Investigations of the copper isotope effect in oxygen-deficient YBa2Cu3O7−δ

We present data on the copper isotope effect (⁶³Cu-⁶⁵Cu), C_u =-nT_c/nm_Cu, for two isotopic pairs of oxygen-deficient YBa₂Cu₃O_7–, where varies between 0.06 and 0.52. _Cu is below 0.01 at =0.06 (fully oxygenated), it takes values between –0.14 and –0.34 in the 60 K plateau. Larger negative values of _Cu are observed away from the plateau. The dependence of _Cu is similar to that of the pressure effect dnT_c/dP.     

Preferentially orientated precipitation in MnTiO3 single crystals

Preferentially orientated precipitation of -TiO₂ (rutile) needles in single crystals of MnTiO₃ grown by a floating-zone method under a controlled atmosphere of oxygen fugacity was studied. Optical microscopy and X-ray analysis revealed that the orientation relation between the -TiO₂ precipitates and the MnTiO₂ matrix is: {000 1}MnTiO₃// {111}-TiO₂ and 11¯20MnTiO₃// 110-TiO₂. The precipitation phenomenon was explained by introducing a nucleation and growth mechanism which was experimentally supported by heat treating experiments.     

The athermal α → ω transformation in Zr-2 at% Nb alloy

The athermal transformation in Zr-2 at.% Nb alloy has been investigated by transmission electron microscopy. Analysis of the selected-area diffraction pattern has shown that the orientation relationships between the omega and the parent-phase in quenched Zr-2 at.% Nb alloy are the same as have been previously observed for the reaction in pure zirconium. Thus it was deduced that the direct transition has taken place in the alloy during cooling. The-originated -particles were visualized using the dark-field technique. The formation of the athermal omega in the-region of-stabilized Zr-Nb alloy is discussed in terms of the relative positions of the free energy equilibrium curvesT ₀ ,T ₀ ,T ₀ and the correspondingM _s ,M _s andT _s start curves. It is concluded that the omega phase can occur over a much wider range of alloy compositions than is usually recognized on the basis of transformation data.     

Similarity solutions in axisymmetric mixed-convection boundary-layer flow

The similarity equations for mixed-convection axisymmetric boundary-layer flow are considered. The equations involve a buoyancy parameter and a curvature parameter . The equations are solved numerically and it is found that for large , and of O(1), an asymptotic solution is approached, the nature of which is discussed. When is also large, of O(^1/4), the problem, at leading order, becomes independent of the mainstream and the free-convection limit is obtained. This problem is also discussed, including the behaviour for large values of ₀, the free-convection curvature parameter. For < 0 we find that the solution can be continued past the point where the wall heat transfer becomes zero (where previous mixed-convection similarity solutions in plane geometry were terminated) with the solution ending as 0^–. The nature of this limit is also discussed. For < 0 it is also found that there are solutions only in _b = < 0 with two branches of solution bifurcating out of = _b , and values of _b are computed for a range of . The behaviour of the solution for large values of the curvature parameter , and of O(1), is discussed where it is shown that the solution proceeds in inverse powers of log .     

Experimental evaluation of relative mode parameters in the irregular earth-to-ionosphere waveguide

Conclusions A model for representing the propagation of superlong waves was selected. Certain relative mode parameters ()₁, ()₂, ()₃, (V)₁, (V)₂, (V)₃, C₁, C₂, and C₃ can be used in order to account for the time-measurement error produced as a resuit of the double-mode signal propagation, to determine in a semiempirical manner the ionosphere's effective reflection height at night and in the daytime, to calculate and apply signal-propagation corrections which take into account phase velocity changes due to variations in the ionosphere height from day to day, and to calculate the fields of transition paths.Translated from Izmeritel'naya Tekhnika, No. 8, pp. 75–78, August, 1974.     

Methanation of carbon deposited directly from CO2 on rhodium-bearing activated magnetite

Methanation reactivity was studied for the surface carbon deposited from CO₂ on the surface of Rh-bearing activated magnetite. The most active material (Rh=0.83 wt %) for methanation was prepared by the impregnation method at 60°C and showed 98% conversion at 300°C. The surface carbon was composed of elemental carbon (-carbon) and polymerized carbon (-carbon), the proportion being dependent on the density of carbon deposited. In temperature-programmed surface reaction, the extent of conversion of the - and -carbon to CH₄ was 0.34 (-carbon) and 0.53 (-carbon), respectively, and the total conversion was 0.87. This result indicates that not only elemental carbon but polymerized carbon (-carbon) could be converted to CH₄ on the Rh-bearing activated (-carbon) magnetite, whereas -carbon is not hydrogenated on activated magnetite.     

Thermal Expansion and Isothermal Compressibility of TlIn1 – xNdxSe2 (0 ≤ x≤ 0.08) Crystals

The thermal expansion coefficient () and isothermal compressibility ( _T ) of TlIn_{1 – x} Nd _x Se₂(0 x 0.08) crystals were measured between 77 and 400 K. In the range 77–160 K, both and _T increase with temperature, the increase in being much steeper. At higher temperatures, and _T change very little. The observed composition dependences of and _T are interpreted in terms of energy-band structure.     

Complex microstructural changes in as-cast eutectoid Zn-Al alloy

Phase transformations and microstructural changes of an as-cast eutectoid Zn-Al alloy (ZnAl₂₂Cu₂) were investigated during isothermal holding. The typical dendritic structures consisted of _s phase as a core with the edge of decomposed _s phase and decomposed _s in the interdendritic regions. A series of complex phase transformations was observed. Both decompositions of _s and _s were determined at an early stage of ageing and a four-phase transformation, _f+T+, was observed at the boundaries of _f phase and the phase, instead of clearly observed at the boundaries of phase, in a solution-treated Zn-Al alloy during prolonged ageing.     

γ ? α2 Phase transformation in fractured high temperature stress rupture Ti-48Al-2Nb(at.%)

The ₂ phase transformation in fractured high temperature stress rupture Ti-48Al-2Nb(at.%) alloy has been studied by analytical electron microscopy. ₂ and phases were found at grain boundaries. ₂ layers that suspended in layers and interfacial ledge higher than 2d ₍₁₁₁₎ at /₂ interfaces were observed in the lamellar grains. These facts indicated that ₂ phase transformation and dynamic recrystallization have occurred during high temperature stress rupture deformation. It can be concluded that deformation induced ₂ phase transformation and dynamic recrystallization resulted in the presence of particles at grain boundaries. A structural and compositional transition area between deformation-induced ₂(or ) and its adjacently original (or ₂) phases was found by HREM and EDS and is suggested as a way to transform between and ₂ phase during high temperature stress rupture deformation. The transition area was formed by slide of partial dislocations on close-packed planes and diffusion of atoms.     

The crystal growth and thermoelectric properties of chromium disilicide

Single crystals of chromium disilicide about 8 mm in diameter and 35 mm long were grown using the floating zone technique. Measurements of electrical resistivity , Hall coefficient R and thermoelectric power were carried out in the temperature range from 85 to 1100 K. The values of and showed the anisotropy over the temperature range studied. The ratios parallel and perpendicular to the c-axis were / =1.9 and /=1.7 respectively, at room temperature. It was found to be a degenerate semiconductor having the hole concentration of 6.3×10²⁰ cm^–3 below 600 K. The effective masses of holes parallel and perpendicular to the c-axis determined from the thermoelectric power and the hole concentration near room temperature were estimated to be five and three times as large as a free electron mass, respectively. The calculation on the values of and was made using those effective masses. These values showed good agreement with the observed values in the temperature range from 150 to 1100 K.