中海36-1AH-90沥青的SBS改性

对中海36-1原油生产出的AH-90沥青进行SBS改性要在190℃左右温度下进行生产.随着改性剂的增加,改性沥青针入度降低,软化点升高,PI提高;稳定剂对改性沥青软化点、粘度等指标有较大影响,要选用适合的稳定剂添加量;相容剂对改性沥青针入度、低温延度有较大影响,要选用合适的相容剂添加量.     

化学助剂对SBS改性沥青的性能影响初探

通过加入化学助剂制备一种反应性SBS改性沥青,研究助剂加入量对改性沥青性能及高温储存后性能影响,对比其与高速剪切工艺所得改性沥青性能差异,并利用荧光显微照片分析两者微观形态的不同。结果表明：改性沥青性能随着助剂加入量增加先变好后变差。助剂加入量为0.6%时,改性沥青低温和高温性能最好;高温储存后延度与老化延度有一定的下降,针入度与软化点变化较小;加入助剂比高速剪切制得的改性沥青的低温性能和储存稳定性更好;荧光显微照片显示,剪切后SBS以颗粒的形式分散在沥青中,而加助荆使SBS与沥青形成均匀连续的网状结构。     

不同老化方式对SBS改性沥青的性能影响

通过对薄膜烘箱老化、PAV老化和紫外老化等不同老化方式下,SBS改性沥青老化前后的针入度、5℃延度、软化点、135℃动力黏度以及弹性恢复等性能变化影响规律进行试验研究。结果表明:老化后SBS改性沥青的5℃延度与135℃运动黏度变化幅度显著,老化作用对SBS改性沥青的高、低温性能影响显著;TFOT短期老化后,SBS改性沥青性能已发生大幅下降,在长期使用过程(紫外老化、PAV老化)中,随老化时间的延长,SBS改性沥青性能衰减幅度逐渐减小。     

机场道面SBS改性沥青适宜储存时间及储存关键控制指标研究

采用不同热储存时间的机场道面专用SBS改性沥青RTFOT老化前后针入度、软化点、延度、黏度指标以及不同储存时间的沥青制备的沥青混合料高温、低温、水稳定性能指标评价了热储存时间对SBS改性沥青及混合料性能影响。结果表明,随SBS改性沥青热储存时间延长,RTFOT老化前后沥青针入度、软化点及5℃延度均减小,沥青储存4 d后135℃黏度及储存5.7 d后5℃延度(RTFOT老化后)已不满足规范(MH/T 5011—2019)要求;混合料单轴贯入强度增加,弯曲极限应变、残留稳定度及冻融劈裂强度比均减小,对于冬严寒区及寒冷区,沥青储存5.1 d后混合料低温指标已不满足规范要求。根据试验结果和规范对沥青及沥青混合料指标最低要求,推荐将135℃黏度、混合料弯曲极限应变及RTFOT老化后的5℃延度作为评价SBS改性沥青适宜储存时间的关键控制指标,建议机场道面SBS改性沥青热储存时间不宜大于4 d。     

胶体磨法生产SBS改性沥青产品质量变化分析及控制

对胶体磨法生产SBS改性沥青产品的主要质量指标针入度、软化点、5℃延度的变化情况进行了考察和原因分析,结果证明通过控制储存过程的温度与时间可以将产品质量的变化控制在合理的范围内。     

工艺条件对SBS改性沥青性质的影响

通过稳定剂加入次数、加入方式、星型SBS加入方式,研究了工艺条件对改性沥青性质的影响。研究发现,稳定剂加入次数越多,改性沥青的软化点越高,薄膜烘箱老化后延度越好。通过剪切方式加入稳定剂和加入SBS得到的改性沥青延度性质更稳定,薄膜烘箱老化前和薄膜烘箱老化后延度变化幅度减小。     

SBS改性沥青性能探究

论文以30#、50#低标号沥青作为基质沥青,采用SBS对基质沥青进行改性,SBS改性实验结果表明:当SBS掺量为0-6%时,随着SBS掺量的增加,30#与50#改性沥青的针入度逐渐降低,软化点逐渐升高,即改性沥青的高温性能提高,改性沥青的抗老化性能以及高温延度得到明显改善;但SBS对改性沥青的低温性能影响较小。     

SBS改性沥青低温延度影响因素分析

阐述了SBS改性沥青低温延度的主要影响因素。通过对基质沥青针入度、反应温度、循环剪切时间及储存条件等进行优化和控制，可提高产品低温延度质量，延缓产品的老化，储存周期明显改善。     

改性剂类型对废胶粉/SBS复合改性沥青性质的影响机理研究

以中油燃料油股份有限公司高富炼油厂生产的50号重交道路沥青为基质沥青,研究了不同化学结构的SBS和不同粒径胶粉对废胶粉/SBS复合改性沥青软化点、针入度、低温延度以及动力粘度的影响,研究表明：复合改性沥青的粘度明显比单一改性剂生产的改性沥青高,星型SBS对软化点和粘度的影响较大,合适粒径的胶粉对复合改性沥青性能的改善较大。     

SBS改性沥青生产工艺关键技术控制的研究

为了考察SBS改性沥青生产过程中剪切时间、剪切温度、剪切速率对SBS改性沥青性能的影响,采用ESSO 90号沥青为基质沥青,4303 SBS为改性剂进行试验研究。结果表明:剪切时间与SBS改性沥青的量有关,一般在45 min至2 h,剪切温度在170~175℃,剪切速率为6 000 r/min,此时,SBS改性沥青的路用性能指标最佳。     

Aging Performance of SBS Modified Asphalt

Abstract

The penetration, softening point, and ductility of the aging basic asphalt and styrene-butadiene-styrene (SBS) modified asphalt were studied, and the thin film oven aging behavior of them was researched by using infrared spectrum. The experimental results showed that the softening point was increased, the penetration and ductility were decreased after basic asphalt thin film oven aging; the results of aging SBS modified asphalt thin film oven aging was similar too. The research of infrared spectrum indicated that absorbing–oxygen oxidation reaction was taking place when basic asphalt film was aging, carbonyl and sulfoxide groups were increased after SBS modified asphalt thin film oven had been aging. The aging extent of SBS modified asphalt was bigger than basic asphalt and the ability of bearing low temperature was better. SBS modified asphalt could have worse anti-aging performances than that of base asphalt.     

废橡胶粉/SBS复合改性沥青制备研究

以SK AH-70为基质沥青,外掺废胶粉和SBS,采用高速剪切法制备复合改性沥青。通过正交实验考察了沥胶比、糠醛抽出油掺量和稳定剂掺量对沥青性能的影响,确定最优条件为:沥胶比为3,糠醛抽出油加入量4%,稳定剂加入量3‰。在最优条件下制备的复合改性沥青软化点为61.0℃,5℃延度为30.0 cm,弹性恢复为85%。废胶粉/SBS复合改性沥青的性能明显优于胶粉改性沥青,而稍低于SBS改性沥青,但是其成本低廉、易于施工,并且性能达到SBS改性沥青的相关要求,具有良好的应用前景。     

道路沥青及SBS改性沥青的紫外老化研究

采用紫外辐射试验对道路沥青和SBS改性沥青进行加速老化试验研究.利用老化前后的软化点、针八度、延度和四组分变化。分析了道路沥青的紫外线老化机理。结果表明:随紫外线老化时间的延长,道路沥青和SBS改性沥青软化点呈上升趋势、针入度和延度呈降低变化趋势,其中又以延度变化最为明显。经紫外线老化后道路沥青和SBS改性沥青的四组分也有变化,其中沥青质略微上升、芳香分略微降低,而饱和分和胶质变化不大。     

利用环氧化SBS改性镇海沥青的研究

采用环氧化SBS改性镇海沥青,研究了改性沥青的针入度、软化点、延度的变化规律,并探讨了环氧化SBS改性沥青的机理.实验结果表明,SBS牌号、ESBS改性剂的环氧基质量分数和加入量以及反应时间等条件郝影响改性沥青的三项指标.     

中海油改性沥青针入度与PG高温等级关系的研究

选取利用中海油36-1沥青制备的4种常用的中海油SBS改性沥青,分别进行针入度分级实验和多个温度下的动态剪切试验,测试沥青的25 ℃针入度、延度、软化点及其PG高温指标。在综合分析试验结果的基础上,提出了中海油改性沥青的针入度等级和PG高温等级之间的关系。二者相关系数达0.99以上,PG等级达到76 ℃时,25 ℃针入度应不大于66.5;PG等级达到82 ℃时,25 ℃针入度应不大于63.0。利用针入度能够较好地预估PG高温等级,为生产提供指导。     

SBS胶乳改性乳化沥青制备技术研究

研制了一种新型改性剂——SBS胶乳,用于对乳化沥青进行改性制备改性乳化沥青。通过考察乳化剂用量对改性乳化沥青贮存稳定性的影响,得出乳化剂的最佳用量(w)为1%;通过考察SBS胶乳对沥青软化点、延度和针入度的影响,得出SBS胶乳改性剂的最佳用量(w)为6%;由光学显微镜分析得出,SBS颗粒和沥青颗粒的大小、密度相近,这是保证SBS在体系中均匀分散的重要因素。根据确定的乳化剂和改性剂的最佳用量,制备出了性能优良的改性沥青乳液。