低毒单体DMAA用于ZrO2/Al2O3坯体注凝成型

采用低毒的单体N, N-二甲基丙烯酰胺(DMAA)制备了氧化锆增韧氧化铝(ZrO₂/Al₂O₃)坯体。讨论了分散剂的用量、 ZrO₂/Al₂O₃浆料的pH值、 粉体中ZrO₂含量、 粉体所占浆料的固相体积分数、 球磨时间、 预混液中DMAA的浓度(质量分数)对ZrO₂/Al₂O₃浆料黏度的影响。并研究了注凝成型ZrO₂/Al₂O₃坯体的性能和显微结构。结果表明, 当浆料pH值为9, 分散剂的添加量为ZrO₂/Al₂O₃粉体质量的0.6%, 球磨时间为6 h, ZrO₂/Al₂O₃浆料具有最小的黏度。固相体积分数的提高和DMAA加入量的增大都会提高ZrO₂/Al₂O₃浆料的黏度, ZrO₂的加入会降低浆料的黏度。用DMAA制备得到的ZrO₂/Al₂O₃坯体结构均匀, 抗弯强度达到25 MPa。      

Al2O3纤维对SiO2基陶瓷型芯的烧缩阻滞

向SiO₂基体粉料中添加Al₂O₃纤维,采用热压注法制备Al₂O₃/SiO₂陶瓷型芯。分析Al₂O₃纤维含量对陶瓷型芯性能的影响。研究结果表明：Al₂O₃纤维含量对Al₂O₃/SiO₂陶瓷型芯的线收缩率、体积密度和抗弯强度均有较大的影响。当Al₂O₃纤维含量大于1wt%时,Al₂O₃/SiO₂陶瓷型芯的线收缩率大幅度降低,稳定在0.335%左右,体积密度随之降低,稳定在1.790 g · cm^-3左右;当Al₂O₃纤维含量为1wt%时,陶瓷型芯抗弯强度达最大值20.48 MPa。分析了Al₂O₃纤维对Al₂O₃/SiO₂陶瓷型芯烧结收缩的阻滞作用机制。     

Bi2O3助熔剂对CaO-B2O3-SiO2/Al2O3玻璃陶瓷复合材料性能的影响

以CaO-B₂O₃-SiO₂(CBS)玻璃粉体和Al₂O₃陶瓷粉体为原料,通过在CBS与Al₂O₃的质量比固定为50:50的玻璃-陶瓷复合材料中添加适量的Bi₂O₃作为烧结助熔剂,探讨了Bi₂O₃助熔剂对CBS/Al₂O₃复合材料的烧结性能、介电性能、抗弯强度和热膨胀系数的影响规律.研究表明:Bi₂O₃助熔剂能通过降低CBS玻璃的转变温度和黏度促进CBS/Al₂O₃复合材料的致密化进程,于880 ℃下烧结即能获得结构较致密、气孔较少的CBS/Al₂O₃复合材料.然而,过量添加Bi₂O₃将使玻璃的黏度过低,从而恶化CBS/Al₂O₃复合材料的烧结性能、介电性能及抗弯强度.当Bi₂O₃的添加量为CBS/Al₂O₃复合材料的1.5wt%时,于880 ℃下烧结即能获得最为致密的CBS/Al₂O₃复合材料,密度为2.82 g·cm^-3,这一材料具有良好的介电性能(介电常数为7.21,介电损耗为1.06×10^-3),抗弯强度为190.34 MPa,0~300 ℃的热膨胀系数为3.52×10^-6 K^-1.     

多层陶瓷结构Al2O3-Fe2O3/3Y-TZP梯度复合陶瓷的制备及性能

为更好地实现口腔修复体的美学修复效果,采用掺杂不同含量Fe₂O₃（0.01wt%~0.09wt%）和Al₂O₃（0.1wt%）的3 mol% Y₂O₃稳定的ZrO₂（3Y-TZP）粉体为原料,经过铺粉、压制、烧结等工艺制得色度渐变的多层陶瓷结构Al₂O₃-Fe₂O₃/3Y-TZP梯度复合陶瓷。对该梯度复合陶瓷的色度分布、烧结性能和力学性能进行检测,同时研究了Fe₂O₃和Al₂O₃的掺杂对3Y-TZP陶瓷组织和性能的影响。结果表明,制得的Al₂O₃-Fe₂O₃/3Y-TZP梯度复合陶瓷色度由红黄向白色沿成分变化方向呈梯度变化,与天然牙齿色度分布规律一致;力学性能呈梯度变化并从无色端到有色端逐渐降低,但仍满足牙科使用需求（≥ 800 MPa）;在无色瓷层中掺杂微量Al₂O₃（0.1wt%）可以改善Al₂O₃-Fe₂O₃/3Y-TZP梯度复合陶瓷的烧结性能,避免在预烧结过程中发生开裂。微量Fe₂O₃和Al₂O₃的掺杂会促进其在烧结过程中的致密化及晶粒长大;微量Fe₂O₃（0.01wt%）和Al₂O₃（0.1wt%）的掺杂有助于提高3Y-TZP陶瓷的挠曲强度,然而随着Fe₂O₃掺杂量的继续增多（≤ 0.09wt%）挠曲强度降低。      

多孔Al2O3f/Al2O3复合材料研究进展

作为20世纪90年代兴起的一类连续陶瓷纤维增强陶瓷基复合材料,连续氧化铝纤维增韧氧化铝(Al₂O_3f/Al₂O₃)复合材料已经发展为与C_f/SiC、SiC_f/SiC等非氧化物复合材料并列的陶瓷基复合材料。以多孔基体实现基体裂纹偏转成为Al₂O_3f/Al₂O₃复合材料主要的增韧设计方法,形成的多孔Al₂O_3f/Al₂O₃复合材料具有优异的抗氧化性能和高温力学性能,可在高温富氧、富含水汽的中等载荷工况中长时服役,是未来重要的热结构材料。经过近30年的发展,多孔Al₂O_3f/Al₂O₃复合材料已被应用于航空发动机、燃气轮机等热端部件。本文综述了多孔Al₂O_3f...     

Fe/Al2O3复合材料的制备和性能

用石墨埋烧方法制备Fe/Al₂O₃复合材料,对其力学性能和微观结构进行了分析。结果表明:Fe/Al₂O₃复合材料的弯曲强度与断裂韧性均随Al₂O₃含量的升高先升高后降低,当Al₂O₃含量（质量分数）为70%时,其弯曲强度与断裂韧性分别达到602.49 MPa和9.33 MPa·m¹/2,其硬度随Al₂O₃含量先降低后升高。在烧结过程中在Fe颗粒周围形成一种成分为FeO与FeAl₂O₄的壳体,在壳体与Fe颗粒之间存在微裂纹缺陷。壳体的形成和壳体与金属颗粒间的微裂纹钝化了外部应力,从而提高了复合材料的韧性。     

原位气相生长法制备碳纳米管/Al2O3陶瓷复合材料

以Al₂O₃陶瓷成型体为基体,通过化学气相反应在陶瓷体内原位生长碳纳米管（CNTs）,制备出CNTs/Al₂O₃陶瓷复合材料。结果表明,Al₂O₃陶瓷体中均匀分布有可观量的多壁CNTs,碳管根部嵌于Al₂O₃晶粒间并从晶粒表面生长出。在Al₂O₃陶瓷成型体中原位生长CNTs需严格控制生长条件,尤其是生长温度（850℃）,温度过高和过低都难以长出CNTs,此外造孔剂、碳源和催化剂也影响CNTs的原位生长。对原位生长的CNTs/Al₂O₃复合体进一步高温烧结获得致密化的复合材料,其导电率达3.7 S/m,较纯Al₂O₃提高13个数量级。在陶瓷成型体中原位生长CNTs是一步法制备CNTs/陶瓷复合材料的新方法,可用于发展高性能的结构陶瓷和具有导电导热等多功能特性的新型陶瓷复合材料。     

燃烧合成ZrB2 / Al2O3 复合粉体及其界面分析

采用燃烧还原合成技术, 以还原体系(B₂O₃ + ZrO2 + Al) 为反应体系制备了ZrB₂ / Al₂O₃ 复合粉体。利用X射线衍射(XRD) 、X 射线光电子能谱(XPS) 和透射电镜( TEM、HRTEM) 对复合粉体的物相组成、化学组成及界面结构进行了表征分析。结果表明, 复合粉体中存在Zr 、B、Al 和O 元素且它们分别以ZrB₂ 和Al₂O₃ 为主要存在形式, ZrB₂ 和Al₂O₃ 为复合粉体的主晶相。复合粉体中有少量ZrO2 的存在, 分析认为是合成反应过程中未参加反应的ZrO2 。ZrB₂ 和Al₂O₃ 颗粒间形成了结合良好的界面, 这主要与ZrB₂ 的结晶过程有关。      

低温燃烧法制备(W,Mo)C/Al2O3/La2O3复合粉末及性能

为了开发出一种无黏结相硬质合金来减少传统硬质合金中钴元素的应用,采用化学法制备(W,Mo)C/Al₂O₃/La₂O₃。以偏钨酸铵、钼酸铵、硝酸铝、硝酸镧、尿素和葡萄糖为原料,通过低温燃烧法探究硝酸盐和尿素、葡萄糖的不同配比,得出最优配比后还原炭化制备(W,Mo)C/Al₂O₃/La₂O₃粉末。在1500~1800℃经离子烧结制备(W,Mo)C/Al₂O₃/La₂O₃无黏结相材料,研究其力学性能并分析强韧化机制。结果表明:硝酸盐和尿素的最佳摩尔配比为1∶2,硝酸盐和葡萄糖的最佳摩尔配比为1∶0.5,加入葡萄糖后颗粒尺寸减小了0.28μm,比表面积提高了75.64%。致密度、维氏硬度和抗弯强度在1600℃时达到最大值分别为:98.45%,2202HV和1203 MPa,断裂韧度在1500℃时达到最大值为7.52 MPa·m^1/2。由于晶粒的细化及第二相颗粒的增韧的影响,(W,Mo)C/Al₂O₃/La₂O₃在1500~1600℃时以沿晶断裂和穿晶断裂为主;晶粒长大以及孔隙的出现导致(W,Mo)C/Al₂O₃/La₂O₃在1700~1800℃时以沿晶断裂为主。     

热压与放电等离子体烧结两种工艺制备Al2O3/Cu复合材料

由机械合金化法(MA)制得纳米级Al₂O₃颗粒弥散镶嵌于微米级Cu颗粒表面的复合粉末, 利用球形化工艺改善所制得复合粉的形貌及粒度范围, 分别采用热压法(HP)和放电等离子体烧结(SPS)法制备Al₂O₃/Cu复合材料。通过测试密度、 电导率、 抗弯强度及SEM复合粉形貌和烧结体断口分析、 微区成分分析, 对比研究了Al₂O₃质量分数分别为0%、 0.5%、 1.0%、 1.5%时Al₂O₃/Cu复合材料的物理、 力学和电学性能。结果表明: 不同制备工艺下随着Al₂O₃含量增加, 材料的抗弯强度先增后降, 电导率除受杂质影响外, 还受材料缺陷的影响, 故变化规律不明显, 对于Al₂O₃含量相同的Al₂O₃/Cu复合材料, 采用SPS法制备的复合材料的致密度、 抗弯强度及电导率均高于HP法; 在弯曲应力下两种制备方法所得复合材料均发生延性断裂。      

Processing, microstructure and properties of C40 Mo(Si,Al)2/Al2O3 composites

The C40 Mo(Si_0.75Al_0.25)₂/Al₂O₃ composites were prepared by spark plasma sintering (SPS) of mechanically alloyed (MA) powders. The Mo(Si_0.75Al_0.25)₂/0–20 vol.% Al₂O₃ materials, showing micron and submicron composite structure, possess a hardness of 13.9–14.6 GPa but a poor toughness of 1.78–1.80 MPa m^1/2. The addition of 30 vol.% Al₂O₃ leads to the formation of the micron C40 Mo(Si_0.75Al_0.25)₂/Al₂O₃ composite with an intergranular distribution of Al₂O₃, that results in a drop of the hardness to 10.2 GPa and an improvement of the toughness to 3.67 MPa m^1/2. The transition of the cleavage facets to the intergranular fracture with the addition of Al₂O₃ is assumed as the main toughening mechanism.     

Improvements in mechanical properties of TiB2 ceramics tool materials by the dispersion of Al2O3 particles

TiB₂–Al₂O₃ composites with Ni–Mo as sintering aid have been fabricated by a hot-press technique at a lower temperature of 1530 °C for 1 h, and the mechanical properties and microstructure were investigated. The microstructure consists of dispersed Al₂O₃ particles in a fine-grained TiB₂ matrix. The addition of Al₂O₃ increases the fracture toughness up to 6.02 MPa m^1/2 at an amount of 40 vol.% Al₂O₃ and the flexural strength up to 913.86 MPa at an amount of 10 vol.% Al₂O₃. The improved flexural strength of the composites is a result of higher density than that of monolithic TiB₂. The increase of fracture toughness is a result of crack bridging by the metal grains on the boundaries, and crack deflection by weak grain boundaries due to the bad wetting characters between Ni–Mo and Al₂O₃.     

Al2O3掺杂BaTi0.85Sn0.15O3陶瓷的制备及性能表征

通过传统固相二次烧结法来制备x wt% Al₂O₃（x=0、1.0、1.5）/BaTi_0.85Sn_0.15O₃（BTS）陶瓷。研究了掺杂不同含量Al₂O₃对BTS陶瓷的微观结构、介电性能及挠曲电性能的影响。结果表明,掺杂Al₂O₃的BTS陶瓷不改变陶瓷的晶体结构,仍为标准钙钛矿结构晶型;Al₂O₃的掺入能够有效降低晶粒尺寸,具有明显的细晶作用。随着Al₂O₃含量的增大,Al₂O₃/BTS陶瓷的介电常数减小,介电损耗得到明显改善,居里峰逐渐宽化且向温度高的方向偏移。Al₂O₃/BTS陶瓷的挠曲电系数随着Al₂O₃含量的增加和测试环境温度的升高均减小。此外,Al₂O₃/BTS陶瓷的挠曲电系数和介电常数之间存在一种近线性关系,但当温度非常接近于居里温度时,这种线性关系减弱。     

Microstructures, densification and mechanical properties of TiC–Al2O3–Al composite by field-activated combustion synthesis

Dense TiC–Al₂O₃–Al composite was prepared with Al, C and TiO₂ powders by means of electric field-activated combustion synthesis and infiltration of the molten metal (here Al) into the synthesized TiC–Al₂O₃ ceramic. An external electric field can effectively improve the adiabatic combustion temperature of the reactive system and overcome the thermodynamic limitation of reaction with x < 10 mol. Thereby, it can induce a self-sustaining combustion synthesis process. During the formation of Al₂O₃–TiC–Al composite, Al is molten first, and reacted with TiO₂ to form Al₂O₃, followed by the formation of TiC through the reaction between the displaced Ti and C. Highly dense TiC–Al₂O₃–Al with relative density of up to 92.5% was directly fabricated with the application of a 14 mol excess Al content and a 25 V cm⁻¹ field strength, in which TiC and Al₂O₃ particles possess fine-structured sizes of 0.2–1.0 μm, with uniform distribution in metal Al. The hardness, bending strength and fracture toughness of the synthesized TiC–Al₂O₃–Al composite are 56.5 GPa, 531 MPa and 10.96 MPa m^1/2, respectively.     

ZrO_2增韧Al_2O_3陶瓷的力学性能和增韧机制

对通过热压烧结法制备的3种陶瓷99.5vol%Al2O3(AD995)、ZrO2(15vol%)/Al2O3和ZrO2(25vol%)/Al2O3的力学性能和增韧机制进行了实验和理论研究。基于复合材料细观力学理论并考虑ZrO2的相变特性,建立了描述ZrO2/Al2O3陶瓷力学性能的本构模型。结果表明:ZrO2的加入细化了基体Al2O3晶粒,ZrO2/Al2O3陶瓷的致密性得到提高;3种陶瓷试件的破坏呈现小变形到脆性破坏的特点,压缩加载下试件应力-应变曲线近似为线性关系;AD995陶瓷的断裂韧性为5.65 MPa·m1/2,ZrO2(25vol%)/Al2O3陶瓷的断裂韧性为8.42 MPa·m1/2,提高了近50%;随ZrO2增韧相含量的增加,ZrO2/Al2O3陶瓷的弹性模量降低而断裂韧性增加,这一变化趋势与实验结果有良好的一致性。     

片状纳米Al2O3/环氧树脂复合材料的制备及性能

采用水热法制备片状纳米Al₂O₃,经过偶联剂改性后与环氧树脂复合,通过溶液混合法制备了不同填充量的片状纳米Al₂O₃/环氧树脂复合材料,研究了片状纳米Al₂O₃用量对片状纳米Al₂O₃/环氧树脂复合材料介电性能和热性能的影响,利用SEM对复合材料的断口形貌进行了表征。结果表明: 片状纳米Al₂O₃在环氧树脂基体中分散良好;随着片状纳米Al₂O₃填充量的增加,复合材料的起始热分解温度升高、介电强度增大,当片状纳米Al₂O₃的填充量为7wt%时,复合材料的介电强度为 29.58 kV/mm,比纯环氧树脂的介电强度提高了30%;复合材料的介电常数(3.8~4.5)和介电损耗(0.015)比纯环氧树脂稍有增大,但仍维持在较好的介电性能范围内。