激光熔覆纳米La_2O_3添加镍基合金涂层的显微组织与耐磨性研究（英文）

以激光工艺制备了添加纳米La_2O_3初料的镍基涂层。激光熔覆之前,高能球磨机充分混合的Ni60A和La_2O_3粉床预置于基体30CrM nS i Ni2A表面。La偏聚于枝晶间从而限制了二次枝晶的成长和熟化。显微组织得到了细化。由于更高的La富集,涂层上表面显微组织细化更为显著,这一现象的上述解释得到EPMA结果佐证。熔覆涂层经过RE显微组织细化和净化,硬度、耐磨性均相对基体金属显著提升,而涂层中裂纹和孔隙均未出现。涂层的摩擦系数曲线COF明显低于基体,磨擦体积损失率和显微硬度值分别是基体数值的1/10和4倍。     

In2O3对Ni60激光熔覆层的影响

向Ni60合金粉末中加入适量的In2O3选取合适的工艺参数，采用激光熔覆技术在45钢表面上获得了无裂纹的高质量熔覆层。对熔覆层显微组织进行了观察和分析，测试了熔覆层的显微硬度和摩擦磨损性能。结果表明，同未加入In2O3的Ni60激光熔覆层相比，加入适当比例In2O3的Ni60熔覆层，虽然硬度有所降低，但硬度分布更加均匀，且在该文摩擦条件下耐磨性提高。In2O3能够降低Ni60激光熔覆层裂纹敏感性的原因在于适量的In2O3能够抑制粗大块状硬质相的生长，改善枝晶分布，细化组织晶粒，提高涂层韧性。     

纳米Y2O3-Co基合金激光熔覆复合涂层的分析

采用纳米Y2O3和Co基合金粉末,并利用激光表面熔覆技术和堆焊技术在Ni基合金基体上制备了纳米Y2O3-Co基合金复合涂层.运用扫描电镜(SEM)等测试方法,研究了复合涂层的显微组织和显微硬度,通过磨损试验和腐蚀试验分析了激光熔覆涂层和单一堆焊层的耐磨性和耐蚀性.结果表明,激光熔覆层显微组织由熔合区、细等轴状枝晶区及粗枝晶区构成;激光熔覆层的显微硬度由堆焊层的512.8 HV提高到868.9HV;激光熔覆层的耐磨性提高了51.2倍,40 min磨损量由堆焊层的25.6 mg降低到激光熔覆层的0.5 mg;激光熔覆层在10%HCl、10% HNO3和10% NaOH中的耐腐蚀性均比堆焊表面有明显改善.     

Y2O3对原位自生TiC增强Ni基涂层组织和性能影响

采用氩弧熔覆的方法,以Ni60A自熔性合金粉末为粘结相,添加Ti粉、C粉和不同含量的稀土氧化物Y₂O₃,在16Mn钢基体上制备出TiC陶瓷颗粒增强金属基熔覆涂层. 运用XRD, SEM等手段对复合涂层的显微组织进行表征和分析,并对熔覆涂层的硬度及耐磨性进行了测试. 结果表明,适量添加Y₂O₃可以使涂层组织中枝晶的方向性减弱、同时细化涂层组织,使涂层组织更加均匀,涂层的硬度和耐磨性有显著提高. 添加2% Y₂O₃熔覆涂层的组织为最细,涂层具有较高的显微硬度和良好的耐磨性能.     

Ti811合金表面激光熔覆涂层微观组织及性能研究

目的研究Ti811合金表面激光熔覆涂层的微观组织及磨损性能。方法利用激光熔覆技术,在Ti811合金表面激光熔覆原位合成了Ti C+Ti B2增强镍基复合涂层。利用X射线衍射仪(XRD)、扫描电镜(SEM)、电子探针(EPMA)、显微硬度计和摩擦磨损试验机,系统地研究了熔覆层的物相组成、显微组织、显微硬度及摩擦磨损性能,并利用二维点阵错配度理论对Ti C的细化机理进行分析。结果激光熔覆涂层与基体呈良好的冶金结合,熔覆层生成物相主要由Ti C、Ti B2、Ti2Ni和γ-Ni组成,其中Ti C呈等轴枝晶状和花瓣状,Y2O3的(111)面与Ti C的(110)面之间的二维点阵错配度为6.813%,Y2O3作为Ti C的非均质形核核心为中等有效。熔覆层的平均显微硬度为913.93HV0.5,约为基体Ti811硬度的2.4倍。熔覆层摩擦系数稳定在0.45～0.52之间,磨损机理主要为粘着磨损与磨粒磨损。结论采用激光熔覆技术能够在Ti811合金表面成功制备Ni基复合增强涂层。熔覆层中Y2O3颗粒具有细晶强化、弥散强化、增加形核率的作用,熔覆层具有较高的显微硬度与良好的耐磨损性能。     

H13钢表面激光熔覆NbC/Ni60复合涂层组织及高温耐磨损性能

目的 研究NbC颗粒的加入量对H13钢表面激光熔覆NbC/Ni60复合涂层的组织、硬度和耐磨性的影响。方法 将Ni60合金粉末与NbC碳化物粉末球磨混合,采用激光熔覆技术,在H13钢基体表面制备不同NbC含量(质量分数分别为0%、10%、20%、30%)增强的NbC/Ni60合金复合涂层。采用电子扫描显微镜(SEM)、X射线衍射仪对复合涂层的微观组织和物相进行分析。借助显微硬度计,研究复合涂层的截面显微硬度分布规律。采用高温摩擦磨损试验机测试复合涂层在真空400℃下的摩擦磨损性能。结果 在激光熔覆NbC/Ni60复合涂层中,物相主要由γ-(Ni, Fe)固溶体、Ni₂Si、CrB、Cr₂₃C₆、NbC组成;熔覆层以胞晶和枝晶为主,NbC含量对复合熔覆层组织及形态具有显著影响,加入少量NbC可使熔覆层组织细化;在NbC的质量分数为20%时,大量弥散的Nb C颗粒在枝晶间呈聚集趋势;在NbC的质量分数为30%时,熔覆层中NbC相呈现块状、花瓣状形貌。NbC/Ni60复合涂层的硬度显著高于H13钢基体,随着NbC含量的增加,N...     

熔覆电流对氩弧熔覆FeCrNiCoMn高熵合金涂层组织及显微硬度的影响

采用氩弧熔覆工艺在Q235基体上制备了等摩尔比FeCrNiCoMn高熵合金涂层,采用倒置金相显微镜、自动转塔显微硬度计及3D激光共聚焦显微镜对高熵合金涂层组织及显微硬度进行了分析。结果表明,不同熔覆电流下,FeCrNiCoMn高熵合金涂层均主要由枝晶组织和枝晶间组织组成,且其枝晶间组织中均生成了大量纳米级的析出物。在180~190 A范围内,随熔覆电流的增大,组织显著细化,且枝晶间组织中纳米级析出物形状规则,分布均匀;熔覆电流增大至200 A,涂层组织过度粗大,枝晶间组织被破坏,枝晶间组织中纳米析出物形状、分布均不理想。不同熔覆电流下,FeCrNiCoMn高熵合金涂层表面显微硬度差别不大。180、190 A熔覆电流制备的涂层比200 A熔覆电流制备的涂层截面显微硬度分布更理想。     

激光熔覆原位析出增强颗粒热力学及显微组织研究

把理论与试验相结合,通过热力学理论计算,选择出合理的激光熔覆涂层体系,利用横流CO2激光器在铜合金表面激光熔覆Ni基复合材料涂层,原位自生陶瓷颗粒增强相.通过对激光熔覆涂层反应体系△GT的计算及XRD分析得知:TiB增强颗粒可以原位生成.利用OM、SEM和显微硬度计,分析测定涂层的显微组织形貌和截面显微硬度分布情况.结果表明:熔覆层与基体具有良好的结合界面,涂层内枝晶组织细小均匀.熔覆层平均显微硬度比基体显著提高,约为基体平均硬度值的3倍.     

熔覆电流对AlCrFeCoNiCu高熵合金涂层显微组织的影响

采用氩弧熔覆工艺在06Cr19Ni10钢基体上制备等摩尔比AlCrFeCoNiCu高熵合金涂层。采用10%草酸溶液体系对不同熔覆电流制备的高熵合金涂层进行电解腐蚀,采用倒置金相显微镜观察试样显微组织,采用3D激光共聚焦显微镜对高熵合金涂层中的细小析出物进行微区三维显微形貌分析,并采用自动转塔显微硬度计对其截面显微硬度进行分析。结果表明,以不同熔覆电流制备的AlCrFeCoNiCu高熵合金涂层均由枝晶组织、枝晶间组织、块状析出物以及纳米级析出物组成。以240 A熔覆电流制备的涂层由于热输入过大,过热粗化的枝晶组织在凝固过程中发生臂端部位的熔解。240 A熔覆电流制备的熔覆涂层的表面硬度达到最高,但截面硬度较低。230 A熔覆电流制备的熔覆涂层的表面硬度、截面硬度均较理想。     

La2O3含量对激光熔覆TiB/Ti涂层显微结构的影响

目的 改善钛合金表面激光熔覆复合涂层的组织结构,提高钛合金的硬度,使其在相应领域得到更广泛的应用.方法 采用激光熔覆快速非平衡合成方法 制备原位反应合成L2O3-TiB增强钛基复合涂层.用L2O3、Ti和B的混合粉末在Ti-6Al-4V基体表面激光熔覆制备L2O3-TiB/Ti复合涂层,并对其进行XRD物相分析、SEM显微结构观察及显微硬度分析.结果 添加不同含量的L2O3的激光熔覆钛合金复合涂层均与基体较好的结合,涂层中均只有α-Ti和TiB两种物相.随L2O3含量的增加,激光熔覆复合涂层中的增强相TiB的形貌越均匀细小,添加不同含量的L2O3的激光熔覆复合涂层的硬度值约为基体材料的2~3倍,添加质量分数为3%的L2O3的激光熔覆复合涂层硬度最高,其显微硬度值大约为1300HV.结论 添加稀土氧化物L2O3后制备的激光熔覆钛合金复合涂层与基体结合良好,稀土元素的添加使涂层组织细化,硬度得到了明显提高.     

原位生成 WC-B4C 增强镍基激光熔覆层及其性能研究

目的通过激光熔覆技术,在Q235钢表面原位生成WC-B4C增强镍基熔覆层。方法以WO3,B2O3,C和Ni60混合粉末为预涂原料,采用激光熔覆技术原位生成WC-B4C增强镍基熔覆层,对熔覆层的显微组织和物相构成进行分析,研究其摩擦磨损性能。结果采用合适的工艺参数,通过原位生成WC-B4C形成的增强镍基涂层形貌良好,与基材呈现较好的冶金结合。熔覆层平均硬度1200HV0.3,摩擦磨损失重仅为纯Ni60熔覆层的1/3。结论熔覆层硬度较高,耐磨性很好。大量原位生成的WC-B4C增强相及其均匀分布是熔覆层硬度和耐磨性提高的原因。     

Amorphization of Fe38Ni30Si16B14V2 surface layers by laser cladding

Fe38Ni30Si16B14V2 amorphous composite coatings were fabricated by laser cladding on AISI 1045 steel in order to increase the wear resistance. The phase and microstructure of the coatings were analyzed by X-ray diffractometry and transmission electron microscopy. The wear properties of the coatings were also investigated by means of sliding wear test. The results show that the coating consists of amorphous phase in majority and nanocrystalline phase in minority. The amorphous coatings can be obtained while the scanning speed is 3 500 mm/min and the laser power is 4.8 kW. With increase of the laser power, the amorphous phase in the coating increases when it is lower than 4.8 kW. A gradient distribution of the microhardness ranges from Hv0.2 1 208 to Hv0.2 891 in the coating from top surface of the coating to the substrate. The amorphous coating is found to possess better property of wear than AISI 1045 steel substrate.     

Microstructure and Sliding Wear Resistance of Laser Cladded WC/Ni Composite Coatings with Different Contents of WC Particle

The aim of this article was to address the effect of WC content on the microstructure, microhardness, and sliding wear resistance of laser cladded WC/Ni composite coatings. The content of WC particle in the feed powder varied in the range of 0-80 wt.%. Experimental results showed that the laser cladded coatings exhibited homogeneous microstructure without pores or cracks. By comparing with the 45# steel substrate, the microhardness of WC/Ni composite coatings was relatively high. The microhardness of coating increased with increasing the content of WC particles. The wear resistance of WC/Ni composite coatings was strongly dependent on the content of WC particle and their microstructure. When the WC content was lower than 40 wt.% in the feed powder, the wear rate of the coatings decreased with increasing WC content. The two-body abrasive wear was identified as the main wear mechanisms. For the coatings with WC content higher than 40 wt.% in the feed powder, their wear rate increased with increasing WC content. The three-body abrasive wear and fatigue wear were the main failures. The coating with 40 wt.% WC in the feed powder exhibited the best wear resistance.     

激光功率对 WO3-V2O5-C 镍基熔覆层硬度的影响

采用激光熔覆技术,在45#钢表面制备WO3-V2O5-C镍基熔覆层。分析了熔覆层的显微组织,测试了熔覆层的显微硬度,研究了熔覆粉末中WO3-V2O5-C的含量及激光功率对熔覆层硬度的影响。结果表明:采用WO3+V2O5+C质量分数为25%的熔覆粉末,以1.4 kW功率进行激光熔覆,所得熔覆层硬度最高,平均值高达1400HV0.3,可大大提高材料的耐磨性。     

Microstructure and properties of WC reinforced Ni-based composite coatings with Y2O3 addition on titanium alloy by laser cladding

ABSTRACT

In this study, WC reinforced Ni-based composite coatings with Y₂O₃ addition were deposited on Ti-6Al-4V titanium substrate by laser cladding. The phases, microstructure, microhardness and wear resistance of the composite coatings were studied by X-ray diffraction, scanning electron microscopy, transmission electron microscopy, microhardness tester and wear tester. The results showed that good metallurgical bonding was achieved between the composite coatings and substrate. The phases mainly were γ-Ni, TiC, TiB₂, Ni₃B, M₂₃C₆ and WC. Most of the WC was dissolved in small pieces of WC during the laser cladding process. The microhardness of the composite coatings was about 3 times that of the titanium substrate and the wear resistance of the composite coatings had a significant increase.     

6061铝合金表面激光熔覆稀土CeO_2+Ni60组织及摩擦磨损性能

为提高铝合金的表面性能,利用激光熔覆技术在6061铝合金表面制备了添加稀土Ce O2的Ni60熔覆层,并通过金相显微镜、SEM、显微维氏硬度计和摩擦磨损试验机等设备研究了CeO2对Ni60熔覆层组织结构、硬度及摩擦磨损性能的影响.结果表明,加入2%的Ce O2可有效地减少熔覆层中的裂纹、孔洞和夹杂物,促进晶粒细化,提高熔覆层的组织均匀性、表面硬度及耐磨损性能;在相同磨粒磨损条件下,CeO2+Ni60熔覆层的耐磨性是铝合金的7.1倍,是Ni60熔覆层的1.6倍;Ni60熔覆层可以显著降低铝合金表面摩擦系数,而添加稀土CeO2能提高Ni60熔覆层的摩擦系数稳定性,从而改善Ce O2+Ni60熔覆层的耐磨性能.     

激光能量密度对65Mn钢表面Ni60A/WC复合涂层摩擦磨损性能的影响规律

目的 改善旋耕刀65Mn钢的摩擦磨损性能,提高农机触土零部件的使用寿命。方法 采用激光熔覆技术在65Mn钢基体表面制备Ni60A/WC复合涂层。通过改变激光功率调节激光能量密度,在不同能量密度下制备Ni60A/WC复合涂层,观察并测试不同参数下复合涂层试样的宏观形貌、微观结构、物相组成、元素分布、显微硬度及摩擦磨损特性,研究激光能量密度对Ni60A/WC复合涂层组织演变及摩擦磨损性能的影响规律和机理。结果 Ni60A/WC复合熔覆层顶部主要有胞状晶和树枝晶,分布较紧密,熔覆层中部主要有树枝状晶,熔覆层底部主要为胞状晶和垂直交界面生长的枝晶,且分布均匀致密。随着激光能量密度的升高,熔覆层的熔高和熔深增加显著,WC硬质相颗粒发生分解,硬质相的数量明显减少,涂层的平均显微硬度降低。在激光能量密度为120 J/mm²时,熔覆层的平均显微硬度为587.1HV1.0,相较于基体,提升了约1.8倍。此时熔覆层的平均摩擦因数最小,为0.312,相较于基体,得到显著提升,摩擦磨损机制为轻微的磨粒磨损。经田间试验测试发现,在激光能量密度为120 J/mm²时制备的带有熔覆层的旋耕刀相较于无熔覆层的旋耕刀,其磨损质量降低了63%。结论 通过控制激光能量密度,可以有效调控Ni60A/WC熔覆层的硬度和耐磨性,可为农机触土易磨损件的减摩耐磨表面强化改性提供理论指导。     

TC4钛合金表面激光熔覆掺Y2O3复合涂层的显微组织和性能

目的提高钛合金表面的耐磨性能。方法在TiB_2:TiC=1:3的粉末配比下,添加不同质量分数Y_2O_3稀土氧化物,制备成膏状混合粉末。采用5 k W横流CO_2激光器,在TC4钛合金表面激光熔覆掺Y_2O_3的TiB_2和TiC粉末,制备耐磨性复合涂层。通过扫描电子显微镜(SEM)、X射线能谱仪(EDS)、X射线衍射仪(XRD)对激光熔覆层的微观形貌和组织成分进行了分析;用显微维氏硬度计对熔覆层的显微硬度进行了测量;用万能摩擦磨损试验机对熔覆层的耐磨性能进行了测试。结果添加4%Y_2O_3后,熔覆层中部组织明显细化,结合区由致密组织结构转变为晶须网状结构;熔覆层的最高显微硬度为1404.6HV0.2,是基体的3.7倍;熔覆层的磨损量减少了66.67%,且其摩擦系数有明显的降低。结论添加4%Y_2O_3对TC4钛合金表面激光熔覆TiB/TiC复合熔覆层耐磨性能有显著的提高。