Microwave Dielectrics in the (La1/2Na1/2)TiO3–Ca(Fe1/2Nb1/2)O3 System

Dielectric properties of the system (1 − x)(La_1/2Na_1/2)TiO₃– _x Ca(Fe_1/2Nb_1/2)O₃, where 0.4 # x # 0.6, have been investigated at microwave frequencies. The temperature coefficient of resonant frequency (τ_f), nearly 0 ppm/°C, was realized at x = 0.58. These ceramics had perovskite structure and showed relatively low dielectric losses. A new dielectric material applicable to microwave devices having Q · f of 12000–14000 GHz and a dielectric constant (ε_r) of 59–60 has been obtained at 1300–1350°C for 5–15 h sintering.     

Reverse Micellar Route to Nanocrystalline Titanates (SrTiO3, Sr2TiO4, and PbTiO3): Structural Aspects and Dielectric Properties

Nanoparticles of strontium titanates (SrTiO₃, Sr₂TiO₄) and lead titanate (PbTiO₃) have been obtained using reverse micelles as nanoreactors. Powder X-ray diffraction studies of the powders after calcining at 800°C show monophasic SrTiO₃, Sr₂TiO₄, and PbTiO₃. X-ray line broadening studies and transmission electron microscopic studies show spherical grains of 30–40 nm size for strontium titanates, while PbTiO₃ is obtained in the form of nanorods. The dielectric constant of SrTiO₃ and Sr₂TiO₄ is found to be 90 and 30, respectively, (at 100 kHz) for samples sintered at 1000°C. PbTiO₃ shows a dielectric constant of 160 (at 100 kHz) after sintering at 900°C. The dielectric constant of Sr₂TiO₄ (with temperature) is highly stable. The temperature variation studies of the dielectric constant of PbTiO₃ show a ferroelectric phase transition at 490°C (1 kHz). The T _c varies with frequency and is found to decrease to 470°C at 100 kHz.     

Synthesis of 0.4Pb(Mg1/3Nb2/3)O3–0.3Pb(Mg1/2W1/2)O3–0.3PbTiO3 Ceramics by Metal Alkoxide Method, and Its Dielectric Properties

0.4Pb(Mg_1/3Nb_2/3)O₃–0.3Pb(Mg_1/2W_1/2)O₃–0.3PbTiO₃+ x MgO ( x = 0 to 0.04) were prepared by a metal alkoxide method. The percent of perovskite phase of the calcined powders increased with increased calcination temperatures. About 89% of perovskite phase was obtained at 1050°C. The dielectric constant of the pellets fired at 1100°C was increased by the addition of 10 wt% excess Mg(OC₂H₅)₂ and had a maximum value of 7532 at 1 kHz.     

Preparation and Characterization of Relaxor Ferroelectric 0.65Pb(Mg1/3Nb2/3)O3–0.35PbTiO3 by a Polymerizable Complex Method

A modified polymerizable complex (PC) method for the preparation of the relaxor ferroelectric 0.65Pb(Mg_1/3Nb_2/3)O₃–0.35PbTiO₃ (PMN–PT) ceramics has been developed using a novel water-soluble Nb precursor. The effects of Pb content and sintering temperature on the structure, morphology, composition, and electrical properties of PMN–PT powders and ceramics were investigated systematically. It was found that the modified PC method could effectively reduce the initial crystallization temperature of the perovskite phase to 500°C. For PMN–PT samples with 15% excess Pb content sintered at 600°C for 2 h, the 87% perovskite phase can be achieved, which is much higher than that in conventional solid-state reactions and other solution-based methods at the same temperature. On further increasing the sintering temperature to 1100°C, the perovskite phase content basically remains constant. This is attributed to the Pb-deficient pyrochlore phase formation. On increasing the sintering temperature to 1250°C, the dielectric constant and remnant polarization of PMN–PT ceramics significantly improved due to the larger grain sizes, enhanced density, and the decreasing pyrochlore phase. PMN–PT ceramics with a 98.5% content of the perovskite phase have been fabricated at 1250°C. It displays typical ferroelectric relaxor characteristics with a remnant polarization of 18 μC/cm², a coercive field of 9.6 kV/cm, a piezoelectric coefficient of d ₃₃=360 pC/N, and room-temperature and maximum dielectric constants of 3600 and 10 500 at 1 kHz, respectively.     

Processing and Electrical Properties in Lead-Based (Pb(Mg1/3Nb2/3)O3, Pb(Yb1/2Nb1/2)O3, PbTiO3) Systems

Lead-based ferroelectric (FE) ceramics exhibit superior electromechanical properties; therefore, there has been an increased focus on developing new lead-based FE materials with high Curie temperature ( T _c) and enhanced properties. The aim of this study was to investigate new compositions in the Pb(Mg_1/3Nb_2/3)O₃–Pb(Yb_1/2Nb_1/2)O₃–PbTiO₃ ( PMN–PYbN–PT) system to enhance the electromechanical properties while increasing the T _c and lowering the sintering temperature. The 0.575[0.5PMN–0.5PYbN]–0.425PT composition at PMN/PYbN (50/50) mole ratio were prepared by reactive sintering PMNT and PYbNT powder mixtures at 950°–1200°C for 4 h. PMNT and PYbNT powders were calcined via the columbite method. Samples were prepared by cold isostatic pressing at 80 MPa. Dense and fully perovskite 0.575[0.5PMN–0.5PYbN]–0.425PT ceramics were fabricated at 975°C for 4 h, and these samples displayed a remnant polarization ( P _r) of 32 μ C/cm², coercive field ( E _c) of 17 kV/cm, and a piezoelectric charge coefficient ( d ₃₃) of 475 pC/N. It is proposed that this ternary system can be tailored for various applications.     

Synthesis of Pyrochlore-Free 0.9Pb(Mg1/3Nb2/3)O3-0.1PbTiO3 Ceramics via a Soft Mechanochemical Route

Single-phase perovskite 0.9Pb(Mg_1/3Nb_2/3)O₃-0.1PbTiO₃ (0.9PMN–0.1 PT) from a stoichiometric mixture of starting materials was synthesized by applying a mechanochemical technique to the stage of a precursor. A stoichiometric mixture of PbO, TiO₂, Mg(OH)₂, and Nb₂O₅ was milled for 60 min and heated at temperatures as low as 850°C for 4 h to obtain a single phase. The maximum dielectric constant of the samples from the milled mixture increased as the sintering temperature increased, with the remarkable grain growth, and attained 24600 at 1200°C. In contrast, poor densification and coexistence of the pyrochlore phase were observed on the samples from the nonmilled mixture. Further observation suggested that the pyrochlore phase concentrated near the surface during sintering and then migrated into the PbZrO₃ packing powder, leading to a pyrochlore–free phase at 1250°C. The dielectric constant of the latter ceramics was explained by the series mixing rule for the dielectric constant of a diphasic solid.     

Mechanical Activation-Assisted Synthesis of Pb(Fe2/3W1/3)O3

Perovskite Pb(Fe_2/3W_1/3)O₃ (PFW) was prepared via a mechanical activation-assisted synthesis route from mixed oxides of PbO, Fe₂O₃, and WO₃. The mechanically activated oxide mixture, which exhibited a specific area of >10 m²/g, underwent phase conversion from nanocrystalline lead tungstate (PbWO₄) and pyrochlore (Pb₂FeWO_6.5) phases on sintering to yield perovskite PFW, although the formation of perovskite phase was not triggered by mechanical activation. When heated to 700°C, >98% perovskite phase was formed in the mechanically activated oxide mixture. The perovskite phase was sintered to a density of ∼99% of theoretical density at 870°C for 2 h. The sintered PFW exhibited a dielectric constant of 9800 at 10 kHz, which was ∼30% higher than that of the PFW derived from the oxide mixture that was not subjected to mechanical activation.     

Effect of Excess PbO on the Sintering Characteristics and Dielectric Properties of Pb(Mg1/3Nb2/3)O3–PbTiO3-Based Ceramics

Additions of excess PbO to the perovskite Pb[(Mg_1/3Nb_2/3)_0.92Ti_0.08]O₃ solid solution enhanced the formation of a liquid phase at 840°C, which served as a densification aid for the ceramics. The liquid phase allowed elimination of pores and promoted grain growth during sintering. With additions of 1 to 2 wt% excess PbO, densities in excess of 97% of theoretical were obtained at a sintering temperature of 950°C. The peak dielectric constants of the resulting ceramics were over 18 000 at 30°C and dissipation factors less than 1%. Additions of PbO in excess of 2 wt% resulted in inferior dielectric properties due mainly to the dilution of the ferroelectric phase.     

Synthesis and Dielectric Properties of Solution Sol-Gel-Derived 0.9Pb(Mg1/3Nb2/3)O3–0.1PbTiO3 Ceramics

A solution sol-gel method has been developed to prepare 0.9Pb(Mg_1/3Nb_2/3)O₃-0.1PbTiO₃ (0.9PMN-0.1PT) ceramics. During the processing the gel first converted to cubic pyrochlore phase at a calcination temperature of 600°C followed by the formation of pure perovskite phase at 775°C. The ceramics sintered at 1250°C for 4 h showed ≈98% of the theoretical density. The room-temperature dielectric constant of the pellets sintered at 1250°C showed a maximum value of 25035 at 1 kHz. Sintering studies at different temperatures revealed that the dielectric constant increased with increasing grain size in these ceramics.     

Synthesis of Pb(Mg1/3Nb2/3)O3 in Excess Lead Oxide by Mechanical Activation

Twenty hours of mechanical activation of mixed oxides at room temperature led to the formation of Pb(Mg_1/3Nb_2/3)O₃ (PMN) in excess PbO. The crystallinity of the activation-derived perovskite PMN phase was further established when the activated PMN–PbO phase mixture was subjected to calcination at 800°C. Pyrochlores, such as Pb₃Nb₄O₁₃ and Pb₂Nb₂O₇, were not observed as transitional phases on mechanical activation and subsequent calcination, although 50% excess PbO was deliberately added. The perovskite PMN phase was recovered by washing off excess PbO using acetic acid solution at room temperature. It was sintered to a relative density of 98.9% of theoretical at 1200°C for 1 h and the sintered PMN exhibited a dielectric constant of ∼14 000 at 100 Hz and a Curie temperature of −11°C.     

Single-Calcination Synthesis of Pyrochlore-Free 0.9Pb(Mg1/3Nb2/3)O3–0.1PbTiO3 and Pb(Mg1/3Nb2/3)O3 Ceramics Using a Coating Method

A coating approach for synthesizing 0.9Pb(Mg_1/3Nb_2/3)O₃–0.1PbTiO₃ (0.9PMN–0.1PT) and PMN using a single calcination step was demonstrated. The pyrochlore phase was prevented by coating Mg(OH)₂ on Nb₂O₅ particles. Coating of Mg(OH)₂ on Nb₂O₅ was done by precipitating Mg(OH)₂ in an aqueous Nb₂O₅ suspension at pH 10. The coating was confirmed using optical micrographs and zeta-potential measurements. A single calcination treatment of the Mg(OH)₂-coated Nb₂O₅ particles mixed with appropriate amounts of PbO and PbTiO₃ powders at 900°C for 2 h produced pyrochlore-free perovskite 0.9PMN–0.1PT and PMN powders. The elimination of the pyrochlore phase was attributed to the separation of PbO and Nb₂O₅ by the Mg(OH)₂ coating. The Mg(OH)₂ coating on the Nb₂O₅ improved the mixing of Mg(OH)₂ and Nb₂O₅ and decreased the temperature for complete columbite conversion to ∼850°C. The pyrochlore-free perovskite 0.9PMN–0.1PT powders were sintered to 97% density at 1150°C. The sintered 0.9PMN–0.1PT ceramics exhibited a dielectric constant maximum of ∼24 660 at 45°C at a frequency of 1 kHz.     

Microwave Dielectric Properties of CaTiO3-CaAl1/2Nb1/2O3 Ceramics Doped with Li3NbO4

The microwave dielectric properties of CaTi_{1− x} (Al_1/2Nb_1/2) _x O₃ solid solutions (0.3 ≤ x ≤ 0.7) have been investigated. The sintered samples had perovskite structures similar to CaTiO₃. The substitution of Ti⁴⁺ by Al³⁺/Nb⁵⁺ improved the quality factor Q of the sintered specimens. A small addition of Li₃NbO₄ (about 1 wt%) was found to be very effective for lowering sintering temperature of ceramics from 1450–1500° to 1300°C. The composition with x = 0.5 sintered at 1300°C for 5 h revealed excellent dielectric properties, namely, a dielectric constant (ɛ_r) of 48, a Q × f value of 32 100 GHz, and a temperature coefficient of the resonant frequency (τ_f) of −2 ppm/K. Li₃NbO₄ as a sintering additive had no harmful influence on τ_f of ceramics.     

Mechanochemical Synthesis of 0.9[0.6Pb(Zn1/3Nb2/3)O3·0.4Pb(Mg1/3Nb2/3)O3]·0.1PbTiO3

Lead zinc niobate–lead magnesium niobate–lead titanate (PZN–PMN–PT) ceramic powders of perovskite structure have been prepared via a mechanochemical processing route. A single-phase perovskite powder of ultrafine particles in the nanometer range was successfully synthesized when a MZN powder (columbite precursor) was mechanically activated for 10 h together with mixed lead and titanium oxides. The following steps are involved when the ternary oxide mixture is subjected to an increasing degree of mechanical activation. First, the starting materials are significantly refined in particle size as a result of the continuous deformation, fragmentation and then partially amorphized at the initial stage of mechanical activation. This is followed by the formation of perovskite nuclei and subsequent growth of these nuclei in the activated oxide matrix with increasing activation time. When calcined at various temperatures in the range of 500–800°C, pyrochlore phase was not detected by XRD phase analysis in the mechanochemically synthesized powder. Only a minor amount (∼2%) of pyrochlore phase was observed when the calcination temperature was raised to 850°C. The PZN–PMN–PT derived from the mechanochemically synthesized powder can be sintered to ∼98% relative density at a sintering temperature of 950°C. The PZN–PMN–PT sintered at 1100°C for 1 h exhibits a dielectric constant of ∼18 600 and a dielectric loss of 0.015 at the Curie temperature of 112°C when measured at a frequency of 0.1 kHz, together with a d ₃₃ value of 323 ×10⁻¹² pC/N.     

Surface Decomposition of Strontium-Doped Soft PbZrO3–PbTiO3

Sintering temperature has a pronounced effect on perovskite phase stability at the surface of Pb_0.88Sr_0.12Zr_0.54Ti_0.44Sb_0.02O₃ (PSZT) soft piezoelectric ceramics ( d ₃₃≈ 600 pC/N). After sintering 4 h at 1070°C, XRD reveals only perovskite PSZT peaks in the bulk and at the surface. As sintering temperature increases, XRD from the ceramic surface reveals a second-phase peak at ∼27° (2θ), 0.316 nm ( d -spacing). After 4 h at 1280°C, further second-phase peaks are observed, confirming it to be monoclinic ZrO₂, accompanied by a strong increase in the degree of tetragonality of the perovskite phase. These observations are consistent with decomposition of the PSZT to ZrO₂ and tetragonal PZT (PbZrO₃–PbTiO₃) associated with PbO loss. SEM and cross-sectional TEM indicated that surface decomposition had progressed ∼0.5 mm into the sample after 4 h at 1280°C.     

Pb(Zn1/3Ta2/3)O3–PbTiO3 Derived from Mechanical Activation

Nanocrystalline Pb(Zn_1/3Ta_2/3)O₃ (PZTa) of perovskite structure, which cannot be synthesized by either the conventional solid-state reaction of mixed oxides or wet chemistry routes, has been successfully synthesized via a mechanical activation route. The effects of PbTiO₃ (PT) doping in PZTa on the phase formation, thermal stability of the nanocrystalline perovskite phase, and dielectric properties of the resulting PZTa–PT are studied. PZTa doped with a low PT content exhibited a diffuse phase transition, while those with high PT contents demonstrated an expected sharp phase transition at the Curie temperature.     

Mechanosynthesis and Thermal Stability of Piezoelectric Perovskite 0.92Pb(Zn1/3Nb2/3)O3–0.08PbTiO3 Powders

The mechanosynthesis of piezoelectric perovskite 0.92Pb(Zn_1/3Nb_2/3)O₃–0.08PbTiO₃ (PZN–PT) by direct mechanochemical activation of the constituent oxides has been studied by X-ray diffraction (XRD) and transmission electron microscopy (TEM). This and the PbO flux method are the only two procedures that have succeeded in synthesizing this phase, which has recently been shown to present very high electromechanical response. The thermal stability of the single perovskite phase powders has been studied by differential thermal analysis/thermogravimetry and by high-temperature XRD as a function of mechanical activation time and pressure. The phase was found to transform into a pyrochlore type structure at temperatures above 400°C. The transformation presented a significant time dependence, and it was slowed down by increasing mechanical activation time and by the application of pressures by hot pressing. Sintering experiments were accomplished and 85% density, 77% perovskite-phase ceramics were obtained after heating at 1000°C for 1 h. Hot pressing at this temperature failed to increase the percentage of perovskite phase. Results are discussed, and procedures for obtaining dense single-phase PZN–PT-based ceramics with ultrahigh piezoelectricity are proposed.     

High-Temperature Dielectrics in the BiScO3–BaTiO3–(K1/2Bi1/2)TiO3 Ternary System

Perovskite solid solution in the (1− x )[0.4BiScO₃–0.6BaTiO₃]+ x (K_1/2Bi_1/2)TiO₃ [BSBT–KBT x ] system was synthesized using conventional sintering and hot-isostatic pressing. Dielectric properties of BSBT ceramics with different dopant levels of KBT were characterized as a function of temperature and frequency for potential use of high-temperature capacitors. The BSBT ceramics with KBT exhibited high dielectric permittivities (ɛ_r) (>1700 at RT) and low dielectric loss over the temperature range from 100° to 300°C, with flat temperature coefficients of permittivity (TCɛs). In addition, BSBT ceramics with increasing KBT were observed to possess dielectric relaxation characteristics at temperatures (>RT) as observed in lead-based relaxors. Furthermore, high energy densities, being on the order of 4.0 J/cm³ at 220 kV/cm was observed for the BSBT–KBT20 ceramics from the electric-field polarization behavior.     

Sequential Combination of Constituent Oxides in the Synthesis of Pb(Fe1/2Nb1/2)O3by Mechanical Activation

Pb(Fe_1/2Nb_1/2)O₃(PFN) has been successfully synthesized via a novel mechanical activation of mixed oxides and columbite precursor consisting of lead oxide and FeNbO₄. A nanocrystalline perovskite phase 5–15 nm in crystallite size was formed after 30 h of mechanical activation at room temperature for both types of starting materials. However, the nanocrystalline PFN phase derived from the mixed oxides of PbO, Fe₂O₃, and Nb₂O₅is unstable, and develops pyrochlore phases when calcined at 500°–900°C, while no pyrochlore phase is observed for the material derived from the columbite precursor consisting of PbO and FeNbO₅. Different sintering behavior and dielectric properties were also observed between the two types of PFN. These differences are accounted for by the compositional inhomogeneity in the material derived from the mixed oxides, as was revealed by Raman spectroscopic studies. This suggests that mechanical activation is analogous to thermal activation, where the phase development is strongly dependent on the sequence of combining the constituent oxides.     

Perovskite Phase Formation in the Relaxor System [Pb(Fe1/2Nb1/2)O3]1-x–[Pb(Zn1/3Nb2/3)O3]x

Phase formation and dielectric properties of the compositions in the system [Pb(Fe_1/2Nb_1/2)O₃]₁_ _x –[Pb(Zn_1/3Nb_2/3)O₃] _x were investigated as possible materials for multilayer ceramic capacitors. The formation of the phase with perovskite structure and dielectric properties of ceramics at room temperature in the entire composition range are presented. The undesirable pyrochlore phase can be suppressed up to x = 0.6 by adopting calcination of B-site oxides, followed by reaction with PbO. Compositions in the single-phase range can be sintered at less than 1000°C.     

A Polyethylene Glycol-Modified Solid-State Reaction Route to Synthesize Relaxor Ferroelectric Pb(Mg1/3Nb2/3)O3–PbTiO3 (PMN–PT)

By introducing polyethylene glycol (PEG) to the conventional simultaneously mixed oxide reaction route, the 0.65Pb(Mg_1/3Nb_2/3)–0.35PbTiO₃ (0.65PMN–0.35PT) powders and ceramics with pure perovskite phase have been successfully synthesized. It is found that PEG interacts with PbO oxide in a way favoring the formation of the desired perovskite phase. As a result, pyrochlore-free 0.65PMN–0.35PT powders are synthesized at a low temperature of 850°C. The ceramics sintered at 1000°C show uniform grains with the size ranging from 1 to 3 μm. The room temperature dielectric constant is 3440. The maximum dielectric constant is 16 220 at 1 kHz. This method can be applied to the synthesis of other Pb-containing and Bi-containing ferroelectric materials, especially the relaxor-type ferroelectrics in which the pyrochlore phase is difficult to eliminate.