链转移剂对含氟丙烯酸酯乳液制备及性能的影响

在链转移剂存在下进行了甲基丙烯酸三氟乙酯的乳液聚合,研究了链转移剂类型和用量以及引发剂用量对聚合物特性黏数、黏均相对分子质量、聚合反应转化率和稳定性、乳胶粒粒径、聚合物结构以及乳胶膜表面性能的影响.     

改性丙烯酸酯压敏胶的制备与性能研究

采用溶液聚合的方法,以丙烯酸异辛酯(2-EHA)为软单体、醋酸乙烯酯为硬单体、乙酸乙酯为溶剂、偶氮二异丁腈(AIBN)为引发剂制备聚丙烯酸酯压敏胶。试验考察了软硬单体的配比、功能单体丙烯酸(AA)和丙烯酸羟乙酯(2-HEA)的配比、交联单体A的含量对压敏胶综合性能的影响。研究结果表明:当m(2-EHA):m(醋酸乙烯酯):m(AA):m(2-HEA)=15:12:0.8:1,w(交联单体A)=0.14%(相对于单体总质量而言)时,制得的压敏胶具有较好的综合性能。由此制备的压敏胶粘带,其干胶厚度为15μm时,剥离强度为6.27 N/25 mm,初粘力为5#钢球,持粘力超过24 h,耐溶剂48 h不脱胶。     

耐热水丙烯酸酯乳液压敏胶研制成功

上海应用技术学院以丙烯酸-2-乙基己酯（2-EHA）、甲基丙烯酸甲酯（MMA）等为单体，N·羟甲基丙烯酰胺（N—MA）作为交联剂，2-丙烯酰胺基-2-甲基磺酸铵盐为可聚合型乳化剂，采用预乳化种子聚合工艺，合成出耐热水型乳液压敏胶粘剂，外观为带蓝荧光的白色乳液。室温下初粘力大（8～16球号）、持粘力优（17．3h）、剥离强度高（0．55～0．73kN／m），耐热剥离强度0．73～0．98kN／m，耐水性强，耐侯性好，适用于多种基材的粘接，例如聚四氟乙烯玻璃布-不锈钢等。     

单体对乳液型丙烯酸酯压敏胶性能的影响

以过硫酸铵(APS)为引发剂、丙烯酸丁酯(BA)和丙烯酸异辛酯(2-EHA)为软单体、甲基丙烯酸甲酯(MMA)为硬单体、丙烯酸(AA)和丙烯酸羟乙酯(HEA)为功能单体,并添加适量的乳化剂、润湿剂、消泡剂和链转移剂等助剂,制备了乳液型丙烯酸酯PSA(压敏胶)。研究结果表明:BA对PSA的内聚力、颜色和软硬度影响较大,HEA对PSA的机械稳定性影响较大,而AA对PSA的黏度影响较大;当w(BA)=96.92%~97.32%、w(HEA)=1.88%和w(AA)=0.80%~1.20%(均相对于单体总质量而言)时,PSA的黏度、机械稳定性和粘接性能俱佳;夏天2%左右的MMA可解决PSA偏软的问题,冬天10%~30%的2-EHA可提高PSA的初粘力。     

UV固化聚丙烯酸酯压敏胶的制备及其性能研究

采用本体聚合方法将丙烯酸酯单体的混合物实施热聚合制备预聚体,采用核-壳聚合法的单体投料方式同时加入链转移剂十二烷基硫酵来控制反应进程。在常温下涂布后直接紫外光交联固化,考察了光引发剂、交联剂、光固化时间等因素对UV固化压敏胶综合性能的影响。     

链转移剂对丙烯酸及其钠盐聚合的研究

以丙烯酸(AA)为单体，采用溶液聚合的工艺路线，通过加入一定量的链转移剂合成了含固量高迭48％、分子量只有几千级的聚丙烯酸(PAA)及其钠盐。并研究了引发荆用量、链转移剂用量对相对分子量的影响。     

可逆加成 -断裂链转移聚合制备 水性丙烯酸酯乳液及其性能研究

以 N-咔唑二硫代甲酸异丙苯酯（ CCBD）为链转移剂,以 N-胺基甲酰马来酸（ NCMA）、丙烯酸丁酯（ BA）、丙烯酸（ AA）为单体,通过可逆加成 -断裂链转移聚合（ RAFT）制备了水性丙烯酸酯类乳液（ PA）,并对 PA的结构进行了表征。考察了 CCBD用量、过硫酸铵（ APS）用量和反应时间等因素对耐冲击性的影响,并对最优条件下制备的 PA进行应用性能测试。结果表明：最优条件为反应时间 4.0 h、CCBD用量 0.5%（摩尔分数）、 APS用量为 5%（摩尔分数）。以最优反应条件制得的 PA具有优异的综合性能。     

水溶性聚酯改性丙烯酸酯乳液压敏胶的制备和性能研究

以水溶性聚酯、丙烯酸酯类单体为原料,采用半连续种子乳液聚合法制备干电池标签用丙烯酸酯压敏胶.探讨了水溶性聚酯用量和加入方式对聚合稳定性的影响.结果表明:水溶性聚酯与单体一起制备成预乳化液一起滴加,聚合最为稳定,制备的压敏胶对PETG材质的干电池标签的粘接效果最好,耐曲面性能优异,干电池标签在45℃下放置一个月不翘口.     

UV固化无溶剂型丙烯酸酯压敏胶的合成与性能表征

以丙烯酸异辛酯(2-EHA)、丙烯酸丁酯(BA)、甲基丙烯酸甲酯(MMA)和四氢化糠基丙烯酸酯(THFA)为主要单体,以丙烯酸(AA)和N,N-二甲基丙烯酰胺(DMAA)为功能性单体,以4-丙烯酰氧基二苯甲酮(ABP)为光引发剂,以十二烷基硫醇(NDM)为链转移剂,通过本体聚合法制备了UV固化无溶剂型丙烯酸酯压敏胶(PSA)。分别探讨了两种功能单体AA和DMAA用量,光引发剂ABP和链转移剂NDM用量对PSA性能的影响。结果表明,当DMAA和AA用量分别为单体总质量的10%和2%时,PSA的120℃熔融黏度适中且粘接性能较优;光引发剂ABP用于PSA体系,且用量为单体总质量的0.2%时,光固化效果最佳;当NDM用量为单体总质量的1.5%时,PSA综合性能最佳。     

乳液型丙烯酸酯压敏胶性能改良研究

本文重点介绍了乳液型丙烯酸酯类压敏胶的研究进展。通过加入增粘树脂、有机硅单体、反应性乳化剂或采用核壳聚合的方式提高其粘结强度,可以改善该类压敏胶的耐水性差、耐高温性差及涂布干燥等缺点,从而使该类压敏胶的用途更加广泛。     

Effect of monomer concentration on the adhesive properties of acrylic pressure-sensitive adhesives

2-Ethylhexyl acrylate (2-EHA)-based co- and terpolymers were synthesized using n-butyl methacrylate (nBMA) and acrylic acid (AA) as comonomers. The change in adhesive properties with the change in monomer concentration was studied. The adhesive, cohesive, and tack characteristics were evaluated under standard conditions as specified by ASTM and/or the Pressure-Sensitive Tape Council (PSTC). The 2-EHA-co-nBMA copolymers showed a good balance between these three characteristics at 50% concentration of 2-EHA. It is noteworthy that with the AA concentration at or above 30% in 2-EHA-co-AA, the polyacrylates lose the tack which is necessary for adhesive bond formation. The 2-EHA-co-AA-co-nBMA terpolymers, where the 2-EHA content was kept constant at 50% and the AA content was varied from 1% to 10% with a corresponding variation in nBMA from 49% to 40%, showed an excellent balance between adhesive, cohesive, and tack strength.     

耐热丙烯酸酯压敏胶粘剂(带)的研制

介绍了耐热高强度丙烯酸酯压敏胶粘剂 (带 )的研制方法 ,讨论了各种单体配比、引发剂、交联剂、溶剂、聚合温度、时间和工艺等因素对压敏胶粘剂性能的影响     

表面保护胶带用聚丙烯酸酯乳液压敏胶的研究

用半连续预乳化种子乳液聚合法合成了保护膜用乳液压敏胶,主要研究了底相种子乳液中乳化剂的用量、多官能度氮丙啶类交联剂的用量对乳液压敏胶性能的影响。研究结果表明:随着种子乳液中乳化剂用量的增加,乳胶粒的粒径减小,乳液粘度、表面张力和接触角增加;增加交联剂的用量可显著提高乳液压敏胶的耐老化性能;同温度相比,湿度对乳液压敏胶的耐老化性能影响更加显著;被保护材料表面的极性和光洁度对压敏胶的耐老化性能亦有显著影响。     

医用自交联聚丙烯酸酯压敏胶的性能研究

研究了一种皮肤用聚丙烯酸酯压敏胶,讨论了自交联剂和干燥时间等因素对压敏胶性能的影响,介绍了医用胶带的制备和测试方法。     

浅析水乳型丙烯酸酯压敏胶的配方设计

通过大量的试验探索和对现有配方的类比分析，对水乳型丙烯酸酯类压敏胶的配方设计进行了探讨研究。认为其决定因素是单体及其配比的筛选以及交联剂，乳化剂和链转移剂的选择，并确认作为压敏胶的丙烯酸酯共聚物的Ｔ_ｇ计算值应低于－４８℃，同时对用于丙烯酸酯类乳液共聚的三种聚合工艺也进行了探讨。     

保护膜用有机硅改性丙烯酸酯乳液压敏胶的研究

以八甲基环四硅氧垸（D1）、γ-甲基丙烯酰氧基丙基三乙氧基硅烷（KH-570）、六甲基二硅氧烷（MM）为主要原料,Me4NOH为催化剂和二甲基亚砜（DMSO）为促进剂,通过本体聚合合成了有机硅大分子。用该有机硅大分子和丙烯酸酯进行乳液共聚制得了有机硅改性丙烯酸酯乳液压敏胶,该压敏胶涂在PE膜上制成的保护膜贴在被保护表面能有效地抑制剥离强度的增长.     

有机硅改性丙烯酸酯乳液压敏胶的研究进展

简述了有机硅改性丙烯酸酯乳液压敏胶常用的改性方法,论述了乳胶液的稳定性、结构、性能及其发展前景。     

耐热性乳液型丙烯酸酯压敏胶的合成

采用种子乳液聚合法合成丙烯酸酯压敏胶,利用自交联单体N-羟甲基丙烯酰胺（NMA）提高其耐热性能,并采用反应型乳化剂DNS-86进一步提高压敏胶综合性能。研究了不同软硬单体用量比和功能单体配比对压敏胶性能的影响,探讨了自交联功能单体用量压敏胶耐热性能的影响,讨论了反应性乳化剂用量对压敏胶性能的贡献。结果表明：以最佳配方所制备出的乳液型压敏胶,其180°耐热剥离强度达到220N／m,耐热初粘力为11号钢球,耐热持粘力大于36h,固体质量分数为50％,粘度为460mPa·s。     

保护胶带用高剥离强度乳液压敏胶的研究

以丙烯酸丁酯(BA)、丙烯酸异辛酯(2-EHA)、甲基丙烯酸甲酯(MMA)、苯乙烯(St)、丙烯酸(AA)、丙烯酸羟丙酯(HPA)为原料进行乳液共聚,合成了保护膜用丙烯酸酯乳液压敏胶。讨论了乳化剂种类及用量、引发剂及缓冲剂用量、聚合温度、聚合时间、种子乳液用量对压敏胶性能的影响。结果表明,合成的压敏胶具有较高的剥离强度和初粘性,同时具有较好的耐高温高湿老化性能。     

有机硅改性丙烯酸酯核-壳结构压敏胶聚合物乳液的研制

采用种子乳液聚合的方法制备了一种新型具有核/壳结构的有机硅改性丙烯酸酯压敏胶聚合物乳液,讨论了多官能团有机硅氧烷功能性单体、核壳单体结构、乳化剂、引发剂以及聚合温度等因素对压敏胶聚合物乳液性能的影响。