我厂生产的二硫化碳(CS_2)是一种易燃、易爆、易挥发、毒性较大、腐蚀较严重的产品。去年十月罐体上的进料口被腐蚀穿孔,挥发跑漏出的CS_2,严重危害工人的身体健康,厂里要求立即修复。但是不能用常规的焊补法。为此,我们采用粘接技术粘补修复,其效果很好。现将粘补方法简述如下:     

电解电容器用铝箔的研究

采用SEM、XRD、失重法和线性极化法,对国产铝箔和日本铝箔进行了研究。结果表明,国产铝箔和日本铝箔虽在表面形貌、元素成分和晶型上稍有差异,线性极化也表明日本铝箔比国产铝箔更易腐蚀,但国产铝箔基本上满足了低酸度腐蚀体系。     

化学镀锌对阳极铝箔腐蚀扩面的影响

通过化学镀法在铝箔表面施镀微量的锌元素,对镀锌后的阳极铝箔腐蚀扩面的过程及机理进行研究。结果表明,化学镀锌后,铝箔在腐蚀过程中其表面形成Zn-Al微电池效应,促进了铝箔的电化学腐蚀,改善了隧道孔形貌,使铝箔的隧道孔分散均匀,孔径减小,且密度明显增大,进而增大了铝箔的比电容。     

JD-44-2铝箔压敏胶粘带

由上海橡胶制品研究所研制的JD-44-2工业用铝箔胶粘带是一种在铝箔上涂以配有交联剂的橡胶型压敏胶粘剂的带状粘接材料。具有综合性能优良、胶粘力强,老化性能优异,良好的施工性能。冰箱内藏式冷凝器是用铝箔压敏胶粘带     

带压粘补输油管线及石油储罐

本文介绍了带压粘补输油管线及石油储罐胶粘剂的选择,粘补过程中几种止漏方法、堵漏专用工具的选用和表面处理。     

铝电容器用铝箔腐蚀与化成研究进展

铝箔腐蚀和化成是制备铝电容器的一个重要过程,由超纯铝箔经过电化学刻蚀制得腐蚀箔,腐蚀箔经过阳极氧化最终得到化成箔。本文从制备工艺的角度对铝箔化成进行了综述,并对腐蚀扩孔、多级化成、复合箔制备的最新进展进行了综述。此外还讨论了腐蚀孔洞的类型、化成液的合理配比、反应机理以及目前研究的不足之处,并提出前景与展望。     

EDTA配位滴定法测定铝箔腐蚀废酸中硫酸根含量

采用EDTA配位滴定法测定铝箔腐蚀废酸中的硫酸根含量,考察了pH值、NH_3-NH_4Cl缓冲溶液的体积、氯化钡-氯化镁混合溶液及乙醇溶液的加入量等对测定硫酸根离子的影响。运用标准加入法和实际样品的多次测定来研究测定硫酸根的精密度和准确度,相对标准偏差(RSD,n=8)为0.24%,回收率在97.6%～102.7%之间,该方法重复性好,精密度高,测定结果准确可靠,满足铝箔腐蚀废硫酸中硫酸根含量测定技术要求。     

电解电容器用铝箔腐蚀液中葡萄糖的作用

研究了葡萄糖对铝箔交流腐蚀扩面的影响,采用循环伏安法对电容结果进行表征。发现葡萄糖的加入,有助于铝箔的腐蚀和扩孔,比电容有较大幅度的提高,并且葡萄糖对低纯度铝箔影响更大,1.0g/L葡萄糖导致低纯铝箔(99.2%)比容约提高30%,高纯铝箔(99.99%)提高约10%。     

湿式煤气柜腐蚀泄漏带压粘补

我公司有座5万m^3湿式煤气柜，1985年投产使用至今。2005年10月检查时发现在西南面气柜顶板和斜侧板连接的焊缝处，出现了十多个腐蚀穿孔及裂缝渗漏的地方，穿孔渗漏处煤气外泄严重，存在着极大的安全隐患，由于柜内煤气具有一定压力，不能用钢板电焊贴补，所以决定采用带压粘补的方法来修复煤气柜，延长煤气柜的使用寿命。     

金属离子对电极箔扩面腐蚀影响的研究进展

对近年来微量金属离子在铝电解电容器用电极箔扩面腐蚀工艺的最新研究成果进行了总结,在铝箔腐蚀过程中,金属离子能与铝形成电偶腐蚀,在铝箔表面指引点蚀生长,使铝箔的腐蚀电位负移,孔密度增大,并孔减少,比电容增大。讨论了它们各自的技术优势和短板,展望了今后微量金属离子对电极箔扩面腐蚀技术在性能及机理研究方面的趋势。     

复合材料补片尺寸和形状对铝板修补结构lamb波传播影响

借助于ANSYS软件建立包含铝板、复合材料层合板补片、胶层和压电陶瓷片(PZT)的压电和逆压电效应的模型,实现在结构中激励和接收lamb波信号,并以试验验证模型的正确性。利用损伤对结构中lamb波传播特性的影响,对复合材料补片修补后的金属损伤结构的损伤检测进行数值模拟研究,研究不同补片尺寸及形状修补8 mm孔对lamb波损伤检测的影响。结果表明,圆形、方形、菱形补片的仿真模拟结果显示不同的形状对A0和S0波包的影响差异较大,不同尺寸的菱形补片也对A0和S0波包有较大差异。     

抗氧化铝箔衬纸复合用淀粉胶的研制

本文主要介绍了抗氧化铝箔衬纸淀粉肢的配方、生产工艺及其性能,并分析了各种因素对胶粘剂性能的影响。     

Joint Strength Optimization of Adhesively Bonded Patches

Aircraft face damage from impact with objects or birds or due to ageing that leads to fatigue cracks. The conventional methods of repairing aircraft metallic structures generally include the use of a plate joined by screws or rivets. Although these methods are efficient in the short term, they introduce stress concentrations leading to the initiation of new cracks that are difficult or impossible to detect by non-destructive methods. For these reasons, it is necessary to develop new methods to improve the behaviour of the structure (especially for long term) and its manufacture cost. One of the solutions that have been studied by the aeronautical industry is the use of patches bonded with structural adhesives. However, adhesively bonded patches have problems of stress concentration at the edges where crack initiation is prone to occur. This problem can be reduced by the use of a taper and a spew fillet at the end of the patch and by the use of a mixed adhesive technique where a ductile adhesive is placed at the edges of the patch. Double strap specimens from 3 mm thick 6063-T6 aluminium alloy sheet were analysed. Aluminium and straps (or patches) with an internal taper, an adhesive spew fillet, and dual adhesives were experimentally tested. The results obtained were explained by a finite element analysis. A taper angle is beneficial only for the brittle adhesive. The use of two adhesives is advantageous for the taperless configuration.     

用氯丁-多异氰酸酯改性胶粘剂粘接传送带接头

根据橡胶传送带接头的断裂形貌 ,对断裂原因进行了分析 ,介绍了氯丁 -多异氰酸酯改性胶粘剂的性能及修复传送带接头的具体工艺     

新型铝箔级层合胶的研制

介绍一种新型的铝箔纸层合胶粘剂,其以醋酸乙烯酯、丙烯酸为混合单体,并在聚合时加入一定量的淀粉、邻苯二甲酸二丁酯,得到的胶粘剂具有较强的粘合性,较好的流平性。     

新型铝箔衬纸复合用酪蛋白胶的研制

介绍了一种以干酪素为主要原料研制的铝箔衬纸胶粘剂的配方、制备工艺及技术性能。采用氨水溶解干酪素,硼砂作交联剂。讨论了固含量、碱、交联剂、反应时间、反应温度等因素对胶粘剂的制备与性能的影响。结果表明:在氨水用量为2.5g,尿素22g,硼砂3.5g,反应温度为65℃左右时制得的酪蛋白胶性能最佳。尿素可提高胶的韧性,使胶粘剂形成胶膜,同时可降低胶粘度,增加胶的流动性。     

聚乙烯醇缩丁醛树脂的性能及应用

概述聚乙烯醇缩丁醛(PVB)的基本性能、反应原理、生产方法及在安全玻璃、工程塑料、纤维、陶瓷花纸、铝箔纸、粘合剂等方面的应用,阐述了我国PVB生产技术改造及向特殊应用领域发展的必要性。     

长链烷基咪唑作用下铝箔的腐蚀行为

研究了长链烷基咪唑缓蚀剂在铝箔腐蚀中的作用。结果表明,温度、盐酸浓度和长链烷基咪唑浓度对铝箔腐蚀有重要的影响。随盐酸浓度加大,腐蚀速率逐步加大;发现离子液体浓度较小时,缓蚀效率变化明显。高温时长链烷基咪唑仍呈现出良好的缓蚀性能。对腐蚀作用机制进行了初步探讨。     

阻燃EVA热熔胶的制备及其在线缆修复中的应用研究

选取二乙基次膦酸铝、焦磷酸二三聚氰胺和氢氧化铝为阻燃剂,制备了用于老化线缆快速修复的阻燃乙烯-醋酸乙烯酯共聚物（EVA）热熔胶,并对热熔胶材料的阻燃性能及线缆修复后的阻燃性能和绝缘性能等进行了测试和表征。结果表明,当3种阻燃剂的质量比为1:1:3,总添加量为50%（质量分数,下同）时,阻燃热熔胶通过垂直燃烧测试UL 94 V-0级且测试过程中无滴落,极限氧指数为27.1%;与纯热熔胶相比,阻燃热熔胶的热释放速率和总热释放量均大幅降低,阻燃体系发挥了很好的协同阻燃作用;修复后线缆的体积电阻率为1.15×1015Ω·m,热熔胶在线缆表面具有良好的成膜性和黏附力,线缆弯折过程中热熔胶不开裂、不脱落;燃烧过程中,修复后的线缆表面形成了膨胀的炭层,能有效保护线缆。     

新型环保屏蔽导电压敏胶粘剂的研制

研究一种环保型的屏蔽导电压敏胶粘剂,该产品具有较强的抗静电释放(ESD)、导电性能和压敏性能。主要应用于导电铝箔胶带的生产和电子工业。所用溶剂毒性低,有利于劳动保护和环境保护。