Regeneration of thermally aged Pt-Rh/CexZr1−xO2-Al2O3 model three-way catalysts by oxychlorination treatments

Pt-Rh/Ce_xZr_1−xO₂-Al₂O₃ with 0.6 and 1.0 wt.% noble metal loadings were prepared and characterized for their metal dispersion with respect to Ce_xZr_1−xO₂-free Pt-Rh/Al₂O₃ in fresh, thermally aged and oxychlorinated states. Thermal ageing at 973 K led to loss of metal dispersion in all cases but to negligible effect on the dispersion of the Ce_xZr_1−xO₂ component where present. Oxychlorination was able to fully recover metal dispersion in all cases but led to different effects on the redox properties of Ce_xZr_1−xO₂ which appeared to be related to the metal loadings. Despite showing improved dispersion following regeneration, higher loaded catalyst showed no improvement in light-off performance for either NO reduction or CO oxidation and showed poorer oxygen storage (OSC) ability, particularly at higher temperatures. Lower loaded catalyst showed improved dispersion, improved OSC and reduced light-off temperatures for NO reduction and CO oxidation after oxychlorination compared to that in the thermally aged state.     

Preparation of CexZr1−xO2 (x = 0.75, 0.62) solid solution and its application in Pd-only three-way catalysts

Nanoparticles of Ce_xZr_1−xO₂ (x = 0.75, 0.62) were prepared by the oxidation-coprecipitation method using H₂O₂ as an oxidant, and characterized by N₂ adsorption, XRD and H₂-TPR. Ce_xZr_1−xO₂ prepared had single fluorite cubic structure, good thermal stability and reduction property. With the increasing of Ce/Zr ratio, the surface area of Ce_xZr_1−xO₂ increased, but thermal stability of Ce_xZr_1−xO₂ decreased. The surface area of Ce_0.62Zr_0.38O₂ was 41.2 m²/g after calcination in air at 900 °C for 6 h. TPR results showed the formation of solid solution promoted the reduction of CeO₂, and the reduction properties of Ce_xZr_1−xO₂ were enhanced by the cycle of TPR-reoxidation. The Pd-only three-way catalysts (TWC) were prepared by the impregnation method, in which Ce_0.75Zr_0.25O₂ was used as the active washcoat and Pd loading was 0.7 g/L. In the test of Air/Fuel, the conversion of C₃H₈ was close to 100% and NO was completely converted at λ < 1.025. The high conversion of C₃H₈ was induced by the steam reform and dissociation adsorption reaction of C₃H₈. Pd-only catalyst using Ce_0.75Zr_0.25O₂ as active washcoat showed high light off activity, the reaction temperatures (T₅₀) of 50% conversion of CO, C₃H₈ and NO were 180, 200 and 205 °C, respectively. However, the conversions of C₃H₈ and NO showed oscillation with continuously increasing the reaction temperature. The presence of La₂O₃ in washcoat decreased the light off activity and suppressed the oscillation of C₃H₈ and NO conversion. After being aged at 900 °C for 4 h, the operation windows of catalysts shifted slightly to rich burn. The presence of La₂O₃ in active washcoat can enhance the thermal stability of catalyst significantly.     

Catalytic behavior of La–Sr–Ce–Fe–O mixed oxidic/perovskitic systems for the NO+CO and NO+CH4+O2 (lean-NOx) reactions

Mixed oxides of the general formula La_0.5Sr_xCe_yFeO_z were prepared by using the nitrate method and characterized by XRD and Mössbauer techniques. The crystal phases detected were perovskites LaFeO₃ and SrFeO_3−x and oxides -Fe₂O₃ and CeO₂ depending on x and y values. The low surface area ceramic materials have been tested for the NO+CO and NO+CH₄+O₂ (“lean-NO_x”) reactions in the temperature range 250–550°C. A noticeable enhancement in NO conversion was achieved by the substitution of La³⁺ cation at A-site with divalent Sr⁺² and tetravalent Ce⁺⁴ cations. Comparison of the activity of the present and other perovskite-type materials has pointed out that the ability of the La_0.5Sr_xCe_yFeO_z materials to reduce NO by CO or by CH₄ under “lean-NO_x” conditions is very satisfying. In particular, for the NO+CO reaction estimation of turnover frequencies (TOFs, s⁻¹) at 300°C (based on NO chemisorption) revealed values comparable to Rh/-Al₂O₃ catalyst. This is an important result considering the current tendency for replacing the very active but expensive Rh and Pt metals. It was found that there is a direct correlation between the percentage of crystal phases containing iron in La_0.5Sr_xCe_yFeO_z solids and their catalytic activity. O₂ TPD (temperature-programmed desorption) and NO TPD studies confirmed that the catalytic activity for both tested reactions is related to the defect positions in the lattice of the catalysts (e.g., oxygen vacancies, cationic defects). Additionally, a remarkable oscillatory behavior during O₂ TPD studies was observed for the La_0.5Sr_0.2Ce_0.3FeO_z and La_0.5Sr_0.5FeO_z solids.     

Ce1−xCuxO2−x/Al2O3/FeCrAl catalysts for catalytic combustion of methane

A series of the Ce_1−xCu_xO_2−x/Al₂O₃/FeCrAl catalysts (x = 0–1) were prepared. The structure of the catalysts was characterized using XRD, SEM and H₂-TPR. The catalytic activity of the catalysts for the combustion of methane was evaluated. The results indicated that in the Ce_1−xCu_xO_2−x/Al₂O₃/FeCrAl catalysts the surface phase structure were the Ce_1−xCu_xO_2−x solid solution, -Al₂O₃ and γ-Al₂O₃. The surface particle shape and size were different with the variety of the molar ratio of Ce to Cu in the Ce_1−xCu_xO_2−x solid solution. The Cu component of the Ce_1−xCu_xO_2−x/Al₂O₃/FeCrAl catalysts played an important role to the catalytic activity for the methane combustion. There were the stronger interaction among the Ce_1−xCu_xO_2−x solid solution and the Al₂O₃ washcoats and the FeCrAl support.     

Catalytic combustion of hydrocarbons with Mn and Cu-doped ceria–zirconia solid solutions

The catalytic activity of a series of CeO₂–ZrO₂ mixed oxides in the total oxidation of methane and light hydrocarbons has been investigated. The influence of dopants like Mn and Cu has also been studied. It is shown that both MnO_x and CuO at low loading dissolve within the ceria–zirconia lattice. This strongly influences the redox behaviour of the catalysts by promoting low-temperature reduction of Ce⁴⁺. In addition, the ternary oxides show better stability to repeated redox cycles, which is attributed to the presence of ZrO₂. The catalytic activity of pure CeO₂ is also enhanced in the presence of ZrO₂, reaching a maximum with Ce_0.92Zr_0.08O₂; a further promotion of activity is observed with the introduction of MnO_x and CuO dissolved into CeO₂–ZrO₂ lattice.     

Development of new catalysts for N2O-decomposition from adipic acid plant

Direct decomposition of N₂O was investigated using simulated and real industrial gas stream coming from an adipic acid plant. Two different kinds of catalysts were studied: (i) LaB_1−xB′_xO₃ and CaB_1−xCu_xO₃ (B = Mn, Fe and B′ = Cu, Ni) perovskites (PVKs) and (ii) supported PVKs (10 or 20 wt.%) on γ-Al₂O₃ and CeO₂–ZrO₂. The structural modifications induced by the composition of PVK samples affect the catalytic performances: mixed oxide formation in CaMn_0.7Cu_0.3O₃ samples allows to reach the highest values of N₂O conversion while the effect of PVK phases is more controversial. The importance of copper on catalytic activities is confirmed by the investigation on CaMn_1−xCu_xO₃ samples. The best results were obtained with a CaMn_0.6Cu_0.4O₃ catalyst calcined at 700 °C for 5 h, in which the presence of copper maximises the Ca₃CuMnO₆ phase formation. The increase in Cu-content produces a large segregation of CuO despite PVK formation. The best catalyst was tested using industrial gas stream, showing good stability also in the presence of H₂O and O₂ (8% v/v ) after 1400 h on-stream. To increase surface area, Cu-containing PVKs were deposed on γ-Al₂O₃ and CeO₂–ZrO₂, and this latter has been recognised as the best support. Indeed, the activity of the PVKs supported on ceria–zirconia is comparable to and even better than that of the bulk catalysts. A possible explanation regards the support contribution in terms of activity and/or promotion of O₂ mobility which enhances the overall activity of the catalyst.     

Pd/Ce0.6Zr0.4O2/Al2O3 as advanced materials for three-way catalysts: Part 1. Catalyst characterisation, thermal stability and catalytic activity in the reduction of NO by CO

Pd-loaded Ce_0.6Zr_0.4O₂ solid solutions supported on Al₂O₃ are investigated as catalysts for the reduction of NO by CO. The attention is focused on the role of the Ce_0.6Zr_0.4O₂ and of the Pd dispersion on the catalytic activity. The system shows a very high activity below 500 K, which is almost independent on the Pd dispersion. The high activity is attributed to a promoting effect of the Ce_0.6Zr_0.4O₂ on the NO conversion. Investigation of the influence of high temperature treatments disclosed a thermal stabilisation of both Ce_0.6Zr_0.4O₂ and Al₂O₃ in the Ce_0.6Zr_0.4O₂/Al₂O₃ system.     

Methane combustion and CO oxidation on LaAl1−xMnxO3 perovskite-type oxide solid solutions

Structural, redox and catalytic deep oxidation properties of LaAl_1−xMn_xO₃ (x=0.0, 0.05, 0.1, 0.2, 0.4, 0.6, 0.8, 1.0) solid solutions prepared by the citrate method and calcined at 1073 K were investigated. XRD analysis showed that all the LaAl_1−xMn_xO₃ samples are single phase perovskite-type solid solutions. Particle sizes and surface areas (SA) are in the 280–1180 Å and 4–33 m² g⁻¹ ranges, respectively. Redox properties and the content of Mn⁴⁺ were derived from temperature programmed reduction (TPR) with H₂. Two reduction steps are observed by TPR for pure LaMnO₃, the first attributed to the reduction of Mn⁴⁺ to Mn³⁺ and the second due to complete reduction of Mn³⁺ to Mn²⁺. The presence of Al in the LaAl_1−xMn_xO₃ solid solutions produces a strong promoting effect on the Mn⁴⁺→Mn³⁺ reducibility and inhibits the further reduction to Mn²⁺. Both for methane combustion and CO oxidation all Mn-containing perovskites are much more active than LaAlO₃, so pointing to the essential role of the transition metal ion in developing highly active catalysts. Partial dilution with Al appears to enhance the specific activity of Mn sites for methane combustion.     

Interaction of NO and NO2 with the surface of CexZr1−xO2 solid solutions – Influence of the phase composition

Structural (XRD) and spectroscopic (EPR, IR and Raman) investigations were performed to elucidate the influence of CeO₂ content on the phase composition and surface chemistry of Ce_xZr_1−xO₂ solid solutions (x = 0.10–0.85), interacting with NO and NO₂ in the absence and presence of oxygen. Strong influence of ceria loading on the adsorption modes of both nitrogen oxides and the nature of the resultant surface species was revealed. Adsorption of NO led to formation of mononitrosyl complexes, dimers and N₂O, whereas interaction of NO₂ with the ceria–zirconia catalyst resulted in the adsorbate disproportionation or coupling, depending on the sample composition.     

Ta、Ba共掺杂石榴石型Li7La3Zr2O12电解质的制备及性能研究

传统锂离子电池采用有机电解液体系,能量密度难以进一步提升,同时存在一定的安全隐患。采用无机固体电解质构建全固态锂电池,在提高电池能量密度同时可兼顾安全性问题。在众多无机固体电解质中,Li₇La₃Zr₂O₁₂(LLZO)石榴石电解质具有离子电导率高、与金属锂接触稳定等优势,成为受人关注的材料。为了进一步提高该材料的导电性,采用固相法合成Ta、Ba共掺杂LLZO(Li_7-x+yLa_3-yBa_yZr_2-xTa_xO₁₂)电解质,采用X射线衍射、扫描电子显微镜和电化学阻抗法分析样品的物相结构、微观形貌及离子电导率。结果表明,Ta⁵⁺掺杂能够稳定立方相结构,Ba²⁺作为掺杂剂和烧结剂,促进晶粒生长和陶瓷致密化,从而降低总电阻。其中,Li_6.45La_2.95Ba_0.05Zr_1.4Ta_0.6O₁₂样品在室温下的总电导率为1.07×10^-3 S·cm^-1,活化能为0.378 eV。Ta⁵⁺/Ba²⁺共掺杂有利于制备高致密度和高电导率的石榴石型电解质材料。     

Superior performance of Ir-substituted hexaaluminate catalysts for N2O decomposition

Novel Ir-substituted hexaaluminate catalysts were developed for the first time and used for catalytic decomposition of high concentration of N₂O. The catalysts were prepared by one-pot precipitation and characterized by X-ray diffraction (XRD), N₂-adsorption, scanning electronic microscopy (SEM) and temperature-programmed reduction (H₂-TPR). The XRD results showed that only a limited amount of iridium was incorporated into the hexaaluminate lattice by substituting Al³⁺ to form BaIr_xFe_1−xAl₁₁O₁₉ after being calcined at 1200 °C, while the other part of iridium existed as IrO₂ phase. The activity tests for high concentration (30%, v/v) of N₂O decomposition demonstrated that the BaIr_xFe_1−xAl₁₁O₁₉ hexaaluminates exhibited much higher activities and stabilities than the Ir/Al₂O₃-1200, and the pre-reduction with H₂ was essential for activating the catalysts. By comparing BaIr_xFe_1−xAl₁₁O₁₉ with BaIr_xAl_12−xO₁₉ (x = 0–0.8), it was found that iridium was the active component in the N₂O decomposition and the framework iridium was more active than the large IrO₂ particles. On the other hand, Fe facilitated the formation of hexaaluminate as well as the incorporation of iridium into the framework.     

Nanosized perovskite-type oxides La1−xSrxMO3−δ (M = Co, Mn; x = 0, 0.4) for the catalytic removal of ethylacetate

Nanometer perovskite-type oxides La_1−xSr_xMO_3−δ (M = Co, Mn; x = 0, 0.4) have been prepared using the citric acid complexing-hydrothermal-coupled method and characterized by means of techniques, such as X-ray diffraction (XRD), BET, high-resolution scanning electron microscopy (HRSEM), X-ray photoelectron spectroscopy (XPS), temperature-programmed desorption (TPD), and temperature-programmed reduction (TPR). The catalytic performance of these nanoperovskites in the combustion of ethylacetate (EA) has also been evaluated. The XRD results indicate that all the samples possessed single-phase rhombohedral crystal structures. The surface areas of these nanomaterials ranged from 20 to 33 m² g⁻¹, the achievement of such high surface areas are due to the uniform morphology with the typical particle size of 40–80 nm (as can be clearly seen in their HRSEM images) that were derived with the citric acid complexing-hydrothermally coupled strategy. The XPS results demonstrate the presence of Mn⁴⁺ and Mn³⁺ in La_1−xSr_xMnO_3−δ and Co³⁺ and Co²⁺ in La_1−xSr_xCoO_3−δ, Sr substitution induced the rises in Mn⁴⁺ and Co³⁺ concentrations; adsorbed oxygen species (O⁻, O₂⁻, or O₂²⁻) were detected on the catalyst surfaces. The O₂-TPD profiles indicate that Sr doping increased desorption of the adsorbed oxygen and lattice oxygen species at low temperatures. The H₂-TPR results reveal that the nanoperovskite catalysts could be reduced at much lower temperatures (<240 °C) after Sr doping. It is observed that under the conditions of EA concentration = 1000 ppm, EA/oxygen molar ratio = 1/400, and space velocity = 20,000 h⁻¹, the catalytic activity (as reflected by the temperature (T_100%) for EA complete conversion) increased in the order of LaCoO_2.91 (T_100% = 230 °C) ≈ LaMnO_3.12 (T_100% = 235 °C) < La_0.6Sr_0.4MnO_3.02 (T_100% = 190 °C) < La_0.6Sr_0.4CoO_2.78 (T_100% = 175 °C); furthermore, there were no formation of partially oxidized by-products over these catalysts. Based on the above results, we conclude that the excellent catalytic performance is associated with the high surface areas, good redox properties (derived from higher Mn⁴⁺/Mn³⁺ and Co³⁺/Co²⁺ ratios), and rich lattice defects of the nanostructured La_1−xSr_xMO_3−δ materials.     

AFeO3 (A=La, Nd, Sm) and LaFe1−xMgxO3 perovskites as methane combustion and CO oxidation catalysts: structural, redox and catalytic properties

Catalytic methane combustion and CO oxidation were investigated over AFeO₃ (A=La, Nd, Sm) and LaFe_1−xMg_xO₃ (x=0.1, 0.2, 0.3, 0.4, 0.5) perovskites prepared by citrate method and calcined at 1073 K. The catalysts were characterized by X-ray diffraction (XRD). Redox properties and the content of Fe⁴⁺ were derived from temperature programmed reduction (TPR). Specific surface areas (SA) of perovskites were in 2.3–9.7 m² g⁻¹ range. XRD analysis showed that LaFeO₃, NdFeO₃, SmFeO₃ and LaFe_1−xMg_xO₃ (x·0.3) are single phase perovskite-type oxides. Traces of La₂O₃, in addition to the perovskite phase, were detected in the LaFe_1−xMg_xO₃ catalysts with x=0.4 and 0.5. TPR gave evidence of the presence in AFeO₃ of a very small fraction of Fe⁴⁺ which reduces to Fe³⁺. The fraction of Fe⁴⁺ in the LaFe_1−xMg_xO₃ samples increased with increasing magnesium content up to x=0.2, then it remained nearly constant. Catalytic activity tests showed that all samples gave methane and CO complete conversion with 100% selectivity to CO₂ below 973 and 773 K, respectively. For the AFeO₃ materials the order of activity towards methane combustion is La>Nd>Sm, whereas the activity, per unit SA, of the LaFe_1−xMg_xO₃ catalysts decreases with the amount of Mg at least for the catalysts showing a single perovskite phase (x=0.3). Concerning the CO oxidation, the order of activity for the AFeO₃ materials is Nd>La>Sm, while the activity (per unit SA) of the LaFe_1−xMg_xO₃ catalysts decreases at high magnesium content.     

Barium-doped Pr2Ni0.6Cu0.4O4+δ with triple conducting characteristics as cathode for intermediate temperature proton conducting solid oxide fuel cell

Proton conducting solid oxide fuel cell (H-SOFC) is an emerging energy conversion device, with lower activation energy and higher energy utilization efficiency. However, the deficiency of highly active cathode materials still remains a major challenge for the development of H-SOFC. Therefore, in this work, K₂NiF₄-type cathode materials Pr_2-xBaNi_0.6Cu_0.4O_4+δ (x=0, 0.1, 0.2, 0.3), single-phase triple-conducting (e^-/O^2-/H⁺) oxides, are prepared for intermediate temperature H-SOFCs and exhibit good oxygen reduction reaction activity. The investigation demonstrates that doping Ba into Pr_2-xBaNi_0.6Cu_0.4O_4+δ can increase its electrochemical performance through enhancing electrical conductivity, oxygen vacancy concentration and proton conductivity. EIS tests are carried at 750℃ and the minimum polarization impedances are obtained when x=0.2, which are 0.068 Ω·cm² in air and 1.336 Ω·cm² in wet argon, respectively. The peak power density of the cell with Pr_1.8Ba_0.2Ni_0.6Cu_0.4O_4+δ cathode is 298 mW·cm^-2 at 750℃ in air with humidified hydrogen as fuel. Based on the above results, Ba-doped Pr_2-xBaNi_0.6Cu_0.4O_4+δ can be a good candidate material for SOFC cathode applications.     

Synthesis, characterization and catalytic activity for NO–CO reaction of Pd–(La, Sr)2MnO4 system

La_xSr_2−xMnO₄ (0 ≤ x ≤ 0.8) oxides were synthesized and single-phase K₂NiF₄-type oxides were obtained in the range of 0.1 ≤ x < 0.5. The catalytic activity of La_xSr_2−xMnO₄ for NO–CO reaction increased with increasing x in the range of solubility limit of La. La_0.5Sr_1.5MnO₄ showed the highest activity among La_xSr_2−xMnO₄ prepared in this study, but its activity was inferior to perovskite-type La_0.5Sr_0.5MnO₃. Among the Pd-loaded catalysts, however, Pd/La_0.8Sr_1.2MnO₄ showed the higher activity and the selectivity to N₂ than Pd/La_0.5Sr_0.5MnO₃ and Pd/γ-Al₂O₃. The excellent catalytic performance of Pd/La_0.2Sr_1.2MnO₄ could be ascribable to the formation of SrPd₃O₄ which was detected by XRD in the catalyst but not in the other two catalysts.     

Metal-loaded CeO2-ZrO2 solid solutions as innovative catalysts for automotive catalytic converters

The redox behaviour of a Ce_0.5Zr_0.5O₂ solid solution is investigated by means of temperature programmed reduction (TPR) and oxygen uptake measurements. It is shown that the introduction of ZrO₂ into the CeO₂ framework, strongly modifies the reduction behaviour in comparison to pure CeO₂. Remarkably, in contrast to the CeO₂, upon repetitive reduction-oxidation processes, the temperature of reduction of the solid solution decreases from 900 to 700 K. The reduction of NO by CO over metal-loaded catalysts is investigated and the role of support Ce³⁺ sites in the enhancing the NO conversion is discussed.     

XPS studies on the oxygen species of LaMn1−xCuxO3+λ

The electronic states of LaMn_1−xCu_xO_3+λ (x=0–0.4) have been studied with X-ray photoelectron spectroscopy (XPS). The valence states of substituted copper ions were Cu²⁺ and the manganese ions were a highly mixed state of Mn³⁺ and Mn⁴⁺. The nonstoichiometry and electronic state of lattice oxygen have been studied. The samples at x=0 and 0.1 had an excess of lattice oxygen but those at x=0.2–0.4 had lattice oxygen deficiency. A modified Auger parameter (Δ′) was used to evaluate the electronic states of oxygen ions. The Δ′ of lattice oxygen increased with increasing substitute quantity. This increase of Δ′ reflected the decrease of ionic bond character of lattice oxygen. The adsorbed oxygen species on LaMn_1−xCu_xO_3+λ was assigned mainly as O⁻ from the peak positions of spectra for the O 1s and O KLL levels, and the Δ′ of this O⁻ decreased with x. This decrease, i.e., the increase of ionic bond character of adsorbed oxygen was correlated well with the value of nonstoichiometry of lattice oxygen.

The rate of CO oxidation at 448 K was increased by the substitution till x=0.4. We consider that this enhancement of reactivity comes from the change of electronic state of adsorbed oxygen, O⁻ itself, i.e., a weak interaction between O⁻ and low coordinated metal site brings about a high reactivity.     

Effect of ceria–zirconia ratio on the interaction of CO with PdO/Al2O3–(Cex–Zr1−x)O2 catalysts prepared by sol–gel method

The current work is devoted to study of CO interaction with PdO/Al₂O₃–(Ce_x–Zr_1−x)O₂ catalysts. Ceria–zirconia–alumina supports with different Ce/Zr ratio were prepared by sol–gel technique. The FT-IR characterization of CO adsorbed at −120 and 25 °C on oxidized and reduced samples revealed that Ce/Zr ratio modifies the surface properties of support and oxidation state of palladium. The catalyst with Ce/Zr molar ratio 0.5/0.5 was characterized with the highest ability to stabilize palladium in oxide state and the highest activity to oxidize CO. Redox treatment of catalysts improves their catalytic activity.     

铈锆固溶体CexZr1-xO2上H2S的选择性催化氧化性能

采用共沉淀法合成一系列具有不同Ce/Zr物质的量比的铈锆固溶体Ce_xZr_1-xO₂,考察Ce/Zr比例对H₂S选择氧化反应催化活性的影响。通过XRD、BET、Raman、XPS、CO₂-TPD、O₂-TPD、H₂-TPR等手段对铈锆固溶体的晶体结构、表面性质、碱性位以及氧化还原性等进行表征。结果表明,所有的铈锆固溶体催化剂均可以在化学计量比的氧气下具有优良的低温催化活性,催化活性随着Ce/Zr比例的提高而增加,其中Ce_0.9Zr_0.1O₂活性最高,(160~260) ℃转化率均保持在95%以上,在180 ℃时硫收率可达到97%,这主要是因为Ce_0.9Zr_0.1O₂具有最多的中度碱性位、活性位数量和强的氧化还原性。同时推测Ce⁴⁺为催化反应的活性位,并遵循氧化还原机理。此外,催化剂的失活主要是由于催化剂表面生成硫酸盐物种,消耗了活性组分Ce⁴⁺。     

Thermoelectric characterization of NaxMx/2Ti1−x/2O2 (M=Co, Ni and Fe) polycrystalline materials

Layered -titanate materials, Na_xM_x/2Ti_1−x/2O₂ (M=Co, Ni and Fe, x=0.2–0.4), were synthesized by flux reactions, and electrical properties of polycrystalline products were measured at 300–800 °C. After sintering at 1250 °C in Ar, all products show n-type thermoelectric behavior. The values of both d.c. conductivity and Seebeck coefficient of polycrystalline Na_0.4Ni_0.2Ti_0.8O₂ were ca. 7×10³ S/m and ca. −193 μV/K around 700 °C, respectively. The measured thermal conductivity of layered -titanate materials has lower value than conductive oxide materials. It was ca. 1.5 Wm⁻¹ K⁻¹ at 800 °C. The estimated thermoelectric figure-of-merit, Z, of Na_0.4Ni_0.2Ti_0.8O₂ and Na_0.4Co_0.2Ti_0.8O₂ was about 1.9×10⁻⁴ and 1.2×10⁻⁴ K⁻¹ around 700 °C, respectively.