不同组成LDHs薄膜的制备及吸附性能研究

以尿素为沉淀剂,M2+/M3+摩尔比为2/1,采用水热法在导电布上制备了三种层状双金属氢氧化物(LDHs)薄膜,并采用X射线衍射仪(XRD)、扫描电子显微镜(SEM)、能谱分析(EDS)、傅里叶变换红外光谱(FT-IR)等手段进行表征.研究结果表明:组成LDHs薄膜的二价金属离子和三价金属离子溶度积之间的差异决定了LDHs薄膜的形貌和粒径.M2+和M3+溶度积相差较小时,NiAl-LDHs和MgAl-LDHs薄膜为片状结构,其中MgAl-LDHs片以ab面垂直导电布生长;M2+和M3+溶度积相差较大的NiFe-LDHs薄膜则由球形团聚构成.甲基橙吸附实验表明,形貌良好、孔隙较多的MgAl-LDHs薄膜具有良好的吸附性能.     

石墨烯复合LDHs对沥青老化及自愈合性能的影响研究

基于沥青在升温后具有更好自愈合性能的特性,利用LDHs抗老化能力强和石墨烯微波热转化效率高的优点,制备出石墨烯复合LDHs(Graphene/LDHs),将其用于改性沥青中,提高老化性能的同时改善其自愈合性能.首先采用剪切共混的方式,制备得到石墨烯复合LDHs改性材料.按照1％、2％和3％的掺量,与70#基质沥青均匀混...     

Ag/ZnAlCe LDHs的制备及光催化性能研究

通过共沉淀和光化学还原法制备纳米Ag负载ZnAlCe LDHs。通过XRD,SEM,EDS,N2吸附脱附,紫外漫反射和电化学等技术分别表征了所制得的样品的结构,表面积,形貌,光响应和电化学性能。ZnAlCe LDHs和纳米Ag的复可向光催化反应过程中引入一些Ag的性质,如优异的电导率和可控性。与纯ZnAlCe LDHs相比,Ag/ZnAlCe LDHs降解罗丹明B(RhB)的效率显著提高,这可归因于对染料的强吸附性、拓宽的光响应范围、费米能级的负移、光生电子高的迁移率,这能有效抑制电子-空穴对的复合。     

LDPE/PP复合消光膜光学及力学性能研究

通过三层流延机制备低密度聚乙烯(LDPE)/聚丙烯(PP)复合消光膜,结合扫描电子显微镜(SEM)、偏光显微镜(POM)等测试技术,研究PP添加量对复合膜材料光学及力学性能的影响规律.结果 表明,当PP添加量为15％时,膜的雾度及透光率分别为96.3％、94.8％,拉伸强度为27.51 MPa,较之未添加PP增加了16...     

Co-Ni LDHs/PES杂化膜协同PMS降解印染废水的研究

分别采用共沉淀法和相转化法制备了Co-Ni层状双氢氧化物(Co-Ni LDHs)和Co-Ni LDHs杂化聚醚砜膜(Co-Ni LDHs/PES)。通过FT-IR、XRD、SEM、TEM、EDX和拉伸强度测试对产物进行了表征。结果表明,所制备的Co-Ni LDHs/PES膜具有优异的机械性和亲水性。当LDHs的负载量为5 mg/L,PMS和AO7浓度分别为1 mmol/L和0.05 mmol/L时,反应20 min,AO7的去除率高达96.58%。Co-Ni LDHs/PES的离子浸出量远小于Co-Ni LDHs。重复使用四次后,Co-Ni LDHs/PES仍具有良好的催化性能。通过自由基猝灭实验和XPS分析研究了Co-Ni LDHs/PES的催化降解机理。在LDHs/PMS体系中同时产生了SO₄^·-、·OH、¹O₂和O₂^·-,其中后者在AO7降解中发挥了重要作用。     

PMMA对聚乙烯散光薄膜性能的影响

利用聚甲基丙烯酸甲酯(PMMA)作为散射剂,利用纳米改性线型低密度聚乙烯(LLDPE),结合三层共挤、光电雾度测试仪、扫描电子显微镜(SEM)等技术制备高性能LLDPE散光膜,研究PMMA添加量对LLDPE散光薄膜性能的影响.结果表明:不同PMMA添加量对LLDPE散光膜光学及力学性能影响显著.当PMMA添加量为15％...     

离子交换法制备LDHs纳米复合材料及其影响因素研究

以层状双金属氢氧化物(LDHs)、氯化镁和氯化铝为原料,通过液相非稳态共沉淀法制备MgAl-Cl-LDHs溶胶,通过离子交换引入己基磺酸钠(SHS),制备SHS-LDHs纳米复合材料,研究了混合溶胶pH值、SHS的初始浓度、碳链长度以及LDHs的浓度对材料性能的影响。研究发现,当混合溶液的pH 7.25,LDHs的浓度不大于0.50%,且SHS的浓度高于20 mmol/L时,CH_3(CH_2)_5SO_3~-才能通过离子交换反应进入LDHs层间,得到SHS-LDHs纳米复合材料。     

离子交换法制备LDHs纳米复合材料及其影响因素研究

以层状双金属氢氧化物(LDHs)、氯化镁和氯化铝为原料,通过液相非稳态共沉淀法制备MgAl-Cl-LDHs溶胶,通过离子交换引入己基磺酸钠(SHS),制备SHS-LDHs纳米复合材料,研究了混合溶胶pH值、SHS的初始浓度、碳链长度以及LDHs的浓度对材料性能的影响。研究发现,当混合溶液的pH 7.25,LDHs的浓度不大于0.50%,且SHS的浓度高于20 mmol/L时,CH_3(CH_2)_5SO_3^-才能通过离子交换反应进入LDHs层间,得到SHS-LDHs纳米复合材料。     

氟弹性体加工助剂对LLDPE薄膜性能的影响

在线型低密度聚乙烯(LLDPE)树脂中添加一定量的氟弹性体加工助剂(PPA)进行造粒、吹膜,考察薄膜的力学性能和光学性能等。结果发现:添加少量PPA后,薄膜的光学性能得到改善,雾度由不添加PPA时的14.0%降低至11.3%,加工能耗也有所降低,但是力学性能受到影响,薄膜的拉伸屈服强度(纵向/横向)由13.4/11.6 MPa降至12.5/10.7 MPa,拉伸断裂强度(纵向/横向)由45.1/40.0 MPa降至40.0/37.6 MPa,落镖冲击破损质量由75.0 g降至59.5 g。     

纳米CaCO_3改性LDPE膜力学性能的研究

采用熔融共混的方法制备了低密度聚乙烯(LDPE)/纳米CaCO3薄膜,并着重对改性膜的力学性能进行了研究。实验表明,适当的表面处理可改善纳米CaCO3在树脂中的分散性及其与树脂的界面粘结,提高了LDPE膜的力学性能。     

水杨酸插层水滑石及其荧光效果研究

以CO32-型镁铝LDHs为前体,采用了焙烧复原法和离子交换法两种不同的插层方法,成功地将水杨酸根阴离子插入到LDHs层间,并用FTIR、XRD、TG-DA和分子荧光光度计等手段对样品进行了表征。结果表明,离子交换法在pH=4条件下的插层效果要比焙烧复原法效果显著;同时,水杨酸根阴离子插入到层间后,因受到LDHs层间静电力、氢键、层板相互作用力等影响,其荧光发射波长发生蓝移,且其发光强度明显减弱。     

共沉淀法制备Zn-Al水滑石

锌铝水滑石是层状双羟基金属氧化物（LDHs）的一种,是一类阴离子型层状功能材料,由于其特殊的层状结构与物理化学性质,在催化、水污染处理、塑料工艺、电工行业、医药和分离等领域,有着广泛的应用。本文采用共沉淀法制备出系列Zn-Al LDHs,采用X-射线衍射、红外光谱、激光粒度分析等表征手段对样品进行分析和表征。考察了滴定方式、pH值及Zn/Al摩尔比对产物结构和粒度的影响,从而得出制备Zn-Al LDHs的最佳条件。结果表明,采用恒定pH值法,在pH=10、Zn/Al摩尔比为3/1的条件下,制得的Zn-Al LDHs晶型完整且粒度分布较窄。     

LDHs改性偏高岭土基地聚物涂料对混凝土耐久性的影响研究

本文提出一种新型偏高岭土基地聚物无机防护涂料.该涂料的基体为偏高岭土基地质聚合物,其有界面结合力强、抗渗性优异的特点,通过选择合适的工艺,加入少量的LDHs新型无机插层材料,以提高该涂料对混凝土的抗碳化性能和抗氯离子渗透性能.通过结合XRD、TG-MS等测试分析技术对该涂料提高混凝土耐久性的微观机理进行了探讨.研究结果表明,此种涂料可以显著提高被涂覆混凝土的抗碳化能力和抗氯离子侵蚀性能,LDHs材料主要通过煅烧处理后的结构重建过程和离子交换实现对碳酸根和氯离子的吸附.     

Study on preparation of layered double hydroxides (LDHs) and properties of EPDM/LDHs composites

Abstract

The aim of this work was to study preparation and characterisation of layered double hydroxides (LDHs) and their effects on the mechanical and flame-retardant properties of ethylene propylene diene (EPDM) polymer. A series of Mg–Al, Ni–Al, and Cu–Al hydrotalcite-like compounds were prepared. The surface morphology, interlayer space, interlamellar structure, and thermal properties of these LDHs were investigated. Results showed that a best thermal stability could be obtained with Cu–Al–LDHs as the most effective components. EPDM/Cu–Al–LDHs composites were prepared by conventional compounding with EPDM and Cu–Al type of LDHs. The cure characteristics, tensile strength, wear resistant, and flame-retardant properties were investigated. The best properties were observed for 10 phr of Cu–Al–LDHs filled composite, which resulted in no obvious changes of tensile strength, increased thermal stability, 45% decrease in abrasion loss, and 53% increase in vertical burning time, respectively, compared to that of pure EPDM matrix.     

PVC水滑石类热稳定剂研究进展

水滑石(LDHs)是一种新型的热稳定剂,其特殊的化学组成决定了其对HCl具有吸收作用,而且其特殊的层状结构可以对其进行层间有机阴离子嵌入改性。将其用于聚合物PVC中,可以起到阻止PVC热分解的作用。文中综述了水滑石稳定剂的制备﹑性能和稳定机理。     

LDHs的改性及其在阻燃材料中的研究与应用进展

综述了水滑石类化合物(LDHs)的改性方法及其在阻燃高分子材料中的应用进展。水滑石的改性应向多元素协效、有机/无机复合和制备大分子型阻燃剂方向发展;阻燃高分子材料既要具有良好的阻燃和抑烟性能,又要具有环境友好、价格低、便于工业化生产等特点。     

AC/LDHs插层复合材料的制备及其在挤出发泡成型中的应用

以苯甲酸插层改性LDHs纳米粉体为交换前体,采用插层置换的方法,制备出一种AC/LDHs新型纳米复合发泡材料.采用XRD、TG-DTA等手段对新材料进行了表征.结果表明pH值是影响插层效果的一个关键因素,且pH=4时,插层效果最好.利用pH=4条件下制备的新型插层复合材料在适当条件下进行挤出发泡成型,可以得到孔径为20～40μm左右的泡孔分布均匀的发泡制品.     

水杨酸根插层Mg-Al水滑石的制备与表征

本文以CO32-型镁铝水滑石为前体,乙二醇为分散介质,用返混沉淀法制备水杨酸根插层水滑石,并用XRD,FT-IR,UV-Vis等手段对样品进行了表征.结果表明,通过改变条件,水杨酸根离子可以引入镁铝水滑石层间,取代层间CO32-,从而得到一种具有屏蔽和吸收紫外能力的有机-无机复合功能材料.     

Preparation and properties of LDHs/polyimide nanocomposites

Layered double hydroxides/polyimide (LDHs/PI) nanocomposites were prepared from solution of polyamic acid (polyimide precursor) and LDH-amino benzoate using N,N-dimethylacetamide as a solvent. LDH-amino benzoate (LDH-AB) was obtained by coprecipitation method. The amino benzoate, grafted on the surface of the Mg/Al nanolayers, as a connector improved the compatibility between the inorganic Mg/Al nanolayers and the organic polyimide molecules. The dispersion behavior of Mg/Al nanolayers was investigated by transmission electron microscopy and X-ray diffraction, indicating that the Mg/Al nanolayers were exfoliated in PI matrix to form LDH-AB/PI nanocomposites. The maximum tensile strength and elongation of the LDH-AB/PI nanocomposites were found with the LDH-AB content of 5 and 4 wt%, respectively. The initial tensile modulus of these nanocomposites was increased with the LDH-AB content. These nanocomposites exhibited higher storage and loss moduli compared to those of pure PI. T_g of these nanocomposites increased with the LDH-AB content. Coefficients of thermal expansion (CTE, below and above T_g) of these nanocomposites deceased with the LDH-AB content. The thermal properties of these nanocomposites were enhanced by the incorporation of Mg/Al nanolayers in PI matrix.     

水滑石类热稳定剂在PVC中应用研究进展

水滑石类热稳定剂是一类新型热稳定剂,具有无毒、廉价和高效的优点。介绍了水滑石的结构特征、对PVC的热稳定作用机理以及在PVC的应用研究进展。总结出提高热稳定剂在PVC中的分散性、与其它类型热稳定剂的复配以及规模生产工艺稳定化是未来水滑石类热稳定剂的研究方向。