Oxygen potential of (U0.88Pu0.12)O2±x and (U0.7Pu0.3)O2±x at high temperatures of 1673-1873 K

The oxygen potential of (U_0.88Pu_0.12)O_2±x (−0.0119 < x < 0.0408) and (U_0.7Pu_0.3)O_2±x (−0.0363 < x < 0.0288) was measured at high temperatures of 1673-1873 K using gas equilibrium method with thermo gravimeter. The measured data were analyzed by a defect chemistry model. Expressions were derived to represent the oxygen potential based on defect chemistry as functions of temperature and oxygen-to-metal ratio. The thermodynamic data, and , at stoichiometric composition were obtained. The expressions can be used for in situ determination of the oxygen-to-metal ratio by the gas-equilibration method. The calculation results were consistent with measured data. It was estimated that addition of 1 wt.% Pu content increased oxygen potential of uranium and plutonium mixed oxide by 2-5 kJ/mol.     

Oxygen potential measurements of Am0.5Pu0.5O2−x by EMF method

The dependence of the oxygen potentials on oxygen non-stoichiometry and temperature of Am_0.5Pu_0.5O_2−x has been obtained by the electromotive force (EMF) method with the cell: (Pt) air |Zr(Ca)O_2−x| Am_0.5Pu_0.5O_2−x (Pt). The x value of Am_0.5Pu_0.5O_2−x was changed at 1333 K over 0.02 < x ? 0.25 by the coulomb titration method. The temperature dependence of the oxygen potential was also measured over the range of 1173-1333 K. It was found that the oxygen potential decreased from −80 to −360 kJ mol⁻¹ with increasing x from 0.021 to 0.22 at 1333 K and that it remained almost constant at −360 kJmol⁻¹ around x = 0.23. It was concluded that Am_0.5Pu_0.5O_2−x should be composed of the single fluorite-type phase over 0.02 < x ? 0.22 and the mixed phases of fluorite-type and (Am, Pu)₉O₁₆ at around x = 0.23.     

Lattice parameters of (U, Pu, Am, Np)O2−x

The solid solutions of (U_{1−z−y’−y”}Pu_zAm_y’Np_y”)O_2−x (z = 0-1, y’ = 0-0.12, y” = 0-0.07) were investigated by X-ray diffraction measurements, and a database for the lattice parameters was updated. A model to calculate the lattice parameters was derived from the database. The radii of the ions present in the fluorite structure of (U, Pu, Am, Np)O_2−x were estimated from the lattice parameters measured in this work. The model represented the experimental data within a standard deviation of σ = ±0.025%.     

Thermodynamic properties of ThxU1−xO2 (0 < x < 1) based on quantum-mechanical calculations and Monte-Carlo simulations

Th_xU_1−xO_2+y binary compositions occur in nature, uranothorianite, and as a mixed oxide nuclear fuel. As a nuclear fuel, important properties, such as the melting point, thermal conductivity, and the thermal expansion coefficient change as a function of composition. Additionally, for direct disposal of Th_xU_1−xO₂, the chemical durability changes as a function of composition, with the dissolution rate decreasing with increasing thoria content. UO₂ and ThO₂ have the same isometric structure, and the ionic radii of 8-fold coordinated U⁴⁺ and Th⁴⁺ are similar (1.14 nm and 1.19 nm, respectively). Thus, this binary is expected to form a complete solid solution. However, atomic-scale measurements or simulations of cation ordering and the associated thermodynamic properties of the Th_xU_1−xO₂ system have yet to be determined. A combination of density-functional theory, Monte-Carlo methods, and thermodynamic integration are used to calculate thermodynamic properties of the Th_xU_1−xO₂ binary (ΔH_mix, ΔG_mix, ΔS_mix, phase diagram). The Gibbs free energy of mixing (ΔG_mix) shows a miscibility gap at equilibration temperatures below 1000 K (e.g., E_exsoln = 0.13 kJ/(mol cations) at 750 K). Such a miscibility gap may indicate possible exsolution (i.e., phase separation upon cooling). A unique approach to evaluate the likelihood and kinetics of forming interfaces between U-rich and Th-rich has been chosen that compares the energy gain of forming separate phases with estimated energy losses of forming necessary interfaces. The result of such an approach is that the thermodynamic gain of phase separation does not overcome the increase in interface energy between exsolution lamellae for thin exsolution lamellae (10 Å). Lamella formation becomes energetically favorable with a reduction of the interface area and, thus, an increase in lamella thickness to >45 Å. However, this increase in lamellae thickness may be diffusion limited. Monte-Carlo simulations converge to an exsolved structure [lamellae || ] only for very low equilibration temperatures (below room temperature). In addition to the weak tendency to exsolve, there is an ordered arrangement of Th and U in the solid solution [alternating U and Th layers || {1 0 0}] that is energetically favored for the homogeneously mixed 50% Th configurations. Still, this tendency to order is so weak that ordering is seldom reached due to kinetic hindrances. The configurational entropy of mixing (ΔS_mix) is approximately equal to the point entropy at all temperatures, indicating that the system is not ordered.     

Raman spectroscopy characterization of actinide oxides (U1−yPuy)O2: Resistance to oxidation by the laser beam and examination of defects

Structural changes in four (U_1−yPu_y)O₂ materials with very different plutonium concentrations (0 ? y ? 1) and damage levels (up to 110 dpa) were studied by Raman spectroscopy. The novel experimental approach developed for this purpose consisted in using a laser beam as a heat source to assess the reactivity and structural changes of these materials according to the power supplied locally by the laser. The experiments were carried out in air and in water with or without hydrogen peroxide. As expected, the material response to oxidation in air depends on the plutonium content of the test oxide. At the highest power levels U₃O₈ generally forms with UO₂ whereas no significant change in the spectra indicating oxidation is observed for samples with high plutonium content (²³⁹PuO₂). Samples containing 25 wt.% plutonium exhibit intermediate behavior, typified mainly by a higher-intensity 632 cm⁻¹ peak and the disappearance of the 1LO peak at 575 cm⁻¹. This can be attributed to the presence of anion sublattice defects without any formation of higher oxides. The range of materials examined also allowed us to distinguish partly the chemical effects of alpha self-irradiation. The results obtained with water and hydrogen peroxide (a water radiolysis product) on a severely damaged ²³⁸PuO₂ specimen highlight a specific behavior, observed for the first time.     

Light ion irradiation effects on stuffed Lu2(Ti2−xLux)O7−x/2 (x = 0, 0.4 and 0.67) structures

We have recently synthesized “stuffed” (i.e., excess Lu) Lu₂(Ti_2−xLu_x)O_7−x/2 (x = 0, 0.4 and 0.67) compounds using conventional ceramic processing. X-ray diffraction measurements indicate that stuffing more Lu³⁺ cations into the oxide structure leads eventually to an order-to-disorder (O-D) transition, from an ordered pyrochlore to a disordered fluorite crystal structure. At the maximum deviation in stoichiometry (x = 0.67), the Lu³⁺ and Ti⁴⁺ ions become completely randomized on the cation sublattices, and the oxygen “vacancies” are randomized on the anion sublattice. Samples were irradiated with 400 keV Ne²⁺ ions to fluences ranging from 1 × 10¹⁵ to 1 × 10¹⁶ ions/cm² at cryogenic temperatures (∼77 K). Ion irradiation effects in these samples were examined by using grazing incident X-ray diffraction. The results show that the ion irradiation tolerance increases with disordering extent in the non-stoichiometric Lu₂(Ti_2−xLu_x)O_7−x/2.     

Oxygen non-stoichiometries in (Th0.7Ce0.3)O2−x

Oxygen non-stoichiometry in (Th_0.7Ce_0.3)O_2−x oxide solid solutions was investigated from the viewpoint of Ce reduction. The oxygen non-stoichiometry was experimentally determined by means of thermogravimetric analysis as a function of oxygen potential at 1173, 1273 and 1373 K. Features of the isotherms of oxygen non-stoichiometry in (Th_0.7Ce_0.3)O_2−x similar to those in oxygen non-stoichiometric actinide and lanthanide dioxides were observed. The oxygen non-stoichiometry in (Th_0.7Ce_0.3)O_2−x was compared with those of CeO_2−x and (U_0.7Ce_0.3)O_2−x. It was concluded that the Ce reduction has some relation to defect forms and their transformations in the solid solutions.     

Phase relations and linear thermal expansion of cubic solid solutions in the Th1−xMxO2−x/2 (M = Eu, Gd, Dy) systems

Cell parameters and linear thermal expansion studies of the Th-M oxide systems with general compositions Th_1−xM_xO_2−x/2 (M = Eu³⁺, Gd³⁺ and Dy³⁺, 0.0 ? x ? 1.0) are reported. The XRD patterns of each product were refined to specify the solid solubility limits of MO_1.5 in the ThO₂ lattice. The upper solid solubility limits of EuO_1.5, GdO_1.5 and DyO_1.5 in the ThO₂ lattice under conditions of slow cooling from 1673 K are represented as Th_0.50Eu_0.50O_1.75, Th_0.60Gd_0.40O_1.80 and Th_0.85Dy_0.15O_1.925, respectively. The linear thermal expansion (293-1123 K) of MO_1.5 and their single-phase solid solutions with thoria were investigated by dilatometery. The average linear thermal expansion coefficients () of the compounds decrease on going from EuO_1.5 to DyO_1.5. The values of for EuO_1.5, GdO_1.5 and DyO_1.5 containing solid solutions showed a downward trend as a function of the dopant concentration. The linear thermal expansion (293-1473 K) of the solid solutions investigated by high-temperature XRD also showed a similar trend.     

Vapour pressure and standard enthalpy of sublimation of H3BO3

A horizontal thermal analysis instrument was adapted as a transpiration apparatus for the measurement of vapour pressure of solid boric acid, H₃BO₃. The experimental parameters necessary for establishing a dynamic isothermal congruent vapourisation equilibrium of H₃BO₃ were identified. Using these optimized transpiration experiments, the vapour pressures were measured in the temperature range 326-363 K. The temperature dependence of the measured values of vapour pressures could be expressed using the expression, log(p/Pa) = 26.83(±0.09) − 9094(±246)/T (K). The standard enthalpy of sublimation, , of H₃BO₃ was estimated to be 174.1 ± 4.7 kJ mol⁻¹ at the mean temperature of the present measurements, viz., 345 K.     

Vaporization behavior and Gibbs energy of formation of Rb2ThO3

The thermodynamic stability of rubidium thorate, Rb₂ThO₃(s), was determined from vaporization studies using the Knudsen effusion forward collection technique. Rb₂ThO₃(s) vaporized incongruently and predominantly as Rb₂ThO₃(s)=ThO₂(s) + 2Rb(g) + 1/2 O₂(g). The equilibrium constant K=p_Rb²·p_O2^1/2 was evaluated from the measurement of the effusive flux due to Rb vapor species under the oxygen potential governed by the stoichiometric loss of the chemical component Rb₂O from the thorate phase. The Gibbs energy of formation of Rb₂ThO₃ derived from the measurement and other auxiliary data could be given by the equation, Δ_fG°(Rb₂ThO₃,s)=−1794.7+0.42T ± .     

Melting behavior of MgO-based inert matrix fuels containing (Pu,Am)O2−x

The melting behavior of MgO-based inert matrix fuels containing (Pu,Am)O_2−x ((Pu,Am)O_2−x-MgO fuels) was experimentally investigated. Heat-treatment tests were carried out at 2173 K, 2373 K and 2573 K each. The fuel melted at about 2573 K in the eutectic reaction of the Pu-Am-Mg-O system. The (Pu,Am)O_2−x grains, MgO grains and pores grew with increasing temperature. In addition, Am-rich oxide phases were formed in the (Pu,Am)O_2−x phase by heat-treatment at high temperatures. The melting behavior was compared with behaviors of PuO_2−x-MgO and AmO_2−x-MgO fuels.     

H2 inhibition of radiation induced dissolution of spent nuclear fuel

In order to elucidate the effect of noble metal clusters in spent nuclear fuel on the kinetics of radiation induced spent fuel dissolution we have used Pd particle doped UO₂ pellets. The catalytic effect of Pd particles on the kinetics of radiation induced dissolution of UO₂ during γ-irradiation in containing solutions purged with N₂ and H₂ was studied in this work. Four pellets with Pd concentrations of 0%, 0.1%, 1% and 3% were produced to mimic spent nuclear fuel. The pellets were placed in 10 mM aqueous solutions and γ-irradiated, and the dissolution of was measured spectrophotometrically as a function of time. Under N₂ atmosphere, 3% Pd prevent the dissolution of uranium by reduction with the radiolytically produced H₂, while the other pellets show a rate of dissolution of around 1.6 × 10⁻⁹ mol m⁻² s⁻¹. Under H₂ atmosphere already 0.1% Pd effectively prevents the dissolution of uranium, while the rate of dissolution for the pellet without Pd is 1.4 × 10⁻⁹ mol m⁻² s⁻¹. It is also shown in experiments without radiation in aqueous solutions containing H₂O₂ and O₂ that ?-particles catalyze the oxidation of the UO₂ matrix by these molecular oxidants, and that the kinetics of the catalyzed reactions is close to diffusion controlled.     

Influence of O/M ratio on sintering behavior of (U0.8, Pu0.2)O2±x

The shrinkage of (U_0.8, Pu_0.2)O_2±x pellets was investigated with the help of a thermal dilatometer in isothermal and isochronal heating tests. During shrinkage measurements in isothermal heating, the oxygen-to-metal ratio of the pellets was maintained at a constant value by controlling the oxygen potential in the sintering atmosphere. The influence of the oxygen-to-metal ratio on the sintering behavior was evaluated from the measurement results. Mainly two mechanisms dominated the sintering of mixed oxide pellets. When the oxygen-to-metal ratio was close to the stoichiometric composition, pellet shrinkage progressed at low temperatures of 1200-1600 K, and the shrinkage rate of the pellets drastically changed with a small deviation from stoichiometric composition. The result showed that a diffusion process was dominated during the sintering of near-stoichiometric compositions. On the other hand, the sintering of reduced mixed oxide pellet proceeded at high temperatures of 1600-1900 K, and the shrinkage rate was very low as compared with stoichiometric mixed oxide.     

Thermal conductivities of hypostoichiometric (U, Pu, Am)O2−x oxide

The thermal conductivities of (U_0.68Pu_0.30Am_0.02)O_2.00−x solid solutions (x = 0.00-0.08) were studied at temperatures from 900 to 1773 K. The thermal conductivities were obtained from the thermal diffusivities measured by the laser flash method. The thermal conductivities obtained experimentally up to about 1400 K could be expressed by a classical phonon transport model, λ = (A + BT)⁻¹, A(x) = 3.31 × x + 9.92 × 10⁻³ (mK/W) and B(x) = (−6.68 × x + 2.46) × 10⁻⁴ (m/W). The experimental A values showed a good agreement with theoretical predictions, but the experimental B values showed not so good agreement with the theoretical ones in the low O/M ratio region. From the comparison of A and B values obtained in this study with the ones of (U,Pu)O_2−x obtained by Duriez et al. [C. Duriez, J.P. Alessandri, T. Gervais, Y. Philipponneau, J. Nucl. Mater. 277 (2000) 143], the addition of Am into (U, Pu)O_2−x gave no significant effect on the O/M dependency of A and B values.     

Microstructural evolution in irradiated uranium-bearing delta-phase oxides A6U1O12 (A = Y, Gd, Ho, Yb, and Lu)

Irradiation-induced microstructural evolution in uranium-bearing delta-phase oxides of A₆U₁O₁₂ (A = rare earth cations) were characterized using grazing incidence X-ray diffraction and transmission electron microscopy. Polycrystalline Y₆U₁O₁₂, Gd₆U₁O₁₂, Ho₆U₁O₁₂, Yb₆U₁O₁₂, and Lu₆U₁O₁₂ samples were irradiated with 300 keV Kr⁺⁺ to a fluence of 2 × 10²⁰ ions/m² at cryogenic temperature (∼100 K). The crystal structure of these compounds was determined to be an ordered, fluorite derivative structure, known as the delta-phase, a rhombohedral symmetry belonging to space group . Experimental results indicate that all these compounds are resistant to amorphization to a displacement damage dose of ∼60 displacements per atom. In these experiments, we sometimes observed an irradiation-induced order-to-disorder phase transformation, from an ordered rhombohedral to a disordered fluorite structure.     

Ga NMR and magnetic susceptibility in δ-phase of Pu1−xGax (x = 0.05, x = 0.08) alloys

⁶⁹Ga nuclear magnetic resonance spectra, line shifts (⁶⁹K) and nuclear spin-lattice relaxation rate have been measured in the 20 years aged Pu_0.95Ga_0.05 and in fresh prepared Pu_0.92Ga_0.08 alloys, stabilized δ-phase, at magnetic field of 9.4 T in the temperature range (10-500) K. The line shift and are determined correspondingly by the static and fluctuating-in-time parts of the local magnetic field that originates in transferred hyperfine coupling the Ga nuclear spin with the nearest f-electron environment of more magnetic Pu.Temperature behavior of the resonance properties is found the same in fresh Pu_0.92Ga_0.08 and aged Pu_0.95Ga_0.05 alloy. The NMR results are in favor that δ-phase of Pu_1−xGa_x alloys represents at T > 200 K the Kondo lattice, in which the localized electronic spins fluctuate independently from each other without any macroscopic coherence. The coherent state like in heavy-fermion liquids emerges in Pu_0.95Ga_0.05 below T^∗ = 200 K. A little bit higher estimate of crossover temperature T^∗ = 250 K was founded for Pu_0.92Ga_0.08.     

Oxygen potential and thermal conductivity of (U, Pu) mixed oxides

(U, Pu) mixed oxides, (U_1−yPu_y)O_2−x, with y = 0.21 and 0.28 are being considered as fuels for the Prototype Fast Breeder Reactor (PFBR) in India. The use of urania-plutonia solid solutions in PFBR calls for accurate measurement of physicochemical properties of these materials. Hence, in the present study, oxygen potentials of (U_1−yPu_y)O_2−x, with y = 0.21 and 0.28 were measured over the temperature range 1073-1473 K covering an oxygen potential range of −550 to −300 kJ mol⁻¹ (O/M ratio from 1.96 to 2.000) by employing a H₂/H₂O gas equilibration technique followed by solid electrolyte EMFmeasurement. (U_1−yPu_y)O_2−x, with y = 0.40 is being used in the Fast Breeder Test Reactor (FBTR) in India to test the behaviour of fuels with high plutonium content. However, data on the oxygen potential as well as thermal conductivity of the mixed oxides with high plutonium content are scanty. Hence, the thermal diffusivity of (U_1−yPu_y)O₂, with y = 0.21, 0.28 and 0.40 was measured and the results of the measurements are reported.     

Thermal studies on fluorite type ZryU1−yO2 solid solutions

Solid state reactions of UO₂ and ZrO₂ in mild oxidizing condition followed by reduction at 1673 K showed enhanced solubility up to 35 mol% of zirconium in UO₂ forming cubic fluorite type Zr_yU_1−yO₂ solid solution. The lattice parameters and O/M (M = U + Zr) ratios of the solid solutions, Zr_yU_1−yO_2+x, prepared in different gas streams were investigated. The lattice parameters of these solid solutions were expressed as a linear equation of x and y: a₀ (nm) = 0.54704 − 0.021x - 0.030y. The oxidation of these solid solutions for 0.1 ? y ? 0.2 resulted in cubic phase MO_2+x up to700 K and single orthorhombic zirconium substituted α-U₃O₈ phase at 1000 K. The kinetics of oxidation of Zr_yU_1−yO₂ in air for y = 0-0.35 were also studied using thermogravimetry. The specific heat capacities of Zr_yU_1−yO₂ (y = 0-0.35) were measured using heat flux differential scanning calorimetry in the temperature range of 334-860 K.     

The U0.8Pu0.2C-W system

A phase diagram of the U_0.8Pu_0.2C-W system has been established based on X-ray diffraction measurements and metallographic observations. A peritectic four-phase reaction has been found to occur at 2100 ± 40°C:

The peritectic point is close to U_0.8Pu_0.2C-27 wt.%W. Composition of the peritectic liquid is near 48(U + Pu)/18W/34C (at %) by analogy with the UC-W system. The liquid phase transforms, during rapid cooling, to a metastable mixture [(U, Pu)C + (U, Pu)metal + W] with accompanied retention of (U, Pu)WC_1.75. The (U, Pu)WC_1.75 phase crystallizes in a UWC_1.75-type monoclinic structure. Essentially single-phase (U_0.8Pu_0.2)WC_1.75 has been produced by sufficient annealing of the arc-melted specimen, with lattice parameters: a₀ = 5.6257 ± 0.0008 Å, b₀= 3.2498 ± 0.0005Å, c₀ = 11.623 ± 0.002 Å, β = 109.61 ± 0.01°. This compound perhaps melts incongruently as:

The terminal solid solubility limit of tungsten in U_0.8Pu_0.2C increases from about 0.8 wt%W at 1500°C to a maximum of about 3.2 wt%W at 2100°C. The partial molar heat of solution of tungsten in U_0.8Pu_0.2C is approximately 14.4 kcal/mole. Un diagramme de phase du système U_0,8Pu_0,2C-W a étée'tabli en se basant sur les mesures par diffraction aux rayons X et par examen métallographique. Une réaction péritectique a quatre phases a été observée à 2100 ± 40°C:

     

Absorption and photoluminescence study of Al2O3 single crystal irradiated with fast neutrons

Colour centers formation in Al₂O₃ by reactor neutrons were investigated by optical measurements (absorption and photoluminescence). The irradiation’s were performed at 40 °C, up to fast neutron (E_n > 1.2 MeV) fluence of 1.4 × 10¹⁸ n cm⁻². After irradiation the coloration of the sample increases with the neutron fluence and absorption band at about 203, 255, 300, 357 and 450 nm appear in the UV-visible spectrum. The evolution of each absorption bands as a function of fluence and annealing temperature is presented and discussed. The results indicate that at higher fluence and above 350 °C the F⁺ center starts to aggregate to F center clusters (F₂, F₂⁺ and ). These aggregates disappear completely above 650 °C whereas the F and F⁺ centers persist even after annealing at 900 °C. It is clear also from the results that the absorption band at 300 nm is due to the contribution of both F₂ center and interstitial ions.