Ag-CuO钎料空气反应钎焊AlN陶瓷接头组织及性能

采用Ag-Cu O钎料实现了Al N陶瓷与自身的空气反应钎焊。研究了Cu O含量、钎焊温度和预氧化温度对界面组织及力学性能的影响规律,分析了连接机理。当钎料成分为Ag-6 mol%Cu O,在1000℃/5 min的钎焊参数下,Al N/Ag-Cu O/Al N接头可获得最高的抗剪切强度为13.9 MPa。采用SEM、EDS及XRD对其接头界面显微组织、断口形貌及成分进行了分析。典型接头界面组织结构为Al N/Cu Al_2O_4/Cu O/Al N+Ag+Cu O/Cu O/Cu Al_2O_4/Al N。然而,在该条件下无法获得无缺陷的接头。为了降低残余热应力获得无缺陷的接头,对Al N陶瓷采用预氧化处理,在Al N陶瓷表面形成一层Al_2O_3层。当预氧化参数为1 000℃/5 h时,Al N陶瓷表面的Al_2O_3层厚度约为10μm。采用成分为Ag-6 mol%Cu O的钎料,在1 000℃/5min的钎焊参数下,对预氧化后的Al N陶瓷进行连接,获得了无缺陷的接头,接头典型界面显微组织为Al N/Al_2O_3/Cu Al_2O_4/Cu O/Ag+Al_2O_3/Cu O/Cu Al_2O_4/Al_2O_3/Al N。接头的抗剪切强度最高为22.6 MPa,与未氧化的Al N陶瓷接头相比提升了62.6%。接头进行抗剪切测试时,断面主要出现在Al N陶瓷母材。     

直接敷铜工艺制备Cu/AlN材料的界面结构及结合性能

通过直接敷铜(DBC)工艺,在AlN陶瓷基板表面于1 000~1 060℃的敷接温度下制备Cu/AlN材料,利用机械剥离机、场发射扫描电子显微镜和X射线衍射仪分析了Cu/AlN的界面结合强度、界面微观形貌和物相组成。结果表明:铜箔和AlN陶瓷基板间的结合强度超过了8.00N·mm~(-1),铜箔和AlN陶瓷之间存在厚度约为2μm的过渡层,过渡层中主要含有Al_2O_3、CuAlO_2和Cu_2O化合物;随着敷接温度升高,Cu/AlN的界面结合强度逐渐增大。     

ZrB_2-YAG-Al_2O_3复相陶瓷的抗氧化性能

通过共沉淀法获得包覆式Al_2O_3-Y_2O_3/ZrB_2复合粉体,对其进行放电等离子烧结制备相应的复相陶瓷,并对不同YAG(钇铝石榴石)、Al_2O_3含量的复相陶瓷进行了氧化试验,用SEM、XRD和电子探针等研究了YAG、Al_2O_3对ZrB_2陶瓷抗氧化性的影响。结果表明:制备的各种复相陶瓷和纯ZrB_2陶瓷相比,在相同氧化条件下表面的氧化层厚度都有所变薄,YAG、Al_2O_3的加入可以改善ZrB_2陶瓷的抗氧化性能;在相同氧化条件下,Al_2O_3含量越多,氧化层厚度越小;在高温条件下,复相陶瓷氧化层中均存在ZrO_2、B_2O_3和Al_(18)B_4O_(33)相,Al_2O_3含量越多,Al_(18)B_4O_(33)相也越多。     

CuO辅助Ag_(72)Cu_(28)共晶钎料在大气环境中实现Al_2O_3陶瓷钎焊的界面反应

采用CuO辅助Ag_(72)Cu_(28)共晶钎料的方法,在大气环境中实现了Al_2O_3陶瓷的钎焊,研究了钎焊接头的剪切强度、微观形貌以及界面反应产物和界面反应机理。结果表明:该方法可以得到结合良好的Al_2O_3陶瓷接头;在钎焊温度为1 050℃、保温时间为10min、CuO质量分数为10%的条件下进行钎焊时,接头的剪切强度最高,为39.04 MPa;在钎焊过程中,由于陶瓷表面CuO的存在使熔融铜向陶瓷表面富集并发生反应,从而实现钎料的润湿和铺展;在钎焊接头中可见清晰的界面过渡层,界面反应产物主要为CuAl_2O_4及CuAlO_2相。     

大气等离子喷涂Ni5Al/Al2O3-3％TiO2复合结构 涂层的显微组织与力学性能

采用大气等离子喷涂(APS)技术在6061铝合金基体表面预制Ni5Al合金黏结层,再在黏结层上喷涂Al_2O_3-3%TiO_2陶瓷层,研究了涂层的物相组成、微观形貌、显微硬度、结合强度、耐磨性能和耐腐蚀性能,分析了其拉伸断裂机理。结果表明:陶瓷层的物相主要由α-Al_2O_3、γ-Al_2O_3和锐钛矿型TiO_2组成;黏结层与基体以及黏结层与陶瓷层均形成了机械结合,但黏结层与基体的结合界面更致密;与基体相比,涂层的显微硬度更高、耐腐蚀性能和耐磨性能更优;涂层的结合强度低于黏结层的,其拉伸断裂位置多在黏结层和陶瓷层之间的界面处以及陶瓷层内部,界面处的拉伸断裂形式为混合断裂,黏结层上的为韧性断口,陶瓷层上的为脆性断口。     

陶瓷涂层刀具切削灰铸铁的试验研究

为了探究陶瓷涂层刀具涂层材质、基体材质对切削性能的影响,试验采用四种陶瓷涂层刀具连续干切削灰铸铁,测试了切削力和切削温度的变化情况以及后刀面的磨损量和已加工表面的粗糙度。结果表明,在刀具基体同为Si_3N_4的条件下,涂层材质为Ti N/Al_2O_3/Ti C的刀具比Ti N/Al_2O_3的切削性能好;在涂层材质同为Ti N的条件下,刀具基体Al_2O_3/Ti CN比Al_2O_3/Ti C的切削性能好。研究发现:四种陶瓷涂层刀具前刀面磨损形式均为微崩刃和月牙洼,后刀面磨损形式均为磨粒磨损和粘着磨损,涂层的磨损形式均为剥落和扩散磨损。     

特高温Al2O3陶瓷—金属化共烧结技术

本文介绍了我所研制的特高温92％Al_2O_3陶瓷—金属化共烧结技术,详细讨论了92％Al_2O_3的组成特性、金属化配方设计和92％Al_2O_3陶瓷—金属化共烧结工艺,分析了陶瓷金属化烧结机理,建立了物理模型,并成功地应用了陶瓷管壳的研制。     

6061/A356异种铝合金脉冲MIG搭接焊*

利用直流脉冲MIG焊接技术,进行6061变形铝合金与A356铸造铝合金板材的搭接焊接,并分析接头的力学性能、微观组织及元素分布。拉伸试验结果表明,当A356铸造铝合金板在上,6061变形铝合金板在下,焊枪行走速度为10 mm/s时,搭接接头抗拉强度最高,为95 MPa。接头拉伸试样的断裂位置都位于焊缝区,断裂形式主要为混合型断裂。微观组织及元素分析结果表明,在A356铝合金一侧的部分熔融区内发生Fe和Mg元素偏聚,形成了片状Al-Fe-Si相和颗粒状Al-Fe-Mg-Si相,这两种富Fe相会削弱接头性能。在6061铝合金一侧的部分熔融区内产生了晶界液化,形成了Al-Mg-Si-Cu相+Al固溶体贫化区的液化组织,且该相周围有Fe元素偏聚。三角区是接头中最薄弱的位置,接头拉伸试样均起裂于此并最终断裂于焊缝。     

热处理对铝合金化学镀镍-钨-磷镀层组织性能的影响

通过扫描电子显微镜、能谱微区成分分析、透射电镜等手段研究了热处理对6061铝合金化学镀镍-钨-磷合金镀层组织性能的影响.结果表明:在试验热处理条件下,镍-钨-磷镀层和基体问扩散主要是镍原子向铝基体中的扩散;铝合金化学镀镍-钨-磷试样525℃热处理1 h后,由于镍原子的扩散,基体和镀层之间形成镍铝合金层,镍铝合金层分为二层,第一层镍铝合金层主要含有Ni2Al3相,第二层镍铝合金层主要含有NiAl3相;在干摩擦滑动条件下,铝合金化学镀试样经525℃热处理1h后表现出良好的耐磨性.     

加食盐重熔铝切屑经验

由于铝是很活泼的元素,铝合金工件在切削过程中产生的切屑表面有一层致密、坚韧的Al_2O_3薄膜,这种熔点高达2100℃的Al_2O_3坚韧薄膜能牢牢裹住切屑中的铝合金,使重熔铝合金切屑时无法穿透该薄膜而分离出来,常常做为熔渣被扒掉,致使铝合金切屑重熔回收率很低,因Al_2O_3熔渣很稠,与铝液不能彻底分离,从而使回收铝合金质量很差,呈暗灰色。     

叶切面最大厚度数值计算与应用

以叶切面最大厚度的数值计算方法为基础,探讨叶切面最大厚度计算的计算机实现,介绍叶切面厚度数值计算法的应用实例.     

Natural frequencies of vibration of a class of solids composed of layers of isotropic materials

In a recent paper, the Ritz method with simple algebraic polynomials as trial functions was used to obtain an eigenvalue equation for the free vibration of a class of homogeneous solids with cavities. The method presented is here extended to the study of a class of non-homogeneous solids, in which each solid is composed of a number of isotropic layers with different material properties. The Cartesian coordinate system is used to describe the geometry of the solid which is modelled by means of a segment bounded by the yz, zx and xy orthogonal coordinate planes and by two curved surfaces which are defined by fairly general polynomial expressions in the coordinates x, y and z. The surface representing the interface between two material layers in the solid is also described by a polynomial expression in the coordinates x, y and z. In order to demonstrate the accuracy of the approach, natural frequencies are given for both a two- and three-layered spherical shell and for a homogeneous hollow cylinder, as computed using the present approach, and are compared with those obtained using an exact solution. Results are then given for a number of two- and three-layered cylinders and, to demonstrate the versatility of the approach, natural frequencies are given for a five-layered cantilevered beam with a central circular hole as well as for a number of composite solids of more general shape.     

盘丝极心偏对三爪自定心卡盘找标精度影响的分析

三爪自定心卡盘作为机床的主要附件,已有一百多年的发展历史,尽管目前随着数控技术的不断发展,越来越多地需求高速动力卡盘,但三爪自定心卡盘目前仍有一定的市场。 要保证卡盘可靠地夹紧工件,必须使其有可靠的夹持精度;要保持卡盘的精度,必须要严格控制各零部件公差及误差,如盘丝的极心偏。 　　极心偏是形成圆的渐开线的基圆圆心 (极心 )与盘丝内孔中心不同心所造成的偏差值。它对卡盘精度的影响分两种情况,一是卡爪夹持弧采用配磨,二是卡爪夹持弧采用单磨。本文主要探讨配磨时的影响。 　　卡爪夹持弧采用配磨,即每台卡盘整体…     

双丝杠驱动机构同步分析

介绍了双丝杠驱动机构工作原理,论述了双丝杠运动产生不同步的原因以及如何判定与解决同步问题。     

圆柱面素线的直线度公差带解析

详细分析了圆柱面素线的直线度公差带在新旧标准中定义和解释的区别，并从对圆柱面素线实际要素检测的角度，提出了推行新标准的实际意义。     

膨胀套导向机构的设计

通过分析膨胀套在实际使用产生滑移受阻现象、卡死现象原因的实质,并在分析产生问题原因的基础上提出了改进措施即：增加导向机构。     

广州地铁APM列车制动机理分析

根据广州市珠江新城旅客自动运输系统(APM)列车的运行特点,介绍APM列车制动系统的制动方式及其特点,分析APM列车动态制动和摩擦制动的工作机理及其区别和联系,阐明APM列车制动系统的电控制过程和气控制过程,从而为APM列车制动系统的维护和管理提供一定的依据.     

磨粉机快辊轴承座加工工艺设计

设计了磨粉机快辊轴承座的加工工艺和具体的工装夹具.利用卧式加工中心加工磨粉机快辊轴承座,辅以能够高效快速夹紧的夹具,既可以保证加工精度,又能够提高加工效率.     

活塞销孔加工工艺的改进

我公司于８０年代末引进Aspera公司年产８０万台冰箱（冷柜）压缩机生产线及软件技术，在压缩机加工中，活塞销孔（如图１所示）的加工是难点之一。用镗床加工，质量一直难以达到要求，废品率很高。后来我们将Aspera公司的加工工艺即精镗后滚光改为精镗后用金刚石铰刀粗、精铰孔，由此解决了这个技术难题。（１）原意大利Aspera公司工艺简述其工艺流程为：钻６．５通孔→扩孔至７＋０．１→粗镗７．４７３＋０．０３６、圆柱度０．０１→精镗至７．９３５＋０．００６、圆柱度０．００２→滚光７．９３８＋０．００６、圆柱度０…     

Development of sclerometric method of studying activation of parameters of damage and fracture of friction deformable surfaces

The article presents a brief review of the wear models based on the kinetic thermofluctuation approach. The materials were developed using SamGTU sclerometric programming software and a set of instruments developed at Samara Engineering University for assessing the parameters of kinetic thermoactivation for surface fracture deformed by friction. The first obtained results of assessments and the estimated prediction of wear resistance exemplified by tribocouple of the aircraft chassis are presented.