Poly(ε-caprolactone)-based additives: Plasticization efficacy and migration resistance

A family of poly(caprolactone) (PCL)-based oligomeric additives was evaluated as plasticizers for poly(vinyl chloride) (PVC). We found that the entire family of additives, which consist of a PCL core, diester linker, and alkyl chain cap, were effective plasticizers that improve migration resistance. The elongation at break and tensile strength of the blends made with the PCL-based additives were comparable to blends prepared with diisononyl phthalate (DINP), a plasticizer typically used industrially, and diheptyl succinate (DHPS), an alternative biodegradable plasticizer. Increasing concentration was found to decrease glass transition temperature (T_g) and increase elongation at break, confirming their role as functional plasticizers. We found that all of the PCL-based plasticizers exhibited significantly reduced leaching into hexanes compared to DINP and DHPS. The PCL-based plasticizers with shorter carbon chain lengths reduced leaching more than those with longer carbon chain lengths.     

Evaluation of the effects of biobased plasticizers on the thermal and mechanical properties of poly(vinyl chloride)

Blends were prepared of poly(vinyl chloride) (PVC) with four different plasticizers; esters of aconitic, citric, and phthalic acids; and other ingredients used in commercial flexible PVC products. The thermal and mechanical properties of the fresh products and of the products after 6 months of aging were measured. Young's modulus of the PVC blends was reduced about 10‐fold by an increase in the plasticizer level from 15 to 30 phr from the semirigid to the flexible range according to the ASTM classification, but a 40‐phr level was required for PVC to retain its flexibility beyond 6 months. At the 40‐phr level, tributyl aconitate performed better than diisononyl phthalate (DINP) or tributyl citrate, in terms of lowering Young's modulus, both in the fresh materials and those aged for 6 months. The effects of the four plasticizers on the glass‐transition temperature (T_g) were similar, with T_g close to ambient temperature at the 30‐ and 40‐phr levels in freshly prepared samples and at 40–60°C in those aged for 6 months. The thermal stability of the PVC plasticized with DINP was superior among the group. Overall, tributyl aconitate appeared to be a good candidate for use in consumer products where the alleged toxicity of DINP may be an issue. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 1366–1373, 2006     

Plasticizers derived from cardanol: synthesis and plasticization properties for polyvinyl chloride(PVC)

Two natural plasticizers derived from cardanol (CD), cardanol acetate (CA) and epoxidized cardanol acetate (ECA), were synthesized and characterized by ¹H NMR and ¹³C NMR. The plasticizing effects of the obtained plasticizers on semi-rigid polyvinylchloride (PVC) formulations were also investigated. Two commercial phthalate ester plasticizers, dioctyl terephthalate (DOTP) and diisononyl phthalate (DINP), were used as controls. Mechanical and thermal properties, compatibility, thermal stability, microstructure, and workability were assessed by dynamic mechanical analysis (DMA), mechanical analysis, thermogravimetric analysis (TGA), scanning electron microscopy (SEM), and dynamic stability analysis, respectively. Results indicated that the natural plasticizer ECA had overallsuperior flexibility, compatibility, thermal stability, and workability comparable to both controls. The obtained CA and ECA have lower volatility resistance and similar extraction and exudation resistance than that of DOTP and DINP. The CA was further blended with DOTP in soft PVC films. Results of DMA, TGA and mechanicalanalysis indicated that CA can serve as a secondary plasticizer to improve the related properties of soft PVC formulations. These CD derived plasticizers show promise as an alternative to fully or partially replace petroleum-based plasticizers.     

Morphologies of miscible PCL/PVC blends confined in ultrathin films

Morphologies of ultrathin films (10–60 nm) of miscible poly(ε-caprolactone)/poly(vinyl chloride) (PCL/PVC) blends have been investigated under isothermal crystallization conditions by real time atomic force microscopy, and electron diffraction techniques. It was found that the morphology and growth rate of PCL/PVC blends strongly depend on the blend composition, crystallization temperature and film thickness. At a film thickness of 30 nm, the truncated lozenge-shape morphology of pure PCL crystals, found when the growth rate is slow, bent with increasing PVC content to form S-shaped or inverted S-shaped crystals, the curvature increasing by lowering the crystallization temperature. Electron diffraction patterns reveal that these crystals are flat-on single crystals with the PCL molecular chains (c axis) in the blends slightly tilted with respect to the lamella normal, while the b direction of the crystal lattice, corresponding to the fast growing direction of the growth front, follows a S line. Upon decreasing the film thickness (<30 nm), the S-shaped or inverted S-shaped crystals transform into four-branch dendritic lamellae.     

Castor Epoxy Fatty Acid Alkyl Ester Estolides as Bioplasticizers for Poly(Vinyl Chloride)

Epoxy fatty acid alkyl ester estolides were synthesized from castor oil to be used as biobased plasticizers for poly(vinyl chloride) (PVC) as a safer replacement for phthalate plasticizers. Initially, castor oil was transesterified with methanol or n-butanol to quantitatively yield castor fatty acid alkyl esters. Acetylation of hydroxyl function with acetic anhydride led to the formation of estolide. The unsaturation was epoxidized, resulting in a bifunctional epoxy fatty acid alkyl ester estolide. The bioplasticizers were compounded with PVC and were evaluated for their functionality and compared with commercial phthalate plasticizer diisononyl phthalate (DINP) and nonphthalate 1,2-cyclohexanoic acid diisononyl ester (DINCH). The bioplasticizers showed excellent gelation, efficiency, and compatibility, as well as plastisol viscosity and thermal properties, comparable to or better than the plastisols prepared with commercial controls DINP and DINCH. The volatility of the methyl ester was inferior to the butyl ester. Both compounds showed low water resistance properties. Further evaluation of the butyl ester under tropical conditions of high temperature and humidity confirmed limited compatibility. This indicates that the castor epoxy fatty acid ester estolides would be better suited for applications that do not come in contact with water for prolonged periods, such as flooring, artificial leather, wiring, or wall coverings.     

Synthesis and application of a natural plasticizer based on cardanol for poly(vinyl chloride)

A natural plasticizer with multifunctional groups, similar in structure to phthalates, cardanol derivatives glycidyl ether (CGE) was synthesized from cardanol by a two‐step modification process and characterized by FT‐IR, ¹HNMR, and ¹³CNMR. The resulting product was incorporated to PVC (CGE/PVC), and plasticizing effect was compared with PVC incorporated with two kinds of commercial phthalate ester plasticizers bis (2‐ethylhexyl) benzene‐1,4‐dicarboxylate (DOTP) and diisononyl phthalate (DINP). Dynamic mechanical analysis and mechanical properties testing of the plasticized PVC samples were performed in order to evaluate their flexibility, compatibility, and plasticizing efficiency. SEM was employed to produce fractured surface morphology. Thermogravimetric analysis and discoloration tests were used to characterize the thermal stabilities. Dynamic stability analysis was used to test the processability of formulations. Compared with DOTP and DINP plasticized samples, CGE/PVC has a maximum decrease of 9.27% in glass transition temperature (T_g), a maximum increase of 17.6% in the elongation at break, and a maximum increase of 31.59°C and 25.31 min in 50% weight loss (T50) and dynamic stability time, respectively. The obtained CGE also has slightly lower volatility resistance and higher exudation resistance than that of DOTP and DINP. © 2015 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2015 , 132, 42465.     

Effects of poly(butylene succinate) and ultrafine wollastonite on the physical properties of plasticized poly(vinyl chloride)

In this study, diisononyl phthalate (DINP), a conventional plasticizer of poly(vinyl chloride) (PVC), was partially replaced by a polymeric plasticizer, poly(butylene succinate) (PBS), in order to reduce the leaching out of low‐molecular‐weight plasticizer from the plasticized PVC. Samples were prepared by melt mixing on a two‐roll mill followed by compression molding into a 3‐mm thick sheet. The DINP/PBS‐plasticized PVC provides a dose‐dependent increase in the tensile properties (tensile strength, Young's modulus, and elongation at break), tear strength, and thermal stability, as compared with the DINP‐plasticized PVC. According to the overall properties, PVC plasticized with 10/30 phr (parts by weight per hundred parts of resin) DINP/PBS was selected for preparing composites with varied loadings of an ultrafine wollastonite (particle size of 1,200 mesh). Their tensile properties, tear strength, thermal stability, and morphology were evaluated and compared with the 40 phr of DINP‐plasticized PVC composites. The results showed an increase in the Young's modulus and thermal stability but a decrease in the tensile strength, elongation at break, and tear strength of either 40 phr of DINP‐ or 10/30 phr of DINP/PBS‐plasticized PVC composites. Therefore, the products may be useful where the dimensional and thermal stability of the plasticized PVC are needed. J. VINYL ADDIT. TECHNOL. 21:220–227, 2015. © 2014 Society of Plastics Engineers     

Characterization of the Plasticized GAP/PEG and GAP/PCL Block Copolyurethane Binder Matrices and its Propellants

Though glycidyl azide polymer (GAP) is a well‐known and promising energetic polymer, propellants based on it suffer from poor mechanical and low‐temperature properties. To overcome these problems, plasticized GAP‐based copolymeric binders were prepared and investigated through the incorporation of flexible‐structural polyethylene glycol (PEG) and polycaprolactone (PCL) into a binder recipe under a Desmodur N‐100 polyisocyanate (N‐100)/isophorone diisocyanate (IPDI) (2 : 1, wt. ratio) mixed curative system. The nitrate esters (NEs) or GAP oligomer were used as energetic plasticizers at various ratios to the polymers. The GAP/PCL binders held the plasticizers much more than the GAP/PEG binders did. The glass transition temperatures (T_g) of segmented copolymeric binders were more dependent on the plasticizer level than the PEG or PCL content. The increase in the plasticizer content decreased the mechanical strength and modulus of binders, while the change of strain was modest. Finally, the NE plasticized GAP‐based solid propellants showed enhanced mechanical and thermal properties by the incorporation of PEG or PCL. The properties of GAP/PCL propellants were superior to those of GAP/PEG propellants.     

Succinate-based plasticizers: Effect of plasticizer structure on the mechanical and thermal performance of poly(vinyl chloride) plastic formulations

A new family of succinate-based plasticizers, consisting of molecules with a linear alkyl chain capped with n-alkyl succinates on both ends, was evaluated as potential bio-based plasticizers for stiff polymers. The influence of the central and side alkyl chain lengths on the mechanical and thermal properties as well as the migration behavior of poly(vinyl chloride) (PVC)/plasticizer blends was evaluated. The central chain length had the greatest influence on plasticizer performance, with shorter chains leading to blends with higher stress at break and surface hardness, whereas long chains produced softer blends. An optimum chain central length of five carbon atoms was observed, with longer chains leading to reduced compatibility and exudation of the plasticizer at higher plasticizer concentrations. The entire family of plasticizers performed comparably or better than the commercial plasticizer di(2-ethylhexyl) phthalate (DEHP) when incorporated into the blend at concentrations of 20–60 parts per hundred resin (phr). Overall, the succinate-based plasticizers/PVC blends all exhibited equal or improved tensile properties (by up to 77%), surface hardness (reduced by up to 43%), glass transition temperature (reduced by up to 11°C), and migration into organic media (reduced by up to 38%) when compared with blends with DEHP at 40 phr.     

Development of nanocomposites based on organically modified montmorillonite and plasticized PVC with improved barrier properties

Montmorillonite (MMT) was organically modified with tributyl citrate (TBC). Organoclays (OMMTs) were processed with diisononyl phthalate (DINP)‐plasticized polyvinyl chloride (PVC) to form polymer nanocomposites. The produced composite materials showed a contradictory change in properties to that expected of a layered silicate nanocomposite, with a decreased E‐modulus and increased gas permeability compared with a material without OMMT. It was experimentally shown that the TBC modifier was extracted from the OMMT and was dispersed in the PVC/DINP matrix, whereupon the OMMT collapsed and formed micrometer‐sized agglomerates. Further investigation revealed that TBC has a significant effect on the gas permeability and the E‐modulus, even at low additions to a DINP‐plasticized PVC. A PVC nanocomposite with the TBC acting as both the OM for MMT and as the primary plasticizer was produced. This material showed a significantly increased E‐modulus as well as a decrease in gas permeability, confirming that it is possible to develop a nanocomposite based on plasticized PVC, if both the organo‐modification of the MMT and the formulation of the matrix are carefully selected. © 2015 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2016 , 133, 42876.     

Energy and material cost savings with polyester/monomeric plasticized PVC compounds

Many plasticized PVC articles are exposed to harsh environments that cause loss of plasticizer through extraction, volatility, or migration. In order to survive in these applications, the PVC must contain plasticizers that have a reasonable degree of permanence. Two approaches are the use of low molecular weight polyester plasticizers, or higher molecular weight polyester/monomeric plasticizer blends. The blend approach can give better cost-performance and, due to faster fusion, reduced energy/manufacturing costs. The blends maintain their advantages even upon further dilution with monomeric plasticizers and in permanence tests of long duration. Although better than monomeric plasticizers, neither the low molecular weight polyester nor the blend system is recommended for applications requiring the ultimate in migration resistance.     

Thermal properties and crystallinity of PCL/PBSA/cellulose nanocrystals grafted with PCL chains

Bionanocomposite films of poly(?‐caprolactone) (PCL) and poly(butilene succinate‐co ‐adipate) (PBSA) blends with cellulose nanocrystals (CNW) grafted with PCL chains (CNW‐g ‐PCL) were prepared by solution casting and their thermal properties and crystallinity were studied. The CNW surface was modified with PCL chains by grafting “from” approaches, in an effort to improve their compatibility with the polymer blends. The grafting efficiency was evidenced by FTIR and TGA analysis. The acicular morphology of CNW‐g ‐PCL was characterized by SEM. The TGA results showed an increase in the thermal stability of the CNW grafted with PCL chains. The PCL/PBSA blends showed higher thermal stability in comparison with the neat polymers and PCL/PBSA/CNW‐g ‐PCL bionanocomposites. DSC results showed the CNW‐g ‐PCL act as a nucleating agent in the bionanocomposites. Additionally, a better interaction of the CNW‐g ‐PCL in the blends of 30/70 composition in comparison with the blends of 50/50 composition was characterized. The results obtained for aforementioned films prepared by solution casting encourage the production of such bionanocomposites by melt compounding (extrusion), aiming the achievement of new bionanocomposites materials with improved thermal and mechanical properties. © 2016 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2017 , 134 , 44493.     

Solutions to reduce release behavior of plasticizers out of PVC-made equipments: binary blends of plasticizers and thermal treatment

In order to reduce migration of plasticizers out of polyvinyl chloride (PVC), several techniques were attempted. First, binary blends of plasticizers were added to PVC, migration was decreased 100 or 1,000 times as compared to PVC samples containing only one plasticizer: the diffusion coefficient was of the order of 10⁻⁸ cm² s⁻¹ for the blend di-2-ethylhexylphthalate (DEHP)/di-2-ethylhexylterephthalate (TDHP) or 10⁻⁹ cm² s⁻¹ for the blend DEHP/DBP. A thermal treatment of PVC samples containing only one plasticizer leads to diffusion coefficients of the order of 10⁻¹⁰ cm² s⁻¹. This second method was also applied to PVC samples plasticized with binary blends. It lowers even more migration of both plasticizers out of PVC. But no particular phenomena were observed with ternary blends of plasticizers introduced in PVC.     

Morphology and crystallization behavior of PCL/SAN blends containing nanosilica with different surface properties

Morphology and crystallization behavior of poly(?‐caprolactone) (PCL) in its 80/20 blends with poly(styrene‐co‐acrylonitrile) (SAN) containing hydrophobic or hydrophilic nanosilica was investigated. It was found that hydrophilic nanosilica displayed a more significant refinement effect on co‐continuous morphology of PCL/SAN blends than hydrophobic nanosilica for its selective distribution within the PCL matrix but closer to the two‐phase interface. Ring‐banded spherulites were observed in both kinds of nanosilica‐filled blends, the periodic distance of which decreased with increasing nanosilica content. Hydrophilic nanosilica reduced the dependence of the periodic distance of ring‐banded spherulites on the crystallization temperature more efficiently than hydrophobic nanosilica. Furthermore, crystallization process of PCL/SAN blends filled with hydrophobic nanosilica was suppressed as the restriction effect of nanosilica on the crystal growth always outweighed their heterogeneous nucleation effect. In contrast, low content of hydrophilic nanosilica (≤1 wt %) were more likely to exhibit growth restriction effect rather than nucleation effect, whereas heterogeneous nucleation effect of higher content of hydrophilic nanosilica (>1 wt %) dominated over growth restriction effect on facilitating the crystallization behavior. © 2016 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2016 , 133, 44157.     

Melt processed PLA/PCL blends: Effect of processing method on phase structure,morphology, and mechanical properties

Poly(lactic acid) (PLA)‐rich poly(lactic acid)/poly(ε‐caprolactone) (PLA/PCL) blends were melt‐blended at different compositions. The compositions such as 90/10 and 80/20 were obtained using three different blending methods and processed by injection molding and hot pressing. All blends were immiscible. The crystallinity of PLA increased slightly in the presence of poly(ε‐caprolactone) (PCL), and the PCL exhibited fractionated crystallization in the presence of PLA. Injection molded specimens, compared with hot pressed specimens, presented much smaller PCL particles regardless of the blending method used. Some interfacial adhesion was observed in all cases. The stiffness of PLA/PCL blends decreased as the PCL content was increased and was independent of processing. Injection molded specimens showed ductile behavior and broke at elongation values close to 140%, while the elongation at break of the hot pressed specimens was clearly lower, most likely due to the larger size of the PCL particles. Although the impact strength of the blends remained low, it improved by approximately 200% with 30% PCL and by 350% with 40% PCL. © 2015 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2015 , 132, 42641.     

Evaluating effects of biobased 2,5‐furandicarboxylate esters as plasticizers on the thermal and mechanical properties of poly (vinyl chloride)

We synthesized 2,5‐furandicarboxylate esters [i.e., dibutylfuran‐2,5‐dicarboxylate, diisoamylfuran‐2,5‐dicarboxylate, and di(2‐ethylhexyl)furan‐2,5‐dicarboxylate] and investigated their potential application as plasticizers of commercial poly(vinyl chloride) (PVC) products. Fourier transform infrared analysis, mechanical tests, scanning electron microscopy investigation, differential scanning calorimetry analysis, dynamic mechanical thermal analysis, thermogravimetric analysis (TGA), melt flow rate (MFR) measurement, and plasticizer migration measurements were used to the evaluate the comprehensive properties of the blended products. The results of the tensile tests demonstrate that the blends exhibited antiplasticization and flexible plastic characteristics at 10 and 50 phr in PVC, respectively. Moreover, flexural and impact test data indicate that the three types of blends exhibited a similar tendency: the hardness decreased continuously as the amount of plasticizer increased. Their morphology indicated that all of the plasticizers had good compatibility with PVC. The resulting glass‐transition temperature of the investigated plasticizers was lower than that of pure PVC, and reduction was largest for the plasticizer with the highest molecular weight. TGA revealed that the thermal degradation of blended polymers occurred in three stages and that all of the blends were stable up to 180°C. Finally, the MFRs of all of the specimens indicated that the addition of a higher concentration of lower molecular weight biobased esters resulted in improved fluidity, but these compounds migrated more easily from the blends. Hence, 2,5‐furandicarboxylic acid derived from biomass has potential as a plasticizer. © 2014 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2014 , 131, 40938.     

Computerized PVC formulating for optimized cost/performance

The versatility of poly(vinyl chloride) is largely a result of its capability to be modified by a wide variety of formulating additives, especially plasticizers and fillers. These additives vary widely with respect to their chemical composition, and the concentrations used in PVC, which impart significant effects on costs and performance properties. Computerized formulating programs have begun to replace laboratory testing directed at developing cost effective PVC formulations. A broad data base is required to capitalize on the many cost effective options posed to the PVC formulator. The Marketing Technical Service function of Exxon Chemical Co. utilizes COPPCO, COmputerized Profit/Performance COnsulting, to evaluate the options. The coherent data base contains 34 different plasticizers ranging from 25 to 90 phr, and can accommodate filler effects over a range of zero to 100 phr. COPPCO performs the following functions: cost and performance properties are predicted for specific formulations; lowest cost formula is defined to satisfy a specified set of performance properties; cost and performance properties are predicted for blends of plasticizers in unfilled and filled PVC compositions; performance properties are graphically presented as a function of PHR of plasticizer and plasticizer blends; graphic contours define constant property values as a function of plasticizer and of filler levels; and three dimensional response surfaces reflect the coincidental variation of both plasticizer and filler levels. COPPCO utilizes SAS (Statistical Analysis System) and Telegraph graphics, combined with sophisticated mainframe programs developed specifically to provide the desired output. Unlimited cost and performance options of the PVC formulator can be evaluated in milliseconds, vs. the traditional laboratory exercises which result in limited data after one to two weeks of sample preparation and testing.     

Viscosity aging of poly(vinyl chloride) plastisol: The effect of the resin type and plasticizer type

The viscosity of freshly prepared poly(vinyl chloride) (PVC) plastisol increases with time, and this phenomenon is called viscosity aging. The increase is rapid in the beginning and slows down to a quasistable value, but a very slow increase continues. The phenomenon may be a result of either the deagglomeration of agglomerated particles or the dissolution of low‐molecular‐weight PVC into the plasticizer. In this work, two typical commercial resins were used, one containing friable agglomerates and the other containing nonfriable agglomerates. With the friable‐agglomerate resin, about 40% of the initially present agglomerates deagglomerated, whereas the viscosity increased in a week to twice the initial value. With the nonfriable‐agglomerate resin, very fine and very low molecular weight particles, about 3% of all the particles, dissolved into the plasticizer in 2 days. The effect of the plasticizer type on the viscosity aging through deagglomeration was investigated with four plasticizers and three plasticizer blends. The emulsifiers used for polymerization, and retained through drying, affected the aging in the beginning. On the other hand, the viscosity after 1 week was free from the effect of the emulsifier and was affected only by the plasticizer type. With the exception of two blends, the 1‐week viscosity was quantitatively related to the dielectric constant divided by the molecular weight of the plasticizer. For the plasticizer blends, one of the plasticizers could have a dominant effect on the promotion of deagglomeration. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 95: 448–464, 2005     

Novel branched poly(ɛ‐caprolactone) as a nonmigrating plasticizer in flexible PVC: Synthesis and characterization

A series of hyperbranched poly(?‐caprolactone) (HPCLs, denoted as D_X) with different molecular weights were synthesized by the copolymerization of GPCL (PCL initiated by glycidol) and succinic anhydride. The chemical structure of D_X was characterized by ¹H‐NMR gel permeation chromatography and inherent viscosity, and D_X was used as the plasticizer for poly(vinyl chloride) (PVC) compared to traditional plasticizer di‐(ethylhexyl) phthalate (DEHP). The thermal properties, morphology, mechanical properties, and migration stabilities of PVC films were explored with differential scanning calorimetry, thermogravimetric analysis, scanning electron microscope, tensile, and migration tests. PVC/D₁ exhibited the best plasticization efficiency up to 107%, with enhanced tensile strength (18.5 MPa) and ultimate elongation (416%) compared to PVC/DEHP (11.5 MPa and 375%, respectively). PVC/D₁ exhibited remarkably high plasticization efficiency as compared to PVC/DEHP at a plasticizer concentration of PVC below 40 wt %. Moreover, the migration test for PVC/D_X films exhibited minimal plasticizers migration even at very harsh conditions. © 2018 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2018 , 135, 46542.     

Crystallization kinetics of thermosetting polymer blends of poly(ε‐caprolactone) and unsaturated polyester resin

A study has been made of the isothermal crystallization kinetics of poly(ε‐caprolactone) (PCL) in partially miscible crosslinked polyester resin (PER)/PCL blends by using differential scanning calorimetry (DSC). For comparison, miscible blends of PCL with uncured polyester resin, i.e., oligoester resin (OER), were also investigated. The overall crystallization rate of PCL remarkably decreased with the addition of amorphous component, OER or PER. The kinetic rate constant K_n decreased sharply for both the OER/PCL blends and the crosslinked PER/PCL blends with decreasing PCL concentration. The mechanism of nucleation and geometry of the growing PCL crystals was not remarkably affected by the incorporation of OER, but changed considerably with the addition of PER. However, the overall crystallization rate of PCL in the crosslinked PER/PCL blends was much higher compared with the corresponding uncured OER/PCL blends, which is attributable to the phase‐separated structure and the reduced miscibility in the crosslinked blends. According to the nucleation and growth theories, the nucleation process was considered to be the rate controlling step in the crystallization. © 1999 John Wiley & Sons, Inc. J Appl Polym Sci 74: 322–327, 1999