Cr13型马氏体不锈钢方坯连铸保护渣的开发

针对特钢厂4机4流连铸机生产的2Cr13、3Cr13、4Cr13铸坯表面凹陷、纵裂缺陷进行分析和研究,通过工艺措施解决了Cr13型马氏体不锈钢铸坯的表面凹陷和纵裂问题。采用预熔型保护渣,其中SiO₂和CaO均为28%～31%、Al₂O₃为6%～9%、Na₂O为7%～10%、F-为3%～6%,以及综合配碳,尤其是增加炭黑的加入量,总C含量为15%～18%。保护渣碱度控制在1.0左右,熔化温度为1130～1150℃,1300℃时黏度为0.40～0.55 Pa·s;保护渣转折温度为1140～1180℃,结晶率约为48.8%。控制中间包内2Cr13钢液过热度≤30℃,3Cr13和4Cr13钢液过热度≤35℃;连铸过程中采用自动加渣方式,控制适宜的渣层厚度并保持液面稳定。     

大方坯连铸结晶器保护渣的研制

对进口结晶保护渣进行具体分析,研制出两种大方坯结晶器保护渣,工业试验结果表明：研制的渣能够替代进口产品,满足大方坯连铸生产工艺的要求。     

结晶器保护渣对连铸坯增碳的影响

本文研究了超低碳钢水通过连铸结晶器,铸坯含碳量增加的现象。讨论了含碳保护渣对超低碳钢铸坯增碳的影响,降低保护渣中碳含量,有利于减少铸坯增碳。     

不同保护渣在连铸大小方坯上的应用

不同保护渣在连铸大小方坯上的应用［德］ＨｏｒｓｔＡｂｒａｔｉｓ等１前言在连铸结晶器内使用的保护渣应满足多方面的要求，也就是借助形成液渣来润滑铸坯使其滑动地通过结晶器，恰如其分地控制和均匀结晶器内的传热，吸收来自钢液中产生的非金属夹杂以及避免钢液面较大...     

CP—6圆坯连铸结晶器保护渣的研制

进行ＣＰ－６圆坯连铸结晶器保护渣的研制，填补了国内空白，达到国际先进水平，取得显著的经济效益和社会效益。     

不锈钢1Cr17板坯连铸过程中保护渣液渣层及渣膜的研究

在板坯连铸过程中取不锈钢1Cr17保护渣的液渣和渣膜试样,研究液渣成分和性能的变化,以及渣膜的性质。保护渣的主要成分（％）为：35．46Ca0、32．84SiO2、7．87Al2O3、3．04MnO、8,48Na2O、7．13F、2．6C。结果表明,开浇后液渣中Al2O3、Cr2O3含量有一定增加,碱度稍有降低,但10min后趋于稳定;液渣熔化温度和粘度相对于原始渣均有不同程度增加,凝固温度变化较小;保护渣变化后的熔化温度仍处于合理范围内,粘度值最多增加了0．08Pa·s;保护渣渣膜由结晶层和玻璃层组成,渣膜结晶率约为71％,结晶矿相主要是枪晶石和少量霞石。     

结晶器保护渣对超低碳钢连铸坯表面渗碳的影响

通过超低碳钢渗碳的理论解析和实验测定，研究连铸保护渣对超低碳钢铸坯表面渗碳的影响。在稳态浇注条件下，超低碳钢铸坯表面渗碳量和渗碳深度很小；在非稳态浇注时期，超低碳钢铸坯表面渗碳量和渗碳深度很大。保护渣中含石墨的连铸坯表面渗碳量和渗碳深度最大，碳黑次之，活性炭最小。     

小方坯不锈钢用保护渣的研制

简述了结晶器保护渣在连铸过程中的重要作用和2Cr13在连铸过程产生表面凹陷的机理。使用物化性能适宜的保护渣可以改善初始坯壳的传热与润滑,控制铸坯表面凹陷的产生。在实验室研究的基础上,研制出了适合于断面为150mm×150mm、拉速为1.0~1.5m/min的2Cr13不锈钢连铸结晶器颗粒保护渣。试验证明2号保护渣性能良好,2Cr13连铸坯因表面凹陷产生的返修率由20%下降到5%。     

1Cr13不锈钢连铸坯与模铸坯轧材内部质量差异探讨

简述了我公司生产1Cr13不锈钢轧材情况,对比1Cr13不锈钢连铸坯与模铸坯轧材的内部质量差异,重点围绕轧材内部质量差异较大的炉号作了分析对比,对造成差异的原因进行探讨,发现1Cr13不锈钢连铸坯轧材内部质量问题主要原因是由连铸坯的缺陷、轧制过程中较小的压缩比和1Cr13不锈钢的化学成分造成的,对此提出改进意见。     

马氏体不锈钢板坯连铸保护渣研制与应用

 由于钢种特点,连铸马氏体不锈钢板坯容易产生裂纹缺陷,影响生产节奏和修磨效率;同时,由于采用通用型保护渣,也无法针对马氏体不锈钢板坯质量问题做出进一步改进。因此,尝试马氏体不锈钢板坯连铸保护渣的国产化研制和使用,通过保护渣碱度、CaF等的不同范围与保护渣结晶、黏度性能的关系研究,确定采用高碱度、低黏度、高结晶性的保护渣设计原则,并由此得出了适应马氏体不锈钢板坯连铸的保护渣设计方案。实际使用过程中,板坯纵裂率下降幅度达到30%,证明了马氏体不锈钢连铸板坯保护渣设计和研制的合理性和可行性。     

Crystallization Extent and Phase Constitution of Slag Films Taken from Continuous Casting Moulds for Stainless Steels

Slag film samples were taken from the mould wall after casting of stainless steel slabs of grade 304, 321, 409L and 430, which represent austenitic, ferritic and titanium stabilized stainless steels. The chemical compositions of the samples were analysed and their phases were identified using a combination of scanning electron microscope (SEM), energy dispersive X‐ray analysis (EDX) and X‐ray diffraction (XRD). Finally the crystallization ratio was determined by SEM. The results show that the chemical compositions of the films during casting differ from the original designed flux composition. Concerning the heat transfer in the mould, the film taken during casting of steel grade 304 showed the highest insulation ability whereas the film taken during casting of steel grade 409L had the lowest insulation ability. The films taken during casting of steel grades 321 and 430 showed average heat insulation abilities. The solidification conditions in the mould during casting of steel grades 304, 321, and 409L matched the solidification requirements of the corresponding steel grades. However, the basicity of the powder for steel grade 430 should be decreased a little in order to improve the lubrication function and counteract sticking tendencies. Perovskite crystals, which usually precipitate at relatively high temperature, were found in the film taken during casting of steel grade 321. This is harmful in view of the safety of the casting process and the surface quality of the slab.     

2Cr13不锈钢铸坯表面质量的控制研究

2Cr13不锈钢属于包晶钢,其物理特性使得其连铸过程中存在表面凹陷及纵裂纹等质量问题。从该钢种凝固特点、钢的线性膨胀系数以及高温力学性能等方面分析了2Cr13不锈钢铸坯表面凹陷及微裂纹产生的原理并提出了相应的工艺措施,运用于生产实践,降低了2Cr13马氏体不锈连铸坯表面凹陷及裂纹率,保证了产品的表面质量。     

不锈钢的连铸技术

本文介绍了不锈钢连铸的一些工艺技术上的主要难点、特点，概述了不锈钢连铸发展的历史及未来发展趋势     

1Cr13不锈钢的土壤腐蚀行为

通过在酸性、中性及碱性土壤中埋设试件的方法,研究了１Ｃｒ１３不锈钢分别经过１年、３年、５年这三种试验周期后的腐蚀行为为特征。结果表明,１ｃｒ１３不锈钢在酸性及中性土壤中腐蚀轻微,在高盐碱必训腐蚀严重,而且以点蚀为主,土壤中Ｃｌ＾－及ＳＯ４＾２－是影响１Ｃｒ１３不锈钢腐蚀行为的最主要因素,随土壤中Ｃｌ＾－及ＳＯ４＾２－增多,１Ｃｒ１３不锈钢的腐蚀失重近似线性增大。     

Thermal Response of Mould in High Speed Casting of Stainless Steel Billet

Ｉｎｖｉｅｗｏｆｈｅａｔｔｒａｎｓｆｅｒ ,ｔｈｅｒｏｌｅｏｆｍｏｕｌｄｉｎｃｏｎｔｉｎｕｏｕｓｃａｓｔｉｎｇｃａｎｎｅｖｅｒｂｅｏｖｅｒｓｔａｔｅｄａｓｉｔｃｏｎ ｔｒｏｌｓｂｏｔｈｔｈｅｂｉｌｌｅｔｑｕａｌｉｔｙａｎｄ ｐｒｏｄｕｃｔｉｖｉｔｙｏｆａｃａｓｔｅｒｔｏａｇｒｅａｔｅｘｔｅｎｔ .Ｉｎｔｈｉｓｓｔｕｄｙ ,ＡｔｌａｓＳｔｅｅｌｗａｓｃｈｏｓｅｎａｓｔｈｅｌｏｃａｔｉｏｎｆｏｒａｐｌａｎｔｔｒｉａｌｂｅｃａｕｓｅｖｅｒｙｌｉｔｔｌｅｄａｔａａｒｅａｖａｉｌａｂｌｅｏｎｈｅａｔｔｒａｎｓｆｅ…     

0Crl3Mn不锈钢热处理工艺研究

通过不同退火时间对0Cr13Mn机擒性能的影响。不同淬火温度对0Cr13Mn组织、性能影响的实验．确立了0Cr13Mn不锈钢的合理热处理参数。     

方坯连铸连续锥度结晶器的设计与选择

设计了两种方坯连铸连续锥度结晶器，并对其结果进行了推广与讨论，分析了连续锥度结晶器选择的技术原则。     

0Cr13不锈钢连铸板坯表面横裂影响因素分析

就0Cr13不锈钢连铸板坯表面横裂形成的原因进行了分析,提出了相应的工艺控制措施,从而杜绝了横裂的产生。