振动挤出对LDPE熔员结晶行为的影响

通过对低密度聚乙烯毛细管动态挤出进行测试分析,探讨了振动力对聚合物挤出物融结晶行为的影响,发现在ＬＤＰＥ熔体流动过程中叠加适当的振动力场后,ＬＤＰＥ挤出物的熔融始态明显变化,结晶度不变的同时,晶粒大小有较大降低,并认为这是振动力场对聚合内部结构产生影响的结果,研究结果对聚合物动态成型加工新的的深入理论研究具有十分重要的意义。     

LDPE 2102 TN 00在交联电缆绝缘料中的应用

利用拉伸试验、红外光谱、凝胶渗透色谱、差示扫描量热法、流变表征等方法．对2102 TN 00等几种低密度聚乙烯的性能进行了测试,并以2102 TN 00为基础树脂分别制备了硅烷交联和过氧化物交联聚乙烯电缆料。结果表明,2102 TN 00适合做聚乙烯交联电力电缆绝缘料的基础树脂。     

重包装薄膜用LDPE 2320D的工业开发

研究了重包装薄膜对低密度聚乙烯(LDPE)分子结构的要求,结合反应温度、反应压力、相对分子质量调节剂种类对LDPE分子结构的影响,确定了重包装薄膜用LDPE 2320D的关键工艺参数。反应压力为270~290MPa,反应器第一至四区的温度为280~290℃,采用丙烯和丙醛作为相对分子质量调节剂时,2320D的支化度为13.6~14.6个/1 000 C,密度为0.921 5~0.922 5 g/cm3,正己烷提取物含量小于60 mg/kg。用2320D吹塑的薄膜横向拉伸屈服应力约为11.0 MPa,雾度小于15.0%;30μm厚的薄膜在120℃加热60 s后,纵、横向收缩率分别为59.3%,29.7%,优于用进口同类产品吹塑的薄膜。     

高速挤出聚乙烯电缆绝缘料的开发

通过研究了以HDPE为基料生产高速通信电缆用绝缘料的分子量分布、流变性能和加工性能,在聚合时通过改变分子量调解剂量和工艺条件,改善其分子量分布使其具有双峰结构从而改善加工性能,结果表明:该产品具有优异的力学性能、介电性能、各项指标达到了邮电部YD/T760-1995标准;同时具有良好的加工性能,能够满足高速挤出的要求。     

LDPE共混改性PP的结晶行为及模压发泡效果

采用单螺杆挤出机制备了低密度聚乙烯(LDPE)共混改性聚丙烯(PP)可发性粒料,并通过模压发泡工艺得到改性PP发泡材料;考察了发泡剂的热分解特性以及LDPE的含量对共混体系的熔融/结晶行为、晶体结构和发泡性能的影响。结果表明:与纯偶氮二甲酰胺(AC)相比,复合发泡剂的分解温度下降了45℃;LDPE的引入没有改变PP的晶型结构,但降低了共混体系的结晶度;当LDPE的含量为15%～20%时,LDPE/PP共混体系的发泡效果最佳。     

振动挤出对LDPE熔融结晶行为的影响

通过对低密度聚乙烯(LDPE)毛细管动态挤出物进行测试分析,探讨了振动力场对聚合物挤出物熔融结晶行为的影响.发现在LDPE熔体流动过程中叠加适当的振动力场后,LDPE挤出物的熔融始态发生明显变化,结晶度不变的同时,晶粒大小有较大降低,并认为这是振动力场对聚合物内部结构产生影响的结果.研究结果对聚合物动态成型加工新技术的深入理论研究具有十分重要的意义.     

LDPE/POE共混物的结晶行为和力学性能

采用熔融共混法制备了低密度聚乙烯（LDPE）／聚烯烃弹性体（POE）共混物,通过差示扫描量热法和广角X射线衍射表征了共？昆物的结晶行为及LDPE、POE结晶的相互影响,研究了共混物的力学性能。随着POE用量的增加,LDPE的结品度稍有减小,结晶的完善性和均一性变差,晶粒尺寸逐渐变小;LDPE在结晶过程中出现了二次结晶;共混物的硬度、定伸应力和熔体流动速率均逐渐减小,拉伸断裂应变则逐渐增加。当w（POE）为30％时,材料的拉伸强度达到最大值,为21.5MPa。随着LDPE含量的增加,POE的结晶度逐渐减小。     

结晶条件对超高分子量聚乙烯熔融再结晶行为的影响

应用常压差示扫描量热(DSC)仪和高压DSC仪研究了熔融温度、熔融时间、冷却速率以及压力对不同分子量的超高分子量聚乙烯(PE–UHMW)熔融再结晶行为的影响。常压DSC的研究表明,随着熔融温度、熔融时间以及冷却速率的增加,PE–UHMW的结晶峰值温度(Tc)逐渐下降。在相同的熔融温度和熔融时间下,PE–UHMW的Tc随分子量的增加而逐渐增加,但在所研究的冷却速率范围内(2.5～40℃／min),在相同的冷却速率下,Tc随分子量的增加变化不大。高压DSC的研究结果表明,结晶过程中增加压力导致PE–UHMW的Tc有所下降,并且结晶峰半峰宽变大。     

LDPE及LDPE/TiO_2纳米复合材料的熔限及等温结晶研究

采用熔融共混法制备了LDPE／TiO2纳米复合材料,以膨胀计对LDPE及LDPE／TiO2复合材料的熔点、熔限及等温结晶进行了研究。结果表明：膨胀计可用于LDPE及LDPE／TiO2纳米复合材料熔点及熔限的测试：与LDPE相比,LDPE／TiO2复合体系的半结晶期及AVrami指数较小,表明TiO2粒子对LDPE的结晶具有明显的异相成核作用;而Avrrdmi指数为非整数,且Avrami作图直线的最后部分与实验点的偏离,则表明LDPE及LDPE／TiO2纳米复合材料的等温结晶过程比Avrami方程要复杂得多。     

微米铜颗粒对Cu/LDPE/MVQ复合材料非等温结晶性能的影响

采用注射成型法制备了铜/低密度聚乙烯/甲基乙烯基硅橡胶(Cu/LDPE/MVQ)复合材料和低密度聚乙烯/甲基乙烯基硅橡胶(LDPE/MVQ)复合材料,采用差示扫描量热法(DSC)研究了复合材料的非等温结晶行为。结果表明,随着冷却速率的加快,复合材料的结晶度逐渐增大。铜颗粒在复合材料中作为异相成核点,同时阻碍着LDPE分子链的运动。     

LDPE交联电缆料PE—K—18D022的开发研究

本文介绍了ＬＤＰＥ交联电缆料ＰＥ－Ｋ－１８Ｄ０２２的开发研制过程，包括：工艺参数的确定，过程控制，最终产品的性能等。生产实践和用户使用表明ＰＥ－Ｋ－１８Ｄ０２２的工艺过程，操作条件合理；生产参数确定准确；产品性能优良，经交联加工后生产的电缆料达到英国ＢＰ公司同类产品水平。     

管式法挤出涂层专用LDPE的性能及质量改进

针对管式工艺生产的挤出涂层专用低密度聚乙烯(LDPE)产品存在涂层与基材的黏结强度低、淋膜缩幅大等问题,通过与同类釜式产品的性能和结构的对比研究发现,管式产品的分子支化程度过低是造成其性能不佳的主要原因。分析了影响产品长链支化程度的工艺因素,并提出了增加产品长支链含量的方法。初步试生产表明:适当提高反应温度、降低反应压力并改变分子量调节剂的注入速度,可以有效地改善挤出涂层产品的性能。     

The effect of chain interpenetration on an ordering process in the early stage of polymer crystal nucleation

In the present study, the degree of chain interpenetration was considered as a structural attribute of the entanglements in polymer chain system. Inter-chain radial distribution function (RDF) was used to perform this measurement. We applied this method to a model system, in which an ordering process in the early stage of polymer crystal nucleation at the atomistic level was simulated by means of molecular dynamics (MD). Initial chain structures possessed different degrees of interpenetration and underwent the ordering process at 400 K. Obtained results indicated that at the nanosecond scale the degree of interpenetration impedes the ordering process remarkably, which agrees with the experimental observation at laboratory time scale. Such behavior among chains indicates that at the atomistic level a creeping polymer chain is able to recognize if the neighbor group on the ‘tube’ is from the same chain or other chains. This recognition manifests that the reptation time of a chain would be influenced by the ‘tube’ composition or the degree of interpenetration. It also showed that the degree of interpenetration changes little during the ordering process, which means that the motion of the chain segments is mainly predominated by the ordering process rather than further adjusting the entanglement extent under the conditions simulated.     

凝胶色谱法测定高聚物的平均分子量及分子量分布

介绍了用凝胶色谱法测定高聚物的平均分子量及分子量分布。     

Investigation of molecular structure of LDPE modified by itaconic acid grafting

Using thermomechanical spectroscopy, the molecular‐weight distribution and relaxation transitions have been investigated in commercial LDPE and grafted by itaconic acid (LDPE‐g‐IA). This grafting in the molten LDPE was done by reactive extrusion with varied content of reactants in the blend under alternating of a shearing rate applied onto the melt. The dependence of structural relaxation changes in LDPE is shown upon the depth of the mechanochemical transformations and the competing reactions at IA grafting, and also on the chemical crosslinking of the macromolecules. The reason for MWD bimodality for LDPE‐g‐IA obtained in dynamic mixing is the raised homogenization degree of the reactive blend and the higher grafted product yield compared with static mixers. The mixer type substantially affects the structure of the LDPE‐g‐IA amorphous phase. The data obtained reflect chemical transformations of LDPE molecules in IA's presence without an initiator of radical reactions (DCP). Most probable is the IA initiation of molecular crosslinking reactions. There could also occur IA thermodegradation and oligomerization. LDPE and IA or products of acid chemical transformations do not agree thermodynamically (the calculated solubility parameters are 16.1 (MJ/m³)^0.5 for polyethylene and 26.4 (MJ/m³)^0.5 for IA). From the above procedure it can be supposed that nongrafted IA (or its oligomers) exerts an antiplastifying effect on LDPE and LDPE‐g‐IA. © 1999 John Wiley & Sons, Inc. J Appl Polym Sci 71: 1771–1779, 1999     

影响超净电缆料用LDPE性能的因素分析

用乙烯为反应单体、过氧化物为引发剂、丙烯(或丙醛、乙烷、丁烯-1)为调节剂制备超净电缆料用低密度聚乙烯(LDPE),对生产过程中影响LDPE的介电性能、加工流变性能以及降低杂质含量等因素进行了分析,提出了改进措施,满足超净电缆料用LDPE的要求.     

HDPE树脂流变参数与分子量分布的关系研究

测定了4种高密度聚乙烯(HDPE)树脂的分子量及其分布,研究了其毛细管流变行为和动态流变行为,并分析了得到的流变参数和分子量分布的关系。结果表明:仅在较低挤出速度或较高温度条件下,用毛细管流变测得的非牛顿指数才能用作分子量分布的量度;用动态流变测得的剪切变稀指数、流变多分散指数、幂率指数均可在一定程度上反映了HDPE树脂分子量分布的大小,其中幂率指数与分子量分布的相关性最好(相关系数r2=0.994)。     

止血性壳聚糖的制备及其凝血效果的研究

在温和均相条件下,对较高脱乙酰度的壳聚糖进行乙酰化,制备不同脱乙酰度的壳聚糖;测试不同脱乙酰度和分子量的壳聚糖醋酸溶液的凝血效果。中药—壳聚糖复合止血材料的制备及其止血功能的研究。