硫化体系对CR／CⅡR共混硫化胶性能的影响

研究了ZnO／S硫化体系、TCY／树脂复合硫化体系、Pb3O4／树脂复合硫化体系对CR／CⅡR共混胶硫化特性、物理机械性能、耐热老化性能、耐油性能的影响。结果表明：采用ZnO／S硫化体系，共混胶的硫化速度较快，转矩较高；采用3种硫化体系的共混胶力学性能相当，而采用TCY／树脂复合硫化体系硫化的共混胶老化后力学性能保持率比ZnO／S／有机促进剂硫化体系高；采用ZnO／S／有机促进剂硫化体系的共混硫化胶耐油性能稍好。     

硫化体系对CR/CIIR共混硫化胶性能的影响

研究了ZnO/S硫化体系、TCY/树脂复合硫化体系、Pb3O4/树脂复合硫化体系对CR/CIIR共混胶硫化特性、物理机械性能、耐热老化性能、耐油性能的影响。结果表明:采用ZnO/S硫化体系,共混胶的硫化速度较快,转矩较高;采用3种硫化体系的共混胶力学性能相当,而采用TCY/树脂复合硫化体系硫化的共混胶老化后力学性能保持率比ZnO/S/有机促进剂硫化体系高;采用ZnO/S/有机促进剂硫化体系的共混硫化胶耐油性能稍好。     

DCP／MgO复合硫化体系的PUR／CR共混物硫化特性

采用硫化特性参数、溶胀指数和DSC谱图等表征了聚氨酯橡胶(PUR)/氯丁橡胶(CR)共混胶的共硫化性能,并研究了PUR/CR的共混比、补强体系与软化体系等对共混胶的硫化特性的影响.结果表明,采用过氧化二异丙苯/氧化镁(DCP/MgO)复合硫化体系,可以使PUR/CR共混胶达到共硫化;增加PUR和炭黑的用量,减少软化剂的用量,则共混胶料的转矩增大;增加PUR用量,可以加快共混胶料的硫化速度,其它因素对硫化速度的影响不明显.当PUR/CR共混比为20/80、DCP 3份、MgO 4份、炭黑N550 30份、软化剂聚异丁烯(PIB)5份时,共混硫化胶有较好的综合性能.     

硫化体系对CM/SBR共混胶性能的影响

研究了6种硫化体系对氯化聚乙烯（CM）/丁苯橡胶（SBR）共混胶力学性能的影响。结果表明,6种硫化体系均能硫化CM/SBR共混胶。其中,复配型硫化剂TCHC的硫化胶综合力学性能最好,过氧化物BI-PB的硫化胶耐热性最好。     

不同硫化体系对SBR/CM共混胶的性能研究

分别以硫磺(S)、硫磺(S)/过氧化二异丙苯(DCP)/助交联剂(TAIC)作为硫化体系,研究了不同共混比对SBR/CM共混胶的硫化特性、力学性能、耐热老化性能和动态力学性能的影响。结果表明:以硫磺/过氧化二异丙苯/助交联剂作为硫化体系下的共混胶,焦烧时间缩短,硫化速度快,交联程度高,弹性大,耐磨性能和耐热老化性能优异;随着CM用量的增加直到10仹,SBR/CM共混胶的交联程度稍微下降,定伸应力、硬度、拉伸永久变形逐渐增大,回弹值、tanδ峰值逐渐减小,DIN磨耗值变化不大,耐热老化性能好。     

硫化体系对CR/EPDM并用胶性能的影响

试验研究几种EPDM硫化体系对CR／EPDM并用胶在不同停放时间后的硫化特性和硫化胶物理性能的影响。结果表明，EPDM硫化体系采用促进剂CZ／EZ／D／硫黄并用体系，在一定停放时间内CR／EPDM并用胶的硫化速率变化不大，硫化胶物理性能与CR硫化胶相近；采用硫化剂BIPB／助交联剂TAIC／硫黄并用体系，CR／EPDM并用胶的硫化速率小，硫化胶的物理性能较差；采用促进剂BZ／M／TMTM／硫黄、促进剂BZ／M／TRA／硫黄或促进剂DM／D／TMTD／硫黄并用体系，胶料停放时间过长会使CR／EPDM并用胶的硫化速率明显减小，且硫化胶的耐热老化性能较差。     

SBR／CR／SEBS共混物形态的研究

加入少量嵌段共聚物ＳＥＢＳ到热力学不相容的共混物ＳＢＲ／ＣＲ中,可以明显降低分散相粒子尺寸,促进体系均匀分散,分散相平均粒子尺寸约为１５μｍ。     

氯丁橡胶/丁苯橡胶共混物的研究

探讨了氯丁橡胶（CR）/丁苯橡胶（SBR）共混胶料的硫化特性,共混硫化胶的力学性能、压缩弹性模量和动态力学性能.研究结果表明：当共混胶料中SBR用量在5～25份范围内时,随着SBR用量增加,共混胶的MH降低,t90时间延长,ML和t10时间变化不大;拉抻强度、300%定伸应力、硬度均随SBR用量的增加而降低;共混硫化胶的压缩弹性模量随SBR用量的增加而降低,当SBR用量为5份后,-40℃时的压缩弹性模量约为纯CR硫化胶的一半;在-20℃以上时,共混硫化胶压缩弹性模量随温度变化曲线较为平稳,斜率较小;DMA结果显示随SBR用量增大,tanδ降低,E′增大,Tg变化不大.     

硫化体系对氯丁橡胶硫化胶性能的影响

研究了金属氧化物（MgO／ZnO）、过氧化物（2,5-二甲基-2,5二叔丁基过氧化己烷,简称双-25）、硫黄、三聚硫氰酸（TCY）4种硫化体系对氯丁橡胶硫化特性、物理机械性能、耐热老化性能和压缩永久变形性能的影响。结果表明：所选4种硫化体系都能较好地硫化氯丁橡胶;双-25和硫黄有较快的硫化速度：TCY和金属氧化物的硫化速度较慢,但二者有很好的抗硫化返原性;硫黄硫化的CR硫化胶拉伸强度较大．但耐热老化性能欠佳;TCY和双-25硫化胶的物理性能能达到金属氧化物的水平．且老化性能较好;金属氧化物有较优的综合力学性能;含TCY的硫化胶有较小高温压缩永久变形。     

CR/SBR/CPE共混物在钢丝编织胶管中的应用研究

研究用CPE部分替代CR／SBR体系中的CR构成CR／SBR／CPE共混物的性能及其在钢丝编织胶管中的应用。结果表明，CR／SBR／CPE的共混比为40／40／20时共混物性能较好，可满足钢丝编织胶管外层胶的要求；采用此混合物生产钢丝编织胶管不需改动工艺和设备，且每千克CR／SBR／CPE共混物成本比CR／SBR低0．4元左右。     

CM/CR共混胶硫化体系的研究

研究了7种硫化体系对氯化聚乙烯橡胶（CM）/氯丁橡胶（CR）共混胶力学性能的影响。结果表明,7种硫化体系均能硫化该共混胶,其中复配型硫化剂（TCHC）的硫化胶拉伸强度最大,亚乙基硫脲（NA-22）的硫化胶力学性能较好,噻二唑酯衍生物（TDD）并用硫化体系的硫化时间最短,三巯基均三嗪（TCY）的共混胶门尼粘度高、加工性能差,过氧化物硫化体系的硫化胶力学性能不佳。平衡溶胀法测试结果显示,交联密度与力学性能有一定相关性。     

双环戊二烯石油树脂对丁苯橡胶性能的影响

用双环戊二烯石油树脂作补强剂,考察了树脂用量对丁苯橡胶加工工艺性能和物理机械性能的影响。结果表明,随着树脂用量的增加,混炼胶门尼粘度值下降,混炼行为变佳;硫化胶拉断伸长率和撕裂强度都随树脂用量的增加而增大;树脂用量为15~20份时,拉伸强度有最大值,炭黑分布效果较好。     

Effect of Some Polymeric Phenolic Antioxidants on the Properties of SBR Vulcanizates

Polymeric antioxidants can be useful in the protection of styrene-butadiene rubber (SBR) against thermal oxidative aging as an alternative to the low molecular weight ones, which migrate out of the rubber articles. Three polymeric compounds were prepared and incorporated into SBR mixes to be evaluated as antioxidants in comparison with the commercial antioxidant, N-isopropyl-N′-phenyl-p-phenylenediamine (IPPD). The rheometric characteristics of the produced SBR mixes were measured and the cure time was determined. The mechanical, swelling, extraction, and compression properties were studied. The results obtained revealed that poly(4-mercaptophenyl)acrylamide has superior effect in the protection of SBR articles against thermal oxidative ageing.     

Improvement of Homogeneity of SBR/CR Rubber Blends with SBR-g-AA Grafted Rubber

The graft copolymerization of acrylic acid (AA) onto styrene butadiene rubber (SBR) was carried out in toluene at 80°C using benzoyl peroxide (BPO) as initiator. The synthesized styrene butadiene rubber-g-acrylic acid (SBR-g-AA) was characterized with Raman IR spectroscopy. A study was conducted on the use of SBR-g-AA for improving the homogeneity of styrene butadiene rubber/chloroprene rubber (SBR/CR) blend. The SBR-g-AA was incorporated into SBR/CR blend with different blend ratios. The homogeneity of such blends was examined with scanning electron microscopy (SEM), differential scanning calorimetry (DSC), and determination of the dielectric properties. The scanning electron micrographs illustrate improvement of the morphology of SBR/CR rubber blend as a result of the incorporation of SBR-g-AA onto that blend. Also, the dielectric constant (permittivity) and the dielectric loss plots versus the SBR/CR blend ratio show straight lines upon incorporation SBR-g-AA, indicating and confirming the homogeneity of that blend. Physico-mechanical properties of the blend vulcanizates, in presence and absence of SBR-g-AA, were determined, and their thermal stability was evaluated after accelerated thermal aging. The results reveal that SBR/CR (25/75) blend possesses the best thermal stability. Swelling behavior in toluene, in motor oil, and in brake fluid of the blend vulcanizates was also assessed.     

SBS对BR／CR共混物形态结构的影响

用光学显微镜研究了少量添加三元嵌段共聚物ＳＢＳ对热力学不相容的共混物ＢＲ／ＣＲ相态结构的影响。结果表明加入１份ＳＢＳ即可明显降低分散相粒子尺寸，减少体系分散性；达到１０份时这种效果已不明显。对共聚物的ＣＭＣ进行了确定，并将实验结果与Ｎｏｏｌａｎｄｉ的理论进行了比较。     

NR/EPDM/CR共混物制作高强度胶管配方研制

研究了天然橡胶、三元乙丙胶与氯丁橡胶并用胶的配方和混炼方法.试验结果表明,这三种胶共混,可以采用硫磺和金属氧化物硫化体系.共混物采取NR和EPDM先行配合混炼,在高温下过滤,再与预先加入硫化剂的CR胶按比例掺混、热炼挤出的工艺方法.胶料的硫化速度较快,强度较高,耐臭氧性能和耐介质性能较好;老化性能优良,耐油性能略有下降.