银钎焊剂水溶法改性处理工艺的优化

采用水溶法改性工艺制备银钎剂，正交试验表明，烘干时间对钎剂性能的影响最大，其次是成分配比及烘干温度．在配方为42％KF 23％KBF4 35％B2O3，烘干时间为45min，烘干温度为350℃时，制备的银钎剂质量稳定且焊接效果良好．     

采煤机截齿铜焊剂的研制与钎焊性能研究

采煤机截齿是采煤过程中大量使用的易损件,钎焊质量不佳造成截齿的巨大消耗和工作效率低下。本实验以YG15硬质合金为截齿齿头,42CrMo钢为截齿齿体,HL105铜焊片为钎料,自制水溶性铜钎焊钎剂代替传统的脱水硼砂,对采煤机截齿进行炉中钎焊。焊接接头强度得到很大提高,达到优等水平。当自制水溶性铜钎剂与水的比例为4:6时,钎料完全湿润,截齿的钎缝充盈度最高,齿头抗弯能力最好,优于工厂生产的截齿,延长了采煤机截齿的使用寿命。     

某铜矿废水的混凝法处理工艺研究

选取聚合氯化铝(PAC)、聚合氯化铁(PFC)、六水合硫酸亚铁(FS)和聚丙烯酰胺(PAM)等4种常用混凝剂,采用正交试验,以CODcr、SS、Cu2+去除率作为评价指标,以Microsoft Excel 2013程序和SPSS统计软件对数据进行回归分析,研究了不同混凝剂处理铜矿废水的效果及最佳混凝条件。结果表明:在以上混凝剂中PFC的混凝效果最佳,而FS的混凝效果最差;最佳的混凝条件为废水调整pH值至7.50,每L废水投加PFC 300mg、PAM 14mg,其CODcr、SS和Cu2+去除率均达94%以上;废水的pH值对混凝效果的影响最大。     

低银铜基钎料化学成分的设计

银基钎料成本高,价格贵,限制了它的应用,现针对水暖器材行业的特点(母材大多是铜或黄铜),设计出一种以Cu-P为基体的低银钎料.添加(2.0±0.2)%Ag,1.5%Ni,1%Sn和适量稀土元素,可改善钎料的综合性能,加工的焊丝或焊条,能达到水暖器材的钎焊要求,且降低了生产成本,提高了产品的市场竞争能力.     

粉状铝基钎料的钎焊性能研究

介绍了粉状铝基钎料的制备方法,探讨了以粉状铝基钎料为焊料,钎焊铝材的工艺性能,从表面张力的角度出发,讨论了粉末粒度对铝材钎焊工艺和性能的影响,结果表明:采用粒度在150～180 μm的粉状铝基钎料钎焊铝材,其焊件的剪切强度较高;采用粒度大于300,μm的粗钎料或粒度小于150 μm的细钎料钎焊铝材,其剪切强度较低,粉状...     

用正交试验法优化爆破参数

爆破参数是影响爆破效果的主要因素，而影响爆破效果的参数较多，其影响因素也较多，因此爆破参数优化的工作量也较大。如采用多因素试验问题的数学法──正交法，来优化爆破参数，可同时考虑多个因素及多个水平，让各个因素同时参与变化，可以大大减少试验工作量，并取得良好的效果，为生产提供了可靠的数据。     

钻井水溶法开采的地表沉陷预计研究

为了准确预计钻井水溶法开采后对地表产生的移动和变形,基于钻井水溶法开采特点,利用由不溶矿物形成的结晶水物质的膨胀率,建立了钻井水溶法开采的等价采高模型。此外,还分析了随机介质理论用于钻井水溶法开采地表沉陷预计的可行性。在阐述概率积分法基本原理的基础上,通过借鉴国内外条带水砂充填开采的预计实例,求得了钻井水溶法开采的概率积分法预计参数,并结合工程实例,利用概率积分法预计了某盐矿开采后引起的地表移动变形。结果表明:建立在上覆岩层软弱、顶板跨落基础上的概率积分预计方法适用于钻井水溶法开采的地表沉陷预计,且钻井水溶法开采后引起的地表移动变形值远小于相同条件下的煤矿开采。     

型煤中钙基固硫剂的高温固硫特征

通过正交试验，在1250℃高温下，研究了用电石渣、消石灰和石灰石作固硫剂的型煤的燃烧固硫性能。结果表明，不同钙基固硫剂之间的固硫效果存在显差异，固硫剂种类和Ca／S摩尔比是影响型煤燃烧固硫效率的主要因素，床层高度对燃烧固硫有重要影响，鼓风量对固硫效率也有一定影响，其中石灰石的高温固硫性能最好。     

不同含量银的谱线宽度测定法

在粉末发射光谱法中用谱线黑度法测定化探样中低含量银,用谱线宽度法测定同批次样品高含量银,方法快速、简便、成本低,能满足测试质量要求。     

Electrochemical dissolution process of chalcopyrite in the presence of mesophilic microorganisms

The dissolution process of chalcopyrite in the presence of mesophilic microorganisms was investigated by electrochemical measurements. X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS) analysis, accompanied by leaching experiments. Results proved that the presence of Acidithiobacillus ferrooxidans enhanced the initial reduction of chalcopyrite to intermediate species (Cu₂S), thus promoting the dissolution of chalcopyrite in the initial stage of bioleaching. However, chalcopyrite tended to be directly oxidized to polysulfide (S_n²⁻) and CuS in the later stage of bioleaching when redox potential was higher than 0.5 V (vs. Ag/AgCl), the formed polysulfide and jarosite can be responsible for the passivation of chalcopyrite in the later stage of bioleaching by A. ferrooxidans. On the contrary, Chalcopyrite was mainly directly oxidized to polysulfide and CuS in the presence of sterile 9K medium or Acidithiobacillus thiooxidans, and the initial reduction reaction was still the rate-limiting step, thus resulting in low copper extraction rate.     

Effects of oxidising agents on dissolution of Gumuskoy silver ore in cyanide solution

The aim of this research was to increase the silver extraction rate of the limonite-manganiferous silver ore from Gumuskoy, north western Turkey. The effects of the addition of oxidising agents (air, hydrogen peroxide and gaseous oxygen) on silver leaching were studied. The use of hydrogen peroxide mixed with air increased the rate of silver dissolution and also shortened the leaching time.     

沙坪洗煤厂煤泥水系统浓缩工艺的优化改造

分析了沙坪洗煤厂煤泥水系统浓缩工艺存在的问题,针对这些问题,提出了工艺优化改造,将两段浓缩工艺改造为单段浓缩工艺,提升了原设计工艺中煤泥水系统浓缩工艺的应变能力,实现了快速切换浓缩池,将煤泥中的中低灰煤泥与高灰煤泥进行分离,提升了加压过滤机处理能力和利用效果,降低了药剂消耗量,获得良好的经济效益.     

中和铁盐法处理高砷酸性废水的响应曲面优化研究

采用响应曲面法中心组合设计对中和铁盐法处理高砷酸性废水工艺过程进行设计并分析了稀释倍数、铁砷摩尔比、pH值及其交互作用对滤液砷含量的影响,建立了关于滤液砷含量的数学模型。方差分析表明,铁砷摩尔比、pH值对滤液砷含量有较显著影响,建立的数学模型拟合度良好,获得优化工艺参数为稀释倍数1.3、铁砷摩尔比为4、pH值为4,实际值与模型预测值相差0.02%,经处理后废水中砷含量为0.35 mg/L。结果表明模型预测结果可靠有效,应用响应曲面法优化得到中和铁盐法处理高砷废水工艺条件合理可行。     

提高锌浸出渣中银浮选回收率的工艺改进

锌冶炼过程中,提高锌浸出渣中银浮选回收率是增加企业生产效益的重要途径之一,文章针对某厂银浮选回收工艺存在的具体问题,着重从如何稳定浮选给矿性质、降低溶液含锌以及稳定浮选流量等方面进行了工艺改进研究,从工艺改进的结果来看,银的回收率提高了近10%,取得了良好的经济效益。     

钎焊工艺制备泡沫铝/铝夹芯板及其力学行为研究

在纯氮气保护下,对泡沫铝及3003型面板开展了焊接温度为605℃保温时间为10min的钎焊实验,采用金相观察、三点弯曲实验等分析测试方法,对泡沫铝/铝夹芯板的焊缝处的微观组织、界面结合、力学性能及断裂失效机理展开研究.结果表明:在605℃保温10min的条件下,钎料与母材实现了良好的冶金结合,焊缝中心组织主要由初生α-Al基体及针状共晶Si组成;泡沫铝/铝夹芯板在三点弯曲变形过程中会经历弹性、坍塌和失效三个变形阶段,其断裂机理属于芯层剪切断裂,而双侧焊接方式可以有效提高泡沫铝/铝夹芯板的受力载荷.     

煤矸石提取氧化铝的工艺条件优化

实验以枣庄煤矿的煤矸石为原料,研究了以高温焙烧和盐酸作为酸浸介质浸取煤矸石中的氧化铝。主要影响因素为煅烧温度、煅烧时间、盐酸的质量分数、固液比、反应温度及酸浸时间,经过实验确定最佳工艺条件为:煅烧温度700℃、煅烧时间30min、酸量60m L、固液比1:6、酸浸时间2h,反应温度105℃,在最佳条件下氧化铝的溶出实验结果表明,Al2O3溶出率为11.6%。     

Si3N4陶瓷钎焊用钎料的熔化特性与元素扩散行为

研究了微量稀土元素Ce以及不同Ti含量,对Si3N4陶瓷钎焊用钎料的熔化特性的影响.结果表明:加入微量稀土Ce,对钎料的熔化特性影响不大;当Ti含量增加到35%时,钎料的结晶温度区间明显变窄;钎料钎焊Si3N4陶瓷后发现,Ti元素向界面结合处偏聚,并与Si3N4陶瓷发生化学反应;提高钎料的Ti含量到35%,钎料和界面都会生成含Ti量高的化合物,且钎料脆性增大;提高Ti含量同时添加微量稀土元素Ce,Ti元素扩散得更加充分,钎料中粗大化合物变细变小.