白云鄂博稀土混合精矿工艺矿物学研究

目前白云鄂博稀土元素的提取主要采用重污染和高能耗的高温浓硫酸焙烧法,“三废”问题至今没有得到合理的解决,且钍元素作为一种伴生组分难以得到再回收利用。本文采用自动矿物分析仪,X射线衍射分析,扫描电镜分析,配分分析,光学显微镜等分析方法对白云鄂博稀土混合精矿的化学成分,矿物组成,粒度及嵌布特征等进行了工艺矿物学研究,结果表明：该稀土混合精矿REO品位59.25%,主要稀土矿物由氟碳铈矿,独居石和氟碳钙铈矿组成,主要脉石矿物为磷灰石、萤石、黄铁矿和磁/赤铁矿。在矿物中主要分布的稀土元素为La、Ce、Pr、Nd、Sm、Gd。矿样中矿石-38 μm占95.92%,氟碳铈矿和独居石单体解离度均在55% 以上,矿石整体嵌布特征较为复杂,稀土矿物与萤石和磷灰石的连生关系最为密切。为简化冶金工艺,高效提取稀土元素,本文提出了采用矿相转化后“浮少抑多”的方法分离氟碳铈矿和独居石的展望,为白云鄂博稀土混合精矿的合理开发应用提供新思路。     

白云鄂博尾矿稀土的工艺矿物学研究

通过偏光显微镜,矿物自动定量分析系统(AMICS)、扫描电子显微镜,能谱分析仪结合化学分析等分析手段对白云鄂博尾矿的物质组成,稀土矿物嵌布特征、稀土元素赋存状态等进行研究。结果表明：尾矿中稀土的含量(REO)为6.42%,稀土矿物主要为氟碳铈矿和独居石,脉石矿物主要有白云石、方解石、石英、长石、闪石、辉石、云母、重晶石和磷灰石等;稀土矿物嵌布粒度细小,氟碳铈矿与独居石单体解离度分别为55.07%、50.47%,与脉石矿物嵌布关系极为复杂。约95%的稀土元素赋存于稀土独立矿物中,约百分之五的稀土以类质同象或细小包裹体分散在其它矿物中。基于上述稀土矿物的嵌布特征及稀土元素的赋存特点,推荐采用分级一磨矿一浮选流程进行试验,以实现稀土矿物的有效回收。     

白云鄂博云母型铁矿石中铁、稀土的赋存状态研究

白云鄂博云母型铁矿石中TFe品位为17.48%,稀土REO品位为2.46%。矿石中矿物组成复杂,含铁矿物主要是磁铁矿和赤铁矿,含有少量铌铁矿、黄铁矿等,稀土矿物以氟碳铈矿和独居石为主。矿石构造主要由黑云母定向排列而成的片状构造、斑杂状构造及浸染状构造;矿物主要为自形-半自形粒状结构、他形粒状结构、尖角状结构、交代残余结构、细脉状结构。磁铁矿多呈半自形至他形粒状变晶结构形式出现,部分呈角砾状集合体与云母共生;赤铁矿多呈半自形和他型粒状结构,也有部分赤铁矿呈微细粒粒状嵌布在脉石矿物中;氟碳铈矿和独居石呈粒状,与周边其它矿物紧密共生、镶嵌关系复杂。磁铁矿和赤铁矿的嵌布粒度不均,氟碳铈矿和独居石的嵌布粒度较细,部分细粒铁矿石和稀土矿物嵌布在脉石矿物中,部分铁矿石中也含有细粒稀土矿物。磨矿细度-0.074 mm占90%下磁铁矿、赤铁矿、氟碳铈矿和独居石的单体解离度仅为51.54%、58.36%、52.27%和63.64%。因此,强化矿石细磨和微细粒高效分选是解决精矿品位和回收率低的有效途径。      

白云鄂博稀土精矿镨钕配分变化规律研究

针对白云鄂博稀土精矿镨、钕配分合量降低的问题,采用配分分析、粒度分析、物相分析、矿物组成分析研究了稀土分选流程中镨、钕配分合量的变化规律。结果表明:稀土精矿中镨、钕配分合量为19.59%,相对入选给矿(强磁尾矿)降低了1.18个百分点;随着矿物粒度的减小,REO-F分布率逐渐降低,镨、钕配分合量与粒度分析结果相矛盾;相对入选给矿(强磁尾矿),稀土精矿中氟碳铈矿与独居石矿物含量比值增加了0.41,稀选尾矿降低了0.50;由于氟碳铈矿镨、钕配分合量低于独居石,故镨、钕配分合量在稀土精矿中降低,在稀选尾矿中升高。该研究对白云鄂博矿稀土元素的回收利用具有一定的指导意义。     

白云鄂博萤石型稀土-铁矿石工艺矿物学研究

针对白云鄂博矿铁、稀土精矿品位低,杂质含量高的问题。以萤石型稀土-铁矿石为研究对象,进行系统的工艺矿物学研究,结果表明：①矿石铁品位为16.92%,稀土REO品位为7.68%,F含量为19.49%(主要是萤石),铌可综合回收。②矿石含铁矿物主要为磁铁矿,赤铁矿含量较低,稀土矿物主要为氟碳铈矿和独居石,主要的脉石矿物为辉石、磷灰石、重晶石、方解石等。③磁铁矿多以半自形至它形粒状结构形式出现,呈浸染状分布或充填在各种矿物粒间,大多与萤石、氟碳铈矿共生,以细粒磁铁矿为主。赤铁矿大多与萤石紧密共生,主要分布于萤石和白云石粒间。④氟碳铈矿是主要稀土矿物,多呈圆粒状或者椭圆粒状,常以条带状集合体、星散状或不规则粒状集合体、微细粒包裹体三种形式产出。独居石多以单颗粒形式呈浸染状与萤石紧密共生,分布于萤石粒间或萤石与白云石接触部位。⑤矿石中磁铁矿主要分布在15.00~74.00μm,分布率为66.69%,氟碳铈矿和独居石的嵌布粒度细,-43.00μm分别占96.39%和88.93%。因此,为提高铁、稀土精矿品位,需要更细的磨矿细度使有用矿物单体解离。     

白云鄂博尾矿中铌、稀土的赋存状态研究

采用化学分析、X射线荧光光谱、ICP-MS、SEM及AMICS等分析方法对白云鄂博尾矿库尾矿中铌、稀土的赋存状态及相应矿物产出特征进行研究。结果表明,尾矿中元素种类较多,矿物组成非常复杂,嵌布粒度很细。尾矿中的稀土矿物主要是氟碳铈矿和独居石,且比例约为2∶1,稀土矿物主要与铁矿物、萤石连生。尾矿中的铌主要以独立矿物形式存在,其次以类质同象形式存在。在铁矿物、稀土矿物及硅酸盐矿物中的铌包括类质同象和微细包裹体两种,而在萤石、碳酸盐、重晶石、石英中,铌以微细粒独立铌矿物包裹体存在。稀土、铌矿物的解离度不高,因此是矿物选别难度所在。此研究结果对白云鄂博稀土尾矿的高效综合利用具有一定的指导意义。     

白云鄂博铁矿石工艺矿物学研究

为了更好地开发利用白云鄂博铁矿石资源,对白云鄂博铁矿石进行了工艺矿物学研究。结果表明：①矿石中的有用矿物主要为磁铁矿、赤铁矿、稀土矿物,脉石矿物主要有萤石、石英、钠辉石、方解石、长石等。②矿石中的主要铁矿物为磁铁矿,以碎屑状及角砾状为主,占磁铁矿总量的70%以上,与钶铁矿、磷灰石、独居石、重晶石等紧密共生,偶见粗粒块状磁铁矿集合体;矿石中的赤铁矿多紧密镶嵌在碎屑状及角砾状磁铁矿中构成铁矿物集合体。③独居石是矿石中分布最广的稀土矿物,呈粒状,与周边其他矿物紧密共生、镶嵌关系复杂。④矿石中的脉石矿物均呈不规则状或他形粒状,脉石矿物间以及脉石矿物与有用矿物间嵌布关系均非常密切,萤石是分布最广的脉石矿物,是细小稀土矿物颗粒的包裹矿物之一。⑤矿石中铁矿物的嵌布粒度均非常细小,磁铁矿较赤铁矿略粗,嵌布粒度大于10 μm的赤铁矿、磁铁矿分别仅占40%和54%。⑥由于矿石中各矿物的嵌布关系复杂,嵌布粒度微细,单体解离困难,因此,宜采用深度还原工艺使微细粒铁矿物聚集长大后再进行回收。     

高品位稀土精矿中稀土、铁、磷、钙元素赋存状态研究

白云鄂博混合稀土精矿稀土品位65.86%,杂质元素P₂O₅、CaO、TFe含量分别为11.26%、3.89%、1.34%。实验采用化学分析、AMICS(自动矿物分析系统)、SEM及EDS等分析手段,研究混合稀土精矿中的稀土及杂质元素赋存状态。研究结果表明：稀土主要以独立矿物形式存在于氟碳铈矿、独居石、氟碳钙铈矿和黄河矿,铁主要存在于磁/赤铁矿和黄铁矿中,磷主要赋存于独居石和磷灰石中,钙主要赋存于萤石、磷灰石、白云石和方解石中,为进一步分选氟碳铈矿和独居石精矿,及降低稀土精矿中杂质元素含量提供矿物学依据。     

氟碳铈矿与独居石矿浮选分离的研究

氟碳铈矿与独居石矿是包头白云鄂博矿中两种主要的稀土矿物,只有将其分离成单一的氟碳铈矿和独居石矿,才会有利于稀土矿的湿法冶金。以明矾为抑制剂,邻苯二甲酸为捕收剂,进行了从包头混合稀土精矿中浮选分离氟碳铈矿与独居石矿的研究,并且确定了实现这两种稀土矿物浮选分离的几个最佳工艺条件。试验结果表明:在弱酸性条件下,控制好明矾和邻苯二甲酸的用量,可以使氟碳铈矿与独居石矿有效分离。     

白云鄂博霓石型稀土-铁矿石工艺矿物学研究

采用化学分析、物相分析、场发射电镜、矿物分析系统等分析手段对矿石中化学元素、矿物组成、粒度组成和嵌布特征等进行研究。结果表明：矿石中TFe品位为17.50%,稀土REO品位为8.43%,此外,Nb₂O₅含量为0.055%,Sc₂O₃含量为0.0034%,可综合回收;矿石中矿物组成复杂,含铁矿物主要是磁铁矿,含有少量赤铁矿、黄铁矿等,稀土矿物以氟碳铈矿和独居石为主,含有少量黄河矿、氟碳钙铈矿;磁铁矿多以半自形结构及集合体形式产出,磁铁矿集合体中可见霓石和稀土矿物呈细脉状沿磁铁矿颗粒间隙分布,有时可见磁铁矿被霓石沿着边缘及裂隙交代;氟碳铈矿呈细脉状充填于磁铁矿裂隙中或氟碳铈矿集合体中可见脉状霓石和磁铁矿;独居石以椭粒状集合体分散嵌布在霓石中;偶尔可见独居石中包裹黄铁矿;氟碳铈矿和独居石的嵌布粒度较细,0.02mm以下粒级分别占55.87%、85.51%,需要极细的磨矿细度才能单体解离。研究结果对该矿石的高效综合利用具有一定理论指导意义。     

Current situation and future trend of China rare earth luminescent material industry

<正>Rare earth luminescent material is one of the most important application sectors of rare earths.China enjoys the exceptional advantage to develop rare earth luminescent material for its abundant rare earth resources.After several decades'endeavor,China's rare earth luminescent material industry,headed by rare earth phosphor for lamp and LED and high efficient rare earth energy-saving light source,has been gradually developed into a scale industry.China has become a major production base of rare earth phosphor for lamps and rare earth     

China rare earth market review

正June 1~10,2014Rare earth market remained weak.Quoted price of rare earth products was similar to that in May.There was no sign of recovery in downstream market.The market of NdFeB magnetic materials and phosphor was depressed.Catalyst,polishing powder and ceramic industries remained inactive.Demand from downstream industry was soft.Consumers purchased on their needs.Suppliers had strong intention to sell.Prices of rare earth products     

Annual Report analysis of Chinese rare earth-related listed companies in 2013

<正>Chinese rare earth-related listed companies have published their 2013 annual reports.It can be understood from their reports that production and operation activities of Chinese rare earth-related companies were still heavily affected by macro economy and industrial policies.They basically followed the steps of national economy.In 2013,world economy recovered slowly but the economy     

Market opportunities and challenges for rare earth polishing powder

正1.Status of rare earth polishing powder Rare earth polishing powder with high content of cerium oxide began to replace iron oxide for glass polishing and became one of the key materials in glass polishing process since 1940.Compared with traditional iron oxide,rare earth polishing powder has many advantages,such as fast polishing rate,high polishing quality and long service life.It can achieve good surface quality and improve operation conditions.For example,in lens polishing,the polishing work that cerium     

Baotou Research Institute of Rare Earths developed a new RE alloy preparation technology

正Pyrometallurgy Laboratory of Baotou Research Institute of Rare Earths had independently developed a new preparation technology of rare earth alloy for NdFeB.The alloy can remarkably enhance the coercivity of NdFeB magnet but also evidently reduce the production cost of the magnet.The new master alloy was prepared in the kA pilot-scale electrolytic cell by the independent technology.The rare earth master alloy can be used as the raw material for NdFeB.Compared     

矿用防爆轴流对旋主要通风机叶片ANSYS模态分析及应用

高效节能矿用防爆对旋主要通风机的叶片是主要通风机运行的关键部件,叶片在运行时不断受到气流的作用力,从而使叶片产生振动,当叶片振动的频率与叶片的固有频率接近时,容易产生共振从而导致叶片的断裂。一旦叶片断裂时,对主要通风机的安全运行产生致命的影响,从而导致矿山、化工等企业发生重大事故,将会产生不可估量的损失。基于有限元分析软件ANSYS,对高效节能矿用防爆轴流对旋主要通风机叶片进行模态分析及产生对应的六阶模态频率,对主要通风机叶片的运行频率、固有频率及产生的共振问题进行了原理分析,并且解决了叶片频率共振的问题,从而为主要通风机叶片结构设计提供理论依据,并对主要通风机叶片的安全运行提供保障。     

2013 NdFeB export analysis

<正>China totally exported nearly 24,000 tonsof NdFeB products during 201 3,including 18,825 tons of permanent magnet,valued USD 1.34 billion at an average price of 71.4 USD/kg;3,277 tons of NdFeB magnetic powder,valued USD 1 01 million at an average price of 30.9 USD/kg;1,334 tons of strip casting ribbon,with total export value of USD 74million at an average price of 55.3 USD/kg;and 586     

Market and recycling of NiMH battery

<正>Market status and future trend of NiMH battery1.Global market of small NiMH battery Global market size of small NiMH batteries declined year on year since 2011.The trend will continue to 2018,at the rate of 5%to 10%annually.Demand for small NiMH batteries will be stable gradually.Many electrical apparatuses are powered by the built-in lithium battery today,which is the main reason for the shrunk market of small NiMH batteries.But,for some products,small NiMH     

China rare earth market review

正September 1-10,2014 Affected by the National Day holiday,rare earth transaction was stagnant and the market showed a weak steady state.As there was no good news for downstream market,some products with flat demand would likely rally slightly for some time to     

唐口煤矿深部复杂开采工作面瓦斯分源涌出规律研究

研究工作面瓦斯涌出规律对工作面瓦斯治理有重要意义。为了得到唐口煤矿深部3号煤层复杂开采条件下工作面回采时期瓦斯涌出时空演化规律,选取6304工作面作为对象,采用实测方法研究6304工作面瓦斯涌出规律。结果表明:6304工作面瓦斯涌出量为6.534 m³/min,其中煤壁占34.27%,落煤占29.62%,采空区占36.11%;沿工作面倾向由低到高,瓦斯浓度整体为上升趋势,其中1—76号架工作面瓦斯浓度小于0.20%,76—102号架瓦斯浓度上升明显,最大为0.387%;上隅角的后部采空区是工作面的瓦斯主要涌出源,上隅角1号测点瓦斯浓度0.78%,上隅角周边3号、5号、7号、8号、9号测点瓦斯浓度平均为0.643%;周期来压时,上隅角瓦斯相对平时较高。研究为针对性的瓦斯分源监控与灾害防治提供基础。