Carbothermic reduction of siderite ore with high phosphorus content reinforced by sodium carbonate

Abstract

A dressing metallurgy flowsheet, which consists of a sodium salt added reinforced reductive roasting–magnetic separation process, is proposed in this paper for the treatment of siderite ore with high phosphorous content. The sodium salt added reinforcement reductive roast process is accomplished by the addition of an appropriate amount of sodium carbonate, which reacts with SiO₂ preventing its counter catalysis on FeO, thereby increasing the reducing reaction activity of FeO and further reinforcing the reduction of siderite. The phosphorus compounds were not reduced in the low temperature reduction process and remained as fluorapatite in the gangue phases. Ultrafine grinding–magnetic separation of magnetic minerals is an efficient way to obtain qualified iron concentrate. It is therefore believed that, with an emphasis on the effect of Na₂CO₃ and its dosage on the reduction of siderite, the technology proposed in this paper will be of benefit to the exploitation of similar refractory iron ore.

Dans cet article, on propose un schéma de procédé de préparation métallurgique, consistant d’un procédé de grillage réductif renforcé d’un sel de sodium ajouté et de séparation magnétique, pour le traitement du minerai de sidérite à haute teneur en phosphore. Le procédé de grillage réductif à renforcement de sel de sodium ajouté est accompli par l’addition d’une quantité appropriée de carbonate de sodium qui réagit avec le SiO₂, empêchant sa ‘contre catalyse’ du FeO, augmentant donc l’activité de la réaction de réduction du FeO et renforçant davantage la réduction de la sidérite. Les composés de phosphore n'étaient pas réduits dans le procédé de réduction à basse température et restaient sous forme de fluorapatite dans les phases de gangue. Le broyage utrafin-séparation magnétique des minéraux magnétiques est une manière efficace d’obtenir un concentré qualifié de fer. En portant l’emphase sur l’effet du Na₂CO₃ et de son dosage sur la réduction de la sidérite, on croit donc que la technologie proposée dans cet article bénéficiera l’exploitation de minerai similaire de fer réfractaire.     

Reduction behaviour of rice husk ash for preparation of high purity silicon

Abstract

The reduction of rice husk ash (RHA) silica for the preparation of high purity silicon was studied using magnesium as the reducing agent. Composite magnesium–RHA pellets with magnesium content varying 0–25 wt-% in excess of stoichiometry requirement were made and heated in the temperature range of 600–900°C under flowing argon. It was found through differential thermal analysis and temperature profile recording that the reaction of RHA silica with magnesium was triggered at ～575°C. Quantitative X-ray diffraction analyses of the reduction products showed that both initial magnesium content of the pellets and the reduction dwell temperature had a significant influence on the yield of silicon. In this study, a charge with 5 wt-% magnesium in excess of the stoichiometric amount at a reduction temperature of 900°C gave a maximum silicon yield.

On a étudié la réduction de la silice de cendre de balle de riz (RHA) dans la préparation de silicium à haut degré de pureté en utilisant du magnésium comme agent de réduction. On a fabriqué des boulettes composites de magnésium-RHA avec une teneur en magnésium variant de 0 à 25% en poids en excès des besoins de la stoechiométrie et on les a chauffées dans la gamme de température de 600 à 900°C sous un flux d’argon. On a trouvé, par analyse thermique différentielle (DTA) et par enregistrement du profil de température, que la réaction de la silice de RHA avec le magnésium était déclenchée à environ 575°C. Des analyses quantitatives par XRD des produits de réduction ont montré que tant la teneur initiale en magnésium des boulettes que la température de maintien de la réduction avaient une influence importante sur le rendement en silicium. Dans cette étude, une charge avec 5% en poids d’excès de magnésium sur la quantité stoechiométrique à la température de réduction de 900°C donnait un rendement maximal de silicium.     

Reduction roasting of high iron bearing zinc calcine for recovery of zinc and iron

High iron bearing zinc sulphide ore is an important resource for zinc, and the reserve is very great in the world. It is very difficult to effectively obtain zinc and iron from the source by traditional technology. In this study, a novel method was proposed for recovery of zinc and iron from high iron bearing zinc calcine, and the key procedure, reduction roasting, was investigated. The effects of CO concentration, CO₂ concentration, temperature and time on reduction roasting were studied respectively. The experimental results show that the content of soluble zinc and magnetic susceptibility reached 91·15% and 4·1×10^?4 m³ kg^?1 under the optimum conditions respectively. About 90%Zn and 9·5%Fe were dissolved from the reduction roasted zinc calcine by low acid leaching, and simultaneously, 84·3%Fe was recycled to the iron concentrate containing iron of 53·2% from zinc leaching residue by low intensity magnetic separation.

Le minerai de sulfure de zinc à haute teneur en fer est une ressource importante du zinc et il en existe une grande quantité dans le monde. Il est très difficile d’obtenir efficacement le zinc et le fer de cette source par la technologie traditionnelle. Dans cette étude, on propose une nouvelle méthode pour la récupération du zinc et du fer à partir de produit calciné de zinc à haute teneur en fer, et on examine la procédure clef, le grillage réducteur. On a étudié respectivement les effets de la concentration de CO, de la concentration de CO₂, de la température et de la durée sur le grillage réducteur. Les résultats expérimentaux montrent que la teneur en zinc soluble et la susceptibilité magnétique atteignaient respectivement 91·15% et 4·1×10^?4 m³ kg^?1 en conditions optimales. Environ 90% du Zn et 9·5% du Fe étaient dissous à partir du produit calciné de zinc de grillage réducteur par lessivage à acide faible, et simultanément, 84·3% du Fe était recyclé en concentré de fer contenant 53·2% de fer à partir du résidu de lessivage du zinc par séparation magnétique à faible intensité.     

Solid structural changes during the reduction of iron oxides

Abstract

The changes in the solid structure, i.e., grain size, shape and pore structure, during the reduction. of reagent-grade hematite to iron by CO?CO₂ mixtures at temperatures between 725 and 925°C were investigated. The reduction of hematite to wustite was found to produce little structural change. In contrast, three mechanisms of structural change occurred during the reduction of wustite to iron. These included the thermal sintering of the wustite, the growth of fibrous iron filaments from the partially reduced wustite grains, and the sintering or “coarsening” of the reduced iron. A quantitative model for the sintering of the wustite is described.

The effects of the structural changes on the reduction kinetics are reviewed. The sintering of the wustite reduced the over-all rate of reduction; the growth of the fibrous iron increased the rate of reduction. The sintering of the iron had little effect on the kinetics. The interaction between the sintering of the wustite and the growth of the fibrous irons, which change the character of the reduction from nontopochemical to topochemical, is also discussed.

Résumé

Les variations de la structure solide, i.e., la grosseur du grain, la forme et la porosité,ont été étudiées au moment de la réduction d'hématite en fer, dans des mélanges de CO?CO₂ aux températures comprises entre 725 et 925°C. La réduction de l'hématite à la wustite s'accompagne d'un léger changement de structure. Au contraire, trois mécanismes de changements structuraux se sont présentés au cours de la réduction de la wustite en fer. Ce sont: le frittage thermique de la wustite, la croissance des filaments fibreux de fer provenant des grains de wustite partiellement réduits et aussi le frittage du fer réduit. Un modéle quantitatif décrit Ie frittage de la wustite.

Les effets des variations structurales sur la cinétique de réduction sont revisés. Le frittage de la wustite a diminué le taux de réduction, alors que la croissancé du fer fibreux a augmente ce taux. Le frittage du fer a un effet minime sur la cinétique. L'interaction entre le frittage de la wustite et la croissance des fibres de fer fait varier Ie caractère de la réduction, de non-topochimique à topochimique.     

The use of a stabilized zirconia cell to study the fluidized bed reduction of iron ore

Abstract

The use of stabilized zirconia cells to follow the progress of the batch reduction of iron ore by hydrogen in a fluidized bed was investigated. The reduction patterns of the several ores examined were very similar, showing clearly the step-wise progression of particles from hematite through magnetite and wustite to iron. Use has been made of this pattern for the timed extraction of particles from the bed for morphological studies of the reaction. By using multiple taps on the zirconia cell, the approach of the gas phase to equilibrium with solids in the bed could be examined. It was also possible to measure the oxygen potential of the solid material in the bed by stopping the reaction. No variation in composition with height was found within experimental error.

Résumé

L'utilisation de cellules de zircone stabilisées pour suivre 1' évolution de la réduction de minerais de fer par l'hydrogène dans un lit fluidisé a été etudiée. Les étapes de réduction de différents minerais examinés étaient très similaires, montrant clairement les étapes correspondant à la réduction de l'hématite puis de la magnétite et de la wiistite jusqu'au fer. Cette progression a permis l'extraction programmée de particules du lit afin de faire des études morphologiques de la réaction. Grâce aces cellules de zircone il a été possible de mesurer l' évolution de la composition de la phase vers l' équilibre avec les solides du lit fluidisé. Il à été aussi possible de mesurer le potentiel d'oxygène des solides du lit en stoppant la réaction. Aucune variation dans la composition avec la hauteur n'a été trouvée, aux erreurs experiméntales près.     

The sticking of iron ore during reduction by hydrogen in a fluidized bed

Abstract

Sticking of particles in the fluidized bed reduction of iron ore at temperatures above 600°C will occur whenever clean iron surfaces impinge. Some as-received ores are sufficiently dirty that iron-iron contact does not take place at low temperatures. However, as the temperature of reduction is raised, there is an increasing tendency for the iron nucleating on the surface of particles to grow into nodules which pierce the dirt film allowing iron-iron contact and hence sticking. Silica in the surface film stops iron nucleation near the surface of particles and thereby prevents iron nodule formation. Ores with silicacontaining coatings can be fully reduced in a fluidized bed at temperatures up to 840°C without sticking.

Résumé

Les particules de minerai de fer au cours de la réduction en lit fluidisé aux températures supérieures à 600°C ont tendance à s'agglomerer aussitôt que des surfaces de fer sont en contact. Quelques minerais utilisés comme tels sont suffisamment impurs pour que le contact fer sur fer ne se produise pas aux basses températures. Cependant, quand la température est élevée, la nucléation du fer a la surface des particules se prolonge par la formation des modules qui percent la couche d'impuretés et favorisent l'agglomération. La présence de silice dans la couche superficielle empêche la nucléation du fer au voisinage de la surface donc aussi la formation de modules de fer. Les minerais contenant de la silice peuvent être réduits complètement dans un lit fluidise a des températures allant jusqu'à 840°C sans s'agglomérer     

Reduction of Ilmenite Concentrates By Methane Containing Gas,Part II: Effects of Preoxidation and Sintering

Abstract

Reduction of preoxidized and sintered ilmenite concentrates by a CH₄-H₂-Ar gas mixture was investigated in a laboratory fixed bed reactor in temperature programmed experiments. The ilmenite concentrates contained different concentrations of TiO2 (55.6-71.5wt%) and iron oxide (Fe_total 14.5-28.2wt%).

In the reduction of ilmenite by hydrogen, during ramping reduction temperature from 230 to 1100 °C, only iron oxides were reduced to metallic iron and the reduction was not complete. The reduction of titania was slight. The ilmenite concentrates were reduced by CH₄-H₂-Ar gas mixture to metallic iron and titanium oxycarbide. Preoxidation and sintering of ilmenite concentrates changed their phase composition and caused a sharp decrease in specific surface area of raw materials and an increase in carburization temperature. Sintering also increased the metallization temperature of iron.

On a étudié, dans un reacteur de laboratoire à lit fixe, lors d'experiences à températures programmées, la réduction de concentrés d'ilménites pre-oxydes et frittes par un melange de gaz de CH4-H2-Ar. Les concentres d'ilmenites contenaient differentes concentrations de TiO2 (55.6-71.5% en poids) et d'oxyde de fer (Fetotal 14.5-28.2% en poids).

Au cours de la réduction de l'ilménite par l'hydrogene, lors de l'augmentation de temperature de réduction de 230 à 1100 °C, seuls les oxydes de fer etaient réduits en fer métallique et, de plus, la réduction n'était pas compléte. La réduction du dioxyde de titane était faible. Les concentrés d'ilménites ont été réduits par le mélange de gaz CH₄-H₂-Ar en fer métallique et en oxycarbure de titane. La préoxydation et le frittage des concentrés d'ilménite ont change leur composition de phase et ont causé une diminution marquée de la surface specifique des matériaux bruts ainsi qu'une augmentation de la température de cémentation. Le frittage a également augmenté la température de métallisation du fer.     

Factors Affecting the Coercivity and Remanence of Artificial Magnetite

Abstract

Sintered chemically pure ferric oxide particles were reduced by a mixture of carbon monoxide and carbon dioxide in a rotary drum furnace. The product was then concentrated in a Davis tube and from the hysteresis loop of the minus 65 plus 100 mesh particles of the magnetics, the volume average remanence and coercivity were obtained.

It was found that the residual magnetism and coercive force of the particles were inversely proportional to the reduction temperature. Reduction time had no significant effect on either coercive force or residual magnetism.

Résumé

Des particules d'oxyde ferrique aggloméré, chimiquement pur, ont été réduites par un mélange de monoxyde de carbone et bioxyde de carbone dans un four à tambour rotatif. Le produit fut ensuite concentré dans un tube Davis, et la rémanence moyenne par volume ainsi que la coercivité furent obtenues du cycle d'hystérésis des particules entre 65 et 100 mailles de la fraction magnétique.

On trouva que la magnétisme residuel et la force coercive des particules étaient inversement proportionnels à la température de réduction. La durée de la réduction n'avait guère d'effet sur la force coercive ou Ie magnétisme résiduel.     

Role of ferric ions in bioleaching of uranium from low tenor Indian ore

Abstract

The role of biogenic ferric ions in leaching of uranium by Acidithiobacillus ferrooxidans from a low grade ore of Turamdih mines, India, has been investigated. Using the enriched culture of bacterial isolate containing mainly A. ferrooxidans from the source mine water, biorecovery of 98% uranium at 20% (w/v) pulp density, pH 1·7 and 35°C temperature using <76 μm particles in 40 days was obtained. The effect of temperature on bioleaching of uranium showed higher recovery at 35°C. The uranium dissolution was facilitated by iron(III) available in the leach liquor because of bacterial oxidation of pyrite and chemical dissolution of magnetite present in the ore under acidic conditions. The biogenically generated Fe(III) ions enhanced uranium dissolution from the uraninite ore. The bioleaching of uranium appeared to follow a chemical control kinetic model with the reaction of lixiviant, Fe(III) and acid on the surface of the solid in the temperature range 25–35°C. Phase identification by XRD and the study of surface morphology of the ore and the residue by SEM study corroborated the above mechanism of uranium leaching.

On a étudié le rôle des ions ferriques biogènes dans la lixiviation de l’uranium par A. ferrooxidans d’un minerai pauvre des mines de Turamdih, en Inde. En utilisant la culture enrichie d’isolat bactérien contenant principalement Acidithiobacillus ferrooxidans de l’eau de source de la mine, on a obtenu une biorécupération de 98% d’uranium à 20% de densité de la pulpe (poids/vol), avec un pH de 1·7 et une température de 35°C, en utilisant des particules de <76 μm, en 40 jours. L’effet de la température sur la biolixiviation de l’uranium montrait une récupération plus élevée à 35°C. La dissolution de l’uranium était facilitée par le fer(III), disponible dans la liqueur de lixiviat grâce à l’oxydation bactérienne de la pyrite et à la dissolution chimique de la magnétite présentes dans le minerai en conditions acides. Les ions Fe(III) engendrés biogéniquement augmentaient la dissolution de l’uranium du minerai d’uraninite. La biolixiviation de l’uranium semblait suivre un modèle cinétique à contrôle chimique avec la réaction du lixiviant – Fe(III) et de l’acide à la surface du solide dans la gamme de température de 25 à 35°C. L’identification de phase par XRD et l’étude de la morphologie de la surface du minerai et du résidu par étude au SEM corroboraient le mécanisme ci-dessus de lixiviation de l’uranium.     

Influence of process parameters on reduction contours during production of ferrochromium in submerged arc furnace

Abstract

Contours of iso‐reduction lines in the submerged arc furnace producing ferrochromium were constructed using a mathematical model based on the temperature profile inside the furnace and the kinetics of reduction of chromite ores. The location and the contours of the iso‐reduction lines are significantly influenced by the temperature profile in the furnace. From the model, it is found that ～27% of the furnace volume is used for the reduction of the ore. The contours are significantly influenced by the degree of pre‐reduction of the ore charged into the furnace. The iso‐reduction lines can be used for enhancing the efficiency of the process and for better control of the operation exploiting options such as intelligent distribution of charge materials over the charge bed.

On a construit des lignes de contour d’iso‐réduction dans le four à arc submergé produisant du ferrochrome en utilisant un modèle mathématique basé sur le profil de température à l’intérieur du four et sur la cinétique de réduction des minerais de chromite. La localisation et les contours des lignes d’iso‐réduction sont influencés significativement par le profil de température dans le four. À partir du modèle, on a trouvé qu’environ 27% du volume du four était utilisé pour la réduction du minerai. Les contours sont influencés significativement par le degré de pré‐réduction du minerai chargé dans le four. On peut utiliser les lignes d’iso‐réduction pour augmenter le rendement du traitement et pour mieux contrôler les options d’exploitation de l’opération comme la distribution intelligente des matériaux de la charge sur le lit de chargement.     

Furnace refractory practice at Manitoba Rolling Mills

Abstract

Iron is considered as an impurity in aluminium alloys due to its detrimental impact on strength and ductility. Much work has been carried out to reduce the iron levels in recycled aluminium alloys. In this investigation, the influence of Mn additions for reducing the Fe content in an Al–Si alloy has been studied. The experimental results and thermodynamic calculations revealed that a reduction of up to 62%Fe content can be achieved. The major mechanism of iron removal is the formation of the primary α-AlFeMnSi particles when held at lower temperatures. The characteristics and compositions of these particles, which settle on the bottom of the alloy melts, were confirmed using optical microscopy and X-ray diffraction techniques.

Dans les alliages d’aluminium, le fer est considéré comme une impureté en raison de son effet négatif sur la résistance et la ductilité. Des travaux ont été menés pour réduire la quantité de fer dans les alliages d’aluminium recyclé. L’étude menée porte sur l’influence des ajouts de manganèse visant à réduire la teneur en fer dans un alliage Al–Si. Les résultats expérimentaux et les calculs thermodynamiques ont révélé qu’il est possible d’atteindre une réduction de 62% de la teneur en Fe. Le principal mécanisme d’extraction du fer est la formation de particules d’alliage α-AlFeMnSi lorsque des températures plus basses sont maintenues. Les caractéristiques et la composition de ces particules, qui se déposent au bas des fontes d’alliage, ont été confirmées à l’aide de microscopie optique et de techniques de diffraction des rayons X.     

Preparation of metallic iron powder from red mud by sodium salt roasting and magnetic separation

Red mud has become one kind of the most hazardous solid waste. In order to recover iron from red mud, the technology of sodium salt roasting and magnetic separation was developed. During the reduction roasting, additives (Na₂SO₄ and CaO) reacted with SiO₂ and Al₂O₃ of red mud, forming NaO?Al₂O₃?2SiO₂, 2CaO?Al₂O₃?SiO₂, 12CaO?7Al₂O₃, CaO?Al₂O₃ and 2CaO?SiO₂, which ameliorates the separation between iron and alumina during magnetic separation. Meanwhile, sodium sulphate also improved the growth of iron grains, increasing the iron grade and iron recovery. The metallic iron powder obtained contained 90·28 wt-%TFe (representing a metallisation degree of 94·87 wt-%) at 92·14 wt-% iron recovery under the optimum conditions, which can be briquetted as a burden material for steel making by electric arc furnace to replace scrap.

La boue rouge est considérée comme l’un des déchets solides les plus nocifs. Afin de récupérer le fer de la boue rouge, on a développé la technologie du grillage au sel de sodium et de la séparation magnétique. Lors du grillage réducteur, les produits d’addition (Na₂SO₄ et CaO) réagissent avec le SiO₂ et l’Al₂O₃ de la boue rouge, formant le NaO?Al₂O₃?2SiO₂, le 2CaO?Al₂O₃?SiO₂, le 12CaO?7Al₂O₃, le CaO?Al₂O₃ et le 2CaO?SiO₂, ce qui améliore la séparation entre le fer et l’oxyde d’aluminium lors de la séparation magnétique. Pendant ce temps, le sulfate de sodium a également amélioré la croissance des grains de fer, augmentant ainsi la qualité du fer et sa récupération. La poudre de fer métallique obtenue contenait 90·28% en poids de FeT (représentant un degré de métallisation de 94·87% en poids), avec une récupération de fer de 92·14% en poids en conditions optimales, qui pouvait être mis en briquettes comme matériau de lit de fusion pour la production de l’acier au four électrique à arc pour remplacer la ferraille.     

ELECTROLYSIS OF LIQUID FAYALITE SLAGS

Abstract

Electrolysis of liquid fayalite slags was carried out at 1250 °C using a liquid copper cathode and an inert platinum anode. At the cathode, iron precipitated with a current efficiency above 55%. The cathodic current efficiency decreased with increasing slag magnetite content. When Cu₂O was added to the slag, metallic copper was formed at the cathode with current efficiencies as high as 80%. In terms of the recovery of copper from metallurgical slags, electrolysis would be most beneficial for slags with a high dissolved copper content such as slags from direct to copper smelting.

Over time, the cell voltage decreased due to an increase in the effective surface area of the anode and also partly due to an increase in the slag conductivity due to increasing magnetite content. The increasing anode area was caused by a magnetite-rich deposit forming around the platinum wire anode.

On a effectué l’électrolyse de laitiers de fayalite liquides à 1250 °C en utilisant une cathode en cuivre liquide et une anode inerte en platine. Le fer était précipité à la cathode avec un rendement du courant au-dessus de 55%. Le rendement du courant cathodique diminuait avec une augmentation de la teneur en magnétite du laitier. Lorsqu’on ajoutait du Cu₂O au laitier, du cuivre métallique se formait à la cathode avec des rendements de courant aussi élevés que 80%. En ce qui concerne la récupération du cuivre à partir des laitiers métallurgiques, l’électrolyse serait davantage bénéfique pour des laitiers ayant une teneur élevée en cuivre dissous, comme des laitiers du traitement direct de fonte de cuivre.

Avec le temps, le voltage de la cellule diminuait à cause d’une augmentation de la superficie efficace de l’anode et aussi en partie à cause d’une augmentation de la conductivité du laitier résultant d’une augmentation de la teneur en magnétite. L’augmentation de la superficie de l’anode était causée par un dépôt riche en magnétite qui se formait autour du fil en platine de l’anode.     

Kinetic analysis of silicothermic process under flowing argon atmosphere

The Pidgeon process, a silicothermic reduction of calcined dolomite under vacuum, is the dominant process to make magnesium metal. Experimental data from Morsi et al., were utilised for kinetics analysis of silicothermic reduction of calcined dolomite under argon atmosphere. A number of kinetic models were assessed to evaluate the rate-controlling step in the process. The results suggest that the reaction is controlled by the solid-state diffusion of reactants with the Jander and Ginstling–Brounshtein model providing the best representation of the process kinetics. Mass transfer effects of magnesium vapour from the surface to the bulk gas phase was also analysed. These results suggest that gas–film mass transfer is not the limiting step of the kinetics. Pore diffusion through briquettes is postulated to have some effect on the kinetics but solid-state diffusion is the major rate-limiting step.

Le procédé Pidgeon, une réduction silicothermique sous vide de dolomie calcinée, est le procédé dominant de production de magnésium métallique. On a utilisé les données expérimentales de Morsi et al pour l’analyse cinétique de la réduction silicothermique de dolomie calcinée sous une atmosphère d’argon. On a estimé un certain nombre de modèles cinétiques afin d’évaluer l’étape du procédé cinétiquement limitante. Les résultats suggèrent que la diffusion à l’état solide des réactants contrôle la réaction, le modèle de Jander et Ginstling-Brounshtein fournissant la meilleure représentation de la cinétique du procédé. On a également analysé les effets du transfert massique de la vapeur de magnésium de la surface vers le c?ur de la phase gazeuse. Ces résultats suggèrent que le transfert de masse gaz-film n’est pas l’étape limitante de la cinétique. On postule que la diffusion par pore à travers les briquettes a un certain effet sur la cinétique mais la diffusion à l’état solide est l’étape majeure cinétiquement limitante.     

Effect of impurity additions on the remanence and coercivity of reduced hematite ores

Abstract

Synthetic ores of pure ferric oxide, and ferric oxide with additions of CaO, SiO₂, MnO₂ and TiO₂ were made up by sintering the mixtures at 1100°C. Subsequent crushing, grinding and screening yielded ores with particle between 149 and 208 microns. The ores were reduced to mainetite between 500°C and 1000°C in a CO-CO₂ atmosphere.

The coercive force and remanence of the reduced ores were determined using a 60 cps hysteresis loop tracer. The addition of CaO decreased the coercive force and remanence of the reduced ore as compared to pure magnetite, whereas the effects of the other additions were not significant. Explanations for the findings are offered.

Résumé

Des minerais synthétiques d'oxide ferrique pur et d'oxyde ferrique additionné de CaO, SiO₂, MnO₂ et TiO₂ ont été élaboré par frittage à 1100°C. Après broyage et tamisage, la tail1e des particules de minerai s' échelonnait de 149 à 208 microns. Ces minerais étaient ensuit réduits en magnétite à des températures variant de 500 à 1000°C en atmosphére de CO-CO₂.

La force coercitive et la rémanence des minerais ainsi réduits, on été mesurees it 60 htz sur une boucle d'hystérésis. On a trouvé qu'une addition de CaO fait diminuer la force coercitive et la rémanence des minerais réduits par rapport à la magnétite pure, tan dis que les effets des autres additions sont sans signification. Une interprétation des résultats est donnee.     

HYDROGEN REDUCTION OF INDUSTRIAL NICKEL OXIDES

Abstract

Thermal gravimetric analysis (TGA) was used to investigate the reduction behaviour of three industrial nickel oxides. Both isothermal and non-isothermal reduction experiments were carried out. Due to the low BET surface area and relative dense structure of the Goro NiO, it was reduced at a slower rate than both Tokyo NiO and Sinter 75 which were the two other nickel oxides investigated.

In the temperature range from 400 to 600 °C, the rate of reduction increased with increasing temperature and increasing hydrogen pressure. Microscopic analysis showed that in this temperature range, the reaction followed the topochemical model. When the temperature was increased to 700 and 800 °C, the reduction rate decreased noticeably. Microscopy showed inner bands of metallization inside the outer metallic rim seen at lower temperatures indicating partial blockage of the interface between the reacted and unreacted NiO core.

On a utilisé la gravimétrie thermique (TGA) pour étudier le comportement de réduction de trois oxydes de nickel industriels. On a effectué des expériences de réduction isotherme et non isotherme. À cause de la faible superficie BET et de la structure relativement dense du NiO Goro, celui-ci était réduit à un taux plus faible que le NiO Tokyo ou le Sinter 75, les deux autres oxydes de nickel étudiés.

Dans la gamme de température de 400 à 600 °C, le taux de réduction augmentait avec une augmentation de la température et une augmentation de la pression d’hydrogène. L’analyse de microscopie a montré que dans cette gamme de température, la réaction suivait le modèle topochimique. Lorsqu’on augmentait la température à 700 et à 800 °C, le taux de réduction diminuait significativement. La microscopie a montré des bandes internes de métallisation à l’intérieur de la bordure métallique externe observée aux plus basses températures, indiquant un blocage partiel de l’interface entre la région ayant réagi et le noyau de NiO n’ayant pas réagi.     

Lateritic saprolite leaching in concentrated magnesium chloride media

Magnesium chloride brines present a number of potential advantages for the processing of lateritic saprolite ores for nickel production. Concentrated MgCl₂ solutions enhance the activity of acid used, allow atmospheric leaching at elevated temperature, and inhibit magnesium dissolution, which reduces acid consumption and increases metal selectivity. However, with a chloride based leach it is economically requisite to recover hydrochloric acid, conventionally accomplished by pyrohydrolysis. This work was performed in conjunction with a novel flowsheet for the processing on saprolite ores, which recovers HCl by the precipitation and subsequent decomposition of magnesium hydroxychlorides, alleviating some of the issues with pyrohydrolysis. Leaching experiments have been conducted in concentrated MgCl₂ brines, up to 4·5 m, to determine the amenable process conditions and explore the kinetics of the process. It was determined that >95% extraction of metals was possible using both aqueous and gaseous HCl, while suppressing the dissolution of Mg from the ore.

Les saumures de chlorure de magnésium présentent un nombre d’avantages potentiels dans le traitement des minerais de saprolite latéritique pour la production du nickel. Les solutions concentrées de MgCl₂ augmentent l’activité de l’acide utilisé, permettent la lixiviation atmosphérique à haute température, et inhibent la dissolution du magnésium, ce qui réduit la consommation d’acide et augmente la sélectivité du métal. Cependant, avec une lixiviation à base de chlorure, on doit récupérer l’acide hydrochlorique pour raison économique, ce qui est accompli conventionnellement par pyrohydrolyse. On a effectué ce travail en conjonction avec un nouveau schéma de procédé pour le traitement des minerais de saprolite, lequel récupère le HCl par précipitation et par décomposition subséquente des hydroxychlorures de magnésium, ce qui atténue certains des problèmes reliés à la pyrohydrolyse. On a effectué des expériences de lixiviation dans des saumures concentrées de MgCl₂, jusqu’à 4·5 m, afin de déterminer les conditions favorables du procédé et d’explorer la cinétique du procédé. On a déterminé qu’il était possible d’extraire >95% des métaux en utilisant à la fois le HCl aqueux et gazeux, tout en supprimant la dissolution du Mg du minerai.     

Removal of Cr(VI) ions from aqueous solution using foundry waste material: Kinetic and equilibrium studies

Abstract

In the present paper, Cr(VI) ions removal from aqueous solutions by adsorption on waste mould (green) sand was investigated. Waste mould sand is byproduct of the grey iron foundry. Batch adsorption test was carried out to determine the removal characteristic for Cr(VI) ions from aqueous solution. The obtained results are promising in the use of waste mould sand as an efficient low cost and non-conventional adsorbent for the removal of Cr(VI) ions from aqueous solutions. The second order kinetics produced better fitting of results in terms of correlation coefficient which suggests that the adsorption kinetics of Cr(VI) ions on the waste mould sand followed the second order kinetic model. In the isotherm studies, Freundlich, Langmuir, Dubin–Radushevich and Redlich–Peterson isotherm models were applied and it was determined that the experimental data conformed to Langmuir isotherm model.

Dans cet article, on examine l’enlèvement d’ions Cr(VI) de solutions aqueuses par adsorption sur le sable (vert) à moulage résiduel. Le sable à moulage résiduel est un sous-produit de la fonderie de fonte grise. On a effectué un essai d’adsorption en discontinu afin de déterminer les caractéristiques d’enlèvement des ions Cr(VI) d’une solution aqueuse. Les résultats obtenus sont prometteurs quant à l’utilisation du sable à moulage résiduel comme adsorbant efficace non conventionnel et à faible coût pour l’enlèvement des ions Cr(VI) de solutions aqueuses. La cinétique de second ordre a produit un meilleur ajustement des résultats par rapport au coefficient de corrélation, ce qui suggère que la cinétique d’adsorption des ions Cr(VI) sur le sable à moulage résiduel suivait le modèle cinétique de second ordre. Dans les études d’isothermes, on a appliqué les modèles d’isotherme de Freundlich, Langmuir, Dubin, – Radushevich et Redlich – et de Peterson et l’on a déterminé que les données expérimentales se conformaient au modèle d’isotherme de Langmuir.     

Solid state and smelting reduction of Panzhihua ilmenite concentrate with coke

Abstract

Solid state and smelting reduction of ilmenite is an important process of upgrading ilmenite to high titania feedstock. In this study, an ilmenite concentrate supplied by Panzhihua Iron and Steel (Group) Co. was first reduced at solid state in an electric resistance furnace, followed by smelting reduction in an induction furnace. The effects of reducing agent (carbon) amount on the chemical composition of the solid state reduction sample and the titania slag reduced from them, were analysed. It was found that the metallisation of iron in the solid reduction samples and the grade of titania slag generally increased with increasing carbon amount from 8 to 12%, and then remained constant when the carbon amount was increased above 12%. The content of metallic iron in the titania slag increased with increasing carbon amount, because the slag viscosity and liquidus temperature increased with decreasing FeO content. It was also known that the content of Ti₂O₃ increased with decreasing the content of FeO in the slag. Some metallic iron particles were found in the high titania slag samples. The liquidus lines and viscosity of the slag were calculated using FactSage to explain the experimental results.

La réduction à l’état solide et par fusion de l’ilménite est un procédé important de valorisation de l’ilménite pour charge d’alimentation à haute teneur en dioxyde de titane. Dans cette étude, un concentré d’ilménite fourni par le groupe Panzhihua Iron and Steel Co. a d’abord été réduit à l’état solide dans un four électrique à résistances, suivi par la réduction par fusion dans un four à induction. On a analysé les effets de la quantité d’agent réducteur (carbone) sur la composition chimique de l’échantillon de réduction à l’état solide et de la scorie de dioxyde de titane réduit à partir de lui. On a trouvé que la métallisation du fer dans les échantillons de réduction solide et la qualité de la scorie de dioxyde de titane augmentaient généralement avec une augmentation de la quantité de carbone de 8 à 12%, et ensuite restaient constantes lorsqu’on augmentait la quantité de carbone au-delà de 12%. La teneur en fer métallique dans la scorie de dioxyde de titane augmentait avec l’augmentation de la quantité de carbone, parce que la viscosité de la scorie et la température du liquidus augmentaient avec une diminution de la teneur en FeO. On sait également que la teneur en Ti₂O₃ augmentait avec une diminution de la teneur en FeO dans la scorie. On a trouvé quelques particules de fer métallique dans les échantillons de scorie à haute teneur en dioxyde de titane. On a calculé les lignes de liquidus et la viscosité de la scorie en utilisant FactSage pour expliquer les résultats expérimentaux.     

A review of problems in iron-ore reduction by solid-state processes

Abstract

This paper reviews the problems involved in iron-ore reduction by the solid-state processes. These processes are mostly limited to a 700°–1100°C temperature range. Because the rate of chemical reactions is relatively slow within this range compared with the blast furnace in which temperatures are much higher, the kinetics of iron-ore reduction assumes great importance.

The generally accepted reduction mechanisms are described as well as the reaction rate-controlling steps and chemical equilibria. With this background as a basis for comparison, the problems in reduction of iron ores in rotary kilns using solid fuel reductants, in shaft furnaces using gaseous reductants and in fluid-bed reactors are analyzed. This analysis shows that rotary kilns present the most problems and fluid-bed reactors the least.

Résumé

Dans cet article on examine les problèmes que comportent les procédés de réduction de minerai de fer à l'etat solide. Pour de tels procédés, la réduction se fait, en général, entre 700 et 1100°C. Les vitesses de réaction sont lentes à de telles températures, en comparaison avec le haut-fourneau où la température est beau coup plus elevee; de ce fait, la cinétique de la réduction du minerai de fer revêt une grande importance.

On décrit les méchanismes de la réduction généralement acceptés, les étapes limitant la vitesse de réaction et les équilibres chimiques, on examine les problèmes que comportent la réduction de minerais de fer en four rotatif avec agents reducteurs solides, en fours verticaux avec gaz réducteurs et en réacteurs à lits fluidisés. De cela on conclut que ce sont les fours rotatifs qui présentent le plus de problèmes et les réacteurs à lits fluidisés qui en présentent le moins.