Chlorination of a Scheelite-Wolframite Concentrate with Chlorine and Sulphur Dioxide

Abstract

The chlorination of a scheelite-wolframite concentrate with chlorine and sulphur dioxide was studied in order to determine the operative conditions that favor the tungsten extraction. Tests were made in a vertical reactor with a static bed and upward flow of reactive gases. Effects of the flow rates of chlorine and of sulphur dioxide, the reaction time and the reaction temperature on the tungsten extraction were analyzed. The evolution of the tungsten extraction determined in our tests was briefly explained from the volatile and non-volatile reaction products formed in each case. The main reaction products identified were WO₂Cl₂, FeCl₂, FeCl₃, CaSO₄ and CaCl₂. The mechanism and apparent activation energy of the reaction were analyzed from data obtained under non-isothermal conditions. The kinetic analysis shows that the presence of non-volatile reaction products affects the chlorination. Effects of the impurity reactivity, the ratio of tungsten-bearing minerals and the particle size of the concentrate on the chlorination were analyzed. Finally, the operative conditions that allowed a tungsten recovery near 90% were determined.

Résumé

On a étudié la chloration au chlore et au bioxyde de soufre d'un concentré de scheelite-wolframite, afin de déterminer les conditions d'opération qui favorisent l'extraction du tungstàne. On a exécuté des tests dans un réacteur vertical à lit statique, á l'ecoulement vers le haut des gaz réactifs. On a analysé l'effet, sur l'extraction du tungstène, des taux d'écoulement du chlore et du bioxyde de soufre, de la durée de réaction et de la température de réaction. On a expliqué brièvement l'évolution de l'extraction du tungstène, déterminée dans nos tests, à partir des produits de réaction volatiles et non volatiles formés dans chaque cas. Les principaux produits de' réaction identifies étaient le WO₂Cl₂, le FeCl₂, le FeCl₃, le CaSO₄ et le CaCl₂. On a analysé le mécanisme et l'énergie d'activation apparente de la réaction á partir de données obtenues so us conditions non isothermes. L'analyse cinétique montre que la préesence de produits de réaction non volatiles affecte la chloration. On a analysé les effets, sur la chloration, de la réactivité des impuretes, de la proportion des mineraux porteurs de tungstene et de la taille de particule du concentre. Finalement, on a déterminé les conditions d'opération qui permettent la récupération de pràs de 90% du tungstène.     

Modelling and simulation of vacuum filtration of ore slurry: a case study on limestone-hosted Indian uranium ore

This paper discusses the results of vacuum filtration studies carried out on a finely ground uranium ore slurry with the objective of maximizing the filtration rate. Constant-pressure experiments were carried out to determine the filtration parameters such as specific cake resistance, cake permeability and medium resistance. The experimental data were analysed using the well-known power law function of the cake-forming pressure with specific cake resistance and cake concentration. The power law model equation developed was experimentally validated and the predicted values agreed very well with the experimental findings with >95% confidence level. This study helps in design and scale-up of filtration units to be used at industrial – size.

Cet article discute des résultats d’études de filtration sous vide effectuées avec une suspension de minerai d'uranium moulu finement, ayant pour objectif de maximiser la vitesse de filtration. On a effectué des expériences à pression constante afin de déterminer les paramètres de filtration comme la résistance spécifique du comprimé, la perméabilité, la résistance moyenne etc. On a analysé les données expérimentales en utilisant la fonction bien connue de la loi exponentielle de la pression de formation du comprimé, avec sa résistance spécifique et sa concentration. On a validé expérimentalement l’équation développée pour le modèle de loi exponentielle. Les valeurs prédites s'accordaient très bien avec les données expérimentales, avec un niveau de confidence > 95%. Cette étude aide à la conception et à l'agrandissement à l’échelle d'unités de filtration pour utilisation à l’échelle industrielle     

Thermal decomposition of pyrite in fluidized beds

Abstract

The thermal decomposition of pyrite concentrate into sulphur arid synthetic pyrrhotite was investigated in bench and semi-pilot scale fluidized bed reactors fired with methane or fuel oil. The pyrite was decomposed in a bed of coarse sand and the product pyrrhotite was carried over with the fluidizing gases and separated in hot cyclones. The effects of fuel/air ratio, reactor temperature, superficial gas velocity, particle size and feed rate on the elimination of labile sulphur were studied. Conversion was enhanced by slightly reducing atmospheres, low feed rates, high gas velocities and reaction temperature (in the range 740° to 830°C). Elutriation rates of pyrrhotite particles from the fluidized bed were measured and mean residence times determined as a function of particle size and superficial gas velocity. Conversion rates are considered with regard to possible rate-controlling steps in the thermal decomposition of pyrite.

Résumé

La décomposition thermique de concentré de pyrite en soufre et en pyrrhotite synthétique a été étudiée en laboratoire et à une échelle semi-pilote dans des réacteurs à lit fluidisé chauffés avec du méthane ou de l'huile combustible. On a décomposé la pyrite sur un lit de sable grossier et la pyrrhotite produite a été entraînée avec le gaz fluidisant et séparée dans des cyclones chauds. Les effets du rapport combustible/air, de la température du réacteur, de la vitesse superficielle du gaz, de la taille des particules et de la vitesse d'alimentation sur l'élimination du soufre labile ont été étudiés. On a amélioré la transformation avec des atmosphàres légàrement réductrices, des vitesses d'alimentation lentes, de grandes vitesses pour le gaz fluidisant et une élévation de la température (dans le domaine 740 à 830°C). La vitesse d'élution des particules de pyrrhotite dans le lit fluidisé à été mesurée et on a déterminé des temps moyens de résidence en fonction de la taille des particules et de la vitesse superficielle du gaz. On a aussi étudié les changements de vitesses afin de déterminer les étapes pouvant contrôler la vi tesse de décomposition thermique de la pyrite.     

Mathematical Model of Bubble Formation at the Tuyeres of a Copper Converter

Abstract

Based on earlier observations that gas discharges from the tuyeres of a non-ferrous converter as discrete bubbles, a mathematical model has been developed to describe the dynamics of bubble formation in copper converting. The bubbles have been assumed to be spherical in shape and to grow at the tuyere tip under conditions of constant flow. The model incorporates the effects of heat transfer to the bubble, chemical reaction between the bubble and the bath and co flowing bath circulation. The model has been used to predict the concentrations of O₂ and SO₂, temperature, volume and rise velocity for the bubble as a function of time, while imposition of a detachment condition has permitted the prediction of the bubble frequency. Thus it has been shown that the oxidation reactions have little effect on the bubble formation while convective heat transfer and bath circulation have a large influence. Bath velocity acts to increase the bubble frequency while heat transfer has the opposite effect. Depending on the value of the heat-transfer coefficient employed, the model predicts the velocity of bath circulation in the vicinity of the tuyere to be between 120 and 260 cm/s. For a given bath velocity, the bubble frequency decreases with increasing air input rate. The implications of these predictions for copper converting are discussed, and it is suggested that present converter operation may be “bubble-volume“ limited.

Résumé

En se fondant sur les observations anterieures que le gaz qui s' échappe des tuyères d'un convertisseur de métaux non-ferreux est sous forme de bulles séparées, nous avons développé un modèle mathématique pour décrire la dynamique de formation des bulles dans le convertissage du cuivre. Nous avons supposé que les bulles ont une forme sphérique et qu'elles croissent à l'extrémité de la tuyère dans des conditions d' écoulement constant. Le modèle incorpore les effets du transfert de chaleur à la bulle, de la réaction chimique entre la bulle et le bain, et la circulation du bain. Le modèle a été utilisé pour prédire les concentrations de O₂ et SO₂, la température, le volume et la vitesse de montee des bulles en fonction du temps, alors que l'introduction d'une condition de séparation a permis de prédire la fréquence des bulles. Ainsi nous avons montré que les réactions d'oxydation ont peu d'effet sur la formation des bulles alors que le transfert de chaleur par convection et la circulation du bain ont une grande influence. La vitesse du bain accroît la fréquence des bulles alors que le transfert de chaleur a l'effet opposé. Dépendant de la valeur du coefficient de transfert de chaleur employé le modèle predit que la vitesse de circulation du bain dans le voisinage de la tuyère est comprise entre 120 et 260 cm/s. Pour une vitesse donnée du bain, la fréquence des bulles décroît lorsque l'on augmente le taux d'arrivée d'air. Les implications de ces predictions pour le convertissage du cuivre sont discutées et nous suggérons que l'opération actuelle des convertisseurs pourrait être limitée par le volume des bulles.     

Wear Characteristics of a Zinc-Based Alloy Compared With a Conventional Bearing Bronze Under Mixed Lubrication Conditions: Effects of Material and Test Parameters

Abstract

This study discusses the sliding wear response of a zinc-based alloy (conforming to ZA 27) in mixed lubrication conditions at different sliding pressures and speeds. A conventional bearing bronze (conforming to SAE 660) was also tested under identical test conditions for comparison purposes.

Wear rate increased with speed and pressure. Further, the zinc-based alloy attained superior wear response (less wear rate and frictional heating) than the bronze at all test speeds except prior to seizure (occurring at 7.0 MPa) at the speed of 4.60 m/s. The trend reversed in the latter case. Wear rate of the specimens also agreed with the degree of frictional heating experienced by them. A higher wear rate corresponded to larger frictional heating and vice versa. Wear behaviour of the samples improved considerably in the present study due to the presence of the oil lubricant as compared to the study in dry conditions.

Wear behaviour of the samples has been discussed in terms of the nature and response of their various microconstituents and the effects produced by varying test speeds and pressures under mixed lubrication conditions. Features of wear surfaces, subsurface regions and debris particles generated during the testing of the specimens further substantiated the observed wear behaviour of the samples and were helpful in understanding the operating wear mechanisms.

Cette étude discute de la réponse à l'usure par glissement d'un alliage à base de zinc (seconformant à ZA 27) sous condition de lubrification mixte à différentes pressions et vitesses de glissement. On a aussi évalué un bronze conventionnel pour palier (se conformant à SAE 660) sous des conditions identiques pour fin de comparaison.

Le taux d'usure augmentait avec la vitesse et la pression. De plus, l'alliage à base de zinc démontrait une réponse supérieure à l'usure (i.e. un plus bas taux d'usure et moins de chaleur de friction) en comparaison avec le bronze, à toutes les vitesses d'évaluation sauf juste avant qu'il ne grippe (ce qui se produit à 7.0 MPa), à la vitesse de 4.60 m/s; la tendance s'inversait dans ce dernier cas. Le taux d'usure des spécimens était aussi en accord avec leur degré d'échauffement par friction, i.e. un plus haut taux d'usure correspondait à un échauffement plus important par friction et vice-versa. Le comportement d'usure des échantillons s'est amélioré considérablement dans la présente étude à cause de la présence de l'huile lubrifiante en comparaison avec l'étude en condition sèche.

On a discuté du comportement d'usure des échantillons en termes de la nature et de la réponse de leurs divers micro constituants ainsi que des effets produits en variant la vitesse et la pression d'évaluation sous condition de lubrification mixte. Les caractéristiques des surfaces d'usures, des régions sous la surface ainsi que des débris de particules générés lors de l'évaluation des spécimens ont davantage établi le comportement observé d'usure des échantillons et étaient utiles pour comprendre les mécanismes d'usure en opération.     

A Perspective of Research and Development in North American Steelmaking

Abstract

A thermomechanical processing technique is used to improve austenitic Hadfield Mn-steel wear properties. ASTM A128 grade C steel billets were sized and multi-pass hot rolled. Rolling has been successfully carried out up to an 80% reduction in thickness on four passes in the temperature range 1200 to 800 °C. The inter-pass time ranged between 9 to 13 seconds. The steel was then solution treated at 900, 1000 and 1100°C for 30 min. at temperature. Austenite grain size was measured and the carbide volume fraction was evaluated. The austenitic grains of the as-cast structure are surrounded by a network of carbides. The carbides have a lamellar structure and are richer in Cr and Mn than the austenitic grains. Austenitizing at 1100 °C was the optimum to dissolve the network of carbides. However, solution treatment at the higher temperature coarsens the austenite grains while decreasing the carbide volume fraction. By contrast, hot rolling creates finer grains and signficantly reduces the carbide content. Furthermore, hot rolling followed by solution treatment further decreases the carbide content and distributes them homogeneously. This process has a positive effect on both the mechanical and wear properties. High reductions by hot rolling of the Hadfield steel creates both deformation bands and a twinned structure. These twinning boundaries are considered as slip obstacles to provide strengthening. A thick sheet martensitic structure is created accompanying twinning. Moreover, solution treatment of the hot deformed steel leads to the formation of a thin martensitic structure.

On utilise une technique de traitement thermomécanique pour améliorer les propriétés d'usure de l'acier austénitique au manganèse. On a coupé et laminé à chaud par passes multiples des billettes d'acier ASTM A 128, de grade C. On a effectué le laminage, avec succès, jusqu'à une réduction de 80% de l'épaisseur, avec quatre passes dans la gamme de température de 1200 à 800 °C. La durée entre les passes était de 9 à 13 secondes. On a ensuite effectué un traitement de mise en solution à 900, 1000 et 1100°C, pendant 30 minutes à la température donnée. On a mesuré la taille de grain de l'austénite et l'on a évalué la fraction volumique du carbure. Les grains d'austénite de la structure brute de coulée sont entourés d'un réseau de carbures. Les carbures ont une structure lamellaire et sont plus riches en Cr et en Mn que les grains d'austénite. La température optimale d'austénitisation pour la dissolution du réseau de carbures était de 1100 °C. Cependant, le traitement de mise en solution à cette température plus élevée produit un grossissement des grains d'austénite tout en diminuant la fraction volumique de carbure. En contraste, le laminage à chaud crée des grains plus fins et réduit significativement le contenu en carbure. En outre, le laminage à chaud suivi par le traitement de mise en solution diminue encore plus le contenu de carbures et distribue ceux-ci de façon homogène. Ce traitement a un effet positif tant sur les propriétés mécaniques que sur les propriétés d'usure. Des réductions élevées par laminage à chaud de l'acier austénitique au manganèse créent des bandes de déformations ainsi qu'une structure maclée. Ces joints de grains de macle sont considérés comme des obstacles au glissement, fournissant ainsi un renforcement. Une feuille épaisse à structure martensitique, accompagnant le maclage, est ainsi créée. De plus, le traitement de mise en solution de l'acier chaud déformé mène à la formation d'une structure martensitique mince.     

CHARACTERIZATION OF OXIDE AND HYDROXIDE IN MgCl2-NaCl MELTS

Abstract

This work is part of a research program whose aim is to develop an electroanalytical technique to determine the amount of dissolved oxide and hydroxide in industrial electrolytes for the electrowinning of Mg. The systems studied were mixtures of MgCl₂ and NaCl ranging from pure MgCl₂ melts to melts containing 10 mole% MgCl₂ and 90 mole% NaCl. MgO and MgOHCl were added to these melts at different temperatures. Voltammetric measurements were performed before and after the addition of MgO or MgOHCl. Melt samples for chemical analysis were withdrawn before and after the additions of these compounds as a function of time after addition. The quenched melt samples were analyzed by carbothermal reduction analysis and by the acid consumption method to obtain the O₂- and OH- contents of the melt. Linear sweep voltammetry was performed with a sweep rate of 200 mV&#x00₂F;sec in the cathodic and anodic potential regions to detect the concentration of dissolved MgOHCl and MgO, respectively. The results indicate a linear relation between MgO and MgOHCl concentrations and the peak current densities for the electrochemical reactions of the dissolved MgO and MgOHCl species in the melt, respectively. The results are promising in view of the possibility to detect voltammetrically in situ both dissolved MgOHCl and MgO in the electrolyte during Mg production.

Ce travail fait partie d’un programme de recherche dont le but est de développer une technique électro-analytique pour la détermination de la quantité d’oxyde et d’hydroxyde dissous dans les électrolytes industriels d’extraction électrolytique du Mg. Les systèmes étudiés consistaient en mélanges de MgCl₂ et de NaCl allant de bains purs de MgCl₂ à des bains contenant 10% mole de MgCl₂ et 90% mole de NaCl. On ajoutait du MgO et du MgOHCl à ces bains à différentes températures. On a effectué des mesures de voltampérométrie avant et après l’addition du MgO ou du MgOHCl. On a retiré des échantillons de bains, pour analyse chimique, avant et après l’addition de ces composés en fonction du temps après l’addition. On a analysé les échantillons de bains trempés par réduction carbothermique et par la méthode de consommation d’acide pour obtenir la teneur en O₂- et en OH- du bain. On a effectué des mesures par voltampérométrie à balayage linéaire avec une vitesse de balayage de 200 mV&#x00₂F;s dans les régions de potentiel cathodique et anodique pour détecter la concentration de MgOHCl et de MgO dissous, respectivement. Les résultats indiquent une relation linéaire entre les concentrations de MgO et de MgOHCl et les pics de densité de courant des réactions électrochimiques des espèces MgO et MgOHCl dissoutes dans le bain, respectivement. Les résultats sont prometteurs en ce qui a trait à la possibilité de détecter directement par voltampérométrie tant le MgOHCl que le MgO dissous dans l’électrolyte lors de la production de Mg.     

Rate of Transfer of Manganese Across Metal-Slag Interface and Interfacial Phenomena

Abstract

The rate of oxidation of manganese in liquid iron by oxidizing slag and rate of reduction of manganese oxide in liquid slag by liquid iron were measured at 1873 K. At the same time the liquid iron-slag interface was observed by an X-ray TV and the shape of iron drops was photographed on a film to determine the interfacial tension. From the results of the rate measurements it was found that the reaction proceeded rapidly over the initial period in the case of oxidation, but not in the case of reduction. The rate of reaction was analysed on the assumption that the reaction was controlled by simultaneous transport of manganese and oxygen. The change of interfacial tension during a run was small in spite of the transfer of surface active oxygen.

Résumé

Les vitesses d'oxydation et de réduction du manganèse ont été mesurées à l'interface métal-scorie d'un bain de fonte liquide à 1873 K. Simultanément, l'interface fonte-scorie a été observée à l'aide d'une caméra de télévision R-X et les goutelettes de fonte photographiées afin de déterminer la tension interfaciale. A partir des résultats des vitesse de réaction, il s'est avéré que la réaction s'effectue rapidement lors de la période initiale d'oxydation, mais non lors de la réduction. La vitesse de la réaction a été analysée en supposant qu'elle était contrôlée par le transport simultané du manganèse et de l'oxygène. Le changement de tension interfaciale lors d'un essai étai faible malgré le transfert d'oxygène actif en surface.     

The effect of the mill speed on the comminution of zircon sand

Abstract

The effect of mill speeds on energy consumption and size reduction of zircon in a ball mill was investigated by comminution tests. Optimum grinding conditions, except mill speed, were determined prior to the investigation for the effect of mill speed.

The experimental results indicate that the most efficient grinding of hard minerals, such as zircon, occurs at around the critical speed of the mill when it is completely filled with zircon, balls and water in the proportion of 1:1:1 by apparent volume.

It is also found that the size-distribution parameter α and the energy-size parameter β of the product ground at around the critical speed of the mill are nearly equal, where abrasion and chipping rather than impact may be the predominant comminution mechanism.

Résumé

Par des essais de comminution, l'effet de la vitesse d'un broyeur à boulet, sur la consommation d'energie et la réduction de taille de la zircone ont été étudies. Avant ces essais les conditions optimales de broyage, sauf la vitesse, ont été determinées.

Les résultats expérimentaux indiquent que Ie broyage le plus efficace pour un minerai dur comme la zircone se produit pour une vitesse voisine de la vitesse critique du broyeur et quand it est complétement rempli de zircone, de boulets et d'eau dans une proportion volumétrique apparente de 1:1:1.

Il apparaît également que le parametré de granulométrie α et la paramétre déceivant l'énergie et la taille βdu produit broyé à une vitesse voisine de la vitesse critique sont sensiblement égaux; agrave; ce moment, les principaux mécanismes de comminution sont l'abrasion et l'écaillement plutôt que le choc.     

Texture and anisotropy of zirconium in relation to plastic deformation

Abstract

Possible modes of plastic deformation of tubular materials are analyzed generally. Based on symmetry considerations applied to known textures of zirconium wire and strip, textures of zirconium tubes are predicted as resulting from a wide range of deformation modes. This is made possible by focusing on the main feature of texture, Le., the orientation distribution of basal poles. A relation between texture and the mechanical anisotropy of zirconium is developed, and rules are suggested for softening and hardening caused by texture change. Experimentally, Zircaloy tubes were deformed by various techniques. The resulting textures were determined by X-ray diffraction and the mechanical anisotropy by Knoop-hardness measurement. Each determination is condensed into two representative figures, one describing the type of texture or anisotropy and the other describing the sharpness of texture or the degree of deviation from isotropy.

The experiments verify the predicted relation between type of texture and mechanical anisotropy, and also indicate how degree of anisotropy depends on sharpness of texture. Changes in texture are investigated in relation to plastic deformation, and further refined rules are derived for the direction and rate of these changes. The initially predicted textures are concluded to be stable, i.e., they are reached only after a certain degree of deformation. Zircaloy tubes of three different textures were subjected to tensile testing, closed-end burst testing and open-end burst testing. The observed texture-softening phenomenon corroborates the rules suggested and is considered to commonly occur, as opposed to texture hardening, which requires special combinations of texture and testing method.

Résumé

Les différents modes de déformation plastique possibles dans les tubes ont été analysés d'une façon générale. En se basant sur des considérations de symétrie appliquées aux textures connues pour le zirconium en fil et en bandes, la texture des tubes de zirconium resultant de divers modes de déformation a été prédite. Ceci est possible si l'on tient surtout compte des principes de la texture, c'est à dire, la distribution des orientations des poles de base. Une relation entre la texture et l'anisotropie du zirconium est développée, et des règles sont suggérées pour l'adoucissement et la consolidation dûs à un changement de texture. Dans les expériences, les tubes de zirconium ont été déformés par plusieurs modes. Les textures résultantes ont été déterminées par la diffraction des rayons-X. et l'anisotropie par des mesures de dureté Knoop. Chacune de ces déterminations est représentée dans deux figures, l'une décrivant le genre de texture ou anisotropie, l'autre décrivant la netteté de la texture ou l'écart du caractère isotrope. Les expériences vérifient la relation prévue entre la texture et l'anisotropie. Les changements de texture sont examinés en fonction de la déformation plastique, et d'autres règles plus rigoureuses sont dérivées pour la direction et la vitesse de ces changements. On conc1ut que les textures prévues initialement sont stables, c'est à dire qu'elles ont lieu apres une certaine déformation. Des tubes de Zircalloy de trois textures différentes ont été soumis à des essais detraction, des essais d'éc1atement à extrémités ouvertes ou fermées.

Le phénomène d'adoucissement observé, causé par la texture, est en accord avec les règles suggérées et est généralement présent, ce qui n'est pas le cas du durcissement causé par la texture, durcissement nécessitant des combinaisons spéciales de texture et de méthodes d'essai.     

Modification of Roll Pass Design of Low Pearlite,Fine-Grained Sheet Steel Using Numerical Modeling and Processing Maps

Abstract

The main objective of this pass design is to achieve fine-grained structure with high strength properties and good ductility for 2.0 mm thickness steel sheet on a six stand finishing mill. Numerical modeling is used to evaluate the different rolling parameters while processing maps are used to determine a workability “window” in which dynamic recrystallization must occur.

The existing rolling parameters would not lead to a dynamically recrystallized structure. The proposed technique retains the sequence of reduction in thickness at the working temperatures, while it diminishes the rotational speed of the first stand and consequently all the other stands. The first stand is proposed to rotate with 25 rpm at 7.2 s-1 rate of deformation. The final rotational roll speed would be 177 rpm at stand no. 6 with 83.4 s-1 rate of deformation at 850 °C. Rolling force and torque needed in the proposed technique are lower than those in the existing ones at most of the passes. The proposed technique saves energy as it reduces the power consumption.

Le principal objectif de cette conception de passe de laminoir est d'obtenir une structure à grain fin avec des propriétés de résistance élevée et une bonne ductilité pour une tôle d'acier d'une épaisseur de 2.0 mm, sur un laminoir finisseur à six cages. On utilise la modélisation numérique pour évaluer les différents paramètres de laminage alors qu'on utilise les plans de formage pour déterminer une "fenêtre” de fabricabilité dans laquelle doit se produire une recristallisation dynamique.Les paramètres actuels de laminage ne peuvent conduire à une structure dynamiquement recristallisée. La technique proposée retient la séquence de réduction en épaisseur aux températures d'opération, tout en diminuant la vitesse de rotation de la première colonne et, par conséquent, de toutes les autres colonnes. On propose que la rotation de la première colonne soit de 25 rpm, avec un taux de déformation de 7.2 s-1. La vitesse du dernier rouleau serait de 177 rpm à la colonne no. 6, avec un taux de déformation de 83.4 s-1, à 850 °C. La force de laminage et le moment de torsion nécessaires pour la technique proposée sont plus bas que ceux qui existent déjà pour la plupart des passes. La technique proposée conserve l'énergie puisqu'elle réduit la consommation de pouvoir.     

Recovery of indium powders from indium chloride solutions by cementationa

A three-step, batch type recovery method was developed to produce indium powders from dilute indium chloride solutions prepared by dissolving indium tin oxide (ITO) electrodes from waste liquid crystal display (LCD) panels in concentrated hydrochloric acid (HCl) solutions. A 5–L batch process was used with individual experimental parameters for cementation, such as temperature and time, which were varied to optimise their effects on the physicochemical properties and purity of the recovered indium powders and the recovery rate. A validation experiment was performed by preparing indium bearing solutions in a 5–180 min kinetic study of indium cementation with aluminium in aqueous HCl solutions at 65°C. The indium powders obtained from the cementation processes were further characterised using various analytical tools, such as ICP/AES, X-ray diffraction (XRD), and scanning electron microscope-energy dispersive X-ray spectroscopy (SEM-EDS). Cementation at 60°C for 10 min resulted in the optimal process efficiency, with a recovery rate and indium purity of 70 and 99·8% respectively. On a développé une méthode de récupération discontinue à trois étapes afin de produire des poudres d'indium à partir de solutions diluées de chlorure d'indium préparées en dissolvant des électrodes d'oxyde d'indium et d'étain (ITO), provenant de panneaux d'affichage à cristaux liquides (LCD) de rebut, dans des solutions concentrées d'acide chlorhydrique (HCl). On a utilisé un procédé discontinu de 5 L avec paramètres expérimentaux individuels de cémentation, comme la température et la durée, que l'on variait afin d'optimiser leurs effets sur les propriétés physicochimiques et la pureté des poudres d'indium récupérées et sur le taux de récupération. On a effectué une expérience de validation en préparant des solutions porteuses d'indium dans une étude cinétique de 5 à 180 min de cémentation de l'indium avec de l'aluminium, dans des solutions aqueuses d'HCl à 65°C. On a ensuite caractérisé les poudres d'indium obtenues à partir des procédés de cémentation en utilisant divers outils analytiques, comme l'ICP/AES, la diffraction des rayons X (XRD), et la microscope électronique à balayage—spectroscopie à dispersion d'énergie (SEM-EDS). On a obtenu le rendement optimal du procédé par cémentation à 60°C pendant 10 min, avec un taux de récupération et une pureté de l'indium de 70 et 99·8%, respectivement.     

Liquid Steel Transfer — The Delivery of Quality

Abstract

During recent years, in parallel with developments in high-speed casting, there have been increasing demands for improved steel quality. These demands are being met by advances in our knowledge of the chemical, physical and thermal interactions between steel, gas, slag and refractory phases which take place within individual reactors as well as during transfer operations. Transfer operations must be precisely controlled, otherwise they become destroyers of quality, and quality achieved within one reactor can be lost during transfer to the next. © 2000 Canadian Institute of Mining and Metallurgy. Published by Elsevier Science Ltd. All rights reserved.

Résumé

Au cours des dernières années, en parallèle avec 1es développements de la coulée haute vitesse, il y a eu une demande croissante de l'amélioration de la qualité de l'acier. On satisfait à ces demandes par l'avancement de notre connaissance des interactions chimiques, physiques et thermiques entre les phases d'acier, de gaz, de scories et de ráfractaires qui se produisent à l'interieur des récteurs individuels aussi bien que lors des opérations de transfert. On doit controler précisément les opérations de transfert, autrement elles deviennent des destructrices de qualité. En eilet, la qualité obtenue à l'intérieur d'un réacteur peut etre perdue lors du transfert vers le réacteur suivant. © 2000 Canadian Institute of Mining and Metallurgy. Published by Elsevier Science Ltd. All rights reserved     

Reduction of chromites in methane-hydrogen mixtures-chromium sesquioxide

Abstract

Chromium sesquioxide can be reduced to chromium metal or carbide by mixtures of hydrogen and methane. The mechanisms and conditions for these reactions have been determined using simulation of the effects of methane cracking by controlled addition of carbon. The work forms a basis for the investigation of reduction of chromite ores by coke-oven or natural gas. This reaction is of economic interest because the oxygen tends to be removed as carbon monoxide, thus retaining the reducing potential of the effluent gases. Kinetic data were collected from temperature programmed experiments to which a model, based upon the shrinking-core concept for gas-solid reactions, was found to be applicable. The solid-solid carbon-chromium oxide reduction is the sum of three chemical reactions and is catalyzed by hydrogen, although carbon monoxide diminishes the effect of this catalysis below 1200°C.

Résumé

Le sesquioxide de chrome peut être réduit à l'état de métal chrome ou de carbure de chrome par les mélanges hydrogène-méthane. Les mécanismes et les conditions de ses réactions ont éte déterminés en utilisant la simulation des effets de «cracking» du méthane par des additions contrôlées de carbone. Ce travail est primordial pour l'étude de la réduction des minerais de chromite pour les gaz des fours à coke ou le gaz naturel. Cette réaction a un intérèt économique parce que l'oxygène tend à être éliminé sous forme monoxyde de carbone, qui conserve le potentiel réducteur des gaz qui s'echappent. Les données cinetiques ont été collectées à partir des expériences avec programmation de la température pour lesquelles un modèle fonde sur l'hypothèse d'une réduction à symétrie sphérique pour les réactions solide-gaz s'est révélé applicable. La réaction solide-solide de réduction de l'oxyde de chrome par le carbone est la somme de trois réactions chimiques et est catalysée par l'hydrogène bien que l'oxyde de carbone diminue son effet catalytique pour des températures inferieures à 1200°C.     

Heat flow in blast furnace hearths

Abstract

Heat flow and temperature distribution in iron blast furnace hearths has been investigated using a digital computer implemented simulation. Furnace hearths, with and without underhearth cooling, have been simulated to provide dynamic thermal response characteristics and to explore refractory material requirements for improved hearth design.

A digital computer program utilizing numerical approximations to the heat flow equations in three dimensions (two dimensions with radial symmetry in the third) was used to calculate unsteady state heat transfer characteristics. Stave cooling, carbon and ceramic refractories, refractory thermal property variations, salamander formation, underhearth cooling systems, and other design and operating parameters were considered in evaluating the steady and unsteady state temperature distributions in blast furnace hearths.

Résumé

On fait l' étude du flux de chaleur et de la distribution de température dans le creuset d'un haut fourneau par une simulation à l'aide d'un ordinateur. Nous considérons le creuset sans ou avec refroidissemen t afin d'obtenir l' évolution des proprietes thermiques et de sonder les besoins en matériaux réfractaire pour ameliorer le design du creuset.

Un programme d'ordinateur basé sur la méthode d'approximations numeriques aux équations tridimentionnelles de transfert de chaleur (deux dimensions rectilignes avec symétrie radiale dans la troisième direction) a été employé dans le calcul du comportement de transfert de chaleur en régime transitoire. Nous avons considéré le refroidissement des douves, l'u tilisation des réfractaires à carbone et à ceramique, la variation des propriétés thermiques des réfractaires, la formation d'un loup ferreux, d'autres designs et les paramètres d' opération dans cette évaluation des distributions des températures en régime transitoire et en régime permanent des creusets des hauts-fourneaux.     

Recovery and recrystallization of carbon steel between intervals of hot working

Abstract

Interrupted compression tests were used to study the static softening of austenite at temperatures from 780 to 1040°C. Prior straining was carried out at strain rates in the range 10^?3 to 10^?1 s^?1 and interruption strains of up to 0.41 were applied to 0.06% C, 0.42% C and 0.68% C steels, as well as to a modified 0.07% C steel containing niobium.

The results indicate that a critical strain is required for the initiation of static, i.e., classical, recrystallization after prior hot deformation. For strains inferior to this critical amount, recrystallization does not occur at all, even after holding intervals of 10⁵ s or more, and softening takes place instead entirely by static recovery. Evidence is presented for the existence of a second critical strain, about twice as large as the first, which corresponds to a point just before the peak in the flow curve. This is the critical strain for the initiation of post-dynamic (metadynamic) recrystallization. The latter process, unlike the mechanism of classical recrystallization, does not involve an incubation period.

The effects of prior strain, strain rate and temperature on the rates of these three softening mechanisms are compared. Some attention is also given to the influence of alloying elements on softening rates in austenite.

Résumé

Des essais de compression à chaud avec interruptions ont été utilisés pour etudier la restauration statique de l'austénite entre 780 et 1040°C.

La déformation initiale a été effectuée à des vitesses variant de 10^?3 à 10^?1 s^?1 et les interruptions ont eu lieu jusqu'à des déformations de 0.41. Ces essais ont été réalisés pour des aciers à 0.06%C, 0.42%C et 0.68%C, ainsi qu'à un acier à 0.07%C modifié au niobium.

Les résultats indiquent qu'une déformation critique est nécessaire pour initier après déformation la recristallisation statique, c'est-à-dire classique.

Pour des valeurs de la déformation inférieure à cette valeur critique, la recristallisation ne se produit jamasi même après des temps de maintient de l0⁵s ou plus et l'adoucissement qui apparaît est entièrement dû à une restauration statique.

La preuve est faite de l'existence d'une second déformation critique, environ deux fois plus élevée que la premiere, et qui correspond à un point situé juste avant le sommet de la courbe effort-déformation. Cette seconde déformation est la déformation critique nécessaire à l'initiation de la recristallisation post-dynamique (métarecristallisation). Contrairement au mécanisme de la recristallisation classique, cette métarecristallisation ne nécessite pas une période d'incubation.

Les auteurs comparent les effets de la déformation initiale, de la vitesse de déformation et de la température sur ces trois mécanismes d'adoucissement. Ils portent une attention spéciale à l'influence des éléments d'alliage sur l'adoucissement de l'austénite.     

The Petch relation and grain boundary hardening

Abstract

The effect of the grain size and solute content on the microhardness of iron-tin alloys has been investigated. It was found that the values of the Petch slope as derived from the hardness dependence on grain size, shows an unusual dependence on tin content. A good correlation between the Petch slope and grain boundary hardening was observed; both increased with tin additions. The results are rationalized in terms of Li's model of dislocation generation from grain boundary ledges and also Hart's grain boundary phase transformation model.

Résumé

L'auteur a étudié les effets de la taille du grain et de la concentration en soluté sur la microdureté d'alliages fer-étain. Les valeurs de la pente de Petch, telles que déduites de l'influence de la taille du grain sur la dureté, révèlent une variation inhabituelle en fonction de la concentration en étain. Une corrélation acceptable entre la pente de Petch et le durcissement des joints de grains est observée, les deux augmentant avec l'addition d'étain. Ces résultats sont interprétés selon le modèle de Li, qui suppose l'émission de dislocations à partir des marches des joints de grains, et aussi selon le modèle de Hart, qui fait appel à une transformation de phase du joint de grain.     

Dissolution Kinetics of Ulexite in Aqueous Edta Solutions

Abstract

The dissolution kinetics of ulexite in aqueous disodium Ethylene Diamine Tetra Acidic Acid (EDTA) solutions has been investigated with respect to the effects of particle size, solution concentration, pH of solution, calcination temperature and reaction temperature. The rate of the reaction decreases as the particle size and pH of the solution increase, but the rate increases with an increase in both solution concentration and reaction temperature. The sample pre-heated at 140 °C has the highest dissolution rate. The rate of the dissolution can be expressed according to the unreacted shrinking core model with changing fluid phase concentration.

On a étudié la cinétique de dissolution de l'ulexite dans des solutions de bisodium aqueux d'EDTA, en rapport avec l'effet de taille de particule, de concentration et de pH de la solution ainsi que des températures de calcination et de réaction. Le taux de réaction diminue avec une augmentation de la taille de particule et de pH de la solution, mais le taux augmente avec une augmentation de la concentration de la solution et de la température de réaction. L'échantillon préchauffé à 140 °C a le plus haut taux de dissolution. On peut exprimer le taux de dissolution d'après le modèle de rétrécissement du noyau non réagi en fonction du changement de concentration de la phase fluide.     

Grain boundaries in recrystallization

Abstract

In this brief survey, the theoretical models for nucleation of new grains in annealed cold-worked metals are reviewed in the light of recent researches in the author's laboratory. The importance of strain-induced boundary migration is gradually emerging. The role of vacancies in enhancing the mobility of grain boundaries is reviewed, and this leads on to a survey of the influence of pores in particular, and precipitates more generally, on the motion of grain boundaries. Areas of ignorance which call for further experiments are pointed out.

The influence of dissolved impurities on grain-boundary motion is excluded from this survey.

Résumé

Dans cette brève synthèse, l'auteur passe en revue, à la lumière de récents travaux effectués dans son laboratoire, les modèles théoriques de germination des grains dans les métaux déformés à froid et recuits. L'importance d'une migration des joints induite par la déformation émerge graduellement. Le rôle des lacunes, qui favorisent la mo bilite des joints de grains, est passé en revue et ceci conduit à une étude de l'influence des pores en particulier, et de précipités plus généralement, sur la migration des joints de grains. L'auteur souligne les domaines, où notre ignorance nécessite d'autres expériences. Est exclue de cette synthèse l'influence des impuretés dissoutes sur la migration des joints de grains.     

Effects of some solid lubricant particles and their concentration in oil towards controlling wear performance of leaded tin bronze bush

Abstract

This investigation pertains to the examination of the sliding wear response of a leaded tin bronze bush as influenced by the changing content of solid lubricants such as talc, graphite and lead when mixed with oil. Wear tests were performed to determine the wear loss, frictional heating and friction coefficient. Characteristics of wear surfaces and subsurface regions threw light on the operating wear mechanisms and further substantiated the observed wear behaviour. The solid lubricants were noted to significantly influence the overall performance of the samples wherein their content produced an identical trend while their type and structure showed a mixed effect.

Cette étude a trait à l’examen de la réponse à l’usure par glissement d’une bague de palier de bronze à l’étain au plomb, influencée par la teneur changeante de lubrifiants solides comme le talc, le graphite ou le plomb, lorsque mélangés avec de l’huile. On a effectué des essais d’usure afin de déterminer la vitesse d’usure, le chauffage dû à la friction et le coefficient de friction. Les caractéristiques des surfaces d’usure et des régions sous la surface ont permis de comprendre les mécanismes d’usure et de substantifier davantage le comportement à l’usure observé. On note que les lubrifiants solides influencent significativement le rendement global des échantillons là où leur concentration produisait une tendance identique alors que leur type et leur structure montraient un effet mixte.