Plastic flow and microstructural evolution in Ti–6Al–2Zr–1Mo–1V alloys during hot deformation

Abstract

The hot deformation behaviour and microstructural evolution in Ti–6Al–2Zr–1Mo–1V alloys have been studied using isothermal hot compression tests. The processing map was developed at a true strain of 0·7 in the temperature range 750–950°C and strain rate range 0·001–10 s^?1. The corresponding microstructures were characterised by means of a metallurgical microscope. Globularisation of lamellae occurring to a greater extent in the range 780–880°C and 0·001–0·01 s^?1 had a peak power dissipation efficiency of 58% at about 850°C and 0·001 s^?1. The specimens deformed in 750–880°C and 0·01–10 s^?1 showed an instability region of processing map, whereas the specimens deformed in 880–950°C and 1–10 s^?1 indicated three kinds of flow instabilities, i.e. macro shear cracks, prior beta boundary cracks and flow localisation bands.     

Dynamic recrystallisation during hot working of Zr–2·5Nb: characterisation using processing maps

Abstract

The characteristics of the hot deformation of Zr–2·5Nb (wt-%) in the temperature range 650–950°C and in the strain rate range 0·001–100 s^?1 have been studied using hot compression testing. Two different preform microstructures: equiaxed (α+β) and β transformed, have been investigated. For this study, the approach of processing maps has been adopted and their interpretation carried out using the dynamic materials model. The efficiency of power dissipation given by [2m/(m+1)], where m is the strain rate sensitivity, is plotted as a function of temperature and strain rate to obtain a processing map. A domain of dynamic recrystallisation has been identified in the maps of equiaxed (α+β) and β transformed preforms. In the case of equiaxed (α+β), the stress–strain curves are steady state and the dynamic recrystallisation domain in the map occurs with a peak efficiency of 45% at 850°C and 0·001 s^?1. On the other hand, the β transformed preform exhibits stress–strain curves with continuous flow softening. The corresponding processing map shows a domain of dynamic recrystallisation occurring by the shearing of α platelets followed by globularisation with a peak efficiency of 54% at 750°C and 0·001 s^?1. The characteristics of dynamic recrystallisation are analysed on the basis of a simple model which considers the rates of nucleation and growth of recrystallised grains. Calculations show that these two rates are nearly equal and that the nucleation of dynamic recrystallisation is essentially controlled by mechanical recovery involving the cross-slip of screw dislocations. Analysis of flow instabilities using a continuum criterion revealed that Zr–2·5Nb exhibits flow localisation at temperatures lower than 700°C and strain rates higher than 1 s^?1.

MST/3103     

Investigation on hot deformation of 20Cr–25Ni superaustenitic stainless steel with starting columnar dendritic microstructure based on kinetic analysis and processing map

Abstract

The deformation behaviour of a 20Cr–25Ni superaustenitic stainless steel (SASS) with initial microstructure of columnar dendrites was investigated using the hot compression method at temperatures of 1000–1200°C and strain rates of 0·01–10 s^?1. It was found that the flow stress was strongly dependent on the applied temperature and strain rate. The constitutive equation relating to the flow stress, temperature and stain rate was proposed for hot deformation of this material, and the apparent activation energy of deformation was calculated to be 516·7 kJ mol^?1. Based on the dynamic materials model and the Murty’s instability criterion, the variations of dissipation efficiency and instability factor with processing parameters were studied. The processing map, combined with the instability map and the dissipation map, was constructed to demonstrate the relationship between hot workability and microstructural evolution. The stability region for hot processing was inferred accurately from the map. The optimum hot working domains were identified in the respective ranges of the temperature and the strain rate of 1025–1120°C and 0·01–0·03 s^?1 or 1140–1200°C and 0·08–1 s^?1, where the material produced many more equiaxed recrystallised grains. Moreover, instability regimes that should be avoided in the actual working were also identified by the processing map. The corresponding instability was associated with localised flow, adiabatic shear band, microcracking and free surface cracks.     

Processing map for hot working of Ni–16Cr–8Fe alloy (IN 600)

Abstract

The hot deformation characteristics of IN 600 nickel alloy are studied using hot compression testing in the temperature range 850–1200°C and strain rate range 0·001–100 s^?l. A processing map for hot working is developed on the basis of the data obtained, using the principles of dynamic materials modelling. The map exhibits a single domain with a peak efficiency of power dissipation of 48% occurring at 1200°C and 0·2 s^?1, at which the material undergoes dynamic recrystallisation (DRX). These are the optimum conditions for hot working of IN 600. At strain rates higher than 1 s^?1, the material exhibits flow localisation and its microstructure consists of localised bands of fine recrystallised grains. The presence of iron in the Ni–Cr alloy narrows the DRX domain owing to a higher temperature required for carbide dissolution, which is essential for the occurrence of DRX. The efficiency of DRX in Ni–Cr is, however, enhanced by iron addition.

MST/1856     

High-temperature deformation behavior of Cu–6.0Ni–1.0Si–0.5Al–0.15?Mg–0.1Cr alloy

The hot compression deformation behavior of Cu–6.0Ni–1.0Si–0.5Al–0.15?Mg–0.1Cr alloy with high strength, high stress relaxation resistance and good electrical conductivity was investigated using a Gleeble1500 thermal–mechanical simulator at temperatures ranging from 700 to 900?°C and strain rates ranging from 0.001?to 1?s^?1. Working hardening, dynamic recovery and dynamic recrystallization play important roles to affect the plastic deformation behavior of the alloy. According to the stress–strain data, constitutive equation has been carried out and the hot compression deformation activation energy is 854.73?kJ/mol. Hot processing map was established on the basis of dynamic material model theories, and Prasad instability criterion indicates that the appropriate hot processing temperature range and strain rate range for hot deformation were 850~875?°C and 0.001~0.01?s^?1, which agreed well with the hot rolling experimentation results.     

Study on hot deformation behaviour of 316LN austenitic stainless steel based on hot processing map

Abstract

316LN is a type of austenitic stainless steel whose grain refinement only depends on hot deformation. The true stress–strain curves of 316LN were obtained by means of hot compression experiments conducted at a temperature range of 900–1200°C and at a strain rate range of 0·001–10 s^?1. The influence of deformation parameters on the microstructure of 316LN was analysed. Both the constitutive equation for 316LN and the model of grain size after dynamic recrystallisation were established, and the effect of different deformation conditions on the microstructure was analysed. The results show that the suitable working region is the one with a relatively higher deformation temperature and a lower strain rate, in which the dynamic recrystallisation is finely conducted. Moreover, the working region that should be avoided during hot deformation was indicated.     

Hot deformation behaviour of precipitation hardening stainless steel

Abstract

The behaviour of 17-4 precipitation hardening (PH) stainless steel was studied using the hot compression test at temperatures of 950–1150°C with strain rates of 0·001–10 s^?1. The stress–strain curves were plotted by considering the effect of friction. The work hardening rate versus stress curves were used to reveal whether or not dynamic recrystallisation (DRX) occurred. Using the constitutive equations, the activation energy of hot working for 17-4 PH stainless steel was determined as 337 kJ mol^?1. The effect of Zener–Hollomon parameter Z on the peak stress and strain was studied using the power law relation. The normalised critical stress and strain for initiation of DRX were found to be 0·89 and 0·47 respectively. Moreover, these behaviours were compared to other steels.     

Hot deformation behaviour and microstructure of a high-alloy gear steel

High strain isothermal compression tests at temperatures of 700–1200°C and strain rates of 0.1–50?s^?1 were performed in a Gleeble-3800 thermal simulator to investigate the hot deformation behaviour of a high-alloy Cr–Co–Mo–Ni gear steel, and the constitution equation and hot processing map were established based on these experiments. The results show that the flow stress can be described by the constitutive equation in hyperbolic sine function, and the optimum hot working regions are at the temperature of 1000–1100°C and strain rate of 0.3–1.0?s^?1. Optical microscopy observations of austenite grains indicate that dynamic recrystallisation occurs when the deformation temperature is over 900°C. The forging was successfully produced on the basis of the above-described researches.     

Hot deformation behavior and processing map of a Fe‐25Ni‐16Cr‐3Al alumina‐forming austenitic steel

The hot deformation behavior of a Fe‐25Ni‐16Cr‐3Al alumina‐forming austenitic steel was studied by hot compression using a Gleeble‐3500 thermal simulator. The compression tests were carried out in the temperatures range from 925 °C to 1175 °C and strain rates range from 0.01 s^‐1 to 10 s^‐1. It was concluded that the flow stress increased with decreasing deformation temperature and increasing strain rate. The constitutive equation was obtained and the activation energy was 420.98 kJ?mol^‐1 according to the testing data. According to the achieved processing map, the optimal processing domain is determined in the temperatures range of 1050 °C – 1075 °C and strain rates range of 0.03 s^‐1 ‐ 0.3 s^‐1. The evolution of microstructure characterization is consistent with the rules predicted by the processing map. During compression at the same temperature, the higher the strain rate is, the higher the hardness will be. The ultimate tensile strength of the steel is 779 MPa with a total elongation of 27.1 % at room temperature.     

Microstructure evolution of ZK40 magnesium alloy during high strain rate compression deformation at elevated temperatures

Abstract

Microstructure evolution of the homogenised ZK40 magnesium alloy was investigated during compression in the temperature range of 250–400°C and at the strain rate range of 0·01–50 s^?1. At a higher strain rate (?10 s^?1), dynamic recrystallisation developed extensively at grain boundaries and twins, resulting in a more homogeneous microstructure than the other conditions. The hot deformation characteristics of ZK40 exhibited an abnormal relationship with the strain rate, i.e., the hot workability increased with increasing the strain rate. However, the dynamic recrystallisation grain size was almost the same with increasing the temperature at the strain rate of 10 s^?1, while it increased obviously at the strain rates of 20 and 50 s^?1. Therefore, hot deformation at the strain rate of 10 s^?1 and temperature range of 250–400°C was desirable and feasible for the ZK40 alloy.     

Processing maps for Fe–24Ni–11Cr–3Ti–1Mo superalloy

Hot deformation characteristics of a Fe-base superalloy were studied at various temperatures from 1000–1200°C under strain rates from 0·001–1 s^− 1 using hot compression tests. Processing maps for hot working are developed on the basis of the variations of efficiency of power dissipation with temperature and strain rate and interpreted by a dynamic materials model. Hot deformation equation was given to characterize the dependence of peak stress on deformation temperature and strain rate. Hot deformation apparent activation energy of the Fe–24Ni–11Cr–1Mo–3Ti superalloy was determined to be about 499 kJ/mol. The processing maps obtained in a strain range of 0·1–0·7 were essentially similar, indicating that strain has no significant influence on it. The processing maps exhibited a clear domain with a maximum of about 40–48% at about 1150°C and 0·001 s^− 1.     

Characterisation of dynamic recrystallisation in nickel using processing map for hot deformation

Abstract

The hot deformation behaviour of polycrystalline nickel has been characterised in the temperature range 750–1200°C and strain rate range 0·0003–100 s^?1 using processing maps developed on the basis of the dynamic materials model. The efficiency of power dissipation, given by [2m/(m+1)], where m is the strain rate sensitivity, is plotted as a function of temperature and strain rate to obtain a processing map. A domain of dynamic recrystallisation has been identified, with a peak efficiency of 31% occurring at 925°C and 1 s^?1. The published results are in agreement with the predictions of the processing map. The variations of efficiency of power dissipation with temperature and strain rate in the dynamic recrystallisation domain are identical to the corresponding variations of hot ductility. The stress–strain curves exhibited a single peak in the dynamic recrystallisation domain, whereas multiple peaks and ‘drooping’ stress–strain curves were observed at lower and higher strain rates, respectively. The results are explained on the basis of a simple model which considers dynamic recrystallisation in terms of rates of interface formation (nucleation) and migration (growth). It is shown that dynamic recrystallisation in nickel is controlled by the rate of nucleation, which is slower than the rate of migration. The rate of nucleation itself depends on the process of thermal recovery by climb, which in turn depends on self-diffusion.

MST/1524     

Evaluation of low strain rate constitutive equation of 7075 aluminium alloy at high temperature

Abstract

The 7075 aluminium alloy is one of the most important engineering alloys utilised extensively in aircraft and transportation industries due to its high specific strength. In the present research, the flow behaviour of this alloy has been investigated using hot compression test at strain rates of 0·001, 0·01, 0·1 and 1 s^?1 and temperatures of 350, 400 and 450°C. The results reveal that dynamic softening occurred in these temperatures and strain rates. The activation energy, strain rate sensitivity and two constitutive equations (hyperbolic sine law and the power law) are derived from the results. It is shown that the hyperbolic sine law has a better agreement with the experimental results.     

The Hot Workability of SiCp/2024 Al Composite by Stir Casting

The hot workability of SiC_p/2024 Al composite was explored by conducting hot compression simulation experiments on Gleeble-3500 under temperatures of 300–500 °C and strain rates of 10^?3–1 s^?1. Constitutive equation was developed through hyperbolic sine function, and the activation energy was calculated to be 151 kJ mol^?1. The hot processing maps referring to dynamic material model were drawn in a true strain range from ?0.2 to ?0.8. At the strain of ?0.8, the recommended regions in processing map contained two domains: superplastic domain (500 °C, 10^?3 s^?1) with an efficiency of about 0.72 and DRX domain (500°C, 1 s^?1) with an efficiency of about 0.45. Together with macrostructure and microstructure observations, it was suggested to remove the DRX region.     

Hot deformation mechanisms in metastable beta titanium alloy Ti–10V–2Fe–3Al

Abstract

The mechanisms of hot deformation in the β titanium alloy Ti–10V–2Fe–3Al have been characterised in the temperature range 650–850°C and strain rate range 0·001–100 s^-1 using constant true strain rate isothermal compression tests. The β transus for this alloy is ～790°C, below which the alloy has a fine grained duplex +β structure. At temperatures lower than the β transus and lower strain rates, the alloy exhibits steady state flow behaviour while at higher strain rates, either continuous flow softening or oscillations are observed at lower or higher temperatures, respectively. The processing maps reveal three different domains. First, in the temperature range 650–750°C and at strain rates lower than 0·01 s^-1, the material exhibits fine grained superplasticity marked by abnormal elongation, with a peak at ～700°C. Under conditions within this domain, the stress–strain curves are of the steady state type. The apparent activation energy estimated in the domain of fine grained superplasticity is ～225 kJ mol^-1, which suggests that dynamic recovery in the β phase is the mechanism by which the stress concentration at the triple junctions is accommodated. Second, at temperatures higher than 800°C and strain rates lower than ～0.1 s^-1, the alloy exhibits large grained superplasticity, with the highest elongation occurring at 850°C and 0.001 s^-1; the value of this is about one-half of that recorded at 700°C. The microstructure of the specimen deformed under conditions in this domain shows stable subgrain structures within large β grains. Third, at strain rates higher than 10 s^-1 and temperatures lower than 700°C, cracking occurs in the regions of adiabatic shear bands. Also, at strain rates above 3 s^-1 and temperatures above 700°C, the material exhibits flow localisation.     

High Temperature Deformation and Microstructural Features of TXA321 Magnesium Alloy: Correlations with Processing Map

The hot deformation of cast TXA321 alloy has been studied in the temperature range 300–500 °C and in the strain rate range 0.0003–10 s^?1 by developing a processing map. The map exhibited four domains in the temperature and strain rate ranges: (1) 300–325 °C and 0.0003–0.001 s^?1, (2) 325–430 °C and 0.001–0.04 s^?1, (3) 430–500 °C and 0.01–0.5 s^?1, and (4) 430–500 °C and 0.0003–0.002 s^?1. The first three domains represent dynamic recrystallization, resulting in finer grain sizes in the first two domains and coarser in the third domain. In the fourth domain, the alloy exhibited grain boundary sliding resulting in intercrystalline cracking in tension and is not useful for its hot working. Two regimes of flow instability were identified at higher strain rates, one at temperatures <380 °C and the other at >480 °C.     

Hot workability of 00Cr13Ni5Mo2 supermartensitic stainless steel

The hot workability of 00Cr13Ni5Mo2 supermartensitic stainless steel was investigated by hot compression and hot tension tests conducted over the temperature range of 950–1200 °C and strain rates varying between 0.1 and 50 s^?1. The processing map technique was applied on the basis of dynamic materials model and Prasad instability criterion. Microstructure evolutions, Zener–Hollomon parameter as well as hot tensile ductility were examined. The results show that, as for the hot working of 00Cr13Ni5Mo2 supermartensitic stainless steel in the industrial production, the large strain deformation should be carried out in the temperature range 1140–1200 °C and strain rate range 0.1–50 s^?1, where the corresponding Zener–Hollomon parameters exhibit low values. Moreover, when deformed under high strain rate range (above 15 s^?1), the deformation temperature can be reduced reasonably.     

Development of processing maps for a Ni-based superalloy

The hot deformation characteristics of a Ni-based superalloy were studied in the temperature range 1050–1180 °C and strain rate range 0.01–10 s^− 1 using hot compression tests. Processing maps for hot working were developed on the basis of the variations of efficiency of power dissipation with temperature and strain rate, interpreted using a dynamic materials model. A hot deformation equation is given to characterize the dependence of peak stress on the temperature and strain rate. A hot deformation apparent activation energy of the Ni-based superalloy is about 496 kJ/mol. The processing maps of the Ni-based superalloy obtained in a strain range of 0.1–0.7 are essentially similar, which indicates that strain does not have a significant influence. The maps exhibit a clear domain with its peak efficiency at about 1140 °C and 0.01 s^− 1; the domain has its peak efficiency of about 36–41% for different strains. On the basis of hot deformation microstructural observations, the full recrystallization region can be identified in the processing map at a strain of 0.7.     

Identification of processing parameters for Fe–15Cr–2.2Mo–15Ni–0.3Ti austenitic stainless steel using processing maps

Abstract

The processing parameters for hot working of Fe–15Cr–2.2Mo–15Ni–0.3Ti austenitic stainless steel (alloy D9) are identified using processing maps developed on the basis of the dynamic materials model and hot compression data in the temperature range 850–1250°C and strain rate range 0.001–100 s^-1. The efficiency of power dissipation increased with increase in temperature and decrease in strain rate. Dynamically recrystallised microstructures resulted when the efficiency of power dissipation was in the range 27–37%, i.e. in the temperature range 1050–1250°C and strain rate range 0.001–0.5 s^-1. Flow localisation occurred in the regions of instability at temperatures lower than 1000°C and at higher strain rates. The dynamic recrystallisation regime observed in this alloy is compared with other austenitic stainless steels, namely, AISI type 304L and 316L.     

Flow behavior and processing map for hot deformation of ATI425 titanium alloy

Flow behavior and processing map play important roles in the hot deformation process of titanium alloys. In this research, compression Gleeble tests have been carried out to investigate the stress–strain relationship at temperatures ranging from 700 to 1000℃ and strain rates ranging from 0.001 to 1 s~(-1) for ATI 425 titanium alloy. Arrhenius type constitutive equation was obtained to describe the compressive flow behavior with modification of additional deformation dead zone, friction model, temperature model and strain rate. The introduction of novel calculation method for value in Arrhenius equation gives more accurate fitting than traditional one. Processing maps were drawn based on the distribution of dissipator co-content, and optimized deformation temperature and strain rate range obtained. It is proven to be accurate and effective through the experimental results. The microstructure analysis shows that more dynamic recrystallization can be achieved in the area with larger value on the processing map.