The effect of residual stresses arising from laser shock peening on fatigue crack growth

Residual stresses have in the past been introduced to manipulate growth rates and shapes of cracks under cyclic loads. Previously, the effectiveness of shot peening in retarding the rate of fatigue crack growth was experimentally studied. It was shown that the compressive residual stresses arising from the shot peening process can affect the rate of crack growth. Laser shock peening can produce a deeper compressive stress field near the surface than shot peening. This advantage makes this technique desirable for the manipulation of crack growth rates. This paper describes an experimental program that was carried out to establish this effect in which steel specimens were partially laser peened and subsequently subjected to cyclic loading to grow fatigue cracks. The residual stress fields generated by the laser shock peening process were measured using the neutron diffraction technique. A state of compressive stress was found near the surface and tensile stresses were measured in the mid-thickness of the specimens. Growth rates of the cracks were observed to be more affected by the tensile core than by the compressive surface stresses.     

Effects of Shot‐Peening on Fretting Fatigue Crack Growth Behavior in Ti‐6Al‐4V

Abstract: The effects of shot‐peening on fretting fatigue crack growth behaviour in titanium alloy, Ti‐6A1‐4V were investigated. Three shot‐peening intensities: 4A, 7A and 10A were considered. The analysis involved the fracture mechanics and finite element sub‐modelling technique to estimate crack propagation lives. These computations were supplemented with the experimentally measured total fretting fatigue lives of laboratory specimens to assess the crack initiation lives. Shot‐peening has significant effect on the initiation/propagation phases of fretting fatigue cracks; however this effect depends upon the shot‐peening intensity. The ratio of crack initiation and total life increased while the ratio of the crack propagation and total life decreased with an increase of shot‐peening intensity. Effects of residual compressive stress from shot‐peening on the crack growth behaviour were also investigated. The fretting fatigue crack propagation component of the total life with relaxation increased in comparison to its counterpart without relaxation in each shot‐peened intensity case while the initiation component decreased. Improvement in the fretting fatigue life from the shot‐peening and also with an increase in the shot‐peening intensity appears to be not always due to increase in the crack initiation resistance from shot‐peened induced residual compressive stress.     

Crack incubation in shot peened AA7050 and mechanism for fatigue enhancement

Shot peening is a dynamic cold‐working process involving the impingement of peening media onto a substrate surface. Shot peening is commonly used as a surface treatment technique within the aerospace industry during manufacturing to improve fatigue performance of structural components. The compressive residual stress induced during shot peening results in fatigue crack growth retardation, improving the performance of shot‐peened components. However, shot peening is a compromise between the benefit of inducing a compressive residual stress and causing detrimental surface damage. Because of the relatively soft nature of AA7050‐T7451, shot peening can result in cracking of the constituent precipitate particles, creating an initial damage state. The aim of this paper is to understand the balance and fundamentals of these competing phenomena through a comparative study throughout the fatigue lifecycle of baseline versus shot‐peened AA7050‐T7451. Microstructure and surface topology characterization and comparison of the baseline and shot‐peened AA7050‐T7451 has been performed using scanning electron microscopy, electron backscatter diffraction, energy dispersive spectroscopy, and optical profilometry techniques. A residual stress analysis through interrupted fatigue of the baseline and shot‐peened AA7050‐T7451 was completed using a combination of X‐ray diffraction and nanoindentation. The fatigue life performance of the baseline versus shot‐peened material has been evaluated, including crack initiation and propagation. Subsurface particles crack upon shot peening but did not incubate into the matrix during fatigue loading, presumably due to the compressive residual stress field. In the baseline samples, the particles were initially intact, but upon fatigue loading, crack nucleation was observed in the particles, and these cracks incubated into the matrix. In damage tolerant analysis, an initial defect size is needed for lifetime assessment, which is often difficult to determine, leading to overly conservative evaluations. This work provides a critical assessment of the mechanism for shot peening enhancement for fatigue performance and quantifies how incubation of a short crack is inhibited from an initially cracked particle into the matrix within a residual stress field.     

Influence of residual stresses from shot peening on fretting fatigue crack growth

One method to improve fretting fatigue life is to shot peen the contact surfaces. Experimental fretting life results from specimens in a Titanium alloy with and without shot peened surfaces were evaluated numerically. The residual stresses were measured at different depths below the fretting scar and compared to the corresponding residual stress profile of an unfretted surface. Thus, the amount of stress relaxation during fretting tests was estimated. Elastic–plastic finite element computations showed that stress relaxation was locally more significant than that captured in the measurements. Three different numerical fatigue crack growth models were compared. The best agreement between experimental and numerical fatigue lives for both peened and unpeened specimens was achieved with a parametric fatigue growth procedure that took into consideration the growth behaviour along the whole front of a semi‐elliptical surface crack. Furthermore, the improved fretting fatigue life from shot peening was explained by slower crack growth rates in the shallow surface layer with compressive residual stresses from shot peening. The successful life analyses hinged on three important issues: an accurate residual stress profile, a sufficiently small start crack and a valid crack growth model.     

Effects of shot-peening intensity on fretting fatigue crack-initiation behaviour of Ti–6Al–4V

The effects of shot‐peening intensity on fretting fatigue crack‐initiation behaviour of titanium alloy, Ti–6Al–4V, were investigated. Three intensities, 4A, 7A and 10A with 100% surface coverage, were employed. The contact geometry involved a cylinder‐on‐flat configuration. Residual stress and improvement in fretting fatigue life were directly related to shot‐peening intensity. The magnitude of compensatory tensile stress and its location away from the contact surface increased with increasing intensity. The relaxation of residual stress occurred during fretting fatigue which increased with increasing the number of cycles. An analysis using a critical plane‐based fatigue crack‐initiation model showed that stress relaxation during the fretting fatigue affects life and location of crack initiation. Greater relaxation of the residual stress caused greater reduction of fatigue life and shifted the location of crack initiation from inside towards the contact surface. Modified shear stress range (MSSR) parameter was able to predict fretting fatigue crack‐initiation location, which agreed with the experimental counterparts. Also, the computed parameter showed an appropriate trend with the experimental observations of the measured fretting fatigue life based on the shot‐peening intensity.     

Characterization of fatigue crack initiation and growth in hybrid aluminium–graphite fibre composite laminates using image analysis

Hybrid aluminum–graphite-epoxy fibre–metal laminates have been tested in open hole tension–tension fatigue at several stress levels. Crack initiation and growth in the outer aluminum layers was monitored by periodic digital imaging of the specimen surface. Image analysis was used to determine the crack length throughout the experiment. Crack growth results were consistent between specimens for each test configuration. A relationship between the crack growth results and stress level was developed using linear elastic fracture mechanics; this successfully characterized the data. The effect of shot peening and alternate hole finishing techniques were considered for fatigue behaviour improvement.     

The influence of partial surface shot peening on fatigue crack growth behaviour of a high‐strength ferritic steel

The effects of partial surface shot peening on the fatigue crack growth behaviour of a ferritic steel have been experimentally investigated in this paper. Dog‐bone specimens fabricated from Optim700QL were tested under tension‐tension fatigue loads. Three distinct extents of partial shot peening, with respect to the crack tip and specimen symmetry line, were tested. The fatigue crack growth results from these experiments have been compared with those obtained from the same specimen geometry but with no peening. The results show that the residual stress fields formed ahead of the initial notch tip due to the partial peening process play a significant role in the fatigue crack growth behaviour of the material and effectively result in accelerated crack propagation at the midwidth of the specimens. It has been shown in this study that partial peening can lead to a fatigue crack growth rate around twice as fast as that of the unpeened specimen.     

Low cycle fatigue life prediction in shot‐peened components of different geometries—part I: residual stress relaxation

In this study, the residual stress relaxation behaviour occurring during low‐cycle fatigue in shot‐peened specimens with either a flat or a notched geometry has been studied. A representative low‐pressure steam turbine material, FV448, was used. The residual stress and strain hardening profiles caused by shot peening were measured experimentally and were then incorporated into a finite element model. By allowing for both effects of shot peening, the residual stress relaxation behaviour was successfully simulated using this model and correlated well with the experimental data. Although more modelling work may be required to simulate the interaction between shot peening effects and external loads in a range of notched geometries, the model predictions are consistent with the specimens tested in the current study. The novelty of this study lies in the development of such a modelling approach which can be used to effectively simulate the complex interaction between shot peening effects and external loads in notched regions. Compared with the un‐notched geometry, the notched geometry was found to be more effective in retaining the improvement in fatigue life resulting from shot peening, by restricting the compressive residual stress relaxation during fatigue loading.     

Influence of post weld treatments on the fatigue behaviour of Al-alloy welded joints

In this paper the influence of different post welding treatments, such as ageing or shot peening, on the fatigue behaviour of Al-alloy welded joints was investigated. The analysed joints were candidates for car structural applications. Several four point bending fatigue tests were conducted on GMAW specimens subjected to different post weld treatments. The residual stress field acting on specimens was measured by the X-ray diffraction (XRD) technique. The results of tests were discussed with the aid of a finite element model of the specimen aimed to calculate the actual fatigue cycle, also taking account of residual stresses and of their redistribution during the test. This allowed to characterize the fatigue resistance of the joints, taking account of the effective stress acting in the region of crack initiation.     

喷丸强化对OCr13Ni8Mo2Al钢疲劳性能的影响

研究了表面喷丸强化后表面残余应力、表面粗糙度和表面层残余压应力场对0Cr13Ni8Mo2Al钢疲劳性能的影响.结果表明:0Cr13Ni8Mo2Al钢经喷丸强化后,在表面层残余压应力场的作用下疲劳裂纹源由表面被"驱赶"到表面强化层下,疲劳寿命得到显著提高.     

喷丸强化对0Cr13Ni8Mo2Al钢疲劳性能的影响

研究了表面喷丸强化后表面残余应力,表面粗糙度和表面层残余应力场对0Cr13Ni8Mo2Al钢疲劳性能的影响,结果表明：0Cr13Ni8Mo2Al钢经喷丸强化后,在表面层残余应力场的作用下疲劳裂纹源由表面被“驱赶”到表面强化层下,疲劳寿命得到显著提高。     

喷丸强化对Ti6Al4V半椭圆表面裂纹J积分和裂纹扩展速率的影响

采用修正的J积分计算方法,考虑残余应力、残余应变和残余应变能,定量计算和分析喷丸强化对半椭圆表面裂纹前沿J积分参数的影响规律。对喷丸强化工艺进行有限元建模仿真,通过改变约束条件生成疲劳裂纹并施加远场载荷,计算J积分和裂纹扩展速率。考虑不同深度的半椭圆表面裂纹和不同丸粒速率对断裂参量的影响。结果表明:丸粒速率一定时,与未喷丸相比喷丸后J积分值的降幅随裂纹深度的增加而减小,喷丸强化有益于抑制疲劳浅裂纹的扩展。当裂纹深度为0.3mm时,裂纹最深点的J积分值由4.25N/mm降低到2.99N/mm,降幅约30.1%。裂纹深度一定时,J积分值随丸粒速率的增大而降低,提高丸粒速率对抑制裂纹扩展更有益。     

Short‐crack thresholds and propagation in an AISI 4340 steel under the effect of SP residual stresses

The effect of residual stresses induced by shot‐peening in a high‐strength AISI 4340 steel has been studied with the purpose of deriving a consistent fatigue model incorporating the results of fatigue crack growth experiments in the threshold region for a broad range of load ratio (R‐ratio ranging from ?2.5 to 0.7), and the effect of short cracks by means of a modified El‐Haddad model. The proposed model, taking into account the effect of crack closure and being capable to assess the conditions for fatigue propagation of short cracks partially embedded in the shot‐peened surface layer, was validated against constant amplitude fatigue experiments conducted in the endurance strength region, ie, for fatigue lives up to 10⁷ cycles, with micronotched specimens in the presence of shot‐peening residual stresses. The proposed model was also validated by comparing the results of fatigue crack propagation simulations with fatigue crack growth experiments under variable amplitude loading, experimentally reproducing the combined effect of service fatigue loads and shot‐peening residual stresses.     

CYCLIC LOADING BEHAVIOUR OF SODA-LIME SILICATE GLASS USING INDENTATION CRACKS

Abstract— Cyclic loading behaviour of soda-lime silicate glass was studied using Vickers indentation flaws. Glass bars were indented in air using a load of 9.8 N. Some samples were annealed in order to remove the indentation residual stress field. Both as-indented and annealed specimens were subjected to static and cyclic bending tests in a water environment using a four-point bending configuration. The influence of maximum stress on lifetime was considered. Crack propagation was examined by fractography and fracture patterns were similar to those observed in static fatigue. Characteristic fracture markers were seen on samples subjected to cyclic load. Experimental results were compared with theoretical predictions which were obtained on the basis of typical sub-critical crack growth behaviour. Precise determination of crack shape and residual stress factors were shown to play an important role in lifetime predictions.     

Experimental evaluation of fatigue crack initiation from corroded hemispherical notches in aerospace structural materials

A test program was developed and executed to evaluate the influence of corroded hemispherical notches on the fatigue crack initiation process in aluminium 7075‐T7351, 4340 steel and D6AC steel. Surface enhancements such as shot peening and laser shock peening were also incorporated as part of the test effort with the intent of assessing any improvements in fatigue performance. The aluminium specimens exhibited a relative insensitivity to the surface enhancements for crack initiation in pits ranging from 0.3 to 2.0 mm, and localized yielding was only a factor for smaller pits operated at an elevated load ratio. Residual stresses created by the surface enhancements as well as localized yielding improved the crack initiation behavior from the base of the pits for both the 4340 and D6AC steel specimens. This behaviour was evident at high and low load ratios. In particular, laser shock peening induced residual stresses produced a significant increase in the crack initiation stress even when localized yielding was not a factor.     

Influence of anodization on the fatigue strength of 7050-T7451 aluminium alloy

In recent years, with higher demand for improved quality and corrosion resistance, recovered substrates have been extensively used. Consequently residual stresses originated from these coatings reduce the fatigue strength of a component. Due to this negative influence occasioned by corrosion resistance protective coatings, an effective process like shot peening must be considered to improve the fatigue strength. The shot peening treatment pushes the crack sources beneath the surface in most of medium and high cycle cases due to the compressive residual stress field (CRSF) induced. The aim of this study was to evaluate the influence on the fatigue life of anodic films grown on 7050-T7451 aluminium alloy by sulphuric acid anodizing, chromic acid anodizing and hard anodizing. The influence on the rotating and reverse bending fatigue strength of anodic films grown on the aluminium alloy is to degrade the stress life fatigue performance of the base material. A consistent gain in fatigue life in relation to the base material was obtained through the shot peening process in coated specimens, associated to a residual stress field compressive near the surface, useful to avoid fatigue crack nucleation and delay or even stop crack propagation.     

A comprehensive investigation on the effects of laser and shot peening on fatigue crack growth in friction stir welded AA 2195 joints

The effects of various surface treatment techniques on the fatigue crack growth performance of friction stir welded 2195 aluminum alloy were investigated. The objective was to reduce fatigue crack growth rates and enhance the fatigue life of welded joints. The crack growth rates were assessed and characterized for different peening conditions at a stress ratio (R) of 0.1, and 0.7. The surface and through-thickness residual stress distribution were also investigated and presented for the various regions in the weld. Tensile residual stresses introduced during the welding process were found to become significantly compressive, particularly after laser peening. The effect of the compressive stresses was deemed responsible for increasing the resistance to fatigue crack growth of the welds. The results indicate a significant reduction in fatigue crack growth rates using laser peening compared to shot peening and native welded specimens. This reduced fatigue crack growth rate was comparable to the base unwelded material.     

Effects of different indentation methods on fatigue life extension of cracked specimens

In this paper, 3 different indentation methods have been investigated for crack arresting and fatigue life enhancement of cracked components. The influence of residual stresses induced by indentation on fatigue crack growth (FCG) rate was explored by experiments and numerical simulations. Fatigue tests were conducted on a group of specimens which were indented on the crack tip by various indentation load magnitudes. For another group of specimens, the double indentation and triple indentation methods were applied on the cracked specimens with the aim of obtaining proper residual stress fields that contribute to higher crack growth retardations. Both the numerical and experimental results revealed that the higher indentation loads led to larger domain of compressive residual stress around the crack tip and consequently to higher fatigue life extension. In addition, the triple indentation method resulted in more FCG retardation compared with single and double indentation methods. Furthermore, for the specimens repaired by double and triple indentation methods, indenting ahead of the crack tip led to retardation in more crack growth compared with the other horizontal positions of indentation.     

Effect of single and multiple overloading on the residual fatigue life of a structural steel

This work was carried out to determine the effect of overload cycles on the fatigue life of a structural steel used for offshore applications. Single and multiple overloads were adopted and the corresponding fatigue crack growth retardation was evaluated. Residual stress fields were measured in the vicinity of the crack tip using an X‐ray diffraction technique and their size compared with that of the overload cyclic plastic zone. In regard to crack growth retardation, the results indicated that the extension in fatigue life increases with an increase in overload, as a consequence of the generation of higher compressive residual stress levels over a larger distance ahead of the crack tip. The effect of two equal and consecutive overloads, with the second one applied at different intervals of crack propagation from the first, was also considered. Larger intervals were shown to lead to a longer residual fatigue life.     

Weld residual stress effects on fatigue crack growth behaviour of aluminium alloy 2024-T351

The interaction between residual stress and fatigue crack growth rate has been investigated in middle tension and compact tension specimens machined from a variable polarity plasma arc welded aluminium alloy 2024-T351 plate. The specimens were tested at three levels of applied constant stress intensity factor range. Crack closure was continuously monitored using an eddy current transducer and the residual stresses were measured with neutron diffraction. The effect of the residual stresses on the fatigue crack behaviour was modelled for both specimen geometries using two approaches: a crack closure approach where the effective stress intensity factor was computed; and a residual stress approach where the effect of the residual stresses on the stress ratio was considered. Good correlation between the experimental results and the predictions were found for the effective stress intensity factor approach at a high stress intensity factor range whereas the residual stress approach yielded good predictions at low and moderate stress intensity factor ranges. In particular, the residual stresses accelerated the fatigue crack growth rate in the middle tension specimen whereas they decelerated the growth rate in the compact tension sample, demonstrating the importance of accurately evaluating the residual stresses in welded specimens which will be used to produce damage tolerance design data.