空心玻璃微球改性酚醛树脂的研究

研究了空心玻璃微球对酚醛树脂(PF)的影响,通过光学显微镜和红外光谱证实了空心玻璃微球的存在.加入质量分数为5%的空心玻璃微球时,PF的硬度和热稳定性均得到提高,在空心玻璃微球小于等于15 μm时高于纯PF.固定空心玻璃微球为15 μm,PF的硬度和热稳定性随着玻璃微球含量的增加先迅速后缓慢提高;冲击强度则随含量的增加先增加后降低,在质量分数5%时达到最大值.     

铋掺杂铝硅酸盐玻璃的超宽带近红外发光性质

采用高温熔融法制备了组分为50SiO_2-xAl_2O_3-(50-x)MgO-Bi_2O_3(x=5,10,15,20,摩尔比)的铋掺杂铝硅酸盐玻璃。研究了铋掺杂铝硅酸盐玻璃超宽带近红外发光性质,探讨了玻璃基质的光学碱度对铋离子宽带发光特性的影响。结果表明:在690nm和808nm的激发下,铋掺杂铝硅酸盐玻璃的红外荧光中心分别位于1106nm和1294nm;随光学碱度的增强,铋离子的红外发光强度减弱。并对铋离子超宽带发光的机理进行了探讨,认为其红外发光源于低价的Bi~+和Bi~(2+)。     

GexAs20Se80-x玻璃的化学组成对结构和物理性质的影响

本文制备了一系列Ge_xAs₂₀Se_80-x硫系玻璃,旨在了解化学组成和平均配位数对其结构和物理性质的影响。采用棱镜耦合法测量玻璃的折射率,采用分光光度法测量玻璃透射率并根据透射谱得到玻璃的光学带隙。研究发现,当玻璃组成满足完全化学计量配比之前,随着Ge含量的增加,玻璃的折射率随之减小,而光学带隙随之增大。通过测量拉曼光谱并对其进行分解,发现随着玻璃化学组成的改变,其结构中异极键相对数量的变化是合理的;而同极键的数量则与光学带隙和折射率的变化密切相关,主要是由于同极键形成的带尾可以降低玻璃的光学带隙。另一方面,玻璃的各个结构单元及物理性质在满足完全化学计量配比的玻璃组成上出现转变行为,由此可以断定,Ge_xAs₂₀Se_80-x硫系玻璃的化学组成主导着其结构和物理性质。     

Er掺杂氟碲酸盐玻璃的制备和上转换发光性能的研究

结合氟化物玻璃和碲酸盐玻璃的各自优势,在空气气氛下通过熔融法制得了光学性能良好的氟碲酸盐玻璃,该体系玻璃具有较低的声子能量,Er掺杂和Er/Yb共掺氟碲酸盐玻璃在980 nm激光的激发下可实现上转换发光,能观察到明显的绿光和红光。对稀土掺杂玻璃进行吸收光谱的分析,并利用J-O理论计算了振子强度参数和光谱品质因数,有较好的发光能力。通过分析可见光光谱,结合Er的能级结构,得出了实现可见光发光的能量传递过程,并利用速率方程证明该过程是线性衰变和上转换的共同作用。     

高折射率玻璃微球表面改性研究

本文介绍了反光标志膜用高折射率（nD）玻璃微球的表面清洗及钛酸醋偶联剂改性工艺流程和溶液配方。经此处理的高nD玻璃微球与反光膜用树脂层表现出良好的亲合性，已在反光膜的研制中得到成功的应用。     

制作球对称梯度折射率微球透镜精确控制折射率剖面形成的方法

分析了球对称梯度折射率（ＧＲＩＮ）球形光学器件的优越性，指出了该类透镜要求经制作所形成的折射率分布更严格地符合理论分布，传统的离子交换技术已不能满足这种技术要求。建议将“使用不同浓度混合熔盐进行多阶段离子交换”的方法应用于制备这类微球透镜，并在球坐标下导出了ＧＲＩＮ分布的级数解。以Ｍａｘｗｅｌｌ鱼眼微球透镜为例进行的数值计算，获得了最佳工艺条件和相应的ＧＲＩＮ分布。结果表明，应用这种离子交换新技术     

基于多孔玻璃的发光材料研究进展

多孔玻璃在过去的几十年中被广泛应用于提纯过滤,生物化学和离子选择等领域,是一种多功能微结构材料.多孔玻璃所制备的材料在光学领域也展现出不俗的优势,成为突破多种光学材料应用瓶颈的关键.对多孔玻璃在可见光和近红外波段的研究进行了综述,介绍了各种稀土离子和金属离子在多孔玻璃中的发光特性,展现了多孔玻璃在制备微晶发光玻璃和封装...     

空心玻璃微球填充改性PVC的研究

采用共混法合成了空心玻璃微球／聚氯乙烯（PVC）复合材料,空心玻璃微球使用前先用硅烷偶联剂KH-550进行了表面改性。通过高倍光学显微镜、红外分析仪、电子拉力机、邵氏硬度检测仪等手段研究了空心玻璃微球的含量对PVC抗拉强度,冲击强度和硬度等性能影响。结果表明：随着玻璃微球含量的逐渐增加,PVC复合材料的拉伸强度先增加后...     

氧化玻璃中Eu^3＋离子的发光研究

应用荧光光谱、红外振动光谱和差热分析等研究了Ｅｕ＾３＋离子在不同氧化物玻璃基质中的发光行为。结果表明：不同氧化物玻璃基质对Ｅｕ＾３＋离子的激发谱和发光谱的峰化影响很小，发光强度按硅酸盐、硼酸盐、钡磷酸盐、铝磷酸盐玻璃顺序递增。玻璃中Ｅｕ＾３＋激活离子与最邻近配位体之间共价键因素引起的近距离作用对无辐射跃迁过程影响比多声子驰豫更强烈，讨论了氧化物玻璃配位体对Ｅｕ＾３＋离子的极化作用与发光强度的关系。     

玻璃非线性光学材料研究进展

全光学装置的成功的关键是材料的选择与开发。此类材料必须具备足够高的非线性折射率和亚皮秒级的响应时间。在这方面光学玻璃具有较大的优质和潜力。对不同玻璃系统进行的旨在提高玻璃非线性光学折射率的研究结果表明，材料的非线性折射率ｎ２大致随其线性折射率ｎ０的增加而提高，通常认为，低折射率玻璃的非线性化学光学效应主要受限离子极化的影响，而网络形成和调整阳离子的作用可忽略不计。     

SiO2-Bi2O3-ZnO无铅玻璃油墨的制备

制备了软化温度在575℃左右的玻璃油墨用SiO2-Bi2 O3-ZnO系无铅玻璃粉,用纽扣实验比较了不同成分玻璃粉的成型流动性,以成玻性能最佳的玻璃粉为原料制备了不同玻璃粉含量的油墨并研究了玻璃粉含量对玻璃油墨成膜性能的影响,最后,用筛选的无铅玻璃油墨按照企业生产工艺制备了汽车后挡玻璃的黑色遮盖层,并与国外品牌荷兰庄信万丰公司的玻璃油墨进行了应用对比.采用差热分析(DTA)、X射线衍射仪(XRD)、扫描电镜(SEM)和热膨胀仪对玻璃粉和玻璃油墨涂层的组织性能进行了表征.试验结果表明,SiO2-Bi2 O3-ZnO系玻璃粉成玻性能良好;当玻璃粉含量为60%时,在680℃、保温1.5 min条件下制备了汽车后挡玻璃油墨涂层,适合目前汽车后挡玻璃生产线的工艺要求,油墨形成的玻璃薄膜具有良好的光泽度、耐酸性和抗粘性.     

BaF2/BaO替代对钡镓锗酸盐玻璃结构的影响

用Raman光谱技术研究了Ga2O3/GaF3GeO2二元玻璃的结构,并用XRD技术和Raman光谱技术研究了BaF2/BaOGa2O3GeO2系统玻璃的结构。讨论了BaF2替代BaO对玻璃结构的影响。结果表明:摩尔组成为20BaO15Ga2O365GeO2玻璃的主要亚稳相是BaGa2·Ge2O8,而以BaF2替代玻璃中的全部BaO后,玻璃的主要亚稳相转变为BaGe2O5。玻璃中引入氟化物后,其中频段强Raman散射峰宽化,主峰值向高频方向移动,表明在玻璃中形成一些较大的四面体环。同时玻璃高频段最强的振动峰同样移向高频,高频带低频侧的肩明显减弱。这些变化可解释为玻璃中Q2振动模的减少和Ga,Ge四面体的对称性降低,使Raman光谱中的高频成分增加。     

氧化镧对钒磷二元玻璃结构的影响

采用红外吸收光谱、Raman光谱和51V静态固体核磁共振研究了La2O3对钒磷二元玻璃结构变化的影响.结果表明:钒作为主要的玻璃形成体构成基本网络,磷以孤立的磷氧四面体分散存在于钒为主体的玻璃网络中.磷氧四面体只与钒连接作用,钒在玻璃中主要以(VO3)n单链、(V2O8n锯齿状链、VO4分枝和V2O4-7基团等形式存在,其中前两种基团占支配地位,对玻璃的性质起决定性影响,La2O3的引入破坏了网络平衡中间态的结构,(V2O8)n锯齿状链结构逐渐转化为(VO3)n单链,使玻璃的结构更加疏松.     

Cation Effects on Anion Distributions in Aluminophosphate Glasses

Alkali aluminophosphate glasses, including those in the system x Al₂O₃·(1− x )CsPO₃ (0 ≤ x ≤ 0.25), were examined by high-performance liquid chromatography (HPLC), infrared (IR), and ²⁷Al magic angle spinning nuclear magnetic resonance (MAS NMR) spectroscopies. Phosphate anions become progressively shorter with the addition of alumina to a metaphosphate glass. Al³⁺ ions are initially incorporated into the structure in octahedral sites, but the average Al coordination number (CN) decreases with increasing alumina content and tetrahedral species are the preferred moiety when [O]/[P] > 3.5. Al[4] sites appear to be associated with monophosphate (Q⁰) anions. The role of modifier size on aluminophosphate structure is investigated. At low alumina content (<15 mol%), the disproportionation of pyrophosphate anions into triphosphate and orthophosphate anions is responsible for the lower average Al CN of cesium aluminophosphate glasses compared with sodium aluminophosphate glasses.     

Effects of lignin as a filler on properties of soy protein plastics. I. Lignosulfonate

A series of biodegradable plastics from soy protein isolate (SPI) and lignosulfonate (LS) with a weight ratio of 0:10 to 6:4 were prepared with 40 wt % glycerol as a plasticizer by compression molding. Their properties were investigated by wide‐angle X‐ray diffraction (WAXD), differential scanning calorimetry (DSC), dynamical mechanical thermal analysis (DMTA), scanning electron microscopy (SEM), and tensile tests. The results indicated that the introduction of a moderate LS content from 30 to 40 parts in the blends could simultaneously enhance the tensile strength, elongation, and Young's modulus of soy protein plastics alone. Studies of the water sensitivity of the materials suggested that the strong interaction between LS and SPI could restrict the effect of water on the swelling and the damage of the materials, resulting in lower water absorption. The improvement of the properties was attributed mainly to the existence of the beneficial microphase separation and the formation of crosslinked structures because of the introduction of LS into soy protein plastics. Therefore, a model of a crosslinked network formed from SPI molecules with an LS center was established based on the existence of strong physical interactions between LS and SPI. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 88: 3284–3290, 2003     

CaO-Al2O3-SiO2系统玻璃颗粒的烧结过程研究

通过大量实验得到了CaO-Al2O3-SiO2系统玻璃颗粒的起始烧结温度(Ts),起始析晶温度(Tc)以及烧结收缩曲线,通过对他们的分析,讨论了组分、烧结温度、烧结时间对玻璃颗粒烧结的影响.确定了有利于烧结的较佳CaO,Al2O3,B2O3含量范围,从而为烧结法生产微晶玻璃提供了有利的理论依据.     

瓶罐玻璃生产关键工艺性能测量方法与应用

综述了瓶罐玻璃生产制备过程中的关键工艺性能的测量表征方法和适用的仪器设备。涉及的关键工艺性能主要包括熔解特性、熔体特性和温黏特性等。熔解特性的分析包括原料成分分析、粒度分析、熔化均匀性分析、澄清分析等;熔体特性的测量包括表面张力测量、高温电阻率测量、羟基含量测量等;温黏特性测量主要包括高温黏度(熔融温度T_m、工作点T_w、液相线T_L)测量、中温黏度(软化点T_s)测量、低温黏度(膨胀软化点T_d、退火点T_a、转变点T_g和应变点T_st等)测量。上述工艺性能精确测量和表征,对制备高质量瓶罐玻璃制品具有重要意义。     

硅烷自组装单分子层生长条件的优化

对长碳链硅烷在玻璃片表面自组装形成单分子层膜进行研究。以甲苯为溶剂,使辛烷基三乙氧基硅烷(OTES)、十二烷基三甲氧基硅烷(DTMS)、3-胺丙基三乙氧基硅烷(APTES)和十八烷基三氯硅烷(OTS)在玻璃表面进行生长,考察反应时间、反应浓度和可水解基团对自组装单分子层膜的影响。用接触角仪和全反射红外光谱仪(FT-IR)对单分子膜进行表征。结果表明:带有—Cl水解基团的OTS最易生长,而带有乙氧基离去基团的OTES比带有甲氧基的DTMS容易反应。在24℃时,1 mmol/L OTES反应20 min自组装单分子层膜生长很好,并且表面比较规整均一。     

Independent Effects of Nitrogen Substitution for Oxygen and Yttrium Substitution for Magnesium on the Properties of Mg-Y-Si-Al-O-N Glasses

Glasses of composition (in equivalent percent) (28 − x )Mg: x Y:56Si:16Al:(100 − y )O: y N, with x = 0, 14, or 28 for y = 0 and 15 and with x = 0, 7, 14, 21, or 28 for y = 10, were prepared by melting and casting. For glasses where the nitrogen content was varied for a constant cationic ratio, the glass molar volume (MV), compactness ( C ), Young's modulus ( E ), glass-transition temperature ( T _g), and dilatometric-softening temperature ( T _ds) varied linearly as the nitrogen content increased, with MV decreasing and the other properties increasing. From the incremental changes in these properties with nitrogen content, for glasses with x = 0, 14, and 28, good linear fits ( R ² > 0.99) were obtained, and best-fit slopes are reported here. The property changes and their linearity were consistent with the increased cross-linking of the glass network by tricoordinated nitrogen. The replacement of magnesium by yttrium led to a nonlinear decrease in glass compactness and to nonlinear increases in MV, T _g, and T _ds. However, linear correlations were found for MV and ionic volume and for T _g, T _ds, and the coordination of (Si,Al)(O,N) tetrahedra of the glass structural units to the modifier cations not involved in charge compensating aluminum ions in fourfold coordination. The replacement of magnesium by yttrium had little effect on Young's modulus, and this result was related to similar changes in the compactness, C . The present results showed that the effects of substituting nitrogen for oxygen and yttrium for magnesium are independent and additive; thus, no synergistic effects of anion and cation substitutions were observed.     

PP-g-MAH预浸渍玻璃纤维毡对GMT界面改性的作用

采用含有马来酸酐接枝聚丙烯(PP–g–MAH,简称MPP)的聚丙烯(PP)树脂对玻璃纤维(GF)毡预浸渍,进行增强体改性,通过直接浸渍工艺、增强体预浸渍工艺、累加浸渍工艺等不同工艺制备GF毡增强PP热塑性复合材料(GMT)。对不同工艺制备的GMT界面形态进行了扫描电子显微镜分析,并测定了预浸渍处理后GF的疏水性,研究了预浸渍工艺中MPP的用量对GMT拉伸、弯曲、冲击等力学性能的影响。结果表明:采用含MPP的PP树脂进行增强体预浸渍改性的方法,改性树脂对GF的包覆效果良好,经预浸渍改性法处理的GF,其疏水性增强;并可以获得与PP/MPP改性树脂直接浸渍GF毡时相似的界面改性效果和相近的GMT力学性能;样品界面改性效果相近的情况下,增强体预浸渍改性方法所需的MPP用量明显少于改性树脂直接浸渍时的用量。