Synthesis and Characterization of Microwave Absorbing SrFe<Subscript>12</Subscript>O<Subscript>19</Subscript>/ZnFe<Subscript>2</Subscript>O<Subscript>4</Subscript> Nanocomposite

Zinc ferrite and strontium hexaferrite; SrFe₁₂O₁₉/ZnFe₂O₄ (SrFe_11.6Zn_0.4O₁₉) nanoparticles having super paramagnetic nature were synthesized by simultaneous co-precipitation of iron, zinc and strontium chloride salts using 5 M sodium hydroxide solution. The resulting precursors were heat treated (HT) at 850, 950 and 1150°C for 4 h in nitrogen atmosphere. The hysteresis loops showed an increase in saturation magnetization from 1.040 to 58.938 emu/g with increasing HT temperatures. The ‘as-synthesized’ particles have size in the range of 20–25 nm with spherical and needle shapes. Further, these spherical and needle shaped nanoparticles tend to change their morphology to hexagonal plate shape with increase in HT temperatures. The effect of such a systematic morphological transformation of nanoparticles on dielectric (complex permittivity and permeability) and microwave absorption properties were estimated in X band (8.2–12.2 GHz). The maximum reflection loss of the composite reaches −26.51 dB (more than 99% power attenuation) at 10.636 GHz which suits its application in RADAR absorbing materials.     

Reaction kinetic,magnetic and microwave absorption studies of SrFe<Subscript>12</Subscript>O<Subscript>19</Subscript>/CoFe<Subscript>2</Subscript>O<Subscript>4</Subscript> ferrite nanocrystals

Mixture of cobalt ferrite and strontium hexaferrite nanocrystals i.e. SrFe₁₂O₁₉/CoFe₂O₄ exhibiting super paramagnetic nature were synthesized by modified flux method. The resulting precursors were heat treated (HT) at 900 and 1200°C for 4 h in nitrogen atmosphere. During heat treatment, transformation proceeds as instantaneous rate of nucleation and three dimensional growth with activation energy of 135.835 kJ/mole. The hysteresis loops showed a hike in saturation magnetization from 1.045 to 84.362 emu/g with an increase in HT temperature. The ‘as synthesized’ particles have size in the range of 10–20 nm with spherical shape. Further, these spherical shape particles tend to change their morphology to hexagonal plates with increase in HT temperatures. The relative complex permittivity and permeability of the composite powder are investigated. The minimum reflection loss of the composite powder reaches to −27.6 dB at 10.8 GHz which suits its application in RADAR absorbing materials.     

Phase-equilibrium data and liquidus for the system “MnO”-CaO-Al<Subscript>2</Subscript>O<Subscript>3</Subscript>-SiO<Subscript>2</Subscript> at Al<Subscript>2</Subscript>O<Subscript>3</Subscript>/SiO<Subscript>2</Subscript> of 0.55 and 0.65

Phase-equilibrium data and liquidus isotherms for the system “MnO”-CaO-(Al₂O₃+SiO₂) at silicomanganese alloy saturation have been determined in the temperature range of 1373 to 1723 K. The results are presented in the form of the pseudoternary sections “MnO”-CaO-(Al₂O₃+SiO₂) with Al₂O₃/SiO₂ weight ratios of 0.55 and 0.65. The primary-phase fields have been identified in this range of conditions.     

Phase transitions in the magnetic superconductor (Dy<Subscript>0.8</Subscript>Y<Subscript>0.2</Subscript>)Rh<Subscript>4</Subscript>B<Subscript>4</Subscript>

A new (Dy_0.8Y_0.2)Rh₄B₄ superconductor (the superconducting transition temperature is T _c ≈ 5.5 K), which has an inherent magnetic subsystem whose properties are determined by the crystal structure of the superconductor, is synthesized at a high pressure (∼8 GPa) and t ≈ 1800°. The magnetic sublattice of the (Dy_0.8Y_0.2)Rh₄B₄ compound is found to substantially affect its superconducting properties and, in a number of cases, to lead to their anomalous variations, namely, to the absence of the traditional Meissner effect and an anomalously abrupt increase in magnetic induction B _k2 (upper critical field) upon a transition of the magnetic subsystem into the antiferromagnetic state. Upon cooling from 250 to 1.6 K, the (Dy_0.8Y_0.2)Rh₄B₄ compound undergoes a number of phase transformations, namely, a paramagnet-ferrimagnet transition at a Curie temperature T _C ≈ 30 K, a superconducting transition at T _c ≈ 5.5 K against the background of a ferrimagnetic order, and a ferrimagnet-antiferromagnet transition (the Neel temperature is T _N ≈ 2.8 K) in the retained superconducting state.     

Effect of Al<Subscript>2</Subscript>O<Subscript>3</Subscript> Concentration on Density and Structure of (CaO-SiO<Subscript>2</Subscript>)-xAl<Subscript>2</Subscript>O<Subscript>3</Subscript> Slag

The effect of Al₂O₃ concentration on the density and structure of CaO-SiO₂-Al₂O₃ slag was investigated at multiple Al₂O₃ mole percentages and at a fixed CaO/SiO₂ ratio of 1. The experiments were conducted in the temperature range of 2154 K to 2423 K (1881 °C to 2150 °C) using the aerodynamic levitation technique. In order to understand the relationship between density and structure, structural analysis of the silicate melts was carried out using Raman spectroscopy. The density of each slag sample investigated in this study decreased linearly with increasing temperature. When the Al₂O₃ content was less than 15 mole pct, density decreased with increasing Al₂O₃ content due to the coupling of Si (Al), whereas above 20 mole pct density of the slag increased due to the role of Al³⁺ ion as a network modifier.     

Oxidation Behavior of a Pd<Subscript>43</Subscript>Cu<Subscript>27</Subscript>Ni<Subscript>10</Subscript>P<Subscript>20</Subscript> Bulk Metallic Glass and Foam in Dry Air

The oxidation behavior of both Pd₄₃Cu₂₇Ni₁₀P₂₀ bulk metallic glass (Pd4-BMG) and its amorphous foam containing 45 pct porosity (Pd4-AF) was investigated over the temperature range of 343 K (70 °C) to 623 K (350 °C) in dry air. The results showed that virtually no oxidation occurred in the Pd4-BMG at T < 523 K (250 °C), revealing the alloy’s favorable oxidation resistance in this temperature range. In addition, the oxidation kinetics at T ≥ 523 K (250 °C) followed a parabolic-rate law, and the parabolic-rate constants (k _p values) generally increased with temperature. It was found that the oxidation k _p values of the Pd4-AF are slightly lower than those of the Pd4-BMG, indicating that the porous structure contributes to improving the overall oxidation resistance. The scale formed on the alloys was composed exclusively of CuO at T ≥ 548 K (275 °C), whose thickness gradually increased with increasing temperature. In addition, the amorphous structure remained unchanged at T ≤ 548 K (275 °C), while a triplex-phase structure developed after the oxidation at higher temperatures, consisting of Pd₂Ni₂P, Cu₃P, and Pd₃P.     

Evaluating the Diffusion Coefficient of Sulfur in Low-Silica CaO-SiO<Subscript>2</Subscript>-Al<Subscript>2</Subscript>O<Subscript>3</Subscript> Slag

The chemical diffusion coefficient of sulfur in the ternary slag of composition 51.5 pct CaO-9.6 pct SiO₂-38.9 pct Al₂O₃ slag was measured at 1680 K, 1700 K, and 1723 K (1403 °C, 1427 °C, and 1450 °C) using the experimental method proposed earlier by the authors. The P_\textS2 P_{{{\text{S}}_{2} }} and P_\textO2 P_{{{\text{O}}_{2} }} pressures were calculated from the Gibbs energy of the equilibrium reaction between CaO in the slag and solid CaS. The density of the slag was obtained from earlier experiments. Initially, the order of magnitude for the diffusion coefficient was taken from the works of Saito and Kawai but later was modified so that the concentration curve for sulfur obtained from the program was in good fit with the experimental results. The diffusion coefficient of sulfur in 51.5 pct CaO-9.6 pct SiO₂-38.9 pct Al₂O₃ slag was estimated to be in the range 3.98 to 4.14 × 10⁻⁶ cm²/s for the temperature range 1680 K to 1723 K (1403 °C to 1450 °C), which is in good agreement with the results available in literature     

Oxidation of Al<Subscript>2</Subscript>O<Subscript>3</Subscript> Scale-Forming MAX Phases in Turbine Environments

High temperature oxidation of alumina-forming MAX phases, Ti₂AlC and Cr₂AlC, were examined under turbine engine environments and coating configurations. Thermogravimetric furnace tests of Ti₂AlC showed a rapid initial transient due to non-protective TiO₂ growth. Subsequent well-behaved cubic kinetics for alumina scale growth were shown from 1273 K to 1673 K (1000 °C to 1400 °C). These possessed an activation energy of 335 kJ/mol, consistent with estimates of grain boundary diffusivity of oxygen (~375 kJ/mol). The durability of Ti₂AlC under combustion conditions was demonstrated by high pressure burner rig testing at 1373 K to 1573 K (1100 °C to 1300 °C). Here good stability and cubic kinetics also applied, but produced lower weight gains due to volatile TiO(OH)₂ formation in water vapor combustion gas. Excellent thermal stability was also shown for yttria-stabilized zirconia thermal barrier coatings deposited on Ti₂AlC substrates in 2500-hour furnace tests at 1373 K to 1573 K (1100 °C to 1300 °C). These sustained a record 35 µm of scale as compared to 7 μm observed at failure for typical superalloy systems. In contrast, scale and TBC spallation became prevalent on Cr₂AlC substrates above 1423 K (1150 °C). Cr₂AlC diffusion couples with superalloys exhibited good long-term mechanical/oxidative stability at 1073 K (800 °C), as would be needed for corrosion-resistant coatings. However, diffusion zones containing a NiAl-Cr₇C₃ matrix with MC and M₃B₂ particulates were commonly formed and became extensive at 1423 K (1150 °C).     

Effect of LiF as Sintering Agent on the Densification and Phase Formation in Al<Subscript>2</Subscript>O<Subscript>3</Subscript>-4 Wt Pct Nb<Subscript>2</Subscript>O<Subscript>5</Subscript> Ceramic Compound

Different amounts of LiF were added to an Al₂O₃-4 pct Nb₂O₅ basic ceramic, as sintering agent. Improved new ceramics were obtained with LiF concentrations varying from 0.25 to 1.50 wt pct and three sintering temperatures of 1573 K, 1623 K, and 1673 K (1300 °C, 1350 °C, and 1400 °C). The addition of 0.5 wt pct LiF yielded the highest densification, 94 pct of the theoretical density, in association with a sintering temperature of 1673 K (1400 °C). Based on X-ray diffraction (XRD), this improvement was due not only to the presence of transformed phases, more precisely Nb₃O₇F, but also to the absence of LiAl₅O₈. The preferential interaction of LiF with Nb₂O₅, instead of Al₂O₃, contributed to increase the alumina sintering ability by liquid phase formation. Scanning electron microscopy (SEM) results revealed well-connected grains and isolated pores, whereas the chemical composition analysis by energy dispersive energy (EDX) indicated a preferential interaction of fluorine with niobium, in agreement with the results of XRD. It was also observed from thermal analysis that the polyethylene glycol binder burnout temperature increased for all LiF concentrations. This may be related to the formation of hydrogen bridge bonds.     

Crystallization Behavior and Microstructure of Silica-Free 5K<Subscript>2</Subscript>O-45CaO-50P<Subscript>2</Subscript>O<Subscript>5</Subscript> Bioglass

The crystallization behavior and microstructure of silica-free 5K₂O-45CaO-50P₂O₅ (KCP) bioglass have been studied using differential thermal analysis (DTA), X-ray diffraction (XRD), scanning election microscopy (SEM), transmission electron microscopy (TEM), and selected area electron diffraction (SAED). The activation energy for the KCP bioglass crystallization is found to be 337.4 kJ/mol using a nonisothermal method. The crystalline phases of the glass surface determined by XRD are KCa(PO₃)₃, 4CaO·3P₂O₅, and β-Ca(PO₃)₂ when the KCP bioglass is crystallized at 903 K for 4 hours. The crystalline phase of the powder samples determined by XRD is β-Ca(PO₃)₂ when silica-free KCP glasses crystallized at 873 to 1073 K for 8 hours. Crystallization starts at the surface of the KCP bioglass and then proceeds toward the interior of the glass matrix. The morphology of β-Ca(PO₃)₂ is a fibrillar shape 20 to 180 nm in length and 17 to 20 nm in diameter, with an aspect ratio ranging from 1.0 to 10.6.     

Structural Transitions and Magnetic Properties of Ni<Subscript>50</Subscript>Mn<Subscript>36.7</Subscript>In<Subscript>13.3</Subscript> Particles with Amorphous-Like Phase

The high-energy ball-milling method was used for fabricating Ni₅₀Mn_36.7In_13.3 fine-sized particles. The as-melt polycrystalline Ni₅₀Mn_36.7In_13.3 alloy exhibits a 14 M modulated martensite structure at room temperature (RT). The atomic pair distribution function analysis together with the differential scanning calorimetry technique proved that the 14 M modulated martensite transformed to a metastable amorphous-like structure after ball milling for 8 hours. Annealing of the ball-milled particles with the amorphous-like phase first led to the crystallization to form a B2 structure at 523 K (250 °C), and then an ordered Heusler L2₁ structure (with a small tetragonal distortion) at 684 K (411 °C). The annealed particles undergo different structural transitions during cooling, tailored by the atomic arrangements of the high-temperature phase. Low-field thermomagnetization measurements show that the ball-milled particles with the amorphous-like structure or the atomically disordered crystalline structure exhibit a magnetic transition from the paramagnetic-like to the spin-glass state with decreasing temperature, whereas the crystalline particles with the ordered Heusler L2₁ structure present a ferromagnetic behavior with the Curie temperature T _c ≈ 310 K (37 °C).     

Study of the Reduction of Industrial Grade MoO<Subscript>3</Subscript> Powders with CO or CO-CO<Subscript>2</Subscript> Gases to Prepare MoO<Subscript>2</Subscript>

Industrial grade MoO₂ powders have a plenty of advantages relative to MoO₃ in the direct alloying steelmaking processes. In this work, the reduction of industrial grade MoO₃ powder with CO gas or the mixed gases of CO and CO₂ has been investigated in detail in order to prepare industrial grade MoO₂ powder. It is found that reaction temperature has a significant effect on the product composition. Using pure CO as the reducing gas, for temperatures below 868 K (595 °C), the main product is MoO₂ with some whisker carbon; for temperatures above 868 K (595 °C) the main reaction products are MoC and amorphous carbon; as the reaction temperature further increased, the final reaction product is Mo₂C. In addition, Mo₄O₁₁ is always formed as an intermediate product during the reaction processes both at lower and higher temperatures, which is similar to that observed on reduction of MoO₃ by H₂. It is found that adding CO₂ to the reducing gases eliminated carbon formation but still allows the formation of MoO₂ during the reaction process. This method may be applied to produce industrial grade MoO₂.     

Thermodynamic evaluation and optimization of the MnO-Al<Subscript>2</Subscript>O<Subscript>3</Subscript> and MnO-Al<Subscript>2</Subscript>O<Subscript>3</Subscript>-SiO<Subscript>2</Subscript> systems and applications to inclusion engineering

All available thermodynamic and phase-diagram data have been critically evaluated and optimized for the liquid-slag phase and for all solid phases at 1 bar pressure from 298 K to above the liquidus temperatures for the systems MnO-Al₂O₃ and MnO-Al₂O₃-SiO₂, and a database of model parameters has been prepared. The modified quasichemical model was employed for the molten-slag phase. Calculations using the database were performed with applications to inclusion engineering for Mn/Si killed steel.     

High-Accuracy X-Ray Diffraction Analysis of Phase Evolution Sequence During Devitrification of Cu<Subscript>50</Subscript>Zr<Subscript>50</Subscript> Metallic Glass

Real-time high-energy X-ray diffraction (HEXRD) was used to investigate the crystallization kinetics and phase selection sequence for constant-heating-rate devitrification of fully amorphous Cu₅₀Zr₅₀, using heating rates from 10 K/min to 60 K/min (10 °C/min to 60 °C/min). In situ HEXRD patterns were obtained by the constant-rate heating of melt-spun ribbons under synchrotron radiation. High-accuracy phase identification and quantitative assessment of phase fraction evolution though the duration of the observed transformations were performed using a Rietveld refinement method. Results for 10 K/min (10 °C/min) heating show the apparent simultaneous formation of three phases, orthorhombic Cu₁₀Zr₇, tetragonal CuZr₂ (C11_b), and cubic CuZr (B2), at 706 K (433 °C), followed immediately by the dissolution of the CuZr (B2) phase upon continued heating to 789 K (516 °C). Continued heating results in reprecipitation of the CuZr (B2) phase at 1002 K (729 °C), with the material transforming completely to CuZr (B2) by 1045 K (772 °C). The Cu₅Zr₈ phase, previously reported to be a devitrification product in C₅₀Zr₅₀, was not observed in the present study.     

Thermal diffusivity measurements of some synthetic CaO-Al<Subscript>2</Subscript>O<Subscript>3</Subscript>-SiO<Subscript>2</Subscript> slags

In an attempt to systematize the knowledge of the heat conduction of liquid silicates, the effective thermal diffusivities of some synthetic slags containing CaO, Al₂O₃, and SiO₂ have been measured, using the three-layer laser-flash method on a differential scheme in the temperature range of 1625 to 1825 K. The effective thermal diffusivities measured, which are a combination of the phononic and photonic heat-transfer mechanisms, were found to increase with increasing temperature for all the presently investigated slags. The slag compositions were chosen in such a way that the changes in the effective thermal diffusivities would reflect the changes in the structure of the slags. It was observed that, at a CaO/Al₂O₃ molar ratio of 4.42, an increase of the SiO₂ content had very little effect on the effective thermal diffusivity values. On the other hand, addition of SiO₂ to a slag with the CaO/Al₂O₃ molar ratio of 2.59 resulted in a significant increase in the effective thermal diffusivity. The addition of Al₂O₃ to slags with a constant CaO/SiO₂ molar ratio resulted in a marked increase in the effective thermal diffusivity. Both these trends indicate that there might be an influence of the network formation in silicate melts on the effective thermal diffusivity.     

Solubilities of Chlorine in CaO-SiO<Subscript>2</Subscript>-Al<Subscript>2</Subscript>O<Subscript>3</Subscript>-MgO Slags: Correlation Between Sulfide and Chloride Capacities

To derive a correlation between sulfide and chloride capacities through our own systematic experimental studies by using a gas equilibrium technique involving Ar-H₂-H₂O-HCl gas mixtures, the solubilities of chlorine were determined for CaO-SiO₂-MgO-Al₂O₃ slags at temperatures between 1673 K and 1823 K (1400 °C and 1550 °C). As a formula to correlate sulfide and chloride capacities, the following equation that is the function of temperature only was obtainable;

Kinetics of Reduction of CaO-FeO<Subscript><Emphasis Type="Italic">x</Emphasis></Subscript>-MgO-PbO-SiO<Subscript>2</Subscript> Slags by CO-CO<Subscript>2</Subscript> Gas Mixtures

Kinetics of the reaction of lead slags (PbO-CaO-SiO₂-FeO _x -MgO) with CO-CO₂ gas mixtures was studied by monitoring the changes in the slag composition when a stream of CO-CO₂ gas mixture was blown on the surface of thin layers of slags (3 to 10 mm) at temperatures in the range of 1453 K to 1593 K (1180 °C to 1320 °C). These measurements were carried out under conditions where mass transfer in the gas phase was not the rate-limiting step and the reduction rates were insensitive to factors affecting mass transfer in the slag phase. The results show simultaneous reduction of PbO and Fe₂O₃ in the slag. The measured specific rate of oxygen removal from the melts varied from about 1 × 10^?6 to 4 × 10^?5 mol O cm^?2 s^?1 and was strongly dependent on the slag chemistry and its oxidation state, partial pressure of CO in the reaction gas mixture, and temperature. The deduced apparent first-order rate constant increased with increasing iron oxide content, oxidation state of the slag, and temperature. The results indicate that under the employed experimental conditions, the rate of formation of CO₂ at the gas-slag interface is likely to be the rate-limiting step.     

Effect of CaO-Al<Subscript>2</Subscript>O<Subscript>3</Subscript>-MgO slags on the formation of MgO-Al<Subscript>2</Subscript>O<Subscript>3</Subscript> inclusions in ferritic stainless steel

A thermodynamic equilibrium between the Fe-16Cr melts and the CaO-Al₂O₃-MgO slags at 1823 K as well as the morphology of inclusions was investigated to understand the formation behavior of the MgO-Al₂O₃ spinel-type inclusions in ferritic stainless steel. The calculated and observed activities of magnesium in Fe-16Cr melts are qualitatively in good agreement with each other, while those of aluminum in steel melts exhibit some discrepancies with scatters. In the composition of molten steel investigated in this study, the log (X _MgO/X _{Al 2}O₃) of the inclusions linearly increases by increasing the log [a _Mg/a _Al ² ·a _O ² ] with the slope close to unity. In addition, the relationship between the log (X _MgO/X _{Al 2}O₃) of the inclusions and the log (a _MgO/a _{Al 2}O₃) of the slags exhibits the linear correlation with the slope close to unity. The compositions of the inclusions are relatively close to those of the slags, viz. the MgO-rich magnesia-spinel solid solutions were formed in the steel melts equilibrated with the highly basic slags saturated by CaO or MgO. The spinel inclusions nearly saturated by MgO were observed in the steel melts equilibrated with the slags doubly saturated by MgO and MgAl₂O₄. The spinel and the Al₂O₃-rich alumina-spinel solid solutions were formed in the steel melts equilibrated with the slags saturated by MgAl₂O₄ and MgAl₂O₄-CaAl₂O₄ phases, respectively. The apparent modification reaction of MgO to the magnesium aluminate inclusions in steel melts equilibrated with the highly basic slags would be constituted by the following reaction steps: (1) diffusion of aluminum from bulk to the metal/MgO interface, (2) oxidation of the aluminum to the Al³⁺ ions at the metal/intermediate layer interface, (3) diffusion of Al³⁺ ions and electrons through the intermediate layer, and (4) magnesium aluminate (MgAl₂O₄ spinel, for example) formation by the ionic reaction.