双金属液复合浇注斗齿的铸件质量控制

主要介绍了斗轮式挖掘机斗齿采用高铬铸铁—钢双液复合浇注的铸造工艺。为防止斗齿产生夹渣，先浇注的铁液液面高度应控制在法兰盘的下表面，钢液的内浇口呈扇形外扩，在双金属过渡区(热节部位)内放置钢筋，既消除了斗齿内部缩孔，又实现了双金属的双重复合。大大提高了斗齿过渡区的强韧性。另外，双液浇注的间隔时间控制在1～1．5min之间为宜。     

球铁型材保温炉中熔体贫氧处理的研究

研究了不同条件下连铸保温炉内铁液球化衰退的过程。结果表明,与砂型铸造相比,连铸球墨铸铁型材在保证球化率＞ ８０％ 时,临界残留球化元素的含量显著降低,其中 Ｍｇ残 和 Ｍｇ残＋ Ｒ Ｅ残 分别为０．００９ ７％ 和０．０２０％ 。与无液面保护相比,在液面利用火焰加热贫氧处理结合熔渣覆盖铁液表面,球化衰退时间延长了一倍。     

双金属液浇注灰/蠕复合铸铁工艺研究

为了得到兼顾强韧性和导热性的复合铸铁,设计了四种双金属液-液浇注工艺.浇注双金属液时,统一采用底注式浇注系统浇注下层金属液,改变浇注上层金属液的浇注系统,上层金属液浇注速度选择为5cm·s-1,两种金属液浇注间隔时间选择为20s,下层金属液浇注高度超过理论结合面15mm.利用计算机数值模拟方法研究了金属液充型过程,并与实际浇注结果进行了对比验证.研究结果表明:采用缝隙扇形式浇注系统,制备出的灰/蠕复合铸铁的抗拉强度达到205 MPa,高于HT200灰铸铁,其500℃时导热系数为36 W·(m·k)-1,高于RuT300蠕墨铸铁.     

晃荡条件下气泡上升速度特性研究

海浪、地震等条件都会导致核动力设备中储存自由液面的设备产生剧烈的晃荡。为了分析晃荡条件下液体中的气泡行为特性,本文运用CLSVOF(coupled level-set and volume-of-fluid)模型追踪两相流体交界面,数值模拟气泡在液体中受余弦简谐激励和自由液面影响的上升过程。计算结果显示余弦简谐激励降低了气泡纵向运动速度,而横向速度略大于激励速度;自由液面的波动在纵向上会使气泡上升速度骤然降低,甚至出现负速度,越接近自由液面横向速度峰值越大。计算结果表明晃荡运动的影响是余弦简谐激励与自由液面波动影响的叠加,晃荡条件下自由液面波动是气泡速度变化的主要因素,气泡的本身属性起次要作用。     

镍/铁双金属体系对多氯联苯的催化脱氯降解

采用化学还原法制备的镍/铁双金属对多氯联苯(PCB)进行降解。实验以镍/铁双金属对PCB的降解率为考察指标,选用L25(56)正交试验方案,考察了降解介质的初始pH值、铁的加入量、镍化率(Ni/Fe质量比)、降解温度和反应时间5个影响因素。结果表明:介质的初始pH值对降解率有极显著影响,其他4个因素的影响不明显。得出的镍/铁双金属对PCB降解的最佳工艺条件为:介质初始pH 2.0、铁加入量0.4 g、反应体系温度60℃、降解时间60 min和镍化率15%,在此条件下获得了79.6%的降解率。     

液面晃荡频率的半解析方法

为了解决内部充液圆柱壳的结构稳定性及安全性会受到内部液体晃荡的影响,本文针对二维圆柱壳在任意充液深度时的自由液面晃荡频率提出了一种半解析求解方法。分别在圆柱壳圆心和自由液面建立结构坐标系和液面坐标系,假设内部液体为无粘不可压缩流体,利用拉普拉斯方程,结合小幅晃荡的表面波方程,得出自由液面的速度势函数,通过坐标变换并结合流体-壳体连续边界条件得出液面运动控制方程,采用伽辽金法得出自由液面晃荡频率。通过与其他方法进行对比验证了晃荡频率及模态求解的准确性,然后对不同充液深度下二维刚性圆柱壳自由液面晃荡频率特性进行了讨论。研究表明：本文提出的方法能够准确有效计算二维充液圆柱壳内部液体不同深度下的晃荡频率。     

不同形状液面上方的饱和蒸汽压

本文在饱和蒸汽压与液面形状关系定性解释的基础上,利用弯曲液面的附加压强,导出了水平液面与凸液面上方饱和蒸汽压之间的定量关系。     

纳米零价铁基双金属复合材料降解水体污染物的研究进展

复杂多样的水体污染物日益破坏生态环境同时威胁人类健康。纳米零价铁基双金属复合材料可用于高效还原降解多种水体污染物。着重从纳米双金属材料的分类、制备、应用进展和反应机理等方面进行综述,针对研究中存在的不足和今后的研究方向提出建议。     

水泥基复合材料界面过渡区体积分数的定量计算

为了计算水泥基复合材料的界面过渡区体积分数,采用最邻近表面分布函数和骨料比表面积2种方法,结合实际骨料的筛分曲线,给出了界面过渡区体积分数定量关系式．结果表明：单位体积水泥基复合材料中,当骨料的体积分数〈0．5,界面厚度〈50μm时,2种方法计算的误差约为10％;界面区厚度越小,2种方法计算的误差也越小．     

化学法测定磷铵管式反应器气液相界面积

本文论述了用化学法测定的磷铵管式反应器在不同流动状况及安装形式下的气液相界面积.实验中发现,在过渡区范围内表观液速对气液相界面积有负效应,对气液传质有不利影响;因而在实际操作过程中应避开过渡区.文中所列实验数据与文献很吻合,说明结论是可信的.     

“一罐制”铁水调度优化模型的研究

铁水转运是钢铁生产的一个关键衔接环节,对控制钢铁生产节奏、保证产品质量起着极其重要的作用.钢铁生产新工艺的“一罐制”铁水运输,缩短了钢铁界面流程,使生产的刚性和连贯性增强,对铁水转运系统的要求更高,因此钢铁企业日益重视对铁水转运调度的研究.在对行车起重机＋铁水车“一罐制”铁水转运和调度的研究基础上,分析了新工艺流程中铁水转运系统的特点,对钢铁生产的调度计划进行优化,建立了基于“一罐制”铁水转运多目标径路优化模型,并给出了模型算法.算法实现了新工艺下铁水物流运输的智能优化调度,使铁水运输趋于准点,降低生产能耗.     

低钒铁水各元素氧化的热力学分析

针对攀钢低钒铁水成分,通过热力学软件Factsage对低钒铁水中各元素的氧化情况进行平衡计算分析。O2,CO2和FeO三种氧化剂,都能够使铁水中的硅、钛、锰、钒氧化进入到钒渣中,氧化顺序为钛、硅、锰、钒。三种氧化剂的氧化能力比较,FeO最强,O2次之,CO2最弱。氧化低钒铁水的钒渣的组分的最大的区别是FeO的百分含量,最少是CO2作为氧化剂时,百分含量为20.1%,钒渣的质量相对较好,所以能够使铁水中各元素的选择性氧化最佳的氧化剂为CO2。     

45号钢堆焊熔敷金属的组织及性能

分别采用焊条CHR172和CHR132在基体材料45号钢上进行了堆焊试验；对焊缝金属和热影响区金属的显微组织进行了分析；对堆焊熔敷金属的硬度进行了测试。结果表明：堆焊金属的显微组织和显微硬度与焊条的种类和堆焊工艺参数有关。焊条CHR172堆焊熔敷金属的硬度比焊条CHR132堆焊熔敷金属的硬度好。     

热压含碳球团制备及性能

采用烟煤加热时产生的胶质体作为黏结剂来压制热压含碳球团.根据胶质体的最高流动度和热稳定性,用单一煤种压制热压球团时,肥煤是最好的黏结煤.相对于同成型条件下的冷压含碳球团,热压含碳球团强度更高,相同还原条件下的反应速度更快.     

A Novel Electrochemical Oxygen Sensor for Determination of Ultra-low Oxygen Contents in Molten Metal

A novel electrochemical oxygen sensor has been developed by using Laβ-Al2O3 as solid electrolyte and Cr+Cr2O3 as reference electrode. The sensor not only can be used as normal oxygen sensor hot also as an ultra-low oxygen sensor. Especially, it is very sensitive to measure ultra-low oxygen in molten metal. For estimating the accuracy of Laβ-Al2O3 oxygen sensor, two series of oxygen activities in molten iron at different oxygen contents and different temperature were measured by both Laβ-Al2O3 oxygen sensor and ZrO2 oxygen sensor. The theoretical values of oxygen activities in molten iron (3.30%C, in mass fraction) at 1723K and 1745K were also evaluated for comparing the measuring results of two sensors. At last, the error of measurement for Laβ-Al2O3 oxygen sensor was discussed too.     

Effect of electromagnetic force on turbulent flow of molten metal in aluminum electrolysis cells

The standard κ-ε model was adopted to simulate the flow field of molten metal in three aluminum electrolysis cells with different anode risers. The Hartman number, Reynolds number and the turbulent Reynolds number of molten metal were calculated quantitatively. The turbulent Reynolds number is in the order of 10^3 , and Reynolds number is in the order of 104 if taking the depth of molten metal as the characteristic length. The results show that the molten metal flow is the turbulence of high Reynolds number, the turbulent Reynolds number is more appropriate than Reynolds number to be used to describe the turbulent characteristic of molten metal, and Hartman number displays very well that electromagnetic force inhibits turbulent motion of molten metal.     

热处理对高铬铸铁磨损特性的影响

高铬铸铁具有优良的耐磨性,主要是由于其基体为马氏体组织,碳化物类型为六方晶系的（Ｆｅ,Ｃｒ）７Ｃ３,碳化物呈六角棒状、针状、条状分布,显著地改善了材质的力学性能．煤粉对管道的磨损,属于软磨粒低应力的磨料磨损,这种高铬铸铁用于此工况下能发挥出其优良的性能．经金属Ｘ射线分析证明碳化物是（Ｆｅ,Ｃｒ）７Ｃ３,通过透射电镜分析,发现其基体组织为奥氏体、板条（位错）马氏体与孪晶马氏体．用电子探针对金相组织中的黑色区进行了分析,发现此处贫铬而易被腐蚀．通过磨损试验证明高铬铸铁耐磨性好,成本低,与稀土高铬镍氮相比,成本降低６０％,与钨铬合金相比,成本降低７０％．     

氧对铸铁凝固组织与性能的影响

液态铸铁中的溶解氧与大气中的氧一样是非常活泼的元素。溶解氧从铸铁熔化至凝固始终与液态金属发生作用。因此,以冶金学原理为理论基础,从研究加氧铁水的冶金特性入手,本文系统地探讨了氧对铸铁凝固,组织与性能的影响,提出了一些新观点。     

压铸件充填特性的研究

本文利用自制的精密压力计,测定了金属液充型过程中的压力,观察了压铸件的金相组织,并测定了其抗拉强度。指出了金属液充型时压力传递的规律及其对压铸件质量的影响。对正确设计浇注系统,合理地进行压铸型设计,提高压铸件质量和经济效益等有实际指导意义。     

Experimental Research for Refractories Used in High-Turbulent-Mixer (HTM)-Reactor

The high turbulent mixer (HTM) process is benefit for improving the quality of iron and steel, but the refractory of the reactor is easy to be eroded by slag and liquid metal at high temperature. Especially for the violent mixing in HTM, refractory can also be im- pacted by molten metal (iron or steel), so it is very important to study and find out new refractory to meet the demand of HTM. Suitable refractory not only can stand the eroding of slag and liquid metal, but also can reduce the loss of electromagnetic energy. According to the experimental results, the influence of different refractory on electromagnetic force is unconspicuous, the refractory with Al,O,-base is better than that with MgO-base for standing the erosion by slag and iron. Al,O,-base refractory is more suitable for HTM process.