氧化铝掺杂聚酰亚胺纳米复合薄膜的制备与性能研究

通过溶液法,成功地制备了氧化铝掺杂聚酰亚胺纳米复合薄膜。探讨了Al2O3用量对聚酰亚胺纳米复合薄膜拉伸强度、热性能、电气强度的影响。结果发现,当Al2O3的质量分数达到5％时,整个复合体系的拉伸强度达到最大,相对于聚酰亚胺母体,复合材料的拉伸强度提高了16％;当Al2O3用量较小时,对聚酰亚胺纳米复合薄膜的Td10的影响不大,但当Al2O3的质量分数超过15％时,Td10则随Al2O3用量的增加而下降;同时实验结果表明,Al2O3的引入可以在一定程度上改善其复合体系的电气强度。     

纳米分子筛/氧化铝复合材料的制备与表征

本文采用溶胶-凝胶法由自制的纳米分子筛和氧化铝制备纳米分子筛/Al2O3复合材料,做了制备纳米分子筛/Al2O3复合材料条件实验(如Al2O3凝胶浓度、煅烧温度、纳米分子筛和Al2O3配比等)。纳米分子筛/Al2O3复合材料进行了傅利叶变换红外光谱(FTIR)、X射线衍射仪(XRD)结构表征。测试了纳米分子筛/Al2O3复合材料的吸水率和吸油性,得出最佳吸水性和吸油性的制备条件。     

Preparation and evaluation of a nanocomposite of polythiophene with Al2O3

The polymerization of thiophene (TP), in bulk and in solution in CHCl₃ by FeCl₃ resulted in the formation of a polymer which was characterized by FTIR as polythiophene (PTP). High yield was realized in the latter case. The polymerization of TP with FeCl₃ and nanodimensional Al₂O₃ resulted in the formation of a nanocomposite which was partly dispersible in aqueous and non‐aqueous media. The dispersibility appeared to be higher when the polymerization was conducted in a suspension containing a higher amount of Al₂O₃. Scanning electron micrographs showed globular particles and the presence of clusters of composite particles. Transmission electron micrographic (TEM) analyses revealed the particle size of the composite to be in the range 22–74 nm. Thermal analyses (TG/DTA) revealed the outstanding stability of PTP–Al₂O₃ composites compared to that of PTP. The conductivity of PTP and of PTP–Al₂O₃ composite was of the order of 10^?3 S cm^?1 for samples doped with I₂. © 2003 Society of Chemical Industry     

Al2O3/ACF复合电极材料的制备及性能表征

以H₃PO₄预处理后的活性炭纤维(ACF)毡为原料,采用浸渍煅烧法制备Al₂O₃/ACF复合电极材料;通过扫描电镜(SEM)、比表面积及孔径分析仪(BET)、X射线衍射(XRD)、X射线光电子能谱(XPS)、傅里叶红外光谱分析仪(FTIR)对负载Al₂O₃前后活性炭纤维的微观结构与电化学性能进行表征,利用自制的电吸附装置对NaCl模拟废水进行电吸附性能测试。结果表明,采用浸渍煅烧法成功制备了Al₂O₃/ACF复合电极材料,Al₂O₃/ACF复合体表面及孔道中有絮状或颗粒状的Al₂O₃存在,比表面积从1244.37 m²·g^-1降为974.59 m²·g^-1;同时,Al元素含量为1.06%,Al₂O₃以无晶相无定形态存在于纤维表面;Al₂O₃/ACF表面形成一些Al O键的官能团,其比电容比ACF提高76.5%。负载Al₂O₃后的ACF电极材料电吸附性能增强,除盐效率较ACF原样电极提升了2.3倍,且电极具有可再生性。Al₂O₃/ACF复合材料可以作为电极材料用于去除废水中的无机盐离子。     

Preparation and property characterization of PAA/Fe3O4 nanocomposite

PAA/Fe₃O₄ nanocomposites were prepared by mixing nano-Fe₃O₄ and polyacrylic acid (PAA) ethanol solution and then evaporating the solvent. The materials were characterized by transmission electron microscope (TEM), Fourier transform infrared spectroscope (FTIR), thermogravimetry analysis (TGA), dynamic ultra-micro hardness tester (DUMHT) and superconducting quantum interference device (SQUID) magnetometer. Results showed that PAA coordinated with nano-Fe₃O₄ to form a cross-linking structure. The presence of nano-Fe₃O₄ enhanced the thermal stability of the nanocomposite. The elasticity and hardness of the nanocomposite increased, and the indentation depth reduced with the increase of Fe₃O₄ content in the composites. The nanocomposites showed superparamagnetic properties at 300 K. Translated from Acta Scientiarum Naturalium Universitatis Sunyatseni, 2006, 45(5): 47–50 [译自: 中山大学学报 (自然科学版)]     

Al2O歧化法制备微细Al2O3/Al复合粉体

真空条件下,以Al2O3和Al为原料,通过Al2O歧化法制备微细Al2O3/Al复合粉体.XRD和SEM分析表明:在反应温度为1200～1400℃时,随着温度的升高,粉体中氧化铝含量升高;冷凝温度约为550～750℃时,复合粉体中的氧化铝包括稳定晶型和不稳定晶型;冷凝温度约为1100～1300℃时,复合粉体中的氧化铝全部为稳定晶型;冷凝温度约为550～650℃时,复合粉体的平均粒径小于0.5μm;冷凝温度约为750℃时,铝熔化、微粒团聚;冷凝温度约为1100～1200℃时,铝形成铝珠,氧化铝为不规则状、平均粒径小于2μm;冷凝温度约为1300℃时,氧化铝为片状.因此,通过选取合适的反应温度、冷凝温度,可以控制Al2O3/Al复合粉体中氧化铝的含量、晶型和粒径.     

Preparation and characterization of Ce-ZrO2/Al2O3 composites by DLP-based stereolithography

This work investigates the printability of Ce-ZrO₂/Al₂O₃ composites through a Digital Light Processing (DLP) technology. Commercially available 10 mol% CeO₂ and 12 mol% CeO₂-stabilized zirconia were mixed with alumina powders, to provide 11 mol% CeO₂-stabilized ZrO₂/16 vol% Al₂O₃ (Ce-ZA₁₆) composite materials. The powders were dispersed under wet conditions, and the homogeneous nanometric dispersion was maintained once added into the liquid monomer. Slurries at several solid loadings were explored, with and without dispersant addition. First, the key role of the dispersant to significantly enhance the solid loading and thus the sintered density was demonstrated. Second, among different dispersant-added slurries at various solid loadings, ranging from 65 to 80 wt%, the best compromise between rheological behavior and curing depth was established. The best formulations, comprised between 70 and 80 wt%, successfully provided fully dense and completely homogeneous composites.     

聚酰亚胺／纳米Al2O3-SiO2和聚酰亚胺／纳米Si3N4杂化材料的结构与性能研究

将纳米Al2O3-SiO2、Si3N4分别均匀分散于聚酰亚胺（PI）前驱体聚酰胺酸中，经过热亚胺化制备了PI／纳米Al2O3-SiO2和PI／纳米鼠N4杂化材料。通过傅里叶变换红外光谱仪、X射线衍射仪、高温微量热天平、静态热机械分析仪和差示热分析仪对杂化材料的微观结构及热性能进行了研究，结果表明，杂化材料中聚酰亚胺和无机纳米粒子之间存在相互作用，形成了复合相态结构；加入纳米Al2O3，SiO2、Si3N4后杂化材料的热稳定性均高于纯聚酰亚胺，但并不完全随无机纳米粒子含量的增加而提高；与纯PI相比，在90～130℃的温度范围内PI-8％Al2O3-SiO2、PI-8％鼠Si3N4热膨胀系数分别降低了约11％和47％，加入8％纳米Al2O3-SiO2、Si3N4后杂化材料的热导率分别提高了约8％和13％。PI／纳米Al2O3-SiO2、Si3N4杂化材料不仅保留了PI原有的优异性能，而且充分发挥了纳米无机粒子对PI的特殊改性性能。     

一维纳米氧化铝载体的合成及表征

采用水热法合成了一维纳米氧化铝,并用XRD、N2吸附-脱附、FT-IR、SEM、TEM以及HRTEM等手段对样品进行了表征,结合高分辨图像和FT-IR表征结果对其暴露晶面进行研究,探讨暴露晶面与表面羟基的关联,探索氧化铝一维结构形成机制。结果表明,合成的样品为单晶纳米棒,长度主要集中在（100~150） nm,宽（10~15） nm,结晶度高,孔径最可几分布为25 nm,孔径较大,表面存在四面体-八面体桥连羟基（Ⅱa型）和八面体三键桥羟基（Ⅲ型）,暴露晶面主要是（100）晶面和（111）晶面。n（OH^-）∶n（Al³⁺）决定一维结构的形成。     

Low pressure plasma-sprayed Al2O3 and Al2O3/SiC nanocomposite coatings from different feedstock powders

This paper describes a preliminary investigation of a nanocomposite ceramic coating system, based on Al₂O₃/SiC. Feedstock Al₂O₃/SiC nanocomposite powder has been manufactured using sol-gel and conventional freeze-drying processing techniques and then low pressure plasma sprayed onto stainless steel substrates using a CoNiCrAlY bond coat. Coatings of a commercial Al₂O₃ powder have also been manufactured as a reference for phase transformations and microstructure. The different powder morphology and size distribution resulting from the different processing techniques and their effect on coating microstructure has been investigated. Phase analysis of the feedstock powders and of the as-sprayed coatings by X-ray diffractometry (XRD) and nuclear magnetic resonance (NMR) showed that the nano-scale SiC particles were retained in the composite coatings and that equilibrium α-Al₂O₃ transformed to metastable γ- and δ-Al₂O₃ phases during plasma spraying. Other minority phases in the sol-gel Al₂O₃/SiC nanocomposite powder such as silica and aluminosilicate were removed by the plasma-spraying process. Microstructure characterisation by scanning electron microscopy (SEM) of the as-sprayed surface, polished cross-section, and fracture surface of the coatings showed evidence of partially molten and unmolten particles incorporated into the predominantly lamella microstructure of the coating. The extent of feedstock particle melting and consequently the character of the coating microstructure were different in each coating because of the effects of particle morphology and particle size distribution on particle melting in the plasma.     

氧化铝/环氧树脂/聚氨酯导热复合材料的制备及表征

采用硅烷偶联剂KH550对氧化铝表面进行改性,并以改性氧化铝为导热填料,以环氧树脂为基体树脂,自制的聚氨酯预聚体为柔性改性剂,制备了氧化铝/环氧树脂/聚氨酯导热复合材料。采用红外光谱对KH550改性氧化铝的结构进行了表征,探讨了影响复合材料热导率的主要因素,研究了改性氧化铝用量对复合材料力学性能的影响,并利用扫描电镜对复合材料的微观结构进行了观察。结果表明,KH550已通过化学键接枝在氧化铝表面。随着KH550改性氧化铝用量的增加,复合材料的拉伸强度逐渐增大,而导热率和断裂伸长率呈现先上升后下降的趋势。当改性氧化铝的用量为150 phr时,复合材料的导热率达到最大值0.66 W/(m·K),拉伸强度和断裂伸长率分别为37.2 MPa和1.62%。随着m(PUA)/m(EP)的增大,复合材料的导热率相应下降,适宜的m(PUA)/m(EP)为15/85。     

负载型纳米FeOZrO2/Al2O3催化剂的制备

主要研究制备以大孔A12O3,为基载体的负载型纳米FeOZrO2/Al2O3,复合载体.采用溶胶-凝胶法制备负载型纳米FeOZrO2/Al2O3,复合载体.利用比表面、透射电子显微镜(TEM)等对载体催化剂进行了表征.结果表明:负载型纳米FeOZrOJhl203复合载体的比表面积达到76.53 sq·m/g,FeOZrO2/Al2O3,中的FeO粒子约为40nm,较Fe0/Al2O3中FeO的粒子(100nm)小且分布均匀.     

电泳沉积氧化铝陶瓷涂层的制备及耐腐蚀性能

以氧化铝溶胶为前驱体,采用电泳沉积和低温煅烧法在低碳钢基体上制备了氧化铝陶瓷涂层,并对其成分、表面形貌及耐蚀性进行了研究。结果表明,将低碳钢片置于以乙醇作为分散介质的0.45mol/L氧化铝溶胶中,在60V恒电位下沉积180s后,再于马弗炉中700°C下煅烧5min,所制得的氧化铝陶瓷涂层在2mol/L盐酸溶液中具有良好的耐蚀性。     

High-temperature mechanical property and thermal shock resistance of Al2O3f/Al2O3 composites

Continuous alumina fiber–reinforced alumina matrix composites (Al₂O_3f/Al₂O₃ composites) were produced via sol–gel process, then the high-temperature mechanical property and thermal shock resistance of Al₂O_3f/Al₂O₃ composites were investigated. The results showed that the composites exhibited excellent high-temperature properties. The mechanical property of the composites was affected by heat treatment (prepared at 1100°C exhibited the most desirable mechanical property). The tensile strength of the composites abruptly decreased at higher temperatures. Although the mechanical property of the composites deteriorated after the thermal shock test was conducted at high temperatures, they exhibited excellent thermal shock resistance. After 50 thermal shock tests conducted at 1300 and 1500°C, the flexural strength of the composites was found to be 124.34 and 93.04 MPa, thus showing a decrease in strength with the increasing temperature.     

3Y-ZrO2/Al2O3复合粉体制备工艺研究

以Al(NO3)3·9H2O和ZrOCl2·8H2O为主要原料,采用醇-水溶液加热结合共沉淀法制备出前驱体。利用DTA-TG和X射线衍射(XRD)分析研究了前驱体的煅烧过程。结果显示,275℃时前驱体已完全分解为非晶态氧化物,800℃时t-ZrO2开始结晶,至1150℃时出现α-A12O3晶体,获得3Y-ZrO2/A12O3复合粉体。该复合粉体在1400℃下常压烧结,可得到相对密度达90.4%的ZTA陶瓷。     

一种新型W/O型微乳液制备超细Al2O3粉体的实验研究

向PEG+正丁醇/正庚烷/水溶液 (NaAlO2 )超声乳化后的W/O微乳液中通入CO2,将制得的凝胶焙烧后制备出了粒度100nm左右的Al(OH)3凝胶与Al2O3超细粉体,实验结果表明:乳化温度、表面活性剂与助表面活性剂之比及偏铝酸钠浓度是影响粉体粒度的主要影响因素.     

Al2O3/Al复合材料的制备及性能研究

本文采用液相法和热压烧结制备出Al203／Al复合材料,并利用DSC／TG、SEM、显维硬度计及万能试验机测试研究了复合材料的热学性能、微观结构及力学性能。结果表明,引入Al后复合陶瓷的断裂韧性有显著提高。     

用于二乙醇胺脱氢的Cu/ZnO/Al2O3/ZrO2催化剂的制备与表征

以氢氧化钠为沉淀剂,硝酸铜、硝酸锌、硝酸铝和硝酸氧锆为原料,采用共沉淀法制备出了用于二乙醇胺脱氢制亚氨基二乙酸的Cu/ZnO/Al2O3/ZrO2催化剂,并用物理吸附(BET)和X射线衍射(XRD)对不同种类的铜基催化剂进行了表征,探讨了ZnO和Al2O3的不同比例对催化剂性能的影响。结果表明,同时加入ZnO和Al2O3的Cu/ZnO/Al2O3/ZrO2催化剂具有大的比表面积,Cu/ZnO/Al2O3/ZrO2催化剂具有非晶态结构。该催化剂适宜的反应条件为:w(NaOH)=30%、反应温度160℃、压力1.0 MPa,二乙醇胺转化率可达100%,亚氨基二乙酸收率可达95.61%。     

Preparation of Al2O3@CaCO3 aggregates and its effects on the thermal shock resistance of Al2O3-MgO castables

Al₂O₃@CaCO₃ aggregates were prepared by impregnating corundum aggregates (particle sizes with 3-1 and 5-3 mm) in precursor solutions (Calcium hydrogen citrate, CaHC₆H₅O₇) followed by heat treatment at 430°C. The phase composition and microstructure of the coatings were characterized via X-ray diffraction and scanning electron microscope, respectively. The novel aggregates were used in Al₂O₃-MgO castables. The effects of the Al₂O₃@CaCO₃ aggregates on the physical properties and thermal shock resistance (TSR) of castables were investigated. The results show that uniform CaCO₃ coating of aggregates (C15) with thickness about 10 µm can be attained when the concentration of Ca²⁺ in solution was 0.15 mol L⁻¹. There was a strong bonding between the aggregates and coating that was constituted by particles with size about 0.2 µm. Both improving physical and TSR properties of the castables are related with the unique layer structure, calcium hexaluminate (CA₆) layer in-situ formed at the aggregate-matrix interface, of added Al₂O₃@CaCO₃ aggregates. There is a mass of multi-deflection of cracks along with the CA₆ layer which consumes more fracture surface energy. The castables with C15 exhibit optimal TSR and the residual strength ratio after the thermal shock test is 29.5%, which is 12.8% higher than the castables with corundum aggregates.     

氧化铝/ZTA强夹层层状复合陶瓷的制备和性能

本实验以氧化铝和ZTA为研究对象,制备出ZTA/Al2O3强夹层层状复合陶瓷,复合陶瓷的冲击韧性是单相Al2O3陶瓷的5.6倍,单相ZTA陶瓷的2.8倍;而且复合陶瓷的断裂韧性和维氏硬度在平行于夹层方向和垂直于夹层方向差别不大,克服了弱夹层陶瓷各向异性的缺点.