2A14铝合金激光-MIG复合填丝焊特性分析

针对2A14铝合金同时进行了激光-MIG复合焊和激光-MIG复合填丝焊试验,对比分析了激光功率、离焦量、焊接速度、焊接电流、光丝间距、填丝速度等工艺参数对两种焊接方法焊缝成形的影响规律.结果表明,铝合金激光-MIG复合填丝焊方法切实可行,工艺适应性良好,与铝合金激光-MIG复合焊相比,均能在较宽的工艺参数范围内实现良好的焊缝成形;相同试验参数条件下,铝合金激光-MIG复合填丝焊的焊缝成形特征与激光-MIG复合焊基本相同,但其熔敷速度明显大于激光-MIG复合焊,焊缝余高明显增加.     

铝合金万瓦级激光-MIG 电弧复合焊缝成形

针对5A06铝合金进行了万瓦级激光-MIG电弧复合焊接工艺试验,分析了激光功率、离焦量、焊接速度、光丝间距对焊缝成形的影响。结果表明,万瓦级激光-电弧复合焊的焊接窗口窄、焊接过程不稳定,焊缝易出现驼峰、凹陷、咬边等缺陷。激光功率、离焦量和焊接速度对焊缝熔深影响较大,激光功率由10 kW增加至30 kW,焊缝熔深增加18 mm,达到29 mm。光丝间距对焊缝熔深熔宽影响较小。通过调节工艺参数,可明显改善铝合金万瓦级激光-MIG电弧复合焊的焊缝成形,适当的工艺参数下,可在达到最大熔深的同时获得具有稳定表面成形的焊缝。     

非铁金属的焊接

20091169焊接工艺对6005A铝合金激光-MIG复合焊焊缝成形的影响/雷祥…//焊接.-2008(7):25~32采用CO2激光-MIG复合焊焊接2.5mm厚的6005A铝合金板,基于正交试验方法研究了焊接工艺参数对焊缝成形的影响。试验结果表明,对复合焊焊缝熔透状态影响显著性从大到小的工艺参数依次为:焊接速度、MIG电流、MIG电压和激光功率,其中前两者影响最为突出。在熔透状态不发生显著变化时,对复合焊焊缝表面成形影响显著性从大到小的工艺参数依次为:MIG电压、焊接速度、激光功率和MIG电流。根据正交试验结果优化了激光-电弧复合焊接6005A的工艺参数,建立了工艺参数选择原则,根据此原则选择合适的参数获得了最佳的焊缝成形。图4表6参13200911705A06铝合金激光填丝焊工艺研究/许飞…//焊接.-2008(8):26~28针对1.2mm厚5A06铝合金薄板YAG激光焊接工艺范围窄和对间隙要求严格等问题,较系统地研究了该铝合金激光填丝焊接工艺。试验中采用ER5356焊丝作为填充金属,对光丝间距、送丝速度、激光功率和焊接速度等影响焊缝成形的各种焊接工艺参数进行了优化分析。研究结果表明:优化工艺参数可以...     

非铁金属的焊接

20091169焊接工艺对6005A铝合金激光-MIG复合焊焊缝成形的影响/雷祥…//焊接.-2008(7):25~32采用CO2激光-MIG复合焊焊接2.5mm厚的6005A铝合金板,基于正交试验方法研究了焊接工艺参数对焊缝成形的影响。试验结果表明,对复合焊焊缝熔透状态影响显著性从大到小的工艺参数依次为:焊接速度、MIG电流、MIG电压和激光功率,其中前两者影响最为突出。在熔透状态不发生显著变化时,对复合焊焊缝表面成形影响显著性从大到小的工艺参数依次为:MIG电压、焊接速度、激光功率和MIG电流。根据正交试验结果优化了激光-电弧复合焊接6005A的工艺参数,建立了工艺参数选择原则,根据此原则选择合适的参数获得了最佳的焊缝成形。图4表6参13200911705A06铝合金激光填丝焊工艺研究/许飞…//焊接.-2008(8):26~28针对1.2mm厚5A06铝合金薄板YAG激光焊接工艺范围窄和对间隙要求严格等问题,较系统地研究了该铝合金激光填丝焊接工艺。试验中采用ER5356焊丝作为填充金属,对光丝间距、送丝速度、激光功率和焊接速度等影响焊缝成形的各种焊接工艺参数进行了优化分析。研究结果表明:优化工艺参数可以...     

铝合金激光焊接技术研究进展

综述铝合金激光焊接技术特点及研究现状,开展3 mm厚LF6铝合金激光-MIG电弧复合焊接工艺研究。文献综述表明,铝合金激光自熔焊接表面成形不好,且易于产生气孔缺陷,激光填丝焊、激光-电弧复合焊以及双光束激光焊等能够有效地解决上述铝合金激光焊接问题。试验研究表明,激光-MIG电弧复合焊接LF6铝合金可获得良好的焊缝成形,内部质量达到QJ1666A-2011Ⅰ级焊缝质量要求,接头强度达到母材的90%以上,具备较为优异的力学性能。     

不锈钢SUS 301L激光填丝搭接焊工艺

以接头形式0.6+2mm的不锈钢SUS 301L为对象,研究激光填丝焊激光功率、焊接速度、送丝速度3个主要工艺参数对焊缝成形、接头截面形貌及连接强度的影响规律。结果表明,随着激光功率的增加,焊缝熔深和熔宽增大,余高减小;随着焊接速度的增加,焊缝熔深、熔宽、余高均减小;随着送丝速度的增加,焊缝熔深和熔宽减小,余高增大。接头的最大拉力为14.43 k N,断裂在上层薄板母材中,焊缝强度大于母材。     

高速列车6N01铝合金型材激光-MIG复合填丝焊接技术

针对高速列车侧墙6N01铝合金型材,主要从焊缝成形、焊缝气孔率、接头强度、焊接变形、焊接效率、金相组织等方面研究了激光-MIG复合填丝焊方法的焊接特性,并与激光-MIG复合焊进行了综合对比。试验结果表明,相同试验条件下,两种焊接接头的表面成形相当,焊缝气孔率均在0. 6%以下,接头强度均达到母材的75%以上,焊接变形均在1 mm以内,与激光-MIG复合焊相比,激光-MIG复合填丝焊在不增加热输入的条件下焊接效率提高了23%。     

铝合金双光束激光焊接过程稳定性分析

从成形、气孔、熔深的波动、激光匙孔、光致等离子体、飞溅等方面研究了铝合金高功率单光束激光和双光束激光焊接过程的稳定性。结果表明,在相同工艺参数下,双光束激光焊缝表面成形明显优于单光束,熔深的波动较单光束小;在相同工艺参数及相同熔深条件下,双光束焊缝气孔率较单光束小,小孔及等离子体的波动周期较单光束长,面积波动变异系数较单光束小,飞溅较单光束更加细小均匀。     

焊接参数对铝合金激光——MIG电弧复合焊缝熔深的影响

以5A06(LF6)铝合金为研究对象,研究了铝合金激光-MIG电弧复合焊(HYBRID焊)时焊接参数的变化对焊缝熔深的影响规律,并将焊接参数的变化对激光-MIG电弧复合焊、MIG电弧焊、激光焊的焊缝熔深的影响进行了综合比较分析.结果表明,若以等效于激光焊熔深的MIG电弧功率为分界线,可以把MIG电弧的功率分成高、低能量两个区,当激光与低能量电弧区的电弧复合时,激光对焊缝的熔深起主导作用,HYBRID焊的熔深大于该区的MIG电弧焊;当激光与高能量电弧区的电弧复合时,电弧对焊缝的熔深起主导作用,HYBRID焊缝主要体现为MIG焊缝的特点,加入激光的优势主要体现在增加焊接速度方面,即高速焊时也可获得良好的焊缝成形.     

焊丝熔化方式对激光焊接过程的影响

研究了两种焊丝熔化方法(电弧预熔丝激光焊、激光填丝焊)激光焊接过程对匙孔稳定性以及焊缝成形的影响,进一步研究了焊丝熔化方法对焊接接头质量的影响,并对比分析了两种焊丝熔化方式对焊接速度的适应性. 结果表明,电弧预熔丝激光焊过程中,熔池表面匙孔开口尺寸变化不大,匙孔较为稳定;激光填丝焊方法由于熔化的液态金属距离匙孔边缘很近,焊接过程中熔池表面匙孔开口尺寸变化较大,而且容易出现熔池表面匙孔的闭合. 与激光填丝焊相比,电弧预熔丝激光焊熔化的焊丝端部可以沿熔池边缘流入,与匙孔边缘的距离较远,匙孔稳定性较好,焊缝气孔数量较少. 当焊接速度为8 m/min时,电弧预熔丝激光焊的焊缝成形良好;而激光填丝焊焊缝背面成形不连续,并且出现了未焊透的缺陷.     

Characteristic of laser-MIG hybrid welding with filling additional cold wire for aluminum alloy

The weld appearance,deposition rate,welding efficiency,stability of arc,laser keyhole characteristic,and weld property were studied by using a novel laser-MIG hybrid welding process with filling wire of aluminum alloy. The results were also compared with those by conventional laser-MIG hybrid welding process. It was found that with the suitable process parameters this novel welding process for aluminum alloy was stable and final weld bead had fine appearance. Compared to conventional laser-MIG hybrid welding process,during this novel welding process the stability of arc,the laser keyhole characteristic and the weld property were similar,while the keyhole cycle frequency and keyhole opening area had differences of 1. 23% and 15. 34%,respectively,and the welding efficiency increased by about 31% without increasing heat input.     

铝合金激光-MIG复合焊熔滴对匙孔作用的模拟

将复合焊接过程中的反冲压力、表面张力等驱动力及熔滴过渡行为考虑在内,建立5A06铝合金激光-MIG复合焊接数值模拟热流耦合模型,由于熔池内的流动及匙孔稳定性对焊接性能有重要影响,因此针对熔滴与匙孔及熔池稳定性的影响进行了系统讨论,并且通过采用不同的熔滴落入位置进行计算.结果表明,当熔滴落入位置距激光中心较近时,熔滴对匙孔的冲击作用较大,匙孔壁的平均流速和波动频率有所增加,匙孔更易由于周期性的熔滴过渡而产生液桥发生闭合,熔滴落入位置还会影响匙孔深宽比,进而影响激光能量的菲涅尔吸收.     

铝合金激光扫描焊接工艺特性

为减少6061铝合金激光焊接缺陷，提高焊接过程稳定性，采用大功率固体激光光束扫描焊接的方法进行焊接工艺开发. 结果表明，当工艺参数在扫描幅度为0.5 ~ 0.7 mm，扫描频率为100 ~ 200 Hz范围内时可以获得质量较高的焊缝. 激光扫描焊接可以明显抑制等离子体的生成，其尺寸相对于常规激光焊接的2/3，其面积变化标准差约为常规激光焊接的1/2. 相对于常规激光焊接技术，激光扫描焊接过程中熔池形状稳定保持圆状，匙孔在其中沿逆时针方向稳定运动，其面积约为常规激光焊接中匙孔面积的2倍.     

6061铝合金激光深熔焊等离子体光谱特征与气孔的相关性

采用光纤激光器对6061铝合金进行焊接,获得了表面成形良好的焊缝. 利用光谱仪和高速摄像机获取等离子体的光谱和图像,分析了激光深熔焊时等离子体的光谱特征,讨论了光谱强度及其波动程度与焊缝气孔的位置及气孔率之间的相关性. 结果表明,6061铝合金激光深熔焊时等离子体的电离度低,光谱中只有金属原子谱线,AlI 396.152 nm谱线的强度能够反映焊接过程中等离子体的光谱特征;等离子体光谱强度及其波动程度与焊缝中氢气孔的形成位置和气孔率均不存在必然联系;等离子体光谱强度与小孔型气孔的位置不存在相关性,但其波动程度能够反映小孔型气孔的气孔率.     

铝合金激光-小功率脉冲MIG电弧复合热源焊接特性分析

针对5A06铝合金,通过一系列对比数据综合分析了MIG焊和激光MIG复合热源焊接技术在焊缝熔深、焊缝成形、焊接速度、焊接热输入等方面的优缺点.结果表明,在MIG平均电流小于200 A的小功率脉冲MIG电弧区域内,等热输入且等焊接速度条件下,激光-MIG复合热源焊接技术与MIG相比可以提高焊缝深宽比1～2倍,增加焊缝熔深0.43～2.5倍;等热输入且等平均焊接电流条件下,与MIG相比,激光MIG复合热源焊接技术可以提高焊接速度0.6～1.5倍,增加焊缝熔深0.5～5.9倍;激光MIG复合热源焊接技术可以用高于MIG焊0.6～6.5倍的焊接速度和更小的焊接热输入获得与MIG同样的焊缝熔深;与MIG焊相比,激光MIG复合热源焊缝的铺展性更好,更适合于高速焊接;MIG复合2 kW的激光能量后会增加平均电弧电压、减小平均电流.     

MB8镁合金激光——MIG复合焊接分析

实现了10 mm厚MB8镁合金的激光-MIG(metal inert gas)复合焊接,并对其工艺稳定性、接头形貌特征、微观组织和力学性能进行了分析.在激光-电弧相互作用下,镁合金复合焊接内的MIG电弧燃烧和熔滴过渡稳定性显著提高,并获得饱满均匀的复合焊缝.在文中试验条件下,复合焊接速度比单独激光焊接高25%.因为表面凹坑缺陷的消除,复合焊接接头抗拉强度远高于激光焊接接头,达到母材的87.2%.此外,复合焊缝熔合区中心区域组织为等轴晶,靠近熔合线区域为柱状晶.在复合焊缝内,相对较低的凝固速度,上半部分宽大电弧区的晶粒尺寸明显大于下半部分细窄激光区.结果表明,激光-MIG复合焊接是MB8镁合金的有效焊接方法.     

铝合金激光-多股绞合焊丝MIG复合焊特性分析

选用多股绞合焊丝替代传统焊丝,将激光热源与多股绞合焊丝MIG焊热源相匹配.借助高速摄像系统,提取焊接过程中熔池和匙孔特征量,开展5A06铝合金激光-多股绞合焊丝MIG复合焊工艺特性研究,探讨了不同工艺参数下焊缝成形与熔池行为相关性及焊接气孔规律性研究.结果表明,主要焊接工艺参数对焊缝成形的影响规律与常规焊丝激光-电弧复...     

Study of the Laser-MIG Hybrid Welded Al-Mg Alloy

The technology of laser-MIG hybrid welding is hotspot in welding researched field at present.It can improve the velocity of the welding,reduce the distortion of the welding,optimize the structure of the welding joint and etc..The 5052 aluminum alloy of the 10mm thick was welded by the laser-MIG hybrid welding.The structure,the alloy elements profile and the mechanical property of the welded joint are researched by the optical microscope,SEM,sclerometer and etc..The results showed:The medium thick Al alloy was welded in high speed by the laser-MIG hybrid welding.The appearance of the welding joint is well.The weld joint and the weld interface are fine.The intenerate region in the welding joint is small.The tensile strength in welding joint has achieved 94.4% of that in base metal.