内置型钢桁架高强混凝土中高剪力墙抗震性能试验研究

为了研究内置型钢桁架高强混凝土中高剪力墙的抗震性能,采用不同的暗柱类型及不同的暗柱和暗支撑型钢配钢率,设计制作了3片1/4缩尺、剪跨比1.8、混凝土强度等级为C70的内置型钢桁架高强混凝土中高剪力墙试件,对其进行水平往复加载试验,比较3片高强混凝土中高剪力墙试件的受力过程、破坏形态、滞回性能、位移延性以及侧向刚度退化特征。试验结果表明:内置型钢桁架高强混凝土中高剪力墙试件的最终破坏形态主要为弯曲型破坏,相比于普通高强混凝土中高剪力墙,其位移延性以及后期侧向刚度退化都有明显改善;增加暗柱型钢配钢率能提高试件的水平承载力,但会降低延性性能;增加暗支撑型钢配钢率能显著改善试件的延性,但承载力变化不明显,说明型钢暗支撑对改善高强混凝土中高剪力墙的抗震性能更为有效。     

内置冷弯薄壁型钢桁架高强混凝土剪力墙抗震性能试验研究

为研究内置冷弯薄壁型钢桁架高强混凝土剪力墙的抗震性能,对8个比例为1/4的剪力墙进行了恒定轴压力下的水平低周往复加载试验,研究了不同剪跨比下内置桁架斜撑截面形式和斜撑截面积对剪力墙破坏机理、滞回性能、变形能力、耗能能力以及刚度退化特征等的影响。研究结果表明:剪力墙的破坏形态主要为弯曲破坏;滞回曲线有较明显的捏缩效应;位移延性系数介于7.42~14.6之间,破坏时的位移角介于1/73~1/44之间;中高剪力墙内置桁架采用等边角钢斜撑变形能力和耗能能力更好,而低矮剪力墙内置桁架采用格构式斜撑则对抗震更为有利;考虑最优暗柱配钢率和斜撑截面积,可取得良好的抗震性能。最后采用有限元分析软件ABAQUS对试件的骨架曲线进行了模拟,有限元分析结果与试验结果吻合较好。     

内置轻钢桁架混凝土组合剪力墙抗震性能试验研究

将冷弯薄壁型钢桁架配置在普通钢筋混凝土剪力墙中代替钢筋而形成轻钢桁架混凝土组合剪力墙。为研究该类墙体的抗震性能,对两组共6个内置轻钢桁架混凝土组合剪力墙进行拟静力试验,研究轴压比和斜撑体积配钢率对其滞回性能、变形性能、刚度退化以及耗能能力的影响。对比了低矮剪力墙和中高剪力墙的位移延性和耗能能力。结果表明：轴压比对该类剪力墙的变形能力和耗能能力均不利,应予以控制;斜撑体积配钢率对提高低矮墙的延性、耗能能力效果明显,但对承载力的提高作用较小;对中高剪力墙,斜撑体积配钢率的增加,对其耗能能力不利。     

一字形型钢高强混凝土短肢剪力墙抗震性能试验研究

对6片一字形型钢高强混凝土短肢剪力墙试件进行低周反复荷载试验,研究不同型钢配置形式、不同轴压比的型钢高强混凝土短肢剪力墙的承载力、滞回特性及破坏机理。试验结果表明:格构式配钢试件和实腹式配钢试件的破坏过程相近,试件内置实腹式钢板较好地抑制了斜裂缝的发展;轴压比对两种配钢形式试件的承载力和延性影响规律一致,即随着轴压比的提高,试件承载力提高而延性下降;格构式配钢试件承载力比实腹式配钢试件略高,但实腹式配钢试件的延性更好。根据试验结果,提出型钢高强混凝土短肢剪力墙承载力计算式,与试验结果对比表明两者吻合较好。     

型钢高强混凝土剪力墙抗震性能试验研究

为了研究型钢高强混凝土剪力墙的抗震性能,对8个剪跨比为2.5的剪力墙试件进行了拟静力试验。通过改变试件的轴压比、配箍特征值和配钢率,研究其在往复水平荷载作用下的破坏机理、滞回性能、变形能力以及耗能能力。试验结果表明,这种剪力墙的破坏形态为墙底部截面约束区混凝土被压碎的弯曲型破坏;试件的滞回曲线饱满,没有明显的捏缩现象;位移延性系数在3.50～4.66之间,并且随着配箍特征值和配钢率的增加,试件的变形能力提高;等效粘滞阻尼比在0.196～0.255之间,试件表现出较好的耗能能力。根据墙体在不同阶段的破坏程度,将型钢混凝土剪力墙结构的性能划分为使用良好、保证人身安全和防止倒塌三个性能水平,提出用位移角作为型钢混凝土剪力墙结构的性能指标,并给出了不同性能水平位移角限值的建议值。图10表6参14     

一字形型钢高强混凝土短肢剪力墙抗震性能试验研究

对6片一字形型钢高强混凝土短肢剪力墙试件进行低周反复荷载试验,研究不同型钢配置形式、不同轴压比的型钢高强混凝土短肢剪力墙的承载力、滞回特性及破坏机理。试验结果表明：格构式配钢试件和实腹式配钢试件的破坏过程相近,试件内置实腹式钢板较好地抑制了斜裂缝的发展;轴压比对两种配钢形式试件的承载力和延性影响规律一致,即随着轴压比的提高,试件承载力提高而延性下降;格构式配钢试件承载力比实腹式配钢试件略高,但实腹式配钢试件的延性更好。根据试验结果,提出型钢高强混凝土短肢剪力墙承载力计算式,与试验结果对比表明两者吻合较好。     

型钢高强混凝土框架柱抗震性能试验研究

基于16个型钢高强混凝土(SRHSC)框架柱试件的低周反复加载试验,对其抗震性能进行了研究。试件设计参数为剪跨比、轴压比、混凝土强度、含钢率和配箍率。对不同设计参数试件的受力特点、破坏形态、滞回性能、骨架曲线、耗能能力、位移延性等主要抗震性能指标进行了分析,得到了试件耗能指标、位移延性与诸设计参数之间的关系曲线。试验结果表明：试件荷载-位移滞回曲线饱满,下降段较为平缓,其他各项抗震性能指标较为优异,总体上表现出良好的抗震性能;混凝土强度等级超过C100的SRHSC框架柱的承载力优势明显,但由于高强混凝土的脆性导致其耗能能力及延性较普通型钢混凝土框架柱稍差;试件剪跨比、含钢率以及配箍率的提高能够增强其抗震性能,而混凝土强度、轴压比的提高将降低其抗震性能。     

高强型钢高性能混凝土剪力墙抗震性能研究

设计了4片高强型钢高性能混凝土剪力墙试件,对其进行了低周反复加载试验。分析了试件在压、弯、剪共同作用下的破坏过程和破坏机理,讨论了含钢率、配箍特征值等参数对这种剪力墙的破坏形态、荷载-位移滞回曲线、骨架曲线、位移延性、刚度退化和耗能能力以及承载力的影响。研究结果表明,轴压比、配钢率、配箍率以及边缘约束区长度等对这种剪力墙的破坏形态、承载力、延性、滞回特性等均有影响,按《型钢混凝土组合结构技术规程》(JGJ 138—2001)中型钢混凝土剪力墙承载力计算公式所得结果与试验结果吻合较好。     

高强钢筋高强混凝土双连梁剪力墙抗震性能试验研究

高强钢筋、高强混凝土剪力墙结构中使用双连梁可以有效改善结构受力性能,解决设计中经常遇到的诸如连梁超筋、截面受剪承载力不足等问题。基于此,设计并制作了2个3层1/4缩尺的高强钢筋高强混凝土双肢剪力墙试件,其中一个试件的连梁采用单连梁形式,另一个试件的连梁采用双连梁形式。在相同的试验条件下,对比研究二者在低周反复荷载作用下的承载力、滞回特性、延性、耗能能力,分析双连梁结构形式在高强钢筋高强混凝土双肢剪力墙中的性能及作用。试验结果表明：具有相同配筋率的分缝双连梁双肢剪力墙结构与小跨高比单连梁双肢剪力墙结构相比,承载力降低了20%～30%,延性增加了约30%,耗能能力增加了约20%,在弹性阶段刚度降低约30%。从最终的破坏形态来看,单连梁剪力墙试件连梁出现了明显的剪切斜裂缝,箍筋全部屈服,最终发生剪切破坏;双连梁剪力墙试件只在连梁端部出现了弯曲裂缝未出现斜裂缝,箍筋自始至终未屈服,最终发生弯曲破坏。双连梁剪力墙结构能有效降低连梁内力,提高其延性。     

改善高强混凝土剪力墙抗震性能的试验研究

通过四片高强度混凝土剪力墙试件）有整体墙和墙板中开竖缝墙）在低周反复荷载作用下的试验,研究开竖缝数量及长度（即墙板柱的剪跨比）对剪力墙的刚度、载力、延性、能耗、破坏形态等抗震性能的影响,结果表明,在剪力墙板中合理地设置竖缝,可使其弹性刚度、承载力变化不大的情况下,较大幅度地提高它的延性,塑性变形和耗能力。     

Experimental study on seismic behavior of mid-rise RC shear wall with concealed truss

In this paper, mid-rise shear wall with concealed truss was proposed. This new composite shear wall includes two kinds of composition: one is the composition of two bearing systems, including truss and shear wall, and the other is the composition of two materials, including steel and concrete. Therefore, it is a double composite shear wall. The experimental study on the seismic behavior of six 1/3 scale mid-rise shear walls, including an ordinary mid-rise shear wall, a mid-rise shear wall with steel frame, and four mid-rise shear wall with concealed truss made of different materials, was studied. Based on the experimental study, the stiffness and its attenuation, bearing capacity, ductility, hysteretic property, energy dissipation, and failure phenomena of each shear wall were contrastively analyzed. The formulas of bearing capacity and stiffness were established. The results obtained from the formulas and those from experiment are in good agreement. Some suggestions for seismic design of shear wall are given in this paper. The experimental results show that the seismic behavior of the mid-rise shear wall with steel frame and that of every truss with different materials is obviously improved.     

型钢超高强混凝土柱抗震性能试验研究

为研究型钢超高强混凝土柱的抗震性能,开展了27根型钢超高强混凝土柱试件的低周反复加载试验。试件设计参数为剪跨比、轴压力水平、配箍、型钢和栓钉配置情况。针对不同设计参数的试件的破坏特征、滞回曲线、水平承载力、耗能能力及变形能力、承载力及刚度退化等进行了分析,得到了各设计参数的影响规律。试验结果表明：型钢超高强混凝土柱的滞回曲线饱满且较稳定;剪跨比较大、轴压比较低、箍筋有效约束指标较大、配置H型或十字型钢的试件具有更好的抗震性能;型钢在箍筋约束效果较好时,能更充分地发挥提高柱抗震性能的作用;通过配置高强度八边形复合箍筋,能有效避免型钢超高强混凝土短柱发生脆性剪切破坏,使得其最终破坏形态为弯曲破坏,从而改善其抗震性能;配置栓钉能提高柱的抗震性能,且当柱的变形能力较强时效果更明显;试验轴压比为0.38或0.45的试件仍具有较强的耗能能力和变形能力,即型钢超高强混凝土柱具有较好的抗震性能。     

方钢管混凝土暗柱内嵌钢板-混凝土组合剪力墙抗震性能试验研究

以某超高层建筑核心筒剪力墙结构为原型,对两端为方钢管混凝土暗柱的内嵌钢板 高强混凝土组合剪力墙进行了拟静力试验研究。试验设计了3个剪跨比为2.0、设计轴压比为0.5的1∶7模型试件,主要变化参数为混凝土强度等级和含钢率。试验结果表明：试件的破坏形态主要为暗柱钢板竖向焊缝开裂、暗柱内混凝土压溃和底部外包钢板局部屈曲,墙中部混凝土的弯剪斜裂缝发展不明显;3个试件的滞回曲线都较为饱满,具有较高的耗能能力,承载力极限状态时的等效黏滞阻尼系数约为0.22;3个试件的屈服位移角平均值为1/214,极限位移角平均值为1/58,延性系数平均值为3.77;在整个加载过程中,弯曲变形和剪切变形对顶点位移的贡献比例基本保持不变,由剪切变形产生的顶点位移约占总顶点位移的20%。     

压弯剪扭复合受力下空腹式槽钢混凝土L形截面柱抗震性能试验研究

为研究槽钢混凝土L形截面柱的抗震性能,对6个L形截面柱开展了压弯剪扭复合受力下的拟静力试验。通过试验观察L形柱的破坏特征,得到其荷载-位移、扭矩-扭转角滞回曲线以及主要试验阶段的特征点参数。基于实测数据,重点分析扭弯比和肢高肢厚比对L形柱的滞回曲线、刚度退化以及延性系数等受力性能的影响。结果表明：L形柱的破坏模式可根据扭弯比的大小分为弯曲破坏、弯剪破坏、弯扭破坏以及扭剪破坏。荷载-位移滞回曲线呈较饱满的弓形,扭矩-扭转角滞回曲线出现“荷载跌落”现象。扭矩的存在使得构件的损伤更严重,耗能更大。当扭弯比为0.89、肢高肢厚比为3.0时,L形柱的延性较好,其延性系数满足规范要求;当扭弯比为0.25、肢高肢厚比为2.5时,L形柱具有较好的抗倒塌能力,其层间位移角满足规范要求。     

内置钢板与内置钢桁架混凝土组合剪力墙抗震性能对比研究

通过对2组内置钢板混凝土组合剪力墙和内置钢桁架混凝土组合剪力墙拟静力试验的模拟,确定计算模型的建立方法,并选取2片相同含钢率的内置钢板混凝土组合剪力墙和内置钢桁架混凝土组合剪力墙模型进行侧向低周反复荷载作用下的计算分析,对比了2片剪力墙模型的承载力、刚度及其退化过程、延性、耗能及滞回特性,并选取实际工程为算例,对采用两种组合剪力墙的整体结构从抗侧刚度、破坏模式、层间位移角、位移时程及塑性发展等方面进行了抗震性能的对比。研究结果表明：对于构件层次,随着墙体高宽比的增大,内置钢板混凝土组合剪力墙的承载力、耗能能力及延性逐渐优于内置钢桁架混凝土组合剪力墙;对于结构层次,当墙体高宽比较大时,采用内置钢板混凝土组合剪力墙结构的抗震性能要优于采用内置钢桁架混凝土组合剪力墙的结构。     

钢管混凝土边框钢纤维混凝土剪力墙受剪承载力计算

通过5个钢管混凝土边框钢纤维混凝土剪力墙和1个钢管混凝土边框混凝土剪力墙的低周反复加载试验,研究钢管混凝土边框钢纤维混凝土剪力墙的受力机理及破坏模式,分析钢纤维体积率和混凝土强度对其抗震性能的影响。结果表明：钢管混凝土边框钢纤维混凝土剪力墙的破坏模式为剪切破坏;墙体裂缝主要为典型的斜裂缝,钢纤维可有效限制剪力墙裂缝宽度,改善裂缝形态;随着钢纤维体积率的增大,剪力墙受剪承载力、延性和耗能能力明显提高;其他影响因素相同的条件下,钢纤维体积率为0.5%、1.0%和1.5%的剪力墙受剪承载力较未掺钢纤维剪力墙的分别提高了4.4%、12.7%和18.6%;随着混凝土强度的提高,剪力墙受剪承载力和耗能能力明显提高,但延性降低;其他影响因素相同的条件下,钢纤维混凝土强度等级为CF60、CF80剪力墙的受剪承载力较CF40剪力墙的分别提高了24%和37%。结合对文中及国内外相关文献试验数据的综合分析,提出了考虑钢纤维体积率和混凝土强度等影响的钢管混凝土边框钢纤维混凝土剪力墙受剪承载力计算方法,与试验结果吻合较好。