研究旨在开发一种以钢渣为碱性激发剂,以烟气脱硫石膏、矿渣粉为主要为原料的脱硫石膏水硬性胶凝材料。该胶凝体系3天抗折强度和抗压强度可达4.4 MPa和15.8 MPa;28天抗折强度和抗压强度可达9.4 MPa和50.7 MPa。其试样的强度随钢渣掺量的增加而增加,而钢渣含量一旦超过8%后,增长幅度变缓,甚至开始降低。XRD和SEM分析表明,脱硫石膏-矿渣-激发剂体系的水化产物主要是钙矾石和C-S-H凝胶。脱硫石膏在水化过程中一部分参与水化形成水化产物钙矾石,其余部分被水化产物所包裹起集料骨架作用。     

钢渣粉性能优化及制备无熟料混凝土的试验研究

为提高固体废弃物综合利用率,通过钢渣分段除铁优化试验和钢渣粉对无熟料混凝土抗压强度影响试验,研究以钢渣-矿渣-脱硫石膏作为胶凝材料制备无熟料全固废混凝土。结果表明,经分段磁选可获得金属铁含量低于0.5%的高性能钢渣粉;当钢渣粉比表面积为640m~2/kg,m(钢渣)∶m(矿渣)=1∶2.5时,无熟料混凝土同时获得较优的3d和28d强度。XRD、TG-DSC、IR和FE-SEM分析表明,在脱硫石膏的激发作用下钢渣和矿渣可以相互促进水化,水化产物以AFt(钙矾石)和C-S-H(水化硅酸钙)凝胶为主。早期钢渣水化促进矿渣的解聚并结合脱硫石膏生成AFt网状结构,随着水化反应的进行胶凝体系生成的C-S-H凝胶充填于AFt网络中使硬化浆体结构致密从而保证强度的增长。     

大掺量工业废渣激发制备钢渣复合胶凝材料的试验研究

在研究不同钢渣掺量胶凝体系稳定性的基础上,以40%的钢渣粉掺加15%矿渣粉、5%硅灰粉,采用自配复合激发剂成功地制备出早期抗折强度、抗压强度达到4.5MPa、18.8MPa且满足42.5强度等级的复合胶凝材料,通过其孔隙率及微观结构测试分析表明:钢渣复合胶凝材料水化产物致密,孔隙率低,后期抗压强度、抗折强度发展较好。     

钢渣矿渣基全固废胶凝材料的水化反应机理

以钢渣、矿渣和脱硫石膏为主要原料制备胶凝材料,使用XRD、IR、TG-DTA和SEM等手段探究胶凝材料的水化反应机理,研究了钢渣掺量对全固废混凝土强度的影响,以及胶凝材料浆体的p H值和代表性离子浓度的变化规律。结果表明,当原料质量比为m(钢渣):m(矿渣):m(石膏)=30:58:12时,全固废混凝土3 d、7 d和28 d可以获得较优的强度。随着反应龄期的增加胶凝材料水化溶液的pH值先减小后增大,Ca2+浓度和硅(铝)溶解物的早期浓度较低,后期浓度有所提高。在脱硫石膏的激发下钢渣和矿渣相互促进水化,水化产物以钙矾石(AFt)和水化硅酸钙(C-S-H)凝胶为主。在反应的后期,水化产物的数量迅速增加。针棒状的AFt晶体穿插在C-S-H凝胶内,使硬化浆体的结构更加致密。     

冶金渣制备高强人工鱼礁结构材料的试验研究

为了研究钢渣粉磨时间和矿渣钢渣复掺比例对矿渣-钢渣-熟料-石膏体系胶凝材料强度的影响,采用一次线性回归得到胶凝材料强度的变化趋势,并利用XRD和SEM方法分析钢渣粉磨和净浆的水化过程.试验表明:矿渣与钢渣的复合比为7∶1,钢渣和矿渣的比表面积分别为550和480 m2/kg,且与质量分数10%的水泥熟料和质量分数10%的脱硫石膏复合的胶凝材料具有较高的强度.以优化后的胶凝材料代替水泥,并以热闷法稳定化的钢渣颗粒为骨料,可以制备出抗压强度达到60 MPa以上,水泥熟料总用量为2%的高强人工鱼礁混凝土.研究表明,对钢渣适度粉磨能改善钢渣性能,适量加入钢渣对促进体系的水化有积极作用.     

自燃煤矸石胶凝材料中钙矾石形成研究

采用XRD分析了自燃煤矸石胶凝材料中活性Al2O3在不同因素影响下水化形成钙矾石的情况.研究结果表明,在相同条件下芒硝存在,时自燃煤矸石中活性Al2O3水化生成钙矾石,而含等量硫的石膏存在时水化浆体中不但有水化产物钙矾石还有未反应的石膏;胶凝体系中不含熟石灰时,活性Al2O3水化首先生成石膏,随着水化的进行再转化成钙矾石,而在有熟石灰时水化则直接生成钙矾石;矿渣促进了自燃煤矸石中Al2O3水化形成钙矾石.     

大掺量钢渣微粉-水泥碱激发特性

为解决钢渣微粉在水泥基复合材料中掺配比例较低的问题，采用力学性能测试、 XRD、 SEM、 FTIR等方法研究激发剂种类、掺量等对钢渣微粉-水泥胶凝材料力学强度和微观结构的影响。结果表明：碱性激发剂可提高钢渣微粉水化速度、增大复合胶凝材料抗压强度，但激发剂种类对胶凝材料激发效果具有差异性；碳酸钠与三乙醇胺复合激发后效果显著，3、 7、 28 d龄期的最佳强度与未掺加激发剂实验组的相比分别提高47%、 72%、 69%;激发剂对复合胶凝材料浆体水化产物种类没有影响；三乙醇胺具有悬浮稳定效应以及降低溶液表面张力的能力，与碳酸钠的强腐蚀效应作用在钢渣微粉水泥体系中协同强化水化反应，使复合胶凝体系中生成更多的水化产物并且相互交织成复杂密实的空间结构。     

高铁钢渣作碱激发剂对过硫磷石膏矿渣凝结硬化性能的影响

磷石膏作为磷化工企业湿法生产磷酸产生的固体废弃物，由于其杂质含量高、晶体结构存在缺陷导致其应用性能远不如其他副产石膏，现已成为我国主要的工业固废之一。为实现磷石膏的低成本化、大掺量化及高性能化应用，本研究基于全固废胶凝材料设计思路，将活性较低的高铁钢渣作为碱激发剂制备过硫磷石膏矿渣水泥，并探究物理、化学活化处理钢渣对胶凝材料凝结硬化的影响。测试结果表明：球磨时间的延长有助于细化大粒径钢渣并分散部分团聚颗粒，提升钢渣各龄期的活性指数，最佳球磨时间为20～40 min。相较于CaO,利用高铁钢渣作为碱激发剂时不利于新拌浆体的早期凝结硬化，但是对后期强度发展具有较好的促进作用，28 d时抗压强度可超过50 MPa。SEM测试结果显示，随着水化的持续进行，基体内生成大量C-(A)-S-H凝胶包裹未反应的石膏，结晶良好的棒状钙矾石填充缝隙和孔洞，进一步提升了基体的密实度。     

矿冶固废基胶结充填料的制备及性能研究

以钢渣、钒钛矿渣为主要原料制备胶结剂,再将其与钒钛铁尾矿制成矿井充填料,通过力学性能、XRD、SEM、FTIR等测试,研究了胶结充填料的性能及胶结剂水化产物的组成和结构。结果表明：当钢渣、钒钛矿渣的质量比为13∶12,胶结剂中钢渣/钒钛矿渣、磷石膏、双氰胺废渣、复合磷酸、水泥熟料的质量比为84∶3.6∶5.4∶4.2∶2.8,充填料胶砂比为1∶4,料浆浓度为80%,减水剂含量为0.178%时,充填料坍落度为214 mm,充填料28 d抗折和抗压强度分别达到4.04 MPa、8.31 MPa,满足GB/T 39489-2020《全尾砂膏体充填技术规范》要求。XRD和SEM分析表明,胶结剂水化产物主要为钙矾石(AFt),磷石膏的存在促进了AFt的形成,而AFt又进一步促进了钒钛矿渣和钢渣中[AlO₄]^5-和[SiO₄]^4-沿桥氧的断裂。     

碳酸化钢渣和矿渣作硅酸盐水泥混合材水化性能研究

通过对钢渣碳酸化前后的硅酸盐相提取及水化放热性能和将碳酸化钢渣和矿渣作为混合材的硅酸盐水泥的胶砂强度和水化产物种类的测定,以及对它们微观形貌的观察,研究了碳酸化钢渣对胶凝体系水化性能的影响.结果表明,碳酸化使钢渣中硅酸盐相的含量由47.06％下降至14.38％;碳酸化促进了钢渣的早期水化,抑制其后期水化;在配比相同的条件下,碳酸化钢渣-矿渣-硅酸盐熟料体系试样的3、28d抗压强度较未碳酸化钢渣-矿渣-硅酸盐熟料体系试样的高;碳酸化生成的CaCO3促进了熟料的水化;碳酸化钢渣促进了胶凝体系中AFt的生成,且生成水合碳铝酸钙.     

Insertion of triangulated surfaces into a meccano tetrahedral discretization by means of mesh refinement and optimization procedures

In this paper, we present a new method for inserting several triangulated surfaces into an existing tetrahedral mesh generated by the meccano method. The result is a conformal mesh where each inserted surface is approximated by a set of faces of the final tetrahedral mesh. First, the tetrahedral mesh is refined around the inserted surfaces to capture their geometric features. Second, each immersed surface is approximated by a set of faces from the tetrahedral mesh. Third, following a novel approach, the nodes of the approximated surfaces are mapped to the corresponding immersed surface. Fourth, we untangle and smooth the mesh by optimizing a regularized shape distortion measure for tetrahedral elements in which we move all the nodes of the mesh, restricting the movement of the edge and surface nodes along the corresponding entity they belong to. The refining process allows approximating the immersed surface for any initial meccano tetrahedral mesh. Moreover, the proposed projection method avoids computational expensive geometric projections. Finally, the applied simultaneous untangling and smoothing process delivers a high‐quality mesh and ensures that the immersed surfaces are interpolated. Several examples are presented to assess the properties of the proposed method.     

Certification Institutions Expected to Update and Transfer Information on Present Standards

Standards are the basis for production enterprises to organize production, ex-factory inspection, trade (delivery) and technical exchanges, product certification, quality arbitration and supervision.……     

From Industry 4.0 to Research 4.0. Development of High Performance Fibers in the Light of Digitization

We associate a variety of innovations with the term ＂Industry 4.0＂. The pioneer of many 4.0 modifications forms the basisfor the trend towards the integrated di...     

Flow calorimeter for enthalpy increment measurements on condensed gases

A flow calorimeter for enthalpy increment measurements on condensed gases is presented. A better knowledge of the properties of the liquefied natural gas is needed, and therefore a liquid loop has been designed for our flow calorimeter. The fluid loop in the calorimeter is designed in order to avoid the two-phase region, since two phases would give compositional disturbances in the measurements. The avoidance of the two-phase region is made possible by increasing the pressure of the test fluid after the measurement section, then heating the fluid at super-critical pressure past the critical point. Finally, the fluid is throttled to the low-pressure gas state at the inlet condition of the compressor that circulates the fluid. To perform the pressure increase, a new cryogenic pump has been designed. To evaluate the new equipment, measurements were taken on liquid ethane over the temperature range 146–256 K at pressure between 0.9 and 5.1 MPa.     

Refrigerators Enter a New Era of Health Preservation Frestech initiates the establishment of China's first standard for household sterilization refrigerators

On November 30, 2007, the China Association for Standardization (CAS) held a press conference at Beijing Diaoyutai State Guest House. Leaders from the China Household Electric Appliance Research Institute, the China Household Electric Appliance Association, and the China Consumers' Association attended and made speeches.……     

Roman iron and steel: A review

ABSTRACT

The production of ferrous metal increased during the Roman Late Republican period, Principate and Empire. The direct bloomery process was used to extract the metal from its ores using slag-tapping and slag-pit furnaces. The fuel was charcoal and an air blast was introduced by bellows-operated tuyères. Iron formed as a bloom, often as a spongy mass of metal, which contained impurities from the smelting process, including unreacted ore, fuel, slag and fragments from the furnace walls, while the metal was often inhomogeneous with varied carbon contents. Blooms were either smithed directly into bars or ingots or they were broken up, which also allowed the removal of gross impurities and a selection of pieces with similar properties to be made. These could then be forge-welded together and formed into characteristically shaped ingots. Making steel in the furnace seems to have been achieved: it depended on the ore and the furnace and conditions within it. Surface carburization was also carried out. Iron and steel were used extensively in construction and for tools and weapons. Fire welding was often used to add pieces of steel to make the edges of tools and weapons, which could be heat-treated by quenching to harden them.     

Optimum-Simulation von Ernteprozessen

Zusammenfassung Bei der Gestaltung von Ernteprozessen — beispielsweise des Prozesses Mähdrusch, Körnertransport und -abnahme — als transportverbundene Fließarbeitsverfahren mit mindestens zwei verschiedenen Arbeitsmitteln gibt es einen großen Optimierungsspielraum. Solche Prozesse sind mehrstufige Bedienungsprozesse mit gemischter Anordnung der Bedienungseinrichtungen. Außerdem besitzen sie stark ausgeprägte räumliche Aspekte. Es wird vor allem gezeigt, welche Merkmale solcher Prozesse in Simulationsmodellen abgebildet sein müssen, welche Zielgrößen in Abhängigkeit von welchen Einflußgrößen unter Berücksichtigung welcher Prozeßbedingungen ermittelt werden sollten und wie der Bewertungsprozeß zur Ermittlung der gewünschten Informationen gestaltet werden muß.     

A study of centrifugal cast high boron high speed steel

In the present study a high‐boron high speed steel (HSS) roll material was designed. Many expensive alloy elements have been substituted by cheap boron alloy, and high‐boron high speed steel roll has been manufactured by centrifugal casting method. The microstructures, mechanical properties and wear resistance of centrifugal casting high‐boron high speed steel roll have been investigated by optical microscopy (OM), scanning electron microscopy (SEM), and X‐ray diffraction (XRD) analysis, hardness test, impact test and wear test. The results indicated that the solidification microstructures of high‐boron high speed steel roll consisted of M₂(B,C), (W,Mo)₂(B,C), M₃(B,C), M₂₃(B,C)₆ type borocarbides and martensite, a small amount of retained austenite. Borocarbides were continuously distributed over the grain boundary. After quenching from 1050 °C, local broken network appeared in partial borocarbides, and fine secondary borocarbide precipitated from the matrix. After tempering from 525 °C, the amount of precipitated borocarbide increased significantly. After heat treatment, the hardness of high‐boron high speed steel roll excelled 60 HRC, and its impact toughness excelled 8.0 J/cm². The single groove steel rolling amount of high‐boron high speed steel rolls increases by 500% than that of bainite cast iron roll, when the rolls are used in K₁ mill housing of bar mill.     

Brainstorming for ISO Strategy 2016-2020

正Responding to ISO’s appeal for survey for the to-be-developed ISO Strategy Plan for 2016-2020,SAC hosted a special workshop over the needs and comments of various fi elds on June 8 in Beijing.The workshop was attended by ISO President-elect and Ansteel General Manager Zhang Xiaogang,SAC Vice-Administrator Yu Xinli,and 30 experts from