Basic electric furnace slag-line and bank maintenance refractories

Abstract

The balancing of electric furnace lining wear can be accomplished by the use of hot-maintenance refractories in the harsh slag-line and bank wear areas. The maintenance materials used resist severe chemical attack in the slag-line and high-temperature erosion in the banks.

The design of Basic specialty products for these areas is constrained by the necessity for the products to: (1) be applied through a pneumatic gun, (2) adhere on impact with the hot wall and (3) densify within minutes after application. These limitations require that the accepted optimum refractory properties be compromised in maintenance materials.

Raw materials available for formulating Basic specialty products include high-purity periclase, dead-burnt magnesite, dead-burnt dolomite and chrome ore. To these are added binders, plasticizers and sintering aids.

Laboratory-determined physical property data can be related to the mineralogical structure deriving from the raw materials and additives employed, and to the chemical attack and erosion resistance of a given refractory composition. These correlations allow for the design and selection of electric furnace maintenance products based on the specific conditions encountered.

Résumé

On peut égaliser l'usure des revêtements des fours électriques par l'usage des réfractaires entretien-à-ehaud dans les régions d'usure sévère de la ligne du laitier et des banes. Il faut que les matériaux d'entretien résistent à l'attaque chimique sévère dans la ligne du laitier et à l' érosion a hautes témperatures dans les banes.

Le design des produits spéciaux “Basic” pour ces régions est contraint par les conditions que le produit: (1) soit appliqué par pulvérisateur pneumatique (2) s'attache au moment de l'impact avec la paroi chaude, (3) se solidifie quelques minutes apres l'application. Ces restrictions nécessitent un compromis des propriétés réfractaires optimales acceptées dans le cas des matériaux d' entretien.

Les matières premières disponibles pour la fabrication des produits spéciaux “Basic” sont: la periclase de haute purité, la magnésie calcinee, la dolomite calcinée, et le minerai du chrome. En plus, on peut ajouter des agglomérants, des plastifiants, et des produits pour aider le frittageo.

On peut relier les propriétés physiques mesurées dans le laboratoire à la structure minéralogique qui en résulte des matières premières et des additions utilisées, ainsi qu'à l'attaque chimique et à la résistance a l' érosion d'un réfractaire d'une composition donée. Ces corrélations nous permettent de concevoir et de sélectionner des produits d'entretien pour des fours électriques basé sur les conditions spécifiques réelees.     

Role of Cr2O3 on formation of reaction sintered dense ZrO2–Al2O3–SiO2 based refractory materials

Abstract

Extremely dense zirconia–mullite composites were developed by reaction sintering of microcalcined fine alumina powder and zircon flour taken in different ratios with Cr₂O₃ as an additive. The powder mixes were isostatically pressed and sintered at 1550°C. The sintered compacts were characterised by different physicomechanical properties, microstructure developed and phase compositions. Cr₂O₃ exhibited positive influence up to certain level of addition on the thermomechanical properties of reaction sintered zirconia–mullite composites including corrosion resistance and microstructure.

On a développé des composites extrêmement denses de zircone et mullite par frittage réactif de poudre fine d’alumine micro calcinée et de farine de zircone en différentes proportions, avec du Cr₂O₃ comme adjuvant. On a pressé les mélanges de poudres au moyen d’une presse isostatique et on les a frittés à 1550°C. On a caractérisé les différentes propriétés physico mécaniques, la microstructure développée et la composition de phases des compacts frittés. Le Cr₂O₃ exhibait une influence positive jusqu’à un certain niveau d’addition sur les propriétés thermomécaniques des composites de zircone et mullite à frittage réactif, incluant la résistance à la corrosion et la microstructure.     

Solid structural changes during the reduction of iron oxides

Abstract

The changes in the solid structure, i.e., grain size, shape and pore structure, during the reduction. of reagent-grade hematite to iron by CO?CO₂ mixtures at temperatures between 725 and 925°C were investigated. The reduction of hematite to wustite was found to produce little structural change. In contrast, three mechanisms of structural change occurred during the reduction of wustite to iron. These included the thermal sintering of the wustite, the growth of fibrous iron filaments from the partially reduced wustite grains, and the sintering or “coarsening” of the reduced iron. A quantitative model for the sintering of the wustite is described.

The effects of the structural changes on the reduction kinetics are reviewed. The sintering of the wustite reduced the over-all rate of reduction; the growth of the fibrous iron increased the rate of reduction. The sintering of the iron had little effect on the kinetics. The interaction between the sintering of the wustite and the growth of the fibrous irons, which change the character of the reduction from nontopochemical to topochemical, is also discussed.

Résumé

Les variations de la structure solide, i.e., la grosseur du grain, la forme et la porosité,ont été étudiées au moment de la réduction d'hématite en fer, dans des mélanges de CO?CO₂ aux températures comprises entre 725 et 925°C. La réduction de l'hématite à la wustite s'accompagne d'un léger changement de structure. Au contraire, trois mécanismes de changements structuraux se sont présentés au cours de la réduction de la wustite en fer. Ce sont: le frittage thermique de la wustite, la croissance des filaments fibreux de fer provenant des grains de wustite partiellement réduits et aussi le frittage du fer réduit. Un modéle quantitatif décrit Ie frittage de la wustite.

Les effets des variations structurales sur la cinétique de réduction sont revisés. Le frittage de la wustite a diminué le taux de réduction, alors que la croissancé du fer fibreux a augmente ce taux. Le frittage du fer a un effet minime sur la cinétique. L'interaction entre le frittage de la wustite et la croissance des fibres de fer fait varier Ie caractère de la réduction, de non-topochimique à topochimique.     

Utilization of direct reduced iron in an electric arc furnace

Abstract

A discussion of the essential characteristics of the materials needed for processing through a counter-current direct reduction furnace and usage in an electric arc furnace constitutes the rust part of this article. Some of the physical and chemical properties are reviewed and correlated with the performance of the Sidbec-Dosco reduction plant.

The impact of utilization of direct reduced iron on the Electric Arc furnace steelmaking practice is then evaluated, in terms of energy, consumption, productivity, electrode and refractories consumptions. Finally the characteristic of the steels produced for wire and flat rolled products using direct reduced iron is reviewed.

Résumé

La première partie de ce travail discute des caractéristiques essentielles des boulettes nécessaires à la réduction directe par un gaz à contrecourant, pour changement dans un four électrique. Certaines propriétés physiques et chimiques sont revues et permettent une corrélation avec les performances de l'usine de réduction de Sidbec-Dosco.

On évalue l'impact que peut avoir l'utilisation de fer directement réduit au four électrique à arc dans la pratique de l'acierage, ceci du point de vue de la consommation d' énergie, de la productivité et de la consommation d' électrodes et de réfractaires. On discute finalement des caractéristiques de l'acier produit pour fils et produits laminés à plat en utilisant le fer réduit directement.     

Chlorination of a Scheelite-Wolframite Concentrate with Chlorine and Sulphur Dioxide

Abstract

The chlorination of a scheelite-wolframite concentrate with chlorine and sulphur dioxide was studied in order to determine the operative conditions that favor the tungsten extraction. Tests were made in a vertical reactor with a static bed and upward flow of reactive gases. Effects of the flow rates of chlorine and of sulphur dioxide, the reaction time and the reaction temperature on the tungsten extraction were analyzed. The evolution of the tungsten extraction determined in our tests was briefly explained from the volatile and non-volatile reaction products formed in each case. The main reaction products identified were WO₂Cl₂, FeCl₂, FeCl₃, CaSO₄ and CaCl₂. The mechanism and apparent activation energy of the reaction were analyzed from data obtained under non-isothermal conditions. The kinetic analysis shows that the presence of non-volatile reaction products affects the chlorination. Effects of the impurity reactivity, the ratio of tungsten-bearing minerals and the particle size of the concentrate on the chlorination were analyzed. Finally, the operative conditions that allowed a tungsten recovery near 90% were determined.

Résumé

On a étudié la chloration au chlore et au bioxyde de soufre d'un concentré de scheelite-wolframite, afin de déterminer les conditions d'opération qui favorisent l'extraction du tungstàne. On a exécuté des tests dans un réacteur vertical à lit statique, á l'ecoulement vers le haut des gaz réactifs. On a analysé l'effet, sur l'extraction du tungstène, des taux d'écoulement du chlore et du bioxyde de soufre, de la durée de réaction et de la température de réaction. On a expliqué brièvement l'évolution de l'extraction du tungstène, déterminée dans nos tests, à partir des produits de réaction volatiles et non volatiles formés dans chaque cas. Les principaux produits de' réaction identifies étaient le WO₂Cl₂, le FeCl₂, le FeCl₃, le CaSO₄ et le CaCl₂. On a analysé le mécanisme et l'énergie d'activation apparente de la réaction á partir de données obtenues so us conditions non isothermes. L'analyse cinétique montre que la préesence de produits de réaction non volatiles affecte la chloration. On a analysé les effets, sur la chloration, de la réactivité des impuretes, de la proportion des mineraux porteurs de tungstene et de la taille de particule du concentre. Finalement, on a déterminé les conditions d'opération qui permettent la récupération de pràs de 90% du tungstène.     

Sintering and Ferrite Formation During High Temperature Roasting of Sulfide Concentrates

Abstract

The newly developed toroidal fluidized bed reactor has potential for improving sulfide roasting efficiency due to its unique and good mass/heat transfer characteristics. To achieve effective roasting at high temperature using the toroidal fluidized bed reactor, engineering issues associated with sintering and ferrite formation are investigated in this study by roasting industrial sulfide concentrates of zinc and copper. Laboratory tests are conducted at 800–1100°C by using an electric tube furnace under controlled roasting conditions. The test program is based on statistical design, and the products are characterized by XRD, SEM and EDX. It is revealed that the oxygen concentration plays an important role in promoting roasting. Roasting temperatures higher than 950°C do not favor roasting conversion due to the sintering of sulfide particles which inhibits oxygen diffusion into the particle core. Close contact of the oxidized particles favors the atomic interdiffusion between particles, leading to the formation of undesired zinc ferrite. Roasting in toroidal fluidized bed reactor results in zinc calcines with increased surface area and reduced zinc ferrite formation, thus improving zinc recovery. © 2000 Published by Elsevier Science Ltd on behalf of the Canadian Institute of Mining and Metallurgy. All rights reserved.

Résumé

Le réacteur toroïdal à lit fluidisé, développé récemment, a le potentiel d'améliorer l'efficacité du grillage du sulfure à cause de ses caractefristiques uniques de bon transfert de masse/chaleur. Afin d'obtenir un grillage efficace à haute température avec le reacteur toroïdal à lit fluidisé, on a examiné,dans cette étude, des questions d'ingénierie associées avec le frittage et la formation de ferrite, en grillant des concentrés industriels de sulfure de zinc et du cuivre. On a effectué des épreuves de laboratoire entre 800–1100°C avec une fournaise électrique tubulaire sous conditions controlées de grillage. Le plan d'évaluation est basé sur la conception statistique. On a caratérisé les produits par XRD, SEM et EDX. On revele que la concentration d'oxygene joue un role important dans l'activation du grillage. Les temperatures de grillage de plus de 950°C ne favorisent pas la transformation du grillage à cause du frittage des particules de sulfure, ce qui inhibe la diffusion d'oxygene au coeur de la particule. Le contact etroit entre les particules oxydees favorise l'inter-diffusion atomique entre les particules, conduisant à la formation de ferrite de zinc indesirable. Le grillage dans le reacteur toroidal à lit fluidise resulte en zinc de calcination ayant une plus grande superficie et en une réduction de la formation de ferrite de zinc, améliorant ainsi la récuperation du zinc. © 2000 Published by Elsevier Science Ltd on behalf of the Canadian Institute of Mining and Metallurgy. All rights reserved.     

Effects of nitrogen and helium shielding mixtures on semiaustenitic stainless steel welds

Abstract

The effect of nitrogen-helium atmos pheres used as a shielding gas for welding of some semiaustenitic stainless steels was studied. Nitrogen, being a strong austenite stabilizer, has the tendency to suppress the amount of retained delta ferrite in the weldment. The addition of 1.0 per cent nitrogen by volume to the helium shielding gas increased the tensile strength of the weldment approximately 4000 psi to within about 1 per cent of the parent metal, and the ductility approximately 33 per cent to within 95 per cent of the parent metal.

The additions of nitrogen to the shielding gas significantly reduced the a mo unt of retained ferrite. However, increasing the nitrogen in excess of 1 per cent by volume drastically reduced the tensile strength and ductility. It is suggested that this reduction in strength and ductility is the result of pertinent alloying components being used up in the formation of nitrides.

Résumé

Les auteurs ont étudié 1'influence de mélanges d'hélium et d'azote utilisés comme gaz de couverture en soudage d'aciers inoxydables semi austénitiques. Stabilisateur puissant de 1'austénite, l'azote tend à diminuer la teneur en fer delta des soudures. En utilisant un gaz renferment 1% en volume d'azote, la résistance à la traction des éprouvettes accuse une augmentation de 4000 psi, la relevant ainsi jusqu'à un écart aussi petit que 1% de la résistance du métal de base; concomitamment, l'allongement s'améliore de 33% et ainsi s'approche jusqu'à 95% de l'allongement du métal de base. L'influence de l'azote, comme moyen de réduire la teneur en fer delta est significative. Toutefois, dès que la quantité d'azote dépasse 1% en volume, la résistance à la traction et l'allongement fléchissent considérablement. Les auteurs avancent que le fléchissement est le résultat de la fixation d'éléments d'alliage par l'azote.     

Wear Characteristics of a Zinc-Based Alloy Compared With a Conventional Bearing Bronze Under Mixed Lubrication Conditions: Effects of Material and Test Parameters

Abstract

This study discusses the sliding wear response of a zinc-based alloy (conforming to ZA 27) in mixed lubrication conditions at different sliding pressures and speeds. A conventional bearing bronze (conforming to SAE 660) was also tested under identical test conditions for comparison purposes.

Wear rate increased with speed and pressure. Further, the zinc-based alloy attained superior wear response (less wear rate and frictional heating) than the bronze at all test speeds except prior to seizure (occurring at 7.0 MPa) at the speed of 4.60 m/s. The trend reversed in the latter case. Wear rate of the specimens also agreed with the degree of frictional heating experienced by them. A higher wear rate corresponded to larger frictional heating and vice versa. Wear behaviour of the samples improved considerably in the present study due to the presence of the oil lubricant as compared to the study in dry conditions.

Wear behaviour of the samples has been discussed in terms of the nature and response of their various microconstituents and the effects produced by varying test speeds and pressures under mixed lubrication conditions. Features of wear surfaces, subsurface regions and debris particles generated during the testing of the specimens further substantiated the observed wear behaviour of the samples and were helpful in understanding the operating wear mechanisms.

Cette étude discute de la réponse à l'usure par glissement d'un alliage à base de zinc (seconformant à ZA 27) sous condition de lubrification mixte à différentes pressions et vitesses de glissement. On a aussi évalué un bronze conventionnel pour palier (se conformant à SAE 660) sous des conditions identiques pour fin de comparaison.

Le taux d'usure augmentait avec la vitesse et la pression. De plus, l'alliage à base de zinc démontrait une réponse supérieure à l'usure (i.e. un plus bas taux d'usure et moins de chaleur de friction) en comparaison avec le bronze, à toutes les vitesses d'évaluation sauf juste avant qu'il ne grippe (ce qui se produit à 7.0 MPa), à la vitesse de 4.60 m/s; la tendance s'inversait dans ce dernier cas. Le taux d'usure des spécimens était aussi en accord avec leur degré d'échauffement par friction, i.e. un plus haut taux d'usure correspondait à un échauffement plus important par friction et vice-versa. Le comportement d'usure des échantillons s'est amélioré considérablement dans la présente étude à cause de la présence de l'huile lubrifiante en comparaison avec l'étude en condition sèche.

On a discuté du comportement d'usure des échantillons en termes de la nature et de la réponse de leurs divers micro constituants ainsi que des effets produits en variant la vitesse et la pression d'évaluation sous condition de lubrification mixte. Les caractéristiques des surfaces d'usures, des régions sous la surface ainsi que des débris de particules générés lors de l'évaluation des spécimens ont davantage établi le comportement observé d'usure des échantillons et étaient utiles pour comprendre les mécanismes d'usure en opération.     

The Effect of Oxide Grain Structure on the High-Temperature Oxidation of Fe,Ni and Cr

Abstract

Investigations have shown that the oxidation rate of metals and alloys is strongly influenced by the oxide grain size. This paper summarizes some of our data on the oxidation of Fe, Ni, Cr, and some alloys and relates the observed oxide grain structures to the oxidation kinetics and transport processes. Fine-grained polycrystalline oxide thickens most rapidly because the many oxide grain boundaries act as preferential paths for rapid diffusion. In contrast, monocrystalline oxide such as forms on some orientations of Ni and Cr thickens very slowly and shows the highest activation energy. Oxide grain size is found to depend on such factors as metal orientation, chemical pretreatment of the surface, cold work, and oxidation procedure.

Résumé

Plusieurs programmes de recherche ont montré que le taux d'oxydation des métaux et alliages dépend de la grosseur des grains des oxydes produits. Cet article présente certains des résultats obtenus en oxydant du Ni, du Cr et certains alliages; un rapport entre la structure des grains d'oxydes produits, d'une part, et d'autre part, la cinétique d'oxydation et les processus de transport présents, a été etabli. Les oxides polycristallins é grain serré facilitent l'oxydation, car leurs nombreux joints de grains offrent une route préférentielle à la diffusion rapide de l'oxygéne. Par contre, selon certaines orientations de Ni et de Cr, l'oxide monocristallin formé s'épaissit très lentement et présente les énergies d'activation les plus élevées. La grosseur des grains d'oxydes dépend de certains facteurs tels que l'orientation du metal oxyde, le prétraitement chimique de la surface, le travail à froid et la procédure d'oxydation.     

Reduction of Ilmenite Concentrates By Methane Containing Gas,Part II: Effects of Preoxidation and Sintering

Abstract

Reduction of preoxidized and sintered ilmenite concentrates by a CH₄-H₂-Ar gas mixture was investigated in a laboratory fixed bed reactor in temperature programmed experiments. The ilmenite concentrates contained different concentrations of TiO2 (55.6-71.5wt%) and iron oxide (Fe_total 14.5-28.2wt%).

In the reduction of ilmenite by hydrogen, during ramping reduction temperature from 230 to 1100 °C, only iron oxides were reduced to metallic iron and the reduction was not complete. The reduction of titania was slight. The ilmenite concentrates were reduced by CH₄-H₂-Ar gas mixture to metallic iron and titanium oxycarbide. Preoxidation and sintering of ilmenite concentrates changed their phase composition and caused a sharp decrease in specific surface area of raw materials and an increase in carburization temperature. Sintering also increased the metallization temperature of iron.

On a étudié, dans un reacteur de laboratoire à lit fixe, lors d'experiences à températures programmées, la réduction de concentrés d'ilménites pre-oxydes et frittes par un melange de gaz de CH4-H2-Ar. Les concentres d'ilmenites contenaient differentes concentrations de TiO2 (55.6-71.5% en poids) et d'oxyde de fer (Fetotal 14.5-28.2% en poids).

Au cours de la réduction de l'ilménite par l'hydrogene, lors de l'augmentation de temperature de réduction de 230 à 1100 °C, seuls les oxydes de fer etaient réduits en fer métallique et, de plus, la réduction n'était pas compléte. La réduction du dioxyde de titane était faible. Les concentrés d'ilménites ont été réduits par le mélange de gaz CH₄-H₂-Ar en fer métallique et en oxycarbure de titane. La préoxydation et le frittage des concentrés d'ilménite ont change leur composition de phase et ont causé une diminution marquée de la surface specifique des matériaux bruts ainsi qu'une augmentation de la température de cémentation. Le frittage a également augmenté la température de métallisation du fer.     

A Review of the Mechanisms of Fatigue

Abstract

Relationships between structure and fatigue properties are briefly reviewed for metals and alloys of the facecentred cubic structure. The effects are considered of stressor strain amplitude, temperature, stacking fault energy, strain ageing, degree of order, precipitation and dispersion hardening, and fibre strengthening, upon crack initiation and propagation.

Résumé

L'auteur traite brièvement des rapports entre la structure et la résistance à la fatigue des métaux et alliages cubiques à faces centrées. II passe en revue L'influence de l'intensité de la contrainte, de l'amplitude de la ,déformation, de la temperature, de l' énergie de faute d'empilement, du vieillissement après déformation, de la nature de l'ordre, du durcissement par précipitation et dispersion, et du renforcement à l'aide de fibres, sur la formation et.la propagation des fissures.     

Reaction-Inhibition During Sintering of SiC with Al2O3 Additions

Abstract

The mechanisms and products of the reactions which occur during the sintering of SiC with Al₂O₃ as a sintering aid were analysed. The effects of two sintering atmospheres, namely pressurised CO and Ar gases, on the reaction thermodynamics and reaction products were investigated. Thermodynamically predicted reaction products were correlated with experimentally determined reaction products. The observed weight losses and the final sintered densities are explained on the basis of the proposed reaction mechanisms. The major finding of the present analysis is that a pressurised CO gas atmosphere greatly enhances the densification characteristics of SiC ceramics.

Résumé

Nous avons analysé les mécanismes et les produits des réactions qui se produisent lors du frittage du SiC avec du Al₂O₃ comme aide de frittage. Nous avons étudié les effets de deux atmospheres de frittage: du CO gazeux pressurisé et du Ar gazeux pressurisé, sur la thermodynamique des réactions et les produits de ces réactions. Les produits des réactions prédits par la thermodynamique ont été mis en corrélation avec les analyses expérimentales de ces produits. Sur les bases des mécanismes de réactions proposées, nous avons expliqué les pertes de poids observées et les densités de frittage finales. La découverte la plus importante de la présente analyse est qu'une atmosphère de CO gazeux pressurisé ameliore beaucoup les caractéristiques de densification des céramiques SiC.     

Equilibrium phase relationships during solidification of Fe-O-C-X alloys

Abstract

Analysis of the solidification process of alloys requires that the phase relationships at equilibrium be known. The problem is complex and difficult for commercial ferrous alloys because of the presence of iron, carbon, oxygen, a deoxidizer, manganese, sulphur, etc. This study develops the phase relationships in the iron-rich corner of four component systems and covers the Fe-O-C-Si and Fe-O-C-Al systems specifically. The equilibrium state is treated at 1 atm pressure. The effects of suppression of formation of CO and of segregation of elements between liquid and solid iron are then analyzed.

Résumé

L'analyse du procédé de solidification des alliages requiert que la relation des phases à l'equilibre soit connue. Le problème est complexe et difficile pour les alliages ferreux commerciaux à cause de la présence de fer, de carbone, d'oxygene, d'un désoxydant, de manganèse, de soufre, etc. L'étude présente développe la relation des phases dans la région riche en fer d'un système à quatre composants, en particulier les systèmes Fe-O-C-Si et Fe-O-C-Al. L'équilibre est traité à 1 atm. de pression. Les effets de la suppression de formation de CO et de ségrégation d'éléments entre le fer liquide et solide sont ensuite analysés.     

Evaluation of Ultrasonic Inspection Procedures by Field Mapping with an Optical Probe

Abstract

Optical interferometric laser probes can be used to visualize the time variation of ultrasonic displacements produced by conventional transducers and their spatial variations over the surface of a test piece. This information can be used to estimate the ultrasonic field distribution incident on the region of the flaws and then can lead to a better evaluation of the reliability of the whole inspection procedure. In this communication the principles at the basis of such a technique are outlined and the optical probe used to perform the measurement is described. An example where the probe maps the inside and the outside of an Electrical Resistance Welded pipe, in which ultrasound undertakes multiple reflections, is presented.

Résumé

Les sondes laser basées sur l'interférometrie optique peuvent être utilisées pour visualiser les variations temporelles des déplacements ultrasonores produits par des palpeurs conventionnels ainsi que leur variations spatiales à la surface d'un échantillon. Les données ainsi obtenues peuvent servir à estimer la distribution du champ ultrasonore incident dans une zone de défauts et ainsi conduire à une meilleure évaluation de la fiabilité de toute la procedure d'inspection. Dans cette communication, nous présentons les principes à la base d'une telle technique d'évaluation et nous décrivons la sonde optique utilisée. Nous présentons un exemple où la sonde est utilisée pour balayer l'intérieur et l'extérieur d'un tuyau soudé par résistance dans lequel l'ultrason subit des reflections multiples.     

Micrbband Formation in Cyclic Extrusion Compression of Aluminum

Abstract

The influence of very large deformations on the properties and microstructures of A199.95 and A199.992 is investigated. The very large deformations are imposed by the cyclic extrusion-compression (CEC) method, which combines extrusion and compression processes. It is found that above true strains of 4 and 8 respectively, the compression proof stresses of A199.992 and A199.95 stabilize. The property stabilization appears to result from the increasing incidence of micro bands which leads to the final constancy of the microstructure parameters. The homogeneous chess-board like microstructure forms during the deformation by the CEC method, as the result of rearrangement of microstructure by the mutually crossing microbands leading to the final dominance of persistent macro shear bands.

Résumé

On a étudié l'influence de très grandes déformations sur les propriétés et la microstructure de l'Al 99.95 et de l'Al 99.992. De très grandes déformations sont imposées par la méthode d'extrusioncompression cyclique (CEC), qui combine des processus d'extrusion et de compression. Au-delà de déformations réelles de 4 et 8 respectivement, les limites apparentes d'élasticité sous compression de l'AI 99.992 et de l'Al 99.95 se stabilisent. Cette stabilisation de la propriété a l'air de résulter de l'augmentation de l'occurrence de micro-bandes, ce qui méne à la constance finale des paramètres de microstructure. La microstructure homogène à apparence d'échiquier se forme lors de la déformation par la méthode CEC, comme résultat du réarrangement de la microstructure par les micro-bandes qui s'entrecroisent mutuellement, menant à la domination finale de bandes persistantes de macro-cisaillement.     

Effects of compaction technique on processing response of aluminium PM alloys

The objective of this research was to assess the effects of compaction method (uni-axial die compaction and cold isostatic pressing) on two aluminium powder metallurgy alloys. Both systems were mixtures of elemental and master alloy powders. Mechanical and physical properties from samples prepared using both methods were compared. Analyses included the measurement of green and sintered densities, tensile properties and microstructural analyses. Results indicated that sintered products of a largely comparable quality could be realised for both alloys regardless of the compaction approach employed. PM2324 displayed sensitivity to compaction pressure such that low values were preferred for cold isostatic pressing (CIP) whereas higher values yielded superior sintered products when die compaction was implemented. Conversely, compaction pressure had no meaningful impact on the sintering behaviour of PM7075 for CIP or die pressed samples.

Le but de cette recherche consistait à évaluer les effets de la méthode de compaction (compaction uniaxe en moule et compression isostatique à froid) sur deux alliages d’aluminium de la métallurgie des poudres. Les deux systèmes consistaient en mélanges de poudres élémentaires et de poudres d’alliage mère. On a comparé les propriétés mécaniques et physiques des échantillons préparés en utilisant les deux méthodes. Les analyses incluaient la mesure de la densité à cru et frittée, les propriétés de traction et les analyses de la microstructure. Les résultats indiquaient que l’on pouvait réaliser des produits frittés d’une qualité très comparable pour les deux alliages, peu importe l’approche de compaction utilisée. PM2324 démontrait une sensitivité à la pression de compaction de telle sorte que des valeurs faibles étaient préférées pour le CIP alors que des valeurs plus élevées produisaient des produits frittés supérieurs avec la compaction en moule. Inversement, la pression de compaction n’avait pas d’impact significatif sur le comportement de frittage de PM7075 pour les échantillons pressés par CIP ou en moule.     

The kinetics of dissolution of enargite in acidified ferric sulphate solutions

Abstract

Over the temperature range 60° to 95°C, sintered discs of synthetic enargite (Cu₃AsS₄) were dissolved slowly in acidified ferric sulphate solutions, yielding both elemental and sulphate sulphur, together with soluble copper and arsenic. The dissolution kinetics were linear and this was interpreted as indicating rate control by a reaction occurring on the surface of this sulphosalt. The activation energy associated with this reaction was 13.3 kcal/mole. The rate of copper extraction increased according to the 0.55 power of the ferric sulphate concentration and the 0.20 power of the sulphuric acid concentration. The rate decreased in a complex manner with increasing strengths of the ferrous sulphate reaction product. Natural enargite dissolves like the synthetic sulphosalt and at approximately the same rate.

Résumé

A des températures variant entre 60°C et 95°C, des disques frittés d'énargite synthétique (Cu₃AsS₄) ont été dissous lentement dans des solutions acides de sulfate ferrique, pour produire du soufre élémentaire et sous forme de sulfate, ainsi que du cuivre et de l'arsenic soluble. Les cinétiques de dissolution suivent une loi linéaire, due à la réaction qui a lieu en surface de ce sulfosel et qui, semble-t-il, contrôlerait la dissolution. L'énergie d'activation associée à la réaction est de 13.3 kcal/mole. Le taux d'extraction du cuivre croît comme la puissance 0.55 de la concentration en sulfate ferrique et la puissance 0.20 de la concentration en acide sulfurique. La vitesse décroît de façon complexe lorsque augmente la concentration du produit de la réaction du sulfate ferreux. L'énargite naturelle se dissout de la même manière que le sulfosel synthétique, et à sensiblement la même vitesse.     

Heat flow in blast furnace hearths

Abstract

Heat flow and temperature distribution in iron blast furnace hearths has been investigated using a digital computer implemented simulation. Furnace hearths, with and without underhearth cooling, have been simulated to provide dynamic thermal response characteristics and to explore refractory material requirements for improved hearth design.

A digital computer program utilizing numerical approximations to the heat flow equations in three dimensions (two dimensions with radial symmetry in the third) was used to calculate unsteady state heat transfer characteristics. Stave cooling, carbon and ceramic refractories, refractory thermal property variations, salamander formation, underhearth cooling systems, and other design and operating parameters were considered in evaluating the steady and unsteady state temperature distributions in blast furnace hearths.

Résumé

On fait l' étude du flux de chaleur et de la distribution de température dans le creuset d'un haut fourneau par une simulation à l'aide d'un ordinateur. Nous considérons le creuset sans ou avec refroidissemen t afin d'obtenir l' évolution des proprietes thermiques et de sonder les besoins en matériaux réfractaire pour ameliorer le design du creuset.

Un programme d'ordinateur basé sur la méthode d'approximations numeriques aux équations tridimentionnelles de transfert de chaleur (deux dimensions rectilignes avec symétrie radiale dans la troisième direction) a été employé dans le calcul du comportement de transfert de chaleur en régime transitoire. Nous avons considéré le refroidissement des douves, l'u tilisation des réfractaires à carbone et à ceramique, la variation des propriétés thermiques des réfractaires, la formation d'un loup ferreux, d'autres designs et les paramètres d' opération dans cette évaluation des distributions des températures en régime transitoire et en régime permanent des creusets des hauts-fourneaux.     

Recovery and recrystallization of carbon steel between intervals of hot working

Abstract

Interrupted compression tests were used to study the static softening of austenite at temperatures from 780 to 1040°C. Prior straining was carried out at strain rates in the range 10^?3 to 10^?1 s^?1 and interruption strains of up to 0.41 were applied to 0.06% C, 0.42% C and 0.68% C steels, as well as to a modified 0.07% C steel containing niobium.

The results indicate that a critical strain is required for the initiation of static, i.e., classical, recrystallization after prior hot deformation. For strains inferior to this critical amount, recrystallization does not occur at all, even after holding intervals of 10⁵ s or more, and softening takes place instead entirely by static recovery. Evidence is presented for the existence of a second critical strain, about twice as large as the first, which corresponds to a point just before the peak in the flow curve. This is the critical strain for the initiation of post-dynamic (metadynamic) recrystallization. The latter process, unlike the mechanism of classical recrystallization, does not involve an incubation period.

The effects of prior strain, strain rate and temperature on the rates of these three softening mechanisms are compared. Some attention is also given to the influence of alloying elements on softening rates in austenite.

Résumé

Des essais de compression à chaud avec interruptions ont été utilisés pour etudier la restauration statique de l'austénite entre 780 et 1040°C.

La déformation initiale a été effectuée à des vitesses variant de 10^?3 à 10^?1 s^?1 et les interruptions ont eu lieu jusqu'à des déformations de 0.41. Ces essais ont été réalisés pour des aciers à 0.06%C, 0.42%C et 0.68%C, ainsi qu'à un acier à 0.07%C modifié au niobium.

Les résultats indiquent qu'une déformation critique est nécessaire pour initier après déformation la recristallisation statique, c'est-à-dire classique.

Pour des valeurs de la déformation inférieure à cette valeur critique, la recristallisation ne se produit jamasi même après des temps de maintient de l0⁵s ou plus et l'adoucissement qui apparaît est entièrement dû à une restauration statique.

La preuve est faite de l'existence d'une second déformation critique, environ deux fois plus élevée que la premiere, et qui correspond à un point situé juste avant le sommet de la courbe effort-déformation. Cette seconde déformation est la déformation critique nécessaire à l'initiation de la recristallisation post-dynamique (métarecristallisation). Contrairement au mécanisme de la recristallisation classique, cette métarecristallisation ne nécessite pas une période d'incubation.

Les auteurs comparent les effets de la déformation initiale, de la vitesse de déformation et de la température sur ces trois mécanismes d'adoucissement. Ils portent une attention spéciale à l'influence des éléments d'alliage sur l'adoucissement de l'austénite.     

Factors affecting the reoxydation of molten steel during continuous casting

Abstract

When molten steel is teemed through air, oxygen picked up by the metal from the atmosphere reacts with other elements dissolved in the steel to form products of reoxidation. Unless removed from the steel prior to solidification, this nonmetallic material will form a major source of inclusions in the final product. In this paper, factors governing the reoxidation of molten steel during continuous casting operations are examined on the basis of information obtained from plant observations, water-model studies and levitation experiments conducted with molten steel droplets.

Résumé

Lorsque le jet de coulée de l'acier passe dans l'air, des éléments de l'acier sont susceptibles de s'oxyder. Les produits d'oxydation donneraient lieu à des inclusions. Les auteurs ont étudié, à partir de la pratique et de lévitation de gouttelettes, les facteurs qui influent sur l'oxydation qui se fait au moment de la coulée continue.