大,薄膜的表面粗糙度增大.退火可使薄膜变为晶态,但是表面粗糙度增大.较大或较小溅射功率下所制备的薄膜其合金成分与合金靶材有较大偏差.     

V_2O_5/V/V_2O_5薄膜退火条件对其的制备及特性的影响

利用间歇通O2的方式,采用射频磁控溅射法在Si3N4衬底上制备V2O5/V/V2O5复合薄膜,研究了不同原位退火条件对薄膜阻值及电阻温度系数(TCR)的影响。结果表明,经过退火处理后的V2O5/V/V2O5复合薄膜方阻值大大降低,电阻-温度曲线呈现良好的线性特性,并具有高TCR值及优良的电学稳定性。利用X射线光电子能谱(XPS)对退火后的V2O5/V/V2O5复合薄膜表面进行V、O元素分析,结果表明,V2O5/V/V2O5复合薄膜各层间的扩散效果显著影响薄膜表面不同价态V离子的含量,低价V离子会随着退火温度的升高及退火时间的延长而增多,薄膜表面对水分子的吸附也随之变强。在实验结果的基础上,利用扩散理论阐述了退火条件对V2O5/V/V2O5复合薄膜电学性能影响的机理。     

Atomic force microscopy (AFM) and X-ray diffraction (XRD) investigations of copper thin films prepared by dc magnetron sputtering technique

This paper addresses the influences of sputtering power and deposition pressure on the surface morphology and structural behavior of dc magnetron sputter-deposited copper (Cu) thin films on p-type silicon grown at room temperature. Results from our experiments show that the deposition rate of the Cu film increases proportionally with the sputtering power and decreases with deposition pressure. From the atomic force microscopy (AFM) and X-ray diffraction (XRD) analysis, high sputtering power enhances the microstructure of the Cu film through the surface diffusion mechanism of the adatom. The poor microstructure as a result of low sputtering power deposition was manifested with the smaller value of Cu film root mean square (RMS) roughness obtained. The deposition pressure has the contrary influence on structural properties of Cu film in which high deposition pressure favors the formation of voided boundaries film structure with degraded film crystallinity due to the shadowing effect, which varies with different deposition pressures.     

Si和GaAs衬底上生成WN_x薄膜(英文)

WNx films with different composition are formed on Si(100) and GaAs (100) by the reactive rf sputtering in a mixed nitrogen-argon gas to study the influence of various conditions upon WNx film,- one of the most promising materials for self-aligned GaAs MESFET. With the increase of the partial pressure ratio of nitrogen gas or the decrease of sputtering pressure, the deposition rate of WNx film decreases and the atomic percentage of N in the film increaces until it is saturated. Annealing at high temperature in flowing H2 gas induces the decreace of atomic percentage of N in WNx film. After annealing at 900℃ for 30 minites in flowing N2 gas, WNx film formed at lower sputtering pressure is found to have W and W2N, and to have W, WN and/or W2N phase at a higher sputtering pressure. AES analysis shows no conspicuous diffusion after annealing. The electrical resisti vity of WNx film decreases by about 75% as compared with that of as-sputtered film.     

RF溅射ZnO薄膜工艺与结构研究

通过RF磁控溅射在Si(100)基片上制备了ZnO薄膜,并研究了磁控溅射中各生长参数,如衬底温度、氧分压及后处理工艺等因素对ZnO薄膜微结构、表面形貌与结晶取向的影响。结果表明:溅射温度和氧分压对薄膜的微结构与择优取向有很大的影响,并对不同的溅射工艺进行了分析比较,从而确定了最佳溅射及后处理条件:RF溅射温度小于300℃,功率为50W,ψ(Ar:O2)为20:5,退火温度550~600℃,并获得了c轴择优取向的ZnO薄膜。     

Au/SiO_2纳米复合膜的形貌及发光特性

采用磁控溅射和退火法在Si(111)衬底上制备Au/SiO2纳米复合薄膜,并在两种实验模式下进行退火处理。模式A:不同的退火温度,退火20min;模式B:退火温度1 000℃,不同的退火时间。用扫描电子显微镜(SEM)、X射线衍射方法(XRD)和光致发光(PL)等测试手段对退火后的Au/SiO2纳米复合薄膜的表面形貌、微观结构和发光特性进行了分析。SEM结果表明,在模式A情况下,随着温度的增加,Au纳米颗粒的大小先增加后减小,这与XRD测试结果相吻合。PL结果表明,在模式B情况下,随着退火时间的增加,发光峰强度先增加后减小。在325nm波长下激发,440nm的发光峰与Au颗粒的大小和数量有关,而523nm的发光峰与纳米复合膜的结构有关,这与SEM平面图相吻合。实验结果表明,Au/SiO2纳米复合薄膜的表面形貌、微观结构和发光特性与退火温度及退火时间有很强的依赖关系。     

磁控溅射工艺参数对Cu薄膜电阻率的影响

在确定Cu薄膜临界尺寸的基础上,选定基底温度、靶基距、溅射功率和工作气压为影响因素设计正交试验,研究了磁控溅射制备工艺对Cu薄膜电阻率的影响。研究结果表明:基底温度是影响薄膜电阻率的最主要因素,电阻率随着基底温度的升高而减小;在工艺条件为基底温度200℃、靶基距45 mm、溅射功率100 W、工作气压0.5 Pa时,所制薄膜的电阻率将会达到最小。最后,结合薄膜微观形貌对试验结论进行了分析,并对最佳工艺条件进行了实验验证。     

直流磁控溅射工艺参数对β-FeSi_2薄膜性能的影响

采用室温直流磁控溅射Fe-Si组合靶的方法,经过后续Ar气氛围退火,在单晶Si(111)衬底上生长β-FeSi2薄膜。研究了溅射功率、工作气压、Ar气流量、沉积时间等工艺参数对β-FeSi2薄膜结构特性及电学特性的影响,通过Raman、Hall、X射线衍射(XRD)等测试对其性能进行表征,对工艺参数进行了优化,在溅射功率为80W、工作气压为1.3Pa和Ar气流量为35SCCM时溅射沉积Fe-Si薄膜,不仅可以得到单一相的β-FeSi2,而且薄膜结晶质量较好。最终,在上述实验条件下制备得到的未掺杂的β-FeSi2薄膜是n型导电的,β-FeSi2薄膜中载流子浓度约为3.3×1016cm-3,迁移率为381cm2/Vs。     

射频溅射功率对非晶Zn-Sn-O薄膜性能的影响

使用射频磁控溅射法,基于不同溅射功率(58、79、116、148和171W)条件在玻璃基底上室温制备了Zn-Sn-O(ZTO)薄膜,并探讨了溅射功率对薄膜的结构、电学性能和光学性能的影响。结果表明,提高溅射功率有助于提升薄膜的沉积速率;XRD分析表明不同溅射功率条件下制备的ZTO薄膜均具备稳定的非晶结构;随着溅射功率的增加,薄膜的电阻率下降,光学吸收边“红移”(光学禁带宽度从3.77eV减小到3.62eV);整体来看,在58~148W溅射功率范围内制备的ZTO薄膜具备较好的可见光透明性,其在380~780nm可见光范围内的平均透过率均超过85%。     

反应溅射法沉积氧化铈过渡层研究

采用直流磁控反应溅射法在双轴织构的镍钨合金(Ni-5%W)基带上生长CeO2过渡层。研究了沉积温度、退火时间、水分压等工艺参数对CeO2薄膜取向的影响,并获得了生长高度双轴织构薄膜的优化工艺条件。X射线面内(Φ)扫描揭示了“[100]CeO2∥[110]Ni-W”的单一外延取向关系,原子力显微镜观察到薄膜在退火处理后表面更加平整、致密。