熔融缩聚法直接合成聚乳酸的研究

采用熔融缩聚法直接合成聚乳酸,探索了催化剂用量、单体浓度、反应温度及反应时间对聚乳酸分子量的影响.结果表明:选用质量分数为1.0%的辛酸亚锡作为催化剂,聚合温度控制在160℃,0.09MPa反应10h,可得到粘均分子量为9.68×103的聚乳酸.     

逐步减压缩聚法制备高分子量聚乳酸的研究

以L-乳酸单体为原料,用逐步减压缩聚法合成了相对高分子量的聚乳酸.探讨了反应条件如:温度、反应时间、催化剂用量、酯化时间、逐步减压时间等对聚乳酸分子量的影响,并采用FTIR、1H NMR测试手段对聚合物进行了结构表征.结果表明,催化剂用量为0.5wt%,反应温度180℃,先酯化7小时,再逐步减压7小时,然后在高真空度70Pa下反应45小时,可得到重均分子量约为12万的聚乳酸.     

微波辐射D,L-丙交酯开环聚合制备聚乳酸

为得到聚乳酸的最佳制备工艺,利用微波辐射技术实现D,L-丙交酯开环聚合制备聚乳酸,实验考查了催化剂种类和用量,微波辐照功率和时间等工艺参数对产物分子量的影响,以及反应过程中体系温度的变化.研究表明,以连续微波炉作为反应器,催化剂Sn(Oct)2用量为丙交酯单体用量的0.56%(质量分数),在功率为90 W的连续微波辐射下反应10 m in,可获得粘均分子量(Mη)为15.92×104的聚乳酸(PDLLA).与家用微波炉相比,采用连续微波炉反应器,可在较短的反应时间内获得较高产率的聚乳酸产物.     

聚乳酸的微波辐射合成方法研究

采用微波加热提供反应所需热量,以丙交酯为原料,辛酸亚锡的甲苯溶液为催化剂,进行丙交酯开环聚合反应,开展了聚乳酸的微波辐射合成工艺及相关基础研究。在最佳条件下(催化剂辛酸亚锡与单体的摩尔比为0.001,SiC作辅助加热介质,微波功率为450W,反应18min)合成了分子量为2.5×104的聚乳酸。     

聚乳酸／纳米二氧化硅复合材料分子量的影响因素

以丙交酯和改性后的纳米二氧化硅为原料,在催化剂作用下,用原位聚合法制备了聚乳酸纳米二氧化硅复合材料。讨论了催化剂的种类和用量、反应时间、反应温度、纳米二氧化硅的用量等因素对复合材料分子量的影响。结果表明,最优的反应条件为:采用辛酸亚锡为催化剂,催化剂用量和二氧化硅用量分别为丙交酯用量的0.25%(质量分数,下同)和5%,在140℃油浴中,氮气保护下反应72 h,可得到重均分子量为1.5091×105的聚乳酸纳米二氧化硅复合材料。     

低温常压下高分子量左旋聚乳酸的微波合成及表征

以辛酸亚锡为催化剂低温常压下引发左旋丙交酯(LLA)开环聚合,快速高效地合成了性能良好的高分子量左旋聚乳酸(PLLA).通过正交实验研究了催化剂用量、反应温度和时间对产物分子量的影响,在催化剂用量0.21%(质量分数),反应温度100℃,反应时间60min时得到产物粘均分子量高达16.21×104.通过红外光谱(FTIR)、核磁共振氢谱(1H-NMR)对产物的结构进行分析,结果证明利用微波能有效地合成左旋聚乳酸,通过差式扫描量热(DSC)、X衍射(XRD)、旋光度和力学性能对左旋聚乳酸膜的性能进行表征,结果显示产物纯净,其结晶度为85.6%,光学纯度为98%,有良好的力学性能.     

聚乳酸接枝淀粉的原位溶液合成及表征

以L-乳酸为接枝单体,辛酸亚锡为催化剂,采用原位溶液接枝工艺,在同一个反应体系中逐次完成淀粉糊化、丙交酯的生成及淀粉的聚乳酸接枝反应,制备了聚乳酸接枝淀粉,工艺简单、易于控制。研究了反应温度、L-乳酸与玉米淀粉质量比、反应时间和催化剂用量等对产物接枝率的影响,采用FTIR,1H-NMR和SEM对接枝产物进行了表征。结果表明:原位溶液合成产物为聚乳酸接枝淀粉;其最佳工艺条件的反应温度为95℃,L-乳酸与玉米淀粉质量比为3∶1,催化剂为乳酸用量的1%(质量分数),反应时间11 h,聚乳酸接枝率可达到14.81%,淀粉颗粒表面聚乳酸包覆均匀。     

药物缓释材料聚磷酸酯-聚乳酸的直接熔融聚合法合成工艺研究

以外消旋乳酸(D,L-LA)、乙二醇和二氯磷酸苯酯为原料,通过熔融聚合法直接合成生物降解材料聚磷酸酯-聚乳酸,用凝胶渗透色谱测定产物的相对分子质量,探讨了预聚方式、催化剂种类和用量,以及熔融聚合反应时间、反应温度对共聚物相对分子质量的影响.在160℃、70Pa、催化剂ZnO的用量0.5%的条件下熔融聚合8h,共聚物的重均分子量可达9200,可以用于药物缓释微球.新合成方法有利于降低聚磷酸酯-聚乳酸作为药物缓释载体材料的合成成本.     

以PMDETA为配体的甲基丙烯酸丁酯ARGET ATRP研究

以廉价配体五甲基二乙烯三胺(PMDETA)、溴化铜(CuBr2)和还原剂为催化体系,进行了甲基丙烯酸丁酯(BMA)的电子转移再生活化剂原子转移自由基聚合研究(ARGET ATRP),考察了影响反应可控性的因素。实验结果表明,配体用量至少为催化剂量10倍(物质的量)以上,反应温度应在65℃～85℃,所得聚合物分子量分布较窄;还原剂用量增加,反应速率变快,但分子量分布变宽;催化剂用量减少时,还原剂相对用量要增加;催化剂的最少用量取决于引发剂与催化剂的物质的量比,当引发剂和催化剂物质的量比小于1:0.02时,催化剂的用量能降到单体物质的量的5×10-5倍,仍保持可控聚合,所得聚合物分子量分布较窄为1.29。     

熔融缩聚合成聚L-乳酸的研究

以L-乳酸为原料,通过熔融缩聚法合成了聚乳酸(PLLA).考察了预聚条件、催化剂种类和用量、催化剂溶解程度、聚合温度及时间对聚乳酸分子量的影响.采用FTIR和1H-NMR分析聚合物结构,GPC测定分子量分布.研究表明,等摩尔量的氯化亚锡(SnCl2)和对甲苯磺酸(TSA)组成的复合催化剂效果最好,SnCl2的用量为预聚物(OLLA)的0.4%为宜;预聚过程和催化剂在OLLA中的充分溶解对提高聚合物分子量具有重要意义;合适的聚合温度约为165 ℃;在发生爬杆现象前,随反应时间的增加,聚乳酸分子量增加.在优化的工艺条件下,可以在较短时间(8 h)内获得分子量为65000左右的聚乳酸.     

Insertion of triangulated surfaces into a meccano tetrahedral discretization by means of mesh refinement and optimization procedures

In this paper, we present a new method for inserting several triangulated surfaces into an existing tetrahedral mesh generated by the meccano method. The result is a conformal mesh where each inserted surface is approximated by a set of faces of the final tetrahedral mesh. First, the tetrahedral mesh is refined around the inserted surfaces to capture their geometric features. Second, each immersed surface is approximated by a set of faces from the tetrahedral mesh. Third, following a novel approach, the nodes of the approximated surfaces are mapped to the corresponding immersed surface. Fourth, we untangle and smooth the mesh by optimizing a regularized shape distortion measure for tetrahedral elements in which we move all the nodes of the mesh, restricting the movement of the edge and surface nodes along the corresponding entity they belong to. The refining process allows approximating the immersed surface for any initial meccano tetrahedral mesh. Moreover, the proposed projection method avoids computational expensive geometric projections. Finally, the applied simultaneous untangling and smoothing process delivers a high‐quality mesh and ensures that the immersed surfaces are interpolated. Several examples are presented to assess the properties of the proposed method.     

Certification Institutions Expected to Update and Transfer Information on Present Standards

Standards are the basis for production enterprises to organize production, ex-factory inspection, trade (delivery) and technical exchanges, product certification, quality arbitration and supervision.……     

From Industry 4.0 to Research 4.0. Development of High Performance Fibers in the Light of Digitization

We associate a variety of innovations with the term ＂Industry 4.0＂. The pioneer of many 4.0 modifications forms the basisfor the trend towards the integrated di...     

Flow calorimeter for enthalpy increment measurements on condensed gases

A flow calorimeter for enthalpy increment measurements on condensed gases is presented. A better knowledge of the properties of the liquefied natural gas is needed, and therefore a liquid loop has been designed for our flow calorimeter. The fluid loop in the calorimeter is designed in order to avoid the two-phase region, since two phases would give compositional disturbances in the measurements. The avoidance of the two-phase region is made possible by increasing the pressure of the test fluid after the measurement section, then heating the fluid at super-critical pressure past the critical point. Finally, the fluid is throttled to the low-pressure gas state at the inlet condition of the compressor that circulates the fluid. To perform the pressure increase, a new cryogenic pump has been designed. To evaluate the new equipment, measurements were taken on liquid ethane over the temperature range 146–256 K at pressure between 0.9 and 5.1 MPa.     

Refrigerators Enter a New Era of Health Preservation Frestech initiates the establishment of China's first standard for household sterilization refrigerators

On November 30, 2007, the China Association for Standardization (CAS) held a press conference at Beijing Diaoyutai State Guest House. Leaders from the China Household Electric Appliance Research Institute, the China Household Electric Appliance Association, and the China Consumers' Association attended and made speeches.……     

Roman iron and steel: A review

ABSTRACT

The production of ferrous metal increased during the Roman Late Republican period, Principate and Empire. The direct bloomery process was used to extract the metal from its ores using slag-tapping and slag-pit furnaces. The fuel was charcoal and an air blast was introduced by bellows-operated tuyères. Iron formed as a bloom, often as a spongy mass of metal, which contained impurities from the smelting process, including unreacted ore, fuel, slag and fragments from the furnace walls, while the metal was often inhomogeneous with varied carbon contents. Blooms were either smithed directly into bars or ingots or they were broken up, which also allowed the removal of gross impurities and a selection of pieces with similar properties to be made. These could then be forge-welded together and formed into characteristically shaped ingots. Making steel in the furnace seems to have been achieved: it depended on the ore and the furnace and conditions within it. Surface carburization was also carried out. Iron and steel were used extensively in construction and for tools and weapons. Fire welding was often used to add pieces of steel to make the edges of tools and weapons, which could be heat-treated by quenching to harden them.     

Optimum-Simulation von Ernteprozessen

Zusammenfassung Bei der Gestaltung von Ernteprozessen — beispielsweise des Prozesses Mähdrusch, Körnertransport und -abnahme — als transportverbundene Fließarbeitsverfahren mit mindestens zwei verschiedenen Arbeitsmitteln gibt es einen großen Optimierungsspielraum. Solche Prozesse sind mehrstufige Bedienungsprozesse mit gemischter Anordnung der Bedienungseinrichtungen. Außerdem besitzen sie stark ausgeprägte räumliche Aspekte. Es wird vor allem gezeigt, welche Merkmale solcher Prozesse in Simulationsmodellen abgebildet sein müssen, welche Zielgrößen in Abhängigkeit von welchen Einflußgrößen unter Berücksichtigung welcher Prozeßbedingungen ermittelt werden sollten und wie der Bewertungsprozeß zur Ermittlung der gewünschten Informationen gestaltet werden muß.     

A study of centrifugal cast high boron high speed steel

In the present study a high‐boron high speed steel (HSS) roll material was designed. Many expensive alloy elements have been substituted by cheap boron alloy, and high‐boron high speed steel roll has been manufactured by centrifugal casting method. The microstructures, mechanical properties and wear resistance of centrifugal casting high‐boron high speed steel roll have been investigated by optical microscopy (OM), scanning electron microscopy (SEM), and X‐ray diffraction (XRD) analysis, hardness test, impact test and wear test. The results indicated that the solidification microstructures of high‐boron high speed steel roll consisted of M₂(B,C), (W,Mo)₂(B,C), M₃(B,C), M₂₃(B,C)₆ type borocarbides and martensite, a small amount of retained austenite. Borocarbides were continuously distributed over the grain boundary. After quenching from 1050 °C, local broken network appeared in partial borocarbides, and fine secondary borocarbide precipitated from the matrix. After tempering from 525 °C, the amount of precipitated borocarbide increased significantly. After heat treatment, the hardness of high‐boron high speed steel roll excelled 60 HRC, and its impact toughness excelled 8.0 J/cm². The single groove steel rolling amount of high‐boron high speed steel rolls increases by 500% than that of bainite cast iron roll, when the rolls are used in K₁ mill housing of bar mill.     

Thixotropy of Systems with Shear Thinning and Plastic Flow Behavior

The definition of the thixotropy is a decrease in viscosity with time in shear and a subsequent recovery of viscosity after the shear deformation is removed.We ...