Magnetic Anomalies and Electronic Structure of Ce<Subscript>2</Subscript>Cu<Subscript>2</Subscript>Mg and Ce<Subscript>2</Subscript>Pd<Subscript>2</Subscript>Mg

The intermetallic compounds RE ₂Cu₂Mg and RE ₂Pd₂Mg (RE=La, Ce) were prepared and characterized by magnetic susceptibility and heat-capacity measurements. They crystallize with an ordered U₃Si₂ type structure (space group P4/mbm) and the cerium compounds contain stable trivalent cerium ions, which undergo antiferromagnetic ordering at ∼7.5 and ∼4 K, respectively. In high magnetic fields Ce₂Cu₂Mg exhibits spin reorientation with critical field strength of 40 kOe at 5 K. The data are compared to the non-magnetic isotypic compounds La₂ T ₂Mg (T=Cu, Ni, Pd) and to the already reported intermediate valent Ce₂Ni₂Mg.     

Catalytic combustion of methane over Pt and PdO-supported CeO<Subscript>2</Subscript>–ZrO<Subscript>2</Subscript>–Bi<Subscript>2</Subscript>O<Subscript>3</Subscript>/γ-Al<Subscript>2</Subscript>O<Subscript>3</Subscript> catalysts

Catalytic combustion of methane was investigated on Pt and PdO-supported CeO₂–ZrO₂–Bi₂O₃/γ-Al₂O₃ catalysts prepared by a wet impregnation method in the presence of polyvinylpyrrolidone. The catalysts were characterized by X-ray fluorescence analysis, X-ray powder diffraction, X-ray photoelectron spectra, transmission electron microscopy, and BET specific surface area measurements. The Pt/CeO₂–ZrO₂–Bi₂O₃/γ-Al₂O₃ and PdO/CeO₂–ZrO₂–Bi₂O₃/γ-Al₂O₃ catalysts were selective for the total oxidation of methane into carbon dioxide and steam, and no by-products such as HCHO, CO, and H₂ were obtained. The catalytic activities of the PdO/CeO₂–ZrO₂–Bi₂O₃/γ-Al₂O₃ catalysts were relatively higher than those of the Pt-supported catalysts, due to the facile re-oxidation of metallic Pd into PdO based on lattice oxygen supplied from the CeO₂–ZrO₂–Bi₂O₃ bulk. A decrease in the calcination temperature during the preparation process was found to be effective in enhancing the specific surface area of the catalysts, whereby particle agglomeration was inhibited. Optimization of the PdO amount and calcination temperature enabled complete oxidation of methane at temperatures as low as 320 °C on the 11.6 wt% PdO/CeO₂–ZrO₂–Bi₂O₃/γ-Al₂O₃ catalyst prepared at 400 °C.     

Syntheses and proton conductivity of mesoporous Nd<Subscript>2</Subscript>O<Subscript>3</Subscript>–SiO<Subscript>2</Subscript> and NdOCl–SiO<Subscript>2</Subscript> composites

Two mesoporous oxide composites of Nd₂O₃–SiO₂ and NdOCl–SiO₂ were synthesized using SBA-15 as a template and neodymium nitrate or neodymium chloride as a precursor. The porous Nd₂O₃–SiO₂ with a SBA-15-like structure has amorphous walls and the porous NdOCl–SiO₂ with a replicated structure of SBA-15 has crystalline walls. These porous materials were characterized by X-ray diffraction, transmission electron microscopy and nitrogen adsorption/desorption. They exhibited significant proton conductivities in the presence of moisture at low temperatures and the highest conductivity observed was 4.55 × 10⁻⁴ S/cm at 47 °C in wet air (RH = 28.6%).     

Crystallization and microstructural evolution of MgO–Al<Subscript>2</Subscript>O<Subscript>3</Subscript>–SiO<Subscript>2</Subscript>–TiO<Subscript>2</Subscript>–La<Subscript>2</Subscript>O<Subscript>3</Subscript> glass-ceramics

Crystallization and microstructure of glasses with the molar compositions 1MgO·1.2Al₂O₃·2.8SiO₂·1.2TiO₂·xLa₂O₃ (x = 0.1 and 0.4) were thermally treated at different temperatures in the range from 950 to 1250 °C and then analyzed by X-ray diffraction and scanning electron microscopy, in combination with energy-dispersive X-ray spectroscopy and electron backscatter diffraction. It was found that the microstructure is first homogeneous with the precipitation of randomly distributed crystals and then indialite domains with embedded perrierite and rutile crystals are formed. For higher temperatures or prolonged times, more domains appear and expand into the bulk of the sample. Finally, the entire sample consists of the indialite domains and the boundaries that are enriched in rutile, perrierite, and magnesium aluminotitanate. Nevertheless, very distinct differences are observed between the samples with different La₂O₃ concentrations. For the sample with x = 0.4, the domains were detected at lower temperatures, while the quantity and size of the domains increase faster due to the promoted precipitation of indialite. For the sample with x = 0.1, in addition to the domain boundaries, secondary boundaries between the “regions” (assemblages of the domains) are observed in a larger length scale. The average size of the crystalline phases found between the “regions” is larger than that typically observed at the domain boundaries. The sizes of the crystals at the boundaries decrease with higher concentrations of La₂O₃, and the crystals (especially perrierite) within the domains become larger, resulting in a more homogeneous microstructure. This results in better dielectric properties, i.e., much higher quality factor for the sample with x = 0.4 in comparison to that with x = 0.1 after heat-treatment at 1150 or 1250 °C.     

BaFe<Subscript>12</Subscript>O<Subscript>19</Subscript> films produced from BaFe<Subscript>2</Subscript>O<Subscript>4</Subscript>/α-Fe<Subscript>2</Subscript>O<Subscript>3</Subscript> heterostructures

BaFe₁₂O₁₉ hexaferrite films have been produced on thermally oxidized single-crystal silicon (SiO₂/Si) substrates by sequential ion-beam sputtering of BaFe₂O₄ and α-Fe₂O₃ targets in an argon-oxygen atmosphere. Their crystal structure has been studied, and the origin of the impurity phases forming during heat treatment has been identified. The results show that heat treatment may lead to the formation of eutectic melts. As a result, the hexaferrite films may contain spherulites.     

Structure and properties of CaF<Subscript>2</Subscript>–B<Subscript>2</Subscript>O<Subscript>3</Subscript> glasses

FTIR spectroscopy has been employed to investigate the structure of CaF₂–B₂O₃ glasses. It is proposed that CaF₂ partially modifies the borate network forming \textCa _{1 / 2} ²⁺ [\textBO _{3 / 2} \textF] ^- {\text{Ca}}_{ 1 / 2}^{ 2+ } [{\text{BO}}_{ 3 / 2} {\text{F]}}^{ - } units. The rest of CaF₂ is assumed to build an amorphous network formed of CaF₄ tetrahedra. Analysis of density and molar volume revealed that the volume of CaF₄ tetrahedron in the studied glasses is slightly greater than that in the crystalline form. Data of density, molar volume, and electric conductivity have been correlated with the glass structure. As far as the authors know, CaF₂–B₂O₃ glasses are investigated for the first time.     

Superconducting Bands Stabilizing Superconductivity in YBa<Subscript>2</Subscript>Cu<Subscript>3</Subscript>O<Subscript>7</Subscript> and MgB<Subscript>2</Subscript>

It is shown that the ceramic superconductor YBa₂Cu₃O₇ as well as the superconducting intermetallic compound MgB₂ possesses a narrow, partly filled “superconducting band” with Wannier functions of special symmetry in their band structures. This result corroborates previous observations about the band structures of numerous superconductors and non-superconductors showing that evidently superconductivity is always connected with such superconducting bands. These findings are interpreted in the framework of a nonadiabatic extension of the Heisenberg model. Within this new group-theoretical model of correlated systems, Cooper pairs are stabilized by a nonadiabatic mechanism of constraining forces effective in narrow superconducting bands. The formation of Cooper pairs in a superconducting band is mediated by the energetically lowest boson excitations in the considered material that carry the crystal-spin angular momentum 1⋅ℏ. These crystal-spin-1 bosons are proposed to determine whether the material is a conventional low-T _c or a high-T _c superconductor. This interpretation provides the electron–phonon mechanism that enters the BCS theory in conventional superconductors.     

Synthesis and characterization of TiO<Subscript>2</Subscript>–NiO and TiO<Subscript>2</Subscript>–WO<Subscript>3</Subscript> nanocomposites

TiO₂–NiO and TiO₂–WO₃ nanocomposites were prepared by hydrothermal and surface modification methods. The samples were analyzed using X-ray diffraction, Scanning Electron Microscope images, Transmission Electron Microscope, Energy dispersive analysis, Zeta potential, Electrophoretic mobility and Photocatalysis activity measurement. XRD data sets of TiO₂–NiO, TiO₂–WO₃ powder nanocomposite have been studied for the inclusion of NiO, WO₃ on the anatase-rutile mixture phase of TiO₂ by Rietveld refinement. The cell parameters, phase fraction, the average grain size, strain and bond lengths between atoms of individual phases have been reported in the present work. Shifted positional co-ordinates of individual atoms in each phase have also been observed.     

Atomistic structure and energetics of interface between Mn-doped γ-Ga<Subscript>2</Subscript>O<Subscript>3</Subscript> and MgAl<Subscript>2</Subscript>O<Subscript>4</Subscript>

The interface between an Mn-doped γ-gallium oxide (Ga₂O₃) thin film and an MgAl₂O₄ (001) substrate has been investigated using high-resolution transmission electron microscopy (HRTEM), high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM), and first-principles calculations. A high-quality Mn-doped γ-Ga₂O₃ film with a defective spinel structure has been epitaxially grown by pulsed laser deposition. The γ-Ga₂O₃ crystal shows an uniform tetragonal distortion with a tetragonality of 1.05 throughout the film thickness of 75 nm. HRTEM and HAADF-STEM observations reveal that the γ-Ga₂O₃ and MgAl₂O₄ crystals form a coherent interface without any interfacial layers or precipitates. The atomistic structure and energies are theoretically evaluated for the interfaces with two types of termination plane, i.e., Mg- and Al₂O₄-termination of MgAl₂O₄. The cation sublattice is found to be continuous for both interfaces despite the defective spinel structure of Mn-doped γ-Ga₂O₃ with some vacant cation sites. The Al₂O₄-termination shows a lower interfacial energy than the Mg-termination under most conditions of the chemical potentials. This behavior is attributed to the energetic preference of the Mn–Al₂O₄ local configuration at the interface.     

High-damping and high-rigidity composites of Al<Subscript>2</Subscript>TiO<Subscript>5</Subscript>–MgTi<Subscript>2</Subscript>O<Subscript>5</Subscript> ceramics and acrylic resin

High-damping materials are widely used in engineering fields. In order to increase the precision of vibration control to different levels, high-damping materials with high-rigidity are required. This study attempts to develop a new high-damping high-rigidity material using ductile ceramics based on the Al₂TiO₅–MgTi₂O₅ system, which has many continuous microcracks along the grain boundaries. Ductile ceramics have high internal friction (Q ⁻¹ = 0.01–0.037), but very low rigidity (<10 GPa). The rigidity of Al₂TiO₅–MgTi₂O₅ ceramics was improved by combining them with a polymer such as acrylic resin. The Young’s modulus and internal friction of the composites of Al₂TiO₅–MgTi₂O₅ ceramics and acrylic resin are investigated. They show high-damping capacity (Q ⁻¹ = 0.03–0.04) with high rigidity (E = 50–60 GPa), and their properties depend on those of the polymer. Thus, the composites fabricated using the above method can serve as high-damping high-rigidity materials.     

Variable—Range hopping in Fe<Subscript>2</Subscript>O<Subscript>3</Subscript>-Bi<Subscript>2</Subscript>O<Subscript>3</Subscript>-K<Subscript>2</Subscript>B<Subscript>4</Subscript>O<Subscript>7</Subscript> glasses

The dc conductivity of the glasses in the Fe₂O₃-Bi₂O₃-K₂B₄O₇ system was studied at temperatures between 223 and 393 K. At temperatures from 300 to 223 K, T^–1/4 (T is temperature) dependence of the conductivity was found, however, both Mott variable-range hopping and Greaves intermediate range hopping models are found to be applicable. Mott and Greaves parameters analysis gave the density of states at Fermi level N (E_F) = 3.13 × 10²⁰–21.01 × 10²⁰ and 1.93 × 10²¹–16.39 × 10²¹ cm^–3eV^–1 at 240 K, respectively. The variable-range hopping conduction occurred in the temperature range T = 300–223 K, since W_D was found to be large (W_D = 0.08–0.14 eV for these glasses) and dominated the conduction at T < 300 K.     

Lewis and Brønsted acids in super-acid catalyst SO<Subscript>4</Subscript><Superscript>2−</Superscript>/ZrO<Subscript>2</Subscript>–SiO<Subscript>2</Subscript>

Super-acid catalyst, SO₄ ^2?/ZrO₂–SiO₂, with high zirconium loading was synthesized and the nature of the surface acid was investigated by FT-IR of pyridine adsorption. With the increasing ZrO₂ content, the Lewis and Brønsted acid sites increased and reached the maximum when Zr/Si (molar ratio) = 1.3. The sample with Zr/Si = 1.3 showed the strongest IR adsorption band in the S=O stretching region (1,300–1,400 cm^?1). Pyrosulfate and monosulfate species existed on the surface of the catalysts and the acidic strength could be enhanced by induction effect of their S=O groups. And there were two kinds of Brønsted acid sites on the surface of the catalysts.     

Crystal Structure of Uranyl Malonate Trihydrate [UO<Subscript>2</Subscript>(OOC)<Subscript>2</Subscript>CH<Subscript>2</Subscript>(H<Subscript>2</Subscript>O)]·2H<Subscript>2</Subscript>O

Single crystals of [UO₂(OOC)₂CH₂(H₂O)]·2H₂O (I) were prepared by recrystallization of finely crystalline uranyl malonate trihydrate under hydrothermal conditions. The crystal structure of I consists of electroneutral [UO₂(OOC)₂CH₂(H₂O)]_n layers and water molecules located between them. The uranium coordination number is 7. The uranium coordination polyhedron is a distorted pentagonal bipyramid with the oxygen atoms of the uranyl group in the apices. The equatorial plane is occupied by four O atoms of three malonate ligands and the water molecule. The malonate anion is coordinated in the bidentate fashion to one uranyl ion to form a six-membered ring and in the monodentate fashion to two other uranyl ions.     

Phase equilibria in the system “CaAl<Subscript>2</Subscript>Si<Subscript>3</Subscript>O<Subscript>10</Subscript>”-Na<Subscript>2</Subscript>Al<Subscript>2</Subscript>Si<Subscript>3</Subscript>O<Subscript>10</Subscript>-H<Subscript>2</Subscript>O

The phase equilibria in the “CaAl₂Si₃O₁₀”-Na₂Al₂Si₃O₁₀-H₂O system are analyzed using structural and thermal analysis data, and the ideal gonnardite structure is modeled. The results suggest that, to ensure a better correlation with the structures of the zeolites in this series, a new structural model of the gonnardite-based solid solution must be selected, with the structure rotated through 45° about the c axis in the ab plane.     

Investigation of solid solution of ZrP<Subscript>2</Subscript>O<Subscript>7</Subscript>–Sr<Subscript>2</Subscript>P<Subscript>2</Subscript>O<Subscript>7</Subscript>

In this study, ZrP₂O₇ was synthesized by the solid state reaction of ZrO₂ and NH₄H₂PO₄ at 900 °C. Then, in set 1; 10, 5, 1, 0.5, 0.1, 0.05, 0.03% previously prepared Sr₂P₂O₇ were doped into ZrP₂O₇, and Sr₂P₂O₇ slightly affect the unit cell parameter of cubic ZrP₂O₇ (a = 8.248(6)–8.233(8) Å). The reverse of this process was also applied to Sr₂P₂O₇ system (set 2). ZrP₂O₇ changes the unit cell parameters of orthorhombic Sr₂P₂O₇ in between a = 8.909(5)–8.877(5) Å, b = 13.163(3)–13.12(1) Å, and c = 5.403(2)–5.386(4) Å. Analysis of the vibrations of the P₂O ₇ ^4? ion and approximate band assignments for IR and Raman spectra are also reported in this work. Some coincidences in infrared and Raman spectra both sets were found and strong P–O–P bands were observed. Surface morphology, EDX analysis, and thermoluminescence properties of both sets were given the first time in this paper.     

Kinetics of Thermal Transformation of Mg<Subscript>3</Subscript>(PO<Subscript>4</Subscript>)<Subscript>2</Subscript> · 8H<Subscript>2</Subscript>O to Mg<Subscript>3</Subscript>(PO<Subscript>4</Subscript>)<Subscript>2</Subscript>

The kinetics of thermal dehydration of Mg₃(PO₄)₂ · 8H₂O was investigated using thermogravimetry at four different heating rates. The activation energies of the dehydration step of Mg₃(PO₄)₂ · 8H₂O were calculated through the isoconversional Ozawa and Kissinger-Akahira-Sunose (KAS) methods and iterative methods, which were found to be consistent and indicate a single mechanism. The possible conversion function of the dehydration reaction for Mg₃(PO₄)₂ · 8H₂O has been estimated through the Coats and Redfern integral equation, and a better kinetic model such as random nucleation of the “Avrami–Erofeev equation (A _3/2 model)” was found. The thermodynamic functions (ΔH*, ΔG*, and ΔS*) of the dehydration reaction are calculated by the activated complex theory and indicate that it is a non-spontaneous process when the introduction of heat is not connected.     

Crystal structure of a Np(V) sesquioxalate,Na<Subscript>4</Subscript>(NpO<Subscript>2</Subscript>)<Subscript>2</Subscript>(C<Subscript>2</Subscript>O<Subscript>4</Subscript>)<Subscript>3</Subscript>·2H<Subscript>2</Subscript>O

The crystal structure of a previously unknown Np(V) sesquioxalate, Na₄(NpO₂)₂(C₂O₄)₃·2H₂O was studied. The crystal structure consists of neptunyl(V) cations, sodium cations, oxalate anions, and water molecules of crystallization. Neptunyl(V) cations and oxalate ions form anionic chains [(NpO₂)₂(C₂O₄)₃] _n ^4n? . The coordination polyhedron (CP) of Np (pentagonal bipyramid) contains two apical “yl” oxygen atoms and five equatorial O atoms of three oxalate ions. The CP of Na(1) and Na(2) cations are combined through the common edges into zigzag chains in the [010] direction. Two independent oxalate ions are tridentate and tetradentate ligands.     

Microstructure,interfaces and creep behaviour of Al<Subscript>2</Subscript>O<Subscript>3</Subscript>–Sm<Subscript>2</Subscript>O<Subscript>3</Subscript> (ZrO<Subscript>2</Subscript>) eutectic ceramic composites

New compositions in the melt-grown eutectic ceramics field are investigated for thermomechanical applications. This paper is focused on the Al₂O₃–Sm₂O₃–(ZrO₂) system. The studied compositions give rise to interconnected microstructures without anisotropy along the growth direction. At variance with the binary eutectic Al₂O₃–SmAlO₃, the homogeneity of the microstructure of the Al₂O₃–SmAlO₃–ZrO₂ ternary eutectic is less sensitive to the growth rate. Interfaces between the alumina and perovskite phases are investigated by high-resolution transmission electron microscopy (TEM). They are semi-coherent. In stepped interfaces, the facets are parallel to dense planes of each phase. The steps have a dislocation character and may accommodate both misfits. The ternary eutectic displays a very good creep behaviour with strain rates very close to those obtained on other previously studied eutectics in the Al₂O₃–RE₂O₃(RE = Y, Gd, Er)–ZrO₂ systems. The deformation micromechanisms are analysed by TEM in the three eutectic phases. After creep, dislocations are present in every phase. The activation of unusual slip systems (pyramidal slip in the alumina phase) shows that high local stresses can be reached. The presence of dislocation networks with low energy configurations is consistent with predominance of dislocation climb processes controlled by bulk diffusion.     

Preparation and characterization of Li<Subscript>2</Subscript>O–CaO–Al<Subscript>2</Subscript>O<Subscript>3</Subscript>–P<Subscript>2</Subscript>O<Subscript>5</Subscript>–SiO<Subscript>2</Subscript> glasses as bioactive material

The aim of the present investigation was to study the role of Al₂O₃ in the Li₂O–CaO–P₂O₅–SiO₂ bioactive glass for improving the bioactivity and other physico-mechanical properties of glass. A comparative study on structural and physico-mechanical properties and bioactivity of glasses were reported. The structural properties of glasses were investigated by X-ray diffraction, Fourier transform infrared spectrometry, scanning electron microscopy and the bioactivity of the glasses was evaluated by in vitro test in simulated body fluid (SBF). Density, compressive strength, Vickers hardness and ultrasonic wave velocity of glass samples were measured to investigate physical and mechanical properties. Results indicated that partial molar replacement of Li₂O by Al₂O₃ resulted in a significant increase in mechanical properties of glasses. In vitro studies of samples in SBF had shown that the pH of the solution increased after immersion of samples during the initial stage and then after reaching maxima it decreased with the increase in the immersion time. In vitro test in SBF indicated that the addition of Al₂O₃ up to 1.5 mol% resulted in an increase in bioactivity where as further addition of Al₂O₃ caused a decrease in bioactivity of the samples. The biocompatibility of these bioactive glass samples was studied using human osteoblast (MG-63) cell lines. The results obtained suggested that Li₂O–CaO–Al₂O₃–P₂O₅–SiO₂-based bioactive glasses containing alumina would be potential materials for biomedical applications.     

Compositional dependence of the structural and dielectric properties of Li<Subscript>2</Subscript>O–GeO<Subscript>2</Subscript>–ZnO–Bi<Subscript>2</Subscript>O<Subscript>3</Subscript>–Fe<Subscript>2</Subscript>O<Subscript>3</Subscript> glasses

(10Li₂O–20GeO₂–30ZnO–(40-x)Bi₂O₃–xFe₂O₃ where x = 0.0, 3, 6, and 9 mol%) glasses were prepared. A number of studies, viz. density, differential thermal analysis, FT-IR spectra, DC and AC conductivities, and dielectric properties (constant ε′, loss tan δ, AC conductivity, σ _ac, over a wide range of frequency and temperature) of these glasses were carried out as a function of iron ion concentration. The analysis of the results indicate that, the density and molar volume decrease with an increasing of iron content indicates structural changes of the glass matrix. The glass transition temperature T _g and onset of crystallization temperature T _x increase with the variation of concentration of Fe₂O₃ referred to the growth in the network connectivity in this concentration range, while glass-forming ability parameter ΔT decrease with increase Fe₂O₃ content, indicates an increasing concentration of iron ions that take part in the network-modifying positions. The FT-IR spectra evidenced that the main structural units are BiO₃, BiO₆, ZnO₄, GeO₄, and GeO₆. The structural changes observed by varying the Fe₂O₃ content in these glasses and evidenced by FTIR investigation suggest that the iron ions play a network modifier role in these glasses while Bi₂O₃, GeO₂, and ZnO play the role of network formers. The temperature dependence of DC and AC conductivities at different frequencies was analyzed using Mott’s small polaron hopping model and, the high temperature activation energies have been estimated and discussed. The dielectric constant and dielectric loss increased with increase in temperature and Fe₂O₃ content.