Synthesis of a novel cross‐linked organophosphorus‐nitrogen containing polymer and its application in flame retardant epoxy resins

A novel cross‐linked organophosphorus–nitrogen polymetric flame retardant additive poly(urea tetramethylene phosphonium sulfate) defined as PUTMPS was synthesized by the condensation polymerization between urea and tetrahydroxymethyl phosphonium sulfate. Its chemical structure was well characterized by Fourier transform infrared (FTIR) spectroscopy, ¹³C and ³¹P solid‐state nuclear magnetic resonance. The synthesized PUTMPS and curing agent m‐phenylenediamine were blended into epoxy resins to prepare flame retardant epoxy resin thermosets. The effects of PUTMPS on fire retardancy and thermal degradation behavior of EP/PUTMPS thermosets were investigated by limiting oxygen index (LOI), vertical burning test (UL‐94), cone calorimeter measurement, and thermalgravimetric analysis (TGA) tests. The surface morphologies and chemical compositions of char residues for cured epoxy resins were investigated by scanning electron microscopy and X‐ray photoelectron spectroscopy (XPS), respectively. Water resistant properties of epoxy resin thermosets were evaluated by putting the samples into distilled water at 70°C for 168 h. The results demonstrated that the EP/12 wt% PUTMPS thermosets successfully passed UL‐94 V‐0 flammability rating and the LOI value reached 31.3%. The TGA results indicated that the incorporation of PUTMPS promoted epoxy resin matrix decomposed and char forming ahead of time, which led to a higher char yield and thermal stability for epoxy resin thermosets at high temperature. The morphological structures and analysis of XPS for the char residues of the epoxy resin thermosets shown that PUTMPS benefited to the formation of a sufficient, more compact, and homogeneous char layer with rich flame retardant elements on the materials surface during burning, which prevented the heat transmission and diffusion, limited the production of combustible gases, inhibited the emission of smoke, and then led to the reduction of the heat release rate and smoke produce rate. After water resistance tests, EP/12 wt% PUTMPS thermosets still remained excellent flame retardancy. Copyright © 2015 John Wiley & Sons, Ltd.     

Preparation and investigation of flame‐retardant epoxy resin modified with a novel halogen‐free flame retardant containing phosphaphenanthrene,triazine‐trione,and organoboron units

In this article, a novel flame retardant (coded as BNP) was successfully synthesized through the addition reaction between triglycidyl isocyanurate, 9,10‐dihydro‐9‐oxa‐10‐phosphaphenanthrene‐10‐oxide and phenylboronic acid. BNP was blended with diglycidyl ether of bisphenol‐A to prepare flame‐retardant epoxy resin (EP). Thermal properties, flame retardancy, and combustion behavior of the cured EP were studied by thermogravimetric analysis, limited oxygen index (LOI) measurement, UL94 vertical burning test, and cone calorimeter test. The results indicated that the flame retardancy and smoke suppressing properties of EP/BNP thermosets were significantly enhanced. The LOI value of EP/BNP‐3 thermoset was increased to 32.5% and the sample achieved UL94 V‐0 rating. Compared with the neat EP sample, the peak of heat release rate, average of heat release rate, total heat release, and total smoke production of EP/BNP thermosets were decreased by 58.2%–66.9%, 27.1%–37.9%, 25.8%–41.8%, and 21.3%–41.7%, respectively. The char yields of EP/BNP thermosets were increased by 46.8%–88.4%. The BNP decomposed to produce free radicals with quenching effect and enhanced the charring ability of EP matrix. The multifunctional groups of BNP with flame retardant effects in both gaseous and condensed phases were responsible for the excellent flame retardancy of the EP/BNP thermosets. © 2017 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2017 , 134, 45291.     

The flame retardant group‐synergistic‐effect of a phosphaphenanthrene and triazine double‐group compound in epoxy resin

A flame retardant tri‐(phosphaphenanthrene‐(hydroxyl‐methylene)‐phenoxyl)‐1, 3, 5‐triazine (Trif‐DOPO) and its control samples are incorporated into diglycidyl ether of bisphenol‐A (DGEBA) and 4, 4′‐diamino‐diphenyl sulfone (DDS) to prepare flame retardant thermosets, respectively. According to the results of limited oxygen index (LOI), UL94 vertical burning test and cone calorimeter test, the Trif‐DOPO/DGEBA/DDS thermoset with 1.2 wt % phosphorus possesses the LOI value of 36% and UL94 V‐0 flammability rating, and Trif‐DOPO can decrease the peak of heat release rate (pk‐HRR) and reduce the total heat release (THR) of thermosets. All these prove better flame retardant performance of Trif‐DOPO than that of 9,10‐dihydro‐9‐oxa‐10‐phosphaphenanthrene‐10‐oxide(DOPO). The residue photos of thermosets after cone calorimetry test disclose that Trif‐DOPO can promote the formation of thick and tough melting char layer for combined action of the flame retardant groups of Trif‐DOPO. The results from thermo gravimetric analysis (TGA) and pyrolysis‐gas chromatography‐mass spectrometry(Py‐GC/MS) show that the groups in Trif‐DOPO can be decomposed and produce PO₂ fragments, phosphaphenanthrene and phenoxy fragments, which can jointly quench the free radical chain reaction during combustion. Therefore, the excellent flame retardancy of Trif‐DOPO is attributed to its flame retardant group‐synergic‐effect. © 2013 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2014 , 131, 39709.     

Synthesis and performance of a novel nitrogen‐containing cyclic phosphate for intumescent flame retardant and its application in epoxy resin

A novel nitrogen‐containing cyclic phosphate (NDP) was synthesized and well characterized by ¹H, ¹³C, ³¹P NMR, mass spectra and elemental analysis. NDP was used as an additive intumescent flame retardant (AIFR) to impart flame retardancy and dripping resistance for diglycidyl ether of bisphenol‐A epoxy resin (DGEBA) curied by 4,4′‐diaminodiphenylsulfone (DDS) with different phosphorus content. The flammability, thermal stability, and mechanical properties of NDP modified DGEBA/DDS thermosets were investigated by UL‐94 vertical burning test, differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), and Izod impact strength and flexural property tests. The results showed that NDP modified DGEBA/DDS thermosets exhibited excellent flame retardancy, moderate changes in glass transition temperature and thermal stability. When the phosphorus content reached only 1.5 wt %, the NDP modified DGEBA/DDS thermoset could result in satisfied flame retardancy (UL‐94, V‐0). The TGA curves under nitrogen and air atmosphere suggested that NDP had good ability of char formation, and there existed a distinct synergistic effect between phosphorus and nitrogen. The flame retardant mechanism was further realized by studying the structure and morphology of char residues using FT‐IR and scanning electron microscopy (SEM). It indicated that NDP as phosphorus‐nitrogen containing flame retardant worked by both of the condensed phase action and the vapor phase action. Additionally, the addition of NDP decreased slightly the flexural strength of the flame retarded DGEBA epoxy resins, and increased the Izod impact strength of these thermosets. © 2014 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2015 , 132, 41859.     

Effect of a novel phosphorus‐containing compound on the flame retardancy and thermal degradation of intumescent flame retardant polypropylene

A novel flame retardant, tetra(5,5‐dimethyl‐1,3‐ dioxaphosphorinanyl‐2‐oxy) neopentane (DOPNP), was synthesized successfully, and its structure was characterized by FT‐IR, ¹H NMR, and ³¹P NMR. The thermogravimetric analysis (TGA) results demonstrate that DOPNP showed a good char‐forming ability. Its initial decomposition temperature was 236.4°C based on 1% mass loss, and its char residue was 41.2 wt % at 600°C, and 22.9 wt % at 800°C, respectively. The flame retardancy and thermal degradation behavior of novel intumescent flame‐retardant polypropylene (IFR‐PP) composites containing DOPNP were investigated using limiting oxygen index (LOI), UL‐94 test, TGA, cone calorimeter (CONE) test, and scanning electron microscopy (SEM). The results demonstrate that DOPNP effectively raised LOI value of IFR‐PP. When the loading of IFR was 30 wt %, LOI of IFR‐PP reached 31.3%, and it passed UL‐94 V‐0. TGA results show that DOPNP made the thermal decomposition of IFR‐PP take place in advance; reduced the thermal decomposition rate and raised the residual char amount. CONE results show that DOPNP could effectively decrease the heat release rate peak of IFR‐PP. A continuous and compact char layer observed from the SEM further proved the flame retardance. © 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2011.     

纳米Al_2O_3对含磷环氧树脂体系的性能影响

研究了以纳米Al_2O_3作为协同阻燃剂,对EP/DOPO和EP/HPCTP树脂固化物阻燃性能的影响。通过热重分析测试(TGA)、动态热机械分析测试(DMA)、氧指数测定(LOI)及垂直燃烧测试(UL-94)重点探讨了树脂固化物的耐热及阻燃性能。测试结果表明,含磷阻燃剂有助于提高环氧树脂固化物的阻燃性能,但会降低其玻璃化转变温度(Tg)。随着纳米Al_2O_3的加入,残炭率(800℃)、极限氧指数(LOI)得到进一步的提高,并且能够在一定程度上提升树脂固化物的玻璃化转变温度(Tg)和初始热裂解温度(T5%)。     

Flame retardant performance of a carbon source containing DOPO derivative in PET and epoxy

The combination of gas‐phase and condensed‐phase action will contribute to high quality flame retardant. A novel 9,10‐dihydro‐9‐oxa‐10‐phosphaphenanthrene‐10‐oxide (DOPO)‐based flame retardant (DOPO‐DOPC), which contains carbon source was synthesized in favor of conducting the effect of gas‐phase as well as promoting the char formation in condensed‐phase. The chemical structure of DOPO‐DOPC was characterized by nuclear magnetic resonance (NMR) and Fourier transform infrared spectroscopy (FTIR). DOPO–DOPC was used as an additive in poly(ethylene terephthalate) (PET) and epoxy resin (EP). The flame retardancy of PET/DOPO‐DOPC and EP/DOPO‐DOPC composites were studied by limiting oxygen index (LOI) and UL‐94 test. The results showed that the incorporation of DOPO–DOPC into PET or EP could obviously improve their flame retardancy. The LOI values of modified PET or EP, which contained 10 wt % DOPO‐DOPC reached 42.8 and 31.7%, respectively. The thermogravimetric analysis (TGA) results revealed that DOPO–DOPC enhanced the formation of char residues. The Laser Raman spectroscopy (LRS) was used to investigate the carbon structure of thermal oxidation residues. Because of the combination of the gas phase flame retardant effect of DOPO moiety and the promoting formation of char residues in condensed phase, the PET and EP composites exhibited significant improvement toward flame retardancy. © 2016 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2017 , 134, 44639.     

Synthesis of a phenylene phenyl phosphine oligomer and its flame retardancy for polycarbonate

A novel flame retardant, phenylene phenyl phosphine oligomer (PPPO) was synthesized and its chemical structure was characterized using Fourier transform infrared spectroscopy, ¹H, ¹³C, ³¹P nuclear magnetic resonance spectroscopy and mass spectrometer. PPPO was used to impart flame retardancy to polycarbonate (PC). Combustion behaviors and thermal degradation properties of PC/PPPO system were assayed by limiting oxygen index (LOI), vertical burning test (UL‐94), cone calorimeter test, and thermogravimetric analysis. PC/6 wt % PPPO passed UL‐94 V‐0 rating with 3.0 mm samples and the LOI value was 34.1%, and PC/8 wt % PPPO also passed UL‐94 V‐0 rating with 1.6 mm samples and the LOI value was 36.3%. Scanning electron microscopy reveals that the char properties had crucial effects on the flame retardancy of PC. Mechanical properties and water resistance of PC/PPPO system were also measured. After water resistance test, PC/6 wt % PPPO with 3.0 mm samples and PC/8 wt % PPPO with 1.6 mm samples kept V‐0 rating and mass loss was only 0.2%. The results revealed that PPPO was an efficient flame retardant for PC. © 2012 Wiley Periodicals, Inc. J. Appl. Polym. Sci., 2013     

Synergistic flame‐retardant effect of halloysite nanotubes on intumescent flame retardant in LDPE

Synergistic flame‐retardant effect of halloysite nanotubes (HNTs) on an intumescent flame retardant (IFR) in low‐density polyethylene (LDPE) was investigated by limited oxygen index (LOI), vertical burning test (UL‐94), thermogravimetric analysis (TGA), cone calorimeter (CC) test, and scanning electronic microscopy (SEM). The results of LOI and UL‐94 tests indicated that the addition of HNTs could dramatically increase the LOI value of LDPE/IFR in the case that the mass ratio of HNTs to IFR was 2/28 at 30 wt % of total flame retardant. Moreover, in this case the prepared samples could pass the V‐0 rating in UL‐94 tests. CC tests results showed that, for LDPE/IFR, both the heat release rate and the total heat release significantly decreased because of the incorporation of 2 wt % of HNTs. SEM observations directly approved that HNTs could promote the formation of more continuous and compact intumescent char layer in LDPE/IFR. TGA results demonstrated that the residue of LDPE/IFR containing 2 wt % of HNTs was obviously more than that of LDPE/IFR at the same total flame retardant of 30 wt % at 700°C under an air atmosphere, and its maximum decomposing rate was also lower than that of LDPE/IFR, suggesting that HNTs facilitated the charring of LDPE/IFR and its thermal stability at high temperature in this case. Both TGA and SEM results interpreted the mechanism on the synergistic effect of HNTs on IFR in LDPE, which is that the migration of HNTs to the surface during the combustion process led to the formation of a more compact barrier, resulting in the promotion of flame retardancy of LDPE/IFR. In addition, the mechanical properties of LDPE/IFR/HNTs systems were studied, the results showed that the addition of 0.5–2 wt % of HNTs could increase the tensile strength and the elongation at break of LDPE/IFR simultaneously. © 2013 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2014 , 131, 40065.     

Synthesis of a novel flame retardant containing phosphorus and sulfur and its application in polycarbonate

A novel flame retardant containing phosphorus and sulfur, bis(2‐tienyl)phenylphosphine (BTPP) was synthesized and characterized with Fourier transform infrared spectroscopy, ¹H, ¹³C, and ³¹P nuclear magnetic resonance. BTPP was used to impart flame retardancy to polycarbonate (PC). Combustion behaviors and thermal degradation properties of PC/BTPP system were assayed by limiting oxygen index (LOI), vertical burning test (UL‐94), cone calorimeter test, and thermogravimetric analysis. PC/3 wt% BTPP passed UL‐94 V‐0 rating with 3.0 mm samples and the LOI value was 36.5%. PC/6 wt% BTPP passed UL‐94 V‐0 rating with 1.6 mm samples and the LOI value was 38.5%. Scanning electron microscopy revealed that char properties had direct effects on the flame retardancy. Mechanical properties and water resistance of PC/BTPP system were also examined. After water resistance test, PC/3 wt% BTPP with 3.0 mm samples and PC/6 wt% BTPP with 1.6 mm samples kept V‐0 rating and mass loss were only 0.2%. POLYM. ENG. SCI., 2012. © 2012 Society of Plastics Engineers     

An easy‐to‐obtain silicone‐containing flame retardant and its effects on the combustion of polycarbonate

A novel silicone‐containing flame retardant (HSOBA) synthesized from hydrogen‐containing silicone oil and Bisphenol A via a simple approach has been incorporated into polycarbonate (PC) matrix to study its effects on the flame retardancy. The flame retardancy of PC/HSOBA composites is investigated by limiting oxygen index (LOI), vertical burning tests (UL‐94), and cone calorimeter measurement. The LOI value of the composites is 31.7 and the UL‐94 rating reaches V‐0, when the content of HSOBA is 3 wt %. Cone calorimeter data confirm that the HSOBA acts as an effective additive functioning both as flame retardants and as smoke suppressant. Evolution of the thermal behaviors of the composites tested by TGA, the morphological structures, and the constituent of char residue after LOI tests characterized by scanning electronic microscopy‐energy‐dispersive X‐ray analysis were used to explain the possible flame‐retardant mode. © 2012 Wiley Periodicals, Inc. J Appl Polym Sci, 2012     

Thermal degradation behaviors and flame retardancy of epoxy resins with novel silicon‐containing flame retardant

A novel macromolecular silicon‐containing intumescent flame retardants (Si‐IFR) was synthesized, and its structure was a caged bicyclic macromolecule containing phosphorus‐silicon characterized by IR. Epoxy resins (EP) were modified with Si‐IFR to get the flame retardant EP, whose flammability and burning behavior were characterized by UL 94 and limiting oxygen index (LOI). Twenty percentage of weight of Si‐IFR was doped into EP to get 27.5% of LOI and UL 94 V‐0. The degradation behavior of the flame retardant EP was studied by thermogravimetry, differential thermogravimetry, scanning electron microscopy, and X‐ray photoelectron spectroscopy analysis. The experimental results exhibited that when EP/Si‐IFR was heated, the phosphorus‐containing groups firstly decompose to hydrate the char source‐containing groups to form a continuous and protective carbonaceous char, which changed into heat‐resistant swollen char by gaseous products from the nitrogen‐containing groups. Meanwhile, SiO₂ reacts with phosphate to yield silicophosphate, which stabilizes the swollen char. The barrier properties and thermal stability of the swollen char are most effective in resisting the transport of heat and mass to improve the flame retardancy and thermal stability of EP. © 2012 Wiley Periodicals, Inc. J. Appl. Polym. Sci., 2013     

Flame‐retardant properties and mechanisms of epoxy thermosets modified with two phosphorus‐containing phenolic amines

Two phosphorus‐containing phenolic amines, a 9,10‐dihydro‐9‐oxa‐10‐phosphaphenanthrene‐10‐oxide (DOPO)‐based derivative (DAP) by covalently bonding DOPO and imine (SB) obtained from the condensation of p‐phenylenediamine with salicylaldehyde, and its analog (AP) via the addition reaction between diethyl phosphite and SB, were used to prepare flame‐retardant epoxy resins. The burning behaviors and dynamic mechanical properties of epoxy thermosets were studied by limited oxygen index (LOI) measurement, UL‐94 test, and dynamic mechanical analysis. The flame‐retardant mechanisms of modified thermosets were investigated by thermogravimetric analysis, Py‐GC/MS, Fourier transform infrared, SEM, elemental analysis, and laser Raman spectroscopy. The results revealed that epoxy thermoset modified with DAP displayed the blowing‐out effect during UL‐94 test. With the incorporation of 10 wt % DAP, the modified thermoset showed an LOI value of 36.1% and V‐0 rating in UL‐94 test. The flame‐retardant mechanism was ascribed to the quenching and diluting effect in the gas phase and the formation of phosphorus‐rich char layers in the condensed phase. However, the thermoset modified with 10 wt % AP only showed an LOI value of 25.7% and no rating in UL‐94 test, which was possibly ascribed to the mismatching of charring process with gas emission process during combustion. © 2016 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2016 , 133, 43953.     

Epoxy resin/phosphorus‐based microcapsules: Their synergistic effect on flame retardation properties of high‐density polyethylene/graphene nanoplatelets composites

Two types of microcapsule flame retardants are prepared by coating ammonium polyphosphate (APP) and aluminum diethylphosphinate (ADP) with epoxy resin (EP) as the shell via in situ polymerization, and blended with high density polyethylene (HDPE)/graphene nanoplatelets (GNPs) composites to obtain flame‐retardant HDPE materials. Fourier transform infrared spectroscopy, scanning electron microscopy (SEM), and water contact angle results confirm the formation of core–shell structures of EP@APP and EP@ADP. The limiting oxygen index (LOI), vertical burning test (UL‐94), cone calorimetry, and Raman spectroscopy are employed to characterize the HDPE/GNPs composites filled with EP@APP and EP@ADP core–shell materials. A UL94 V‐0 level and LOI of 34% is achieved, and the two flame retardants incorporated in the HDPE/GNPs composite at 20 wt % in total play a synergistic effect in the flame retardancy of the composite at a mass ratio of EP@ADP:EP@APP = 2:1. According to the cone‐calorimetric data, the compounding composites present much lower peak heat release rate (300 kW/m²) and total heat release (99.4 MJ/m²) than those of pure HDPE. Raman spectroscopic analysis of the composites after combustion reveals that the degree of graphitization of the residual char can reach 2.31, indicating the remarkable flame retarding property of the composites. © 2018 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2018 , 135, 46662.     

Effect of charring agent THEIC on flame retardant properties of polypropylene

Tris(2‐hydroxyethyl) isocyanurate (THEIC) was used as charring agent and combined with ammonium polyphosphate (APP) to form an intumescent flame retardant (IFR) for polypropylene (PP). The flame retardancy and combustion performance of PP/IFR composite was tested by limiting oxygen index (LOI), UL‐94 vertical burning test and cone calorimeter. The results showed that PP/IFR composite had highest LOI of 34.8 and obtained V‐0 rating when 30 wt % IFR was loaded and mass ratio APP/THEIC was 2 : 1. The peak heat release (PHRR) and total heat release (THR) values of PP composite containing FRs were remarkably reduced compared with that of pure PP. However, water resistant test demonstrated the PP/IFR composite had poor flame retardant durability, both the LOI value and UL‐94 V‐rating decreased when PP/IFR composite was soaked in water at 70°C after 36 h. The degradation process and the char morphology of IFR and PP/IFR composite were investigated by TGA and SEM images. The possible reaction path between APP and THEIC in the swollen process was proposed. © 2014 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2015 , 132, 41214.     

Novel flame‐retardant epoxy composites containing aluminium β‐carboxylethylmethylphosphinate

A novel flame‐retardant aluminum β‐carboxylethylmethylphosphinate [Al(CEP)] was synthesizedby a simple process. The effect of Al(CEP) on the curing of epoxy resin (EP) was investigated with differential scanning calorimetry (DSC) and Fourier transform infrared spectroscopy. The flame retardancy and thermal properties of Al(CEP)/EP were analyzed by a limiting oxygen index (LOI), vertical burning test (UL‐94), scanning electron microscopy (SEM) with energy‐dispersive X‐ray (EDX), gravimetric analyses, and DSC. Results disclosed that curing of EP is delayed by incorporating Al(CEP). The flexural strength of EP is reduced but the flexural modulus is increased by adding Al(CEP). Adding Al(CEP) depresses the decomposition of EP while leads to a increase in the glass transition temperature (T_g), in char formation and in flame retardancy of EP. EP containing 25 phr Al(CEP) provides LOI of 28.3% and passes UL‐94 V‐0 rating. SEM results show that the sample passing V‐0 rating can form the condensed char whereas porous char is observed from the sample failing in V‐0 rating after combustion. EDX analysis shows that the condensed char presents higher weight ratio of carbon to phosphorus than the porous char, indicating appropriate amount of Al(CEP) is necessary for formation of the stable char. POLYM. ENG. SCI., 55:657–663, 2015. © 2014 Society of Plastics Engineers     

Synthesis of phospholipidated β‐cyclodextrin and its application for flame‐retardant poly(lactic acid) with ammonium polyphosphate

In this study, phospholipidated β‐cyclodextrin (PCD) was obtained by the condensation between β‐cyclodextrin and phenyl phosphonic acid dichloride, which was characterized by Fourier transform infrared (FTIR) spectra, ¹H‐NMR, and thermogravimetric analysis (TGA). The thermal stability and flame retardancy of the poly(lactic acid) (PLA) blends [PLA–ammonium polyphosphate (APP)–PCD] were measured by TGA coupled to FTIR spectroscopy, vertical burning test (UL‐94), limiting oxygen index (LOI), and cone calorimetry tests. The results show that the mass ratio and loading amount of APP and PCD affected the properties of PLA. When the loading of APP and PCD was 30 wt % and the mass ratio of APP to PCD was 5:1, the highest LOI value of 42.6% (that of neat PLA was 19.7%) and a UL‐94 V0 rating were achieved, and the reduction of the total heat release was greater than 80%. Even when the total amount of APP and PCD was decreased to 20 wt % with the same mass ratio, the flame‐retardant PLA still can achieved a UL‐94 V0 rating. The improved performance was explained by the formation of an intumescent, continuous, contact char layer. Moreover, the reaction between APP and PCD contributed to the improvement of the thermal stability of the char residue. © 2017 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2018 , 135, 46054.     

Synthesis of a novel curing agent containing organophosphorus and its application in flame‐retarded epoxy resins

A novel amine‐terminated and organophosphorus‐containing compound m‐aminophenylene phenyl phosphine oxide oligomer (APPPOO) was synthesized and used as curing and flame‐retarding agent for epoxy resins. Its chemical structure was characterized by Fourier transform infrared (FTIR) spectroscopy, ¹H nuclear magnetic resonance (¹H NMR), ¹³C nuclear magnetic resonance, and ³¹P nuclear magnetic resonance. The flame‐retardant properties, combusting performances, and thermal degradation behaviors of the cured epoxy resins were investigated by limiting oxygen index (LOI), vertical burning test (UL‐94), cone calorimeter test, and thermogravimetric analysis. The EPO/APPPOO thermosets passed V‐1 rating with the thickness of 3.0 mm and the LOI value reached 34.8%. The thermosets could pass V‐2 rating when the thickness of the samples was 1.6 mm. The cone calorimeter test demonstrated that the parameters of EPO/APPPOO thermosets including heat release rate and total heat release significantly decreased compared with EPO/PDA thermosets. Scanning electron microscopy revealed that the incorporation of APPPOO into epoxy resins obviously accelerated the formation of the compact and stronger char layer to improve flame‐retardant properties of the cured epoxy resins during combustion. The mechanical properties and water resistance of the cured epoxy resins were also measured. After the water‐resistance test, EPO/APPPOO thermosets still remained excellent flame retardant and the water uptake was only 0.4%. © 2014 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2014 , 131, 41159.     

An effective flame retardant for poly(ethylene terephthalate) synthesized by phosphaphenanthrene and cyclotriphosphazene

A novel flame retardant [9,10‐Dihydro‐9‐oxa‐10‐phosphaphenanthrene‐10‐oxideÔtriphosphazene (DOPO–TPN)] based on phosphaphenanthrene and cyclotriphosphazene was synthesized and used to improve the flame retardancy of poly(ethylene terephthalate) (PET). The structure of DOPO–TPN was characterized by nuclear magnetic resonance, Fourier transform infrared spectroscope (FTIR), and elemental analysis. PET/DOPO–TPN composites with different amount of DOPO–TPN were prepared and the flame retardancy was determined by limiting oxygen index (LOI) and vertical burning test (UL‐94). With the incorporation of 5 wt % DOPO–TPN, the composite achieved a LOI value of 34% and UL‐94 V‐0 rating. The thermal properties of the PET/DOPO–TPN composites were investigated by thermogravimetric analysis. The flame retardant mechanism was investigated by pyrolysis‐gas chromatography/mass spectrometry (Py‐GC/MS), FTIR, and scanning electron microscopy (SEM). The Py‐GC/MS results showed that DOPO based fragments would exist in the gas phase during the pyrolysis of PET/DOPO–TPN composites which demonstrated that DOPO–TPN could act through gas‐phase action to exert flame retardant effect. The results of FTIR and SEM demonstrated that DOPO–TPN could promote the formation of compact and intact char residues to inhibit the heat and combustible gas transmission in condensed phase. © 2017 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2017 , 134, 45246.     

Synthesis of a novel flame retardant containing phosphazene and triazine groups and its enhanced charring effect in poly(lactic acid) resin

A novel flame retardant heax‐[N,N′,N″‐tris‐(2‐amino‐ethyl)‐[1,3,5] triazine‐2,4,6‐triamine] cyclotriphosphazene (HTTCP) containing phosphazene and triazine groups was synthesized and characterized by Fourier transform infrared spectroscopy (FTIR), solid‐state ¹H and ¹³C nuclear magnetic resonance (NMR) spectroscopy. HTTCP was applied to PLA matrix. The results of thermal gravimetric analysis (TGA), the limited oxygen index (LOI), and cone calorimeter test indicated that the HTTCP enhanced the thermal stability and flame retardant properties of PLA. When the mass fraction of HTTCP was 25 wt %, the PLA composite acquired a LOI value of 25.2% and the lower pk‐HRR at 290 kW/m². The excellent flame retardancy of HTTCP was attributed to the group synergistic effect between phosphazene and triazine groups. However, when combined HTTCP with APP (the total amount remaining 25 wt %, the ratio of HTTP to APP are 1:1 and 1:2), high values of LOI (over 40%) and UL94 V‐0 rating without dripping reached simultaneously. Meanwhile, the heat release rate, total heat release and mass loss rate were all decreased dramatically. Scanning electron microscopy (SEM) demonstrated that HTTCP/APP system benefited to the formation of more intumescent, dense, compact char layer on the materials surface which could effectively prevent the underlying material from degradation during burning. © 2016 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2017 , 134, 44660.