Localized mechanical property assessment of SiC/SiC composite materials

SiC fiber-reinforced SiC matrix composites (SiC/SiC) are under consideration as a structural material for a range of nuclear applications. While these materials have been studied for decades, recently new small scale materials testing techniques have emerged which can be used to characterize SiC/SiC materials from a new perspective. In this work cross section nanoindentation was performed on SiC/SiC composites revealing that both the hardness and Young’s modulus was substantially lower in the fiber compared to the matrix despite both being SiC. Using scanning electron microscopy it was observed that the grain growth of the matrix during formation was radially out from the fiber with a changing grain structure as a function of radius from the fiber center. Focused ion beam machining was used to manufacture micro-cantilever samples and evaluate the fracture toughness and fracture strength in the matrix as a function of grain orientation in the matrix. Additionally microstructural characterization techniques like Raman spectroscopy, X-ray diffraction, and microtomography were used to evaluate differences in the matrix and fibers of the composite.     

Extraction of cellulose nanocrystals from plant sources for application as reinforcing agent in polymers

In the last few decades, the usages of plant sources-based stiff fillers as reinforcement material in polymer composites have attracted significant interests of researchers. The crystalline part of the semicrystalline cellulose chains as found in the plant cell walls represents the most highly potential reinforcing agents for polymer. This review systematically covers the extraction of nano-sized cellulose crystals from plant cell wall which involving the applications of several highly effective techniques. The topic about the derivation of products functionality at each stage as well as their influences on the final reinforcing capability is also covered. Apart from these, a detailed overview of current knowledge on the surface modification of nanocellulose has been provided also. Inasmuch, this paper is desired to encourage the emergence of preparation of cellulose derivative nanocrystals with controlled morphology, structure and properties, so that enable positive development of biocompatible, renewable and sustainable reinforcing materials for polymer composites field.     

Measurement of resistance curves in the longitudinal failure of composites using digital image correlation

This paper presents a new methodology to measure the crack resistance curves associated with fiber-dominated failure modes in polymer–matrix composites. The crack resistance curves not only characterize the fracture toughness of the material, but are also the basis for the identification of the parameters of the softening laws used in the numerical simulation of fracture in composite materials. The proposed method is based on the identification of the crack tip location using Digital Image Correlation and the calculation of the J-integral directly from the test data using a simple expression derived for cross-ply composite laminates. It is shown that the results obtained using the proposed methodology yield crack resistance curves similar to those obtained using Finite Element based methods for compact tension carbon–epoxy specimens. However, it is also shown that, while the Digital Image Correlation based technique mitigates the problems resulting from Finite Element based data reduction schemes applied to compact compression tests, the delamination that accompanies the propagation of a kink-band renders compact compression test specimens unsuitable to measure resistance curves associated with fiber kinking.     

Microwave assisted-in situ synthesis of porous titanium/calcium phosphate composites and their in vitro apatite-forming capability

Microwave irradiation has been proven to be an effective heating source in synthetic chemistry, and can accelerate the reaction rate, provide more uniform heating and help in developing better synthetic routes for the fabrication of bone-grafting implant materials. In this study, a new technique, which comprises microwave heating and powder metallurgy for in situ synthesis of Ti/CaP composites by using Ti powders, calcium carbonate (CaCO₃) powders and dicalcium phosphate dihydrate (CaHPO₄·2H₂O) powders, has been developed. Three different compositions of Ti:CaCO₃:CaHPO₄·2H₂O powdered mixture were employed to investigate the effect of the starting atomic ratio of the CaCO₃ to CaHPO₄·2H₂O on the phase, microstructural formation and compressive properties of the microwave synthesized composites. When the starting atomic ratio reaches 1.67, composites containing mainly alpha-titanium (α-Ti), hydroxyapatite (HA), beta-tricalcium phosphate (β-TCP) and calcium titanate (CaTiO₃) with porosity of 26%, pore size up to 152 μm, compressive strength of 212 MPa and compressive modulus of 12 GPa were formed. The in vitro apatite-forming capability of the composite was evaluated by immersing the composite into a simulated body fluid (SBF) for up to 14 days. The results showed that biodissolution occurred, followed by apatite precipitation after immersion in the SBF, suggesting that the composites are suitable for bone implant applications as apatite is an essential intermediate layer for bone cells attachment. The quantity and size of the apatite globules increased over the immersion time. After 14 days of immersion, the composite surface was fully covered by an apatite layer with a Ca/P atomic ratio approximately of 1.68, which is similar to the bone-like apatite appearing in human hard tissue. The results suggested that the microwave assisted-in situ synthesis technique can be used as an alternative to traditional powder metallurgy for the fabrication of Ti/CaP biocomposites.     

Tensile and thermomechanical properties of short carbon fiber reinforced polyamide 6 composites

In this study, carbon fiber (CF) reinforced polyamide 6 (PA6) composites were prepared by using melt mixing method. Effects of fiber length and content, on the mechanical, thermal and morphological properties of CF reinforced PA6 composites were investigated. Fiber length distributions of composites were also determined by using an image analyzing program. It was seen that the maximum number of fibers were observed in the range of 0–50 μm. Mechanical test results showed that, increasing CF content increased the tensile strength, modulus and hardness values but decreased strain at break values of composites. DSC results showed that T_g and T_m values of composites were not changed significantly with increasing CF content and length. However, heat of fusion and the relative degree of crystallinity values of composites decreased with ascending CF content. DMA results revealed that storage modulus and loss modulus values of composites increased with increasing CF content.     

A review on basalt fibre and its composites

In recent years, both industrial and academic world are focussing their attention toward the development of sustainable composites, reinforced with natural fibres. In particular, among the natural fibres (i.e. animal, vegetable or mineral) that can be used as reinforcement, the basalt ones represent the most interesting for their properties. The aim of this review is to illustrate the results of research on this topical subject. In the introduction, mechanical, thermal and chemical properties of basalt fibre have been reviewed. Moreover, its main manufacturing technologies have been described. Then, the effect of using this mineral fibre as reinforcement of different matrices as polymer (both thermoplastic and thermoset), metal and concrete has been presented. Furthermore, an overview on the application of this fibre in biodegradable matrix composites and in hybrid composites has been provided. Finally, the studies on the industrial applications of basalt fibre reinforced composites have been reviewed.     

The use of composite materials in modern orthopaedic medicine and prosthetic devices: A review

The use of fibre reinforced composite materials for biomedical purposes is reviewed. The development of polymer composite materials has, in recent years, led to technological advances across a wide range of applications in modern orthopaedic medicine and prosthetic devices. Composites typically possess a superior strength to weight characteristic compared to monolithic materials and offer excellent biocompatibility. They are, therefore, favourable for both hard- and soft-tissue applications as well as the design of prostheses. In particular, the development of specifically designed carbon fibre sports prostheses now allows lower-limb amputees to actively participate in competitive sports. Sensory feedback systems, porous composite materials for tissue engineering and functional coatings for metallic implants are further developments anticipated to be introduced in next generation orthopaedic medicine.     

Lignocellulosic fibre mediated rubber composites: An overview

The rising concern towards the reduction in the use of petroleum-based, non-renewable resources and the need for more versatile polymer-based composite materials have led to increasing interests on natural polymer composites filled with natural organic fillers, i.e. coming from renewable and biodegradable sources. This paper reviews wood flour and other lignocellulosic fibres filled rubber composites, including cellulosic rubber composites, cellulosic thermoplastic elastomers, nanocellulose based rubber nanocomposites, with the aims at providing the most state of the art information for directing further scientific research, possible commercialization and design of cellulosic rubber composites. It has been found that 1) the surface properties of natural cellulose, hence the compatibility and interface of the natural cellulose and matrix rubber/plastics, are crucial for the successful development of the composites, such, physical and chemical modification and additives have been widely attempted to improve the incompatibility and poor interfacial adhesion between the filler and matrix; 2) the curing characteristics, mechanical properties, thermal stability and morphologies of the composites are complex but closely related to not only the interfacial properties, but also the compositions (e.g. the concentration of cellulosic materials) and other processing parameters; 3) the nature of hydrophilic cellulosic and hydrophobic matrix rubber and/or plastics requires an accurate introduction of coupling agent, one end of its structure shall be compatible to hydrophilic and the other to hydrophobic. The reviews on the main paths and results of study on the advanced nanocellulose reinforced rubber nanocomposites and sandwiches indicate much potentials and needs for further in-depth studies.     

Development of a new constitutive model considering the shearing effect for anisotropic progressive damage in fiber-reinforced composites

A corrected Linde's criterion considering the shearing effect for anisotropic progressive damage is developed to describe the elastic-brittle behavior of fiber-reinforced composites. Based on this criterion, a new three-dimensional (3D) nonlinear finite element model for static damage of unidirectional fiber-reinforced composites is proposed within a framework of continuum mechanics. The model is validated by taking 3D braided composites as example to study the relationship between the damage of materials and the effective elastic properties. The impregnated unidirectional composites are treated as homogeneous and transversely isotropic materials, whose properties are calculated by the Chamis' equations. The more accurate failure mechanisms of composites are revealed in the simulation process, and the effects of braided parameters on the uniaxial tensile behavior of 3D braided composites are investigated. Comparison of numerical results and experimental data is also carried out, which shows a better agreement than that of former study using the 3D Hashin's criterion.     

Effects of aluminium nitride inclusions on thermal and electrical properties of epoxy and polypropylene: An experimental investigation

Thermal and dielectric properties of polymers reinforced with micro-sized aluminium nitride (AlN) particles have been studied. A set of epoxy–AlN composites, with filler content ranging from 0 to 25 vol% is prepared by hand lay-up technique. With similar filler loading, polypropylene -AlN composites are fabricated by compression molding technique. Density (ρ_c), effective thermal conductivity (k_eff), glass transition temperature (T_g), coefficient of thermal expansion (CTE) and dielectric constant (ε_c) of these composites are measured experimentally. The various experimental data were interpreted using appropriate theoretical models. Incorporation of AlN in both the resin increases the k_eff and T_g whereas CTE of composite decreases favourably. The dielectric constant of the composite also found to get modified with filler content. With improved thermal and modified dielectric characteristics, these AlN filled polymer composites can possibly be used for microelectronics applications.     

A composite material used as a membrane for ophthalmology applications

New biomaterials for intracorneal ophthalmologic implants were designed, manufactured and characterized. A composite material in the form of a membrane was manufactured in a two-stage process. The first stage of the process depended on preparation of multidimensional (MD-type) fibrous polymer composite. A stable terpolymer polytetraflouroethylene-co-polyvinylene fluoride-co-polypropylene (PTFE–PVDF–PP) was used as a composite matrix, and sodium alginate-based biopolymer (NA) in the form of short fibres and/or powder were used as porogenic constituents. The composite materials were subjected to physicochemical treatment in order to remove a water soluble biopolymer. The treatment led to about 50% of open porosity within the polymer matrix. Depending on the membrane type the mean pore size determined with SEM microphotographs was 15–25 μm. Permeability and durability of the membranes in simulated eye fluid (culture medium enriched with albumin) was tested. The size and shape of the pores before and after the permeability test were compared (SEM), and they depend on the porogen form. Mechanical parameters of the composite materials such as; tensile strength, Young’s modulus, and strain to failure were measured. A membrane derived from fibres and particles showed better mechanical properties than a membrane derived from porogen particles. Microstructure and mechanical properties make the membranes a good candidate for ophthalmological implants.     

Nano-epoxy resins containing electrospun carbon nanofibers and the resulting hybrid multi-scale composites

For the first time, electrospun carbon nanofibers (ECNFs, with diameters and lengths of ∼200 nm and ∼15 μm, respectively) were explored for the preparation of nano-epoxy resins; and the prepared resins were further investigated for the fabrication of hybrid multi-scale composites with woven fabrics of conventional carbon fibers via the technique of vacuum assisted resin transfer molding (VARTM). For comparison, vapor growth carbon nanofibers (VGCNFs) and graphite carbon nanofibers (GCNFs) were also studied for making nano-epoxy resins and hybrid multi-scale composites. Unlike VGCNFs and GCNFs that are prepared by bottom-up methods, ECNFs are produced through a top-down approach; hence, ECNFs are more cost-effective than VGCNFs and GCNFs. The results indicated that the incorporation of a small mass fraction (e.g., 0.1% and 0.3%) of ECNFs into epoxy resin would result in substantial improvements on impact absorption energy, inter-laminar shear strength, and flexural properties for both nano-epoxy resins and hybrid multi-scale composites. In general, the reinforcement effect of ECNFs was similar to that of VGCNFs, while it was higher than that of GCNFs.     

Biodegradability of all-cellulose composite laminates

The high mechanical properties of single-polymer composites based on degradable non-derivatised cellulose, aka all-cellulose composites, have recently captured the attention of researchers. All-cellulose composites possess the intriguing combination of high strength and biodegradability. However, the biodegradation behaviour of all-cellulose composites has so far not been reported. In this work, soil burial experiments were carried out to compare the biodegradation behaviour of all-cellulose composites with conventional biocomposites in order to investigate the end-of-life disposal of this relatively new class of bio-based composite materials. All-cellulose composites are characterised by exceptional biodegradability with mass losses of up to 73% following a soil burial time of 70 days. An investigation of the mechanisms of biodegradation of all-cellulose composites is undertaken for the first time.     

Study on short ramie fiber/poly(lactic acid) composites compatibilized by maleic anhydride

Short ramie fiber reinforced poly(lactic acid) (PLA) composites without and with maleic anhydride (MA) were developed. The influence of PLA-g-MA as a compatibilizer on the properties of the composites was studied. The tensile, flexural and impact strength of the composites have improvements with the addition of PLA-g-MA. The morphology of fracture surface evaluated by SEM indicates that the composites with the addition of PLA-g-MA can get better adhesion between the fiber and the matrix. And the Vicat softening temperature and the degradation temperature of the composites are increased with the addition of PLA-g-MA. However, PLA-g-MA leads the glass transition temperature (T_g) decrease according to the DSC results.     

The influence of nano/micro hybrid structure on the mechanical and self-sensing properties of carbon nanotube-microparticle reinforced epoxy matrix composite

Nano/micrometer hybrids are prepared by chemical vapor deposition growth of carbon nanotubes (CNTs) on SiC, Al₂O₃ and graphene nanoplatelet (GNP). The mechanical and self-sensing behaviors of the hybrids reinforced epoxy composites are found to be highly dependent on CNT aspect ratio (AR), organization and substrates. The CNT–GNP hybrids exhibit the most significant reinforcing effectiveness, among the three hybrids with AR1200. During tensile loading, the in situ electrical resistance of the CNT–GNP/epoxy and the CNT–SiC/epoxy composites gradually increases to a maximum value and then decreases, which is remarkably different from the monotonic increase in the CNT–Al₂O₃/epoxy composites. However, the CNT–Al₂O₃ with increased AR ⩾ 2000 endows the similar resistance change as the other two hybrids. Besides, when AR < 3200, the tensile modulus and strength of the CNT–Al₂O₃/epoxy composites gradually increase with AR. The interrelationship between the hybrid structure and the mechanical and self-sensing behaviors of the composites are analyzed.     

Molecular characterizations,mechanical properties and anti-algal activities for PVC and wood/PVC composites containing urea- and triazine-based algaecides

Material behaviors and anti-algal performances of PVC and wood PVC composites (WPVCs) were examined after adding commercial algaecides of different types and contents. Three different wood types commonly found in tropical climates – namely, Xylia kerrii Craib and Hutch.; Hevea brasiliensis Muell.; and Mangifera indica Linn. – were of interest. Isoproturon (3-(4-isopropylphenyl)-1,1-dimethylurea), a urea-based algaecide, and Terbutryn (N²-tert-butyl-N⁴-ethyl-6-methylthio-1,3,5-triazine-2,4-diamine), a triazine-based algaecide, were used as anti-algal agents in this study; concentrations in the specimens varied from 0 to 1500 ppm. Surface color, thermal properties, chemical structure and mechanical properties of the materials were also monitored. The results revealed that addition of Isoproturon tended to considerably change the surface color of the materials, particularly for PVC which had the highest ΔE^* value, whereas addition of Terbutryn did not. The effect of wood types was found to influence the initial surface color of the materials. Evidence based on DSC, FT-IR and contact angle testing indicated that Isoproturon had a strong molecular interaction with PVC and could induce PVC degradation. The mechanical properties of PVC and WPVC were affected by the addition of wood, but not by algaecide addition. The results of the growth inhibition zone and chlorophyll-a content in Chlorella vulgaris TISTR 8580 suggested that Terbutryn exhibited better anti-algal performance than Isoproturon with a recommended dosage of 1000 ppm while Isoproturon at 1500 ppm could act as an effective coupling agent in WPVC composites.     

Optimal design of customised hip prosthesis using fiber reinforced polymer composites

The need for new materials in orthopaedic surgery arises from the recognition of the stress-shielding effect of bone by high-modulus implants presently made of engineering alloys. A lower modulus implant material will result in the construction of a more biomechanically compatible prosthesis. In this respect, composite materials are gaining importance because they offer the potential for implants with tailor-made stiffness in contrast to metals. In the present study, the bending stiffness of composite prosthesis is matched with that of bone in both the longitudinal and radial directions by choosing optimal carbon fiber reinforced polyether ether ketone (PEEK) matrix lay-up. A numerical optimization algorithm is developed to deduce the optimal composite femoral prosthesis lay-up that matches the stiffness properties of the femoral bone in both the transverse and longitudinal directions. Effective bending moments and compressive forces acting on the hip joint are considered in the design of the optimal length and diameter of the prosthesis. The optimization algorithm was implemented, by using MATLAB(R)™ for designing the composite prosthesis to a patient’s specific requirement. Finally the efficiency of the composite stem is compared with that of metallic alloy stems in terms of stress shielding using a finite element program.     

Growing polystyrene chains from the surface of graphene layers via RAFT polymerization and the influence on their thermal properties

The polystyrene (PS) macromolecular chains were grafted on the surface of graphene layers by reversible addition-fragmentation chain transfer (RAFT) polymerization. In this procedure, a RAFT agent, 4-Cyano-4-[(dodecylsulfanylthiocarbonyl) sulfanyl] pentanoic acid, was used to functionalize the thermal reduced graphene oxide (TRGO) to obtain the precursor (TRGO-RAFT). It can be calculated that the grafting density of PS/graphene (PRG) composites was about 0.18 chains per 100 carbons. Successful in-plain attachment of RAFT agent to TRGO and PS chain to TRGO-RAFT was shown an influence on the thermal property of the PRG composites. The thermal conductivity (λ) improved from 0.150 W m⁻¹ K⁻¹ of neat PS to 0.250 W m⁻¹ K⁻¹ of PRG composites with 10 wt% graphene sheets loading. The thermal property of PRG composites increased due to the homogeneous dispersion and ordered arrangement of graphene sheets in PS matrix and the formation of PRG composites.     

Assessment of three oxide/oxide ceramic matrix composites: Mechanical performance and effects of heat treatments

Mechanical performance of three oxide/oxide ceramic matrix composites (CMCs) based on Nextel 610 fibers and SiOC, alumina, and mullite/SiOC matrices respectively, is evaluated herein. Tensile strength and stiffness of all materials decreased at 1000 °C and 1200 °C, probably because of degradation of fiber properties beyond 1000 °C. Microstructural changes in the composites during exposure at 1000 °C and 1200 °C for 50 h reduce their flexural strength, fracture toughness and work of fracture. A literature review regarding mechanical properties of several oxide/oxide CMCs revealed lower influence of fiber properties on composite strength compared with elastic modulus. The tested composites exhibit comparable stiffness and strength but higher fracture toughness compared with average values determined from a literature review. Considering CMCs with different compositions, we observed an interesting linear trend between strength and fracture toughness. The validity of the linear relationship between fracture strength and flexural toughness for CMCs is discussed.     

Effect of fiber loading on the properties of treated cellulose fiber-reinforced phenolic composites

The effect of fiber loading on the properties of treated cellulose fiber-reinforced phenolic composites was evaluated. Alkali treatment of the fibers and reaction with organosilanes as coupling agents were applied to improve fiber–matrix adhesion. Fiber loadings of 1, 3, 5, and 7 wt% were incorporated to the phenolic matrix and tensile, flexural, morphological and thermal properties of the resulting composites were studied. In general, mechanical properties of the composites showed a maximum at 3% of fiber loading and a uniform distribution of the fibers in such composites was observed. Silane treatment of the fibers provided derived composites with the best thermal and mechanical properties. Meanwhile, NaOH treatment improved thermal and flexural properties, but reduced tensile properties of the materials. Therefore, the phenolic composite containing 3% of silane treated cellulose fiber was selected as the material with optimal properties.