RESEARCH ON THE RHEOLOGY OF MAGNESIUM OXYCHLORIDE CEMENT Ⅰ—RHEOLOGICAL BEHAVIOR

１．ＩｎｔｒｏｄｕｃｔｉｏｎＴｈｅＭＯＣａｒｅａｎｉｍｐｏｒｔａｎｔｃｌａｓｓｏｆｃｅｍｅｎｔｉｔｏｕｓｍａｔｅｒｉａｌｓ．Ｔｈｅｒｈｅｏｌｏｇｉｃａｌｂｅｈａｖｉｏｒｏｆｆｒｅｓｈｐａｓｔｅｉｓｏｂｖｉｏｕｓｌｙｉｍｐｏｒｔａｎｔｄｕｒｉｎｇｔｈｅｍｉｘｉｎｇ,ｔｒａｎｓｐｏｒｔｉｎｇ,ｐｌａｃｉｎｇ,ｃｏｎｓｏｌｉｄａｔｉｎｇａｎｄｆｉｎｉｓｈｉｎｇｏｐｅｒａｔｉｏｎｓ,ｂｕｔａｌｓｏｃｏｎｔｒｏｌｓｉｎｐａｒｔｔｈｅｐｒｏｐｅｒｔｉｅｓｏｆｈａｒｄｅｎｅｄｃｏｎｃｒｅｔｅ．Ｌｉｋｅｐｏｒｔ…     

RESEARCH ON THE RHEOLOGY OF MAGNESIUM OXYCHLORIDE CEMENT Ⅱ—STUDY OF INFLUENTI AL FACTORS ON RHEOLOGICAL PROPERTIES

１．ＩｎｔｒｏｄｕｃｔｉｏｎＴｈｅｒｈｅｏｌｏｇｉｃａｌｂｅｈａｖｉｏｒｓｏｆｔｈｅＭＯＣｗａｓｒｅｐｏｒｔｅｄｂｙｒｅｆｅｒｅｎｃｅ〔１〕．Ｉｎｇｅｎｅｒａｌ,ｄｉｆｆｅｒｅｎｔｉｎｆｌｕｅｎｔｉａｌｆａｃｔｏｒｓｃａｕｓｅｄｉｆｆｅｒｅｎｃｅｒｈｅｏｌｏｇｉｃａｌｂｅｈａｖｉｏｒｓｏｆｐｏｒｔｌａｎｄｃｅｍｅｎｔ〔３,４〕．ＴｈｅｉｎｆｌｕｅｎｃｅｓｏｆｆｉｎｅｎｅｓｓｏｆｔｈｅｍａｇｎｅｓｉａａｎｄｔｅｍｐｅｒａｔｕｒｅｏｆｔｈｅＭｇＣｌ２ｓｏｌｕｔｉｏｎｓｏｎｔｈｅｒｈｅｏｌｏｇｉｃａ…     

微弧氧化对AZ91D镁合金力学性能的影响

利用扫描电镜观察AZ91D镁合金微弧氧化膜形貌,通过静拉伸试验和疲劳试验研究微弧氧化后AZ91D镁合金试件的抗拉强度和疲劳性能,借助体视显微镜和扫描电镜观察疲劳断口形貌。结果表明,微弧氧化陶瓷膜内层致密,具有良好的韧性,并且与基体结合强度高,微弧氧化处理对 AZ91D镁合金的抗拉强度没有影响。微弧氧化处理后,在均值S_m=4.72 kN、幅值S_a=3.15 kN、应力比R=0.2、载荷为等幅谱及频率为10 Hz疲劳试验条件下,AZ91D 镁合金的平均疲劳寿命为54148次循环,与化学氧化处理相当。     

AZ31镁合金薄板的CO2激光焊接接头性能

采用CO2激光焊接试验系统对AZ31镁合金薄板进行了焊接,研究了不同工艺条件下焊缝熔宽的变化,并对焊接接头的微观组织和接头性能进行了研究.试验结果表明,激光功率和焊接速度对焊缝熔宽有较大的影响.显微硬度测试和接头拉伸试验结果表明:焊接接头区域的显微硬度和抗拉强度都高于母材,焊接接头具有良好的力学性能.接头区域的晶粒细化和新的合金相的形成是接头性能改善的主要原因.     

熔剂中添加LaCl3对Mg合金显微组织与性能的影响

测试分析了含有不同量LaCl3的熔剂对Mg合金的力学性能、组织、断口形貌以及腐蚀行为的影响．结果表明，LaCl3以熔剂形式加入Mg合金中，合金内会形成粒状细小的Al10La2Mn7稀土相，该稀土相起到γ相形核核心的作用，使γ相得到细化．LaCl3可以提高合金的抗拉强度σb和延伸率δ当熔剂中含有5％的LaCl3时，σb和δ分别从161MPa和2．1％上升到最大值203MPa和4．2％．分别提高了26％和100％．之后，随着LaCl3加入量的进一步提高，在精炼过程中会造成熔剂结团，并增加Mg熔体内的夹杂，合金的力学性能反而下降．LaCl3不改变Mg合金的断裂机理，断口形貌仍为准解理断裂．研究还表明，含5％LaCl3的熔剂能明显改善Mg合金的耐蚀性，在5％Nacl溶液中腐蚀速率从1.10mg／(cm^2-d)下降到0．17mg／(cm^3-d)，降低了84％．     

合金化元素Zn对GW系镁合金组织和力学性能的影响

通过OM、XRD、SEM等分析方法及托伸实验研究了合金化元素Zn对GW系镁合金铸造组织和力学性能的影响.研究结果表明:加入合金化元素Zn后,合金组织发生较大变化,形成雪花状的δ-Mg枝晶,第二相由骨骼状变为相互连结的网状;而且在固溶处理以及时效处理过程中,二者形貌没有变化.实验合金GWZ721热处理后室温的抗拉强度达到250 MPa,屈服强度达到235 MPa,延伸率达到6.2%,显著优于实验合金GW72.热处理后的高温瞬时抗拉强度和屈服强度随着温度的升高均略有下降,延伸率有所上升.在200,250和300 ℃时,实验合金的抗拉强度仍分别保持为225,220和205 MPa.     

STUDY OF PREPARATION PROCESS OF TUNGSTEN POWDER BY SHS WITH A MAGNESIUM THERMIT STAGE

Tungsten powder was fabricated from the system CaWOrMg by self-propagating high-temperature synthesis (SHS) with a magnesium thermit stage. The physic-chemical change during heating and the effects of pressure of sample and diluents (W powder) on product have been studied. The experimental results show that the porosity of combustion product and the particle size of final tungsten powder decrease with increasing pressure of sample. Addition of diluents could increase the particle size of final tungsten powder. The purity of tungsten is improved by leaching in NaOH solution. The results of spectral analysis and particle size distribution of final tungsten powder show that the final Tungsten powder has a median diameter of 0.87μm, specific surface area of 1.09m^2/g and purity of above 99.0%.     

咪唑啉自组装单分子膜在镁合金AZ91D表面的防腐蚀研究

用咪唑啉水溶液在镁合金(AZ91D)电极表面制备了自组装单分子膜，研究了该组装膜在0.2 mol/L NaCl中对AZ91D的缓蚀作用.通过接触角、FT-IR、EIS和线性极化等方法对自组装膜的形成过程和保护效率进行了研究，得出最佳的咪唑啉组装液浓度为5×10-4mol/L和最佳组装时间为72 h下的缓蚀效率.     

聚苯胺/环氧涂层对AZ91D镁合金耐蚀性能的影响

通过化学氧化法合成本征态及氢氟酸掺杂态聚苯胺(PANI),用红外光谱对其结构进行表征。以环氧树脂为成膜物质,在AZ91D镁合金基体上制备了本征态及氢氟酸掺杂的 PANI/环氧涂层,用EIS方法研究涂层在3.5%NaCl溶液中的耐蚀性,并用SEM对浸泡后基体表面形貌进行观察。实验结果表明,与环氧清漆相比,本征态PANI的加入明显改善了环氧涂层的耐蚀性,而氢氟酸掺杂后进一步提高了PANI/环氧涂层的性能。用XPS对基体表面分析,发现添加聚苯胺的涂层在镁合金表面形成了具有保护作用的产物膜。     

Ca加入量对Mg-5Al-0.4Zn基铸造合金组织与力学性能的影响

用砂型铸造了不同Ca含量的Mg-5Al-0.4Zn-0.2Mn-Sr-Ti-xCa合金.当x为0.37,0.70,0.93,1.69时,合金相组成为α-Mg,（α＋Al2Ca）共晶和Mg17Al12.当x=2.93时,相组成为α-Mg和（α＋（Mg,Al）2Ca）共晶.随着x增加,合金的室温力学性能（σb和δ）呈下降趋势,但合金在200℃下的强度先升高,后又降低.高温延伸率随x增加而下降.合金200℃下的屈服强度σ0.2,200℃随x的增大而稳步增加.组织的热稳定性分析表明,Ca溶入Mg17Al12相使得其自身的耐热性提高.晶界上耐高温相Al2Ca或（Mg,Al）2Ca的形成,在高温下对晶界具有钉扎作用,并降低了晶界处的溶质扩散速度,使晶界强度提高.TEM分析表明,含Ca合金在200℃拉伸时,（1010）棱柱面和（1121）角锥面上的位错参与了滑移.不同滑移系的位错滑移到晶界时,受到晶界上Al2Ca相阻挡而发生位错塞积.     

EFFECT OF Mo AND Mo2C ON THE MICROSTRUCTURE AND PROPERTIES OF THE CERMETS BASED ON Ti（C,N）

Effect of Mo and Mo2 C on the microstructure and properties of Ti（C,N）-based cermets was investigated in this article. The results have indicated that the weight percentage of Mo from 5 to 10 can reduce Ti（C,N） grain diameter and thickness of the rim, and Ti（C,N） grain can be wetted by Ni-Cu-Mo liquid so as to get small contiguity of Ti（C,N） grain. In that way, the transverse rupture strength of Ti（C,N）-based cermets has reached 1800-1900 MPa; the fracture toughness has been due to 16-18 MPa.m1/2. But 15 wt pct Mo was not more effective on Ti（C,N）-based cermets, because the thickness of the rim becomes larger. In the circumstance of Mo2 C, 5 wt pct Mo2 C was good for microstructure and properties of Ti（C,N）-based cermets, but 11 wt pct Mo2C has resulted in larger contiguity of Ti（C,N） grain and big Ti（C,N） grain diameter so as to reduce transverse rupture strength and fracture toughness. So that, the effect of Mo on Ti（C,N）-based cermets is better than Mo2C.     

镁熔体在空气/HFC-134a气氛中的高温氧化特性及机理分析

用热重法测定了镁熔体在1,1,1,2-四氟乙烷(HFC-134a)与空气混合气体保护下的氧化动力学曲线,用X射线衍射仪和能谱仪分析了氧化膜中氧化产物组成和元素成分,讨论了氧化机理并提出了一个氧化模型.结果表明:镁熔体的高温氧化行为与HFC-134a的浓度有关.HFC-134a浓度较低时,氧化膜主要由MgO组成,氧化过程表现出线性动力学的特征.HFC-134a浓度较高时,氧化膜主要由MgF2组成,氧化过程遵循抛物线规律.随着混合气体中HFC-134a浓度的增加,镁熔体的氧化速率减小.熔体温度对氧化行为也有一定的影响.     

EFFECT OF PREDEFORMATION MANNER ON SEMI-SOLID STRUCTURE OF AZ61 MAGNESIUM ALLOY IN SIMA PROCESS

The effect of predeformation manner, predeformation ratio and isothermal heat-treat parameter on the non-dendrite structure of AZ61 magnesium alloy in SIMA process was studied. Under coequal heat-treat condition, the impact of the hot upsetting pre- deformation on semi-solid microstructure in SIMA process was compared with that of the cold compressive predeformation. The results indicate that non-dendrite microstructure in AZ61 magnesium alloy billets can be obtained by hot or cold upsetting predeformation in SIMA process, although their mechanisms of evolution are different. Increasing hot or cold upsetting predeformation ratio can enhance the effect and quality of the non-dendrite microstructure formed before storage energy up to saturation, but the proper isothermal temperature and holding time should be selected.     

YNi_5相及其对Ni_3Al合金性能的影响SCIEI

本文研究了Ni_3Al合金中的 YNi_5相及该相对合金组织与性能的影响.结果表明:Ni_3Al合金中加入Y以后,可产生 YNi_5相,并且随Y含量的增加YNi_5相的数量不断增加,在Y含量≤0.1wt-％时,Y主要以固溶形式存在,而在Y含量≥0.3wt-％时主要以YNi_5相的形式存在.YNi_5相的出现可明显细化合金晶粒,使平直晶界变成弯曲状.少量的Y(≤0.1wt-％)对合金的高温压缩性能和抗氧化性能有好处,而当Y含量较高≥0.3wt-％时,由于有大量的条状,无规则状YNi_5相在晶内和晶界析出,对Ni_3Al基合金的高温强度、塑性及抗氧化性产生有害的影响。     

激光毛面钢板的使用性能

介绍了激光毛面钢板的表面形貌特征及其对钢板使用性能的影响。激光毛面钢板有较小的摩擦系数和较高的抗擦伤能力，有很好的冲压流动性和塑性变形能力以及表面光亮度。     

镁合金微弧氧化深色陶瓷膜制备及耐蚀性研究

通过正交实验在AZ91镁合金表面制备出了深色陶瓷膜,并进一步研究了陶瓷膜的耐蚀性.利用XES对陶瓷膜成分进行分析,探讨陶瓷膜层显色的原因.结果表明,浓度比为55∶30∶4∶20的N1-N2-C-N3溶液中,采用恒压方式电压在350 V～450 V或恒流方式电流密度在1.2 A/dm2～2.4 A/dm2时,可制备出获理想的棕黄色、棕色、棕黑色陶瓷膜;棕色（400 V）和棕黄色（0.8 A/dm2）陶瓷膜腐蚀曲线相对较为平缓,耐蚀性最佳.     

累积叠轧焊AZ31镁合金微观组织和织构演变的EBSD研究

对AZ31镁合金热轧板在350℃进行了累积叠轧焊(ARB)变形,采用EBSD技术研究了AZ31镁合金的微观组织和织构演变.结果表明,ARB可以显著细化AZ31镁合金的晶粒组织,经过3道次变形后平均晶粒尺寸为2.18μm,后续的ARB变形使AZ31镁合金的微观组织更均匀,但晶粒不会再显著细化,说明存在临界ARB变形道次,使晶粒细化和晶粒长大之间达到动态平衡.AZ31镁合金在ARB变形过程中的晶粒细化机制为连续动态再结晶,尤其还观察到了旋转动态再结晶.动态再结晶的形变储存能来源于多道次累积的剧烈应变和沿厚度方向分布复杂的剪切变形.ARB变形过程中旋转动态再结晶和剪切变形使新晶粒c轴发生旋转,导致基面织构弱化.     

纯银自然时效的软化特性

研究了纯度为99.99％(A_1)和99.9％(A_2)银材的时效软化行为,讨论影响银材时效软化速率的诸多因素。实验指出在90天的时效周期内,只有当ε=0～99％在0℃或者当ε≤40％在20～50℃条件下A_1和A_2的机械性能相对稳定。银材的时效软化是由于其内部结构产生再结晶组织所致。     

温度对N80碳钢CO_2腐蚀产物膜性能的影响

用电化学阻抗谱技术研究了不同温度下N80油套管钢在饱和CO2模拟地层水中的腐蚀电化学性能,并观察了腐蚀产物膜的形貌.结果表明,中、低温条件下,温度升高,膜的致密性增加,离子在膜内的扩散过程减弱;当温度达到200℃时,扩散阻抗下降,扩散过程变得相对容易.腐蚀产物膜呈双层结构,其厚度随温度的升高而逐渐减小.去除腐蚀产物膜后的试样表面形貌显示,随着温度的升高,腐蚀坑逐渐变小,直至最后转变为均匀腐蚀;当温度达到200℃时,点蚀坑又变大,表明腐蚀有进一步加剧的迹象.     

(Al_2O_3-SiO_2)_(sf)／AZ91D镁基复合材料微弧氧化膜的制备及电化学阻抗谱分析

在硅酸盐电解液体系中,采用交流微弧氧化方法在增强体体积分数为33%的(Al_2O_3-SiO_2)_(sf)/AZ91D镁基复合材料表面制备出完整的保护性氧化膜.利用SEM,EDS和XRD分析了氧化膜的形貌、成分和相组成,测量了膜层的显微硬度分布.采用电化学阻抗谱(EIS)评价了微弧氧化表面处理前后复合材料的电化学腐蚀性能,确立了不同浸泡时间对应的等效电路.结果表明,微弧氧化膜主要由MgO和Mg_2SiO_4相组成,最大硬度达到1017 HV.氧化膜电化学阻抗模值|Z|与镁合金基体相比大幅度提高,耐腐蚀性能明显高于基体.在3.5%NaCl溶液里浸泡96 h后,EIS出现感抗弧,显示膜内部开始出现点蚀破坏.氧化膜耐蚀性由膜内致密层特性所决定.