nano-ATO对双层共挤PE-LD农用棚膜性能的影响

采用双螺杆挤出机制备含有不同组分的nano-ATO/线型低密度聚乙烯(PE-LD)内层和外层母粒,利用双层共挤吹塑制备PE-LD/nano-ATO双层农用棚膜,并对PE-LD/nano-ATO棚膜进行了紫外老化处理;通过傅立叶变换红外光谱(FTIR)研究了不同含量nano-ATO在复合棚膜内外层母粒中的相容性,探讨了nano-ATO的用量对复合棚膜流滴性、拉伸性能和透光性的影响。结果表明,抗氧剂、紫外吸收剂、油酸酰胺、流滴剂和用硅烷偶联剂处理过的nano-ATO等物质可以与PE-LD相容;nano-ATO的加入可以提高棚膜内层的流滴性和棚膜的拉伸强度,但会降低棚膜对光的透过率;nano-ATO对紫外光有反射或折射作用,可以降低棚膜的老化程度,因此,紫外老化后的棚膜,拉伸强度和透光率的下降都会有所减缓。综合判断,nano-ATO添加量为2%～3%时,复合棚膜的抗老化性及其它综合性能较佳。     

LDPE/纳米水滑石复合材料农用棚膜的研究

将纳米水滑石有机化改性以后，采用插层法制备出LDPE／纳米水滑石复合材料，挤出吹塑农用棚膜。对棚膜的力学性能、透光性能、耐老化性能、流滴消雾性能进行测试，结果表明：纳米水滑石的用量约为3％时．棚膜的拉伸强度、直角撕裂强度和断裂伸长率、透光率、耐老化性、红外光线的阻透性等出现峰值；纳米水滑石的用量约为0．3％时，棚膜的流滴消雾效果好，持效性长。     

LDPE/纳米水滑石复合材料农用棚膜的研究

将纳米水滑石有机化改性以后，采用插层法制备LDPE／纳米水滑石复合材料，挤出吹塑农用棚膜。对棚膜的力学性能、透光性能、耐老化性能、流滴消雾性能进行测试。结果表明：纳米水滑石的质量分数约为3％时，棚膜的拉伸强度、直角撕裂强度和断裂伸长率、透光率、耐老化性、红外光线的阻透性等出现峰值；纳米水滑石的质量分数约为0．3％时，棚膜的流滴消雾效果好，持效性长。     

VC-BA/纳米CaCO3复合母粒增韧PVC

采用氯乙烯-丙烯酸丁酯共聚弹性体(VC-BA)和经表面处理的纳米碳酸钙(nano-CaCO_3)制备VC- BA/nano-CaCO_3复合母粒,再用该复合母粒与聚氯乙烯(PVC)共混,制备了VC-BA/nano-CaCO_3复合母粒增韧的PVC复合材料。复合母粒中m(VC-BA)/m(nano-CaCO_3)为2:3时,增韧效果最佳。nano-CaCO_3与VC-BA有协同增韧作用,且nano-CaCO_3能够补强。当PVC和复合母粒质量比为100:20时,材料的冲击强度达到49.5 kJ/m~2,是纯PVC的10倍,拉伸强度为51.0 MPa。     

聚乙烯醇/水杨酸/纳米二氧化钛复合水凝胶膜的制备及性能

用纳米二氧化钛(nano-TiO_2)对聚乙烯醇/水杨酸(PVA/SA)水凝胶膜进行改性,考查了不同nano-TiO_2用量的PVA/SA/nano-TiO_2复合水凝胶膜的结构与性能。结果表明:复合膜的透明度随nano-TiO_2用量的增加而降低,而其抗菌性、抗紫外线性及透气性均随nano-TiO_2用量的增加而提高;复合膜的力学性能随nano-TiO_2用量的增加呈先上升后下降的趋势,而其溶胀性却恰好与之相反;当nano-TiO_2用量为5.0%时,复合水凝胶膜的透气系数为0.737 9 m~2/(s·kPa),拉伸强度为8.44 MPa,最大紫外线透过率仅为71.12%,透光率达69.08%,对大肠杆菌与霉菌均具有较好的抑制作用,15℃时溶胀度达19.41%。     

有机蒙脱土对五层共挤聚烯烃棚膜性能影响

采用内添加法,先将有机蒙脱土(OMMT)与不同助剂混合,熔融挤出制备聚烯烃消雾流滴功能母粒,再通过五层共挤吹膜工艺生产制备聚烯烃棚膜,探讨了OMMT对五层共挤聚烯烃棚膜力学性能、光学性能和消雾流滴性能的影响。结果表明,聚烯烃高分子链可在OMMT中插层复合,形成聚烯烃/OMMT高分子复合材料,并能提高聚烯烃棚膜的力学性能,延长棚膜的消雾流滴时间;虽然棚膜的透光率下降,但其雾度得到一定提高,能提高其光散射能力。当母粒中OMMT添加量为5%时,棚膜的力学性能和消雾流滴性能最好,拉伸强度为37.5 MPa,断裂伸长率为522.4%,直角撕裂强度133.8 kN/m,落镖冲击破损质量为606 g,透光率为89%,雾度为29%;在(55±1)℃水浴中的消雾流滴时间达到11天。     

燕化公司EVA薄膜流滴性能

北京燕化石油化工股份有限公司生产的乙烯一乙酸乙烯共聚物(EVA)与市售流滴防雾母粒配合．生产具有优良性能的长寿流滴功能棚膜。薄膜表面接触角测试、加速流滴试验、大田扣棚应用试验表明,添加流滴防雾母粒后,水与薄膜的接触角明显降低;薄膜加速流滴试验的流滴失效时间大于190h：大田扣棚应用无滴期大于5个月。燕化公司生产的LD369、LD361与市场上常用的同类EVA产品性能相当。     

纳米ZnO／聚乙烯薄膜和纳米TiO2／聚乙烯薄膜紫外屏蔽性能的比较

采用母粒法,分别将纳米ZnO、TiO2粉体添加到线型低密度聚乙烯中,再经挤出吹膜系统吹塑成膜,研究了两种粉体薄膜紫外屏蔽性能的差异.结果发现:纳米ZnO、纳米TiO2两种粉体均使得聚乙烯薄膜紫外屏蔽性能有一定程度的提高,但是在相同粉体质量分数下,在不同的波段,二者的光透过能力存在差异.虽然在紫外光波段纳米ZnO阻隔效果不如纳米TiO2;但是纳米ZnO颗粒与TiO2相比,具有较好的可见光透过性,从而对纳米复合粉体应用时的透明性影响小.     

纳米无机复合粒子改性棚膜的制备及性能研究

将纳米无机复合粒子与其他功能助剂制备成功能母粒后直接在三层共挤棚膜机组上生产纳米无机粒子改性棚膜,并对其性能进行了研究.结果表明,该棚膜的力学功能得到了提高,透光率提高了2%,雾度提高了1%;经实验窒加速劣化和实际铺晒试验,该棚膜的使用寿命可提高一倍;通过紫外光谱和红外光谱确定了该棚膜具有紫外线屏蔽功能的同时具有优良的保温性能.     

纳米TiO_2银交换粉体与柠檬酸改性LDPE薄膜的制备

将纳米TiO_2银交换粉体、柠檬酸添加到低密度聚乙烯(LDPE)中,经共混、流延得到共混薄膜,并研究了其性能。结果表明:随着高浓度母粒用量的增加,共混薄膜的断裂拉伸应变、透光率降低,透气性、雾度、抗菌性能提高,拉伸强度先增加后降低;且LDPE/高浓度母粒A/高浓度母粒B薄膜的力学性能、透气性能、抗菌性均优于LDPE/高浓度母粒A薄膜。综合考虑,选择高浓度母粒A与高浓度母粒B为2.0 phr的薄膜作为保鲜包装膜,为开发无机-有机协同高效抗菌、抗菌与气调相结合的保鲜包装膜提供支持。     

Transparent plasticised PVC film with ultraviolet and high-energy visible light shielding performance

In this paper, the ultraviolet (UV) absorbers and pigment yellow were added into the plasticised poly (vinyl chloride) (PVC) films for the purpose of improving the UV and high-energy visible light (HEV) shielding performance. The optical properties were investigated by a Ultraviolet-visible-near-infrared (UVPC) spectrophotometer and a transmission & haze meter. It was found that all the samples exhibited high transmittance and low haze. UV326 was more effective than UV531 as an UV absorber. Pigment yellow played a positive role in the optical properties. By a simple combination of 0.5?phr UV326 and 6?×?10^?3?phr pigment yellow, more than 80% optical transparency in the visible light range (400–800?nm) and 90% shielding efficiency of UV light (from 200 to 400?nm) were realised. Furthermore, the presence of pigment yellow in PVC matrix could effectively block HEV, and the average transmittance of HEV decreased with the increasing pigment yellow concentration.     

Preparation and characterization of PVC/CsxWO3 composite film with excellent near-infrared light shielding and high visible light transmission

Near-infrared (NIR) shielding is essential not only in the building and automobile glass films but also in achieving energy conservation. However, effectively shielding NIR and maintaining high transmittance in the visible light region have been great challenges in the past decade. Recently, hexagonal cesium tungsten bronze (Cs_xWO₃) nanoparticles have been widely studied due to the excellent transparency in the visible light region and strong heat-shielding ability in the NIR region. Herein, a design concept of transparent polyvinyl chloride (PVC)/Cs_xWO₃ composite film, as a heat insulation material for glasses, was proposed. To achieve this purpose, the PVC/Cs_xWO₃ composite film was prepared by incorporating Cs_xWO₃ slurry with better dispersion than traditional Cs_xWO₃ nanoparticles powder into a transparent PVC matrix. By the UV-Vis-NIR spectrophotometer characterization, the PVC/Cs_xWO₃ composite film containing 2.1 phr Cs_xWO₃ slurry displays high blocking of NIR (78%) and high transmittance of visible light (76%). In order to further understand the actual heat insulation effect from the PVC/Cs_xWO₃ composite films, the indoor sunlight simulation test and outdoor cooling experiment with solar illumination variations were carried out, which both showed heat insulation that is superior to the antimony tin oxide and indium tin oxide thin films prepared in our previous work. In addition, the mechanical property of PVC/Cs_xWO₃ composite films shows almost no change with the increase of Cs_xWO₃ slurry. The PVC/Cs_xWO₃ composite films simultaneously achieve excellent shielding of NIR and high transmittance of visible light, which makes it an ideal material to alleviate the current building energy consumption issues.     

LLDPE/LDPE/TiO2复合膜的分散及光学性能

讨论了纳米TiO2在线型低密度聚乙烯（LLDPE），低密度聚乙烯（LDPE）复合体系中的分散和体系流变行为，研究了复合薄膜的光学性能。结果表明，以高流动性LDPE为基体的纳米TiO2母料，加入LLDPE，LDPE体系中后。复合体系的表观粘度有所提高。但拉伸粘度显著下降。纳米TiO2母料在LLDPE／LDPE复合体系中具有良好的分散性，复合薄膜中的纳米TiO2为一次粒子。纳米TiO2起到了异相成核剂的作用。球晶的粒子得到细化。在本研究的纳米填充范围内（质量分数不大于1.0％），复合薄膜的透光度基本不变。雾度发生了较大幅度上升，复合薄膜在紫外光区域的吸收显著增强。     

纳米无机粒子抑制喷绘PVC膜中增塑剂析出的研究

用纳米SiO2和纳米CaCO3来抑制喷绘用聚氯乙烯（PVC）膜中增塑剂的析出,并探讨了纳米SiO2和纳米CaCO3对喷绘PVC膜喷绘性能的影响。结果表明,纳米CaCO3和纳米SiO2可以有效抑制喷绘PVC膜中增塑剂的析出,纳米无机粒子含量越高,其抑制作用越明显,但纳米无机粒子含量超过20份时,PVC膜的力学性能和喷绘性能下降;纳米无机粒子提高了喷绘PVC膜的油墨吸收速度;当纳米SiO2和纳米CaCO3团聚颗粒较大时,对PVC膜的喷绘性能产生不利影响。     

掺无机纳米矿粉水泥复合净浆的化学收缩与自收缩

依据ASTM试验标准,改良其试验方法,测量水泥复合净浆化学收缩与自收缩,研究单掺不同粒度无定型纳米二氧化硅、亲水型和表面预湿型纳米碳酸钙、不同晶型和粒度纳米二氧化钛三种无机纳米矿粉对其早期收缩的影响。研究表明：一定掺量范围内,无机纳米矿粉的掺入显著提高复合净浆化学收缩与自收缩,且随龄期增长,差异渐大,其中尤以掺纳米二氧化硅最甚,且纳米粒度越小,早期收缩越大。与不亲水但表面预湿型纳米碳酸钙相比,同掺量条件下掺亲水型纳米碳酸钙的净浆早期收缩更大。纳米氧化钛掺量3．0％～5．0％,净浆化学收缩最大,自收缩值增幅不大,远远低于掺纳米二氧化硅和掺碳酸钙的。无机纳米矿粉对水泥基材料早期收缩行为的影响与所掺纳米矿粉种类、晶型、颗粒尺度、表面状态以及掺量等密切相关。     

纳米CaCO_3改性PVC糊及其软制品力学性能研究

研究了活性纳米碳酸钙(CaCO3)用量对PVC糊树脂的粘度及其软制品拉伸强度、伸长率等力学性能的影响。结果表明,随CaCO3加入量(0～30份)的增加,PVC糊树脂粘度明显提高;纳米碳酸钙加入量为15份时,PVC软制品的拉伸强度达到最高值;纳米碳酸钙加入量越大,伸长率越低,其中加入量为5～15份时,伸长率下降幅度较小,加入量大于15份时,伸长率大幅度降低。     

掺镧二氧化钛纳米薄膜杀菌性的研究

介绍了一种掺镧二氧化钛纳米薄膜,它不但在紫外光区具有光催化杀菌作用,而且在可见光区也具有杀菌作用,可以涂于灯具达到保护环境的目的。测量此材料的选出功,证明其在可见光区有催化作用,并由实验证明,在可见光区光照2h可杀死大肠杆菌和金黄色葡萄球菌,而且对人无毒无害。该纳米材料在环境保护中具有很好的应用前景。     

湿法白炭黑/天然橡胶母胶在全钢载重子午线轮胎带束层中的应用

采用湿法制备白炭黑/天然橡胶(NR)母胶,并分别采用NR标准配方和带束层粘合配方制备硫化胶,对硫化胶的性能进行研究,并与干法制备硫化胶性能进行对比.结果表明:湿法白炭黑/NR母胶中白炭黑均匀分散;当采用NR标准配方时,随着白炭黑用量的增大,胶料的门尼粘度和拉伸强度增大,填充10份高分散白炭黑硫化胶的定伸应力、拉伸强度和撕裂强度均明显高于易分散白炭黑硫化胶;当采用带束层粘合配方时,含湿法母胶胶料的加工性能较好,白炭黑用量为10份时,含湿法母胶硫化胶老化后钢丝帘线的粘合力保持率较大,粘合性能较好.     

DMDBS成核改性聚丙烯抗菌薄膜的研究

以二(3,4-二甲基二苄叉)山梨糖醇(DMDBS)为成核剂,油酸酰胺改性载银磷酸锆为抗菌剂,聚丙烯(PP)为基体树脂,制备了成核剂母粒、抗菌剂母粒和PP抗菌薄膜,并对PP抗菌薄膜的抗菌性能、光学性能及力学性能等进行了研究。结果表明:经DMDBS改性的PP抗菌薄膜,球晶尺寸减小,结晶密度增大,结晶温度提高;含0.2%DMDBS和0.8%改性载银磷酸锆的PP薄膜的纵、横向拉伸强度分别为49.92、33.42MPa,透光率为88.5%,雾度为3.0%,对大肠杆菌和金黄色葡萄球菌抗菌率分别为99.33%和98.35%。     

复合改性纳米TiO_2的抗紫外性能及其应用

采用硅烷偶联剂(KH570)以及偶联剂和有机物(山梨醇、油酸、钛酸酯、聚乙二醇6000)复合对纳米二氧化钛(TiO_2)进行表面改性,研究了偶联剂和复合改性剂对纳米TiO_2抗紫外性能的影响。通过扫描电子显微镜、二次粒径分析、沉降试验、傅里叶变换红外光谱、同步热分析等对改性前后的纳米TiO_2进行表征。结果表明,KH570+聚乙二醇6000复合改性的纳米TiO_2二次粒径最小,平均粒径为0.047μm;沉降试验中其上清液在350 nm处的吸光度达最高为1.067 76;吸油值最大达86.19 cm~3/g,呈现良好的分散性和疏水性。另外,KH570+聚乙二醇6000改性的纳米TiO_2具有相对最强的紫外吸收能力,而且对亚甲基蓝溶液的降解率相对最小。将改性后的纳米TiO_2添加到PVC基体中,制得PVC/TiO_2薄膜,该薄膜经120 h加速老化后,发现由KH570+聚乙二醇6000改性纳米TiO_2制得的PVC薄膜的光透过率相对最低,拉伸性能最高,体现了其相对优越的抗紫外性能以及KH570+聚乙二醇6000相对优异的改性效果。