A study on synthesis and properties of Fe<Subscript>3</Subscript>O<Subscript>4</Subscript> nanoparticles by solvothermal method

Magnetic nanoparticles (Fe₃O₄) were synthesized by the solvothermal method using FeCl₃ · 6H₂O and ethylene glycol as a reactant. Powder X-ray diffraction, FT-IR, TEM, SEM, and VSM were used to characterize the magnetic particles. The reacting factors, such as reacting time, the concentration of iron source and surfactant, especially the effect of NaAc · 3H₂O, were studied. The results indicated that NaAc · 3H₂O plays the role not only as a dispersant but also a structure-directing agent. The synthesized Fe₃O₄ particles showed excellent magnetic property, which made them have potential for application in magnetic nanodevices and biomedicine.     

Preparation and characterization of spindle-like Fe<Subscript>3</Subscript>O<Subscript>4</Subscript> mesoporous nanoparticles

Magnetic spindle-like Fe₃O₄ mesoporous nanoparticles with a length of 200 nm and diameter of 60 nm were successfully synthesized by reducing the spindle-like α-Fe₂O₃ NPs which were prepared by forced hydrolysis method. The obtained samples were characterized by transmission electron microscopy, powder X-ray diffraction, attenuated total reflection fourier transform infrared spectroscopy, field emission scanning electron microscopy, vibrating sample magnetometer, and nitrogen adsorption-desorption analysis techniques. The results show that α-Fe₂O₃ phase transformed into Fe₃O₄ phase after annealing in hydrogen atmosphere at 350°C. The as-prepared spindle-like Fe₃O₄ mesoporous NPs possess high Brunauer-Emmett-Teller (BET) surface area up to ca. 7.9 m² g^-1. In addition, the Fe₃O₄ NPs present higher saturation magnetization (85.2 emu g^-1) and excellent magnetic response behaviors, which have great potential applications in magnetic separation technology.     

Effect of surface modification of Fe<Subscript>3</Subscript>O<Subscript>4</Subscript> nanoparticles on the preparation of Fe<Subscript>3</Subscript>O<Subscript>4</Subscript>/polystyrene composite particles via miniemulsion polymerization

Fe₃O₄ nanoparticles were modified by n-octadecyltrimethoxysilane (C18TMS) and 3-trimethoxysilylpropylmethacrylate (MPS). The modified Fe₃O₄ nanoparticles were used to prepare Fe₃O₄/polystyrene composite particles by miniemulsion polymerization. The effect of surface modification of Fe₃O₄ on the preparation of Fe₃O₄/polystyrene composite particles was investigated by transmission electron microscopy, Fourier transform infrared spectrophotometer (FT-IR), contact angle, and vibrating sample magnetometer (VSM). It was found that C18TMS modified Fe₃O₄ nanoparticles with high hydrophobic property lead to the negative effect on the preparation of the Fe₃O₄/polystyrene composite particles. The obtained composite particles exhibited asymmetric phase-separated structure and wide size distribution. Furthermore, un-encapsulated Fe₃O₄ were found in composite particles solution. MPS modified Fe₃O₄ nanoparticles showed poor hydrophobic properties and resulted in the obtained Fe₃O₄/polystyrene composite particles with regular morphology and narrow size distribution because the ended C=C of MPS on the surface of Fe₃O₄ nanoparticles could copolymerize with styrene which weakened the phase separation distinctly.     

Preparation and properties of poly(acrylic acid-co-styrene)/Fe<Subscript>3</Subscript>O<Subscript>4</Subscript> nanocomposites

Poly(acrylic acid-co-styrene)/Fe₃O₄ nanocomposites were prepared using poly(acrylic acid-co-styrene) (P(AA-co-St)) and nano-Fe₃O₄ particles. The resultant materials were characterized by transmission electron microscope (TEM), Fourier transform infrared (FTIR), thermogravimetric analysis (TGA), advanced rheology expand system and superconducting quantum interference device (SQUID) magnetometer. The diameter of the magnetic particles was around 3–14 nm. The experimental results reveal that the acrylic acid segment of P(AA-co-St) can react with nano-Fe₃O₄. With increasing reaction time the storage modulus, loss modulus, complex viscosity and shear stress of the P(AA-co-St)/Fe₃O₄ ethanol suspension were increased, and the suspension changed from liquid-like behavior to gel-like behavior for the reaction between P(AA-co-St) and Fe₃O₄, as found during the rheology measurements. The thermal stability of P(AA-co-St) decreased with the addition of nano-Fe₃O₄, and the nanocomposites exhibited superparamagnetic properties above the blocking temperature.     

Synthesis of polyvinyl alcohol hydrogel grafted by modified Fe<Subscript>3</Subscript>O<Subscript>4</Subscript> nanoparticles: characterization and doxorubicin delivery studies

During the last two decades, serious efforts have been directed towards the synthesis and coating magnetic nanoparticles for biomedical applications. Among many different types of polymeric coating materials that have been utilized in previous studies, we have selected polyvinyl alcohol (PVA). In this study, we report a novel type of magnetite nanocomposite-based PVA hydrogel. For this purpose, first, Fe₃O₄ nanoparticles were modified through hexamethylene diisocyanate (HMDI) and then PVA was modified by bromoacetyl bromide to produce bromoacetylated PVA. The modified PVA was cross-linked through various diamines such as ethylene-diamine, propylene-diamine and hexamethylenediamine. The prepared weak tridimensional PVA hydrogels were further reacted through unreacted hydroxyl groups with Fe₃O₄, modified by HMDI to form magnetite hard tridimensional hydrogels. The swelling behavior of the prepared magnetite nanocomposites were investigated and showed a fast initial swelling followed by a mild increase until attaining equilibrium. The structural, morphological, thermal and magnetic properties of the synthesized magnetite nanocomposites were confirmed by FTIR, thermal gravimetric analysis, vibrating sample magnetometer and scanning electron microscopy. The doxorubicin anti-tumor drug was loaded on a selected synthesized magnetic hydrogel and in vitro drug release studies were done in phosphate buffer solution in 37 °C.     

Synthesis and thermal behavior of Fe<Subscript>3</Subscript>O<Subscript>2</Subscript>(BO<Subscript>4</Subscript>) oxoborate

Iron oxoborate Fe₃O₂(BO₄) has been first produced in solid-phase chemical reactions. Its thermal behavior in the temperature range 20–900°C is studied with the use in-situ high-temperature powder X-ray diffraction. It is shown that Fe₃O₂(BO₄) begins decomposing with the formation of Fe₂O₃ in the temperature range 660–900°C. Thermal expansion is sharply anisotropic at room temperature (α_max/α_min = 7) and becomes more isotropic with an increase in the temperature (α_max/α_min = 1.2). The degree of oxidation of Fe³⁺ has been confirmed by Mössbauer spectroscopy (at a room temperature), and two nonequivalent positions in the structure have been detected, which are occupied by iron atoms with the octahedral environment of the oxygen atoms.     

Selective Synthesis of Fe<Subscript>2</Subscript>O<Subscript>3</Subscript> and Fe<Subscript>3</Subscript>O<Subscript>4</Subscript> Nanowires Via a Single Precursor: A General Method for Metal Oxide Nanowires

Hematite (α-Fe₂O₃) and magnetite (Fe₃O₄) nanowires with the diameter of about 100 nm and the length of tens of micrometers have been selectively synthesized by a microemulsion-based method in combination of the calcinations under different atmosphere. The effects of the precursors, annealing temperature, and atmosphere on the morphology and the structure of the products have been investigated. Moreover, Co₃O₄ nanowires have been fabricated to confirm the versatility of the method for metal oxide nanowires.     

Preparation of stable magnetic nanofluids containing Fe<Subscript>3</Subscript>O<Subscript>4</Subscript>@PPy nanoparticles by a novel one-pot route

Stable magnetic nanofluids containing Fe₃O₄@Polypyrrole (PPy) nanoparticles (NPs) were prepared by using a facile and novel method, in which one-pot route was used. FeCl₃·6H₂O was applied as the iron source, and the oxidizing agent to produce PPy. Trisodium citrate (Na₃cit) was used as the reducing reagent to form Fe₃O₄ NPs. The as-prepared nanofluid can keep long-term stability. The Fe₃O₄@PPy NPs can still keep dispersing well after the nanofluid has been standing for 1 month and no sedimentation is found. The polymerization reaction of the pyrrole monomers took place with Fe³⁺ ions as the initiator, in which these Fe³⁺ ions remained in the solution adsorbed on the surface of the Fe₃O₄ NPs. Thus, the core-shell NPs of Fe₃O₄@PPy were obtained. The particle size of the as-prepared Fe₃O₄@PPy can be easily controlled from 7 to 30 nm by the polymerization reaction of the pyrrole monomers. The steric stabilization and weight of the NPs affect the stability of the nanofluids. The as-prepared Fe₃O₄@PPy NPs exhibit superparamagnetic behavior.     

Research of mica/Fe<Subscript>3</Subscript>O<Subscript>4</Subscript> pearlescent pigment by co-precipitation

Experiments on preparation of mica/Fe₃O₄ pearlescent pigment were performed to discuss influences of several crucial parameters on final products. The samples were characterized by XRD, HRSEM, FTIR and color measurement, the content of Fe₃O₄ on the mica surface was also analyzed by XPS. It was found that the smoothness, compactness and colour deepness of the coating were influenced by different pH values and temperatures. The optimum preparation parameters of mica/Fe₃O₄ pearlescent pigment were obtained: the value of pH ≥ 9.2; the concentration of sodium hydroxide was 0.5 mol/l; the concentration ratio of Fe³⁺ to Fe²⁺ was 1.6 : 1; the velocity of magnetic stirring was 138 ≤ v ≤ 151 r/min; reaction temperature was 70–80°C; calcination temperature was 350°C and calcination time was 3 h.     

Soft Template Synthesis of Super Paramagnetic Fe<Subscript>3</Subscript>O<Subscript>4</Subscript> Nanoparticles a Novel Technique

The present study reports a facile technique for the synthesis of crystalline super paramagnetic nano ferrite (Fe₃O₄) particles using diethyl amine as a soft template. The spectral properties of Fe₃O₄ nanoparticles were characterized by UV–visible and Fourier Transform Infrared (FTIR) spectroscopies while the crystalline structure and particle size was estimated using X-Ray diffraction (XRD) as well as transmission electron microscopy (TEM) techniques. The super paramagnetic behavior of Fe₃O₄ nanoparticles was determined using vibrating sample magnetometer (VSM) at 300 K. The results of the studies revealed that this technique could be adopted to synthesize agglomerate free super paramagnetic Fe₃O₄ nanoparticles which may find potential application in the filed of biosensor and corrosion protective coatings.     

Heterogeneous Fenton degradation of Orange II by immobilization of Fe<Subscript>3</Subscript>O<Subscript>4</Subscript> nanoparticles onto Al-Fe pillared bentonite

A novel catalyst, Fe₃O₄ nanoparticle decorated Al-Fe pillared bentonite (Fe₃O₄/Al-Fe-P-B), was prepared by in situ precipitation oxidization method. The catalyst was characterized by SEM, XRD and Raman spectroscopy. The Fe₃O₄ nanoparticles mainly exist on the surface or enter into the pore of bentonite, with better dispersing and less coaggregation. The catalytic activity of Fe₃O₄/Al-Fe-P-B was investigated in the degradation of Orange II (OII) by heterogeneous Fenton-like process. The effects of initial concentration of hydrogen peroxide, catalyst loading, temperature and initial pH on the degradation of OII were investigated. The Fe₃O₄/Al-Fe-P-B showed higher degradation efficiency of OII than bare Fe₃O₄ or Al-Fe-P-B in the degradation experiment. The enhanced catalytic activity of Fe₃O₄/Al-Fe-P-B in heterogeneous Fenton system was due to the synergistic effect between Al-Fe-P-B and Fe₃O₄. The novel catalyst can achieve solid-liquid separation easily by sample magnetic separation and has a good reusability and stability.     

Examining the use of Fe<Subscript>3</Subscript>O<Subscript>4</Subscript> nanoparticles to enhance the NH<Subscript>3</Subscript> sensitivity of polypyrrole films

Summary Polypyrrole (PPy) composite films with different contents of Fe₃O₄ were prepared by in-situ polymerization of pyrrole in aqueous solutions. The dependence of dc current changes on the response of the samples exposure to NH₃ vapor has been investigated. The results shows the composite films are more stable than the pristine ones after being exposed to NH₃ vapor. Meanwhile, the response time was reduced with increasing the Fe₃O₄ content in the films. The results might be originated from the structural changes in the PPy films caused by the addition of Fe₃O₄.     

Synthesis of spinel Ni<Subscript>0.75</Subscript>Zn<Subscript>0.25</Subscript>Fe<Subscript>2</Subscript>O<Subscript>4</Subscript> and the properties of a coating obtained by gas-flame spraying

Ferrite Ni_0.75Zn_0.25Fe₂O₄ was prepared by the solid-state synthesis and thermal decomposition of the complex oxalate Ni_0.75Zn_0.25Fe₂(C₂O₄)₃ · 6H₂O. The oxalate precursor and the products obtained at different stages of the thermal decomposition were identified by differential thermal analysis and X-ray and X-ray photoelectron spectroscopy. The properties of a ferromagnetic coating deposited on a substrate by gasflame coating were studied. The magnetic properties of the Ni-Zn ferrite product and the ferromagnetic coating were also investigated.     

Effect of HCl Concentration on the Dispersity of Fe<Subscript>3</Subscript>O<Subscript>4</Subscript> Nanoparticles

In this paper, monodisperse 6 nm-sized Fe₃O₄ nanoparticles with spinel crystalline structure were synthesized via a co-precipitation method. The effect of HCl concentrations on Fe₃O₄ samples was investigated by TEM, VSM and UV–vis. HCl-modified Fe₃O₄ nanoparticles solution was a stable, clear, transparent cationic colloid. The results showed that HCl had a great influence on the dispersity of Fe₃O₄ nanoparticles and almost no influence on the materials magnetism.     

One-pot method fabrication of superparamagnetic sulfonated polystyrene/Fe<Subscript>3</Subscript>O<Subscript>4</Subscript>/graphene oxide micro-nano composites

In this work, using monodispersed sulfonated polystyrene (SPS) microspheres as carriers, FeCl₃·6H₂O and FeSO₄·7H₂O as precursors, NaOH as precipitant in the presence of graphene oxide (GO), SPS/Fe₃O₄/GO micro-nano composites were fabricated by a simple one-pot method employing an inverse coprecipitation in-situ compound technology. The SPS/Fe₃O₄/GO micro-nano composites were characterized by scanning electron microscopy, transmission electron microscopy, X-ray powder diffractometer, Fourier transform infrared spectroscopy, nitrogen adsorption/desorption isotherms and vibrating sample magnetometer. The results show that the SPS/Fe₃O₄/GO micro-nano composites were fabricated with SPS as core, GO and Fe₃O₄ nanoparticles as shell. The SPS/Fe₃O₄/GO micro-nano composites had larger BET specific surface area, average pore width and micropore volume than the pure SPS microspheres. Meanwhile, the SPS/Fe₃O₄/GO micro-nano composites had superparamagnetism and hydrophilic property. The saturation magnetization (M_s) of the SPS/Fe₃O₄/GO micro-nano composites was 10.86 emu/g, which was enough to ensure the convenient magnetic separation of solid and liquid phase.     

Catalytic properties of Co<Subscript>3</Subscript>O<Subscript>4</Subscript> nanoparticles for rechargeable Li/air batteries

Three types of Co₃O₄ nanoparticles are synthesized and characterized as a catalyst for the air electrode of a Li/air battery. The shape and size of the nanoparticles are observed using scanning electron microscopy and transmission electron microscopy analyses. The formation of the Co₃O₄ phase is confirmed by X-ray diffraction. The electrochemical property of the air electrodes containing Co₃O₄ nanoparticles is significantly associated with the shape and size of the nanoparticles. It appears that the capacity of electrodes containing villiform-type Co₃O₄ nanoparticles is superior to that of electrodes containing cube- and flower-type Co₃O₄ nanoparticles. This is probably due to the sufficient pore spaces of the villiform-type Co₃O₄ nanoparticles.     

Synthesis and properties of flux-cast refractories in the Al<Subscript>2</Subscript>O<Subscript>3</Subscript>-MgO-B<Subscript>2</Subscript>O<Subscript>3</Subscript> system

Details are given of the synthesis and testing of flux-cast refractory materials in the alumina-rich region of the Al₂O₃-MgO-B₂O₃ system; XRD and petrography indicate that the main structure-forming phases are corundum and magnesian spinel. In subordinate amounts there are the boroaluminate 9Al₂O₃·2B₂O₃ and the previously unknown compound 4Al₂O₃·MgO·2B₂O₃, whose composition has been established by microprobe analysis. Corrosion tests showed that three-component systems containing magnesium and boron oxides at levels of 5–10% do not increase the corrosion resistance of refractories in molten sodium-calcium-silicate glass and electrovacuum borosilicate glass. __________ Translated from Novye Ogneupory, No. 3, pp. 161–163, March, 2008.     

Modification of Mg<Subscript>3</Subscript>Si<Subscript>2</Subscript>O<Subscript>5</Subscript>(OH)<Subscript>4</Subscript> nanotubes by magnetite nanoparticles

The magnetite nanoparticles and nanocomposite “Nanotube of hydrosilicate Mg—magnetite nanoparticles—Mg-ChR-NT/Fe₃O₄-NP” were obtained by coprecipitation. The composition of the synthesized samples has been established by X-ray diffraction. Using transmission electron microscopy, the presence of magnetite nanoparticles has been detected both inside the NTs and at the external surface of the NT walls. The specific surface of the NTs, nanoparticles, and composite is determined.     

Gd<Superscript>3+</Superscript> doped Fe<Subscript>3</Subscript>O<Subscript>4</Subscript> nanoparticles with proper magnetic and supercapacitive characteristics: A novel synthesis platform and characterization

A novel electrochemical procedure was developed for the facile preparation of Gd-doped iron oxide nanoparticles (GdIO-NPs). A simple galvanostatic deposition (i=10 mA cm^-2) was done in an additive-free aqueous solution containing FeCl₂·4H₂O, Fe(NO₃)₃·9H₂O and GdCl₃·6H₂O. The XRD, FE-SEM, EDS and TEM characterizations showed that the product is composed of 15% GdIO-NPs with 10 nm in size. VSM analysis proved that the GdIO-NPs are superparamagnetic. The cyclic voltammetry and charge-discharge tests showed that the prepared GdIO-NPs are capable to deliver specific capacity as high as 190.1 F g^-1 at 0.5A g^-1 and capacity retention of 95.1% after 2000 cycling. Based on the results, it was concluded that the developed electrochemical strategy acts as an efficient procedure for the preparation of lanthanide doped MNPs with proper magnetic and supercapacitive characters.