硼对快凝Ni3Al组织结构及力学性能的影响

本文通过快凝及加硼合金化的方法改善金属间化合物Ni_3Al的韧性。实验表明:加入0.5-1.4at.-％的硼对Ni_3Al的塑性提高最有利。结构分析表明:在含1.37at.-％硼的Ni_3Al中,硼以Ni_(23)B_6弥散相及晶界偏聚方式存在;当硼量增至2.22at.-％时,硼以粗大的Ni_(23)B_6及NiB_(12)相在晶界处析出。无硼的Ni_3Al晶界为大角度晶界;当硼加至1.37at.-％时,Ni_3Al晶界以位错排列成亚晶界,以小角晶界形式存在。     

MICROSTRUCTURE OF RAPIDLY SOLIDIFIED TiAl ALLOY POWDER

The rapidly solidified powder of Ti-34Al-2Mn alloy was obtained by means of ultrasonicgas atomisation (USGA) technique.The tupical size of the powder is 27 μm.X-ray diffractionresults show that the powder consists of major α_2-phase and minor γ-phase.Under opticalmicroscope both equiaxed and dendritical microstructure features were observed on RS pow-der sections.After annealing at 900 ℃/for 2 h in vacuum,most of α_2-phase transforms intoγ-phase,resulting in refinement of structure.     

EFFECT OF POWDER SIZE ON MICROSTRUCTURE AND PROPERTIES OF RAPIDLY SOLIDIFIED Al-Li-Mg-Zr ALLOY

The microstructure and properties of the rapidly solidified Al-Li-Mg-Zr alloy,in relation tothe particle size of supersonic atomizing powder,have been investigated.The finer the size andthe structure of powder,the higher the strength of the alloy.While the overfine powder mayworsen plasticity of the alloy.The proper powder seems to be sized 40—100um.     

快速凝固Al—Li—Mg—Zr合金粉末粒度对组织和性能影响

研究超音雾化快速凝固Al—Li—Mg—Zr合金粉末粒度对组织和性能的影响中发现,粉末粒度越细,组织越细,合金强度越大;但粒度太细,又会导致塑性变差。试验合金粒度范围选用40—100μm为佳。     

MICROSTRUCTURE AND MECHANICAL PROPERTIES OF RAPIDLY SOLIDIFIED Al－Fe BASED ALLOYS

ＭＩＣＲＯＳＴＲＵＣＴＵＲＥＡＮＤＭＥＣＨＡＮＩＣＡＬＰＲＯＰＥＲＴＩＥＳＯＦＲＡＰＩＤＬＹＳＯＬＩＤＩＦＩＥＤＡｌ－ＦｅＢＡＳＥＤＡＬＬＯＹＳＷ．Ｊ．Ｐａｒｋ；Ｓ．Ａｈｎ；Ｒ．Ｓｃｈｍｅｅｓ；ａｎｄＮａｃｋＪ．Ｋｉｍ（１）（ＣｅｎｔｅｒｆｏｒＡｄｖ...     

锰对Ti－45Al－10Nb合金的组织和性能的影响

研究了Ｍｎ对Ｔｉ－４５Ａｌ－１０Ｎｂ（原子分数）合金铸态组织和１１００℃再结晶组织的影响以及Ｍｎ对于Ｔｉ－４５Ａｌ－１０Ｎｂ合金力学性能的影响。结果表明，Ｍｎ能促进Ｔｉ－４５Ａｌ－１０Ｎｂ合金的再结晶过程，并改善合金的力学性能     

硼对Fe_3Al合金力学性能和显微组织的影响SCIEI

本文研究了不同硼含量对Ｆｅ－２８Ａｌ－１．９４Ｃｒ合金组织结构和室温、高温力学性能的影响．加入０．０３８ａｔ．－％Ｂ后，有细小的（Ｆｅ，Ｃｒ）_２Ｂ相析出，随着硼含量增加，析出相增多增大，加入１．１８ａｔ．－％Ｂ后，析出相变成网络状．０．０３８－０．２２ａｔ．－％Ｂ可明显改善合金的塑性和强度，０．０３８ａｔ．－％Ｂ使合金压缩屈服强度由５３２ＭＰａ提高到６７８ＭＰａ，塑性由１５％提高到２５％，过量的硼不但降低了合金的塑性，也使强度明显下降．６００℃时，较低的硼含量对塑性有利，而较高的硼含量则可以提高高温强度．     

Zr,Cr和B对Ni3Al合金组织和力学性能的影响

本文研究了含Zr(0—0.6at.-％),Cr(0—7.7at.-％)和B(0—2.22at.-％)的Ni_3Al合金的组织和室温至1050℃拉伸性能。结果表明,Ni_3Al合金的屈服强度随温度升高而增加,表现出反常的温度关系。到达峰值后,随温度升高,屈服强度降低。Zr和Zr+Cr在整个试验温度范围都增加Ni_3Al合金的屈服强度,并改善高温抗张强度和塑性。硼增加Ni_3Al合金的抗张强度和屈服强度,同时改善塑性。但当硼含量超过1.37at.-％时,则降低强度和塑性。当硼含量超过溶解度极限时,Ni_3Al合金中形成岛状和球状的Ni_(20)Al_3B_6和Ni_3Al的共晶组织,对强度和塑性都是有害的。     

熔体温度对快凝Al－Si过共晶合金条带微观组织及性能的影响

研究了提高熔体喷射温度和附加高温（１２００℃）处理对快凝Ａｌ－（１４％－１８％）Ｓｉ合金条带微观组织结构、硬度及韧性的影响，分析了因不同处理温度而引起的熔体结构变化对快凝微观组织的影响规律的冶金物理本质，实验发现，快凝熔体喷射温度的提高或在熔体喷射前附加高温（如１２００℃）或恒温均匀化处理，有利于合金微观组织均匀化和细化，有利于快凝条带综合机械性能的优化．     

Ni3Al—Fe基合金组织与力学性能的研究

本文研究了合金化的Ni_3Al-Fe基合金高温变形后的组织及瞬时拉伸性能和700—900℃的蠕变持久性能,结果表明,合金由γ′的β相组成,其晶粒在温度低于1000℃时保持稳定;屈服强度在<600℃时也保持稳定;合金的高温塑性好,蠕变研究表明,该合金在700—900℃蠕变由位错攀移控制,其蠕变激活能为439kJ/mol,应力敏感系数为4.     

快速凝固TiAl基合金微晶的显微组织

用气体雾化方法制备了Ti-34Al-2Mn合金的微晶粉末,粉末典型粒度为27μm。X射线衍射结果表明,快冷态的粉末主要由α_2相和少量γ相组成。金相组织显示出等轴块状晶粒和树枝状结晶两种形态。经900℃,2h真空退火后,大部分α_2相转变成γ相,使原来的组织更加细化。     

快速凝固Al－TiC自生复合材料的显微组织和力学性能

将常规熔铸工艺与快速凝固技术相结合，成功地制备出Ａｌ－ＴｉＣ自生复合材料．常规熔铸Ａｌ－ＴｉＣ自生复合材料中ＴｉＣ的体积分数为１４．５％，颗粒尺寸为０．２－１．０μｍ，一般呈聚集态分布；与类似工艺条件下的人工复合材料相比，业已表现出较好的综合力学性能．快凝及热挤成型以后，ＴｉＣ的体积分数约为１３．５％，颗粒尺寸减至４０－８０ｎｍ，并弥散分布于晶粒尺寸为０．３０－０．８０μｍ的α－Ａｌ基体上，室温拉伸强度增加了约１００ＭＰａ，表现出良好的高温力学性能．     

MICROSTRUCTURE OF A RAPIDLY SOLIDIFIED Fe-C-Sn ALLOY

The microstructure of a laser-melted Fe-4% C-10% Sn alloy has been studied.Anon-crystalline phase was found in the upper part of the laser-melted zone:At the bottom ofthe melted zone,however,the microcrystalline zone which consists of α-Fe and a bet phasewas observed.Fine twinning martensite exists in the other area of the melted zone.     

挤压加工对SiCp／Al复合材料组织和性能的影响

开展了挤压加工对 Si Cp/ Al复合材料显微组织和力学性能的实验研究。结果表明 :挤压加工有助于提高 Si C颗粒分布的均匀性 ,挤压棒料中的 Si C颗粒在挤压方向上定向、有序地排列 ,呈现出带状组织的特征 ;挤压加工还可以消除 Si Cp/ Al复合材料毛坯中的显微疏松缺陷 ,改善铝合金基体对 Si C颗粒损伤的容限性能 ,从而大幅度地提高复合材料的强度和塑性     

急冷凝固Ni3Al合金中的亚稳相

通过急冷凝固,在Al含量超过化学计量值(25at.—％)的Ni_3Al和Ni_3Al(B)中会出现一种片层状的两相组织。经电子衍射和X射线衍射分析确定为基体γ’相和亚稳相。利用约化胞方法计算表明亚稳相为正交结构(α=0.2355nm,b=0.4157nm,c=0.1683nm),实验结果还表明,硼合金化对片层状组织的形成没有影响。     

铬含量及时效对快速凝固Cu－Cr－0．05Zr合金组织与性能的影响

研究了铬含量及时效对快速凝固Ｃｕ－Ｃｒ－０．０５ｚｒ合金组织与性能的影响。结果表明，该合金系的硬度随过饱和的铬含量增加而线性提高；临界凝固速度随铬含量的增加而增大；铬的析出会降低它在铜中的极限溶解度；当凝固速度高至使柱状晶间距小于１μｍ时，铬在单相过饱和固溶体中的极限溶解度可超过３％。合金Ｃｕ－０．８４Ｃｒ－０．０５Ｚｒ经时效处理后，硬度提高一倍以上。铬改善了此类合金的热稳定性及硬化效应。     

快速凝固Al—TiC自生复合材料的显微组织和力学性能

将常规熔铸工艺与快速凝固技术相结合，成功地制备出Ａｌ－ＴｉＣ自生复合材料．常规熔铸Ａｌ－ＴｉＣ自生复合材料中ＴｉＣ的体积分数为１４．５％，颗粒尺寸为０．２－１．０μｍ，一般呈聚集态分布；与类似工艺条件下的人工复合材料相比，业已表现出较好的综合力学性能．快凝及热挤成型以后，ＴｉＣ的体积分数约为１３．５％，颗粒尺寸减至４０－８０ｎｍ，并弥散分布于晶粒尺寸为０．３０－０．８０μｍ的α－Ａｌ基体上，室温拉伸强度增加了约１００ＭＰａ，表现出良好的高温力学性能．     

EFFECT OF Zr,Cr AND B ADDITIVES ON MICROSTRUCTURE AND MECHANICAL PROPERTIES OF Ni_3Al ALLOYS

The microstructure and the mechanical properties from room temperature up to 1050℃ ofNi_3Al alloys containing 0—0.6 at.-%Zr,0—7.7 at.-%Cr and 0—2.22 at.-%B have beenstudied.It was found that the temperature dependence of their yield strength variation revealsto be anomalous,i.e.the strength increases with the temperature raising,and then decreasestill it surpassed the peak value.Both Zr and Zr+Cr may improve the yield strength of the al-loys in the entire range of testing temperatures,as well as the tensile strength and elongationunder high temperatures.B is favourable to raise the tensile and yield strengths of the alloys,and also plasticity.But the strength will reduce as B added is over 2.22 at.-%.TheNi_(20)Al_3B_6 and Ni_3Al eutectic mixture like islands and globes precipitated inside the grainsand along the grain bounderies,which are harmful to the strength and ductility,may beformed when the B content exceeds the limit of solubility.     

快速凝固Al－Fe－Ti－C合金的显微结构及退火过程中的相变

研究了快速凝固Ａｌ－Ｆｅ－Ｔｉ－Ｃ合金的显微结构及退火过程中的相变。初始快凝态组织由α－Ａｌ微胞晶组成，在胞晶边界分布着较大并拉长的非晶相；在胞晶内部则为细小弥散的球状亚稳Ａｌ_６Ｒｅ相（底心正交结构），Ｔｉ和Ｃ全部过饱和固溶于α－Ａｌ中。当７７３Ｋ退火５ｈ时，非晶相转变为α_Ｔ－ＡｌＦｅＳｉ相（斜方结构），Ａｌ_６Ｆｅ相部分转变为片状Ａｌ_３Ｆｅ相（底心单斜结构），部分长大但仍保持球状和底心正方结构过饱和固溶于α－Ａｌ基体中的Ｔｉ和Ｃ则以ＴｉＣ形式弥散析出。     

MECHANICAL PROPERTIES IMPROVEMENT OF TiAl BY MICROSTRUCTURE REFINING

ＭＥＣＨＡＮＩＣＡＬＰＲＯＰＥＲＴＩＥＳＩＭＰＲＯＶＥＭＥＮＴＯＦＴｉＡｌＢＹＭＩＣＲＯＳＴＲＵＣＴＵＲＥＲＥＦＩＮＩＮＧＨｕａｎｇＢａｉｙｕｎ；ＨｅＹｕｅｈｕｉ；ＫｏｎｇＧａｏｎｉｎｇ；ＱｕＸｕａｎｈｕｉ（ＰｏｗｄｅｒＭｅｔａｌｌｕｒｇｙＲｅｓｅａ...