TiO2 nanofibers doped with rare earth elements and their photocatalytic activity

In the present study rare earth doped (Ln³⁺–TiO₂, Ln = La, Ce and Nd) TiO₂ nanofibers were prepared by the sol–gel electrospinning method and characterized by XRD, SEM, EDX, TEM, and UV-DRS. The photocatalytic activity of the samples was evaluated by Rhodamine 6G (R6G) dye degradation under UV light irradiation. XRD analysis showed that all the synthesized pure and doped titania nanofibers contain pure anatase phase at 500 °C but at 700 °C it shows both anatase and rutile phase. XRD result also shows that Ln³⁺-doped titania probably inhibits the phase transformation. The diameter of nanofibers for all samples ranges from 200 to 700 nm. It was also observed that the presence of rare-earth oxides in the host TiO₂ could decrease the band gap and accelerate the separation of photogenerated electron–hole pairs, which eventually led to higher photocatalytic activity. To sum up, our study demonstrates that Ln³⁺-doped TiO₂ samples exhibit higher photocatalytic activity than pure TiO₂ whereas Nd³⁺-doped TiO₂ catalyst showed the highest photocatalytic activity among the rare earth doped samples.     

Enhanced photocatalytic degradation of rutile/anatase TiO2 heterojunction nanoflowers

Rutile/anatase TiO₂ heterojunction nanoflowers were prepared via a facile one-step hydrothermal approach using titanium tetrachloride and urea as the raw materials, cetyl trimethyl ammonium bromide (CTAB) as the template. The prepared TiO₂ nanoflowers were characterized by XRD, SEM, TEM and BET analyses. The photocatalytic performance of the as-prepared TiO₂ samples for methyl blue degradation under simulated solar light was investigated. TiO₂ heterojunction nanoflowers with mixed rutile/anatase phase (prepared with 3 mmol CTAB) give the highest photocatalytic activity. In addition, TiO₂ nanoflowers show excellent stability after 9 cycles under the same conditions. These results suggested that the mixed phase anatase/rutile TiO₂ heterojunction nanoflowers have great potential for the future photodegradation of real dye waste water.     

HIPed TiO2 dense pellets with improved photocatalytic performance

The effects of heating method and temperature on physical, structural and photocatalytic behaviors of TiO₂ pellets prepared by conventional heating and hot isostatic pressing have been evaluated. The pellets of submicron TiO₂ powders were heated to 600, 650, 700, 750 and 1000 °C using both processing methods in order to compare anatase to rutile phase transformation and densification behaviors. Bulk densities and porosities were calculated using the Archimedes method. XRD analysis were performed to calculate anatase/rutile ratios. Microstructures were characterized using SEM. Photocatalytic experiments have been performed under full spectrum irradiation. Degraded methylene blue samples were periodically monitored through UV–vis spectrophotometer to determine degradation kinetics. Anatase to rutile transformation is slightly faster and densification is better for lower temperatures for conventional heating, however HIPing gives better densification above 750 °C as it also retards rutile transformation. Mixed phase structures and HIPed samples showed the best photocatalytic performance which makes this method advantageous.     

Suspension high velocity oxy-fuel spraying of a rutile TiO2 feedstock: Microstructure,phase evolution and photocatalytic behaviour

Nano-structured TiO₂ coatings were produced by suspension high velocity oxy fuel (SHVOF) thermal spraying using water-based suspensions containing 30 wt% of submicron rutile powders (~180 nm). By changing the flame heat powers from 40 kW to 101 kW, TiO₂ coatings were obtained with distinctive microstructures, phases and photocatalytic behaviour. Spraying with low power (40 kW) resulted in a more porous microstructure with the presence of un-melted nano-particles and a lower content of the anatase phase; meanwhile, high powers (72/101 kW) resulted in denser coatings and rougher surfaces with distinctive humps but not necessarily with a higher content of anatase. Linear sweep voltammetry (LSV) was used to evaluate the photocatalytic performance. Surprisingly, coatings with the lowest anatase content (~20%) using 40 kW showed the best photocatalytic behaviour with the highest photo-conversion efficiency. It was suggested that this was partially owing to the increased specific surface area of the un-melted nano-particles. More importantly, the structural arrangement of the similarly sized TiO₂ nano-crystallites between rutile and antase phases also created catalytic “hot spots” at the rutile−anatase interface and greatly improved the photo-activity.     

Effect of polymer concentration,needle diameter and annealing temperature on TiO2-PVP composite nanofibers synthesized by electrospinning technique

In this study, TiO₂-PVP nanofibers were successfully synthesized on an aluminium collector by using cost-effective electrospinning technique. The nanofibers were prepared at different polymer concentrations, needle diameters and annealing temperatures and properties were studied by various characterizations. The structural properties were studied by X-ray diffraction (XRD) and Raman spectroscopy techniques. Surface morphology and elemental analysis of the samples were investigated by scanning electron microscopy (SEM) attached with energy dispersive spectroscopy (EDS). The optical properties were carried out by UV–Visible absorption spectroscopy (UV–Vis). By varying the polymer concentration and needle diameter, the effect of viscosity and surface tension on the formation of TiO₂-PVP nanofibers was clearly observed by SEM micro images. EDS spectrum shows effective composition of pure TiO₂ nanofibers. XRD peaks observed at temperatures 500 °C, 700 °C and 900 °C confirmed the anatase, mixed and rutile phases of TiO₂ nanofibers respectively. Raman studies also confirmed these phases of TiO₂ nanofibers. The optical band-gap values calculated using Kubelka-Munk function lies in the range of 3.02–3.22 eV.     

Kinetics of anatase transition to rutile TiO2 from titanium dioxide precursor powders synthesized by a sol-gel process

Kinetics of anatase transition to rutile TiO₂ from titanium dioxide precursor powders synthesized by a sol-gel process have been studied using differential thermal analysis (DTA), X-ray diffraction, transmission electron microscopy (TEM), selected area electron diffraction (SAED), nano beam electron diffraction (NBED) and high resolution TEM (HRTEM). The DTA result shows residual organic matter decomposed at 436 K. The transition temperature for amorphous precursor powders converted to anatase TiO₂ occurred at 739 K. Moreover, the full anatase transition to rutile TiO₂ occurred at 1001 K. The activation energy of anatase TiO₂ formation was 128.9 kJ/mol. On the other hand, the activation energy of anatase transition to rutile TiO₂ was 328.4 kJ/mol. Mesoporous structures can be observed in the TEM image.     

Photocatalytic activity of oxide coatings on fired clay substrates

The coating of fired clay substrates with various metal oxides, such as anatase, rutile, zinc oxide and tin oxide was achieved using a simple spraying technique followed by a thermal treatment. The photocatalytic activity of the layer was characterized through measurement of the absorption spectrum, in the range 400–800 nm, of methylene blue deposited on top of the coating. Results show that the presence of anatase enhances the degradation of methylene blue when it is exposed to ultraviolet light. Thermal treatment at 1050 °C transforms anatase crystals into thermodynamically stable rutile. This results in a decrease of the photocatalytic activity, which can be explained by increase of the grain size and by a difference in the crystal structure. Measurements of the photocatalytic activity of ZnO and SnO₂ show that these two oxides also exhibit photocatalytic properties. In particular, ZnO is a promising alternative material to anatase.     

Characteristics and catalytic properties of Co/TiO2 for various rutile:anatase ratios

This present study revealed a dependence of rutile:anatase ratios in titania on the characteristics and catalytic properties of Co/TiO₂ catalysts during CO hydrogenation. In this study, Co/TiO₂ catalysts were prepared using various titania supports consisting of various rutile:anatase ratios of titania. In order to identify the characteristics, all catalyst materials were characterized using XRD, SEM/EDX, TPR, and hydrogen chemisorption. CO hydrogenation (H₂/CO = 10/1) was also performed to determine the overall activity and selectivity. It was found that both activity and selectivity were altered by changing the rutile:anatase ratios in the titania support.     

Inactivation of pathogenic Klebsiella pneumoniae by CuO/TiO2 nanofibers: A multifunctional nanomaterial via one-step electrospinning

The fabrication and characterization of one-dimensional CuO/TiO₂ nanofibers with high photocatalytic and antibacterial activities are presented. The CuO/TiO₂ nanofibers were prepared by electrospinning of colloid composed of titanium isopropoxide, poly(vinylpyrroliodine) (PVP) and copper nanoparticles and calcination at 700 °C in air for 1 h. The antibacterial activity was tested using Klebsiella pneumoniae as model organism by calculation of the minimum inhibitory concentration (MIC). The obtained CuO/TiO₂ nanofibers showed prominent photocatalytic activity under visible light to degrade reactive black5 and reactive orange16 dyes in aqueous solutions and effectively catalyze K. pneumoniae inactivation. The decomposition process of the cell wall and cell membrane was directly observed by TEM analysis after the exposure of the K. pneumoniae to the nanofibers. Interestingly, the introduced photocatalyst can be reused with the same photocatalytic activity. Overall, the combination of CuO and TiO₂ can be synergistic and resulted in CuO/TiO₂ composite nanofibers having superior photocatalytic and antimicrobial potential to impede K. pneumoniae growth which causes bacterium to die ultimately.     

Synergic effect of cation doping and phase composition on the photocatalytic performance of TiO2 under visible light

The synergic effect of cation doping and phase composition for the further improvement of the photocatalytic activity of TiO₂ under visible light is reported for the first time. Fe^3 + and Sn^4 + co-doped TiO₂ with optimized phase composition were synthesized through a simple soft-chemical solution method. The visible-light-driven photocatalytic activity of Fe^3 + and Sn^4 + co-doped TiO₂ was 5 times of that of Evonik P25 TiO₂ using degradation of methylene blue as model reaction. The synthesized photocatalysts were characterized by powder X-ray diffraction, UV–Vis diffuse reflectance spectroscopy, X-ray photoelectron spectroscopy, ¹¹⁹Sn Mössbauer spectroscopy, and X-ray absorption fine structure spectroscopy. It is indicated that Sn^4 + doping can facilitate the phase transition from anatase to rutile. The different ratios of anatase and rutile can be achieved by tuning the amount of Sn^4 + doped into the lattice. Furthermore, the doping of Sn^4 + into TiO₂ lattice can stabilize the phase composition when Fe^3 + is co-doped. In the Fe^3 + and Sn^4 + co-doped TiO₂, Sn^4 + is mainly used to tune and stabilize the phase composition of TiO₂ and Fe^3 + acts as a doping cation to narrow the band gap of TiO₂. Both band gap and phase composition of TiO₂ can be tuned effectively by the simultaneous introduction of Fe^3 + and Sn^4 +. The synergic effect of optimized phase composition (anatase/rutile = 25/75) and narrowed band gap should be the two main reasons for the promoted photocatalytic activity of TiO₂ under visible light.     

One-step preparation of size-defined aggregates of TiO2 nanocrystals with tuning of their phase and composition

One-step route based on the thermal decomposition of the double salt (NH₄)₂TiO(SO₄)₂ (ammonium titanyl sulfate, ATS) is presented to prepare size-defined aggregates of Ti-based nanoparticles with structural hierarchy. The component of Ti-based networks is tunable from anatase/rutile TiO₂, nitrogen-doped TiO₂, TiN_xO_1−x, to TiN depending on the atmospheres and reaction temperatures. The as-prepared Ti-based powders were characterized by X-ray diffraction analysis (XRD), transmission electron microscopy (TEM), UV–vis diffuse reflectance spectra (DRS), and BET surface area techniques. It is found that TiO₂ in the predominant rutile phase could be achieved by the thermal decomposition of ATS in flowing Ar gas. Furthermore, the nitrogen-doped TiO₂, TiN_xO_1−x solid solution and TiN were prepared by the thermal decomposition of ATS in flowing NH₃ gas by varying the temperatures. The network of anatase TiO₂ with a specific surface area up to 64 m² g⁻¹ contains large mesopores with a mean diameter of ca. 15 nm, and the large pore size allows more accessible surface and interface available for the photocatalytic degradation of large-molecule dyes. The photocatalytic activity of the prepared TiO₂ and nitrogen-doped TiO₂ under UV–vis light irradiation is compared to Degussa P-25 using the photocatalytic degradation of methylene blue (MB) as a model reaction. The anatase TiO₂ nanoparticles derived from one-step route show the highly efficient photocatalytic activity for the degradation of MB in comparison with Degussa P-25. The presence of large-sized rutile in the TiO₂ powder decreases the specific surface area and thus the powder exhibits a lower photocatalytic activity.     

Photocatalytic Nb2O5-doped TiO2 nanoparticles for glazed ceramic tiles

TiO₂ nanoparticles are currently used as coating for self-cleaning building products. In order to achieve high self-cleaning efficiency for outdoor applications, it is important that titania is present as anatase phase. Moreover, it is desirable that the particle sizes are in nano-range, so that a large enough surface area is available for enhanced catalytic performance. In this work, TiO₂ nanoparticles doped with 0–5 mol% Nb₂O₅ were synthesized by co-precipitation. Nb₂O₅ postponed the anatase to rutile transformation of TiO₂ by about 200 °C, such that after calcination at 700 °C, no rutile was detected for 5 mol% Nb₂O₅-doped TiO₂, while undoped TiO₂ presented 90 wt% of the rutile phase. A systematic decreasing on crystallite size and increasing on specific surface area of TiO₂ were observed with higher concentration of Nb₂O₅ dopant. Photocatalytic activity of anatase polymorph was measured by the decomposition rate of methylene blue under ultraviolet and daylight illumination and compared to commercial standard catalyst (P25). The results showed enhanced catalysis under UV and visible light for Nb₂O₅-doped TiO₂ as compared to pure TiO₂. In addition, 5 mol% Nb₂O₅-doped TiO₂ presented higher photocatalytic activity than P25 under visible light. The enhanced performance was attributed to surface chemistry change associated with a slight shift in the band gap.     

Solar light photocatalytic hydrogen production from water over Pt and Au/TiO2(anatase/rutile) photocatalysts: Influence of noble metal and porogen promotion

Hydrogen production from water under artificial solar light irradiation was performed over a series of Pt and Au/TiO₂(anatase/rutile) photocatalysts. Different TiO₂ supports with varying anatase/rutile contents were compared, based on either sol–gel synthesis or commercial TiO₂. The influence of template promotion on sol–gel TiO₂ synthesis has been studied using different porogens or templates. Among various factors influencing the hydrogen evolution efficiency, it was pointed out that the following parameters were crucial to enhance H₂ evolution: (i) the nature and content of the metallic co-catalyst, (ii) the surface, crystallographic, and porosity properties of the TiO₂ anatase/rutile support, (iii) the anatase/rutile ratio, (iv) the metal–support interactions, and (v) the relative amount of methanol added as a sacrificial reagent. The influence of these different factors was studied in detail. In optimized conditions, important H₂ production efficiency (120 μmol/min) was obtained over days without deactivation and with very low amounts of methanol.     

Enhanced photocatalytic activity of TiO2-ZnO thin films deposited by dc reactive magnetron sputtering

The effect of deposition conditions on the photocatalytic activity of TiO₂-ZnO thin films was studied. By using a (Ti)₉₀-(Zn)₁₀ alloy target, the samples were deposited at room temperature on glass substrates by dc reactive magnetron sputtering and post-annealed in air at 500 °C. The dependence of the physical properties of the films on the O₂/Ar gas ratio and the deposition working pressure was investigated. XRD patterns showed mainly the formation of the anatase phase of TiO₂. Optical absorption measurements exhibited a blue shift of the band-gap energy with increasing working pressure. XPS spectra indicated the presence of the Ti⁴⁺ and Zn²⁺ oxidation states, which correspond to TiO₂ and ZnO, respectively. The chemical state of Ti was further analyzed by means of the modified Auger parameter, α’, which gave a value of ca. 873 eV. The photocatalytic property of the films was assessed by the degradation of a methylene blue aqueous solution. The maximum photocatalytic performance was observed for the samples deposited at 3.0 mTorr and O₂/Ar gas ratio of 10/90. These results are explained in terms of the structural, optical, and morphological properties of the films.     

Synthesis of phase- and shape-controlled TiO2 nanoparticles via hydrothermal process

The TiO₂ nanoparticles with anatase (5.7–12.7 nm), rutile (5.4–8.8 nm), mixed (4.4–8.6 nm) phase were individually prepared using the hydrothermal method. The structure and shape of the particles could be controlled by careful alterations of the hydrothermal conditions. Herein, the TiO₂ nanoparticles were successfully synthesized by employing Ti-isopropoxide as the titanium source into hydrochloric acid solution at mild conditions. The crystal structures such as anatase, rutile and mixed phase of TiO₂ nanoparticles were determined by means of concentration of hydrochloride. Especially, we observed that the rutile TiO₂ crystallites were grown into one-dimensional nanostructures, especially, nanowires, with increasing reaction time. The mechanism of the crystallization of the nanoparticles and the growth habit of TiO₂-rutile structure were discussed.     

Photocatalytic activity of titanium dioxide coatings: Influence of the firing temperature of the chemical gel

Heterogeneous photocatalysis can be exploited for the decomposition of micro-organisms which have developed on the surfaces of building materials. In this work, the efficiency of titanium dioxide coatings on fired clay products is examined. The sol–gel method is used to synthesize a fine TiO₂ powder with a specific surface area of 180 m² g^?1. Thermal treatment of the chemical gel at 340 °C leads to crystallisation in the anatase phase and with further temperature increase, crystallite growth. For thermal treatments in the range 580–800 °C, there is a progressive transition from anatase to rutile. However, despite a decrease in specific surface area of the powder attributed to aggregation/agglomeration, the coherent domain size deduced from X-ray diffraction measurements remains almost constant at 23 nm. Once the transition is completed, increase of thermal treatment temperature above 800 °C leads to further crystallite growth in the rutile phase. The thermally treated titania powders were then sprayed onto fired clay substrates and the photocatalytic activity was assessed by the aptitude of the coating to degrade methylene blue when exposed to ultraviolet light. These tests revealed that the crystallite size is the important controlling factor for photocatalytic activity rather than the powder specific surface area or the anatase/rutile polymorph ratio.     

Preparation,characterization and photocatalytic activity evaluation of micro- and mesoporous TiO2/spherical activated carbon

The influences of heat-treatment temperature and activation time on the properties of TiO₂ supported on spherical activated carbon (TiO₂/SAC) were investigated. Nano-sized TiO₂ was dispersed on the spherical activated carbon with the size of 10–30 nm. Some anatase phase of TiO₂ was transformed to rutile phase of TiO₂ with an increase of heat-treatment temperature. All of the TiO₂/SAC photocatalysts had microporous structure, with the mesopore volume increasing over an activation time of 6 h. The TiO₂/SAC photocatalysts obtained at activation times of 6 h and 9 h were observed synergistic effects between adsorption and photocatalysis in the removal of humic acid.     

Fabrication of nitrogen-doped TiO2 monolith with well-defined macroporous and bicrystalline framework and its photocatalytic performance under visible light

In this study, hierarchically porous bicrystalline nitrogen-doped titania (N-doped TiO₂) monolithic material was fabricated by a simple two-step approach: (i) preparation of TiO₂ porous monolith by a sol–gel process of titanium alkoxide in a mild condition utilizing a chelating agent and mineral salt and (ii) annealing of TiO₂ porous monolith obtained under a modest flow of ammonia gas at 700 °C for 2 h. The phase composition, crystal structure, morphology, pore structure, and porous properties of the final product were studied by means of X-ray diffraction (XRD), scanning electron microscopy (SEM), mercury porosimetry, and nitrogen physisorption measurement, respectively. The resultant N-doped TiO₂ porous monolith possesses a bicrystalline (anatase and rutile) framework with a well-defined macroporosity. The results from X-ray photoelectron spectroscopy (XPS) confirm the formation of OTiN bonds in the N-doped TiO₂ porous monolith. The photocatalytic activity of N-doped TiO₂ porous monolith was evaluated by the photodegradation of Rhodamine B over the samples under visible light. Nearly 50% of Rhodamine B in aqueous solution was efficiently degraded by N-doped TiO₂ porous monolith with the mixed-phase of anatase and rutile under visible light within 120 min.     

Decomposition of nonionic surfactant on a nitrogen-doped photocatalyst under visible-light irradiation

A visible-light-active N-containing TiO₂ photocatalysts were prepared from crude amorphous titanium dioxide by heating amorphous TiO₂ in gaseous NH₃ atmosphere. The calcination temperatures ranged from 200 to 1000 °C, respectively. UV–vis/DR spectra indicated that the N-doped catalysts prepared at temperatures <400 °C absorbed only UV light (E_g = 3.3 eV), whereas samples prepared at temperatures ≥400 °C absorbed both, UV (E_g = 3.10–3.31 eV) and vis (E_g = 2.54–2.66 eV) light. The chemical structure of the modified photocatalysts was investigated using FT-IR/DRS spectroscopy. All the spectra exhibited bands indicating nitrogen presence in the catalysts structure. The photocatalytic activity of the investigated catalysts was determined on a basis of a decomposition rate of nonionic surfactant (polyoxyethylenenonylphenol ether, Rokafenol N9). The most photoactive catalysts were those calcinated at 300, 500 and 600 °C. For the catalysts heated at temperatures of 500 and 600 °C Rokafenol N9 removal was equal to 61 and 60%, whereas TOC removal amounted to 40 and 35%, respectively. In case of the catalyst calcinated at 300 °C surfactant was degraded by 54% and TOC was removed by 35%. The phase composition of the most active photocatalysts was as follows: (a) catalyst calcinated at 300 °C—49.1% of amorphous TiO₂, 47.4% of anatase and 3.5% of rutile; (b) catalyst calcinated at 500 °C—7.1% of amorphous TiO₂, 89.4% of anatase and 3.5% of rutile; (c) catalyst calcinated at 600 °C—94.2% of anatase and 5.8% of rutile.     

Anatase–rutile transformation of TiO2 sol–gel coatings deposited on different substrates

Titanium dioxide is widely used in a lot of applications. The properties of TiO₂ strongly depend on its phase composition. The transformation temperature between phases is influenced by a lot of factors. One of them is a type of substrate under the TiO₂ film. In presented work, thin films of TiO₂ were deposited by the sol–gel method on silicon, stainless steel (304 L) and Co–Cr–Mo alloy (Vitallium). The process of anatase–rutile phase transformation was investigated by Scanning Electron Microscopy (SEM) and X-Ray Diffraction (XRD) studies of deposited coatings. The results were compared with anatase–rutile transformations temperature of TiO₂ powders obtained by analogous sol–gel process. The temperature of anatase–rutile phase transformation changed in the range of 700–1000 °C and strongly depends on a kind of substrate. It was found that anatase–rutile transformation of TiO₂ coating proceeded at a higher temperature than rutilization of titania powders.