纳米La0．8Ba0．2MnO3／Ni粉复合体系的微波吸收性能

采用溶胶-=凝胶法制备La0．8Ba0．2MnO3粉体,并与纳米Ni粉按不同质量比复合,制得复合材料样品。测量样品在2-18GHz频率范围内的复介电常数、复磁导率并计算微波反射系数,分析不同组分对材料微波吸收性能的影响及其可能的吸收机制。研究结果表明：复合体系比单一组分样品具有更好的吸收效果;当La0．8Ba0．2MnO3含量为62、5％时,材料微波吸收效果最佳;当样品厚度为2mm时,大于10dB的吸收频宽达到3．6GHz,最大吸收峰值为24dB;当样品厚度为1．8mm时,大于10dB的吸收频宽达到3．3GHz,最大吸收峰值为44dB;LaMnO,在A位掺杂Ba2＋,其电磁性能将发生变化,再与磁性纳米Ni粉复合,介电损耗和磁损耗的综合作用能使体系的微波吸收效能显著加强。     

泡沫吸波材料结构对吸波性能的影响

为了研究吸波材料结构与吸波性能的关系,以无机泡沫吸波材料作为基体,采用多层复合研究阻抗匹配特性对吸波性能的影响,当材料为"透波层/吸收层"的2层复合结构时,在2.0~18.0 GHz频段反射率均小于-10.0dB,且于12.7 GHz处出现最大衰减峰为-21.5 dB.采用角锥和锥台处理研究材料表面构造对吸波性能的影响,结果表明:表面处理可以明显提高材料吸波性能,且角锥处理优于锥台处理.5×5阵列角锥的有效吸收带宽(反射率小于-10.0 dB)为15.3 GHz,反射率在9.4 GHz处到达最小值为-43.4 dB;8×8阵列角锥的有效吸收带宽(反射率小于-10.0 dB)为18.0 GHz,平均反射率达-34.5 dB.     

La1-xCexMnO3凝胶晶化过程与微波吸收性能

用溶胶一凝胶法制备了La1-xCexMnO3粉体,根据DSC-TGA、FT-IR、XRD分析了样品的晶化过程,用圆柱体法测试了样品的室温电阻率,用微波网络分析仪测试样品的微波吸收性能．结果表明,样品凝胶在煅烧时经过脱水、剧烈分解、逐渐晶化等过程,900％左右形成稳定的钙钛矿结构并伴有少量CeO2杂相;室温电阻率处于半导体范围,且随掺杂量z增加而减小;样品厚度为2．2mm、x=0．4时,13．2GHz频率位置处微波吸收峰值为27dB,10dB频宽为3．2GHz．分析认为,合适的电阻率、钙钛矿晶体极化驰豫及共振、铁磁团簇转向及共振是材料具有良好微波吸收性能的原因．     

PVA碳化法制备SiC@C一维纳米复合材料及其吸波性能

以自制的SiC纳米线作为原料,采用聚乙烯醇(PVA)碳化法,在无催化剂的条件下制备SiC@C一维纳米复合材料。采用扫描电镜(SEM)、透射电镜(TEM)、X射线衍射(XRD)等测试手段对制备产物进行了表征,并对其微波吸收性能进行了研究。结果表明:在PVA的分散温度为70℃,PVA与SiC的质量比为10∶1,反应时间为2h,碳化温度为1 000℃,碳化时间1h的工艺参数下制备的SiC@C一维纳米复合材料在2~18GHz内电磁吸收损耗可达-26.754dB,其频宽高达5.2GHz(11.12~16.32GHz),匹配厚度仅为2.0mm,可以实现对频宽、轻质、高频率的强吸收要求。     

多壁碳纳米管复合材料的微波吸收性能

用石蜡分别与多壁碳纳米管及大内径薄多壁碳纳米管按不同的质量比混合,制得了复合吸波材料.采用同轴法测量了复合材料在2~18GHz范围内的复介电常数和复磁导率,并计算了材料对微波的反射率,分析了其吸波性能.结果表明:碳纳米管复合材料在2~18GHz范围具有吸波性能.其中质量分数为15%的多壁碳纳米管的最大吸收峰在10.4GHz,其值为-21.7dB,质量分数为15%的大内径薄壁多壁碳纳米管的最大吸收峰在11.2GHz,值为-17.6dB.     

掺杂聚苯胺吸波材料的研究

用不同化学合成方法分别制备了HCl-PAn、H2SO4-PAn、H2SO4-PAn-FeCl3和DBSA-PAn粉末，采用3cm波导式测量线在8～14GHz频率范围内，用多点拟合的实验和计算方法对掺杂聚苯胺的微波吸收特性及参量进行了研究。并将HCl-PAn和DBSA-PAn粉末与石蜡共混复合，制备了聚苯胺复合材料，着重研究了这2种聚苯胺用量对复合材料电导率的影响。结果表明，DBSA-PAn复合材料的电导率突变较HCl-PAn复合材料早，同时，令人注意的是，将HCl-PAn与浓H2SO4-PAn-FeCl3按一定的比例混合，可以合成出平均衰减为13．37dB、最大衰减为26．7dB、密度为0．7g／cm^3、频宽为10．34～14GHz的有利于吸收微波的材料。     

(1-x)Ba(Mg1/3Ta2/3)O3-xBaTiO3复合微波介质陶瓷的合成

以传统电子陶瓷制备工艺合成了(1-x)Ba(Mg1/3Ta2/3)O3-xBaTiO3(0＜x＜11/12,简称BMTT)二元复合钙钛矿微波介质陶瓷.研究了不同BaTiO3(BT)掺入量对BMTT介电性能和结构的影响.实验结果表明Ti4+与Mg2+、Ta5+离子对构成类质同相代换,形成BMTT系列固溶体,与Ba(Mg1/3Ta2/3)O3(BMT)具有相同的晶体结构.当体系组成为0.5Ba(Mg1/3Ta2/3)O3-0.5BaTiO3时,在1 480℃下烧结且保温3 h所制备的陶瓷材料微波介电性能为εr=89,Q*f=12 700 GHZ,τf=190×10-6/℃ .     

球磨工艺对Y-Fe-Cr合金吸波性能影响

采用XRD、SEM和矢量网络分析仪分析相结合的方法研究球磨时间对Y-Fe-Cr合金微粉吸波性能的影响.结果表明:随着球磨时间从50 h不断增加,Y9Fe88Cr3吸波合金的吸收峰逐渐向低频移动;当球磨时间低于70 h时,合金扁平化及各向异性较好,其反射率较低,合金粉末吸波性能较好,在吸波涂层厚度为d=1.8 mm条件下,球磨时间为50 h和70 h的合金粉末的电磁波吸收峰峰值分别达到-14.7 dB和-14.4 dB,＜-10 dB的吸波带宽均达到7 GHz;当球磨时间达到80 h后,由于合金粉末颗粒碎化变细导致各向异性变差,其吸波性能变差,在吸波涂层厚度为d=1.8 mm条件下,合金粉末电磁波吸收峰峰值和＜-10 dB的吸波带宽分别为-12.5 dB和3.5 GHz,较球磨时间为70 h之前的合金粉末的吸波峰值和带宽减小了2 dB和3.5 GHz.研究结果为制备同类吸波合金微粉提供一定的理论依据.     

PPy@Fe2O3核壳结构的复合织物的电磁性能研究

以厚度薄、透气透湿性好的柔性涤棉织物作为基布,采用工艺简单的溶胶-凝胶法和原位聚合法两步制备了PPy@Fe₂O₃核壳结构的复合织物,并研究了掺杂剂和氧化剂与吡咯的摩尔比对其电磁性能的影响。结果表明：当氧化剂和掺杂剂与吡咯摩尔比为2∶1时,复合织物的反射损耗最小,在13.0 GHz时达到最小值为-7.96 dB,可以吸收84.0%的电磁波,小于5 GHz的带宽达到11.4 GHz(6.6 GHz～18.0 GHz)。     

双层混杂纤维／炭黑改性环氧树脂复合材料的制备及其吸波性能

通过采用整体压制的方法制备了双层混杂纤维／炭黑改性环氧树脂复合材料,对其吸波性能进行了研究。结果表明：随着炭黑含量的增加,材料的反射衰减峰向低频移动,当炭黑含量较高时,吸收主要作用在低频波段,且存在明显的双反射衰减峰。当炭黑含量为6％时,在13．6GHz处反射衰减峰值可达-20．6dB,≤-10dB的有效带宽为3．6GHz。当炭黑含量为8％时,双反射衰减峰分别在10．6GHz和7．8GHz,峰值分别为-17．0dB和-14．9dB,≤-10dB的有效带宽为6．7GHz。     

Influence of absorbent on electromagnetic wave absorbing property of porous concrete

Influences of ferrite content and iron ore powder content on electromagnetic wave absorbing property of porous concrete are studied.The radar cross section(RSC)of samples was tested in a microwave anechoic chamber.Results show that the optimum content of ferrite is 15%,and the minimum,maximum and average reflectivity of the sample is-46.60 dB,-10.84 dB and-23.75 dB,respectively.And the sample’s improved bandwidth is 8.2 GHz.The optimum content of iron ore powder is 20%,and the minimum,maximum and average reflectivity of the sample is-34.69 dB,-9.25 dB and-20.69 dB,respectively.And the sample’s improved bandwidth is 6 GHz.In conclusion,appropriate ferrite and iron ore powder can improve wave absorbing property and widen wave absorption bandwidth of porous concrete.     

Microwave Absorption Properties of the Carbonyl Iron/EPDM Radar Absorbing Materials

Employing carbonyl iron powder and Ethylene-Propylene-Diene Monomer(EPDM)as the absorbent and matrix,rubber radar absorbing materials(RAM)were prepared.Effects of the carbonyl iron volume fraction and the thickness of the RAM on the microwave absorption properties in the frequency range of 2.6-18GHz were studied,and a mathematical analysis was made using the electromagnetic theory. The experimental results indicate that the minimum reflectivity of the radar absorbing materials continuously decreases with the increase of the carbonyl iron volume fraction,and the absorption peak also moves towards the low frequency for the same thickness of the RAM.The minimum reflectivity of the 3.0 mm RAM is -21.7dB at 3.5 GHz when the volume fraction of carbonyl iron is 45%.The reflectivity of the RAM is not in direct proportional to the thickness of the RAM,when the RAM has the same volume fraction of the carbonyl iron.The reflectivity of the RAM presents a regular trend at a given carbonyl iron volume fraction in the frequency range of 2.6-18 GHz.With the increase of the thickness,the maximum absorption peak moves towards low frequency band,the minimum reflectivity firstly decreases and then increases,and the absorption bandwidth for reflectivity<-10 dB firstly increases and then decreases.The microwave absorption properties of the RAM are determined by the thickness and the composition of the radar absorbing materials. Theoretical analysis indicates that the reflectivity of the RAM is determined by the matching degree of the air’s characteristic impedance and the input impedance.     

钡铁氧体表面化学镀Ni-P合金的制备及性能

为提高钡铁氧体的吸波性能,以钡铁氧体为芯材,采用化学镀的方法制备表面包覆Ni-P镀层的钡铁氧体复合粒子.并利用XRD、SEM、EDS及矢量网络分析仪对其晶体结构、表面形貌、成分、电磁吸收性能进行分析.结果表明:钡铁氧体表面包覆完整的Ni-P合金镀层,化学镀工艺显著改善材料的电磁性能,并提高材料对电磁波的吸收能力,镀后复合粒子在2～18GHz频段内,最大反射率为-24.3dB,大于-10dB的吸收频带宽约2.8GHz.     

Electromagnetic shielding and absorption properties of fiber reinforced cementitious composites

In order to investigate the electromagnetic shielding effectiveness (SE) and absorbing properties of fiber reinforced concrete, steel fiber, carbon fiber and synthetic polyvinyl alcohol (PVA) fiber reinforced concrete were researched. The results show that with the increase of fiber volume fraction, the SE and trend of frequency change of corresponding fiber reinforced concrete are enhanced. When the volume content of steel fiber is 3%, the SE of concrete is above 50 dB and its frequency is above 1.8 GHz. Moreover, in the range of 8-18 GHz, steel fiber, carbon fiber and PVA fiber all can improve the microwave absorption properties of concrete. The concrete with 0.5% carbon fiber can achieve the best absorbing property, the minimum reflectivity is about -7 dB; while steel fiber optimal volume fraction is 2%. The reflectivity curve of PVA fiber reinforced concrete fluctuates with the frequency, and the minimum value of the reflectivity is below -10 dB. The results show that fiber reinforced concrete could be used as EMI(electromagnetic interference) prevention buildings by attenuating and reflecting electromagnetic wave energy.     

铁氧体/铁粉混合材料的电磁吸波性能

以铁氧体、铁粉作为吸收剂制备多种电磁吸波涂料,测试与分析所得电磁吸波涂料的电导率、电磁参数及吸波性能。结果表明随着铁粉掺量的增加,所得电磁吸波涂料的电导率增加,在中高频区介电损耗和磁损耗均有所提高;铁粉与铁氧体的质量比为2：8时吸波涂层的吸波性能最好;反射率损耗〈-10.0 dB时的有效吸收频段在中低频区,有效带宽达4.5 GHz,最大吸收率为-16.63 dB。     

立方体α-Fe合成及其含量对吸波性能的影响

为了研究形状各向异性与吸波剂含量对吸波性能的影响,利用溶剂热法成功制备了具有形状各向异性的立方晶形微纳米Fe粉.采用X射线衍射仪、扫描电子显微镜、X射线光电子谱等手段,对所制样品的微观结构、形貌与组成成分进行了研究.利用矢量网络分析仪研究了吸波剂含量对吸波性能的影响.结果表明,立方体状α-Fe的尺寸约为300 nm,其质量分数与微波吸收性能呈非线性增强关系.当α-Fe质量分数为50%时,反射损耗高达-48. 9 dB,频率为8. 78 GHz,对应的涂层厚度为2 mm,反射损耗小于-10 dB的频率范围为2. 04～18 GHz,对应的涂层厚度范围为1. 28～7 mm.     

左、右手材料结构吸波性能的计算机仿真

为了考察在吸波体结构设计中引入左手材料所产生的效果,提出了空气/左手介质/右手介质/金属结构吸波体模型,用传输线模型对该结构的吸波特性进行了理论分析,并用遗传算法对结构进行了优化与计算机仿真.研究结果表明,在微波垂直入射条件下,当材料整体电磁参量最优匹配时,在0.4～10 GHz频带内该结构能实现平均-12 dB的反射率.表明左手介质的引入有利于实现材料整体电磁参量的较好匹配,提高吸收峰值,拓宽吸波体的带宽.这为宽频带/多频带吸收材料的研制提供了一条可供选择的途径.     

Preparation and properties of Ni-plated glass beads/PVC composite

Ni-plated glass beads（GB） was obtained by electroless plating, based on PVC adhesive, Niplated GB/PVC composite was prepared. Temperature insulation, fi re retardation and microwave absorption properties were tested, the results showed that the nickel coating was compact and continuous, Ni-plated GB/ PVC composite is a kind of excellent temperature insulated, fi re retardate and light-weight material, and especially for microwave absorption well; Refl ectivity was lower than-2 dB in the frequency range of 11-17 GHz.