LiNi0.55Co0.15Mn0.30O2正极材料的合成及电化学性能研究

采用共沉淀法合成类球形氢氧化镍钴锰前驱体,经混料机与碳酸锂均匀混合,在氧化气氛下经过高温焙烧得到LiNi0.55Co0.15Mn_0.30O₂化学组分的三元正极材料.通过设计合理的配锂量、保温时间、气氛条件,并对烧制温度设计试验进行考察研究,最终优选出较优的工艺条件.      

Na、Zr复合改性提高LiNi0.8Co0.1Mn0.1O2正极材料理化性能

基于LiNi_0.8Co_0.1Mn_0.1O₂正极材料在高电压下的电化学性能不佳问题,通过简单的共沉淀法得到前驱体Ni_0.8Co_0.1Mn_0.1（OH）₂,与适当的Na源、Zr源及Li源球磨后得到改性材料。通过对比Na和Zr单掺杂或共改性来探究改性材料电化学性能的变化。XRD结果表明,掺杂Na和Zr后,所有改性材料的Li间距和过渡金属层间距均扩大,电化学性能测试发现改性后的材料其循环、倍率性能等均得到明显提升。其中Na、Zr共改性的LiNi_0.8Co_0.1Mn_0.1O₂（NCM-Na-Zr）,其循环和倍率性能得到显著改善,在2.75~4.35 V、1C倍率下循环200次后,仍然有177.4 mAh/g放电比容量和87.7%的容量保持率。      

钒掺杂对LiNi1/3Co1/3Mn1/3O2正极材料电化学性能的影响

LiNi_1/3Co_1/3Mn_1/3O₂ (LNCM)因其高比容量等优点在动力电池领域受到广泛关注。然而,较差的循环性能和严重的安全问题限制了其应用前景。离子掺杂是提高材料电化学性能的有效方法之一。采用溶胶凝胶法,以NH₄VO₃为钒源,成功制备了钒掺杂LiNi_1/3-xCo_1/3Mn_1/3V_xO₂正极材料。结果表明:LiNi_1/3-0.02Co_1/3Mn_1/3V_0.02O₂ (LNCMV)电极材料表现出优秀的储锂性能(0.5 C时,80次循环后,放电比容量为169 mAh/g)。通过V⁵⁺替代LiNi_1/3Co_1/3Mn_1/3O₂正极...     

锂离子正极材料LiNi0.5Mn0.3Co0.2O2的合成与掺杂Al的性能研究

采用共沉淀法合成镍钴锰氢氧化物前躯体,使其和碳酸锂混合均匀后,高温焙烧合成锂离子正极材料LiNi_0.5Mn_0.3Co_0.2O₂,研究了掺杂Al（OH）₃对材料循环性能的影响.用X射线衍射和扫描电镜对合成的粉末进行了表征,用电性能测试仪研究了材料的电化学性能.研究发现:温度为850 ℃时焙烧的材料具有最优的电性能,1C电流初始放电比容量达到157.2 mAh/g（2.75~4.2V）,循环50次放电比容量保持率为94.8 %,循环100次材料的放电比容量保持率为90.1 %.通过少量掺杂Al（OH）₃的电池材料结晶性有所提高,晶型趋于完整,但是材料的放电比容量有所降低,前100次循环掺杂对材料循环稳定性无显著改善效果.      

锂离子电池正极材料LiNi1/3Co1/3Mn1/3O2研究进展

介绍了比容量高、循环性能优异、成本较低的LiNil/3Co1/3Mnl/3O2正极材料近年来在合成技术及其掺杂改性、表面修饰等方面所取得的成果和进展,并对其未来的发展趋势进行了展望。     

LiNi1/3Co1/3Mn1/3O2正极材料的合成与性能

采用共沉淀-高温固相法制备LiNi_1/3Mn_1/3Co_1/3O₂正极材料,利用XRD和SEM对所制试样的晶体结构和形貌进行表征,研究了烧结温度对材料电化学性能的影响.结果表明,焙烧温度为850 ℃制备的材料具有较好电化学性能,在25 ℃,电压范围为2.75~4.2 V,1 C充电6 C放电下首次放电比容量为124.2 mAh/g,50次循环后容量保持率为95.2 %.      

铌掺杂对镍基正极材料LiNi0.8Co0.1Mn0.1O2电化学性能影响

解决镍基正极材料LiNi_0.8Co_0.1Mn_0.1O₂的电化学循环稳定性和高温循环性能是其产业化推广应用的关键。研究了掺杂铌改性高镍正极材料,优化材料的电化学性能,提升循环稳定性。首先以硫酸盐为原料,在N₂保护气氛下,采用共沉淀法合成三元球形Ni_0.8Co_0.1Mn_0.1（OH）₂前驱体,通过高温固相反应与LiOH·H₂O,Nb₂O₅合成Li（Ni_0.8Co_0.1Mn_0.1）_1-xNb_xO₂（x=0,0.01,0.02,0.03）系列正极材料。X射线衍射结果表明,Nb5+离子可少量进入正极材料晶格,并在正极材料表面形成化学稳定性好的Li₃NbO₄。当x=0.02时,在室温25 ℃,电压2.75~4.2 V,0.2 C倍率下首次放电比容量为172.9 mAh/g,100次循环后容量保持率为97.47%,在50 ℃,0.5 C倍率下循环20次容量基本不变,平均放电比容量为183.7 mAh/g,且该样品具有较好的倍率性能。      

合成方法对富锂锰基正极材料Li1.2Mn0.54Ni0.13Co0.13O2电化学性能的影响

采用共沉淀法、溶胶凝胶法和固相法合成了富锂锰基正极材料Li_1.2Mn_0.54Ni_0.13Co_0.13O₂,并通过XRD、SEM、EDS等对所合成材料的物相结构和微观组织等进行了表征,采用电池测试系统对由合成材料组装的CR2032纽扣式半电池进行电化学性能测试。研究表明,三种合成方法都成功合成了具有层状结构的富锂锰基正极材料,其中共沉淀法制备的样品阳离子混排程度最低,元素分布和颗粒大小均匀,晶界边缘清晰,并且无明显团聚。从电化学性能来看,在2.0～4.8 V的电压范围内,0.1 C倍率下共沉淀法合成样品的首圈放电比容量最高,在充放电循环100圈后,仍保持195.8 mA·h/g的放电比容量,容量保持率为87.3%。相较而言,溶胶凝胶法和固相法制备的样品容量保持率较低,分别为84.5%和83.8%。与溶胶凝胶法和固相法制备样品相比,共沉淀法可有效提高Li_1.2Mn_0.54Ni_0.13Co_0.13...     

正极材料LiFePO4的电化学性能的改进

采用固相反应法合成了LiFePO₄正极材料。在20mA/g的电流密度下进行恒电流充放电,比容量可以达到135mAh/g。为了改进LiFePO₄的性能,提高其高倍率性能,尝试了两种途径并合成出Li(Fe_0.8Mn_0.2)PO₄和LiFePO₄/C。低倍率充放电实验得出的两个样品的比容量分别可达到145mAh/g和144mAh/g,而且表现出了良好的循环性能和平坦的电压平台。以上两种方法制备出的材料均具有较好的高倍率性能。

     

Cu掺杂LiNi0.6Co0.2Mn0.2O2的电化学性能

采用共沉淀法制备前驱体,高温固相合成正极材料Li（Ni_0.6Co_0.2Mn_0.2）_1-xCu_xO₂（x=0、0.01、0.015和0.02）,通过X射线衍射、SEM和电池测试系统及电化学工作站测试,对其结构、形貌和电化学性能进行表征.结果表明,掺杂少量的Cu, 样品均具有α-NaFeO₂型结构,没有出现杂相; 样品（108）/（110）峰分裂明显,材料有着良好的层状结构;随着Cu掺杂量的增加,c和c/a增大,层间距增大,Li+脱嵌通道增大,改善导电性.Cu掺杂1 %和1.5 %的I_（003）/I_（104）比值分别为1.467、1.438,比0 %的1.431值大,减小了阳离子混排.首次放电比容量依次为170.6 mAh/g、164.1 mAh/g、163.6 mAh/g和162.4 mAh/g,当x为0,1 %,2 %经过100次循环,保持率为87.1 %、98.7 %、和87.7 %;x为1.5 %,比容量从161.8 mAh/g增加到173.9 mAh/g,性能较优.      

Synthesis and electrochemical properties of Ce-doped LiNi_（1/3）Mn_（1/3）Co_（1/3）O_2 cathode material for Li-ion batteries

The layered material of Ce-doped LiNi1/3Mn1/3Co1/3O2 with α-NaFeO2 was synthesized by a co-precipitation method. X-ray diffraction (XRD) showed that Ce-doped LiNi1/3Mn1/3Co1/3O2 had the same layered structure as the undoped LiNi1/3Mn1/3Co1/3O2. The scanning electron microscopy (SEM) images exhibited that the particle size of Ce-doped LiNi1/3Mn1/3Co1/3O2 was smaller than that of the undoped LiNi1/3Mn1/3Co1/3O2. The Ce-doped LiNi1/3Mn1/3Co1/3O2 samples were investigated on the Li extraction/insertion performances through charge/discharge, cyclic voltammogram (CV), and electrochemical impedance spectra (EIS). The optimal doping content of Ce was x=0.02 in the LiNi1/3-xMn1/3Co1/3CexO2 samples to achieve high discharge capacity and good cyclic stability. The electrode reaction reversibility was enhanced, and the charge transfer resistance was decreased through Ce-doping. The improved electrochemical performances of the Ce-doped LiNi1/3Mn1/3Co1/3O2 cathode materials were attributed to the addition of Ce4+ ion by stabilizing the layer structure.     

正极材料Li[Ni1/3Li1/9Mn5/9]O2的结构和充放电过程研究

应用X射线衍射,选区电子衍射和同步X射线衍射等方法,对锂离子电池正极材料Li[Ni_1/3Li_1/9Mn_5/9]O₂的结构和充放电行为进行了研究.结果表明Li[Ni_1/3Li_1/9Mn_5/9]O₂可标定为单相α-NaFeO₂,并具有$\\sqrt 3 $a_hex.×$\\sqrt 3 $a_hex.×$\\sqrt 3 $c_hex.超结构特征.电池充电时,伴随锂离子的脱出,相邻氧原子层间的静电斥力逐渐增大,当电压为3.8V时应力达到最大.接近4.6V时,晶胞常数c急剧下降,绝大多数Li⁺从材料的锂层拔出,Ni²⁺发生氧化.4.6~4.8V之间c增大,a变化很小,说明过渡金属层中的Li⁺拔出,而过渡金属离子的氧化状态未改变.     

单晶LiNi0.83Co0.1Mn0.07O2正极材料的合成及电化学性能

采用共沉淀-高温固相法合成单晶LiNi_0.83Co_0.1Mn_0.07O₂正极材料。采用XRD,SEM和恒流充放电等测试手段对材料的晶体结构、形貌和电化学性能等进行研究。测试结果表明,材料形成形貌良好的单晶颗粒,Li+/Ni2+离子混排程度较低,材料具有良好的a-NaFeO₂层状结构。在2.75~4.3 V下,扣式电池0.1 C首次放电比容量达209.63 mAh/g,库仑效率为91.19%,0.2 C循环100次后容量保持率为100.09%。      

LiNi0.5Co0.2Mn0.3O2正极材料的高电压研究

使用LiNi_0.5Co_0.2Mn_0.3O₂正极材料制作出软包电池,在不同电压上限（4.2 V、4.25 V、4.3 V、4.35 V）下进行电化学测试,再采用X射线衍射（XRD）和扫描电镜（SEM）, 对循环100次后的极片进行结构和形貌表征. XRD图谱表明,循环100次后的材料仍具有α-NaFeO₂型结构,并且仍是层状结构,但电压上限为4.35 V时材料I₀₀₃/I₁₀₄值小于1.2,出现了较高的阳离子混乱.在4.2 V、4.25 V、4.3 V和4.35 V的电压上限下,电池的首次放电容量依次为161.5 mAh/g、162.9 mAh/g、169.2 mAh/g和176.6 mAh/g.相较于4.2 V,电压上限为4.25 V、4.3 V和4.35 V时, 容量提高率依次为0.87%、4.77%和9.35%.电压上限为4.2 V、4.25 V、4.3 V和4.35 V的电池200次循环（0.2 C）测试后,容量保持率依次为95.09%、94.41%、95.52%、95.56%.虽然电压上限为4.35 V时材料出现阳离子无序,但其电化学性能却是最好的,可能是由于Co离子高价迁移到Li层时注入过量电荷,使通过大的二次粒子内部晶界网络时具有高电子传导性.      

富锂材料Li[Li0.2Mn0.54Co0.13Ni0.13]O2的ZrO2包覆及电化学性能

近几年,锂离子电池富锂材料xLi₂MnO₃·(1-x) LiMO₂(M=Ni、Co、Mn等) 由于其高放电比容量、高电压、低廉的价格受到人们越来越多的关注.但是,富锂材料循环性能差、倍率性能低、首圈充放电效率低和电压降等问题是阻止富锂材料商业化的几个主要原因。采用液相法合成富锂材料Li[Li_0.2Mn_0.54Co_0.13Ni_0.13]O₂,通过表面包覆一层ZrO₂, 放电倍率1 C下循环100圈之后,2% ZrO₂包覆量的富锂材料的放电比容量比未包覆的放电比容量多53.8 mAh/g,大大提高富锂材料的循环性能.      

熔盐法合成LiMn1/3Ni1/3Co1/3O2及AA电池的电化学性能

以KCl为熔盐,采用熔盐法合成了锂离子电池正极材料LiMn1/3Ni1/3Co1/3O2,扫描电子显微镜(SEM)显示此方法制备产物具有较好的晶形,颗粒较均匀.XRD表征结果显示产物为层状结构,充放电测试结果显示出材料在3.6 V平台附近有较大的可逆容量.在900℃时保温8 h时合成的LiMn1/3Ni1/3Co1/3...     

钠源对正极材料Na3V2（PO4）3性能的影响

采用溶胶凝胶-高温固相法,用不同的钠源制备NASICON结构钠离子电池正极材料Na₃V₂（PO₄）₃.借助扫描电子显微镜（SEM）,X射线衍射分析（XRD）,电池测试系统及电化学工作站对制备的Na₃V₂（PO₄）₃结构,形貌,电性能和内阻进行表征.研究结果表明,以Na₂CO₃为钠源合成Na₃V₂（PO₄）₃有更好的颗粒尺寸,形貌结构完整,充放电性能及循环稳定性更好,阻抗也较小;在2.5~4.0 V电压范围内,以0.2 C进行充放电,首次放电比容量达到110.8 mAh/g,50次循环后容量保持率为85.1 %.