The corrosion behavior of Ni-Al alloys and Ni-Nb-Al alloys in a H2/H2O/H2S gas mixture

The corrosion behavior of two Ni-Al alloys and four Ni-Nb-Al alloys was studied over the temperature range of 600° C to 1000° C in a mixed-gas of H₂/H₂O/H₂S. The parabolic law was generally followed, although linear kinetics were also observed. Multiple-stage kinetics were observed for the Ni-Al alloys. Generally, the scales formed on Ni-13.5Al and Ni-Nb-Al alloys were multilayered, with an outer layer of nickel sulfide with or without pure Ni particles and a complex inner scale. The outer scale became porous and discontinuous with increasing temperature. Very thin scales formed on Ni-31Al. The reduction in corrosion rate with increasing Al content is ascribed to the formation of Al₂O₃ and Al₂S₃ in the scale. Platinum markers were found at the interface between the outer and inner scales.     

The corrosion behavior of Ni-Mo alloys in a H2/H2O/H2S gas mixture

The corrosion behavior of Ni-Mo alloys containing up to 40 wt.% Mo was studied over the temperature range of 550–800C in a mixed gas of H₂/H₂O/ H₂S. The scales formed on all alloys contained only sulfides and were doublelayered. The outer scale was single-phase Ni₃S₂. Depending on the alloy composition and reaction conditions, the inner scale was: (1) a mixture of MoS₂ plus Ni₃S₂ with/without Ni, (2) MoS₂, or (3) MoS₂ plus intermetallic particles and/or double sulfide Ni_2.5Mo₆S_6.7. Neither internal oxidation nor internal sulfidation were observed at lower temperatures. Internal sulfidation was however observed at higher temperature when the scale apparently melted. The parabolic law was generally obeyed for the most concentrated alloys. For the two more-dilute alloys the kinetics were mostly linear. A decrease in the corrosion rate occurred with increasing Mo content of the alloy and may be attributed to the presence of increasing volume fractions of MoS₂ and/or of a double Ni-Mo sulfide in the inner region of the scale. For the two most concentrated alloys this may also be due to the presence of a number of particles of the unsulfidized intermetallic compound, which is Ni₃Mo for Ni-30Mo, but NiMo for Ni-40Mo.     

The corrosion behavior of Fe-Nb-Al alloys in H2/H2O/H2S atmospheres

The corrosion behavior of eight Fe-Nb-Al ternary alloys was studied over the temperature range 700–980°C in H₂/H₂O/H₂S atmospheres. The corrosion kinetics followed the parabolic rate law for all alloys at all temperatures. The corrosion rates were reduced with increasing Nb content for Fe-x Nb -3Al alloys, the most pronounced reduction occurred as the Nb content increased from 30 to 40 wt.%. The corrosion rate of Fe-30Nb decreased by six orders of magnitude at 700°C and by five orders of magnitude at 800°C or above by the addition of 10 wt.% aluminum. The scales formed on low-Al alloys (3 wt.% Al) were duplex, consisting of an outer layer of iron sulfide (with Al dissolved near the outer-/inner-layer interface) and an inner complex layer of Fe_xNb₂S₄(FeNb₂S₄ or FeNb₃S₆), FeS, Nb₃S₄ (only detected for Nb contents of 30 wt.% or higher) and uncorroded Fe₂Nb. No oxides were detected on the low-Al alloys after corrosion at any temperature. Platinum markers were found to be located at the interface between the inner and outer scales for the low-Al alloys, suggesting that the outer scale grew by the outward transport of cations (Fe and Al) and the inner scale grew by the inward transport of sulfur. The scales formed on high-Al alloys (5 wt.% Al) were complex, consisting primarily of Nb₃S₄, Al₂O₃ and (Fe, Al)_xNb₂S₄, and minor amounts of (Fe, Al)S and uncorroded intermetallics (FeAl and Fe₂Nb). The formation of Nb₃S₄ and Al₂O₃ blocked the transport of iron through the inner scale, resulting in the significant reduction of the corrosion rates.     

High-temperature sulfidation behavior of Ni-Nb alloys

The sulfidation properties of Ni-Nb alloys containing additions of niobium up to 40 wt.% have been studied at atm over the temperature range 550-700 °C. The sulfidation reactions followed the parabolic rate law; the sulfidation rates decreased with increasing amounts of niobium. An Arrhenius plot of the rate constants gave activation energies of 25.0+3.5 kcal/ mole. The scales formed on Ni-Nb alloys were multilayered, generally consisting of an outer layer of nickel sulfide ( NiS_1+x and Ni₃S₂) and an inner complex layer of NiNb₃S₆ plus NbS₂. The position of the original metal surface was notedy platinum-wire marker experiments to be the interface between the inner andouter layers. The location of the marker indicates that the outer layer, generally greater in thickness than the inner layer, grew by outward diffusion of the nickel cations, and the inner layer formed probably by the inward diffusion of sulfur. Neither preferential sulfidation nor internal sulfidation was observed. The development of the scale structures from the transient stage to steady state was also studied.     

The high-temperature corrosion behavior of Co-Nb alloys in mixed-gas atmospheres

The corrosion of Co-Nb alloys containing up to 30 wt.% Nb in H₂-H₂S-H₂O gas mixtures was studied over the temperature range of 600–800°C. The gas composition falls in the stability region of cobalt sulfide and Nb₂O₅ in the phase diagrams of the Co-O-S and Nb-O-S systems at all temperatures studied. Duplex scales, consisting of an outer layer of cobalt sulfide and a complex, heterophasic inner layer, were formed at all temperatures studied. In addition to cobalt sulfide and CoNb₃S₆, a small amount of NbO₂ was found in the inner layer. The reason for the formation of NbO₂ over that of Nb₂O₅ in the scale is that the outer sulfide scale lowers the oxygen activity within the scale into the NbO₂-stability region. Two-stage kinetics were observed for all alloys, including an initial irregular stage usually followed by a steady-state parabolic stage. The steady-state parabolic rate constants decreased with increasing amounts of Nb, except for Co-20Nb corroded at 700°C. Nearly identical kinetics were observed for Co-20Nb corroded at 600°C and 700°C. The presence of NbO₂ particles leads only to a limited decrease of the available cross-section area for the outward-diffusing metal ions. The activation energies for all alloys are similar and are in agreement with those obtained in a study of the sulfidation of the same alloys. The primary corrosion mechanism involves an outward Co transport.     

Effect of Al on high-temperature corrosion of Co-15a/oNb alloys in H2-H2O-H2S environments

Co–15 at.% Nb alloys containing up to 15 at.% Al were corroded in gaseous H₂–H₂O–H₂S mixtures over the temperature range of 600–900°C. The corrosion kinetics followed the parabolic rate law at all temperatures. Corrosion resistance improved with increasing Al content except at 900°C. Duplex scales formed on alloys consisting of an outer layer of cobalt sulfide and a heterophasic inner layer. A small amount of Al₂O₃ was found only on Co–15Nb–15Al. Contrary to what formed in Co–Nb binary alloys, neither NbS₂ nor NbO₂ were found in the inner layer of all alloys, but Nb₃S₄ did form. The absence of NbS₂ and NbO₂ is due to the formation of stable Al₂O₃ and Al₂S₃ that effectively blocked the inward diffusion of oxygen and sulfur, respectively, and to the reduction of activity of Nb by Al additions in the alloys. Intercalation of ions in the empty hexagonal channels of Nb₃S₄ is associated with the blockage of the transport of cobalt. An unknown phase (possibly Al_0.5NbS₂) was detected. Alloys corroded at 900°C were abnormally fast and formed a scale containing CoNb₃S₆ and Co. Pt markers were found at the interface between the inner and outer layers.     

The corrosion of Fe-Mo alloys in H2/H2O/H2S atmospheres

The corrosion of Fe-Mo alloys containing up to 40 wt.% Mo was studied over the temperature range 600–980C in a H₂/H₂O/H₂S mixture having a sulfur pressure of 10^–5 atm. and an oxygen pressure of 10^–20 atm. at 850C. All alloys were two-phase, consisting of an Fe-rich solid solution and an intermetallic compound, Fe₃Mo₂. The scales formed on Fe-Mo alloys were bilayered, consisting of an outer layer of iron sulfide (FeS) and of a complex inner layer whose composition and microstructure were a function of the reaction temperature and of the Mo content of the alloys. No oxides formed under any conditions. The corrosion kinetics followed the parabolic rate law at all temperatures. The addition of Mo caused only a slight decrease of the corrosion rate. Platinum markers were always located at the interface between the inner and outer scales, indicating that outer scale growth was primarily due to outward diffusion of iron, while the inner scale growth had a contribution from inward diffusion of sulfur.     

The effect of Al on the corrosion behavior of Ni-Mo in a H2/H2O/H2S gas mixture

The corrosion behavior of seven Ni-Mo-Al alloys was investigated over the temperature range of 600–950°C in a mixed-gas atmosphere of H ₂/H ₂O/H ₂ S. The parabolic law was followed at low temperatures, while linear kinetics were generally observed at higher temperatures. At a fixed Mo content, the transition from parabolic to linear kinetics shifted to higher temperature with increasing Al concentration. Double-layered scales generally formed on alloys having a low Al content, consisting of an outer layer of nickel sulfide and a complex inner scale. The thickness of the outer scale and the inner scale decreased as the Al content increased. The outer scale became porous and discontinuous with increasing Al content and temperature. Al ₂ O ₃ was detected in the scales of all alloys corroded at higher temperatures ( 800°C), even though the amount of Al ₂ O ₃ was very small in some cases. The decrease in corrosion rate with increasing Al content may be attributed to the formation of Al ₂ O ₃,Al _0.55 Mo ₂ S ₄,and Al ₂ S ₃ in the inner scale.     

The high-temperature corrosion behavior of Fe-Mo-Al alloys in H2/H2O/H2S mixed-gas environments

The corrosion behavior of 11 Fe-Mo-Al ternary alloys was studied over the temperature range 700–980°C in H₂/H₂O/H₂S mixed-gas environments. With the exception of Fe-10Mo-7Al, for which breakaway kinetics were observed at higher temperatures, all alloys followed the parabolic rate law, despite two-stage kinetics which were observed in some cases. A kinetics inversion was observed for alloys containing 7 wt.% Al between 700–800°C. The corrosion rates of Fe-20Mo and Fe-30Mo were found to be reduced by five orders of magnitude at all temperatures by the addition of 9.1 or higher wt.% aluminum. The scales formed on low-Al alloys (5 wt.% Al) were duplex, consisting of an outer layer of iron sulfide (with some dissolved Al) and a complex inner of Al_0.55Mo₂S₄, FeMo₂S₄, Fe_1.25Mo₆S_7.7, FeS, and uncorroded FeAl and Fe₃Mo₂. Platinum markers were always located at the interface between the inner and outer scales for the low-Al alloys, indicating that outer-scale growth was due mainly to outward diffusion of cations (Fe and Al), while the inner scale was formed primarily by the inward flux of sulfur anions. Alloys having intermediate Al contents (7 wt.%) formed scales that consisted of FeS and Al₂O₃. The amount of Al₂O₃ increased with increasing reaction temperature. The high-Al-content alloys (9.1 and 10 wt.%) formed only Al₂O₃ which was responsible for the reduction of the corrosion rates.     

Corrosion of Ni-Ti alloys in the molten (Li,K)2CO3 eutectic mixture

The corrosion of pure Ni and of binary Ni-Ti alloys containing 5, 10, and 15 wt.% Ti respectively in molten (0.62Li,0.38K)₂CO₃ at 650°C under air has been studied. The corrosion of the single-phase Ni-5Ti alloy was slower than that of pure Ni, forming an external scale composed of NiO and TiO₂. The two-phase Ni-10Ti and Ni-15Ti alloys underwent much faster corrosion than pure Ni, producing an external scale containing NiO and TiO₂, and a thick internal oxidation zone of titanium mainly involving the intermetallic compound TiNi₃ in the original alloys. The rates of growth of the external scales for the Ni-Ti alloys were reduced with the increase of their titanium content, while the internal oxidation was significantly enhanced. The corrosion mechanism of the alloys is also discussed.     

Sulfidation kinetics and mechanism of some Ni-Mo-Al and Ni-Al alloys over the temperature range 600–800°C

The sulfidation behavior of five Ni-Mo-Al ternary alloys and two Ni-Al binary alloys was studied over the temperature range 600–800°C in sulfur vapor of 10^–2 atm. The effect of sulfur pressure was also investigated at and10^–4 atm. using two Ni-Mo-Al alloys. The sulfidation of all Ni-Mo-Al andNi-Al alloys followed the parabolic rate law. The sulfidation rate decreasedwith increasing Al content for a given Mo content for Ni-Mo-Al alloys. Twobinary alloys, Ni-13.5Al and Ni-31Al, sulfidized at comparable rates toNi-30Mo-7.5Al, which has excellent sulfidation resistance. The activationenergies for ternary alloys range from 44.8–50.8 kcal/mol, whereas those forNi-13.5Al and Ni-31Al are 41.5 and 39.1 kcal/mol, respectively. Complexscales formed on all Ni-Mo-Al alloys, consisting of an outer layer of nickelsulfide and an inner layer of MoS₂, A1₂S₃, and Al_0.55Mo₂S₄. Sulfide scalesformed on Ni-Al alloys were bilayered, consisting of an outer layer of nickelsulfide and an inner layer of A1₂S₃. The low sulfidation rate of the ternaryalloys was attributed to the combined presence of both A1₂S₃ and Al_0.55Mo₂S₄.The sulfidation kinetics of two Ni-Mo-Al alloys are independent of sulfurpressure, suggesting that the growth of the inner layer was the dominant process.     

The high-temperature corrosion of Fe-Nb alloys in a H2/H2O/H2S gas mixture

The corrosion of Fe-Nb alloys containing up to 40 wt.% Nb has been studied over the temperature range 600–980°C in a mixed gas of constant composition having sulfur and oxygen pressures ranging from 10^–8 to 10^–4 atm. and from 10^–27 to 10^–18 atm., respectively. All alloys were two-phase, consisting of an Fe-rich solid solution and an intermetallic compound, Fe₂Nb. The scales formed on the Fe-Nb alloys were duplex, consisting of an outer layer of iron sulfide (FeS) and an inner complex layer of Fe_xNbS₂(FeNb₂S₄ or FeNb₃S₆), FeS and unreacted Fe₂Nb. No oxides were detected at any temperature. The addition of Nb reduced the corrosion rate. The corrosion kinetics of Fe-Nb alloys followed the parabolic rate law, regardless of alloy composition and temperature. Platinum markers, attached to the original alloy surfaces, were always located at the interface between the inner and outer scales.     

The effect of preoxidation on the sulfidation of Ni-20Cr (2–5)Al Alloys

Ni-20Cr alloys with 2, 3.5, and 5 wt.% Al have been preoxidized up to 100 hr at 1000°C in dry H₂, in H₂/23% H₂O and in air and subsequently exposed to an H₂/5% H₂S atmosphere at 750° C. During the preoxidation treatment different types of oxide scales were formed which affect the sulfidation protection in different ways. Optimum results were obtained for alloys with 3.5 and 5 wt.% Al after 20 hr exposure to dry H₂ at 1000°C. A thin Al₂O₃ scale is formed which decreases the sulfur attack by more than one order of magnitude. Preoxidation conditions for Ni-20Cr-2Al alloys in H₂ and for Ni-20Cr-2Al and Ni-20Cr-3.5Al in H₂/H₂O were observed to be less effective. No improvement was found for preoxidation in air or for Ni-20Cr-5Al alloys preoxidized in H₂/H₂O.     

High-temperature corrosion of Co-15Mo alloys containing ternary additions of Al in mixed-gas environments

The corrosion behavior of Co-15 at.% Mo alloys containing up to 20at.% Al in gaseous H ₂ -H ₂ O-H ₂ S mixtures was studied over the temperature range of 600–900°C. The corrosion kinetics of all alloys followed the parabolic rate law over the temperature range of interest. Corrosion resistance increased with increasing aluminum content. Complex scales formed on the alloys, consisting of an outer layer of cobalt sulfide and a heterophasic inner layer. Al ₂ O ₃ formed only at high temperatures in alloys having aluminum additions of 15at.% or more. The absence of Al ₂ O ₃ in some cases is due to the small volume fraction of the intermetallic phase CoAl in the alloys and the nature of the slow growth rate of Al ₂ O ₃.Improvement in corrosion resistance is attributed to the presence of a ternary sulfide, Al _0.55 Mo ₂ S ₄,and Al ₂ O ₃ in the inner layer.     

The effect of Mo on the high-temperature sulfidation of Ni

The sulfidation behavior of Ni-Mo alloys containing up to 40 wt.% Mo was studied at =0.01 atm. over the temperature range of 550–800°C. The alloys included two solid solutions (Ni-10Mo and Ni-20Mo), the single-phase intermetallic compound Ni₄Mo(Ni-29Mo), and two alloys which were two-phase, Ni-30Mo and Ni-40Mo (Ni₄Mo+Ni₃Mo). The sulfidation of all alloys followed the parabolic rate law. The rate of sulfidation decreased with increasing amounts of Mo. Activation energies for sulfidation gave values of 39.1±1.0 kcal/mol. The sulfide scales were bilayered, consisting of an outer layer nickel sulfide (NiS_1+x and Ni₃S₂) and an inner, complex layer of MoS₂ plus intermetallic particles. The rate-controlling step of the sulfidation for the alloys was inward sulfur diffusion and/or outward nickel diffusion through the inner MoS₂ layer. Neither selective sulfidation nor internal sulfidation were observed. No significant difference in the sulfidation kinetics, sulfide structure, and scale constitution could be noted between single-phase alloys and two-phase alloys. The location of the markers was the interface between the inner and outer layers, indicating that the inner layer formed by inward diffusion of sulfur, and the outer layer grew by outward nickel diffusion. The inability to form a continuous protective molybdenum sulfide layer is discussed in terms of the structure of MoS₂ and changes caused by intercalation of Ni into the layered crystal structure. The decrease in sulfidation rate with increasing Mo was attributed to increasing amounts of the intermetallic compound. The increasing volume fraction of particles decreased the available diffusion area in the inner layer and provided a blocking effect.     

Effects of sulfur pressure on the sulfidation behavior of 310 stainless steel

High-temperature sulfidation behavior of 310 stainless steel was studied over the temperature range of 700–900°C above a pure sulfur pool with the sulfurvapor range of 10^–4–10^–1 atm. The corrosion kinetics followed the parabolic rate law in all cases. The corrosion rates increased with increasing temperature and sulfur pressure. The scales formed on 310 stainless steel were complex and multilayered. The outer scale consisted of iron sulfide (with dissolved Cr), (Fe, Ni)₉S₈ and chromium sulfides (Cr₂S₃ and Cr₃S₄ with dissolved Fe), while the inner layer was a heterophasic mixture of Cr₂S₃, Cr₃S₄, NiCr₂S₄, and Fe₁–_xS. Platinum markers were found to be located at the interface between the inner and outer scales, suggesting that the outer scale grew by the outward transport of cations (Fe, Ni, and Cr), and the inner scale grew by the inward transport of sulfur. The formation of Cr₂S₃, Cr₃S₄, and NiCr₂S₄ partly blocked the transport of iron through the inner scale, resulting in a reduction of the corrosion rates as compared with the results in the literature.     

The high-temperature corrosion behavior of Nb-Al alloys in a H2/H2S/H2O gas mixture

The corrosion behavior of pure Nb and three Nb Al alloys containing 12.5, 25, and 75 at.% Al was studied over the temperature range of 800–1000°C in a H₂/H₂S/H₂O gas mixture. Except for the Nb-12.5Al alloy consisting of a two phase structure of -Nb and Nb₃Al, other alloys studied were single phase. The corrosion kinetics followed the parabolic rate law in all cases, regardless of temperature and alloy composition. The parabolic rate constants increased with increasing temperature, but fluctuated with increasing Al content. The Nb-75Al alloy exhibited the best corrosion resistance among all alloys studied, whose corrosion rates are 1.6–2.2 orders of magnitude lower than those of pure-Nb (depending on temperature). An exclusive NbO₂ layer was formed on pure Nb, while heterophasic scales were observed on Nb-Al alloys whose compositions and amounts strongly depended on Al content and temperature. The scales formed on Nb-12.5Al consisted of mostly NbO₂ and minor amounts of Nb₂O₅, NbS2, and -Al₂O₃, while the scales formed on Nb-25Al consisted of mostly Nb₂O₅ and some -Al₂O₃. The scales formed on Nb-75Al consisted of mostly -Al₂O₃ and Nb₃S₄ atT 900°C, and mostly -Al₂O₃ , Nb₃S₄ and some AlNbO₄ at 1000°C. The formation of -Al₂O₃ and Nb₃S₄ resulted in a significant reduction of the corrosion rates.     

The corrosion behavior of Co-Mo alloys in H2-H2O-H2S environments

The corrosion behavior of Co alloyed with up to 40 wt.% Mo alloys was studied in H₂-H₂O-H₂S gas mixtures over the temperature range between 600C and 900C. The parabolic rate constants for corrosion decreased with increasing amounts of Mo. The compositions of all gas atmospheres fall in the sulfide(s stability region of the ternary M-O-S phase diagrams at all temperatures investigated. All the corrosion scales were composed of sulfides, while no oxide was detected. The sulfide scales formed were duplex at all temperatures except at 900C. The outer layer consisted primarily of cobalt sulfide, while the inner layer was complex and heterophasic, the phases formed being highly composition dependent. MoS₂ predominated in the inner layer for all alloys. However, a metallic Mo layer was formed in the innermost layer of Co-40 Mo. Activation energies were different for all alloys, increasing with increasing Mo content. Identical kinetics were observed for Co-30Mo corroded at 700–800C. A Chevrel-phase Co_1.62Mo₆S₈ was present in scales formed on the samples exhibiting the temperature-independent kinetics. A possible model in which Co_1.62Mo₆S₈ forms preferentially in H₂-containing mixed gas is suggested. Alloys corroded at 900C formed a lamellar-structure scale which contained Co and CoMo₂S₄ layers perpendicular to the alloy surface. A eutectoid decomposition of an unknown Co-Mo sulfide may be responsible for the presence of the lamellar structure.     

Effect of Nb on the high-temperature sulfidation behavior of cobalt

The sulfidation behavior of Co-Nb alloys containing up to 30wt.% Nb was studied in sulfur vapor at a pressure of 0.01 atm in the temperature range of 600–700°C. Increasing niobium content decreased the sulfidation rate, following the parabolic rate law. An activation energy of 25.6 kcal/mole was obtained for Co-10Nb, Co-20Nb, and Co-25Nb, while a value of 20.5 kcal/mole was found for Co-30Nb. All were two-phase alloys, consisting of solid solution -Co and the intermetallic compound, NbCo₃. The two-phase alloys formed a rather thick outer layer of cobalt sulfides and a heterophasic inner layer that was complex. The inner layer always contained the mixed sulfide CoNb₂S₄ which, depending on the alloy composition, coexisted with cobalt sulfide, NbS₂, and / or NbCo₃ particles. Short-time sulfidations showed that the solid solution initially sulfidized rapidly to form nodules of cobalt sulfide, whereas the NbCo₃ phase formed a thin protective layer of NbS₂. The nodules grew laterally until they coalesced into the continuous, outer thick layer, while the NbS₂ completely or partially reacted with the cobalt sulfide to form CoNb₂S₄. Platinum markers were always found at the interface between the inner and outer scales, the location of the original metal surface.     

Effect of alloy grain size and silicon content on the oxidation of austenitic Fe-Cr-Ni-Mn-Si alloys in a SO2-O2 gas mixture

Austenitic Fe-18Cr-20Ni-1.5Mn alloys containing 0, 0.6, and 1.5 wt.% Si were produced both by conventional and rapid solidification processing. The cyclic oxidation resistance of these alloys was studied at 900°C in a SO ₂-O ₂ gas mixture to elucidate the role of alloy microstructure and Si content on oxidation properties in bioxidant atmospheres. All the large-grained, conventionally processed alloys exhibited breakaway oxidation during cyclic oxidation due to their poor rehealing characteristics. The rapidly solidified, fine-grained alloys that contained less than 1.5 wt.% Si exhibited very protective oxidation behavior. There was considerable evidence of sulfur penetration through the protective chromia scale. The rapidly solidified alloys that contained 1.5 wt.% Si underwent repeated scale spallation that led to breakaway oxidation behavior. The scale spallation was attributed to the formation of an extensive silica sublayer in the presence of sulfur in the atmosphere.