High‐quality surface passivation of silicon solar cells in an industrial‐type inline plasma silicon nitride deposition system

We have studied the surface passivation of silicon by deposition of silicon nitride (SiN) in an industrial‐type inline plasma‐enhanced chemical vapor deposition (PECVD) reactor designed for the continuous coating of silicon solar cells with high throughput. An optimization study for the passivation of low‐resistivity p‐type silicon has been performed exploring the dependence of the film quality on key deposition parameters of the system. With the optimized films, excellent passivation properties have been obtained, both on undiffused p‐type silicon and on phosphorus‐diffused n⁺ emitters. Using a simple design, solar cells with conversion efficiencies above 20% have been fabricated to prove the efficacy of the inline PECVD SiN. The passivation properties of the films are on a par with those of high‐quality films prepared in small‐area laboratory PECVD reactors. Copyright © 2004 John Wiley & Sons, Ltd.     

Textured silicon surface passivation by high‐rate expanding thermal plasma deposited SiN and thermal SiO2/SiN stacks for crystalline silicon solar cells

Expanding thermal plasma (ETP) deposited silicon nitride (SiN) with optical properties suited for the use as antireflection coating (ARC) on silicon solar cells has been used as passivation layer on textured monocrystalline silicon wafers. The surface passivation behavior of these high‐rate (>5 nm/s) deposited SiN films has been investigated for single layer passivation schemes and for thermal SiO₂/SiN stack systems before and after a thermal treatment that is normally used for contact‐firing. It is shown that as‐deposited ETP SiN used as a single passivation layer almost matches the performance of a thermal oxide. Furthermore, the SiN passivation behavior improves after a contact‐firing step, while the thermal oxide passivation degrades which makes ETP SiN a better alternative for single passivation layer schemes in combination with a contact‐firing step. Moreover, using the ETP SiN as a part of a thermal SiO₂/SiN stack proves to be the best alternative by realizing very low dark saturation current densities of <20 fA/cm² on textured solar‐grade FZ silicon wafers and this is further improved to <10 fA/cm² after the anneal step. Optical and electrical film characterizations have also been carried out on these SiN layers in order to study the behavior of the SiN before and after the thermal treatment. Copyright © 2008 John Wiley & Sons, Ltd.     

Bulk and surface passivation of silicon solar cells accomplished by silicon nitride deposited on industrial scale by microwave PECVD

Bulk and surface passivation by silicon nitride has become an indispensable element in industrial production of multicrystalline silicon (mc‐Si) solar cells. Microwave PECVD is a very effective method for high‐throughput deposition of silicon nitride layers with the required properties for bulk and surface passivation. In this paper an analysis is presented of the relation between deposition parameters of microwave PECVD and material properties of silicon nitride. By tuning the process conditions (substrate temperature, gas flows, working pressure) we have been able to fabricate silicon nitride layers which fulfill almost ideally the four major requirements for mc‐Si solar cells: (1) good anti‐reflection coating (refractive index tunable between 2·0 and 2·3); (2) good surface passivation on p‐type FZ wafers (S_eff<30 cm/s); (3) good bulk passivation (improvement of IQE at 1000 nm by 30% after short thermal anneal); (4) long‐term stability (no observable degradation after several years of exposure to sunlight). By implementing this silicon nitride deposition in an inline production process of mc‐Si solar cells we have been able to produce cells with an efficiency of 16·5%. Finally, we established that the continuous deposition process could be maintained for at least 20 h without interruption for maintenance. On this timescale we did not observe any significant changes in layer properties or cell properties. This shows the robustness of microwave PECVD for industrial production. Copyright © 2005 John Wiley & Sons, Ltd.     

Industrial high‐rate (∼5 nm/s) deposited silicon nitride yielding high‐quality bulk and surface passivation under optimum anti‐reflection coating conditions

High‐quality surface and bulk passivation of crystalline silicon solar cells has been obtained under optimum anti‐reflection coating properties by silicon nitride (a‐SiN_x:H) deposited at very high deposition rates of ∼5 nm/s. These a‐SiN_x:H films were deposited using the expanding thermal plasma (ETP) technology under regular processing conditions in an inline industrial‐type reactor with a nominal throughput of 960 solar cells/hour. The low surface recombination velocities (50–70 cm/s) were obtained on p‐type silicon substrates (8·4 Ω cm resistivity) for as‐deposited and annealed films within the broad refractive index range of 1·9–2·4, which covers the optimum bulk passivation and anti‐reflection coating performance reached at a refractive index of ∼2·1. Copyright © 2005 John Wiley & Sons, Ltd.     

Excellent boron emitter passivation for high‐efficiency Si wafer solar cells using AlOx/SiNx dielectric stacks deposited in an industrial inline plasma reactor

Excellent passivation of boron emitters is realised using AlO_x/SiN_x dielectric stacks deposited in an industrial inline plasma‐enhanced chemical vapour deposition reactor. Very low emitter saturation current density (J_0e) values of 10 and 45 fA/cm² are obtained for 180 and 30 Ω/sq planar p⁺ emitters, respectively. For textured p⁺ emitters, the J_0e was found to be 1.5–2 times higher compared with planar emitters. The required thermal activation of the AlO_x films is performed in a standard industrial fast‐firing furnace, making the developed passivation stack industrially viable. We also show that an AlO_x thickness of 5 nm in the AlO_x/SiN_x stack is sufficient for obtaining a J_0e of 18 fA/cm² for planar 80 Ω/sq p⁺ emitters, which corresponds to a 1‐sun open‐circuit voltage limit of the solar cell of 736 mV at 25 °C. Copyright © 2012 John Wiley & Sons, Ltd.