Solid-State Synthesis of Te-Doped Mg<Subscript>2</Subscript>Si

Te-doped Mg₂Si (Mg₂Si:Te _m , m = 0, 0.01, 0.02, 0.03, 0.05) alloys were synthesized by a solid-state reaction and mechanical alloying. The electronic transport properties (Hall coefficient, carrier concentration, and mobility) and thermoelectric properties (Seebeck coefficient, electrical conductivity, thermal conductivity, and figure of merit) were examined. Mg₂Si was synthesized successfully by a solid-state reaction at 673 K for 6 h, and Te-doped Mg₂Si powders were obtained by mechanical alloying for 24 h. The alloys were fully consolidated by hot-pressing at 1073 K for 1 h. All the Mg₂Si:Te _m samples showed n-type conduction, indicating that the electrical conduction is due mainly to electrons. The electrical conductivity increased and the absolute value of the Seebeck coefficient decreased with increasing Te content, because Te doping increased the electron concentration considerably from 10¹⁶ cm⁻³ to 10¹⁸ cm⁻³. The thermal conductivity did not change significantly on Te doping, due to the much larger contribution of lattice thermal conductivity over the electronic thermal conductivity. Thermal conduction in Te-doped Mg₂Si was due primarily to lattice vibrations (phonons). The thermoelectric figure of merit of intrinsic Mg₂Si was improved by Te doping.     

Thermoelectric Properties of Sb-Doped Mg<Subscript>2</Subscript>Si<Subscript>0.3</Subscript>Sn<Subscript>0.7</Subscript>

Mg₂(Si_0.3Sn_0.7)_1−y Sb _y (0 ≤ y ≤ 0.04) solid solutions were prepared by a two-step solid-state reaction method combined with the spark plasma sintering technique. Investigations indicate that the Sb doping amount has a significant impact on the thermoelectric properties of Mg₂(Si_0.3Sn_0.7)_1−y Sb _y compounds. As the Sb fraction y increases, the electron concentration and electrical conductivity of Mg₂(Si_0.3Sn_0.7)_1−y Sb _y first increase and then decrease, and both reach their highest value at y = 0.025. The sample with y = 0.025, possessing the highest electrical conductivity and one of the higher Seebeck coefficient values among all the samples, has the highest power factor, being 3.45 mW m⁻¹ K⁻² to 3.69 mW m⁻¹ K⁻² in the temperature range of 300 K to 660 K. Meanwhile, Sb doping can significantly reduce the lattice thermal conductivity (κ _ph) of Mg₂(Si_0.3Sn_0.7)_1−y Sb _y due to increased point defect scattering, and κ _ph for Sb-doped samples is 10% to 20% lower than that of the nondoped sample for 300 K < T < 400 K. Mg₂(Si_0.3Sn_0.7)_0.975Sb_0.025 possesses the highest power factor and one of the lower κ _ph values among all the samples, and reaches the highest ZT value: 1.0 at 640 K.     

Preparation and Thermoelectric Properties of La-Doped SrTiO<Subscript>3</Subscript> Ceramics

Single-phase polycrystalline La _x Sr_1−x TiO₃ (x = 0, 0.04, 0.06, 0.08, and 0.12) ceramics were prepared by the conventional solid-state reaction method using high-activity hydroxides as the raw materials. The electrical conductivity of all the samples increased with increasing x value and decreased with measurement temperature, while the thermal conductivity decreased with increasing x value and measurement temperature. The La_0.12Sr_0.88TiO₃ sample showed the lowest thermal conductivity of 2.45 W m⁻¹ K⁻¹ at 873 K and the largest ZT of 0.28 at 773 K. The present work revealed that hydroxides with high activity as raw materials are beneficial to improve the thermoelectric properties, especially to decrease the thermal conductivity.     

Preparation and Thermoelectric Properties of LaGd<Subscript>1+<Emphasis Type="Italic">x</Emphasis></Subscript>S<Subscript>3</Subscript> and SmGd<Subscript>1+<Emphasis Type="Italic">x</Emphasis></Subscript>S<Subscript>3</Subscript>

Thermoelectric materials are attractive since they can recover waste heat directly in the form of electricity. In this study, the thermoelectric properties of ternary rare-earth sulfides LaGd_1+x S₃ (x = 0.00 to 0.03) and SmGd_1+x S₃ (x = 0.00 to 0.06) were investigated over the temperature range of 300 K to 953 K. These sulfides were prepared by CS₂ sulfurization, and samples were consolidated by pressure-assisted sintering to obtain dense compacts. The sintered compacts of LaGd_1+x S₃ were n-type metal-like conductors with a thermal conductivity of less than 1.7 W K⁻¹ m⁻¹. Their thermoelectric figure of merit ZT was improved by tuning the chemical composition (self-doping). The optimized ZT value of 0.4 was obtained in LaGd_1.02S₃ at 953 K. The sintered compacts of SmGd_1+x S₃ were n-type hopping conductors with a thermal conductivity of less than 0.8 W K⁻¹ m⁻¹. Their ZT value increased significantly with temperature. In SmGd_1+x S₃, the ZT value of 0.3 was attained at 953 K.     

Thermoelectric Properties of In<Subscript>0.3</Subscript>Ga<Subscript>0.7</Subscript>N Alloys

We report on the experimental investigation of the potential of InGaN alloys as thermoelectric (TE) materials. We have grown undoped and Si-doped In_0.3Ga_0.7N alloys by metalorganic chemical vapor deposition and measured the Seebeck coefficient and electrical conductivity of the grown films with the aim of maximizing the power factor (P). It was found that P decreases as electron concentration (n) increases. The maximum value for P was found to be 7.3 × 10⁻⁴ W/m K² at 750 K in an undoped sample with corresponding values of Seebeck coefficient and electrical conductivity of 280 μV/K and 93␣(Ω cm)⁻¹, respectively. Further enhancement in P is expected by improving the InGaN material quality and conductivity control by reducing background electron concentration.     

Development of (Bi,Sb)<Subscript>2</Subscript>(Te,Se)<Subscript>3</Subscript>-Based Thermoelectric Modules by a Screen-Printing Process

In major applications, optimal power will be achieved when thermoelectric films are at least 100 μm thick. In this paper we demonstrate that screen-printing is an ideal method to deposit around 100 μm of (Bi,Sb)₂(Te,Se)₃-based films on a rigid or flexible substrate with high Seebeck coefficient value (90 μV K⁻¹ to 160 μV K⁻¹) using a low-temperature process. Conductive films have been obtained after laser annealing and led to acceptable thermoelectric performance with a power factor of 0.06 μW K⁻² cm⁻¹. While these initial material properties are not at the level of bulk materials, the complete manufacturing process is cost-effective, compatible with large surfaces, and affords a mass-production technique.     

Improvement of Thermoelectric Power Factor of Hydrothermally Prepared Bi<Subscript>0.5</Subscript>Sb<Subscript>1.5</Subscript>Te<Subscript>3</Subscript> Compared with its Solvothermally Prepared Counterpart

We report on the successful hydrothermal synthesis of Bi_0.5Sb_1.5Te₃, using water as the solvent. The products of the hydrothermally prepared Bi_0.5 Sb_1.5Te₃ were hexagonal platelets with edges of 200–1500 nm and thicknesses of 30–50 nm. Both the Seebeck coefficient and electrical conductivity of the hydrothermally prepared Bi_0.5Sb_1.5Te₃ were larger than those of the solvothermally prepared counterpart. Hall measurements of Bi_0.5Sb_1.5Te₃ at room temperature indicated that the charge carrier was p-type, with a carrier concentration of 9.47 × 10¹⁸ cm⁻³ and 1.42 × 10¹⁹ cm⁻³ for the hydrothermally prepared Bi_0.5Sb_1.5Te₃ and solvothermally prepared sample, respectively. The thermoelectric power factor at 290 K was 10.4 μW/cm K² and 2.9 μW/cm K² for the hydrothermally prepared Bi_0.5Sb_1.5Te₃ and solvothermally prepared sample, respectively.     

Influence of Doping on Structural and Thermoelectric Properties of AgSbSe<Subscript>2</Subscript>

A series of samples with nominal compositions of AgSb_1−x Sn _x Se₂ (with x = 0.0, 0.1, 0.2, and 0.3) and AgSbSe_2−y Te _y (with y = 0.0, 0.25, 0.5, 0.75, and 1.0) were prepared. The crystal structure of both single crystals and polycrystalline samples was analyzed using x-ray and neutron diffractometry. The electrical conductivity, thermal conductivity, and Seebeck coefficient were measured within the temperature range from 300 K to 700 K. In contrast to intrinsic AgSbSe₂, samples doped with Sn and Te exhibit apparent semiconducting properties (E _g = 0.3 eV to 0.5 eV), lower electrical conductivity, and higher values of the Seebeck coefficient for a small amount of Sn (x = 0.1). Further doping leads to decrease of the thermoelectric power and increase of the electrical conductivity. In order to explain electron transport behavior observed in pure and doped AgSbSe₂, electronic structure calculations were performed by the Korringa–Kohn–Rostoker method with coherent potential approximation (KKR–CPA).     

Thermoelectric Properties of Half-Heusler Bismuthides ZrCo<Subscript>1−<Emphasis Type="Italic">x</Emphasis></Subscript>Ni<Subscript><Emphasis Type="Italic">x</Emphasis></Subscript>Bi (<Emphasis Type="Italic">x</Emphasis> = 0.0 to 0.1)

The usefulness of half-Heusler (HH) alloys as thermoelectrics has been mainly limited by their relatively large thermal conductivity, which is a key issue despite their high thermoelectric power factors. In this regard, Bi-containing half-Heusler alloys are particularly appealing, because they are, potentially, of low thermal conductivity. One such a material is ZrCoBi. We prepared pure and Ni-doped ZrCoBi by a solid-state reaction. To evaluate thermoelectric potential we measured electrical resistivity (ρ = 1/σ) and thermopower (σ) up to 1000 K and thermal conductivity (κ) up to 300 K. Our measurements indicate that for these alloys resistivity of approximately a few mΩ cm and thermopower larger than a hundred μV K⁻¹ are possible. Low κ values are also possible. On the basis of these data we conclude that this system has a potential to be optimized further, despite the low power factors (α ² σT) we have currently measured.     

Thermoelectric Properties of Zr<Subscript>3</Subscript>Mn<Subscript>4</Subscript>Si<Subscript>6</Subscript> and TiMnSi<Subscript>2</Subscript>

The Seebeck coefficient, electrical resistivity, and thermal conductivity of Zr₃Mn₄Si₆ and TiMnSi₂ were studied. The crystal lattices of these compounds contain relatively large open spaces, and, therefore, they have fairly low thermal conductivities (8.26 Wm⁻¹ K⁻¹ and 6.63 Wm⁻¹ K⁻¹, respectively) at room temperature. Their dimensionless figures of merit ZT were found to be 1.92 × 10⁻³ (at 1200 K) and 2.76 × 10⁻³ (at 900 K), respectively. The good electrical conductivities and low Seebeck coefficients might possibly be due to the fact that the distance between silicon atoms in these compounds is shorter than that in pure semiconductive silicon.     

Effects of Ca and Mn Additions on the Microstructure and Dielectric Properties of (Bi<Subscript>0.5</Subscript>Na<Subscript>0.5</Subscript>)TiO<Subscript>3</Subscript> Ceramics

Dielectric ceramics based on the solid solution (1 − x)Bi_0.5Na_0.5TiO₃ (BNT)-xCaTiO₃ (CT) were synthesized by the conventional solid-state route. BNT with various contents of CT formed a complete solid solution and exhibited a rhombohedral structure. CT in this solid solution with BNT was observed to decrease the dielectric constant at higher temperatures and raise the dielectric constant at lower temperatures. On the other hand, decreased ferroelectricity was observed with increasing CT concentration, resulting in a downward shift of the depolarization temperature and a decrease of the dissipation factor. With the addition of Mn²⁺ to 0.86BNT-0.14CT, the temperature characteristics of capacitance were improved (−55°C to 250°C, ΔC/C _25°C ≤ ±15%). By doping with 1.5 wt.% Mn²⁺, the dielectric constant at room temperature reached over 900, with a dielectric loss of less than 1%.     

Thermoelectric Properties of <Emphasis Type="Italic">p</Emphasis>-Type Mg<Subscript>2.00</Subscript>Si<Subscript>0.25</Subscript>Sn<Subscript>0.75</Subscript> with Li and Ag Double Doping

Mg₂Si_1−x Sn _x -system solid solutions are ecofriendly semiconductors that are promising materials for thermoelectric generators in the middle temperature range. To produce a thermoelectric device, high-performance p- and n-type materials must be balanced. In this paper, p-type Mg_2.00Si_0.25Sn_0.75 with Li and Ag double doping was prepared by the liquid–solid reaction method and hot-pressing. Effects of Li and Ag double doping on thermoelectric properties were investigated in the temperature range from room temperature to 850 K. All sintered compacts were identified as single-phase solid solutions with anti-fluorite structure. The carrier concentration increased with the double doping. The temperature dependence of resistivity of the double-doped samples was similar to that of a metal. The seebeck coefficient increased with temperature to a maximum value and then decreased in the intrinsic region. Thermal conductivity decreased linearly with increasing temperature, reaching a minimum near the intrinsic region, and then increased rapidly because of the contribution of the bipolar component. The dimensionless figure of merit reached 0.32 at 610 K for Mg_2.00Si_0.25Sn_0.75 double-doped with Li-5000 ppm and Ag-20000 ppm.     

Thermoelectric Performance of Zn and Nd Co-doped In<Subscript>2</Subscript>O<Subscript>3</Subscript> Ceramics

Polycrystalline In₂O₃ ceramics co-doped with Zn and Nd were prepared by the spark plasma sintering (SPS) process, and microstructure and thermoelectric (TE) transport properties of the ceramics were investigated. Our results indicate that co-doping with Zn²⁺ and Nd³⁺ shows a remarkable effect on the transport properties of In₂O₃-based ceramics. Large electrical conductivity (~130 S cm⁻¹) and thermopower (~220 μV K⁻¹) can be observed in these In₂O₃-based ceramic samples. The maximum power factor (PF) reaches 5.3 × 10⁻⁴ W m⁻¹ K⁻² at 973 K in the In_1.92Nd_0.04Zn_0.04O₃ sample, with a highest ZT of ~0.25.     

Microstructure and Thermoelectric Properties of AgSbO<Subscript>3</Subscript> Ceramics Prepared by Ion-Exchange Powder Synthesis and Normal Sintering

Silver antimonate (AgSbO₃) is a potential high-temperature thermoelectric oxide with a low thermal conductivity, but it is difficult to fabricate dense bulk material with high phase purity. Well-dispersed AgSbO₃ nanopowder with an average diameter of 50 nm was synthesized by an ion-exchange process in this study, the sintering density of which was apparently enhanced. Nearly single-phase AgSbO₃ ceramic samples with a relative density close to 90% were obtained when sintered at a relatively low temperature (1273 K). The electrical conductivity of AgSbO₃ increased greatly with increasing sintering temperature, probably because of defects originating from the compositional deviation caused by sintering, in addition to increased density. This study also confirmed that AgSbO₃ had a low thermal conductivity, from 1.1 W m⁻¹ K⁻¹ at room temperature to 0.8 W m⁻¹ K⁻¹ at 673 K.     

Thermoelectric Properties of NdGd<Subscript>1+<Emphasis Type="Italic">x</Emphasis></Subscript>S<Subscript>3</Subscript> Prepared by CS<Subscript>2</Subscript> Sulfurization

Ternary rare-earth sulfides NdGd_1+x S₃, where 0 ≤ x ≤ 0.08, were prepared by sulfurizing Ln₂O₃ (Ln = Nd, Gd) with CS₂ gas, followed by reaction sintering. The sintered samples have full density and homogeneous compositions. The Seebeck coefficient, electrical resistivity, and thermal conductivity were measured over the temperature range of 300 K to 950 K. All the sintered samples exhibit a negative Seebeck coefficient. The magnitude of the Seebeck coefficient and the electrical resistivity decrease systematically with increasing Gd content. The thermal conductivity of all the sintered samples is less than 1.9 W K⁻¹ m⁻¹. The highest figure of merit ZT of 0.51 was found in NdGd_1.02S₃ at 950 K.     

Thermoelectric Properties of Nb-Doped Ordered Mesoporous TiO<Subscript>2</Subscript>

Mesoporous materials have pores with diameters between 2 nm and 50 nm, the presence of which generally decreases the thermal conductivity of the material. By incorporating mesoporous structures into thermoelectric materials, the thermoelectric properties of these materials can be improved. Although TiO₂ is an ordinary insulator, reduced TiO₂ shows better electrical conductivity and is therefore a potential thermoelectric material. Furthermore, the addition of a dopant to TiO₂ can improve its electrical conductivity. We hypothesized that, by doping ordered mesoporous TiO₂ films with niobium, we would be able to minimize the thermal conductivity and maximize the electrical conductivity. To investigate the effects of Nb doping and a mesoporous structure on the thermoelectric characteristics of TiO₂ films, Nb-doped mesoporous films were investigated using x-ray diffraction, ellipsometry, four-point probe measurements, and thermal conductivity analysis. We found that Nb doping of ordered mesoporous TiO₂ films improved their thermoelectric properties.     

Microstructures and Thermoelectric Properties of an Annealed Ti<Subscript>0.5</Subscript>(Hf<Subscript>0.5</Subscript>Zr<Subscript>0.5</Subscript>)<Subscript>0.5</Subscript>NiSn<Subscript>0.998</Subscript>Sb<Subscript>0.002</Subscript> Ribbon

The thermoelectric half-Heusler compound Ti_0.5(Hf_0.5Zr_0.5)_0.5NiSn_0.998Sb_0.002 was fabricated by spin-casting and subsequent annealing. ZT at room temperature increased with annealing time through an increase in absolute Seebeck coefficients despite a decrease in electrical conductivity. ZT reached 0.10 after annealing at 1050 K for 48 h. In powder x-ray diffraction analysis, each half-Heusler peak was accompanied by a bump at the high-angle side, corresponding to a minor Ti-rich half-Heusler phase. The quantity and Ti composition of the minor phase increased with annealing time, although those of the major half-Heusler phase were almost constant. In transmission electron microscopic analysis, granular domains, several nanometers in size, with atomic ordering or disordering were observed. Thermoelectric properties were␣improved by annealing through the growth of heterogeneous microstructures of the Ti-rich and Ti-poor half-Heusler grains and of the granular domains.     

Thermal Conductivity of Bi<Subscript>0.5</Subscript>Sb<Subscript>1.5</Subscript>Te<Subscript>3</Subscript> Affected by Grain Size and Pores

A fine measurement system for measuring thermal conductivity was constructed. An accuracy of 1% was determined for the reference quartz with a value of 1.411 W/m K. Bi_0.5Sb_1.5Te₃ samples were prepared by mechanical alloying followed by hot-pressing. Grain sizes were varied in the range from 1 μm to 10 μm by controlling the sintering temperature in the temperature range from 623 K to 773 K. The thermal conductivity was 0.89 W/m K for the sample sintered at 623 K, while a grain size of 1.75 μm was measured by optical microscopy and scanning electron microscopy. The thermal conductivity increased on the sample sintered at 673 K because of grain growth and decreased on those sintered at the temperatures from 673 K to 773 K because the increase of pore size caused to decrease thermal conductivity. The increase of thermal conductivity for the samples sintered at temperatures above 773 K was affected by the increase of carrier concentration.     

Thermoelectric Properties of Ca-Filled CoSb<Subscript>3</Subscript>-Based Skutterudites Synthesized by Mechanical Alloying

Ca _z Co_4−x (Fe/Mn) _x Sb₁₂ skutterudites were prepared by mechanical alloying and hot pressing. The phases of mechanically alloyed powders were identified as γ-CoSb₂ and Sb, but they were transformed to δ-CoSb₃ by annealing at 873 K for 100 h. All specimens had a positive Hall coefficient and Seebeck coefficient, indicating p-type conduction by holes as majority carriers. For the binary CoSb₃, the electrical conductivity behaved like a nondegenerate semiconductor, but Ca-filled and Fe/Mn-doped CoSb₃ showed a temperature dependence of a degenerate semiconductor. While the Seebeck coefficient of intrinsic CoSb₃ increased with temperature and reached a maximum at 623 K, the Seebeck coefficient increased with increasing temperature for the Ca-filled and Fe/Mn-doped specimens. Relatively low thermal conductivity was obtained because fine particles prepared by mechanical alloying lead to phonon scattering. The thermal conductivity was reduced by Ca filling and Fe/Mn doping. The electronic thermal conductivity was increased by Fe/Mn doping, but the lattice thermal conductivity was decreased by Ca filling. Reasonable thermoelectric figure-of-merit values were obtained for Ca-filled Co-rich p-type skutterudites.     

Thermoelectric Properties of Co<Subscript>4</Subscript>Sn<Subscript>6</Subscript>Se<Subscript>6</Subscript> Ternary Skutterudites

A ternary ordered variant of the skutterudite structure, the Co₄Sn₆Se₆ compound, was prepared. Polycrystalline samples were prepared by a modified ceramic method. The electrical conductivity, the Seebeck coefficient and the thermal conductivity were measured over a temperature range of 300–800 K. The undoped Co₄Sn₆Se₆ compound was of p-type electrical conductivity and had a band gap E _g of approximately 0.6 eV. The influence of transition metal (Ni and Ru) doping on the thermoelectric properties was studied. While the thermal conductivity was significantly lowered both for the undoped Co₄Sn₆Se₆ compound and for the doped compounds, as compared with the Co₄Sb₁₂ binary skutterudite, the calculated ZT values were improved only slightly.