The effects of Bi(Mg2/3Nb1/3)O3 on piezoelectric and ferroelectric properties of K0.5Na0.5NbO3 lead-free piezoelectric ceramics

To improve the temperature stability of piezoelectric properties of Na_0.5K_0.5NbO₃ (KNN)-based ceramics, Bi(Mg_2/3Nb_1/3)O₃ (BMN) was used to modify Na_0.5K_0.5NbO₃ (KNN)-based ceramics by a conventional sintering technique. Piezoelectric and ferroelectric properties of 0.99K_0.5Na_0.5NbO₃-0.01Bi(Mg_2/3Nb_1/3)O₃ ceramics were studied. It is found that 0.01BMN-0.99KNN ceramics exhibits stable piezoelectric properties as the temperature changes due to the composition fluctuation on B sites (d₃₃ ≈ 130 pC/N, dielectric loss tg θ ≤ 5% in the range 25-300 °C). These results indicate that these materials are promising lead-free piezoelectric ceramic candidates for practical applications.     

Piezoelectric and dielectric properties of Dy2O3-doped (Bi0.5Na0.5)0.94Ba0.06TiO3 lead-free ceramics

(Bi_0.5Na_0.5)_0.94Ba_0.06TiO₃ + x wt% Dy₂O₃ with x = 0-0.3 ceramics were synthesized by conventional solid-state processes. The effects of Dy₂O₃ on the microstructure, the piezoelectric and dielectric properties were investigated. X-ray diffraction pattern confirmed that the coexistence of tetragonal and rhombohedral phases in the (Bi_0.5Na_0.5)_0.94Ba_0.06TiO₃ composition was not changed by adding 0.05-0.3 wt% Dy₂O₃. SEM images indicate that all the ceramics have pore-free microstructures with high density, and that doping of Dy₂O₃ inhibits the grain growth of the ceramics. The addition of Dy₂O₃ shows the double effects on decreasing the piezoelectric and dielectric properties for 0 < x < 0.15 when Dy³⁺ ions substitute B-site Ti⁴⁺ ions, and increasing the properties for 0.15 < x < 0.3 when Dy³⁺ ions enters into A-site of the perovskite structure. The optimum electric properties of piezoelectric constant d₃₃ = 170 pC/N and the dielectric constant ?_r = 1900 (at a frequency of 1 kHz) are obtained at x = 0.3.     

Enhancement microwave dielectric properties of La(Mg0.5Sn0.5)O3 ceramics by substituting Mg with Ni

The microwave dielectric properties of La(Mg_0.5−xNi_xSn_0.5)O₃ ceramics were examined with a view to their exploitation for mobile communication. The La(Mg_0.5−xNi_xSn_0.5)O₃ ceramics were prepared by the conventional solid-state method at various sintering temperatures. The X-ray diffraction patterns of the La(Mg_0.4Ni_0.1Sn_0.5)O₃ ceramics revealed no significant variation of phase with sintering temperatures. Apparent density of 6.71 g/cm³, dielectric constant (?_r) of 20.19, quality factor (Q × f) of 74,600 GHz, and temperature coefficient of resonant frequency (τ_f) of −85 ppm/°C were obtained for La(Mg_0.4Ni_0.1Sn_0.5)O₃ ceramics that were sintered at 1550 °C for 4 h.     

Microstructure, ferroelectric, and piezoelectric properties of (1 − x − y)Bi0.5Na0.5TiO3-xBaTiO3-yBi0.5Ag0.5TiO3 lead-free ceramics

Lead-free (1 − x − y)Bi_0.5Na_0.5TiO₃-xBaTiO₃-yBi_0.5Ag_0.5TiO₃ (BNT-BT-BAT-x/y, x = 0-0.10, y = 0-0.075) piezoelectric ceramics were synthesized by conventional oxide-mixed method. The microstructure, ferroelectric, and piezoelectric properties of the ceramics were investigated. Results show that a morphotropic phase boundary (MPB) between rhombohedral and tetragonal phases of BNT-BT-BAT-x/0.04 ceramics is formed at x = 0.06-0.08. The addition of BAT has no obvious change on the crystal structure of BNT-BT ceramics while it causes the grain size of the ceramics to become more homogenous. Near the MPB, the ceramics with x = 0.06 and y = 0.05-0.06 possess optimum electrical properties: P_r ∼ 42.5 μC/cm², E_c ∼ 32.0 kV/cm, d₃₃ ∼ 172 pC/N, k_p ∼ 32.6%, and k_t ∼ 52.6%. The temperature dependences of k_p and polarization versus electric hysteresis loops reveal that the depolarization temperature (T_d) of BNT-BT-BAT-0.06/y ceramics decreases with increasing y. In addition, the polar and non-polar phases may coexist in the BNT-BT-BAT-x/y ceramics above T_d.     

Phase transition and piezoelectric properties of K0.48Na0.52NbO3-LiTa0.5Nb0.5O3-NaNbO3 lead-free ceramics

Plate-like NaNbO₃ (NN) particles were used as the raw material to fabricate (1 − x)[0.93 K_0.48Na_0.52Nb O₃-0.07Li(Ta_0.5Nb_0.5)O₃]-xNaNbO₃ lead-free piezoelectric ceramics using a conventional ceramic process. The effects of NN on the crystal structure and piezoelectric properties of the ceramics were investigated. The results of X-ray diffraction suggest that the perovskite phase coexists with the K₃Li₂Nb₅O₁₅ phase, and the tilting of the oxygen octahedron is probably responsible for the evolution of the tungsten-bronze-typed K₃Li₂Nb₅O₁₅ phase. The Curie temperature (T_C) is shifted to lower temperature with increasing NN content. (1 − x)[0.93 K_0.48Na_0.52NbO₃-0.07Li(Ta_0.5Nb_0.5)O₃]-xNaNbO₃ ceramics show obvious dielectric relaxor characteristics for x > 0.03, and the relaxor behavior of ceramics is strengthened by increasing NN content. Both the electromechanical coupling factor (k_p) and the piezoelectric constant (d₃₃) decrease with increasing amounts of NN. 0.01-0.03 mol of plate-like NaNbO₃ in 0.93 K_0.48Na_0.52NbO₃-0.07Li(Ta_0.5Nb_0.5)O₃ gives the optimum content for preparing textured ceramics by the RTGG method.     

Phase evolution, crystal structure and dielectric behavior of (1 − x)Nd(Zn0.5Ti0.5)O3 + xBi(Zn0.5Ti0.5)O3 compound ceramics

The phase evolution, crystal structure and dielectric properties of (1 − x)Nd(Zn_0.5Ti_0.5)O₃ + xBi(Zn_0.5Ti_0.5)O₃ compound ceramics (0 ≤ x ≤ 1.0, abbreviated as (1 − x)NZT-xBZT hereafter) were investigated. A pure perovskite phase was formed in the composition range of 0 ≤ x ≤ 0.05. The B-site Zn²⁺/Ti⁴⁺ 1:1 long range ordering (LRO) structure was detected by both XRD and Raman spectra in x ≤ 0.05 samples. However, this LRO structure became gradually degraded with an increase in x. The dielectric behaviors of the compound ceramic at various frequencies were investigated and correlated to its chemical composition and crystal structure. A gradually compensated τ_f value was obtained in (1 − x)NZT-xBZT microwave dielectrics at x = 0.03, which was mainly due to the dilution of dielectric constant in terms of Claussius-Mossotti differential equation.     

X-ray diffraction and dielectric studies across morphotropic phase boundary in (1 − x) [Pb(Mg0.5W0.5)O3]-xPbTiO3 ceramics

We present here the results of comprehensive X-ray diffraction and dielectric studies on several compositions of (1 − x)[Pb(Mg_0.5W_0.5)O₃]-xPbTiO₃ (PMW-xPT) solid solution across the morphotropic phase boundary. Rietveld analysis of the powder X-ray diffraction data reveals cubic (space group Fm3m) structure of PMW-xPT ceramics for the compositions with x ≤ 0.42, tetragonal (space group P4mm) structure for the compositions with x ≥ 0.72 and coexistence of the tetragonal and cubic phases for the intermediate compositions (0.46 ≤ x ≤ 0.68). Temperature dependence of the dielectric permittivity above room temperature exhibits diffuse nature of phase transitions for the compositions in the cubic and two phase region while the compositions with tetragonal structure at room temperature exhibit sharp ferroelectric to paraelectric phase transition. The PMW-xPT compositions with coexistence of tetragonal and cubic phases at room temperature exhibit two anomalies in the temperature dependence of the dielectric permittivity above room temperature. Using results of structural and dielectric studies a partial phase diagram of PMW-xPT ceramics is also presented.     

Relationships between Zr substitution for Ti and microwave dielectric properties in Mg(ZrxTi1−x)O3 ceramics

The influence of Zr substitution for Ti on the microwave dielectric properties and microstructures of the Mg(Zr_xTi_1−x)O₃(MZ_xT) (0.01 ≤ x ≤ 0.3) ceramics was investigated. The quality factors of Mg(Zr_xTi_1−x)O₃ ceramics with x = 0.01-0.05 were improved because the solid solution of a small amount of Zr⁴⁺ substitution in the B-site could increase density and grain size. An excess of Zr⁴⁺ resulted in the formation of a great deal of secondary phase that declined the microwave dielectric properties of MZ_xT ceramics. The temperature coefficient of resonant frequency (τ_f) of Mg(Zr_xTi_1−x)O₃ ceramics slightly increased with increasing Zr content, and the variation in τ_f was attributed to the formation of secondary phases.     

Study of structural, dielectric and electrical behavior of (1 − x)Ba(Fe0.5Nb0.5)O3-xSrTiO3 ceramics

Polycrystalline samples of BaFe_0.5Nb_0.5O₃ and (1 − x)Ba(Fe_0.5Nb_0.5)O₃-xSrTiO₃ [referred as BFN and BFN-ST respectively] (x = 0.00, 0.15 and 0.20) have been synthesized by a high-temperature solid-state reaction technique. The XRD patterns of the BFN and BFN-ST at room temperature show a monoclinic phase. The microstructure of the ceramics was examined by the scanning electron microscopy (SEM) and shows the polycrystalline nature of the samples with different grain sizes, which are inhomogeneously distributed through the sample surface. Detailed studies of dielectric and impedance properties of the materials in a wide range of frequency (100 Hz-5 MHz) and temperatures (30-270 °C) showed that properties are strongly temperature and frequency dependent. Complex Argand plane plot of ?″ against ?′, usually called Cole-Cole plots is used to check the polydispersive nature of relaxation phenomena in above mentioned compounds. Relaxation phenomena of non-Debye type have been observed in the BFN and BFN-ST ceramics, as confirmed by the Cole-Cole plots.     

High-dielectric-constant and low-loss microwave dielectric in the (1 − x)La(Mg0.5Ti0.5)O3-x(Ca0.8Sr0.2)TiO3 solid solution system

The microwave dielectric properties and microstructures of (1 − x)La(Mg_0.5Ti_0.5)O₃-x(Ca_0.8Sr_0.2)TiO₃ ceramics, prepared by a mixed oxide route, have been investigated. The forming of solid solutions was confirmed by the XRD patterns and the measured lattice parameters for all compositions. A near zero τ_f was achieved for samples with x = 0.5, although the dielectric properties varied with sintering temperature. The Q × f value of 0.5La(Mg_0.5Ti_0.5)O₃-0.5(Ca_0.8Sr_0.2)TiO₃ increased up to 1475 °C, after which it decreased. The decrease in dielectric properties was coincident with the onset of rapid grain growth. The optimum combination of microwave dielectric properties was achieved at 1475 °C for samples where x = 0.5 with a dielectric constant ?_r of 47.12, a Q × f value of 35,000 GHz (measured at 6.2 GHz) and a τ_f value of −4.7 ppm/°C.     

Effect of addition of Ba(W0.5Cu0.5)O3 in Pb(Mg1/3Nb2/3)O3-Pb(Zn1/3Nb2/3)O3-Pb(Zr0.52Ti0.48)O3 ceramics on the sintering temperature, electrical properties and phase transition

In this work, we report on the Pb(Mg_1/3Nb_2/3)O₃-Pb(Zn_1/3Nb_2/3)O₃-Pb(Zr_0.52Ti_0.48)O₃ (PMN-PZN-PZT) ceramics with Ba(W_0.5Cu_0.5)O₃ as the sintering aid that was manufactured in order to develop the low-temperature sintering materials for piezoelectric device applications. The phase transition, microstructure, dielectric, piezoelectric properties, and the temperature stability of the ceramics were investigated. The results showed that the addition of Ba(W_0.5Cu_0.5)O₃ significantly improved the sintering temperature of PMN-PZN-PZT ceramics and could lower the sintering temperature from 1005 to 920 °C. Besides, the obtained Ba(W_0.5Cu_0.5)O₃-doped ceramics sintered at 920 °C have optimized electrical properties, which are listed as follows: (K_p = 0.63, Q_m = 1415 and d₃₃ = 351 pC/N), and high depolarization temperature above 320 °C. These results indicated that this material was a promising candidate for high-power multilayer piezoelectric device applications.     

Complex impedance analysis of (Y2O3 + CeO2)-YCr0.5Mn0.5O3 composite NTC ceramics

Ceramic compositions based on (aY₂O₃ + bCeO₂)-0.4YCr_0.5Mn_0.5O₃ (a + b = 0.6) were prepared by conventional solid state reaction at 1200 °C, and sintered under air atmosphere at 1600 °C. For 0 ≤ a < 0.6, XRD patterns have shown that the major phases presented in the calcined powders are Y₂O₃, CeO₂ and orthorhombic perovskite YCr_0.5Mn_0.5O₃ phase, respectively. SEM and EDAX observations confirm the YCr_0.5Mn_0.5O₃ phases mostly exist at the grain, whereas the Y₂O₃ and CeO₂ phases mainly exist at the grain boundaries. Complex impedance analysis shows that, for 0 < a ≤ 0.6, single semicircular arc whose shape does not show any change with temperature. Nevertheless, for a = 0, two overlapping semicircular arcs are observed at and above 300 °C. The grain boundary properties exhibit thermistor parameters with a negative temperature coefficient characteristic. The relaxation behavior and conduction for the grain boundary could be due to a space-charge relaxation mechanism and oxygen vacancies, respectively.     

Microstructure, dielectric and ferroelectric properties of 0.94Bi0.5Na0.5TiO3-0.06BaTiO3 (NBTB) and 0.05BiFeO3-0.95NBTB ceramics: Effect of sintering atmosphere

0.94Bi_0.5Na_0.5TiO₃-0.06BaTiO₃ (NBTB) and 0.05BiFeO₃-0.95NBTB (BF-doped NBTB) lead-free ceramics were prepared by solid state reaction method. The ceramics were sintered at 1180 °C for 2 h in O₂ and N₂. All ceramics exhibited a single phase of perovskite structure. Relative amount of tetragonal phase was related to the sintering atmospheres. Both grain size and shape were influenced by the sintering atmospheres. Sintering the ceramics in N₂ weakened their dielectric anomalies corresponding to the transition from ferroelectric phase to the so-called “intermediate phase”. When the NBTB and BF-doped NBTB ceramics were sintered in N₂, their maximum dielectric constant and the degree of diffuseness of the transition from the “intermediate phase” to paraelectric phase increased, but their Curie temperatures decreased. The difference in dielectric properties of the ceramics sintered in different atmospheres was closely related to the difference in oxygen vacancy concentration. The correlation between ferroelectric properties and sintering atmospheres is associated with a competing effect among oxygen vacancy concentration, A-site vacancy concentration and percentage of tetragonal phase.     

Synthesis and electrochemical performance of Li(Ni0.8Co0.15Al0.05)0.8(Ni0.5Mn0.5)0.2O2 with core-shell structure as cathode material for Li-ion batteries

The core-shell structure cathode material Li(Ni_0.8Co_0.15Al_0.05)_0.8(Ni_0.5Mn_0.5)_0.2O₂ (LNCANMO) was synthesized via a co-precipitation method. Its applicability as a cathode material for lithium ion batteries was investigated. The core-shell particle consists of LiNi_0.8Co_0.15Al_0.05O₂ (LNCAO) as the core and a LiNi_0.5Mn_0.5O₂ as the shell. The thickness of the LiNi_0.5Mn_0.5O₂ layer is approximately 1.25 μm, as estimated by field emission scanning electron microscopy (FE-SEM). The cycling behavior between 2.8 and 4.3 V at a current rate of 18 mA g⁻¹ shows a reversible capacity of about 195 mAh g⁻¹ with little capacity loss after 50 cycles. High-rate capability testing shows that even at a rate of 5 C, a stable capacity of approximately 127 mAh g⁻¹ is retained. In contrast, the capacity of LNCAO rapidly decreases in cyclic and high rate tests. The observed higher current rate capability and cycle stability of LNCANMO can be attributed to the lower impedance including charge transfer resistance and surface film resistance. Differential scanning calorimetry (DSC) indicates that LNCANMO had a much improved oxygen evolution onset temperature of approximately 251 °C, and a much lower level of exothermic-heat release compared to LNCAO. The improved thermal stability of the LNCANMO can be ascribed to the thermally stable outer shell of LiNi_0.5Mn_0.5O₂, which suppresses oxygen release from the host lattice and not directly come into contact with the electrolyte solution. In particular, LNCANMO is shown to exhibit improved electrochemical performance and is a safe material for use as an electrode for lithium ion batteries.     

Crystal structure and dielectric properties of La(Mg0.5Ti0.5)O3-Ca0.8Sm0.4/3TiO3 solid solution system at microwave frequencies

The crystal structure and the dielectric properties of (1 − x)La(Mg_0.5Ti_0.5)O₃-xCa_0.8Sm_0.4/3TiO₃ ceramics have been investigated. Ca_0.8Sm_0.4/3TiO₃ was employed as a τ_f compensator and was added to La(Mg_0.5Ti_0.5)O₃ to achieve a temperature-stable material. The formation of (1 − x)La(Mg_0.5Ti_0.5)O₃-xCa_0.8Sm_0.4/3TiO₃ solid solutions were confirmed by the XRD results and the measured lattice parameters for all compositions. The dielectric properties are strongly correlated to the sintering temperature and the compositional ratio of the specimens. Although the ?_r of the specimen could be boosted by increasing the amount of Ca_0.8Sm_0.4/3TiO₃, it would instead render a decrease in the Q × f. The τ_f value is strongly correlated to the compositions and can be controlled by the existing phases. A new microwave dielectric material 0.45La(Mg_0.5Ti_0.5)O₃-0.55Ca_0.8Sm_0.4/3TiO₃, possessing a fine combination of microwave dielectric properties with an ?_r of 47.83, a Q × f of 26,500 GHz (at 6.2 GHz) and a τ_f of −1.7 ppm/°C, is proposed as a very promising candidate material for today's 3G applications.     

Dielectric properties and crystal structure of La(Mg1/2Ti1/2)O3 ceramics with Mg substituted by Co

Solid solutions of (1 − x)La(Co_1/2Ti_1/2)O₃-xLa(Mg_1/2Ti_1/2)O₃ were used to prepare La(Mg_1−xCo_x)_1/2Ti_1/2O₃ using solid-state synthesis. X-ray diffraction patterns of the sintered samples revealed single phase formation. A maximum density of 6.01 g/cm³ was obtained for La(Mg_1−xCo_x)_1/2Ti_1/2O₃ (x = 1) ceramics sintered at 1375 °C for 4 h. The maximum values of the dielectric constant (?_r = 29.13) and the quality factor (Q × f = 80,000 GHz) were obtained for La(Mg_1−xCo_x)_1/2Ti_1/2O₃ with 1 wt% ZnO additive sintered at 1375 °C for 4 h. The temperature coefficient of resonant frequency τ_f was −59 ppm/°C for x = 0.3.     

Relationship between structure and properties in high-temperature Bi(Al0.5Fe0.5)O3-PbTiO3 piezoelectric ceramics

Ceramic samples of xBi(Al_0.5Fe_0.5)O₃-(1 − x)PbTiO₃ (BAF-PT, x = 0.05-0.5) solid solutions were fabricated using the conventional solid state reaction method. X-ray diffraction analysis revealed that all compositions can form single perovskite phase with tetragonal symmetry. The relationship between the tetragonal lattice parameters, tetragonality c/a, cell volume, and ferro-piezoelectric characterization as a function of x was systematically investigated. The BAF modification can effectively improve the poling condition at a proper BAF content. A combination of piezoelectric constant of d₃₃ (50-60 pC/N), electromechanical planar coupling coefficients of k_p (20.3-22.5%), and high Curie temperature T_c (>478 °C) suggested that BAF-PT could be a good candidate for high-temperature piezoelectric applications.     

Properties of praseodymium-doped bismuth potassium titanate (Bi0.5K0.5TiO3) synthesised using the soft combustion technique

Bismuth potassium titanate (Bi_0.5K_0.5TiO₃; BKT) and praseodymium-doped BKT (Bi_0.5(1−x)Pr_xK_0.5TiO₃; BPKT) powders were synthesised using the soft combustion technique. Fine particles of 10-100 nm of BKT and BPKT were produced. A single phase BKT was obtained with a minimum of 0.5 mol of glycine. Various compounds of Bi_0.5(1−x)Pr_xK_0.5TiO₃ where x = 0.01, 0.03, 0.05, 0.10, 0.15 and 0.20 were prepared. Pure BKT and BPKT powders were obtained after calcination at 800 °C for 3 h. After sintering at 1050 °C for 5 h, pure BKT and BPKT pellets were obtained for x = 0 and 0.01. However, for BPKT with x = 0.03, 0.05, 0.10, 0.15 and 0.20, a minor amount of Bi₄Ti₃O₁₂ (BIT) secondary phase was present after sintering at 1050 °C for 5 h. The crystallite size and grain size of all the samples followed similar trends, first increasing from x = 0 (undoped BKT) to x = 0.05 and then decreasing above x = 0.05. Among the undoped and doped samples, BPKT with x = 0.05 had the highest dielectric properties (?_r = 713.87) due to its large crystallite size (68.66 nm), large grain size (∼435 nm) and high relative density (93.39%).     

Characterization of sol-gel synthesised lead-free (1 − x)Na0.5Bi0.5TiO3-xBaTiO3-based ceramics

The crystal structure, microstructure, dielectric and ferroelectric properties of (1 − x)Na_0.5Bi_0.5TiO₃-xBaTiO₃ ceramics with x = 0, 0.03, 0.05, 0.07 and 0.1 are investigated. A structural variation according to the system composition was investigated by X-ray diffraction (XRD) analyses. The results revealed that the synthesis temperature for pure perovskite phase powder prepared by the present sol-gel process is much lower (800 °C), and a rhombohedral-tetragonal morphotropic phase boundary (MPB) is found for x = 0.07 composition which showing the highest remanent polarization value and the smallest coercive field. The optimum dielectric and piezoelectric properties were found with the 0.93Na_0.5Bi_0.5TiO₃-0.07BaTiO₃ composition. The piezoelectric constant d₃₃ is 120 pC/N and good polarization behaviour was observed with remanent polarization (P_r) of 12.18 pC/cm², coercive field (E_c) of 2.11 kV/mm, and enhanced dielectric properties ?_r > 1500 at room temperature. The 0.93Na_0.5Bi_0.5TiO₃-0.07BaTiO₃-based ceramic is a promising lead-free piezoelectric candidate for applications in different devices.