C和W对低合金Cr-Mo钢焊缝金属组织和冲击韧性的影响

使用OM、SEM、EPMA、EBSD等手段并进行热膨胀和冲击等实验,研究了C和W元素对第四代钠冷快堆用低合金Cr-Mo钢钨极氩弧焊(TIG)熔敷金属微观组织和冲击韧性的影响.结果 表明:多道次焊接热循环使多层多道焊缝金属的组织分布不均匀,分为表层焊缝组织和中间焊缝组织.表层焊缝组织,可分为熔化区(MZ)、粗晶区(CGH...     

热输入对Inconel 617镍基高温合金激光焊接接头显微组织与力学性能的影响EI北大核心

采用两种热输入不同的焊接工艺参数对3 mm壁厚的Inconel 617镍基高温合金进行激光焊接。通过光学显微镜和扫描电子显微镜对焊接接头显微组织进行观察分析,并测试了焊接接头在室温(25℃)及高温(900℃)下的拉伸性能。结果表明:激光焊接热输入对Inconel 617焊接接头显微组织及力学性能影响明显。在高热输入(200 J/mm)条件下,焊缝正面宽度3.88 mm,熔化区中部晶粒尺寸粗大,取向杂乱,树枝晶二次枝晶间距较大(6.71μm),枝晶间碳化物颗粒尺寸较为粗大,枝晶间Mo,Cr等合金元素的凝固偏析较为严重。焊接接头热影响区宽度约0.29 mm,在晶界和晶内形成了γ+碳化物共晶组织,这是由于焊接升温过程中,热影响区内球状碳化物颗粒与周边奥氏体发生组分液化,并在焊后凝固过程中形成共晶。低热输入(90 J/mm)工艺参数获得的焊缝正面宽度为2.28 mm,焊缝呈沿熔合线母材外延生长并沿热流方向定向凝固形成的柱状晶形态。焊缝中部树枝晶二次枝晶间距较小(2.26μm),枝晶间碳化物颗粒尺寸细小,热影响区宽度约0.15 mm。室温(25℃)拉伸测试表明:高热输入下获得的焊接接头由于焊缝中固溶元素偏析造成的局部组织弱化,从焊缝中部破坏,强度与伸长率有所降低,低热输入条件下获得的焊接接头从母材破坏。而高温实验条件下(900℃),母材晶界发生弱化导致所有试样均从母材破坏。     

石油储罐钢焊接热影响区模拟研究

采用焊接热模拟技术,研究不同焊接热输入条件下焊接热循环对石油储罐钢焊接热影响区粗晶区(CGHAZ)的组织和性能的影响.结果表明:实验钢在80～100kJ/cm的大热输入下,热影响区仍能够保持良好的低温韧性;随着焊接热输入的增加,实验钢CGHAZ组织变粗大,低温冲击功下降;钢中弥散分布着大量细小TiN粒子,在焊接热循环中...     

HAZ microstructure simulation in welding of a ultra fine grain steel

In the present work the evolution of grain structure in the weld HAZ (heat affected zone) under welding thermal cycle was simulated. Especially the grain growth in the HAZ of a SS400 ultra fine grain steel was investigated. An integrated 3-D Monte Carlo (MC) simulation system for grain growth of the weld HAZ was developed based on Microsoft Windows. The results indicate that MC simulation is an effective way to investigate the grain growth in weld HAZ. The method not only simulates the non-isothermal dynamics process of the grain growth in the weld HAZ, but also visualizes the austenite grains realistically. Moreover, the thermal pinning effect can be easily included in the simulation process. The grain sizes of the CGHAZ (coarse grain heat affected zone) obtained from MC simulation are basically in agreement with the experimental measurement of the real welded joints under different heat input. Furthermore, the simulation indicates that the grain growth degree is higher for the SS400 ultra fine grain steel compared to conventional steel. With the increase in the heat input, the grain growth of the CGHAZ rapidly increases. Because the activation energy of the grain growth is lower for the SS400 ultra fine grain steel, austenite grains can grow at a relatively lower temperature, hence the range of the CGHAZ becomes wider.     

核用SA508-4N钢粗晶区再热裂纹敏感性评价

采用等温恒速拉伸方法评价了核用SA508-4N钢焊接粗晶区(CGHAZ)的再热裂纹敏感性。使用激光共聚焦、扫描电镜和透射电镜观测和分析粗晶区和断口处的组织、裂纹以及断口形貌,结果表明：SA508-4N钢的母材为回火马氏体,较高含量的碳和铬影响碳化物的大小和分布状态,粗晶区马氏体的形成不利于抑制再热裂纹的产生。碳化物的析出使晶内和晶界的强度不同,当晶内强度大于晶界强度时形成沿晶脆性断裂;当晶内和晶界强度的差距较小时断裂形式包括穿晶和沿晶断裂。SA508-4N钢粗晶区对再热裂纹不敏感,成分A粗晶区的抗再热裂纹能力比成分B的高。在实际生产中,优选的工艺参数为：成分A、焊接t_8/5为25 s、焊后热处理温度580℃。     

Joint properties of friction stir welded AZ31B– H24 magnesium alloy

Abstract

The weldability of friction stir welded hot rolled AZ31B-H24 magnesium alloy sheet, 4 mm in thickness, was evaluated, varying welding parameters such as tool rotation speed and travel welding speed. Sound welding conditions depended mainly on sufficient heat input during the welding process. Insufficient heat input, which was generated in the case of higher travel speed and lower rotation speed, caused an inner void or lack of bonding in the stir zone. The microstructure of the weld zone was composed of five regions: base metal, heat affected zone, thermomechanically affected zone, stir zone I and stir zone II. Unlike the general feature of friction stir welded aluminium alloys, the grain size of the weld zone was larger than that of the base metal. Stir zones I and II were characterised by partial dynamic recrystallisation and full dynamic recrystallisation, respectively. The hardness of the weld zone was lower than that of the base metal owing to grain growth. A wider range of defect free welding conditions was acquired at higher tool rotation speed and lower welding speed. The maximum tensile strengh was 240 MPa, which was ~85% of the base metal value of 293 MPa. The fracture location was close to the stir zone.     

Influence of peak temperature during in-service welding of API X70 pipeline steels on microstructure and fracture energy of the reheated coarse grain heat-affected zones

In this investigation, thermal simulated specimens were used to investigate the effect of second peak temperature during in-service welding on characteristic fracture energy and microstructure feature of the subcritically (SC), intercritically (IC), supercritically (SCR), and unaltered (UA) reheated coarse grain heat-affected zones (CGHAZs). The API X70 high-strength pipeline micro-alloyed steel was subjected to processing during in-service welding by applying double thermal cycle shielded metal arc welding process with heat input of 9.3 kJ/cm and thermal cycles to simulate microstructure of reheated CGHAZs. This consisted of first thermal cycle with a peak temperature of 1350 °C, then reheating to different second peak temperatures of 600, 800, 1000, and 1200 °C with a constant cooling rate of 60 °C/s. Toughness of the simulated reheated CGHAZs were assessed using Charpy impact testing at −20 °C, and the corresponding fractographs, optical micrographs, and electron micrographs have been examined. It is found that accelerating cooling rate during in-service welding has an improving effect on the microstructure of CGHAZs. Owing to small heat-input and accelerating cooling, the grain size in reheated CGHAZs is relatively small and the brittle microphases are eliminated or minimized. The Charpy impact results show that the CGHAZ fracture energy is improved after the second thermal cycle. The SC CGHAZ showed higher absorbed impact energy and the IR CGHAZ had less absorbed energy, but the phenomenon of embrittlement in IR CGHAZ is not serious. Therefore, it can be concluded that the fracture energy of CGHAZ and IR CGHAZ can be improved by accelerating cooling with appropriate cooling rate.     

析出强化超细晶粒钢焊接热影响区粗晶区的组织和性能

为研究焊接对800 MPa级Ti、Nb复合微合金化析出强化超细晶粒钢组织性能的影响.运用Gleeble3500热模拟试验机,对实验钢进行单道次焊接热循环试验,并研究冷却速度、冷却时间t8/5对焊接热影响区粗晶区(CGHAZ)组织、性能的影响.结果表明:冷却速度5~15℃/s,CGHAZ的组织为贝氏体,冷却速度进一步增大,会出现马氏体.随着冷却时间t8/5的增加,原奥氏体晶粒尺寸逐渐增加,硬度值逐渐降低,冲击韧性先上升后下降.t8/5为20~120 s时,CGHAZ显微硬度(223~250.4 HV)均小于母材的显微硬度(270.6 HV),出现软化现象,t8/5为20 s时,冲击吸收功最高,为18.2 J,但仅有母材的25.3%.经历焊接热循环后,奥氏体晶粒粗化以及CGHAZ出现贝氏体组织是导致脆化的主要原因.     

On the heterogeneous microstructure development in the welded joint of 12MnNiVR pressure vessel steel subjected to high heat input electrogas welding

Microstructure features of 12MnNiVR pressure vessel steel welded joint deposited by the high heat input electrogas welding have been systematically investigated. It is revealed that the welded joint is featured by a heterogeneous juxtaposition. The coarse grained heat-affected zone (CGHAZ) primarily consists of lath bainites and minor granular bainites. The fine grained heat-affected zone (FGHAZ) is dominated by polygonal ferrites, pearlites, and fine cementite particles. Moreover, electron backscatter diffraction results further demonstrate that the CGHAZ is populated by coarse prior austenite grains (PAGs) with high frequency (61.3%) of low angle grain boundaries (LAGBs). On the other hand, the FGHAZ is filled with fine PAGs with a lower frequency (19.6%) of LAGBs. Such microstructural differences may likely contribute to differed mechanical properties for samples tested at designed positions.     

Conventional and in situ tensile test of friction stir welded steel – Optimization of processing parameters

In the present investigation, steel plates were joined at different tool traversing speed by friction stir welding keeping other parameters same. Microstructural characterization was carried out with optical and scanning electron microscopes. At weld nugget pearlite and bainite were present within ferrite matrix. Thermo‐mechanically and heat affected zones microstructure consisted of pearlite and ferrite. Second phase area fraction and matrix grain size at different regions were varied depending on welding parameters. Weld nugget exhibited substantial improvement in microhardness with respect to base metal. In this respect heat affected zone revealed minimum microhardness and was below base metal value. Tensile tests were carried out on standard and miniature specimens in scanning electron microscope. Highest joint efficiency to the tune of ～82 % and ～120 % of that of base metal obtained for standard and miniature specimens, respectively machined from weld fabricated at lowest welding speed. With increment in welding speed assembly strength was reduced for both types of specimens. Standard specimens failed from heat affected zone and miniature specimens failed through centre of weld nugget. Apart from matrix grain size and second phase area fraction, precipitation of microalloyed carbide / carbonitride was responsible for altering the joint strength.     

热输入对E36钢SAW焊缝组织及韧性的影响

为提高建造海洋采油平台的效率、减少生产周期,进而为实际生产提供数据支持,采用3种不同热输入对海洋采油平台用E36钢进行埋弧焊焊接,通过光学显微镜(OM)、透射电镜(TEM)、扫描电镜(SEM)和电子背散射衍射技术(EBSD)对焊缝微观组织及夹杂物形貌进行了观察,研究了不同热输入对焊缝组织及韧性的影响,并分析了不同热输入对焊缝夹杂物尺寸分布和成分的影响.结果表明:热输入为50 k J/cm时,焊缝金属韧性较好;随着焊接热输入的增加,焊缝的冲击韧性降低,但仍能满足性能指标,焊缝金属中夹杂物成分相差较大,有效夹杂物数量减少,焊缝金属中大角度晶界比例减少;对于E36钢,热输入为160 k J/cm时不仅能使韧性符合要求还能提高生产效率.     

热输入对Q1100钢焊接接头低温韧性及耐蚀性能的影响

采用10 kJ/cm和15 kJ/cm两种焊接热输入对Q1100超高强钢进行熔化极气体保护焊,研究焊接接头的组织性能及局部腐蚀行为。结果表明：两种热输入焊接接头的焊缝组织主要为针状铁素体和少量的粒状贝氏体,粗晶区组织均为板条贝氏体,细晶区组织均为板条贝氏体和粒状贝氏体,临界相变区组织为多边形铁素体、马奥岛和碳化物的混合组织。两种热输入焊接接头中电荷转移电阻均为母材>热影响区>焊缝区,母材耐蚀性最好,热影响区次之,焊缝区耐蚀性最差。在腐蚀过程中,焊缝区作为阳极最先被腐蚀,当腐蚀一定时间后,腐蚀位置发生改变,阳极腐蚀区域转移到母材区,而焊缝区作为阴极得到保护。热输入为10 kJ/cm时,焊接接头具有更好的低温韧性和耐蚀性,其焊缝和热影响区-40℃冲击功分别为46.5 J和30.2 J。     

Q960E超高强钢焊接接头组织和性能研究

目的 对Q960E超高强钢的焊接工艺进行研究以获得高强高韧的焊接接头。方法 选择超高强钢Q960E作为母材、FK1000ER120S–G焊丝作为填充材料进行MAG焊,采用改变焊接电流的方式来研究焊接热输入对焊接接头组织和性能的影响。结果 当焊接电流为155～230 A时,均获得了全焊透无明显缺陷的焊缝。随着焊接热输入的增大,焊接接头中各亚区宽度增大,其中焊缝区变化最为显著,在最小热输入条件下焊缝宽度为3.98 mm,在最大热输入条件下焊缝宽度增至5.53 mm。对焊接接头进行组织分析发现,焊缝组织主要为针状铁素体和板条马氏体;完全相变区组织主要为板条马氏体;未完全相变区组织主要为回火马氏体和部分重结晶形成的马氏体。硬度测试表明,在热影响区的回火区发生了软化现象,最低硬度仅为290HV;在完全相变区发生了硬化现象,硬度最大值可达500HV。在不同热输入条件下,焊接接头各亚区硬度变化趋势一致,焊接接头抗拉强度为995～1 076 MPa,拉伸试验均断裂在热影响区,断后伸长率为9.33%～10.21%,断裂时存在颈缩现象,为韧性断裂。随着热输入的增加,粗晶区马氏体板条束宽度增大,未完全相变区...     

热输入对Q890高强钢焊缝组织及性能的影响

针对国内某钢厂最新研制的Q890高强钢,采用三种不同的热输入对其进行气体保护焊接,研究了不同热输入对焊缝金属组织、硬度及冲击韧性的影响.结果表明,3种热输入下,焊缝组织主要以板条贝氏体为主,并含有粒状贝氏体、少量的板条马氏体和残余奥氏体.随着热输入的增大,焊缝组织中贝氏体铁素体板条粗化,板条马氏体逐渐减少,而粒状贝氏体逐渐增多,部分残余奥氏体由薄膜状向块状转变;焊缝金属硬度随着热输入的增大而下降;焊缝金属的冲击韧性亦呈逐渐下降的趋势.     

热输入对10CrNi3MoV钢MAG焊接头组织和性能的影响

为制定合理的焊接工艺,保证焊接质量,设置不同焊接热输入进行了10CrNi3MoV钢MAG焊接。采用微观组织分析、断口观察、力学测试等手段研究了焊接热输入对接头组织及性能的影响。结果表明,热输入较小时（E=11.0 kJ·cm^-1、E=14.4 kJ·cm^-1）,焊缝组织以针状铁素体为主,并含有部分粒状贝氏体、先共析铁素体等;热输入较大时（E=18.1 kJ·cm^-1）,针状铁素体占比降低,粒状贝氏体、先共析铁素体等增多,组织粗化。随热输入的增大,粗晶区晶粒粗化,组织由板条马氏体逐步转变为板条贝氏体,板条界限模糊,并有粒状贝氏体出现;焊缝金属强度降低,冲击韧性先略有升高后显著降低,断裂形式由微孔聚缩型韧断变为准解理/韧性混合断裂。热输入E=14.4 kJ·cm^-1时,焊缝组织以细密的针状铁素体为主,具有最佳强韧性匹配。     

Influence of peak temperature during simulation and real thermal cycles on microstructure and fracture properties of the reheated zones

The objective of this paper is to study the influence of the second peak temperature during real and simulated welding on properties of the subcritically (S), intercritically (IC) and supercritically (SC) reheated coarse grained heat affected (CGHAZ) zones. The X80 high strength pipeline microalloyed steel was subject to processing in a double-pass tandem submerged arc welding process with total heat input of 6.98 kJ/mm and thermal cycles to simulate microstructure of reheated CGHAZ zones. This involved heating to a first peak temperature (T_P1) of 1400 °C, then reheating to different second peak temperatures (T_P2) of 700, 800 and 900 °C with a constant cooling rate of 3.75 °C/s. Toughness of the simulated reheated CGHAZ regions were assessed using Charpy impact testing at 0 °C, −25 °C and −50 °C. The microstructure of the real and simulated reheated CGHAZ regions was investigated using an optical microscope and field emission scanning electron microscope. Morphology of the martensite/austenite (MA) constituent was obtained by the use of a field emission scanning electron microscope. The blocky and connected MA particles, along prior-austenite grain boundaries, act as a brittle phase for the initiation site of the brittle fracture. Charpy impact results indicated that IC CGHAZ had less absorbed energy with higher transition temperature and hardness. The SC CGHAZ region showed higher absorbed impact energy with lower hardness. Design of multipass weld joints with less IC CGHAZ regions can result in a higher toughness property.     

A comparative study of laser-arc double-sided welding and double-sided arc welding of 6 mm 5A06 aluminium alloy

In order to study the interactions between the two heat sources in both laser-arc double-sided welding (LADSW) and double-sided arc welding (DSAW), some welding characteristics including weld configuration, energy efficiency, weld microstructure and mechanical properties of the both processes were contrastively investigated. The results show that the weld cross-section of LADSW within the proper welding parameter takes on the combination of typical weld profiles of gas tungsten arc welding and laser welding, while the DSAW takes on a quasi-symmetrical shape. The energy efficiency of LADSW is higher than DSAW, probably due to the higher heat transfer efficiency in laser welding and stronger effect of laser on the arc. The weld microstructures of the both processes characterized by scanning electron microscope mainly consist of α and β phase, whereas the grain size and second-phase particle size vary a great deal for the different heat input. The tensile strength of LADSW is 91.7% of base metal, compared with that of 82.3% of DSAW, and the elongation is also higher than DSAW. The fracture micromorphology of LADSW indicates a more typical dimple fracture than that of DSAW. It is considered that the better mechanical properties of LADSW are attributed to the finer grain size.     

XRD and TEM analysis of microstructure in the welding zone of 9Cr-1Mo-V-Nb heat-resisting steel

Under the condition of tungsten inert gas shielded welding (TIG) + shielded metal arc welding (SMAW) technology, the microstructure in the welding zone of 9Cr-1Mo-V-Nb (P91) heat-resisting steel is studied by means of X-ray diffractometry (XRD) and transmission electron microscopy (TEM). The test results indicate that when the weld heat input (E) of TIG is 8.5 ∼ 11.7 kJ/cm and the weld heat input of SMAW is 13.3 ∼ 210 kJ/cm, the microstructure in the weld metal is composed of austenite and a little amount of δ ferrite. The substructure of austenite is crypto-crystal martensite, which included angle. There are some spot precipitates in the martensite base. TEM analysis indicates that the fine structure in the heat-affected zone is lath martensite. There are some carbides (lattice constant, 1.064 nm) at the boundary of grain as well as inside the grain, most of which are Cr₂₃C₆ and a little amount of (Fe, Me)₂₃C₆.     

Effect of cathodic potential on stress corrosion cracking behavior of different heat-affected zone microstructures of E690 steel in artificial seawater

In this work,the stress corrosion cracking(SCC)behavior of E690 steel base metal(BM)and different heat-affected zone(HAZ)microstructures,i.e.,coarse grain HAZ(CGHAZ),fine grain HAZ(FGHAZ),and intercritical HAZ(ICHAZ),was investigated at different cathodic potentials in artificial seawater by slow strain rate tensile tests,scanning electron microscopy and electron back-scattered diffraction measurements.The results show that the HAZ microstructures and BM exhibit different SCC susceptibilities:FGHAZ相似文献   

Ti75合金激光焊接接头的组织及力学性能

采用10 kW的连续光纤激光器对3 mm厚的Ti75合金板进行激光焊接,通过调整不同的激光功率来获得全熔透的焊接接头.同时,观察了不同热输入下焊接接头的宏观形貌、微观组织,测试了焊接接头的力学性能和显微硬度,对接头不同部位的组织特征及成形原因进行了分析.结果表明,随着焊接过程中激光功率的增加,焊缝的宽度逐渐变大,在不同...