稀土元素Ce对锡银铜无铅钎料显微组织的影响

研究了不同含量的稀土Ce对Sn-3．8Ag-0．7Cu无铅钎料的显微组织的影响，结果表明，微量稀土Ce的加入可以细化组织，抑制金属间化合物的生长。稀土Ce含量为0．03％（质量分数）时，组织均匀、细小，钎料润湿性能好，钎缝力学性能佳。当Ce含量为0．03％（质量分数）时，无铅钎料组织中开始出现黑色的富Ce相，并随Ce量的增加而增多。对显微组织的分析和理论计算表明，含稀土Ce锡银铜无铅钎料组织中的黑色的富Ce相为Ce与Sn的化合物。     

SnAgCuEr系稀土无铅钎料的显微组织

系统研究了添加微量稀土Er对Sn3.8Ag0.7Cu无铅钎料合金显微组织和性能的影响.试验发现,微量Er的添加,使Sn3.8Ag0.7Cu钎料合金的熔化温度稍有降低,铺展面积有所增加,抗剪强度有所提高.通过显微组织观察,加Er后网状共晶物体积百分比增大,初晶金属间化合物(IMC)的尺寸变小.微量Er抑制了时效过程钎料与铜基体界面IMC层(IML)的增厚,时效400 h后差别更明显,有利于提高钎料接头的可靠性.指出含微量稀土的SnAgCuEr合金是性能优良的无铅钎料合金.     

Ag-Cu-Zn-Sn-xGa-yIn钎料性能与显微组织

通过对Ag-Cu-Zn-Sn-xGa-yIn钎料的钎焊试验发现:单独添加Ga或In元素时,Ga,In元素的添加量分别控制在3%,1.5%(质量分数)左右最佳;复合添加Ga与In元素时,Ag-Cu-Zn-Sn-3Ga-2In的力学性能最佳.对钎焊接头拉伸断口进行分析结果表明,Ag-Cu-Zn-Sn-3Ga-2In接头断口具备明显韧性断裂特征.当In元素添加量超过2%时,对钎焊接头强度的影响趋于平缓,但是断口已具有明显的解理形貌.Ga,In元素在钎料基体中分布均匀,无明显偏析现象,但是Ag-Cu-Zn-Sn-xGa-yIn钎料基体组织呈现明显的"骨架"状特征.     

稀土La改性Ag-Cu-Ti钎料的显微组织和力学性能

系统研究了钎焊CBN工具用稀土元素La改性Ag-Cu-Ti钎料合金的熔化温度、微观组织、显微硬度及钎料与45钢基体钎焊接头抗剪强度.结果表明,稀土元素La对Ag-Cu-Ti钎料合金的熔点影响很小,但是可以促进钎料的合金化,提高其合金化程度,稀土La加入量不超过0.5%(质量分数)时可以改善Ag-Cu-Ti钎料合金的微观组织,使金属间化合物分布更加均匀,提高Ag-Cu-Ti钎料合金的显微硬度,还可以明显改善钎料与45钢基体的钎焊接头抗剪强度.     

Ag和RE对表面组装用SnAgCuRE无铅钎料显微组织的影响

采用扫描电镜和能谱分析等检测手段,分别研究了Ag和RE含量对SnAgCuRE系钎料合金显微组织的影响.结果表明,随着Ag和RE含量的增加,SnAgCuRE无铅钎料的显微组织中的共晶组织所占比例增大,钎料合金中富Sn相的组织细化.但Ag含量超过3.2 wt％时,会出现大的板条状Ag3Sn初晶,因此,Ag的最佳添加量在2.0wt％～3.0wt％.当RE添加量达到0.5wt％时,会出现大块的花瓣状和点、条状的CeSn3和LaSn3稀土化合物相,聚集在共晶组织和富Sn相界面处,导致钎料性能下降.     

微量In对AgCuZn钎料组织和性能的影响

研究了不同In含量银钎料的熔化温度、铺展性能、钎料显微组织以及钎缝力学性能的变化规律.以紫铜、黄铜为母材,采用火焰钎焊方法,用对接和搭接接头形式进行钎焊试验.结果表明,在银钎料中添加微量In元素,能够降低钎料的熔化温度,改善钎料的铺展性能,并显著改变钎料显微组织.对于黄铜对接来说,钎焊接头的抗拉强度,随银钎料中In含量的增加而呈抛物线方式增加;除黄铜对接接头外,其它形式的接头断裂位置均在母材上,说明含In银钎料的力学性能优良.     

AgCuZn-X(Ga, Sn, In, Ni)钎料显微组织及钎焊接头研究

研究了不同合金元素Ga,Sn,In和Ni添加对Cd银基钎料及其钎焊接头的显微组织影响,同时对AgCuZn-X(Ga,Sn,In,Ni)钎料的对接和搭接实验做了对比实验分析。结果表明,添加Ga,Sn,In和Ni4种元素的银钎料具有"特有的镓结构",具有较低的固相线和液相线,其钎缝力学性能优异,由SEM观察钎缝显微组织可知,低银含镓钎料具有与高银高镓钎料相近的织网状致密组织,添加适当的元素可以显著提高低银钎料的性能。     

稀土元素Ce对Zn-22Al钎料组织和性能的影响

研究了稀土元素Ce的添加对Zn-22Al钎料的电阻率、熔化特性、铺展性能、显微组织以及钎焊接头抗剪强度的影响.结果表明,铈的加入对钎料的电阻率、熔化特性影响甚微,但显著改善了钎料的铺展性能,细化了钎料的基体组织,提高了钎焊接头的抗剪强度.当Ce元素的添加量达到0.05%时,钎料在铝、铜两种母材上的铺展面积取得最大值,分别较未添加时提高了21.4%和11.6%;钎焊接头抗剪强度达到最大值91.3 MPa,比未添加稀土时提高了30.3%.稀土铈含量继续增加时,其显微组织中出现脆性稀土相并且尺寸有增大的趋势,钎料铺展性能、钎焊接头强度明显恶化.     

镓对Ag-Cu-Zn钎料组织和力学性能的影响

研究了不同镓含量银钎料的铺展性能、钎缝力学性能以及钎料的显微组织变化规律.结果表明,通过添加微量合金元素、优化含镓银钎料的化学成分,可得到铺展性能优良、钎缝力学性能较高的含镓银钎料.以黄铜为母材,采用火焰钎焊方法,分别采用对接和搭接接头形式,研究测试了钎焊接头的力学性能.结果表明,两种接头形式的钎焊接头均断裂在母材,说明含镓银钎料具有较高的钎缝力学性能,完全可以替代含镉的银钎料.     

Sn对Cu-Sn-Ti钎料显微组织与性能的影响

为揭示Sn调控Cu-Sn-Ti钎料显微组织与力学性能的规律,采用真空非自耗熔炼法制备Cu-Sn-Ti钎料,利用扫描电镜、X射线衍射仪、能谱仪、万能材料试验机等,研究了Sn对Cu-Sn-Ti钎料的显微组织、显微硬度、剪切强度及断口形貌的影响.结果表明,钎料显微组织随Sn含量增加而演变的规律为：枝晶状初生α-Cu基体相+共晶组织+晶间组织→初生α-Cu基体相+共晶组织→共晶组织→初生CuSn₃Ti₅相+粗化共晶组织+α-Cu基体相(富Sn)+Cu₄₁Sn₁₁相+SnTi₃相,其中晶间组织为α-Cu相和CuSn₃Ti₅相的混合组织+少量的(SnTi₃+CuTi相+Cu₃Ti相).随着Sn含量的增加,钎料显微硬度呈先增大后减小的趋势,钎料剪切强度呈逐渐减小的趋势,断口形貌由准解理断裂向解理断裂+准解理断裂的混合形态转变.增加Sn含量促使钎料形成粗化的CuSn₃Ti_5<...     

Zhang Guoqing, Feng Xingmei, Feng Zhanying, Tang Chao, Wang Feng and Qi Yuefeng Effect of mixed rare earth and Sr on microstructure and brazability of Al-20Cu-5Si-2Ni filler metal

The objective of this study is to investigate the influence of adding tiny amount of mixed rare earth ( La, Ce) and Sr to Al-20Cu-5Si-2Ni filler metal, by analyzing the microstructure, wettability and mechanical properties of brazed joints. The results show that with the addition of mixed rare earth ( La, Ce) into Al-20Cu-5Si-2Ni alloy, the α-Al solid solution as well as CuAl₂ ( Ni) intermetallic compound phase significantly reduced, while more Al-Si eutectic phase and Al-Si-Cu ternary eutectic phase were produced. And as mixed rare earth ( La, Ce) added in, the wettability of Al-20Cu-5Si-2Ni filler metal decreased, while the shear strength of the brazed joints increased. The addition of Minor Sr modificated Al 20Cu-5Si-2Ni filler metal, further reduced the CuAl₂ ( Ni) intermetallic compound phase, which was partially replaced Al-Si-Cu ternary eutectic phase. As a result, the tensile strength as well as the wettability of the filler metal was improved.     

稀土对Al-Si-Zn-Cu钎料工艺性能的影响

在Al-Si-Zn-Cu 钎料的基础上添加La,Ce混合稀土,研究了La,Ce对钎料组织及力学性能的影响。结果表明,随着稀土元素含量的增加,Al-Si-3Zn-15Cu钎料合金的抗拉强度、铺展面积均逐渐增大。添加稀土的Al-Si-3Zn-15Cu合金的微观组织为α-Al固溶体+(Al+Si)共晶+(Al+Si+Cu)共晶+Si相。La,Ce混合稀土减少了杂质在晶界上的偏聚,降低了晶粒长大速度,细化了晶粒。稀土对第二相粒子进行变质,使其网状结构得以优化和改善,因而提高了钎料的强度和塑性。     

稀土Ce对H13钢CCT曲线的影响

通过测定无Ce和添加0.026%Ce的H13热作模具钢的连续冷却转变(CCT)曲线,研究了稀土元素Ce对H13钢CCT曲线的影响。结果表明,0.026%Ce加入H13钢中可起到净化钢液、改善组织、细化晶粒和消除未溶碳化物的作用,并使珠光体转变和贝氏体转变曲线左移,珠光体相变和贝氏体相变提前,珠光体(A+P+C)和贝氏体(A+B+C)转变区域变大,马氏体(A+M+C)转变区域相应缩小。Ce的加入使H13钢的硬度增大,且硬度随冷却速度的增加而增大。     

BAg17CuZnSn-xCe钎料组织及性能分析

通过向BAg17CuZnSn钎料中添加微量的稀土元素Ce,研究了微量Ce元素的添加对低银钎料组织及焊接性能的影响.结果表明,当Ce元素质量分数为0.15%时,BAg17CuZnSn-0.15钎料在黄铜和不锈钢母材表面铺展面积较BAg17CuZnSn钎料分别提高了12.1%和37.4%,钎焊接头的抗剪强度达到最大值340.2 MPa.随着Ce元素的添加,钎料的自腐蚀电位逐渐正移,钎料的耐腐蚀性能得到提升.Ce元素对BAg17CuZnSn-xCe钎料基体中的CuZn化合物相有明显的细化作用,当Ce元素质量分数为0.15%时,钎料组织最为细小、均匀.但是当Ce元素质量分数达到0.5%时,钎料中出现了Ce-Sn化合物相.     

稀土Ce对激光熔覆高硼贝氏体涂层性能的影响

利用激光熔覆制备了不同Ce含量的高硼贝氏体涂层.采用扫描电镜对不同Ce含量的涂层组织进行表征;利用显微硬度计检测熔覆层显微硬度;通过万能拉伸机测试熔覆涂层的断裂韧性;用往复摩擦磨损试验机测试涂层的磨损性能.结果表明:经稀土Ce改性后,初生奥氏体晶粒尺寸减小,晶间网格状硼化物形态得到改善,呈现断网或颗粒状.三点弯曲断裂韧...     

稀土Ce对4Cr5MoSiV1钢组织的影响

对不同稀土Ce含量的4Cr5MoSiV1试验钢经热加工处理后的显微组织进行了观察和分析,研究Ce含量对其显微组织的影响。结果表明,稀土Ce的加入,使4Cr5MoSiV1钢铸态、锻态、正火和球化退火态的组织得到改善,晶粒细化、夹杂物变性、成分偏析减轻、未溶碳化物消除。但当稀土Ce含量超过0.026%时,上述改善作用逐渐减弱,甚至起到恶化的效果。     

Creep behavior of SnAgCu solders with rare earth Ce doping

Extensive testing was carried out to study the effects of rare earth Ce doping on the properties of SnAgCu solder alloys.The addition of 0.03%(mass fraction) rare earth Ce into SnAgCu solder may improve its mechanical properties,but slightly lower its melting temperature.The tensile creep behavior of bulk SnAgCuCe solders was reported and compared with SnAgCu solders.It is found that SnAgCuCe solders show higher creep resistance than SnAgCu alloys.Moreover,Dorn model and Garofalo model are successfully used...