Glass-Forming Ability and Crystallization Tendency Evaluated by the DTA Method in the Na2O–B2O3–Al2O3 System

In order to evaluate the crystallization tendency of glasses, the ratio of the crystallization temperature to the liquidus temperature ( T _c/ T _L) was obtained by DTA measurement for the Na₂O–B₂O₃ and Na₂O–B₂O₃–Al₂O₃ systems. The critical cooling rate for glass formation ( Q *) was also measured. The measurements were performed in the composition range of (100 − x )Na₂O–( x )B₂O₃, ( x = 25–35 and 60–100 mol%), and (100 − y )0.5Na₂O·0.5B₂O₃−( y )Al₂O₃, ( y = 6–34 mol%). The relationship between T _c/ T _L and Q * was discussed. A linear relationship between T _c/ T _L and log Q * for these systems was found. Furthermore, the relationship between T _c/ T _L and Q * was verified by computer simulation based on the crystallization kinetics of glass or supercooled liquid.     

Effect of Sb2O3 on Thermal Properties of Glasses in Bi2O3–B2O3–SiO2 System

Glasses with compositions 50Bi₂O₃– x Sb₂O₃–10B₂O₃–(40– x ) SiO₂ ( x =0, 1, 3, 5, 8, 10) have been prepared by conventional melt quench technique. Substitution of Sb₂O₃ for SiO₂ exerted an obvious effect on properties of glasses, especially, increased glass transition temperature ( T _g) and crystalline temperature ( T _c) greatly. Results of infrared transmission spectra attributed the effect to the formation of new bridging bonds of Sb–O–B and Sb–O–Si in glass network.     

Subsolidus Phase Relationships in the Ga2O3–Al2O3–TiO2 System

Subsolidus phase relationships in the Ga₂O₃–Al₂O₃–TiO₂ system at 1400°C were studied using X-ray diffraction. Phases present in the pseudoternary system include TiO₂ (rutile), Ga_{2−2 x} Al_{2 x} O₃ ( x ≤0.78 β-gallia structure), Al_{2−2 y} Ga_{2 y} O₃ ( y ≤0.12 corundum structure), Ga_{2−2 x} Al_{2 x} TiO₅ (0≤ x ≤1 pseudobrookite structure), and several β-gallia rutile intergrowths that can be expressed as Ga_{4−4 x} Al_{4 x} Ti _{n −4}O_{2 n −2} ( x ≤0.3, 15≤ n ≤33). This study showed no evidence to confirm that aluminum substitution of gallium stabilizes the n =7 β-gallia–rutile intergrowth as has been mentioned in previous work.     

Weakly Coupled Relaxor Behavior of BaTiO3–BiScO3 Ceramics

The structural and dielectric properties of (1− x )BaTiO₃– x BiScO₃ ( x =0–0.5) ceramics were investigated to acquire a better understanding of the binary system, including determination of the symmetry of the phases, the associated dielectric properties, and the differences in the roles of Bi₂O₃ and BiScO₃ substitutions in a BaTiO₃ solid solution. The solubility limit for BiScO₃ into the BaTiO₃ perovskite structure was determined to be about x =0.4. A systematic structural change from the ferroelectric tetragonal phase to a pseudo-cubic one was observed at about x =0.05–0.075 at room temperature. Dielectric measurements revealed a gradual change from proper ferroelectric behavior in pure BaTiO₃ to highly diffusive and dispersive relaxor-like characteristics from 10 to 40 mol% BiScO₃. Several of the compositions showed high relative permittivities with low-temperature coefficients of capacitance over a wide range of temperature. Quantification of the relaxation behavior was obtained through the Vogel–Fulcher model, which yielded an activation energy of 0.2–0.3 eV. The attempt characteristic frequency was 10¹³ Hz and the freezing temperature, T _f, ranged from −177° to −93°C as a function of composition. The high coercive fields, low remanent polarization, and high activation energies suggest that in the BiScO₃–BaTiO₃ solid solutions, the polarization in nanopolar regions is weakly coupled from region to region, limiting the ability to obtain long-range dipole ordering in these relaxors under field-cooled conditions.     

Properties of Sm2O3─Al2O3─SiO2 Glasses for In Vivo Applications

The compositional range for glass formation below 1600°C in the Sm₂O₃─Al₂O₃─SiO₂ system is (9–25)Sm₂O₃─(10–35)Al₂O₃─(40–75)SiO₂ (mol%). Selected properties of the Sm₂O₃─Al₂O₃─SiO₂ (SmAS) glasses were evaluated as a function of composition. The density, refractive index, microhardness, and thermal expansion coefficient increased as the Sm₂O₃ content increased from 9 to 25 mol%, the values exceeding those for fused silica. The dissolution rate in 1 N HCl and in deionized water increased with increasing Sm₂O₃ content and with increasing temperature to 70°C. The transformation temperature ( T _g ) and dilatometric softening temperature ( T _d ) of the SmAS glasses exceeded 800° and 850°C, respectively.     

Modification of MgAl2O4 Microwave Dielectric Ceramics by Zn Substitution

MgAl₂O₄ microwave dielectric ceramics were modified by Zn substitution for Mg, and their dielectric characteristics were evaluated, along with their structures. Dense (Mg_{1− x} Zn _x )Al₂O₄ ceramics were obtained by sintering at 1550°–1650°C in air for 3 h, and the (Mg_{1− x} Zn _x )Al₂O₄ solid solution was determined in the entire composition range. With Zn substitution for Mg, the dielectric constant ɛ of MgAl₂O₄ just varied from 7.90 to 8.56, while the Q × f value had significantly improved up to a maximal value of 106 000 GHz at x =1.0. Moreover, the τ_f of MgAl₂O₄ ceramics had declined from −73 to −63 ppm/°C.     

Structure and Properties of Low Phonon Antimony Glasses in the K2O–B2O3–Sb2O3–ZnO System

The monolithic glass-forming region of the low phonon and low softening point antimony glasses containing high Sb₂O₃ (40–75 mol%) in the novel quaternary K₂O–B₂O₃–Sb₂O₃–ZnO system has been found with the help of X-ray diffraction (XRD) analysis. The structure of a series of glasses with the general composition of (mol%) 15K₂O–15B₂O₃–(70− x )Sb₂O₃– x ZnO (where x =5–25) has been evaluated by infrared reflection spectral (FT-IRRS) analyses. All the glasses are found to possess a low phonon energy of around 600 cm⁻¹, as revealed by FT-IRRS. Their softening point ( T _s), glass transition temperature ( T _g), and coefficient of thermal expansion (CTE) have been found to vary in the ranges of 351°–379°C, 252°–273°C, and 195–218 × 10⁻⁷ K⁻¹, respectively. These properties are found to be controlled by their fundamental property, like the covalent character of the glasses, which is found to increase with an increase in Sb₂O₃ content. In addition, the devitrified glasses have been characterized by XRD and field emission scanning electron microscopy, which manifests the presence of nanozinc antimony oxide crystals with sizes of 21–43 nm. The exhibited properties have revealed that they are a new class of versatile materials.     

Characterization of a Large-Scale Nondoped YBa2Cu3O7−x Superconductor Prepared by Plastic Forming Without High-Pressure Molding

A slurry containing YBa₂Cu₃O_{7− x} particles and a fine YBa₂Cu₃(OH) _x colloid solution was prepared, and a large-scale bulk YBa₂Cu₃O_{7− x} superconductor (about 50 mm × 35 mm × 2 mm) was produced by plastic forming without high-pressure molding. The samples molded from the slurry were dried and then fired at 1223 K in air. X-ray diffraction data indicated that the samples had the characteristic orthorhombic YBa₂Cu₃O_{7− x} structure. Measurements of electrical resistance were carried out between 300 and 50 K by the standard four-probe DC electrical measurement. The samples began superconducting at an onset temperature around 92 K, and the full-transition temperature (critical temperature) ( T _c) was 88.7±1.4 K. The critical current density ( J _c) measured at 77 K was about 440 A/cm², the value of J _c was improved by the heat treatment under an oxygen atmosphere, and J _c=1.6 × 10³ A/cm² was observed. Under the magnetic field (B=1 T), the sample held its superconductivity, and demonstrated that this method can be used to produce the magnetic shielding used in magnetic resonance imaging diagnosis.     

Crystal Chemistry and Phase Equilibrium Studies of the BaO(BaCO3)–½R2O3–CuOx Systems in Air: VI, R = Neodymium

Crystal chemistry and subsolidus phase equilibrium studies of the Ba-Nd-Cu-O system near the CuO and Nd₂O₃ corners have been carried cut at 950°C in air. Two solid-solution series have been identified in the Ba-Nd-Cu-O system. The first series involves the high- T _c superconductor phase, and has the formula Ba_2–xNd_1+xCu₃O_6+z, where × < ≅ 0.7. At the ideal compound stoichiometry of Ba₂NdCu₃O_6+z, the transformation from the high- T _c orthorhombic to tetragonal phase occurs at 550°–575°C in air. This temperature varies as a function of composition, and at x ≅ 0.2 to 0.3 it occurs at 950°C. The second solid solution is the non-superconducting "brown phase" represented by Ba_2+2x-Nd_4–2xCu_2–xO_10–2z 0 ≤ x ≤ 0.1. Preliminary phase diagrams of the BaO–Nd₂O₃ and Nd₂O₃–CuO_x systems are also presented. Standard X-ray diffraction patterns of BaNd₂–CuO₅ and (Nd_1.9Ca_0.1)CuO_4–z are provided.     

Properties of (Y)ZrO2–Al2O3 and (Y)ZrO2–Al2O3–(Ti or Si)C Composites

The effect of Al₂O₃ and (Ti or Si)C additions on various properties of a (Y)TZP (yttria-stabilized tetragonal zirconia polycrystal)–Al₂O₃–(Ti or Si)C ternary composite ceramic were investigated for developing a zirconia-based ceramic stronger than SiC at high temperatures. Adding Al₂O₃ to (Y)TZP improved transverse rupture strength and hardness but decreased fracture toughness. This binary composite ceramic revealed a rapid loss of strength with increasing temperature. Adding TiC to the binary ceramic suppressed the decrease in strength at temperatures above 1573 K. The residual tensile stress induced by the differential thermal expansion between ZrO₂ and TiC therefore must have inhibited the t - → m -ZrO₂ martensitic transformation. It was concluded that a continuous skeleton of TiC prevented grain-boundary sliding between ZrO₂ and Al₂O₃. In contrast, for the ternary material containing β-SiC in place of TiC, the strength decreased substantially with increasing temperature because of incomplete formation of the SiC skeleton.     

Effect of Alkali Metal Oxide Addition on the Sinterability of MgO–B2O3–Al2O3 Glass–Al2O3 Filler Composites

The sintering of a composite of MgO–B₂O₃–Al₂O₃ glass and Al₂O₃ filler is terminated due to the crystallization of Al₄B₂O₉ in the glass. The densification of a composite of MgO–B₂O₃–Al₂O₃ glass and Al₂O₃ filler using pressureless sintering was accomplished by lowering the sintering temperature of the composite. The sintering temperature was lowered by the addition of small amounts of alkali metal oxides to the MgO–B₂O₃–Al₂O₃ glass system. The resultant composite has a four-point bending strength of 280 MPa, a coefficient of thermal expansion (RT—200°C) of 4.4 × 10⁻⁶ K⁻¹, a dielectric constant of 6.0 at 1 MHz, porosity of approximately 1%, and moisture resistance.     

Subsolidus Phase Relations in the Ga2O3-In2O3-SnO2 System

Subsolidus phase relationships in the Ga₂O₃–In₂O₃–SnO₂ system were studied by X-ray diffraction over the temperature range 1250–1400°C. At 1250°C, several phases are stable in the ternary system, including Ga₂O₃( ss ), In₂O₃( ss ), SnO₂, Ga_{3− x} In_{5+ x} Sn₂O₁₆, and several intergrowth phases that can be expressed as Ga_{4−4 x} In_{4 x} Sn _{n −4}O_{2 n −2} where n is an integer. An In₂O₃–SnO₂ phase and Ga₄SnO₈ form at 1375°C but are not stable at 1250°C. GaInO₃ did not form over the temperature range 1000–1400°C.     

Crystalline Phases and YAG Laser-Induced Crystallization in Sm2O3–Bi2O3–B2O3 Glasses

The glass formation region, crystalline phases, second harmonic (SH) generation, and Nd:yttrium aluminum garnet (YAG) laser-induced crystallization in the Sm₂O₃–Bi₂O₃–B₂O₃ system were clarified. The crystalline phases of Bi₄B₂O₉, Bi₃B₅O₁₂, BiBO₃, Sm _x Bi_{1− x} BO₃, and SmB₃O₆ were formed through the usual crystallization in an electric furnace. The crystallized glasses consisting of BiBO₃ and Sm _x Bi_{1− x} BO₃ showed SH generations. The formation of the nonlinear optical BiB₃O₆ phase was not confirmed. The formation (writing) region of crystal lines consisting of Sm _x Bi_{1− x} BO₃ by YAG laser irradiation was determined, in which Sm₂O₃ contents were∼10 mol%. The present study demonstrates that Sm₂O₃–Bi₂O₃–B₂O₃ glasses are promising materials for optical functional applications.     

Synthesis of (Mg,Si)Al2O4 Spinel from Aluminum Dross

The spinel (Mg,Si)Al₂O₄ was synthesized from aluminum dross using an induction synthesis method. X-ray diffraction analyses on products formed at different temperatures provided an understanding of the formation mechanism of the spinel. After removal of soluble components, the induction heating of the dross resulted first in the oxidation of some of the AlN component and the subsequent formation of the spinel by the following reaction: x SiO₂+ (1− x )MgO + [1−( x /3)]Al₂O₃+ (2 x /3)AlN = (Mg_{1− x} ,Si _x )Al₂O₄+ ( x /3)N₂( g ).     

Spectroscopic Properties of Er3+-Doped Na2O–La2O3–Al2O3–SiO2 Glasses

Er³⁺-doped sodium lanthanum aluminosilicate glasses with compositions of (90− x )(0.7SiO₂·0.3Al₂O₃)· x Na₂O·8.2La₂O₃· 0.6Er₂O₃·0.2Yb₂O₃·1Sb₂O₃ (in mol%) ( x = 12, 20, 24, 40, 60 mol%) were prepared and their spectroscopic properties were investigated. Judd–Ofelt analysis was used to calculate spectroscopic properties of all glasses. The Judd–Ofelt intensity parameter Ω _t ( t = 2, 4, 6) decreases with increasing Na₂O. Ω₂ decreases rapidly with increasing Na₂O while Ω₄ and Ω₆ decrease slowly. Both the fluorescent lifetime and the radiative transition rate increase with increasing Na₂O. Fluorescence spectra of the ⁴ I _13/2 to ⁴ I _15/2 transition have been measured and the change with Na₂O content is discussed. It is found that the full width at half-maximum decreases with increasing Na₂O.     

Structure, Thermal Behavior, Chemical Durability, and Optical Properties of the Na2O–Al2O3–TiO2–Nb2O5–P2O5 Glass System

The FTIR, Raman, UV-Vis, ³¹P MAS-NMR, DTA, and refractive index measurements have been combined to investigate a series of glasses with the general formula 20Na₂O–5Al₂O₃− x TiO₂–(45− x )Nb₂O₅–30P₂O₅, 15≤ x ≤45. The glass structure, as well as thermal, optical, and chemical durability properties, were then described as functions of the f _Nb/ f _Ti ratio. An increase of the f _Nb/ f _Ti ratio correlates with a decrease in length of the average phosphate chains linked through Nb–O–P and Ti–O–P bonds, with an increase in the glass stability and with increase in the linear refractive indices at 632.8 nm from 1.79 to 1.89. Furthermore, niobium is more effective than titanium in improving chemical durability.     

Energetics of La2O3–HfO2–SiO2 Glasses

A series of La₂O₃–HfO₂–SiO₂ glasses, approximately along the join 0.73SiO₂–0.27( x HfO₂–(1− x )La₂O₃), 0< x <0.3), was prepared using containerless processing techniques (aerodynamic levitation combined with laser heating in oxygen). The enthalpy of formation and enthalpy of vitrification at 25°C were obtained from drop solution calorimetry of these glasses and appropriate crystalline compounds in a molten lead borate (2PbO–B₂O₃) solvent at 702°C. The enthalpy of formation from crystalline oxides was exothermic and became less exothermic with increasing HfO₂ content. Heat contents were measured by transposed temperature drop calorimetry and depended linearly on the HfO₂ content. Differential scanning calorimetry showed that both the onset glass transition and the onset crystallization temperature of these glasses increased with increasing HfO₂ content. Upon slow cooling in air, the glasses crystallized to a mixture of baddeleyite, cristobalite, lanthanum disilicate, and hafnon.     

Metastable Phase Selection and Partitioning for Zr(1−x)AlxO(2−x/2) Materials Synthesized with Liquid Precursors

Aqueous solutions of zirconium acetate and aluminum nitrate were spray pyrolyzed at 250°C and upquenched to different temperatures to yield metastable solid solutions of composition Zr_{(1− x )}Al_xO_{(2− x /2)}. An amorphous oxide forms first during pyrolysis which subsequently crystallizes as a single phase for x ≤ 0.57 (≤40 mol% Al₂O₃). The crystallization temperature increased with Al₂O₃ content. Electron diffraction, supported by Raman spectroscopy, indicates that the initial phase is tetragonal. At higher temperatures, the initial solid solation partitions to other metastable phases, viz., t -ZrO₂+γ-Al₂O₃, prior to achieving their equilibrium phase assemblage, m -ZrO₂+α-Al₂O₃. Partitioning yields a nanocomposite microstructure with grain sizes of 20–100 nm, compared to the 3 to 5 nm in the initial, single phase. Compositions containing 45 to 50 mol% Al₂O₃ concurrently crystallize and partition. The structure selected during crystallization and the partitioning phenomena are discussed in terms of diffusional constraints during crystallization, which are conceptually similar to those operating during rapid solidification.     

Effects of La on Dielectric and Piezoelectric Properties of Pb1−xLa2x/3(Nb0.95Ti0.0625)2 O6 Ceramics

Ceramics with the chemical compositions of Pb_{1− x} La_{2 x /3}(Nb_0.95Ti_0.0625)₂O₆ (0≤ x ≤0.060) (PLTN) were prepared by the conventional solid-state reaction method. X-ray diffraction analysis indicated that Ti and La doping not only decreased the rhombohedral–tetragonal phase transformation temperature, but also stabilized the orthorhombic phase of PLTN ceramics. All ceramics sintered at 1190°–1250°C had shown the pure orthorhombic ferroelectric phase. La doping suppresses grain growth and inhibits the formation of pores and cracks, resulting in an increase in relative density up to 97%. The amount of La doping to PLTN ceramics obviously affect ceramics' piezoelectric constant ( d ₃₃) and dielectric loss (tanδ). The sample with x =0.015 possesses high Curie temperature ( T _c=560°C), low dielectric loss (tanδ=0.0054), and excellent piezoelectric constant ( d ₃₃=92 pC/N), presenting a high potential to be used in high-temperature applications as piezoelectric transducers.     

Mullite-Type Structures in the Systems Al2O3–Me2O (Me = Na, K) and Al2O3–B2O3

A morphous solids belonging to the systems Al₂O₃–Me₂O (Me = Na, K) and Al₂O₃–B₂O₃ were prepared by nitrate decomposition, introducing boron in the form of boric acid. Crystalline metastable solids with pseudotetragonal symmetry were obtained from thermal treatment at 850° to 900°C for the compositions Al₆Me_xO_{(9+0.5 x )} ( x ≅ 1; Me = Na, K) and Al_{6- x} B _x O₉ (1 x 3). The resultant solids were stable only within a difinite temperature range and transformed, with further treatment increases, into stable equilibrium phases. The structures of the metastable phases were examined by X-ray diffraction and Fourier transform infrared spectroscopy, and both analyses showed a mullite type of framework, inside of which the atomic coordinates were refined in the Pbam (no. 55) space group. The present results indicate that these silica-free mullite structures are stabilized by two different mechanisms: (1) interstitial occupation of bulky cations (Na⁺, K⁺) or (2) substitution of B for Al in some of the tetrahedral positions.