Copper Removal from Molten Steel by Gasification

A novel method is proposed to enhance the gasification and removal of copper from molten steel by adding ammonium salts or urea into molten steel under normal pressure. The decopperization experiments were conducted in a molybdenum-wire resistance furnace at 1 873 K. The copper content of about 400 g of a mild steel was reduced from 0.49 %(mass fraction, the same below) and 0.51 % to 0.31 % and 0.38 % using 0.7 g of NH4Cl and 0.5 g of (NH4)2C2O4 respectively, while the copper content of the molten steel was reduced from 0.61 % to 0.56 % using 2.00 g of NH2CONH2.     

喂丝法钢液脱铜

提出了用喂丝法向钢液中插入铵盐或氨基化合物的脱铜方法.在常压下,Ar气氛中,向钢液中分别加入NH₄Cl和NH₂CONK₂把约300g钢水含铜量从0.6%降至0.47%～0.5%,仅用脱铜剂2～4g.氯化铵有氯化和铵分解的双重脱铜作用,比尿素脱铜效果更好.     

熔盐电解法制备钨铜合金粉

在NaCl-KCl-Na2WO4-CuO体系中采用熔盐电解法直接制取钨铜合金粉,并对产物进行了XRD、SEM及EDS分析。结果表明,在780～800℃电解、阴极电流密度106～133mA/cm2、电解时间3～4h、电压2.2～3.2V的条件下,可以得到纯度99%以上、平均粒度0.91μm的钨铜合金粉末,各项指标基本达到了工业上烧结钨铜合金的要求。     

Formation Free Energies of Solid Solution between Tri‐Calcium Phosphate and Di‐Calcium Silicate

In order to determine the free energy changes for the reaction molten copper containing phosphorus was brought into equilibrium with mixtures of tri‐calcium silicate + di‐calcium silicate + solid solution between tri‐calcium phosphate and di‐calcium silicate in a stream of Ar + H₂ + H₂O gas mixture at temperatures between 1548 and 1598 K, and the results are expressed as      

电场作用下钢液脱铜研究进展

阐述了国内外的各种主要脱铜方法;电场下钢水脱铜方法．该方法立意很新,即通过施加特殊电场,在阴极附近富集铜离子,在此基础上加选定的脱铜剂发生脱铜反应进行钢水脱铜．通过实验室钢水中铜的富集试验,结合工业现场情况,初步探讨了电场下钢水脱铜的工业应用的可行性．该种脱铜方法有一定的工业试验基础,在冶金工业上有着很广阔的应用前景．     

提高结晶器铜管使用寿命实践

从钢水质量、铸机设备、工艺操作、铜管结构及生产管理等方面分析了铜管使用寿命的影响因素。通过降低钢水过热度、改善设备运行条件、加强软水质量监控、修订各项管理制度,使铜管过钢量大大提高,年降成本40多万元。     

从氰化液中萃取铜的机理研究

本文研究了氢氧化三烷基甲铵(转型的N_(163))—煤油体系从氰化液中萃取铜的机理。采用多种方法对萃合物的研究表明,铜以Cu(CN)_4~(8-)的形式被萃入有机相,萃合物的主要形式分别为Cu(CN)4·3(R_8CH_3N)和Cu(CN)_4·(ReCH_3N)_2(R_8CH_3N)。     

太阳能电池及多晶硅的生产

在简述太阳能电池原理和发展的基础上,分析了太阳能电池用多晶硅的生产方法.认为:改良的熔盐电解法和熔盐三层电解精炼法有可能直接制取太阳能级多晶硅,此法一旦研究成功,将大幅度地降低太阳能级多晶硅生产成本,应引起人们的关注.     

高铜载金炭铁盐法脱铜试验研究

某高铜载金炭中金品位2. 58 kg/t,铜品位50. 85 kg/t。针对该载金炭中铜品位高,影响吸附作业的问题,采用铁盐法进行脱铜试验研究,并考察脱铜液再生利用的影响因素。结果表明:采用铁盐法脱铜工艺处理高铜载金炭,在液炭比9∶1,脱铜时间6 h,脱铜温度25℃,氯化铁用量6 kg/t,硫酸用量15 kg/t的条件下,脱铜率可达97. 52%,且金基本不被浸出;脱铜液采用萃取-反萃工艺处理,可实现铜的综合回收,萃余液通过空气氧化后返回脱铜作业循环利用,脱铜率可达到97. 46%。     

Nitrogen Removal from Molten Steel under Argon DC Glow Plasma

Under argon DC glow plasma, the nitrogen removal from molten steel was studied. The experimental result showed that nitrogen mass percent could be reduced to 0. 000 8 %. The change of polarity had no impact on nitrogen removal when the nitrogen mass percent was low. The mechanism of denitrogenation of molten steel under argon DC glow plasma was discussed.     

LiCl-KCl熔盐中电解还原钛铁矿的研究

在LiCl-KCl熔盐中,采用熔盐电解法还原钛铁矿,研究了电解时间、槽电压及电解温度对还原钛铁矿的影响,探讨了在熔盐中钛铁矿电解脱氧的机理。结果表明,钛铁矿还原优先生成铁,钛氧化物由高价到低价逐步还原,而未得到金属钛及其合金,说明在LiCl-KCl熔盐中,TiO的脱氧还原是钛铁矿熔盐电解生成金属钛及其合金的反应限制性步骤。     

稀土电解废熔盐的综合利用研究

主要研究了从氟化体系熔盐电解过程产生的废熔盐回收合格熔盐和氧化稀土的工艺条件；采用本工艺得到的熔盐可直接返回电解生产线使用，制取的氧化稀土质量都达到国家标准，稀土总收率达90．09％。     

可溶阳极电解生产1~#电钴的工艺研究

介绍采用Ｐ２０４ 萃取除Ｆｅ、Ｚｎ 和Ｍｎ,ＨＡ－ＰＥ２０６协萃体系除Ｃｕ,ＨＡ－ＰＥ２０６协萃体系除Ｎｉ、Ｃｕ,并用净化后液进行可溶阳极电解得到１＃ 电解钴的工艺研究过程。     

含钒钢水SPHC精炼生产实践

针对承钢含钒钢水SPHC试制初期出现的成渣晚、造白渣困难、增碳回硅及钢水浇铸困难等问题分析了原因,通过优化渣料、转炉及LF炉工艺,实施早化渣、早成渣、保持白渣时间,保证弱吹氩时间,精确控制处理周期的生产组织模式,SPHC精炼工艺获到了平均脱硫率64.5%、铸坯T[O]28.5×10-6、钢水可浇性100%的良好冶金效果。     

在氟盐体系中钕离子阴极过程的研究

采用循环伏安法和计时电流法研究了ＬｉＦ－ＫＦ熔盐体系中钕离子在钼电极上的还原过程。结果表明,在本实验条件下,钕离子的电化学反应是一步还原,阴极过程受扩散控制。且在沉积的初级阶段是三维半球形瞬时成核,而后是扩散控制下的晶核长大过程     

我国氟盐体系氧化钕电解制备金属钕

本文论述了我国氟化物熔盐体系,电解氧化钕制备金属钕工艺技术及装备的现状、最新进展。并就大型电解槽工艺技术及装备的研究进行了探讨。     

一次烧结成型制备碳氧钛可溶阳极工艺探索

以沥青作为添加剂,开展了一次烧结成型制备碳氧钛可溶阳极探索试验,研究该种可溶阳极在NaCl-KCl-TiCl_x熔盐体系中的电化学溶解行为。结果表明:在较优的工艺条件下,制备的一次烧结成型可溶阳极密度为1.3~1.4 g/cm~3,摔落强度符合电解要求;一次烧结成型可溶阳极在低价钛(NaCl-KCl-TiCl_x)熔盐体系中能实现稳定电化学溶解。     

提高中间包钢水温度合格率的措施

针对韶钢第三炼钢厂钢水中间包温度波动大、中间包温度合格率偏低等的情况,在钢包精炼、连铸、生产组织等影响温度的各个控制环节进行了优化,钢水中间包温度控制合格率由80%左右提高到95%以上.     

超低磷钢生产技术

总结了超低磷钢的生产工艺，对生产超低磷钢有关各个环节：铁水预处理，转炉冶炼，钢水炉外脱磷尤其是钢水炉外脱磷的渣系组成及脱磷工艺进行了详细的论述。     

耐火材料对钢水洁净度的影响

文中就耐火材料对钢水洁净度的影响进行了综述，表明了耐火材料在冶炼过程中的双重重要性，除传统观念外，耐火材料还可起到净化钢水的作用。